不同pH值下合成的双中孔和六方中孔SiO_2的表征(英文)

在相同的反应体系中当ｐｈ值从约９．５调变至１１时分别合成出双中孔ＳｉＯ２和六方中孔ＳｉＯ２材料,并用ＸＲＤ、Ｎ２吸附、ＴＥＭ、ＴＧ／ＤＴＡ和ＦＴＩＲ等测试手段对合成产物进行了表征。实验结果表明,双中孔ＳｉＯ和六 方中孔ＳｉＯ２是合成中必然出现的两种不同的中孔物相。与六方中孔ＳｉＯ２相比,双中孔ＳｉＯ２也具有典型中孔 材料的特征ＸＲＤ谱图,虽然仅呈现一个易让人产生不完全晶化误解的相对较宽的单ＸＲＤ衍射峰（ｄ＝５．２ｎｍ）,但它却给出一种独特的Ｎ２吸附等温线和窄的双峰中孔孔径分布曲线。由于孔壁的无定形及表面活性剂分子与ＳｉＯ２骨架间相似的相互作用,两类材料给出类似的ＦＴＩＲ谱图和ＴＧ／ＤＴＡ曲线。然而,在双中孔ＳｉＯ２的ＦＴＩＲ谱图中９６０ｃｍ处峰强度的微小变化可能意味着在锻烧脱除模板剂后双中孔ＳｉＯ２较六方中孔ＳｉＯ２具有更高的骨架聚合度。     

A NOVEL ALUMINOSILICATE WITH BIMODAL MESOPORE DISTRIBUTION——SYNTHESIS AND CHARACTERIZATION

用十六烷基三甲基氯化铵和四乙基氢氧化铵作混合模板剂直接水热合成出一种新型的硅酸铝材料（ＮＫＦ２）。该材料具有明显的双中孔分布，其中一种中孔分布在约３．８ｎｍ，另一种在２．６ｎｍ。用Ｘ射线衍射、扫描电镜、Ｎ２吸附、红外、热重分析和２７Ａｌ、２９ＳｉＭＡＳＮＭＲ对合成样品进行表征，以弄清固体产物的孔结构和局域原子排布。产物具有无定形的骨架墙和很宽范围的ＳｉＯＳｉ键角。所有Ａｌ原子都在四配体环境中。同时讨论了形成机理。     

MCM－41中孔分子筛的合成及其性质

以十六烷基三甲基溴化铵（ＣＴＡＢ）作模板剂，研究了水热体系中中孔ＭＣＭ－４１分子筛的合成条件。在Ｈ_２Ｏ／Ｓｉ介于１２～１００，Ｓｉ／Ａｌ介于１０～∞，ＣＴＡＢ／Ｓｉ介于０．０８～０．２时，可以合成出ＭＣＭ－４１分子筛。在加入煤油等混合烃的合成体系中，可以合成出孔径大于４ｎｍ的ＭＣＭ－４１分子筛。用ＸＲＤ、ＳＥＭ、Ｎ_２吸附对合成样品加以表征，证明它们具有典型的中孔分子筛特性。探针反应证明它具有中强酸中心。     

阴离子X~-(F~-、Cl~-、Br~-)对中孔分子筛MCM-41合成与性质的影响

在凝胶体系ＮａＸ（Ｆ、Ｃｌ、Ｂｒ）Ｎａ２ＯＡｌ２Ｏ３ＳｉＯ２ＣＴＡＢ（十六烷基三甲基溴化铵）Ｈ２Ｏ中，研究了水热合成中孔ＭＣＭ４１的合成条件。实验证明，在３９８Ｋ下晶化８～１６ｄ，ＮａＸ／ＳｉＯ２介于０．０１～０．０５时，均可合成出ＭＣＭ４１分子筛；ＮａＦ的加入，可以加快ＭＣＭ４１分子筛的晶化速度；ＮａＢｒ的加入，对形成ＭＣＭ４１分子筛有阻碍作用。采用ＸＲＤ、ＳＥＭ、ＴＧＤＴＡ和Ｎ２吸附对合成样品加以表征，证明合成样品具有介孔分子筛特性。     

Mo/SiO2及V改性的Mo/SiO2催化剂的微孔特征及其对甲烷部分氧化合成甲醛反应的影响

在常压下评价Ｍｏ／ＳｉＯ２催化剂的制备条件对反应性能的，利用Ｎ２的吸附等温线计算了Ｍｏ－Ｖ／ＳｉＯ２催化剂的比表面积和孔径分布，进而讨论了不同的Ｖ加入量对Ｍｏ／ＳｉＯ２催化剂的微孔特征及其催化性能的影响，找到了适宜的Ｖ／Ｍｏ质量比及使甲醛收率最高的最佳孔径，通过ＸＲＤ和ＴＥＭ的测试分析讨论了制备条件对微观状态的影响和Ｖ与Ｍｏ之间的相互作用。     

Mo/SiO_2及V改性的Mo/SiO_2催化剂的微孔特征及其对甲烷部分氧化合成甲醛反应的影响

在常压下评价了Ｍｏ／ＳｉＯ２催化剂的制备条件对反应性能的影响．利用Ｎ２的吸附等温线计算了ＭｏＶ／ＳｉＯ２催化剂的比表面积和孔径分布，进而讨论了不同的Ｖ加入量对Ｍｏ／ＳｉＯ２催化剂的微孔特征及其催化性能的影响，找到了适宜的Ｖ／Ｍｏ质量比及使甲醛收率最高的最佳孔径．通过ＸＲＤ和ＴＥＭ的测试分析讨论了制备条件对微观状态的影响和Ｖ与Ｍｏ之间的相互作用．     

NO^—2离子的光催化反应研究（Ⅱ）

研究了ＮＯ＾－２离子在ＴｉＯ２表面的光催化反应,结果表明,体系ｐＨ值升高及Ｃｒ,Ｃｌ＾－,ＳＯ＾２－４离了的加入均对ＮＯ＾－２离子在ＴｉＯ２表面的暗态吸附产生抑制作用,而ＮＯ＾－２在ＴｉＯ２表面的光照反应转化率则随ｐＨ值的升高出现先减小后增大的总体变化趋势。     

负载型双氯基桥联双核钼(Ⅴ)催化剂的合成、表征及其催化合成碳酸乙烯酯的性能

用表面反应改性法合成了ＭｏＯＣｌ／ＳｉＯ２催化剂。分析测定结果表明：钼（Ⅴ）离子夺ＳｉＯ２表面以双齿配位形式与表面氧刍合;双核钼（Ⅴ）间以ｕ－双氯基桥联。用ＩＲ,ＴＰＤ,ＴＰＳＲ－ＭＳ和ＴＰＳＲ－ＩＲ研究了ＭｏＯＣｌ／ＳｉＯ２催化剂对ＣＯ２与ＥＯ（环氧乙烷）的化学吸附特性及催化合成ＥＣ（碳酸乙烯酯）的反应性能。结果表明：ＣＯ２在催化剂表面形成桥式吸附态,桥基配体是表面反应的活性中心;ＥＯ在催化剂表     

SiO2负载的氮化钼催化剂的合成和表征

采用ＭｏＯ３／ＳｉＯ２和ＮＨ３程序升温反应的方法合成了一系列不同Ｍｏ含量的Ｍｏ２Ｎ／ＳｉＯ２催化剂，并采用ＸＲＤ、ＢＥＴ、ＸＰＳ、ＴＰＲ、Ｈ２－ＴＰＤ和ＩＲ等手段，结合中压下吡啶加氢脱氮反应，研究了它们的表面性质和反应性能。发现Ｍｏ２Ｎ／ＳｉＯ２催化剂在反应性能和吸氢性质等方面类似于非负载的氮化钼。氮化前后，低Ｍｏ担载量催化剂的比表面积降低不大，在高Ｍｏ担载量下，由于氮化态的Ｍｏ－ＳｉＯ２催化剂上     

在（TPA）2O—Na2O—SiO2—H2O体系中MFI型硅沸石的结晶行为（Ⅱ）

以白炭黑和硅溶胶为硅源，在（ＴＰＡ）２Ｏ－Ｎａ２Ｏ－ＳｉＯ２－Ｈ２Ｏ体系６０℃下合成了高结晶度纯相硅沸石，由ＳＥＭ没得其晶粒尺寸为０．２μｍ和０．４５μｍ用ＸＲＤ线宽法是的为０．０２μｍ，一１８０℃时合成的硅沸石样品相比，低温合成的细晶粒硅沸石已上备内米级的若干特性，其正己烷吸附量反常增大；ＸＲＤ、ＦＴＩＲ、＾２９ＳｉＭＡＳ ＮＭＲ和ＴＧ／ＤＴＧ／ＤＴＡ的研究证明，其结构破坏温度和单斜／正交对称性     

合成条件对硅胶整体柱中孔结构的影响

硅胶整体柱是目前备受关注的液相色谱固定相。本文考察了合成条件对硅胶整体柱中孔结构的影响,包括反应体系的pH值、聚乙二醇(PEG)含量及分子量。实验表明,反应体系的pH值能有效地调控硅胶整体柱的中孔孔径及孔结构,当pH值为2或5时,整体柱中孔孔径较小;而当pH值为3或9时,孔径较大,孔结构趋于圆筒状。整体柱的中孔平均孔径随着PEG含量和分子量的增加而增加,其孔径分布也逐渐变宽。     

以光诱导Fenton反应控制M-PEIs纳米凝胶的粒径

基因治疗,就是将正常基因导入体内以弥补缺失或替换突变基因来医治囊性纤维化和血友病等[1]多种疾病.而制备高效安全的基因转染载体至今仍是基因治疗的一个瓶颈.非病毒类载体的基因转染效率目前虽不高,但由于其具有低毒、低免疫反应、无基因插入片断大小限制、制备方便、易保存     

Synthesis, characterization, and in vitro pH-controllable drug release from mesoporous silica spheres with switchable gates

To accomplish pH-controllable drug release on mesoporous carrier, one of the best ways is to graft stimuli-responsive organic molecules around mesopore outlets. In this work, the pH-responsive propyldiethylenetriamine groups (abbreviative phrase: multiamine chains) were grafted around mesopore outlets of mesoporous silica spheres (MSS) and expected to act as pH-responsive gates. To this end, three multiamine-grafted MSS (i.e., NM1, NM2, and NM3) were synthesized under different reaction temperatures and reaction times. The reaction temperature and time for multiamine grafting were 25 °C and 12 h for NM1, 100 °C and 1 h for NM2, and 100 °C and 12 h for NM3, respectively. Through systematic investigations of TEM, SEM, N(2) adsorption/desorption, TG, and (29)Si MAS NMR, it was found that NM3 had the highest grafting amount of multiamine chains. It was further confirmed that the multiamine chains around the pore outlets of NM3 played the role of "molecular switch" that could well control the transport of guest drug molecules. In contrast, the multiamine chains around the pore outlets of NM2 and NM3 did not show gate effect. The difference should be decided by the fact whether the grafting amount of multiamine chains around mesopore outlets were sufficient under determined reaction temperature and time. In the tests of in vitro drug release, multiamine-gated MSS (i.e., NM3) showed highly sensitive response to the solution pH. At high pH (pH 7.5), ibuprofen (IBU) in this carrier released rapidly and completely within 2 h; at low pH (pH 4.0 or 5.0), only a small part of the IBU (13 wt %) was slowly released from this carrier and the most of IBU was effectively confined in mesopores.     

不同分子筛的氮氩分离性能

采用水溶液离子交换法制备了不同离子交换的13X和4A分子筛,并在25℃下测 定了它们的静态吸附等温线和动态穿透曲线。研究发现,Ca~(2+)离子和Li~+离子 交换的13X和4A分子筛对氮的吸附性能都明显优于其相应的钠型分子筛,而它们对 氩的吸附量变化不大,说明这两种离子交换的分子筛是较好的氮氩分离吸附剂。从 动态吸附的结果来看,所研究的各种分子筛都有一个最优的吸附分离压力,在本论 文研究的压力范围内,这个最优压力在0.6MPa附近。通过穿透曲线推算出的混合气 体吸附量和纯气体吸附量的对比可以得出,对于氮氩吸附选择性较高的分子筛,氮 的存在对氩的吸附量有较大的影响。     

钒酸铋颜料制备实验的改进——pH优化

使用改进的实验装置研究钒酸铋颜料制备实验中p H对产物的影响。X射线衍射分析结果表明,在选定实验条件下,产物为四方相为主的四方、单斜两相混合物。p H对钒酸铋颜色有重要影响。酸性条件下颜色偏深,为土黄色;碱性条件下为亮黄色,且p H越大,颜色越淡。推荐反应p H为9,此时产物颜色呈色调较好的亮黄色。     

Selective Synthesis in Microdroplets of 2-Phenyl-2,3-dihydrophthalazine-1,4-dione from Phenyl Hydrazine with Phthalic Anhydride or Phthalic Acid

Pyridazine derivatives are privileged structures because of their potential biological and optical properties. Traditional synthetic methods usually require acid or base as a catalyst under reflux conditions with reaction times ranging from hours to a few days or require microwave assistance to induce the reaction. Herein, this work presents the accelerated synthesis of a pyridazine derivative, 2-phenyl-2,3-dihydrophthalazine-1,4-dione (PDHP), in electrosprayed microdroplets containing an equimolar mixture of phenyl hydrazine and phthalic anhydride or phthalic acid. This reaction occurred on the submillisecond timescale with good yield (over 90 % with the choice of solvent) without using an external catalyst at room temperature. In sharp contrast to the bulk reaction of obtaining a mixture of two products, the reaction in confined microdroplets yields only the important six-membered heterocyclic product PDHP. Results indicated that surface reactions in microdroplets with low pH values cause selectivity, acceleration, and high yields.     

Sol–gel synthesis, characterization and catalytic activity of γ-alumina with bimodal mesopore distribution

In this study, boehmite sols were used for preparation of mesoporous γ-alumina with bimodal mesopore distribution. Superfine nanospheres of poly(methyl methacrylate) (PMMA) prepared by water based emulsion polymerization method were used as a template. Nitrogen sorption revealed that aluminas prepared using this approach demonstrated bimodal mesopore size distribution with maxima at 3.8 and 25.7 nm, respectively. Catalytic tests showed that bimodal mesopore distribution within γ-Al₂O₃ prepared with PMMA nanospheres as a template provides improved catalytic activity in the methanol dehydration reaction.     

二甲醚合成催化剂失活原因的研究

采用胶体沉积法制备了Cu-ZnO-ZrO2／HZSM-5二甲醚合成催化剂．对二甲醚合成过程中催化剂的失活原因进行了初步研究．采用BET，NH3TPD，TPD，TP0和N2O脉冲实验对催化剂使用前后比表面积，表面酸性，表面吸附物种，表面积碳和活性组分Cu比表面积的变化进行了研究．发现，在二甲醚合成过程中，催化剂表面酸性，催化剂表面吸附物种和表面积碳变化较小，不是导致催化剂失活的主要原因．而催化剂在使用过程中活性组分Cu烧结使Cu比表面积降低是催化剂失活的主要原因．