水氯镁石气固反应制备无水氯化镁

用盐湖水氯镁石在氮气保护下135℃脱水2h成低水合水氯镁石。低水合水氯镁石与固体氯化铵按质量比1:6.5混合,高温下使反应体系中NH3的分压达49.6KPa以上,在440℃脱水18分钟和710℃煅烧12分钟成无水氯化镁。分析结果表明:制得的无水氯化镁中氧化镁的质量分数为小于0.15%。X射线衍射和电镜扫描图证明,制得的无水氯化镁无杂相,颗粒大而均匀,分散性好,适合于电解制备金属镁。方法简单,生产成本低,固体氯化铵可以回收循环使用。     

复盐法制备无水氯化镁的热解机理及动力学研究

The complex compound (MgCl₂·C₆H₅NH₂·HCl·6H2O) was prepared by reaction of C₆H₅NH₂·HCl with MgCl₂·6H₂O. Reaction mechanism and kinetics of the compounds decomposition were studied by means of the TG-DTA-MS coupling technique and the TG-DTA technique. The results show that there are four steps in the complex′s thermal decomposition, the first two steps correspond to the loss of six crystal waters and the last two steps loss one Aniline hydrochloride. The first three steps belong to the R2 mechanism with 2-dimentional phase boundary reaction as the control step, and the last step belongs to the D3 with 3-dimensional diffusion (sphere Jander equ.) as the control step. The apparent active energy of four steps are, 127.4 kJ·mol^-1, 124.8 kJ·mol^-1, 142.3 kJ·mol^-1 and 329.0 kJ·mol^-1, respectively and the frequency factor are 1.28 × 10¹⁸ s^-1, 7.94 × 10¹⁵ s^-1, 5.98 × 10¹⁶ s^-1 and 4.39 × 10³⁴ s^-1, respectively.     

碱式氯化镁5Mg(OH)2·MgCl2·3H2O的制备与表征

以氨水和盐湖盛产的水氯镁石为原料经过两步反应制备碱式氯化镁.第一步,水氯镁石和氨水反应制备氢氧化镁;第二步,利用氢氧化镁和水氯镁石,通过水热反应得到了具有纤维形貌、结晶较好的碱式氯化镁.应用化学分析、XRD、SEM和FIIR等手段对产物进行测试与表征.化学分析结果表明产物组成为5Mg(OH)2·MgCl2·3H2O.将得到的5Mg(OH)2·MgCl2·3H2O和碱式氯化镁系列标准XRD图对照,未有较好的匹配,且结合化学分析和已报道碱式硫酸镁具有5Mg(OH)2·MgSO4·3H2O物相,因而推测其为新物相;SEM图中5Mg(OH)2·MgCl2·3H2O纤维直径约为0.4μm,平均长度大于24 μm,长径比大于60;FTIR图谱中3419 cm-1附近出现了氢键的O-H伸缩振动吸收峰,1635 cm-1附近出现了游离水中H-O-H的弯曲振动吸收峰.水热合成的5Mg(OH)2·MgCl2·3H2O和常压下的产物相比直径较小,晶形更完整,强度更高.     

碱式氯化镁5Mg(OH)2·MgCl2·3H2O的制备与表征

以氨水和盐湖盛产的水氯镁石为原料经过两步反应制备碱式氯化镁。第一步,水氯镁石和氨水反应制备氢氧化镁;第二步,利用氢氧化镁和水氯镁石,通过水热反应得到了具有纤维形貌、结晶较好的碱式氯化镁。应用化学分析、XRD、SEM和FIIR等手段对产物进行测试与表征。化学分析结果表明产物组成为5Mg(OH)₂·MgCl₂·3H₂O。将得到的5Mg(OH)₂·MgCl₂·3H₂O和碱式氯化镁系列标准XRD图对照,未有较好的匹配,且结合化学分析和已报道碱式硫酸镁具有5Mg(OH)₂·MgSO₄·3H₂O物相,因而推测其为新物相;SEM图中5Mg(OH)₂·MgCl₂·3H₂O纤维直径约为0.4 μm,平均长度大于24 μm,长径比大于60;FTIR图谱中3 419 cm^-1附近出现了氢键的O-H伸缩振动吸收峰,1 635 cm^-1附近出现了游离水中H-O-H的弯曲振动吸收峰。水热合成的5Mg(OH)₂·MgCl₂·3H₂O和常压下的产物相比直径较小,晶形更完整,强度更高。     

有机溶剂法无水氯化镁的制备与表征

Ammonium carnallite was synthesized by hydrated magnesium chloride in salt lake and ammonium chloride solution. Dehydrated ammonium carnallite was dissolved in methanol under low temperature by feeding ammonia, to prepare anhydrous magnesium chloride. The results show that anhydrous magnesium chloride contains magnesium oxide in an amount less than 0.1% by weight, the yield of magnesium chloride was above 99.5%. Ammonium carnallite, ammoniation magnesium chloride and anhydrous magnesium chloride were characterized by thermoanalysis, X-ray powder diffraction and scanning electron microscopy.     

钾长石矿热分解过程的研究

研究了钾长石矿热分解过程的反应行为和动力学.对6种钾长石体系进行了热力学分析,计算了各反应在800～1600K的△G_T⁰,并以此指导实验.研究了焙烧温度、停留时间和助剂配比对钾长石体系热分解为水溶性钾的影响,得出最佳操作条件.添加0.9%添加剂Ⅰ能使适宜焙烧温度由1323K降至1223K,钾分解率可达84%.不加与加入添加剂Ⅰ的2种钾长石体系热分解过程皆符合克-金-布动力学方程,均受固膜扩散控制,表观活化能分别为184.84kJ/mol和158.9kJ/mol,并给出相应的动力学方程.     

过氧化苯甲酰的热分解研究

The thermal decomposition process of benzoyl peroxide was investigated by Accelerating Rate Calorimeter. The curves of thermal decomposition temperature and pressure versus time for the systems were obtained. The curves of temperature rising-rate versus thermal decomposition temperature were also obtained. After the data revision disposal and analysis processing, thermal decomposition parameters and kinetic data of benzoyl peroxide were calculated, respectively.     

MgAl-水滑石热分解过程动力学研究

类水滑石化合物Hydrotalcite-like Compounds(简称HTLcs)又称阴离子粘土,是由带正电荷的氢氧化物层和层间阴离子构成[1]。由于在类水滑石结构中含有大量的结构羟基和层间可分解的阴离子,所以其热稳定性较差,易于分解形成具有一定酸碱性及大比表面的复合氧化物,该复合氧化物由于具有晶粒小、活性元素分布均匀、比表面积大等特点,表现出了优异的催化性能[2~5]。近年来,以HTLcs为前体经高温焙烧制备双金属复合氧化物备受关注[6]。揭示类水滑石热解机理、选择焙烧条件是催化剂制备的关键所在。本文利用TG-DTA技术详细研究了不同镁铝比HTL…     

甲氰菊酯的热容及热力学性质的研究

采用精密自动绝热量热测量了自已合成并提纯到0.9916(摩尔分数)的甲氰菊酯在80~400K温区的热容.在此温区发现一固液熔化相变.其熔化温度、摩尔熔化焓、摩尔熔化熵分别为:(322.476^+~-0.012)K,(18.57^+~-0.29)kj.mol^-^1,(57.59^+~-1.01)J.K^-^1.mol^-^1.报道了该物质每隔5K的热力学函数值,用热重法研究了该化合物的热分解,对试样的化学纯度进行了量热研究。     

阴离子型有机化合物在LDHs上的动力学和热力学研究

本文考察水滑石焙烧产物MgAl-LDO吸附3种阴离子染料AcidRed88（AR88）、AcidOrange 3（AO3）、AcidViolet90（AV90）过程中的热力学和动力学机理,并在不同温度下探究该吸附过程的热力学参数。实验结果表明：MgAl-LDO对染料阴离子的吸附过程复合Langmuir吸附等温模型,且为自发、放热的过程。3种染料在MgAl-LDO上的吸附过程均符合准二级反应动力学模型,且该吸附过程是由MgAl-LDO与阴离子染料之间的反应速率控制而不是两者之间的扩散作用。计算所得的吉布斯自由能绝对值在7~15kJ·mol^-1,这主要是由染料阴离子与MgAl-LDHs层板的氢键作用产生,结合MaterialsStudio 5.5软件模拟染料分子在MgAl-LDHs上的排列分布,推测MgAl-LDO对阴离子染料的吸附机理是表面吸附（占优势）与层间插层的协同作用。     

铵光卤石气固反应法制备无水氯化镁

铵光卤石气固反应法制备无水氯化镁;ouig     

Synthesis and Thermal Study of Magnesium Complexes with 8-hydroxyquinolinate Derivatives

Magnesium ion was reacted with 5,7-dibromo-, 5,7-dichloro-, 7-iodo-and 5-chloro-7-iodo-8-hydroxyquinoline, in acetone/ammonium hydroxide medium under constant stirring to obtain (I) Mg[(C₉H₄ONBr₂)₂]·2H₂O; (II) Mg[(C₉H₄ONCl₂)₂]·3H₂O; (III) Mg[(C₉H₅ONI)₂]·2H₂O and (IV)Mg[(C₉H₄ONICl)₂]·2.5H₂O complexes. The compounds were characterized by elemental analysis, IR spectra, ICP, TG-DTA and DSC. Through thermal decomposition residues were obtained and characterized, by X-ray diffractometry, as a mixture of hexagonal MgBr₂ and cubic MgO to the (I) compound at 850°C; cubic MgO to the (II), (III) and (IV) compounds at750, 800 and 700°C, respectively. This revised version was published online in July 2006 with corrections to the Cover Date.     

草酸镁二水合物的非等温热分解动力学

The thermal decomposition of the magnesium oxalate dihydrate in a static air atmosphere was investigated by TG-DTG techniques. The intermediate and residue of each decomposition were identified from their TG curve. The kinetic triplet, the activation energy E, the pre-exponential factor A and the mechanism functionsf（a） were obtained from analysis of the TG-DTG curves of thermal decomposition of the first stage and the second stage by the Popesou method and the Flynn-Wall-Ozawa method.     

Non-isothermal Kinetics of the Thermal Decomposition of 3-Nitro-1,2,4-triazol-5-one Magnesium Complex

Introduction3 Nitro 1,2 ,4 triazol 5 one (NTO)metalcomplexeshavemanyspecialstructuresandsomepotentialusesinammunition .1 4 Wepreviouslypreparedanddeterminedthecrystalstructureofitsmagnesiumcomplex ,5andinthispaper ,wediscusseditsthermalbehaviorbyDSCandTG/DTGtechniquesandstudieditsnon isothermalkineticsbythemeansoftheKissingermethod ,theOzawamethod ,thedifferentialmethodandtheintegralmethod .ExperimentalSample[Mg(H2 O) 6 ](NTO) 2 ·2H2 Owaspreparedasfollows :AcalculatedamountofMg(OH…     

Study of In Situ Formation of Magnesium Hydroxide Whisker via Basic Magnesium Chloride Whisker Regulated by Organic Parcels at Low Temperature

In this work, we demonstrate an in situ phase conversion from basic magnesium chloride（BMC） into magnesium hydroxide whisker by using polar organic solvent at low temperature. The morphology and phase composition of magnesium hydroxide whiskers prepared at different reaction temperature, alkali concentration and organic solvent were analyzed by X-ray diffraction（XRD） and scanning electronic microscope（SEM）. It was found that when one of the organic solvents such as absolute ethyl alcohol, butanol, polyethylene glycol（PEG-400）, acetone, et al. was selected as the template, the precursor BMC can transform into whisker-like magnesium hydroxide through precipitate transformation in low temperature and non-hydrothermal system. It can be reasonably explained that the regulation of Mg^2＋ solubility by those organic solvents and the sustained release of Mg^2＋ dissolution by organic adsorption played a significant role in the formation of magnesium hydroxide whisker via BMC whisker as the precursor.     

探究镁与氯化钠溶液反应的微观过程*

镁在常温下和水发生反应的速率较慢,这是因为镁表面存在氢氧化镁附着层的保护作用,但是镁可以和NaCl溶液发生较快的反应,在产生大量气泡的同时生成白色固体。通过对白色固体进行分析发现,在有Cl^-的环境下氢氧化镁会逐渐转化为碱式氯化镁,同时也会导致溶液pH的升高。经过实验探究发现,镁在不同浓度NaCl溶液中的反应现象存在差异,在反应过程中溶解氧含量也会下降。     

鬼臼毒素及其衍生物热分解反应的动力学研究

The thermal behavior and thermal decomposition kinetic parameters of podophyllotoxin （1） and 4 derivatives, picropodophyllin （2）, deoxypodophyllotoxin （3）, fl-apopicropodophyllin （4）, podophyllotoxone （5） in a temperature-programmed mode have been investigated by means of DSC and TG-DTG. The kinetic model functions in differential and integral forms of the thermal decomposition reactions mentioned above for first stage were established. The kinetic parameters of the apparent activation energy Ea and per-exponential factor A were obtained from analy- sis of the TG-DTG curves by integral and differential methods. The most probable kinetic model function of the decomposition reaction in differential form was （1- a）^2 for compounds 1-3,2/3·a^-1/2 for compound 4 and 1/2（1-a）·[-In（1-a）]^-1 for compound 5. The values of Ea indicated that the reactivity of compounds 1-5was increased in the order： 5〈4〈2〈1〈3. The values of the entropy of activation △S^≠, enthalpy of activation △H^≠ and free energy of activation △G^≠ of the reactions were estimated. The values of △G^≠ indicated that the thermal stability of compounds 1-3 with the samef（a） was increased in the order： 2〈3〈1.