Grain size of nanocrystalline YSZ buffer layers fabricated by ion beam deposition

Amorphous or nanocrystalline thin films are capable to be efficient diffusion barrier layers for YBCO coated conductors of ion beam assisted deposition route. Nanocrystalline Yttria-Stabilized Zirconia (YSZ) buffer layers were fabricated by the ion beam deposition. Kr and Ar gases were utilized for the dual Kaufman type sputtering ion sources sequently. Both of the ion beams were fixed at 200 mA, while the ion energy was in the range of 450–2000 eV. The thickness of the YSZ buffer layers was several hundreds of nanometers. The grain size of YSZ thin films, which varied from 2 to 20 nm, was calculated by Scherrer Formulation based on the X-ray diffraction measurement results. The grain size always decreased at first and then increased when the ion energy was increased. In the cases Kr gas was utilized and Ar gas was utilized, the grain size reached its minimum value at the ion energy of about 1800 eV and 1000 eV, respectively. Such phenomenon was discussed using the thermodynamic theory of thin film nucleation. Deposition rate and substrate temperature were the two chief variables of the critical nuclei concentration and grain size.     

Influence of argon ambience on the structural,morphological and optical properties of pulsed laser ablated zinc sulfide thin films

Nanostructured zinc suplhide thin films are successfully deposited on quartz substrates using pulsed laser deposition (PLD) under different argon pressures (0, 5, 10, 15 and 20 Pa). The influence of argon ambience on the microstructural, optical and luminescence properties of zinc sulfide (ZnS) thin films is systematically investigated. The GIXRD data suggests rhombohedral structure for ZnS films prepared under different argon ambience. Self-assembly of grains into well-defined patterns along the y direction is observed in the AFM image of the film deposited under argon pressure 20 Pa. All the films show a blue shift in optical band gap. This can be due to the quantum confinement effect and less widening of conduction and valence band for the films with less thickness and smaller grain size. The PL spectra of the different films are recorded at excitation wavelengths 250 nm and 325 nm and the spectra are interpreted. The PL spectra of the films recorded at excitation wavelength 325 nm show intense yellow emission. The film deposited under an argon pressure of 15 Pa shows the highest PL intensity for excitation wavelength 325 nm. For the PL spectra (excitation at 250 nm), the highest PL intensity is observed for the film prepared under argon free ambience. In our study, 15 Pa is the optimum argon pressure for better crystallinity and intense yellow emission when excited at 325 nm.     

Effect of Al-doping on optical and electrical properties of spray pyrolytic nano-crystalline CdO thin films

CdO and Al-doped CdO nano-crystalline thin films have been prepared on glass at 300 °C substrate temperature by spray pyrolysis. The films are highly crystalline with grain size (18–32 nm) and found to be cubic structure with lattice constant averaged to 0.46877 nm. Al-doping increased the optical transmission of the film substantially. Direct band gap energy of CdO is 2.49 eV which decreased with increasing Al-doping. The refractive index and dielectric constant varies with photon energy and concentration of Al as well. The conductivity of un-doped CdO film shows metallic behavior at lower temperature region. This behavior dies out completely with doping of Al and exhibits semiconducting behavior for whole measured temperature range. Un-doped and Al-doped CdO is an n-type semiconductor having carrier concentration is of the order of ∼10²¹ cm⁻³, confirmed by Hall voltage and thermo-power measurements.     

Effect of thickness on the structural,optical and electrical properties of thermally evaporated PbI2 thin films

This work describes the physical properties of lead iodide (PbI₂) thin films with different thicknesses that were deposited on ultrasonically cleaned glass substrates using a thermal evaporation technique at 5×10^-6 torr. The initial material was purified by the zone refining technique under an atmosphere of argon gas. XRD analysis of the material demonstrates that the thin films were preferably oriented along the (001) direction. The size of the crystallites was calculated from the Scherer relation and found to be in the range of ～5–10 nm, with higher values being observed for increasing film thicknesses. The optical energy band gaps were evaluated and determined to belong to direct transitions. Because the band gap increased with decreasing film thickness, a systematic blue shift was observed. The surface morphologies of PbI₂ films exhibited a clear increase in grain size with increasing film thickness. The photoluminescence and dc conductivity of the thin films are also discussed.     

Hydrogen permeation of tungsten phosphate glass thin films

Thin films of tungsten phosphate glasses were deposited on a Pd substrate by a pulsed laser deposition method and the flux of hydrogen passed thorough the glass film was measured with a conventional gas permeation technique in the temperature range 300–500 °C. The glass film deposited at low oxygen pressure was inappropriate for hydrogen permeation because of reduction of W ions due to oxygen deficiency. The membrane used in the hydrogen permeation experiment was a 3-layered membrane and consisted of Pd film (~ 20 nm), the glass film (≤ 300 nm) and the Pd substrate (250 µm). When the pressure difference of hydrogen and thickness of the glass layer were respectively 0.2 MPa and ~ 100 nm, the permeation rate through the membrane was 2.0 × 10^? 6 mol cm^? 2 s^? 1 at 500 °C. It was confirmed that the protonic and electronic mixed conducting glass thin film show high hydrogen permeation rate.     

Nanocrystalline diamond thin films deposited by 35 kHz Ar-rich plasmas

We give evidence of nanometric size (5–15 nm) crystalline diamonds in carbon thin films obtained at low substrate temperature (15 °C) under the action of low pressure (0.1–0.3 Torr) 35 kHz excited CH₄/Ar (80–95%) plasmas. The decrease in Ar concentration was found to lead to higher film hardness while crystalline nanodiamonds are observed in a wide interval (1–3.5 h) of deposition times but only for very high Ar concentration (95%). The polycrystalline nanodiamond grains are found over 10–20% within an amorphous carbon matrix. It is suggested that the distribution of nanodiamond grains might be connected to the nonuniform ion energy distribution in the Ar-rich plasma generated at 35 kHz. Morphological and structural features of the deposited films were also investigated.     

Factors affecting the electro-optical and structural characteristics of nano crystalline Cu doped (Cd–Zn)S films

This work investigates the effects of the temperature, deposition time and annealing ambient on the electro-optical and structural properties of nano crystalline (Cd–Zn)S films prepared by chemical bath deposition (CBD). The deposited films being uniform and adherent to the glass substrates are amorphous in nature and the crystallinity as well as the grain size is found to increase on post-deposition annealing. The obtained specimens are thoroughly characterized before and after annealing paying particular attention to their structure, composition and morphology. Annealing in air reduces the extent of disorder in grain boundaries and energy band-gap. A correlation between the structural and optical properties is investigated in detail. The surface morphology and structural properties of the as-deposited and annealed (Cd–Zn)S thin films are studied using X-ray diffraction (XRD), scanning electron microscope (SEM) and optical transmission spectra. The optical transmission spectra are recorded within the range of 300–800 nm and 300–900 nm. The electroluminescent (EL) intensity is found to be maximum at a particular temperature, which decreases with further increase in temperature and peaks of photoluminescent (PL) and EL spectra are centered at 546 nm and 592 nm. The emission intensity also increases with increasing thickness of the film.     

Hard magnetic properties of rapidly annealed NdFeB thin films on Nb and V buffer layers

NdFeB thin films of the form A (20 nm)/NdFeB(d nm)/A(20 nm), where d ranges from 54 to 540 nm and the buffer layer A is Nb or V were prepared on a Si(1 0 0) substrate by magnetron sputtering. The hard Nd₂Fe₁₄B phase is formed by a 30 s rapid anneal or a 20 min anneal. Average crystallite size ranged from 20 to 35 nm with the rapidly annealed samples having the smaller crystallite size. These samples also exhibited a larger coercivity and energy product than those treated by a 20 min vacuum anneal. A maximum coercivity of 26.3 kOe at room temperature was obtained for a Nb/NdFeB (180 nm)/Nb film after a rapid anneal at 725°C. Initial magnetization curves indicate magnetization rotation rather than nucleation of reverse domains is important in the magnetization process. A Brown's equation analysis of the coercivity as a function of temperature allowed us to compare the rapidly annealed and 20 min annealed samples. This analysis suggests that rapid annealing gives higher quality crystalline grains than the 20 min annealed sample leading to the observed large coercivity in the rapidly annealed samples.     

Preparation of cadmium stannate films by spray pyrolysis technique

Cadmium stannate thin films were prepared by spray pyrolysis technique using cadmium acetate and tin(II) chloride precursors at substrate temperatures 450 °C and 500 °C. XRD pattern confirms the formation of orthorhombic (1 1 1) cadmium stannate phase for the film prepared at substrate temperature of 500 °C, whereas, films prepared at 450 °C are amorphous. Film formation does not occur at substrate temperature from 300 to 375 °C. SEM images reveal that the surface of the prepared Cd₂SnO₄ film is smooth. The average optical transmittance of ∼86% is obtained for the film prepared at substrate temperature of 500 °C with the film thickness of 400 nm. The optical band gap value of the films varies from 2.7 to 2.94 eV. The film prepared at 500 °C shows a minimum resistivity of 35.6 × 10⁻⁴ Ω cm.     

Thickness dependence of Ic and Jc of LTG-SmBCO coated-conductor on IBAD-MgO tapes

We have reported SmBa₂Cu₃O_y (SmBCO) films on single crystalline substrates prepared by low-temperature growth (LTG) technique. The LTG-SmBCO films showed high critical current densities in magnetic fields compared with conventional SmBCO films prepared by pulsed laser deposition (PLD) method. In this study, to enhance critical current (I_c) in magnetic field, we fabricated thick LTG-SmBCO films on metal substrates with ion-beam assisted deposition (IBAD)-MgO buffer and estimated the I_c and J_c in magnetic fields.All the SmBCO films showed c-axis orientation and cube-on-cube in-plane texture. T_c of the LTG-SmBCO films were 93.1–93.4 K. J_c and I_c of a 0.5 μm-thick SmBCO film were 3.0 MA/cm² and 150 A/cm-width at 77 K in self-field, respectively. Those of a 2.0 μm-thick film were 1.6 MA/cm² and 284 A/cm-width respectively. Although I_c increased with the film thickness increasing up to 2 μm, the I_c tended to be saturated in 300 A/cm-width. From a cross sectional TEM image of the SmBCO film, we recognized a-axis oriented grains and 45° grains and Cu–O precipitates. Because these undesired grains form dead layers, I_c saturated above a certain thickness. We achieved that I_c in magnetic fields of the LTG-SmBCO films with a thickness of 2.0 μm were 88 A/cm-width at 1 T and 28 A/cm-width at 3 T.     

Field electron emission from amorphous carbon films grown in pure methane plasma

By using RF plasma-enhanced chemical vapor deposition, amorphous carbon films were grown in pure methane plasma. Field emission of the films were examined as a function of substrate temperature. It was found that the emission current from the samples prepared at substrate temperatures higher than 600 °C were considerably improved. According to the results by Raman spectroscopy, growth of graphite crystallites were promoted with high substrate temperatures. Moreover, the surface morphology was abruptly changed at high substrate temperatures over 600 °C. We discuss the field emission characteristics of the amorphous carbon films with regard to the structural features and the surface morphology.     

Exciton-polariton state in nanocrystalline SiC films

We studied the features of optical absorption in the films of nanocrystalline SiC (nc-SiC) obtained on the sapphire substrates by the method of direct ion deposition. The optical absorption spectra of the films with a thickness less than ~500 nm contain a maximum which position and intensity depend on the structure and thickness of the nc-SiC films. The most intense peak at 2.36 eV is observed in the nc-SiC film with predominant 3C-SiC polytype structure and a thickness of 392 nm. Proposed is a resonance absorption model based on excitation of exciton polaritons in a microcavity. In the latter, under the conditions of resonance, there occurs strong interaction between photon modes of light with λ_ph=521 nm and exciton of the 3С polytype with an excitation energy of 2.36 eV that results in the formation of polariton. A mismatch of the frequencies of photon modes of the cavity and exciton explains the dependence of the maximum of the optical absorption on the film thickness.     

The improvement of pyroelectric properties of PZT thick films on Si substrate by TiOx barrier layer

The effects of TiO_x diffusion barrier layer thickness on the microstructure and pyroelectric characteristics of PZT thick films were studied in this paper. The TiO_x layer was prepared by thermal oxidation of Ti thin film in air and the PZT thick films were fabricated by electrophoresis deposition method (EPD). To demonstrate the barrier effect of TiO_x layer, the electrode/substrate interface and Si content in PZT thick films were characterized by scanning electron microscope (SEM) and X-ray energy dispersive spectroscopy (EDS), respectively. The TiO_x barrier thickness shows significant influence on the bottom electrode and the pyroelectric performance of the PZT thick films. The average pyroelectric coefficient of PZT films deposited on 400 nm TiO_x layer was about 8.94 × 10⁻⁹ C/(cm² K), which was improved by 70% than those without diffusion barrier layer. The results showed in this study indicate that TiO_x barrier layer has great potential in fabrication of PZT pyroelectric device.     

Influence of UV light irradiation on film thickness distribution of tin oxide films by photochemical vapour deposition

Tin oxide (non-doped) films have been prepared by a photochemical vapour deposition (photo-CVD) from Tetramethyltin (TMT) (Sn(CH₃)₄) and O₂ (containing O₃). A low-pressure mercury lamp was used as the light source. The effect of the UV light irradiation on the film thickness distribution along 5 cm×5 cm area was examined. By piling Teflon films on the surface of the suprasil window, the light intensity of 184.9 nm UV wavelength of the low-pressure mercury lamp was controlled, while that of 253.7 nm wavelength through the Teflon hardly changed. As a result, the uniformity of the film thickness distribution was improved as the light intensity (184.9 nm) increased. The UV 184.9 nm light irradiation may have improved the uniformity of the reactive species distribution in the vapour phase, which may result in the formation of the uniform thickness distribution.     

Characteristics of silicon oxide thin films prepared by sol electrophoretic deposition method using tetraethylorthosilicate as the precursor

Silicon dioxide films were prepared on p-type Si (1 0 0) substrates by sol electrophoretic deposition (EPD) using tetraethylorthosilicate (TEOS) at low temperature. According to the variation of sol dipping conditions, we estimated the characteristics of SiO₂ films, such as composition, surface morphology, wet etch rate, breakdown voltage, etc. The growth rate of the film increased linearly with increasing TEOS quantity in solution. It increased exponentially with the increase in deposition time, and the film thickness was saturated at approximately 200 nm on hydrophilic Si surface after more than 6 days. The growth rate of the EPD SiO₂ films on the hydrophobic Si surface was much lower than that of the film on the hydrophilic Si surface.     

Influence of growth temperature and deposition duration on the structure,surface morphology and optical properties of InN/YSZ (1 0 0)

InN films with the wurtzite structure have been grown directly on YSZ (1 0 0) substrate by the RF-magnetron sputtering technique. Strongly (0 0 2) oriented films with smooth surfaces (0.7–2.9 nm surface roughness depending on substrate temperature), were grown within 30 min. Films deposited for 60 min developed three-dimensional (3D) pyramidal islands on top of their surfaces, which diminished the residual elastic strain. The optical absorption edge and PL peak energy around 1.7 eV were found to redshift with increasing film thickness and substrate temperature.     

Effect of GZO thickness and annealing temperature on the structural,electrical and optical properties of GZO/Ag/GZO sandwich films

The GZO/Ag/GZO sandwich films were deposited on glass substrates by RF magnetron sputtering of Ga-doped ZnO (GZO) and ion-beam sputtering of Ag at room temperature. The effect of GZO thickness and annealing temperature on the structural, electrical and optical properties of these sandwich films was investigated. The microstructures of the films were studied by X-ray diffraction (XRD). X-ray diffraction measurements indicate that the GZO layers in the sandwich films are polycrystalline with the ZnO hexagonal structure and have a preferred orientation with the c-axis perpendicular to the substrates. For the sandwich film with upper and under GZO thickness of 40 and 30 nm, respectively, it owns the maximum figure of merit of 5.3 × 10⁻² Ω⁻¹ with a resistivity of 5.6 × 10⁻⁵ Ω cm and an average transmittance of 90.7%. The electrical property of the sandwich films is improved by post annealing in vacuum. Comparing with the as-deposited sandwich film, the film annealed in vacuum has a remarkable 42.8% decrease in resistivity. The sandwich film annealed at the temperature of 350 °C in vacuum shows a sheet resistance of 5 Ω/sq and a transmittance of 92.7%, and the figure of merit achieved is 9.3 × 10⁻² Ω⁻¹.     

Texture and strain in CoPt/Ag nanocomposite films

The texture and microstrain in CoPt/Ag nanocomposite films is monitored as a function of film thickness. Perpendicular anisotropy due to (0 0 1) texturing is achieved by annealing films with thickness below 15 nm at 600°C. As a function of film thickness δ the texture evolves from weak (0 0 1) below 9 nm to strong (0 0 1) at δ=12 nm which deteriorates rapidly above 15 nm and evolves to (1 1 1) above 40 nm. The strain is minimized in the range of film thickness where the (0 0 1) texturing is optimum indicating a texturing mechanism related to the reduction of mechanical strain energy.     

Extraordinary fast oxide ion conductivity in La1.61GeO5−δ thin film consisting of nano-size grain

Thin films of La_1.61GeO_5−δ, a new oxide ionic conductor, were fabricated on dense polycrystalline Al₂O₃ substrates by a pulsed laser deposition (PLD) method and the effect of the film thickness on the oxide ionic conductivity was investigated on the nanoscale. The deposition parameters were optimized to obtain La_1.61GeO_5−δ thin films with stoichiometric composition. Annealing was found necessary to get crystalline La_1.61GeO_5−δ thin films. It was also found that the annealed La_1.61GeO_5−δ film exhibited extraordinarily high oxide ionic conductivity. Due to the nano-size effects, the oxide ion conductivity of La_1.61GeO_5−δ thin films increased with the decreasing thickness as compared to that in bulk La_1.61GeO_5−δ. In particular, the improvement in conductivity of the film at low temperature was significant .The electrical conductivity of the La_1.61GeO_5−δ film with a thickness of 373 nm is as high as 0.05 S cm^− 1 (log(σ/S cm^− 1) = − 1.3) at 573 K.     

Effect of film thickness on the transport properties of MgB2 synthesized by spray pyrolysis

Polycrystalline MgB₂ films of different thickness have been prepared by employing spray pyrolysis technique on MgO (1 0 0) substrate. The MgB₂ and other phases have been confirmed using X-ray diffraction technique and no trace of impurities phases have been found. The resistivity behavior shows that the superconducting transition temperature lies in the range of 37–39 K with narrow transition width. The transport critical current density vary with films thickness and achieved highest value ～1.2 × 10⁶ A/cm² at 20 K for 2.0 μm thick film and its values increase as thickness increases.