Effect of electrostatic interaction on the methylene blue and methyl orange adsorption by the pristine and functionalized carbon nanotubes

Multi-walled carbon nanotubes (MWCNTs) were functionalized with cysteamine groups by several percentage of mass as adsorbents, then kinetics adsorption capacity was investigated for methylene blue (MB) and methyl orange (MO) as anionic and cationic dyes adsorbate molecules, respectively. The effect of temperature (from 283 to 303 K), contact time and initial concentration of the MB and MO dyes in a solution (10 to 40 ppm) was considered. The optimal contact time was found to be about 60 min. Some kinetics model such as pseudo-first-order, pseudo-second-order, intra-particle diffusion and the Elovich were tested. The adsorptions of MB dye on the pristine and functionalized MWCNT surfaces were found to be the intra-particle diffusion and the pseudo-second-order kinetic model, respectively and for adsorption of MO dye by the pristine and low functionalized MWCNTs and highly functionalized tubes, found to be the pseudo-second-order and intra-particle diffusion kinetic model, respectively, based on the chi-square statistic (X²) and also high correlation coefficient (R²) values.     

Patterning of Aluminium thin film on polyethylene terephthalate by multi-beam picosecond laser

High speed patterning of a 30 nm thick Aluminium thin film on a flexible Polyethylene Terephthalate substrate was demonstrated with the aid of Computer Generated Holograms (CGH׳s) applied to a phase only Spatial Light Modulator. Low fluence picosecond laser pulses minimise thermal damage to the sensitive substrate and thus clean, single and multi-beam, front side thin film removal is achieved with good edge quality. Interestingly, rear side ablation shows significant Al film delamination. Measured front and rear side ablation thresholds were F_th=0.20±0.01 J cm⁻² and F_th=0.15±0.01 J cm⁻² respectively. With laser repetition rate of 200 kHz and 8 diffractive spots, a film removal rate of R>0.5 cm² s⁻¹ was demonstrated during patterning with a fixed CGH and 5 W average laser power. The effective laser repetition rate was f_eff~1.3 MHz. The application of 30 stored CGH׳s switching up to 10 Hz was also synchronised with motion control, allowing dynamic large area multi-beam patterning which however, slows micro-fabrication.     

Contact resistance of multi-walled carbon nanotube/natural rubber nanocomposites with metallic ball

This paper reports on the contact resistance (R_c) between carbon filler/natural rubber (NR) nanocomposite and gold ball: three varieties of nanocomposites were prepared from carbon black (CB) and two kinds of multi-walled carbon nanotubes (MWCNTs) with different diameter. R_c of MWCNT/NR nanocomposite was remarkably less than that of CB/NR nanocomposites. The relationship between R_c of MWCNT/NR nanocomposites and applied load was expressed in the formula, R_c=C·P⁻ⁿ (P: load, C and n: constant): for the MWCNTs (diameters of 13 nm)/NR and MWCNTs (diameters of 67 nm)/ NR nanocomposites, they were expressed as R_c=1724·P^−0.6 and R_c=344·P^−0.37, respectively. The former (MWCNT, ϕ13 nm) showed higher R_c than the latter (MWCNT, ϕ67 nm) over whole region of applied load. The mechanical hardness of the former was higher (90 HsA) than that of the latter (82 HsA). Therefore, the smaller contact area between the nanocomposite and gold ball of the former resulted in higher R_c. The apparent specific contact resistivity was calculated from the observed values of R_c and contact area: 130 Ω mm² and 127 Ω mm² for the former (MWCNT, ϕ13 nm) and the latter (MWCNT, ϕ67 nm), respectively.     

Microfabrication of solenoid-type RF SMD chip inductors with an Al2O3 core

We investigated micron size, high-performance, and solenoid-type radio-frequency surface-mounted device (SMD) chip inductors with a low-loss Al₂O₃ core for a GHz drive microwave circuit application. Copper coils with a diameter of 27 μm were used and the chip inductors fabricated in this study are 0.86 × 0.46 × 0.45 mm³. The high-frequency characteristics of the inductance (L), quality factor (Q), and impedance (Z) of the developed inductors were measured using a RF impedance/material analyzer (HP4291B with HP16193A test fixture). The developed inductors have a self-resonant frequency of 3.7–5.2 GHz and exhibit L of 15–34 nH. The inductors have Q of 38–49 over the frequency ranges of 900 MHz–1.7 GHz. The calculated data obtained from the equivalent circuit and the derived equation of Q described the high-frequency data of L, Q, and Z of the inductors developed quite well.     

Quick response PZT/P(VDF-TrFE) composite film pyroelectric infrared sensor with patterned polyimide thermal isolation layer

The fabrication method and the pyroelectric response of a single element infrared sensor based lead zirconate titanate (PZT) particles and polyvinylidene fluoride P(VDF-TrFE) copolymer composite thick film is reported in this paper. A special thermal insulation structure, including polyimide (PI) thermal insulation layer and thermal insulation tanks, was used in this device. The thermal insulation tanks were fabricated by laser micro-etching technique. Voltage responsivity (R_V), noise voltage (V_noise), noise equivalent power (NEP), and detectivity (D^*) of the PZT/P(VDF-TrFE) based infrared sensor are 1.2 × 10³ V/W, 1.25 × 10⁻⁶ V Hz^1/2, 1.1 × 10⁻⁹ W and 1.9 × 10⁸ cm Hz^1/2 W⁻¹ at 137.3 Hz modulation frequency, respectively. The thermal time constant of the infrared sensor τ_T was about 15 ms. The results demonstrate that the composite infrared sensor show a high detectivity at high chopper frequency, which is an essential advantage in infrared detectors and some other devices.     

SnO2-decorated multiwalled carbon nanotubes and Vulcan carbon through a sonochemical approach for supercapacitor applications

Multiwalled carbon nanotubes (MWCNTs) and Vulcan carbon (VC) decorated with SnO₂ nanoparticles were synthesized using a facile and versatile sonochemical procedure. The as-prepared nanocomposites were characterized by means of transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, and Fourier transform infra red spectroscopy. It was evidenced that SnO₂ nanoparticles were uniformly distributed on both carbon surfaces, tightly decorating the MWCNTs and VC. The electrochemical performance of the nanocomposites was evaluated by cyclic voltammetry and galvanostatic charge/discharge cycling. The as-synthesized SnO₂/MWCNTs nanocomposites show a higher capacity than the SnO₂/VC nanocomposites. Concretely, the SnO₂/MWCNTs electrodes exhibit a specific capacitance of 133.33 F g⁻¹, whereas SnO₂/VC electrodes exhibit a specific capacitance of 112.14 F g⁻¹ measured at 0.5 mA cm⁻² in 1 M Na₂SO₄.     

Ultrasonic and DFT study of intermolecular association through hydrogen bonding in aqueous solutions of d(−)-arabinose

The experimental measurements of density, viscosity and ultrasonic velocity of aqueous d-arabinose solutions were carried out as functions of concentration (0.1 ≤ m [mol kg^? 1] ≤ 1.0) and temperature (303.15 ≤ T [K] ≤ 323.15). The isentropic compressibility (β_s), acoustic impedance (Z), hydration number (H_n), intermolecular free length (L_f), classical sound absorption (α/f²)_class and shear relaxation time (τ) were calculated by using the measured data. These parameters have been interpreted in terms of solute–solvent interactions. The quantum chemical calculations were performed to study the hydrogen bonding in interacting complex formed between α-D-arabinopyranose in ¹C₄ conformation and water molecules. Computations have been done by using Density Functional Theory (DFT) method at B3LYP/6-31+g(d) level of theory to study the equilibrium structure of α-d-arabinose, α-D-arabinopyranose–water interacting complex and vibrational frequencies. The solution phase study was carried out using Onsager's reaction field model in water solvent. The computed and scaled vibrational frequencies are in good agreement with the main features of the experimental spectrum when seven water molecules are considered explicitly with α-D-arabinopyranose in ¹C₄ conformation. The interaction energy (E_total), hydrogen bond lengths and dipole moment (μ_m) of the interacting complex are also presented and discussed with in the light of solute–solvent interactions.     

Polymorphic phase transition and thermal stability in squaric acid (H2C4O4)

Phase transformations in squaric acid (H₂C₄O₄) have been investigated by thermogravimetry and differential scanning calorimetry with different heating rates β. The mass loss in TG apparently begins at onset temperatures T_di=245±5 °C (β=5 °C min^?1), 262±5 °C (β=10 °C min^?1), and 275±5 °C (β=20 °C min^?1). A polymorphic phase transition was recognized as a weak endothermic peak in DSC around 101 °C (T_c⁺). Further heating with β=10 °C min^?1 in DSC revealed deviation of the baseline around 310 °C (T_i), and a large unusual exothermic peak around 355 °C (T_p), which are interpreted as an onset and a peak temperature of thermal decomposition, respectively. The activation energy of the thermal decomposition was obtained by employing relevant models. Thermal decomposition was recognized as a carbonization process, resulting in amorphous carbon.     

Strongly enhanced flux pining of GdBCO coated conductors with BaSnO3 nanorods by pulsed laser deposition

We report the effects of BSO addition on the crystallinity, texture, and the field dependency of critical current density (J_c) of GdBCO coated conductors (CCs) prepared by pulsed laser deposition (PLD). Undoped and BSO-doped GdBCO films showed only c-axis oriented growth, and the incorporated BSO nanorods exhibited epitaxial relationship with the GdBCO matrix. In comparison with undoped film, BSO-doped GdBCO film exhibited greatly enhanced J_c and higher pinning force densities in the entire field region of 0–5 T (H//c) at 77 and 65 K. The BSO-doped GdBCO film showed the maximum pinning force densities (F_p) of 6.5 GN/m³ (77 K, H//c) and 32.5 GN/m³ (65 K, H//c), ～2.8 times higher than those of the undoped sample. Cross-sectional TEM analyses exhibited nano-structured BSO nanorods roughly aligned along the c-axis of the GdBCO film, which are believed effective flux pinning centers responsible for strongly improved critical current densities in magnetic fields.     

Synthesis of TiO2 nanoparticles and spectroscopic upconversion luminescence of Nd3+-doped TiO2–SiO2 composite glass

Nd³⁺-doped TiO₂–SiO₂ composites were prepared by sol–gel method. Optical properties such as radiative life-time (τ), stimulated emission cross-section (σ_p) and branching ratio (β) were calculated using Judd–Ofelt theory. Violet to blue upconversion emissions at 380 nm (⁴D_3/2→⁴I_11/2), 399 nm (²P_3/2→⁴I_11/2), 420 nm (²D_5/2→⁴I_9/2) and 452 nm (²P_3/2→⁴I_13/2) were obtained under 578 nm xenon-lamp excitation. The choice of 578 nm is justified by the absorption spectra of the same samples, which shows a strong absorption peak at 578 nm. This 578 nm excitation pump produces upconversion in Nd³⁺ by a sequential two-photon absorption process.     

Measurement of optical and surface properties of PLZT thin films

Lanthanum-modified lead zirconate titanate (Pb_0.93La_0.07(Zr_0.3Ti_0.7)_0.93O₃, PLZT7/30/70) thin films with and without a seeding layer of PbTiO₃ (PT) were successfully deposited on indium-doped tin oxide (ITO) coated glass substrate via spin coating in conjunction with a sol–gel process, and a top transparent conducting thin film of SnO₂ was also prepared in the same way. The thicknesses of PLZT and PT layers are 0.5 μm and 24 nm, respectively. The retardance of PLZT film was measured by a new heterodyne interferometer and enhanced by application of a seeding layer of PT. The Pockels linear electro-optical coefficient of PLZT film with a PT layer was determined to be 3.17 × 10^?9 m/V when the refractive index is considered as 2.505, which is one order larger than 1.4 × 10^?10 m/V for PLZT12/40/60 doped with Dy reported in the literature. The root-mean-square (rms) roughness of PLZT thin film with a PT layer (R_rms = 6.867 nm) was larger than that of PLZT film (R_rms = 0.799 nm). From the comparisons, the average transmittance of PLZT film with a PT seeding layer was 77.01%, which was a little smaller than that of PLZT film (around 80.75%). Experimental results imply that the PT seeding layer plays a key role in the increase of retardance value, leading to a higher Pockels coefficient.     

Thickness dependence of Ic and Jc of LTG-SmBCO coated-conductor on IBAD-MgO tapes

We have reported SmBa₂Cu₃O_y (SmBCO) films on single crystalline substrates prepared by low-temperature growth (LTG) technique. The LTG-SmBCO films showed high critical current densities in magnetic fields compared with conventional SmBCO films prepared by pulsed laser deposition (PLD) method. In this study, to enhance critical current (I_c) in magnetic field, we fabricated thick LTG-SmBCO films on metal substrates with ion-beam assisted deposition (IBAD)-MgO buffer and estimated the I_c and J_c in magnetic fields.All the SmBCO films showed c-axis orientation and cube-on-cube in-plane texture. T_c of the LTG-SmBCO films were 93.1–93.4 K. J_c and I_c of a 0.5 μm-thick SmBCO film were 3.0 MA/cm² and 150 A/cm-width at 77 K in self-field, respectively. Those of a 2.0 μm-thick film were 1.6 MA/cm² and 284 A/cm-width respectively. Although I_c increased with the film thickness increasing up to 2 μm, the I_c tended to be saturated in 300 A/cm-width. From a cross sectional TEM image of the SmBCO film, we recognized a-axis oriented grains and 45° grains and Cu–O precipitates. Because these undesired grains form dead layers, I_c saturated above a certain thickness. We achieved that I_c in magnetic fields of the LTG-SmBCO films with a thickness of 2.0 μm were 88 A/cm-width at 1 T and 28 A/cm-width at 3 T.     

Enhanced performance of bi-layer Nb2O5 coated TiO2 nanoparticles/nanowires composite photoanode in dye-sensitized solar cells

Dye sensitized solar cells (DSSCs) were fabricated based on coumarin NKX-2700 dye sensitized bi-layer photoanode and quasi-solid state electrolyte sandwiched together with cobalt sulfide coated counter electrode. A novel bi-layer photoanode has been prepared using composite mixtures of 90 wt.% TiO₂ nanoparticles + 10 wt.% TiO₂ nanowires (TNPWs) as active layer and Nb₂O₅ is coated on the active layer, which acts as scattering layer. Hafnium oxide (HfO₂) was applied over the TNPWs/Nb₂O₅ photoanode film, as a blocking layer. TiO₂ nanoparticles (TNPs), TiO₂ nanowires (TNWs) and TNPWs/Nb₂O₅ were characterized by X-ray diffractometer (XRD), scanning electron microscope (SEM) and transmission electron microscope (TEM). The sensitizing organic dye coumarin NKX-2700 displayed maximum absorption wavelength (λ_max) at 525 nm, which could be observed from the UV–vis spectrum. DSSC-1 fabricated with composite bi-layer photoanode revealed enhanced photo-current efficiency (PCE) as compared to other DSSCs and illustrated photovoltaic parameters; short-circuit current J_SC = 18 mA/cm², open circuit voltage (V_OC) = 700 mV, fill factor (FF) = 64% and PCE (η) = 8.06%. The electron transport and charge recombination behaviors of DSSCs were investigated by electrochemical impedance spectra (EIS) and the results illustrated that the DSSC-1 showed the lowest charge transport resistance (R_tr) and the longest electron lifetime (τ_eff). Therefore, in the present investigation, it could be concluded that the novel bi-layer photoanode with blocking layer increased the short circuit current, electron transport and suppressed the recombination of charge carriers at the photoanode/dye/electrolyte interface in DSSC-1.     

AZO/Ag/AZO multilayer films prepared by DC magnetron sputtering for dye-sensitized solar cell application

Ag films were deposited on Al-doped ZnO (AZO) films and coated with AZO to fabricate AZO/Ag/AZO multilayer films by DC magnetron sputtering on glass substrates without heating of glass substrates. The best multilayer films have low sheet resistance of 19.8 Ω/Sq and average transmittance values of 61% in visible region. It was found that the highest figure of merit (F_TC) is 6.9 × 10⁻⁴ Ω⁻¹. For the dye-sensitized solar cell (DSSC) application, the multilayer films were used as transparent conductive electrode (multilayer films/ZnO + Eosin-Y/LiI + I₂/Pt/FTO). The best DSSC based on the multilayer films showed that open circuit voltage (V_oc) of 0.47 V, short circuit current density (J_sc) of 2.24 mA/cm², fill factor (FF) of 0.58 and incident photon-to-current conversion efficiency (η) of 0.61%. It was shown that the AZO/Ag/AZO multilayer films have potential for application in DSSC.     

Photo-curable epoxy functionalized cyclotetrasiloxane as a gate dielectric for organic thin film transistors

We synthesized a new photo-curable organic/inorganic hybrid material, cyclotetrasiloxane (CTS) derivative containing cyclohexene-1,2-epoxide functional groups (CTS-EPOXY), and its characteristics are compared with a prototypical organic gate insulator of poly(4-vinylphenol) (PVP) in the organic thin film transistors (OTFTs) using pentacene as an active p-type organic semiconductor. Compared with PVP, CTS-EPOXY shows better insulating characteristics and surface smoothness. A metal/insulator/metal (MIM) device with the 300-nm-thick CTS-EPOXY film shows more than two orders of magnitude lower current (less than 40 nA/cm² over the voltage range up to 60 V) compared with PVP. In addition, the pentacene TFT with CTS-EPOXY as a gate dielectric layer shows slightly higher field-effect mobility of μ_FET = 0.20 cm²/V s compared to that with PVP.     

High oxide ion conductivity in Fe and Mg doped LaGaO3 as the electrolyte of solid oxide fuel cells

La(Sr)Ga(Fe,Mg)O₃ exhibited the high oxide ion conductivity and the electrical power generating property of SOFC single cell using La_0.7Sr_0.3Ga_0.7Fe_0.2Mg_0.1O_3-δ (LSGFM) electrolyte was investigated in this study. The transport number of oxide ion is almost 0.8 in LSGFM and so open circuit potential (OCV) is as low as 0.8 V. OCV was strongly affected by anode materials and the highest OCV was achieved on Ni–Fe bimetallic anode. The extremely high power density was achieved by using LSGFM for electrolyte of SOFC. The maximum power densities of the cells can be elevated by coating with oxide ion conductor film at anode side. The maximum power density increased in the following order for coating film: LSGM > SDC > YSZ. The maximum power density of 197 and 100 mW/cm² can be achieved at 873 and 773 K, respectively, when LSGM film deposited on the anode side of LSGFM. Therefore, LSGFM can be used as electrolyte of SOFC operating at intermediate temperature.     

Effect of nitrogen partial pressure on Al–Ti–N films deposited by arc ion plating

AlTiN films with different nitrogen partial pressures were deposited using arc ion plating (AIP) technique. In this study, we systematically investigated the effect of the nitrogen partial pressure on composition, deposition efficiency, microstructure, macroparticles (MPs), hardness and adhesion strength of the AlTiN films. The results showed that with increasing the nitrogen partial pressure, the deposition rate exhibited a maximum at 1.2 Pa. Results of X-ray photoelectron spectroscopy (XPS) analysis revealed that AlTiN films were comprised of Ti–N and Al–N bonds. XRD results showed that the films exhibited a (1 1 1) preferred growth, and AlTi₃N and TiAl_x phases were observed in the film deposited at 1.7 Pa. Analysis of MPs statistics showed MPs decreased with the increase in the nitrogen partial pressure. In addition, the film deposited at 1.2 Pa possessed the maximum hardness of 38 GPa and the better adhesion strength.     

Thermal diffusivity measurement of YBa2Cu3O7−x thin film with a picosecond thermoreflectance technique

The thermal diffusivity of YBa₂Cu₃O_7?x (YBCO) film was measured using the optical pump–probe method. A theoretical finite-difference model was employed to calculate the diffusivity value, and the best fit for the c-axis oriented YBCO film showed an average thermal diffusivity of 0.25 ± 0.05 mm² s^?1. The obtained result is compared to previous reports measured using various methods.     

Kinetic studies of the electrochemical nitrogen reduction and incorporation into yttria stabilized zirconia

The kinetics of the electrochemical reduction of molecular nitrogen at gold micro electrodes on yttria stabilized zirconia (YSZ) solid oxide electrolyte is studied by steady state polarization measurements. From the η / lg i plot for both cathodic and anodic polarization the apparent transfer coefficients α_a and α_c are evaluated. The sum of α_a + α_c exceeds unity and thus a multistep electron transfer process is suggested. The concept of the stoichiometric number is applied to the electrode reaction N₂ + 6e⁻ = 2N³⁻ supposing that the overall process involves at least two intermediate species. On the basis of the evaluation of the experimental results the reaction N₂⁻ + e⁻ ⇌ N₂²⁻ is suggested as the rate determining reaction step for the cathodic nitrogen reduction and nitride formation.     

Synthesis of ammonia at atmospheric pressure with Ce0.8M0.2O2−δ (M = La,Y, Gd,Sm) and their proton conduction at intermediate temperature

Ionic conduction in fluorite-type structure oxide ceramics Ce_0.8M_0.2O_2−δ (M = La, Y, Gd, Sm) at temperature 400–800 °C was systematically studied under wet hydrogen/dry nitrogen atmosphere. On the sintered complex oxides as solid electrolyte, ammonia was synthesized from nitrogen and hydrogen at atmospheric pressure in the solid states proton conducting cell reactor by electrochemical methods, which directly evidenced the protonic conduction in those oxides at intermediate temperature. The rate of evolution of ammonia in Ce_0.8M_0.2O_2−δ (M = La, Y, Gd, Sm) is up to 7.2 × 10^− 9, 7.5 × 10^− 9, 7.7 × 10^− 9, 8.2 × 10^− 9 mol s^− 1 cm^− 2, respectively.