聚苯胺/Co_(0.5)Zn_(0.5)Fe_2O_4纳米复合材料的制备及电磁性能

采用高分子凝胶法制备尖晶石型Co0.5Zn0.5Fe2O4,原位聚合法制备纯聚苯胺和聚苯胺/Co0.5Zn0.5-Fe2O4纳米复合材料.使用傅立叶红外光谱(FTIR)、紫外可见吸收光谱(UV-Vis)、X射线衍射仪(XRD)和透射电子显微镜(TEM)对复合材料进行了表征.FTIR和XRD的结果表明样品为纯聚苯胺和聚苯胺/Co0.5Zn0.5-Fe2O4.UV-Vis光谱表明聚苯胺/Co0.5Zn0.5Fe2O4苯环上的π-π*和n-π*分别红移了23nm和5nm.TEM照片可知,聚苯胺和聚苯胺/Co0.5Zn0.5Fe2O4粒子的平均粒径分别约为50nm和70nm.在8.2～12.4GHz测试频率范围内,聚苯胺/Co0.5Zn0.5Fe2O4的ε″数值在9.2～12.3之间,u″数值在0.15～0.16之间;聚苯胺/Co0.5-Zn0.5Fe2O4介电损耗低于纯聚苯胺,而磁损耗高于纯聚苯胺.     

磁性Fe_3O_4@PS@PAMAM-Ag复合催化粒子的制备及其可再生催化性能(英文)

采用聚苯乙烯(PS)包裹Fe3O4磁性纳米粒子,制得Fe3O4@PS复合微球,以此作为磁性载体,通过微球表面的羧基将聚酰胺-胺类树形大分子(PAMAM)连接到磁性载体上,然后使Ag纳米粒子镶嵌在树形分子层中,制得可再生的金属复合催化粒子Fe3O4@PS@PAMAM-Ag.并采用红外光谱、扫描电镜、电感耦合等离子体质谱(ICP-MS)和X射线光电子能谱等方法对复合催化粒子进行了表征,结果表明,树形分子可以较好地分散和稳定金属Ag纳米粒子,所制复合催化粒子表面Ag含量为1.64%,具有较高的催化还原对硝基苯酚的活性.同时,利用外加磁场可以方便快捷地从反应体系中分离出来,继续用于下一次反应中,复合催化粒子循环使用6次后,仍保持完全的催化性能.     

添加Al2O3对Ni0.5Zn0.5Fe2O4纳米纤维结构和磁性能的影响

采用静电纺丝技术制备了添加0～20wt%Al2O3的Ni0.5Zn0.5Fe2O4纳米纤维。通过XRD、FESEM、TEM和VSM对样品的物相结构、形貌和磁性能进行了表征。结果表明,所合成的复合纳米纤维的直径都分布在40～150 nm之间,添加到纤维中的Al2O3主要以非晶态形式分布于铁氧体晶粒边界;随着Al2O3添加量的增加,可观察到γ-Fe2O3相逐渐析出,Ni-Zn铁氧体的晶格常数单调减小,说明有一些Al2O3进入到尖晶石晶格中取代了B位的Fe3+离子,Ni-Zn铁氧体的平均晶粒尺寸先增大后减小,在Al2O3添加量为8wt%时达到最大值39.2 nm;比饱和磁化强度和矫顽力随Al2O3添加量的增加呈现出相同的变化规律,先减小后增大,当Al2O3添加量超过5wt%时又开始变小。     

PtSn/Al2O3/MCM-41催化剂的丙烷脱氢催化性能

用微型催化反应装置评价, 并结合X射线粉末衍射(XRD)、表面积和孔结构测试、程序升温还原(TPR)、氢化学吸附和热重分析等方法研究了负载型PtSn/γ-Al2O3, PtSn/MCM-41和PtSn/Al2O3/MCM-41催化剂的丙烷脱氢反应催化性能. 发现PtSn/Al2O3/MCM-41催化剂具有较PtSn/MCM-41催化剂高的丙烷脱氢反应活性和较PtSn/γ-Al2O3催化剂高的反应稳定性. 实验结果表明, 纯硅MCM-41载体表面的锡物种因与载体相互作用较弱故易被还原, 导致铂金属分散度和催化剂的丙烷脱氢活性较低. 用Al2O3修饰MCM-41可以增强Sn物种与Al2O3/MCM-41载体之间的相互作用, 提高PtSn/Al2O3/MCM-41催化剂铂金属分散度和丙烷脱氢催化活性. 并且, 积炭后的PtSn/Al2O3/MCM-41催化剂具有较高的铂金属表面裸露度, 故具有较高的丙烷脱氢反应稳定性. PtSn/Al2O3/MCM-41催化剂优良的丙烷脱氢催化性能可能不仅与Sn-载体Al2O3/MCM-41较强的相互作用有关, 而且与Al2O3/MCM-41载体的介孔结构有关.     

富表面氧空位Fe2O3/ZnO催化剂在光催化合成氨中的应用

光催化合成氨是一种绿色节能的合成氨技术,设计制造丰富的表面氧空位和异质结构是促进氮分子活化和抑制电子-空穴复合的重要方法。我们以乙二醇作为还原剂,采用溶剂热法制备合成了Fe2O3/ZnO光催化剂,利用X射线衍射(XRD)、透射电镜(TEM)、电子顺磁共振(EPR)、紫外-可见漫反射(UV-Vis DRS)、荧光光谱(PL)及光电流(PC)对Fe2O3/ZnO催化剂进行表征,并考察了Fe2O3/ZnO催化剂在常温、常压下的光催化合成氨的性能。4%Fe2O3/ZnO催化剂在无牺牲剂下用于光催化合成氨,有较好的光催化效率和稳定性,其合成氨效率达到2059μmol·L-1·g-1·h-1。其高催化效率归因于:可见光区域吸收的提高、氮分子在表面氧空位与Fe3+活性中心上的协同活化及光生电子与空穴的高分离效率。     

Effect of Al2O3 Binder on the Precipitated Iron-Based Catalysts for Fischer-Tropsch Synthesis

A series of iron-based Fischer-Tropsch synthesis (FTS) catalysts incorporated with Al2O3 binder were prepared by the combination of co-precipitation and spray drying technology. The catalyst samples were characterized by using N2 physical adsorption, temperature-programmed reduc-tion/desorption (TPR/TPD) and Mossbauer effect spectroscopy (MES) methods. The characterization results indicated that the BET surface area increases with increasing Al2O3 content and passes through a maximum at the Al2O3/Fe ratio of 10/100 (weight basis). After the point, it decreases with further increase in Al2O3 content. The incorporation of AI2O3 binder was found to weaken the surface basicity and suppress the reduction and carburization of iron-based catalysts probably due to the strong K-Al2O3 and Fe-Al2O3 interactions. Furthermore, the H2 adsorption ability of the catalysts is enhanced with increasing Al2O3 content. The FTS performances of the catalysts were tested in a slurry-phase continuously stirred tank reactor (CSTR) under the reaction conditions of 260℃, 1.5 MPa, 1000 h-1 and molar ratio of H2/CO 0.67 for 200 h. The results showed that the addition of small amounts of Al2O3 affects the activity of iron-based catalysts to a little extent. However, with further increase of Al2O3 content, the FTS activity and water gas shift reaction (WGS) activity are decreased severely. The addition of appropriate Al2O3 do not affect the product selectivity, but the catalysts incorporated with large amounts of Al2O3 have higher selectivity for light hydrocarbons and lower selectivity for heavy hydrocarbons.     

Fe_3O_4/CdTe/聚氨酯纳米复合物的制备及其性能研究

由共沉淀法和Stober法制备了伯胺基功能化SiO2稳定的Fe3O4磁性纳米粒子Fe3O4@SiO2-NH2;Fe3O4@SiO2-NH2与二异氰酸酯及咪唑阳离子二醇、聚乙二醇的反应使其表面形成阳离子型聚氨酯稳定层;通过阳离子型聚氨酯与CdTe量子点表面修饰的巯基乙酸间的电荷相互作用,制备得到了Fe3O4/CdTe/聚氨酯纳米复合物.用X射线衍射(XRD)、红外吸收光谱(FTIR)、热重分析(TGA)、透射电子显微镜(TEM)、磁强计(VSM)、紫外吸收光谱(UV)、荧光发射光谱(PL)表征了该纳米复合物的结构与性能.结果表明,CdTe量子点均匀地分散在Fe3O4@SiO2磁性纳米粒子周围,所得纳米复合物在溶剂中分散均匀,不团聚,且具有超顺磁性,并保持了CdTe量子点的荧光性能.     

Fe-Mn/Al2O3催化剂低温 NH3选择性催化还原 NO的性能

本文制备了一系列 Fe-Mn/Al2O3催化剂,并在固定床上考察了其 NH3低温选择性催化还原 NO的性能.首先考察了不同 Fe负载量制备的催化剂的脱硝性能,优选出最佳的 Fe负载量;在此基础上,研究了 Mn负载量对催化剂脱硝效率的影响;最后,对优选催化剂的抗 H2O和抗 SO2性能进行了实验研究;同时,对催化剂由于 SO2所造成的失活机制进行了考察.采用 N2吸附-脱附、X射线衍射、透射电镜、能量弥散 X射线谱、程序升温还原、程序升温脱附、X射线光电子能谱、热重和傅里叶变换红外光谱等方法对催化剂进行了表征.结果表明,最佳的 Fe和 Mn负载量均为8%,所制的8Fe-8Mn/Al2O3催化剂在150°C的脱硝效率可达近99%;同时,在整个低温测试区间(90–210°C)的脱硝效率均超过了92.6%. Fe在催化剂表面主要以 Fe3+形态存在,而 Mn主要包括 Mn4+和 Mn3+; Mn的添加提高了 Fe在催化剂表面的积累,促进了催化剂比表面积增大和活性物种分散,改善了催化剂氧化还原性能和对 NH3的吸附能力.催化剂的高活性主要是由于其具有较大的比表面积、高度分散的活性物种、增加的还原特性和表面酸性、较低的结合能、较高的 Mn4+/Mn3+和增强的表面吸附氧.此外,8Fe-8Mn/Al2O3的催化性能受 H2O和 SO2影响较小,抗 H2O和 SO2能力较强.同时,反应温度对催化剂的抗硫性有重要影响,在较低的反应温度下,催化剂抗硫性更好; SO2造成催化剂活性降低主要是由于催化剂表面硫酸盐物种的生成.一方面,表面硫酸铵盐的生成造成催化剂孔道堵塞和比表面积降低,减少了反应中的气固接触从而导致活性降低;另一方面,催化剂表面的活性物种被硫酸化,造成反应中的有效活性位减少,从而降低了催化剂活性.     

Fe3O4/Polypyrrole/Au nanocomposites with core/shell/shell structure: synthesis, characterization, and their electrochemical properties

Uniform Fe3O4 nanospheres with a diameter of 100 nm were rapidly prepared using a microwave solvothermal method. Then Fe304/polypyrrole (PPy) composite nanospheres with well-defined core/shell structures were obtained through chemical oxidative polymerization of pyrrole in the presence of Fe3O4; the average thickness of the coating shell was about 25 nm. Furthermore, by means of electrostatic interactions, plentiful gold nanoparticles with a diameter of 15 nm were assembled on the surface of Fe3O4/PPy to get Fe3O4/PPy/Au core/shell/shell structure. The morphology, structure, and composition of the products were characterized by transmission electronic microscopy (TEM), scanning electronic microscopy (SEM), X-ray powder diffraction (XRD), and Fourier transform infrared (FT-IR) spectroscopy. The resultant nanocomposites not only have the magnetism of Fe3O4 nanoparticles that make the nanocomposites easily controlled by an external magnetic field but also have the good conductivity and excellent electrochemical and catalytic properties of PPy and Au nanoparticles. Furthermore, the nanocomposites showed excellent electrocatalytic activities to biospecies such as ascorbic acid (AA).     

Application of Fe2O3/Al2O3 Composite Particles as Oxygen Carrier of Chemical Looping Combustion

Chemical looping combustion (CLC) of carbonaceous compounds has been proposed, in the past decade, as an efficient method for CO2 capture without cost of extra energy penalties. The technique involves the use of a metal oxide as an oxygen carrier that transfers oxygen from combustion air to fuels. The combustion is carried out in a two-step process: in the fuel reactor, the fuel is oxidized by a metal oxide, and in the air reactor, the reduced metal is oxidized back to the original phase. The use of iron oxide as an oxygen carrier has been investigated in this article. Particles composed of 80 wt% Fe2O3, together with Al2O3 as binder, have been prepared by impregnation methods. X-ray diffraction (XRD) analysis reveals that Fe2O3 does not interact with the Al2O3 binder after multi-cycles. The reactivity of the oxygen carrier particles has been studied in twenty-cycle reduction-oxidation tests in a thermal gravimetrical analysis (TGA) reactor. The components in the outlet gas have been analyzed. It has been observed that about 85% of CH4 converted to CO2 and H2O during most of the reduction periods. The oxygen carrier has kept quite a high reactivity in the twenty-cycle reactions. In the first twenty reaction cycles, the reaction rates became slightly higher with the number of cyclic reactions increasing, which was confirmed by the scanning electron microscopy (SEM) test results. The SEM analysis revealed that the pore size inside the particle had been enlarged by the thermal stress during the reaction, which was favorable for diffusion of the gaseous reactants into the particles. The experimental results suggested that the Fe2O3/Al2O3 oxygen carrier was a promising candidate for a CLC system.     

Synthesis and characterization of magnetic and luminescent Fe_3O_4/CdTe nanocomposites using aspartic acid as linker

In this study,the preparation of a new kind of magnetic and luminescent Fe₃O₄/CdTe nanocomposites was demonstrated. Superparamagnetic Fe₃O₄ nanoparticles were first synthesized by hydrothermal coprecipitation of ferric and ferrous ions,followed by the modification of their surfaces with tetramethylammonium hydroxide（TMAOH） and the chemical activation with aspartic acid.The surface-modified Fe₃O₄ nanoparticles were then covalently coated with CdTe quantum dots（QDs）,which were modified with mercaptoacetic acid（MPA）,to form the Fe₃O₄/CdTe magnetic and luminescent nanocomposites through the coordination of the amino groups on the surfaces of Fe₃O₄ and the carboxyl groups on CdTe QDs.The structure and properties of as-synthesized nanocomposites were characterized.It was indicated that the nanocomposites possessed structure with an average diameter of 40- 50 nm,yellow-green emission feature and room temperature ferro-magnetism.Both the fluorescence and UV-vis absorption spectra of the nanocomposites showed a blue shift comparing with those of CdTe QDs.The mechanism of the blue shift was presented.The nanocomposites retained the ferromagnetic property with a saturation magnetization of 8.9 emu/g.     

聚(苯胺-吡咯)共聚物/Fe3O4网状纳米纤维复合物的制备及吸波性能

在十六烷基三甲基溴化胺（CTAB）存在下,将苯胺（An）与吡咯（Py）两种单体在Fe3O4磁流体中原位化学氧化共聚制备了PAn-co-PPy/Fe3O4网状纳米纤维复合材料。通过改变CTAB的浓度、An/Py单体的配比及Fe3O4磁流体的用量获得了形态和电磁性能可调控的纳米纤维复合物。采用SEM、TEM、XRD、TG、电导和磁性能测试对复合物进行了表征,通过矢量网络分析仪获得了试样在2-18 GHz范围的复介电常数和复磁导率,经计算获取相应的微波反射损耗曲线。结果表明共聚复合物具有比单一的聚合物、共聚物、PAn/Fe3O4及PPy/Fe3O4更优越的微波吸收性能,样品（含Fe3O412.4 wt%）在9.0 GHz处具有最大的反射损耗为 -36.5 dB,损耗超过 -10 dB的频带宽度达4.7 GHz。     

渣油加氢处理过程中Mo-V/Al_2O_3的催化性能及协同效应

采用孔饱和浸渍法制备了不同Mo/(Mo+V)原子比的Mo-V/Al2O3催化剂,运用拉曼光谱、H2程序升温还原和高分辨透射电镜对催化剂进行了表征,同时以萘为模型化合物,考察了催化剂的加氢活性;以科威特常渣为原料,考察了其加氢脱金属和脱硫活性.结果表明,在上述反应中,Mo与V具有协同作用.由于渣油中金属和硫的存在形态不同,并且V-Mo-S相和V-S相对于渣油加氢脱金属反应的催化作用要大于渣油加氢脱硫反应,因此与Ni-Mo/Al2O3催化剂相比,Mo-V/Al2O3催化剂的脱金属活性较高,而脱硫活性较低.     

NF3 decomposition over some metal oxides in the absence of water

NF3 decomposition in the absence of water over Al2O3, Fe2O3, Co3O4 and NiO, and transition metal oxides (Fe2O3, Co3O4 and NiO) coated Al2O3 reagents was investigated. The results show that Al2O3 is an active reagent for NF3 decomposition with 100% conversion lasting for 8.5 h at 400 ℃. Fe2O3, Co3O4 and NiO coated Al2O3 reagents are superior to bare Al2O3, and 5%Co3O4/Al2O3 has a high reactivity with NF3 full conversion maintaining for 10.5 h. It is suggested that the presence of transition metal oxide is beneficial to the reactivity of Al2O3, and results in a significant enhancement in the fluorination of Al2O3.     

CuO/ZnO/Y2O3/γ-Al2O3双功能催化剂上二甲醚水蒸气重整制氢

将沉积-沉淀法制备的CuO/ZnO/Y2O3催化剂同γ-Al2O3进行机械混合, 制备了CuO/ZnO/Y2O3/γ-Al2O3双功能催化剂, 用于二甲醚水蒸气重整制氢反应, 实验结果表明其活性、稳定性等均优于常用的CuO/ZnO/Al2O3/γ-Al2O3催化剂. 结合N2吸附-脱附(BET)、N2O化学吸附(N2O chemisorption)、NH3程序升温脱附(NH3-TPD)、X射线衍射(XRD)、H2程序升温还原(H2-TPR)等表征手段研究了两种催化剂在表面酸性及微观结构上的差异, 发现CuO/ZnO/Y2O3催化剂具有相对较高的铜分散度, 铜晶粒更加细小化, 并且具有高温稳定性的Y2O3可能起到隔离铜的作用, 在一定程度上防止了铜晶粒的团聚, 从而改善了重整组分的性能, 提高了双功能催化剂的重整制氢活性及稳定性.     

Fe3O4 nanoparticle-integrated graphene sheets for high-performance half and full lithium ion cells

We synthesized Fe(3)O(4) nanoparticle/reduced graphene oxide (RGO-Fe(3)O(4)) nanocomposites and evaluated their performance as anodes in both half and full coin cells. The nanocomposites were synthesized through a chemical co-precipitation of Fe(2+) and Fe(3+) in the presence of graphene oxides within an alkaline solution and a subsequent high-temperature reduction reaction in argon (Ar) environment. The morphology and microstructures of the fabricated RGO-Fe(3)O(4) nanocomposites were characterized using various techniques. The results indicated that the Fe(3)O(4) nanoparticles had relatively homogeneous dispersions on the RGO sheet surfaces. These as-synthesized RGO-Fe(3)O(4) nanocomposites were used as anodes for both half and full lithium-ion cells. Electrochemical measurement results exhibit a high reversible capacity which is about two and a half times higher than that of graphite-based anodes at a 0.05C rate, and an enhanced reversible capacity of about 200 mAh g(-1) even at a high charge/discharge rate of 10C (9260 mA g(-1)) in half cells. Most important of all, these fabricated novel nanostructures also show exceptional capacity retention with the assembled RGO-Fe(3)O(4)/LiNi(1/3)Mn(1/3)Co(1/3)O(2) full cell at different C rates. This outstanding electrochemical behavior can be attributed to the unique microstructure, morphology, texture, surface properties of the nanocomposites, and combinative effects from the different chemical composition in the nanocomposites.     

焙烧温度对低温水煤气变换Au/Fe2O3催化剂性能的影响

采用改性沉积-沉淀法制备了系列低温水煤气变换Au/Fe2O3催化剂, 发现经300 ℃焙烧的样品具有较好的催化活性和稳定性. 并运用N2物理吸附、原位X 射线粉末衍射(in situ XRD)、程序升温还原(H2-TPR)和X射线光电子能谱(XPS)等技术, 探讨焙烧温度对催化剂性能的影响机制, 同时对样品的失活原因进行了分析. 结果表明, 催化剂性能与焙烧温度引起的金和载体氧化铁的相互作用以及载体还原性质的变化密切相关. XPS表征结果说明, 尽管反应后在催化剂表面有碳酸盐或类碳酸盐物种生成, 但半定量分析表明这些物种的形成不是催化剂失活的主要原因;根据在低温水煤气变换反应过程中Au/Fe2O3催化剂的比表面积明显下降, 载体的结晶度也明显提高, 推断Au/Fe2O3催化剂载体的结构性质的变化才是其失活的主要原因.     

负载型La0.8Sr0.2MnO3燃烧催化剂的载体效应

Combustion catalysts La0.8Sr0.2MnO3 supported on γ-Al2O3, α-Al2O3, cordierite (2MgO•2Al2O3•5SiO2) and ZrO2 were compared. Further investigation was focused on LSM/ γ-Al2O3 catalyst. It was observed that LSM/γ－Al2O3 catalyst loaded with 20% (mass fraction) LSM (La0.8Sr0.2MnO3 or corresponding oxides), heated at 750℃ or above, perovskite-type oxides were found by XRD examination, whereas, the same catalyst loaded with 10% or less LSM, perovskite oxides were absent, calcination temperature about 750℃ is necessary for the formation of perovskite structure in LSM/γ-Al2O3 catalysts. High activity of complete oxidation of xylen will be obtained when perovskite-type oxides.
Investigation of TPR showed that neat LSM or LSM/γ-Al2O3(20%) was reduced by H2-N2 mixed gas. Two degradation processes took place. In the first, reduced temperature peak was about 350 - 450℃. If reduction ended at 400℃, perovskite structure was retained, which may be due to the reduction of Mn3+to Mn2+ on the surface of LSM only. In the second process, perovskite structure was destroied, and La2O3, Mn2O3, Mn - Sr - O oxides could be obtained, which took place in the temperature range 685 - 750℃ and ended at 800℃. This was proved by TPR experiments (Fig. 3, 5) and XRD patterns (Fig. 4)
Catalysts LSM/γ-Al2O3(10% or 20%) heated at 500℃ have only one TPR peak, i. e. lower temperature peak. This is due to the absence of perovskite-type oxides in the catalysts. However, neat LSM or LSM/γ-Al2O3(20%) heated 750℃ or above, not only the first low temperature TPR peak but also the second peak, which is contributed by the perovskite-type oxides in these catalysts appeared. Therefore, the second TPR peak, i. e. the higher temperatue peak is a characteristic peak for perovskite-type oxides in the reduced process. When LSM/ γ-Al2O3 (10%) catalys is heated at 750℃, no perovskite-type oxides were detected by XRD, and the second reduction peak was absent also in TPR process. \
The order of the second reduction peak temperature(characteristic peak of perovskite - type ox- ides) is: neat LSM(750℃）> LSM/γ-Al2O3 20% (685-698℃) -deposited LSM/γ-Al2O3 (698℃) > LSM/γ-Al2O3 15% (677 - 680℃) >(LSM/γ-AL2O3 10% 620 - 630℃, for Mn - Al - O medium oxides on surface). It is correleted with the increasing of the effect of support sequentially.
When LSM/γ-Al2O3 catalysts were heated at 900℃, more stable phase, spinel MnAl2O4 appeared, which could be proved by TPR of model catalyst MnAl2O4/γ-Al2O3.     

铌改性的Pd/Al2O3催化剂催化苯燃烧反应简

采用浸渍法制备了Nb改性的Pd/Al2O3催化剂,考察了该催化剂催化苯燃烧反应性能,并研究了催化剂的稳定性. 结果表明,Nb的添加明显提高了Pd/Al2O3催化剂性能,在195 ℃时苯转化率达到90%,苯的完全燃烧温度降低了40 ℃. 采用X射线衍射(XRD)、X射线光电子能谱(XPS)、透射电子显微镜(TEM)、H2 程序升温还原(H2-TPR)、NH3程序升温脱附(NH3-TPD)和氮气吸附等手段对催化剂进行了表征,结果表明,Nb的加入不仅提高了Pd物种的分散度,同时改变了部分Pd的价态,形成适宜反应的PdO-Pd物种,并促进了催化剂表面氧浓度的增加,使氧物种氧化能力增强,从而提高了催化性能. 1%Pd-5%Nb/Al2O3催化剂的催化活性高于2.0%Pd/Al2O3催化剂.     

中空Fe203/G-NS纳米复合材料的制备和储锂性能

以三氯化铁和氧化石墨烯(Graphite oxide,GO)为原料,采用水热法一步合成了中空Fe2O3/石墨烯(Graphene nanoslheet,GNS)纳米复合材料.研究结果表明,Fe2O3/GNS纳米复合材料的形成是由于Fe3+催化氧化GO中的羧基等官能团释放出CO2,并以原位形成的CO2气泡为模板形成了中空...