Forming and Gathering of SnO2 Nanoparticles on External Surface of High Silica TON, MFI and FAU Type Zeolites

Tin dioxide （SnO2） nano-particles were prepared on high silica TON, MFI and FAU type zeolites by impregnation of SnC12 solution and subsequent calcination at 873 K. XRD and SAED were used to characterize the crystalline phase, and TEM was used to characterize the morphology, the particle size and the agglomerative state of the formed nano-materials. The nano-particles, which possess 8 nm, 10-80 nm and 6 nm in size, were found to form on the outer surface of TON, MFI and FAU zeolites, respectively. SnO2 microcapsules and SnOz netlike nanostructure were obtained by decomposition of SnO2-TON and SnO2-MFI in 40% hydrofluoric acid at room temperature. Compared with the nano-particles formed on NaY zeolite, the special morphology and the agglomerative state of SnO2 nanostructures on TON and MFI type zeolites with one and two dimension channel system indicate that the heterogeneous framework, surface structure and property perform important function for forming and growing SnO2 nanostructure on the outer surface of the zeolites.     

干法合成纯硅丝光沸石

在Ｎａ２Ｏ－ＳｉＯ２－ＥＡ体系中利用干法首次成功地合成了纯硅丝光沸石，采用ＸＲＤ，ＳＥＭ及ＩＲ等仪器分析方法对产物的结构，形貌，红外有架振动及稳定性等进行了表征。实验结果表明，干法合成的纯硅丝光沸石具有良好的耐酸性；与水热体系合成的丝光沸石相比，干法得到的丝光沸石的晶胞体积出现较明显的收缩趋势。     

FeZSM—5催化剂上乙苯脱氢反应机理研究—瞬态应答法

采用快速动态法制备了具有MFI结构的硅铁沸石分子筛,研究了该分子筛上乙苯脱氢反应的瞬变行为.结合表面吸附态的红外、顺磁结果发现,苯乙烯通过化学活性吸附的乙苯脱氢形成.通过这个模型可满意地解释瞬态曲线和稳态下的动力学行为.     

在（TPA）2O—Na2O—SiO2—H2O系统中MFI型硅沸石的结晶行为（I）：结…

以四丙基溴化铵作模板剂，以白炭黑（Ｉ）、硅溶胶（Ⅱ）和水玻璃（Ⅲ）为不同硅源在１４０￣１８０℃合成ＭＦＩ型硅沸石。反应物配比相同，其结晶动力学曲线有明显差异。从它们的成核诱导期及生长速度计算出各体系硅沸石晶核形成活化能与生长活化能，在体系（Ｉ）中为４６／７６ｋＪ／ｍｏｌ，体系（Ⅱ）中为４１／４３ｋＪ／ｍｏｌ，体系（Ⅲ）中为３８／７９ｋＪ／ｍｏｌ。产物结晶粒径的大小由各体系成核活化能与生长活化能的差     

β沸石合成与表征的研究进展

β沸石由Mobil公司的Wadlinger等［‘j于1967年首次合成,由于长期未能解决其结构测定问题,加之ZSM系列沸石的合成和成功应用,因此未能引起人们的足够重视,直至1988年揭示了其特有的三维结构特征,尸沸石重又引起人们的兴趣．它具有良好的热和水热稳定性、适度的酸性D‘和酸稳定性及疏水性,且是唯一具有交叉十二元环通道体系的高硅沸石,其催化应用表现出烃类反应不易结焦和使用寿命长的特点,在烃类裂解、异构化、烷烃芳构化、烷基化以及烷基转移反应等方面,表现出优异的催化性能,是十分重要的催化材料．1尸沸石表征1．1卢沸石的…     

高硅无铝Mo-Beta沸石的合成与结构表征

用水热晶化法合成了无铝Mo-Beta沸石,讨论了合成条件对无铝Mo-Beta沸石晶化的影响,通过化学分析、XRD、IR、DTA/TGA、TEM、NMR、ICP和UV-Vis紫外漫反射光谱测定了样品的n(SiO₂)/n(MoO₃)比,并对其结构进行了表征,结果表明,所合成的Mo-Beta沸石晶粒均匀,Mo存在于沸石骨架中,由于Mo的掺入,引起Beta沸石红外光谱、差热分析曲线及晶胞参数, ²⁹SiMASNMR谱等发生变化。     

HL/HW复合沸石对烃类催化裂化催化剂性能的影响

将不同HW沸石含量(以W及L沸石的XRD特定峰强度Iw/IL值表示HW沸石在HL/HW复合沸石中的含量)的HL/HW复合沸石与REUSY沸石按相同比例复配后作为烃类催化裂化催化剂的活性组分,采用标准轻油微反方法对催化剂进行了活性评价(MAT),考察了不同HW含量的HL/HW复合沸石对催化剂活性、反应产物分布、汽油产品辛烷值及催化剂上积炭的影响.结果表明,当,Iw/IL值在0～0.12变化时,MAT指数和汽油收率逐渐上升,比积炭逐渐减少,气体收率先减后增;当Iw/IL值大于0.12时,MAT指数、气体收率和汽油收率均下降,比积炭总体呈增加趋势;当Iw/IL值为0.12时,评价的综合指标达到最佳,与不加HL及HW沸石的参比样品相比,汽油产品的芳烃含量和辛烷值分别提高了9.85%和3.01%,烯烃含量下降了1.30%.     

新型催化材料丝光沸石金属铬覆盖物

新型催化材料的研制一直是催化界努力探索的课题。1990年Davis等利用改进的水热法制备了Y型沸石Cu的覆盖物(Y/Cu),并预言这一新型材料有可能在催化、电化学和光化学等领域发挥重要的作用,但到目前为止,有关其应用方面的研究未见报道。 以往制备金属-沸石分子筛材料大多是采用离子交换法、浸渍法等。固-液、汽-液同晶置换法则将金属原子直接引入沸石阴离子骨架,形成杂原子分子筛。沸石金属覆盖     

六硅Y沸石的研制及性能

ＬｉＮａＹ沸石经ＳｉＣｌ４气相同晶脱铝补硅后制得系列高硅铝比,高结晶度的Ｙ沸石,用低温氮吸附法,救是样品对Ｎ２的吸附－－脱附等温线,从而计算其比表面和孔体积,并采用ＢＪＨ模型计算孔径分布。用真空重量法测定了四种Ｃ６化合物（正己烷,２,３－二甲基丁烷、苯、环己烷）的吸附等温线,探讨吸附量与吸附物的性能（极性、几何构型）,吸附量一吸附剂脱铝深度的关系,从而得到,经ＳｉＣｌ４同晶取代后Ｙ沸石的孔结构和表     

我国一些天然沸石矿样的物化性能

本文用XRD、IR、DTA及ESR等方法研究了我国7种天然沸石矿样的结构、品位、酸性及其杂质组份与色泽的关系。这些矿样大都是丝光沸石与斜发沸石相伴而生。但其相对含量不一。此外,还有一种纯度很高的高岭土矿。它在常温下具有化学吸附空气中氧分子的能力。