Lithium insertion to ReO3-type metastable phase in the Nb2O5–WO3 system

Lithium insertion to distorted ReO₃-type metastable solid solution Nb_xW_1−xO_3−x/2 (0≤x<0.25) has been studied by chemical and electrochemical methods. In the course of lithium insertion into tetragonal compounds, transition to a cubic phase was found to occur in the region where values of y (in Li_yNb_xW_1−xO_3−x/2) fall between 0.2 and 0.3, and the phase transition was found to depend on the conditions of the reaction. Changes in OCV and lattice parameters in tetragonal region (y<0.2) were discussed from the viewpoint of the ordering of lithium ions. Also, the component diffusion coefficient of lithium in tetragonal compounds Li_0.1Nb_xW_1−xO_3−x/2 (0≤x≤0.23) was found to increase with niobium content when x≤0.10, and to saturate at 4×10⁻⁹ cm²/s.     

Oxygen permeability of La2Cu(Co)O4+δ solid solutions

Formation of the La₂Cu_1−xCo_xO_4+δ solid solutions with orthorhombic K₂NiF₄-type structure was found to be in the range of 0≤x≤0.30 at temperatures above 1270 K. Incorporating cobalt into the copper sublattice of lanthanum cuprate leads to increasing oxygen hyperstoichiometry and decreasing electrical conductivity. Thermal expansion coefficients of the La₂Cu_1−xCo_xO_4+δ (x=0.02–0.30) ceramics at 470–1100 K were calculated from the dilatometric data to vary in the range (12.2–13.2)×10⁻⁶ K⁻¹. Studying the dependence of oxygen permeation fluxes through La₂Cu(Co)O_4+δ on the membrane thickness demonstrated that the oxygen transport at the thickness values below 1 mm is limited by both surface exchange rate and bulk ionic conductivity. Oxygen permeability of the La₂Cu_1−xCo_xO_4+δ solid solutions was ascertained to increase with cobalt concentration at x=0.02–0.10 and to decrease with further dopant additions, indicating a participation of interstitial oxygen in the ionic transport.     

Mixed electronic and ionic conductivity of LaCo(M)O3 (M=Ga, Cr, Fe or Ni).: V. Oxygen permeability of Mg-doped La(Ga, Co)O3−δ perovskites

The LaGa_1−x−yCo_xMg_yO_3−δ solid solutions with rhombohedrally-distorted perovskite structure were ascertained to form in the concentration range of 0≤y≤0.10 at x=0.60 and 0≤y≤0.20 at x=0.35–0.40. Increasing cobalt content results in increasing electrical conductivity and thermal expansion of the perovskites. Thermal expansion coefficients of the LaGa_1−x−yCo_xMg_yO_3−δ ceramics were calculated from the dilatometric data to vary in the range of 12.4–19.8×10⁻⁶ K⁻¹ at 300–1100 K. Doping La(Ga,Co)O_3−δ solid solutions with magnesium leads to increasing oxygen nonstoichiometry, electronic and oxygen ionic conductivity. Oxygen permeation fluxes through LaGa_1−x−yCo_xMg_yO_3−δ membranes were found to be limited by the bulk ionic conduction and to increase with magnesium concentration, being essentially independent of cobalt content.     

Preparation, characterization and oxide ion conductivity in U-substituted Bi4V2O11

A Bi₂V_{1 − x − y}U_xBi_yO_{5.5 + 0.5x − y} solid solution derived from Bi₄V₂O₁₁ has been prepared and characterized with x up to 0.125 for y = 0. Partial substitution of U⁶⁺ for V⁵⁺ in Bi₄V₂O₁₁ leads to the stabilization at room temperature of the high-oxide ion conducting γ-phase, in contrast with other M⁶⁺ dopants which stabilize the β-phase. The lower conductivity in U substituted system compared with BICUVOX.10 is attributed to its higher activation energy. Conductivity values and activation energies of the U substituted phases compare well with Bi₂UO₆.     

Lithium scandium phosphate-based electrolytes for solid state lithium rechargeable microbatteries

Li₃Sc₂(PO₄)₃ is a promising candidate for use as an electrolyte in solid state lithium rechargeable microbatteries due to its stability in air, ease of preparation, and resistance to dielectric breakdown. The room temperature ionic conductivity was optimized resulting in an increase of over two orders of magnitude to 3×10⁻⁶S/cm. The formation of Li₃(Sc_2−xM_x)(PO₄)₃, where M=Al³⁺ or Y³⁺, resulted in the decrease of porosity, greater sinterability, and considerable enhancement of the ionic conductivity. Yttrium substitutions enhanced the conductivity slightly while aluminum increased the room temperature ionic conductivity to 1.5×10⁻⁵S/cm for x=0.4. Preliminary electron beam evaporation of Li₃Sc₂(PO₄)₃ yielded amorphous thin films with ion ic conductivity as high as 5×10⁻⁵S/cm and a composition of Li_4.8Sc_1.4(PO₄)₃.     

Ionic conduction properties of layer-type oxides NaxMx/2Ti1−x/2O2 (M=Ni, Co; 0.60≤x≤1.0)

Layer-type oxide Na_xM_x/2^IITi_1−x/2^IVO₂ (M=Co, Ni; 0.60≤x≤1.0) has been prepared by solid state reactions. In both series, two structural variants of type -NaFeO₂ (O3) and β-RbScO₂ (P2) have been obtained consecutively as x decreases with a borderline composition around x_c0.7. With the decrease of x, the ionic conductivity has been found to increase up to 8.4×10⁻² S cm⁻¹ at 770 K (Na_0.67Co_0.33Ti_0.67O₂). Compositions of P2 have been found to exhibit the conductivity values two to five times greater than those of O3, primarily due to the larger rectangular threshold available for the diffusion of Na⁺ ions. Such a structural effect has also been considered to depend on the polarizability of alkali ion. HT-XRD and ²³Na-NMR data of Na_0.67Co_0.33Ti_0.67O₂ strongly suggest that the diffusion of Na⁺ ion is deeply related with the local distortion of trigonal prismatic sites, leading to the change of activation energy around 430 K.     

Phonon Raman scattering in Nd1+xBa2−xCu3O7−δ and Pr1+xBa2−xCu3O7−δ single crystals

The polarized Raman spectra of Nd_1+xBa_2−xCu₃O_7−δ (−0.023≤x≤0.107) and Pr_1+xBa_2−xCu₃O_7−δ (0.01≤x≤0.15) single crystals have been investigated. It was found that the Cu(2) A_g mode softens by 6 cm⁻¹ in Nd 1:2:3 and 4 cm⁻¹ in Pr 1:2:3 as x increases. These frequency shifts cannot be explained by the change in the relevant bond lengths due to Nd(Pr)-substitution for Ba. The variations with x of the two low frequency modes may be affected by change of their hybridization and/or change of their force constants. The linewidths of Ba mode in Pr 1:2:3 are broader than those in Y 1:2:3. This result suggests that the Pr substitution on Ba sites occurred even in a very small value of x. In x(yy) geometry the relative intensity of the Ba and O(4) modes in Nd 1:2:3 is greater than those in Pr 1:2:3. The difference between Nd 1:2:3 and Pr 1:2:3 in the relative intensity of the Ba and O(4) modes may be produced by the chains.     

Nax/2Bi1−x/2MoxV1−xO4 and Bi1−x/3MoxV1−xO4 New Scheelite-related phases

New Scheelite-related solid solutions of the compositions Na_x/2Bi_1−x/2Mo_xV_1−xO₄ (0≤x≤1) and Bi_1−x/3 Mo_xV_1−xO₄(0≤x≤0.2) have been synthesised by the substitution of Na and Mo at the A and B sites respectively of the ABO₄ type ferroelastic BiVO₄. The phases were characterised using chemical analysis, powder X-ray diffraction, scanning electron microscopy, EDAX, and Raman spectroscopy. While almost a continuous solid solution is obtained for the series Na_x/2Bi_1−x/2Mo_xV_1−xO₄, the absence of Na at the A-site results only in a narrow stability region for the other series, Bi_1−x/3 Mo_xV_1−xO₄ where 0≤x≤0.2. Raman spectra of selected samples at room temperature also suggest that vanadium and molybdenum atoms are disordered at the tetrahedral sites.     

Perovskite-like system (Sr,La)(Fe,Ga)O3−δ: structure and ionic transport under oxidizing conditions

The maximum solid solubility of gallium in the perovskite-type La_1−xSr_xFe_1−yGa_yO_3−δ (x=0.40–0.80; y=0–0.60) was found to vary in the approximate range y=0.25–0.45, decreasing when x increases. Crystal lattice of the perovskite phases, formed in atmospheric air, was studied by X-ray diffraction (XRD) and neutron diffraction and identified as cubic. Doping with Ga results in increasing unit cell volume, while the thermal expansion and total conductivity of (La,Sr)(Fe,Ga)O_3−δ in air decrease with gallium additions. The average thermal expansion coefficients (TECs) are in the range (11.7–16.0)×10⁻⁶ K⁻¹ at 300–800 K and (19.3–26.7)×10⁻⁶ K⁻¹ at 800–1100 K. At oxygen partial pressures close to atmospheric air, the oxygen permeation fluxes through La_1−xSr_xFe_1−yGa_yO_3−δ (x=0.7–0.8; y=0.2–0.4) membranes are determined by the bulk ambipolar conductivity; the limiting effect of the oxygen surface exchange was found negligible. Decreasing strontium and gallium concentrations leads to a greater role of the exchange processes. As for many other perovskite systems, the oxygen ionic conductivity of La_1−xSr_xFe_1−yGa_yO_3−δ increases with strontium content up to x=0.70 and decreases on further doping, probably due to association of oxygen vacancies. Incorporation of moderate amounts of gallium into the B sublattice results in increasing structural disorder, higher ionic conductivity at temperatures below 1170 K, and lower activation energy for the ionic transport.     

Studies of lithium intercalation in 3R-WS2

The lithium intercalation into the layered dichalcogenide 3R-WS₂ has been investigated by electrochemical reduction and by chemical reaction in n-butyl lithium solution. Essential results are (a) a charge transfer of nearly 0.6e⁻/W in Li_xWS₂, (b) a small increase of the c-axis parameter of about 0.6%, and (c) a high mobility of the Li⁺-ions. The chemical diffusion coefficient of Li⁺-ions is estimated to be 8 × 10⁻⁹ cm² s⁻¹ in the composition range 0 ≤ x ≤ 0.25. The appearance of a structural transformation from 3R-WS₂ to 2H-Li_xWS₂ is interpreted on grounds of instabilities in the interlayer structure.     

Characterization and cathode performance of Li1 − xNi1 + xO2 prepared with the excess lithium method

Samples of Li_{1 − z}Ni_{1 + x}O₂ with various x values were synthesized and their electrochemical properties, phase transitions, and ordering phenomena were investigated comparatively. In order to synthesize samples with a small x value, an excess lithium was used as a starting material to compensate for lithium loss during the calcination process. A stoichiometric sample with a large reversible capacity of more than 200 mAh g⁻¹ is also described.     

Trapping mechanism of superconductivity suppression induced by Pr substitution in the Ho1−xPrxBa2Cu3O7−δ system

Pr concentration dependence of the superconducting transition temperature T_c in the Ho_1−xPr_xBa₂Cu₃O_7−δ system is determined from measurements of DC electrical resistance. This dependence coincides with that for the parallely studied Y_1−xPr_xBa₂Cu₃O_7−δ reference system. Both systems have the same value of the critical concentration x_c=0.58, in accordance with nearly equal ionic radii of Ho³⁺ and Y³⁺ ions. It has been shown that the T_c(x) curve can be described with a single mechanism based on a decreasing number of sheet holes trapped by Pr^IV-ions, if one takes also into account that the number of these ions changes with x.     

Effects of cation- or oxide ion-defect on conductivities of apatite-type La–Ge–O system ceramics

A series of apatite-type La–Ge–O ceramics were prepared and their cation-defect at the 4f+6h sites and oxide ion-defect at 2a site were investigated. In La_xGe₆O_12+1.5x ceramics of x=6–12, the higher conductivities were obtained in the region of apatite composition, La_x(GeO₄)₆O_1.5x−12 (x=8–9.33), and the highest conductivity was achieved for La₉(GeO₄)₆O_1.5 (x=9), where the number of cation (La³⁺) occupying the 4f+6h sites is 9 and the number of oxide ion occupying the 2a site is 1.5. The ceramics with cation- and oxide ion-defects were La_9−0.66xSr_x(GeO₄)₆O_1.5 (x=0–1), La_9−1.33xZr_x(GeO₄)₆O_1.5 (x=0–1), La_9−xSr_x(GeO₄)₆O_1.5−0.5x (x=0–3), La_9−xZr_x(GeO₄)₆O_1.5+0.5x (x=0–1), La_x(GeO₄)_3x−21(AsO₄)_27−3xO_1.5 (x=0–3), La_x(GeO₄)_33−3x(AlO₄)_3x−27O_1.5 (x=0–3), La₉(GeO₄)_6−x (AlO₄)_xO_1.5−0.5x (x=0–3), La₉(GeO₄)_6−x(AsO₄)_xO_1.5+0.5x (x=0–1), La_9.33−xSr_x(GeO₄)₆O_2−0.5x (x=0–1.2) and La_x(GeO₄)_4.5(AlO₄)_1.5O_1.5x−12.75 (x=8.8–9.83), which were prepared by the partial substitution of La³⁺and GeO₄⁴⁻of the basic apatite La₉(GeO₄)₆O_1.5 with Sr²⁺ or Zr⁴⁺ and AlO₄⁵⁻ or AsO₄³⁻. Such substitutions lowered the conductivity of La₉(GeO₄)₆O_1.5. These results were discussed by the electrostatic interaction between Sr²⁺, Zr⁴⁺, AlO₄⁵⁻ or AsO₄³⁻ and oxide ion as a conductive species.     

Lithium insertion into Li4V3O8

The lithium insertion characteristics of lithium vanadate, Li₄V₃O₈, were investigated using LiV₃O₈ prepared by the precipitation technique as the starting material. The Li₄V₃O₈ phase was formed by lithiation over x=1.5 in Li_1+xV₃O₈, and the diffusion of lithium in this phase determined the reaction rate of insertion more than x=1.5. Improvement of insertion kinetics in the Li₄V₃O₈ phase extended the lithium insertion limit from x=3.2 to x=4.0, compared with the case of LiV₃O₈ by conventional high temperature synthesis. Lithium insertion proceeds as the single-phase reaction in the range of 3.2<x<4.0.     

Disruption of antiferromagnetic order in Zn-doped La2CuO4

The magnetic phase diagram of La₂(Cu_1−xZn_x)O₄ has been determined from zero-field muon-spin-rotation (ZF-μSR) data taken at LAMPF for 0 ≤ x ≤ 0.10. Antiferromagnetic onset temperatures follow T_N(x) from susceptibility measurements on the same samples. However, the order becomes long range, as evidenced by a well-defined internal magnetic field, only at temperatures well below T_N. Extrapolation of our results yields T_N → 0 K at x = 0.11 for a single (Cu_1−xZn_x)O₂ plane, and comparison with YBa₂(Cu_1−xZn_x)₃O₆ implies identical disruption of magnetism by Zn doping in the single- and double-plane systems.     

Characterization of nonstoichiometric nickel manganite spinels NixMn3−x□3δ/4O4+δ by temperature programmed reduction

Cation deficient spinels Ni_xMn_3−x□_3δ/4O_4+δ (0≤x≤1) have been prepared by thermal decomposition of mixed oxalates Ni_x/3Mn_(3−x)/3(C₂O₄)·nH₂O in air at 623 K. They have been characterised by temperature programmed reduction (TPR) under H₂, the reaction being followed by gravimetric and powder X-ray diffraction measurements. It has been shown that TPR proceeds in several steps. The first steps correspond to the loss of nonstoichiometric oxygen leading to the formation of a stoichiometric oxide. During the following stages the manganese cations are reduced, causing the spinel structure to be destroyed, and the formation of solid solution of NiO in a cubic MnO. Subsequently, Ni²⁺ cations undergo a reduction to metallic nickel, and, finally, a mixture of nonstoichiometric MnO_1−δ and metallic nickel is formed. These oxides contain a high level of vacancies which vary with the nickel content with a maximum of δ≈1 near x=0.6. This nonstoichiometry is ascribed both to the presence of Ni³⁺ and excess of Mn⁴⁺.     

Tuning the multiferroic properties of Pb(Fe1/2Nb1/2)O3 by cationic substitution

A series of substituted lead iron niobate compounds with the general formula Pb²⁺_(1−x)A^Z_x(Fe_{{(1−(2−Z)x)/2}}Nb_{{(1+(2−Z)x)/2}})O₃ (0<x<0.6 and A=La³⁺, K⁺ or Sr²⁺) were prepared by a modified solid-state synthesis. The relative concentrations of Fe³⁺ and Nb⁵⁺ were adjusted to compensate the charge imbalance due to the aliovalent substitution. The dielectric constant and magnetic susceptibilities were studied as a function of temperature. The temperature of the dielectric maximum, T_M, of the substituted compounds decreased linearly with increasing concentration of the substituent ions. The magnetic measurements showed an antiferromagnetic transition at temperatures T_N1 due to the superexchange interactions mediated by Fe–O–Fe and an additional antiferromagnetic-type transition at T_N2. T_N1 linearly increased with the increasing concentration of Fe³⁺ ion at the B-site of ABO₃-type substituted compounds. T_M is shown to be directly dependent on the concentration of the ferroactive Nb⁵⁺ ions at the B-site and Pb²⁺ ions at the A-site.     

Electrons and holes in undoped Nd2CuO4

Nd₂CuO_4±δ is the non-superconducting prototype of the Re_2−xM_xCuO₄t−y family (Re=Pr, Nd, Sm and M=Ceor Th) of n-type oxide superconductors. Four-probe DC conductivity, EMF in P(O₂) gradient, and thermopower measurements have been used to characterise its electric transport and defect structure between 300 and 900°C and between 5×10⁻⁴ and 1 atm oxygen partial pressure.

The results show that Nd₂CuO_4±δ can be oxygen under-stoichiometric (with n-type conductivity), near-stoichiometric, and over-stoichiometric (with p-type conductivity) in different T, P(O₂) ranges.     

The effect of oxygen vacancy on the oxide ion mobility in LaAlO3-based oxides

The electrical property of (La_1−xSr_x)_1−z(Al_1−yMg_y)O_3−δ (LSAM; x≤0.3, y≤0.15 and z≤0.1) was measured using the DC four-probe method as a function of temperature (500–1000°C) and oxygen partial pressure (1–10⁻²² atm). Among LSAMs, (La_0.9Sr_0.1)AlO_3−δ showed the highest ionic conductivity, σ_i=1.3×10⁻² S cm⁻¹ at 900°C. A simultaneous substitution at A and B sites or A site deficiency is expected to create larger oxygen vacancy and higher ionic conductivity. However, it showed a negative effect. The effect of the vacancy increase did not effect monotonously the ionic conductivity. It was found that the concentration of oxygen vacancy, [V_O], influences not only the oxide ion conductivity, σ_i, but also the mobility, μ_v, of [V_O]. These properties exhibit a maximum at around [V_O]=0.05. With the increase in [V_O], the activation energy, E_a, of the ionic conduction dropped from 1.8 to ca. 1.0 eV at [V_O]=0.05 and became almost constant at [V_O]>0.05. The dependency of the pre-exponential term, μ⁰_v, and E_a on [V_O] was analyzed and their effect on μ_v and σ_i was discussed with respect to crystal structure and defect association. It was estimated that the crystal structure mainly governs these properties. The effect of defect association could not be ignored but is considered to be a complicated correlation.     

Spectroscopic study of BixEu1−xVO4 and BiyGd1−yVO4 mixed oxides

The mixed oxides Bi_xEu_1−xVO₄ and Bi_yGd_1−yVO₄ crystallize in a zircon-type structure, for 0 <x < 0.6 and 0 < y < 0.64, and in a fergusonite-type structure, for 0.94 < x < 1 and 0.93 < y < 1. A process of competition between the dominant and the constrained effects of the lone-pair 6s² of Bi³⁺ is discussed. The diffuse reflectance spectroscopic studies of these mixed oxides are presented. The observed broad bands are attributed to charge transfer processes and the sharp peaks in the Bi_xEu_1−xVO₄ spectra are ascribed to intra-configurational 4f – 4ftransitions of the Eu³⁺ ion. The broad absorption shift in BiLnVO₄ (Ln : Eu and Gd) compounds to the longer wavelengths range, when Bi is introduced in the LnVO₄ lattice, is ascribed to charge transfer processes in a Bi-VO₄ center and are interpreted assuming a Jahn-Teller effect in the excited state of Bi³⁺. The concept of an internal pressure of Bi³⁺ ions is also used to explain the broad A-band shifts.