Characteristics of ZnO:Al thin films co-doped with hydrogen and fluorine

Fluorine and hydrogen co-doped ZnO:Al (AZO) films were prepared by radio frequency (rf) magnetron sputtering of ZnO targets containing 1 wt.% Al₂O₃ on Corning glass at substrate temperature of 150 °C with Ar/CF₄/H₂ gas mixtures, and the structural, electrical and optical properties of the as-deposited and the vacuum-annealed films were investigated. In as-deposited state, films with fairly low resistivity of 3.9-4 × 10⁻⁴ Ω cm and very low absorption coefficient below 900 cm⁻¹ when averaged in 400-800 nm could be fabricated. After vacuum-heating at 300 °C, the minimum resistivity of 2.9 × 10⁻⁴ Ω cm combined with low absorption loss in visible region, which enabled the figure of merit to uplift as high as 4 Ω⁻¹, could be obtained for vacuum-annealed film. It was shown that, unlike hydrogenated ZnO films which resulted in degradation upon heating in vacuum at moderately high temperature, films with fluorine addition could yield improved electrical properties mostly due to enhanced Hall mobility while preserving carrier concentration level. Furthermore, stability in oxidizing environment could be improved by fluorine addition, which was ascribed to the filling effect of dangling bonds at the grain boundaries. These results showed that co-doping of hydrogen and fluorine into AZO films with low Al concentration could be remarkably compatible with thin film solar cell applications.     

Influence of deposition temperature on the crystallinity of Al-doped ZnO thin films at glass substrates prepared by RF magnetron sputtering method

Al-doped ZnO (AZO) transparent conducting films were successfully prepared on glass substrates by RF magnetron sputtering method under different substrate temperatures. The microstructural, electrical and optical properties of AZO films were investigated in a wide temperature range from room temperature up to 350 °C by X-ray Diffraction (XRD), Field-Emission Scanning Electron Microscopy (FESEM), High-Resolution Transmission Electron Microscopy (HRTEM), Hall measurement, and UV–visible meter. The nature of AZO films is polycrystalline thin films with hexagonal wurtzite structure and a preferred orientation along c-axis. The crystallinity and surface morphologies of the films are strongly dependent on the growth temperature, which in turn exerts a great effect on microstructural, electrical and optical properties of the AZO films. The atomic arrangement of AZO film having an wurtzite structure was indeed identified by the HRTEM as well as the Selected Area Electron Diffraction (SAED). The defect density of AZO film was investigated by HRTEM. The film deposited at 100 °C exhibited the relatively well crystallinity and the lowest resistivity of 3.6 × 10⁻⁴ Ω cm. The average transmission of AZO films in the visible range is all over 85%. More importantly, the low-resistance and high-transmittance AZO film was also prepared at a low temperature of 100 °C.     

Influence of substrate temperature and post-treatment on the properties of ZnO:Al thin films prepared by pulsed laser deposition

Highly transparent conductive Al₂O₃ doped zinc oxide (AZO) thin films have been deposited on the glass substrate by pulsed laser deposition technique. The effects of substrate temperature and post-deposition annealing treatment on structural, electrical and optical properties of AZO thin films were investigated. The experimental results show that the electrical resistivity of films deposited at 240 °C is 6.1 × 10⁻⁴ Ω cm, which can be further reduced to as low as 4.7 × 10⁻⁴ Ω cm by post-deposition annealing at 400 °C for 2 h in argon. The average transmission of AZO films in the visible range is 90%. The optical direct band gap of films was dependent on the substrate temperature and the annealing treatment in argon. The optical direct band gap value of AZO films increased with increasing annealing temperature.     

Effects of post-annealing on structural, optical and electrical properties of Al-doped ZnO thin films

Aluminum-doped zinc oxide (AZO) films were deposited at 400 °C by radio-frequency magnetron sputtering using a compound AZO target. The effects of annealing atmospheres as well as hydrogen annealing temperatures on the structural, optical and electrical properties of the AZO films were investigated. It was found that the electrical resistivity varied depending on the atmospheres while annealing in air, nitrogen and hydrogen at 300 °C, respectively. Comparing with that for the un-annealed films, the resistivity of the films annealed in hydrogen decreased from 9.8 × 10⁻⁴ Ω cm to 3.5 × 10⁻⁴ Ω cm, while that of the films annealed in air and nitrogen increased. The variations in electrical properties are ascribed to both the changes in the concentration of oxygen vacancies and adsorbed oxygen at the grain boundaries. These results were clarified by the comparatively XPS analyzing about the states of oxygen on the surface of the AZO films. There was great increase in electrical resistivity due to the damage of the surfaces, when AZO films were annealed in hydrogen with a temperature higher than 500 °C, but high average optical transmittance of 80-90% in the range of 390-1100 nm were still obtained.     

Optical and electrical characteristics of Al-doped ZnO thin films prepared by aqueous phase deposition

Transparent conducting Al-doped ZnO (AZO) thin films have been deposited by sol-gel route. Starting from an aqueous solution of zinc acetate by adding aluminum chloride as dopant, a c-axis oriented polycrystalline ZnO thin film 100 nm in thickness could be spin-coated on glass substrates via a two-step annealing process under reducing atmosphere. The effects of thermal annealing and dopant concentration on the structural, electrical and optical properties of AZO thin films were investigated. The post-treated AZO films exhibited a homogenous dense microstructure with grain sizes less than 10 nm as characterized by SEM photographs. The annealing atmosphere has prominent impact on the crystallinity of the films which will in turn influence the electrical conductivity. By varying the doping concentrations, the optical and electrical properties could be further adjusted. An optimal doping concentration of Al/Zn = 2.25 at.% was obtained with minimum resistivity of 9.90 × 10⁻³ Ω-cm whereas the carrier concentration and mobility was 1.25 × 10²⁰ cm⁻³ and 5.04 cm² V⁻¹ s⁻¹, respectively. In this case, the optical transmittance in the visible region is over 90%.     

A study on the wet etching behavior of AZO (ZnO:Al) transparent conducting film

This paper studies the wet etching behavior of AZO (ZnO:Al) transparent conducting film with tetramethylammonium hydroxide (TMAH). The optimum optoelectronic film is prepared first using designated RF power, film thickness and controlled annealing heat treatment parameters. The AZO film is then etched using TMAH etchant and AZ4620 photoresist with controlled etchant concentration and temperature to examine the etching process effect on the AZO film optoelectronic properties. The experimental results show TMAH:H₂O = 2.38:97.62 under 45 °C at the average etch rate of 22 nm/min as the preferred parameters. The activation energy drops as the TMAH concentration rises, while the etch rate increases along with the increase in TMAH concentration and temperature. After lithography, etching and photoresist removal, the conductivity of AZO film dramatically drops from 2.4 × 10⁻³ Ω cm to 3.0 × 10⁻³ Ω cm, while its transmittance decreases from 89% to 83%. This is due to the poor chemical stability of AZO film against AZ4620 photoresist, leading to an increase in surface roughness. In the photoresist postbaking process, carbon atoms diffused within the AZO film produce poor crystallinity. The slight decreases in zinc and aluminum in the thin film causes a carrier concentration change, which affect the AZO film optoelectronic properties.     

Optimization of the optical and electrical properties of electron beam evaporated aluminum-doped zinc oxide films for opto-electronic applications

Aluminum-doped zinc oxide (AZO) thin films have been deposited by electron beam evaporation technique on glass substrates. The structural, electrical and optical properties of AZO films have been investigated as a function of annealing temperature. It was observed that the optical properties such as transmittance, reflectance, optical band gap and refractive index of AZO films were strongly affected by annealing temperature. The transmittance values of 84% in the visible region and 97% in the NIR region were obtained for AZO film annealed at 475 °C. The room temperature electrical resistivity of 4.6×10⁻³ Ω cm has been obtained at the same temperature of annealing. It was found that the calculated refractive index has been affected by the packing density of the thin films, whereas, the high annealing temperature gave rise to improve the homogeneity of the films. The single-oscillator model was used to analyze the optical parameters such as the oscillator and dispersion energies.     

Induction of p-type conduction in sputtered deposited Al-N codoped ZnO thin films

Al and N codoped ZnO thin films were grown on n-Si (100) substrate by sputtering technique. Hall effect measurements of as-grown films exhibited n-type conduction, however 500 °C Ar annealed codoped films showed p-type conductivity with a hole concentration of 9.9 × 10¹⁶ cm^− 3, resistivity of 15.95 Ω-cm and hole mobility of 3.95 cm²/Vs, respectively. Codoped ZnO thin films were found to be highly c-axis oriented with good crystal quality. A neutral acceptor-bound exciton and donor-acceptor-pair emissions that appeared at room temperature photoluminescence measurement verify p-type conduction in Al and N codoped ZnO film. The current-voltage characteristics of p-n heterojunction evidently showed a diode like rectifying behaviour.     

The enhanced conductivity and stability of AZO thin films with a TiO2 buffer layer

Aluminum doped zinc oxide (AZO) films were substitutes of the SnO₂:F films on soda lime glass substrate in the amorphous thin-film solar cells due to good properties and low cost. In order to improve properties of AZO films, the TiO₂ buffer layer had been introduced. AZO films with and without TiO₂ buffer layer were deposited on soda lime glass substrates by r.f. magnetron sputtering. Subsequently, one group samples were annealed in vacuum (0.1 Pa) at 500 °C for 120 s using the RTA system, and the influence of TiO₂ thickness on the properties of AZO films had been discussed. The XRD measurement results showed that all the films had a preferentially oriented (0 0 2) peak, and the intensity of (0 0 2) peak had been enhanced for the AZO films with TiO₂ buffer layer. The resistivity of TiO₂ (3.0 nm)/AZO double-layer film is 4.76×10⁻⁴ Ω cm with the maximum figure merit of 1.92×10⁻² Ω⁻¹, and the resistivity has a remarkable 28.7% decrease comparing with that of the single AZO film. The carrier scattering mechanism of TiO₂ (3.0 nm)/AZO double-layer film had been described by Hall measurement in different temperatures. The average transmittance of all the films exceeded 92% in the visible spectrum. Another group samples were heat treated in the quartz tube in air atmosphere, and the effect of TiO₂ thickness on thermal stability of AZO films had been discussed.     

Deposition of quasi-crystal Al-doped ZnO thin films for photovoltaic device applications

Quasi-crystal aluminum-doped zinc oxide (AZO) films were prepared by in situ radio frequency (RF) magnetron sputtering (sputtering without annealing) on glass substrates. The influence of deposition parameters on the optoelectronic and structural properties of the in situ deposited quasi-crystal AZO films was investigated in order to compare resulting samples. X-ray diffraction (XRD) patterns show that the quasi-crystal AZO thin films have excellent crystallization improved with increase of the RF power and substrate temperature, with an extremely preferential c-axis orientation exhibit sharp and narrow XRD pattern similar to that of single-crystal. Field emission scanning electron microscopy (FESEM) images show that quasi-crystal AZO thin films have uniform grains and the grain size increase with the increase of RF power and substrate temperature. Craters of irregular size with the columnar structure are observed in the quasi-crystal AZO thin films at a lower substrate temperature while many spherical shaped grains appeared at a higher substrate temperature. The average optical transmittance of all the quasi-crystal AZO films was over 85% in the 400-800 nm wavelength range. The resistivity of 4.176 × 10⁻⁴ Ω cm with the grain size of 76.4891 nm was obtained in the quasi-crystal AZO thin film deposited at 300 °C, under sputtering power of 140 W.     

Transparent conductive ZnO:Al films grown by atomic layer deposition for Si-wire-based solar cells

Structural, electrical, and optical properties of atomic layer-controlled Al-doped ZnO (ZnO:Al) films grown by atomic layer deposition (ALD) on glass substrates were characterized at various growth temperatures for use as transparent electrodes. The Al atomic content in ZnO:Al films increased due to the reduced ZnO film growth rate with increasing temperature. The preferred orientation of ZnO:Al films was changed, and the optimum condition for best crystallinity was identified by varying the growth temperature. Furthermore, the carrier concentration of free electron was increased by substituting the Zn sites with Al atoms in the crystal, resulting from monolayer growth based on alternate self-limiting surface chemical reactions. The electrical resistivity of ZnO:Al film grown by ALD at 225 °C reached the lowest value of 8.45 × 10⁻⁴ Ω cm, with a carrier mobility of 9.00 cm² V⁻¹ s⁻¹ and optical transmittance of ∼93%. This result demonstrates that ZnO:Al films grown by ALD possess excellent potential for applications in electronic devices and displays as transparent electrodes and surface passivation layers.     

Formation of Al-N co-doped p-ZnO/n-Si (1 0 0) heterojunction structure by RF co-sputtering technique

Al-N co-doped ZnO (ZnO:Al-N) thin films were grown on n-Si (1 0 0) substrate by RF co-sputtering technique. As-grown ZnO:Al-N film exhibited n-type conductivity whereas on annealing in Ar ambient the conduction of ZnO:Al-N film changes to p-type, typically at 600 °C the high hole concentration of ZnO:Al-N co-doped film was found to be 2.86 × 10¹⁹ cm⁻³ and a low resistivity of 1.85 × 10⁻² Ω-cm. The current-voltage characteristics of the obtained p-ZnO:Al-N/n-Si heterojunction showed good diode like rectifying behavior. Room temperature photoluminescence spectra of annealed co-doped films revealed a dominant peak at 3.24 eV.     

Effect of Cr and V dopants on the chemical stability of AZO thin film

The effect of the dopants of Cr and V on the optoelectronic properties of AZO thin film by pulsed DC magnetron sputtering has been investigated. We also use HCl and KOH solutions to conduct the chemical stability of AZO:Cr:V thin film. The experimental results show that the optimum AZO optoelectronic properties without Cr and V doping obtain the resistivity of 9.87 × 10⁻⁴ Ω cm, optical transmittance of 84% and surface roughness rms value of 2.6 nm. The chemical stability of AZO will increase after Cr and V doping. Under the added V = 0.19 wt.%, Cr = 0.56 wt.%, AZO:Cr:V thin film showed 52% increased chemical stability and 128% decrease in surface roughness after etching (the resistivity was 3.62 × 10⁻³ Ω cm and optical transmittance 81%). From the experimental results, the higher resistivity obtained after KOH etching compared with after HCl etching. The reason is that the Zn/Al ratio will reduce after etching and cause the AZO film carrier density to reduce as well. However, the optical transmittance obtained after KOH etching will be higher than that after HCl etching. This is because that a better surface roughness after KOH etching obtained than after HCl etching.     

High work function of Al-doped zinc-oxide thin films as transparent conductive anodes in organic light-emitting devices

Deposition of Al-doped ZnO (AZO) films with various film thicknesses on glass substrates was performed to investigate the feasibility of using AZO films as anode electrodes in organic light-emitting devices (OLEDs). The electrical resistivity of the AZO films with a 180-nm thickness was 4.085 × 10⁻² Ω cm, and the average optical transmittance in the visible range was 80.2%. The surface work function for the AZO films, determined from the secondary electron emission coefficients obtained with a focused ion beam, was as high as 4.62 eV. These results indicate that AZO films grown on glass substrates hold promise for potential applications as anode electrodes in high-efficiency OLEDs.     

Effect of annealing on structural, optical and electrical properties of nanostructured Ge thin films

Ge thin films with a thickness of about 110 nm have been deposited by electron beam evaporation of 99.999% pure Ge powder and annealed in air at 100-500 °C for 2 h. Their optical, electrical and structural properties were studied as a function of annealing temperature. The films are amorphous below an annealing temperature of 400 °C as confirmed by XRD, FESEM and AFM. The films annealed at 400 and 450 °C exhibit X-ray diffraction pattern of Ge with cubic-F structure. The Raman spectrum of the as-deposited film exhibits peak at 298 cm⁻¹, which is left-shifted as compared to that for bulk Ge (i.e. 302 cm⁻¹), indicating nanostructure and quantum confinement in the as-deposited film. The Raman peak shifts further towards lower wavenumbers with annealing temperature. Optical band gap energy of amorphous Ge films changes from 1.1 eV with a substantial increase to ∼1.35 eV on crystallization at 400 and 450 °C and with an abrupt rise to 4.14 eV due to oxidation. The oxidation of Ge has been confirmed by FTIR analysis. The quantum confinement effects cause tailoring of optical band gap energy of Ge thin films making them better absorber of photons for their applications in photo-detectors and solar cells. XRD, FESEM and AFM suggest that the deposited Ge films are composed of nanoparticles in the range of 8-20 nm. The initial surface RMS roughness measured with AFM is 9.56 nm which rises to 12.25 nm with the increase of annealing temperature in the amorphous phase, but reduces to 6.57 nm due to orderedness of the atoms at the surface when crystallization takes place. Electrical resistivity measured as a function of annealing temperature is found to reduce from 460 to 240 Ω-cm in the amorphous phase but drops suddenly to 250 Ω-cm with crystallization at 450 °C. The film shows a steep rise in resistivity to about 22.7 KΩ-cm at 500 °C due to oxidation. RMS roughness and resistivity show almost opposite trends with annealing in the amorphous phase.     

Structural, optical and electrical characterization of highly conducting Mo-doped In2O3 thin films

Highly conducting and transparent thin films of molybdenum-doped indium oxide were deposited on quartz by pulsed laser deposition. The effect of growth temperature and oxygen partial pressure on the structural, optical and electrical properties was studied. We find that the film transparency depends on the growth temperature. The average transmittance of the films grown at different temperatures is in range of 48-87%. The X-ray diffraction results show that the films grown at low temperature are amorphous while the films grown at higher temperature are crystalline. Electrical properties are found to be sensitive to both the growth temperature and oxygen pressure. Resistivity of the films decreases from 1.3 × 10⁻³ Ω cm to 8.9 × 10⁻⁵ Ω cm while mobility increases from 9 cm²/V s to 138 cm²/V s as the growth temperature increases from room temperature to 700 °C. However, with increase in oxygen pressure, resistivity increases but the mobility decreases after attaining a maximum. The temperature-dependent resistivity measurements show transition form semiconductor to metallic behavior. The film grown at 500 °C under an oxygen pressure of 1.0 × 10⁻³ mbar is found to exhibit high mobility (250 cm²/V s), low resistivity (6.7 × 10⁻⁵ Ω cm), and relatively high transmittance (∼90%).     

Investigation of p-type behavior in Ag-doped ZnO thin films by E-beam evaporation

Ag-doped ZnO (ZnO:Ag) thin films were grown on glass substrates by E-beam evaporation technique. The structural, electrical and optical properties of the films were investigated as a function of annealing temperature. The films were subjected to post annealing at different temperatures in the range of 350-650 °C in an air ambient. All the as grown and annealed films at temperature of 350 °C showed p-type conduction. The films lost p-type conduction after post annealing treatment temperature of above 350 °C, suggesting a narrow post annealing temperature window for the fabrication of p-type ZnO:Ag films. ZnO:Ag film annealed at 350 °C revealed lowest resistivity of 7.25 × 10⁻² Ω cm with hole concentration and mobility of 5.09 × 10¹⁹ cm⁻³ and 1.69 cm²/V s, respectively. Observation of a free-to-neutral-acceptor (e,A^o) and donor-acceptor-pair (DAP) emissions in the low temperature photoluminescence measurement confirms p-type conduction in the ZnO:Ag films.     

The effect of heating rate on the structural and electrical properties of sol-gel derived Al-doped ZnO films

Al-doped ZnO (AZO) films are prepared by sol-gel method with a proper annealing procedure. For the first time, we find that the heating rate which is normally neglected during the post annealing process plays a significant role in improving AZO properties. The AZO film with nanorod structure is obtained by using a rapid heating rate. The AZO nanorods can provide a faster conduction pathway for charge transport due to the high crystal quality and thus enhance the conductivity of the film significantly. After hydrogen treatment, the AZO nanorod film exhibits a minimum resistivity of 1.4 × 10⁻³ Ω cm. This approach to the preparation of AZO nanorods by a simple rapid annealing process may be helpful for the development of sol-gel-derived TCO films.     

Effect of composition and deposition temperature on the characteristics of Ga doped ZnO thin films

ZnO films doped with Ga (GZO) of varying composition were prepared on Corning glass substrate by radio frequency magnetron sputtering at various deposition temperatures of room temperature, 150, 250 and 400 °C, and their temperature dependent photoelectric and structural properties were correlated with Ga composition. With increasing deposition temperature, the Ga content, at which the lowest electrical resistivity and the best crystallinity were observed, decreased. Films with optimal electrical resistivity of 2-3 × 10⁻⁴ Ω cm and with good crystallinity were obtained in the substrate temperature range from 150 to 250 °C, and the corresponding C_Ga/(C_Ga + C_Zn) atomic ratio was about 0.049. GZO films grown at room temperature had coarse columnar structure and low optical transmittance, while films deposited at 400 °C yielded the highest figure of merit (FOM) due to very low optical absorption despite rather moderate electrical resistivity slightly higher than 4 × 10⁻⁴ Ω cm. The optimum Ga content at which the maximum figure of merit was obtained decreased with increasing deposition temperature.     

The influence of substrate temperature on the morphology, optical and electrical properties of thermal-evaporated ZnTe Thin Films

The structural, morphological, optical and electrical properties of ZnTe films deposited by evaporation were investigated as a function of substrate temperature (at −123 and 27 °C) and post-deposition annealing temperature (at 200, 300 and 400 °C). It was determined that films deposited at both substrate temperatures were polycrystalline in nature with zinc-blende structure and a strong (1 1 1) texture. A small Te peak was detected in XRD spectra for both substrate temperatures, indicating that as-deposited ZnTe films were slightly rich in Te. Larger grains and a tighter grain size distribution were obtained with increased substrate temperature. Scanning electron microscopy (SEM) studies showed that the microstructures of the as-deposited films agreed well with the expectations from structure zone model. Post-deposition annealing induced further grain growth and tightened the grain size distribution. Annealing at 400 °C resulted in randomization in the texture of films deposited at both substrate temperatures. Optical spectroscopy results of the films indicated that the optical band gap value increased from 2.13 to 2.16 eV with increased substrate temperature. Increasing the annealing temperature sharpened the band-edge. Resistivity measurements showed that the resistivity of films deposited at substrate temperatures of −123 and 27 °C were 32 Ω cm, and 1.0 × 10⁴ Ω cm, respectively with corresponding carrier concentrations of 8.9 × 10¹⁵ cm⁻³ and 1.5 × 10¹⁴ cm⁻³. Annealing caused opposite changes in the film resistivity between the samples prepared at substrate temperatures of −123 and 27 °C.