评述了热致液晶聚酯的共混物与复合材料的研究新进展,揭示了热行为与相容性、流变性与加工性以及形态结构与多种性能之间的内在联系,展望了应用于高强高模纤维与塑料、低热膨光纤涂层及低透气包装膜等高性能材料的前景.     

热致性液晶乙基纤维素和聚丙烯共混物的结构与性能

乙基纤维素（ＥＣ）和聚丙烯共混物沿取向方向有明显的絮条状结构，ＥＣ含量增加使Ｔｃ提高，△Ｈ和Ｔｍ有所降低，共混物的成核能力降低，结晶度下降，（１１０）晶面尺寸减小，（０４０）晶面尺增大。ＥＣ／ＰＰ共混物的ηａ、τａ值更接近于ＰＰ结果。力学测定结果给出，ＥＣ／ＰＰ＝１０／９０的共混物抗张模量有所增加。     

新型聚芳醚酮与热致性液晶高聚物共混物流变性能和力学性能的研究

本文研究了新型聚芳醚酮与热致性液晶高聚物(PEK-C/LCP)共混物的流变性能及力学性能。结果表明:由于LCP的加入,PEK-C的熔体粘度降低;随着剪切速率的增加,共混物熔体流动活化能从223.5KJ/mol降为102.2KJ/mol。共混物的玻璃化转变温度从纯PEK-C的218℃降为199℃;除模量增加外,其它力学性能均有所下降。同时利用SEM观察了共混物冲击断面形貌,未发现有LCP微纤维生成。     

PPESK/PES共混物热性能及动态机械性能研究

采用熔融共混法制备了不同重量比例的新型含二氮杂萘酮结构聚芳醚砜酮(PPESK)与聚醚砜(PES)共混物.利用热失重(TGA)及动态热机械仪(DMTA)对该共混物的热性能及动态机械性能进行了研究.研究结果表明,在氮气氛围中,PPESK热分解分为两步反应进行,反应级数n=1,说明PPESK在氮气氛围中的热分解反应类型与β(升温速率)无关而与材料物性有关;采用Ozawa方法得出在15%热失重前,热分解活化能的平均值为240 kJ/mol;随着升温速率的提高,PPESK热降解速率有减缓趋势.在280℃以前,PPESK储能模量值随温度变化较小,保持在较高值,温度在280~330℃之间,储能模量值降低幅度突变.另外,PPESK中加入PES会降低其储能模量值及其热稳定性.     

含热致液晶性共聚酯的聚砜共混物

将一种含萘环的热致液晶性共聚酯与聚砜树脂熔融共混并挤塑成条。毛细管流变性测试表明，这一共聚酯降低了共混物的表观粘度，甚至低于其本身的粘度。共混物受剪切作用形成了各向异性的微纤增强结构，并具有皮芯结构，在液晶聚俣物含量低到２％与０．５％的样条中仍有共聚酯微纤形成。共聚酯微纤提高了聚砜的力学性能，含２０％共聚酯共混物挤塑条的位伸模量为聚砜树脂的二倍半。     

芳香族热致液晶聚（对羟基苯甲酸—对苯二甲酸双酚A酯）的流变性能

用Ｉｎｓｔｒｏｎ３２１１型毛细管流变仪研究了以对羟枯苯甲酸、对苯二甲酯和双酚为单体合成的共聚芳酯液晶熔体的流变性能。结果表明，切变速率、熔体温度及ＰＨＢ链节含量对切粘度和结构粘度有很大的影响。     

热致液晶共聚酯／含酚酞侧基聚芳醚砜共混物的流变行为研究

采用溶液共混制备耻不同比例的热致液晶共聚酯／含酚酞侧基聚芳醚砜共混物。利用锥板流变仪对共混体系的熔体流变性能进行了初步研究，测定了熔体粘度－温度、粘度－剪切速度的关系，结果表明该液晶聚合物能明显降低聚芳醚砜的熔体粘度。     

热致性液晶聚合物的种类对液晶/环氧树脂共混物固化反应动力学的影响

采用等温DSC固化动力学研究方法,用自催化动力学模型对反应型热致性液晶聚合物/环氧树脂共混体系进行研究.结果表明,EP/DDS未改性体系,在α＜40%范围遵循自催化反应机理;EP/DDS/LCPU共混改性体系,在α＜60%范围遵循自催化动力学反应机理,而且自催化反应速率和非催化反应速率均大于未改性体系,表明反应型热致性液晶聚合物的活性基团对固化反应起到了催化促进作用;EP/DDS/PHBHT共混改性体系能够较好符合n级反应机理,固化反应的活化能较大,说明没有反应基团的液晶聚合物(PHBHT)对固化反应无明显促进作用.     

新型热致型液晶苯代聚芳醚酮的单畴液晶行为

通过偏光显微镜研究了在外力场作用下新型热致型液晶苯代聚芳醚酮的向列相单畴液晶行为。结果表明，聚合物在剪切力作用下形成条带织构，强外力场能使介晶基元沿基质表面平行排列，形成均匀织构的单畴区。由于裂纹的存在，观察到了四条和六条黑刷的纹影织构。     

含热致液晶性共聚酯的聚砜共混物

将一种含萘环的热致液晶性共聚酯与聚砜材脂熔融共混并挤塑成条．毛细管流变性测试表明，这一共聚酯降低了共混物的表观粘度，甚至低于其本身的粘度．共混物受剪切作用形成了各向异性的微纤增强结构，并具有皮芯结构．在液晶聚合物含量低到２％与０．５％的样条中仍有共聚酯微纤形成．共聚酯微纤提高了聚砜的力学性能，含２０％共聚酯共混物挤塑条的位伸模量为聚砜树脂的二倍半．     

The Rheological and Extrusion Behaviour of Blends Based on Phenolphthalein Poly(ether-ether-sulfone) and Thermotropic Liquid Crystalline Polymer

ＩｎｔｒｏｄｕｃｔｉｏｎＩｎｔｈｅｌａｓｔｔｗｏｄｅｃａｄｅｓ，ｐａｒｔｉｃｕｌａｒａｔｅｎｔｉｏｎｈａｓｂｅｅｎｄｅｖｏｔｅｄｔｏｕｓｉｎｇｔｈｅｔｈｅｒｍｏｔｒｏｐｉｃｌｉｑｕｉｄｃｒｙｓｔａｌｉｎｅｐｏｌｙｍｅｒｓ（ＴＬＣＰ）ａｓａｒｅｉｎｆｏ...     

Synthesis and Characterization of Thermotropic Liquid Crystalline Polyesters

Abstract

Synthesis and characterization of polyesters of 4,4′-dihydroxy biphenyl with succinic, adipic, suberic and sebacic acids were carried out. Initially the diacids were converted to the corresponding acid chlorides in dimethyl formamide (DMF). 4,4′-dihydroxy biphenyl was prepared from 4-hydroxy biphenyl by bromination and subsequent hydrolysis. The low molecular weight polyesters were prepared by the condensation of diacid chlorides with 4,4′-dihydroxy biphenyl in DMF at appropriate temperature. All the polymers were characterized by ¹H NMR, FT-IR, DSC and hot stage polarizing microscope. Thermotropic liquid crystalline behaviour was established by high temperature X-ray (HTXRD) at various temperature intervals. It was found that among the four compounds prepared, three of them showed nematic phase liquid crystallinity with the exception of the ester of succinic acid.     

芳香族热致液晶聚（对羟基苯甲酸－对苯二甲酸双酚A酯）的流变性能

用Ｉｎｓｔｒｏｎ３２１１型毛细管流变仪研究了以对羟基苯甲酸（ＰＨＢ）、对苯二甲酸（ＴＰＡ）和双酚Ａ（ＢＰＡ）为单体合成的共聚芳酯液晶熔体的流变性能。结果表明，切变速率、熔体温度及ＰＨＢ链节含量对切粘度和结构粘度有很大的影响。切变速率在１０～１０３／Ｓ、温度２９５～３３０℃范围内，共聚酯粘流活化能△Ｅη为７４．５～２０５．１（ｋＪ／ｍｏｌ）。液晶熔体在剪切流中存在屈服应力τｏ，随温度升高τｏ值降低。在低温、低切变速率下，共聚酯熔体的弹性很小，甚至呈现挤出收缩现象。     

含氧化偶氮苯介晶基元共聚醚的合成与液晶行为

以1,6-二溴己烷(A)和1,10-二溴癸烷(B)为共缩聚单体,按不同摩尔配比与4,4'-二羟基氧化偶氮苯经相转移催化共聚醚化反应,合成了一系列主链上含有氧化偶氮苯介晶基元的共聚醚,它们均有好的液晶性,其取向膜观察到条带织构,当A/B的摩尔比为1时液晶态范围最宽。     

热致液晶／PEEK／嵌段共聚物共混体系的结构与性能

用ＷＡＸＤ、ＳＥＭ及力学性能测试等研究热致液晶／ＰＥＥＫ／嵌段共聚物三元共混体系形态、结构和性能。结果表明嵌段共聚物的加入，使体系具有一定的相容性和较好的界面粘接，共混物的强度、模量有一定的提高，对共混物的结晶行为具有明显的影响，当热致液晶含量高时，基材与液晶两相间出现明显的分离现象，即“皮－芯”结构．     

一种新型聚芳醚酮的热致液晶行为

聚芳醚酮具有优异的耐热性和环境稳定性 ,作为特种工程塑料在宇航、军工等高技术领域得到了广泛的应用 [1 ] .但其熔融温度较高 ,熔体粘度较大 ,在加工中存在一定困难 .热致液晶高分子 ( TLCP)具有较低的粘度 ,复合在热塑性高分子基体中的 TL CP在剪切力或拉伸应变流的作用下发生取向、变形成纤 ,其强度比热塑性基体高 1～ 2个数量级 ,另外 TL CP微纤提供了极大的纤维粘附表面积 ,因此 ,TL CP与聚合物共混具有广阔应用前景 .本文通过联苯二酚、 2 -叔丁基 - 1 ,4-对苯二酚与 4,4′-二氟二苯酮的亲核取代反应合成了一种具有热致液晶性…     

混合液晶与尼龙1010三元共混物的研究

采用ＤＣＳ、ＰＯＭ、ＳＥＭ及力学性能测试，研究了不同对羟基苯甲醛和对苯二甲酸乙二醇酯含量的液晶共聚酯ＰＥＴ４０／ＰＨＢ６０（ＬＣＰ１）和ＰＥＴ３０／ＰＨＢ７０（ＬＣＰ２）的共混物与尼龙１０１０为基体的三元混体系。结果表明，液晶共混物的力学性能比单组分有明显提高，通过改变混合液晶中两组分的含量可调节其加工温度与粘度，从而满足了与尼龙１０１０共混的加工窗口要求。混合液晶的加入对尼龙１０１０的结晶与熔融