高硅Y沸石“二次孔”结构的物理吸附法研究

用低温氮物理吸附法研究了化学法和水热法相结合制备的两个系列Y沸石的孔结构性质。研究结果表明, 用不同化学试剂处理Y沸石形成的孔结构有明显差别。但是, 当把由此得到的Y沸石在相同条件下交替进行水热处理和化学处理时, 孔结构却呈现类似的变化趋势, 即总比表面积、微孔比表面积和微孔体积是先下降后上升, 经第二次水热和化学处理是再次下降再次回升。而过程中产生的“二次孔”比表面积却呈现先上升后下降, 又回升又下降的相反的变化趋势。这种变化趋势, 可能与水热处理和化学处理过程中非骨架铝物种的形成与消失有关。     

大孔吸附树脂对金莲花黄色素的吸附性能研究

本文研究了大孔吸附树脂吸附金莲花黄色素的性能.研究结果表明:采用静态吸附法,从X-5、AB-8、D-296R、NKA、S-8 五种吸附树脂中筛选出一种吸附、解吸性能都较为理想的大孔吸附树脂X-5,并对其进行了静态吸附动力学的研究,得出的静态吸附动力学曲线反映了树脂的吸附量随时间的变化关系,其吸附动力学方程符合Langmiur提出的吸附速率方程.采用动态吸附法,得到动态吸附透过曲线和动态解吸曲线,其中采用80%乙醇溶液作为洗脱剂,其动态解吸率为88.79%.     

大孔吸附树脂对盐酸阿霉素吸附性能的研究

本文选用ＨＡ－０１、ＨＡ－０２、ＨＡ－０３大孔吸附树脂对盐酸阿霉素进行静态和动态吸附实验。测定了３种大孔吸附剂的比表面积,孔容及平均孔径,讨论了吸附树脂的孔结构参数与吸附特性的关系,以及盐酸阿霉素溶液浓度,树脂用量等条件对大孔吸附树脂吸附性能的影响。     

D160大孔吸附树脂对染料木黄酮吸附性能的研究

研究了D160大孔吸附树脂对染料木黄酮的吸附性能.结果表明,在pH4.00时,该树脂对染料木黄酮有较好的吸附性能;静态饱和吸附容量为64.5mg/g树脂;用95%乙醇溶液作解吸剂,二次累计解吸率接近100%;表现速率常数k298=1.01×10-4s-1;测得吸附热力学参数分别为:△H=32.2kJ/mol,△S=119J/(mol·K),△G288=-2.03kJ/mol,△G298=-3.22kJ/mol,△G308=4.41kJ/mol.等温吸附服从Freundlich和Langmuir等温吸附规律;研究还表明,提高振荡频率对吸附有利.     

吸附剂的物理结构和表面性质的研究——酸处理对硅胶孔结构和吸附性能的影响

测定了样品的孔结构参数和水蒸气吸附性能。试验表明:用pH3.00酸化的自来水洗涤酸性水凝胶可制得典型的细孔硅胶;用3mol/L以上的硫酸溶液浸泡酸性水凝胶可制得平均孔半径约为300的特粗孔硅胶。     

HA型大孔吸附树脂及活性炭对胆红素吸附性能的研究

本文选用HA型大孔吸附剂对患者血中胆红素进行了动态、静态吸附性能实验,考察了其对血液生化的影响。同时,用瑞典GAMBRO肾罐中活性炭进行了比较,实验结果表明,HA吸附剂对直接胆红素的吸附功效与进口活性基本相同,但血液生化指标HA吸附剂优于活性炭。     

氩吸附法研究多级孔分子筛的孔结构

采用不同方法分别制备了双介孔分子筛、介微孔分子筛及介孔沸石材料,利用氩吸附法并结合XRD技术表征了多级孔分子筛的孔结构。探讨了适用于多级孔分子筛的孔径分布计算方法,揭示了不同类型吸附等温线与孔径分布、孔型及孔容等之间的关系。研究表明,对于多级孔分子筛、微孔和介孔的孔径分布分别用SF法和BJH法计算较适宜,全孔分析可用NLDFT法计算。通过对TS-1介孔沸石的孔结构分析发现, TPAOH 在改性制备介孔TS-1的过程中起到了生成介孔及促进二次晶化的双重作用。     

含糖基大孔吸附树脂的合成及对银杏 黄酮的吸附性能研究

本文以葡萄糖为原料,合成了甲基丙烯酸葡萄糖酯单体,与马来松香丙烯酸乙二醇酯共聚合成含糖基大孔吸附树脂。采用FT-IR、紫外、热重、扫描电镜、核磁等分析方法进行表征。以芸香叶苷为模拟物,研究了含糖基大孔吸附树脂对芸香叶苷的吸附性能,结果表明吸附动力学过程符合拟一级动力学方程及液膜扩散方程,Freundlich可较好的描述含糖基大孔吸附树脂对芸香叶苷的吸附过程,为"优惠吸附"过程,是吸热、自发的慢过程。在此优化的条件下,将含糖基大孔吸附树脂对银杏黄铜进行分离纯化,可将黄酮含量为25%的银杏提取物提纯到80.9%;树脂重复使用10次后吸附量仍为7.9 mg·g~(-1)。     

大孔吸附树脂对银杏内酯和白果内酯吸附性能的研究

本文比较了ＡＢ－８、Ｄ４０２０、ＮＫＡ－９、ＡＢＤ－４和ＤＭ－１３０五种大孔吸附树脂对银杏内酯Ａ、Ｂ和白果内酯的吸附及解吸性能,并研究了相应的吸附动力学过程,实验结果表明ＡＢ－８树脂是一种较适宜的吸附剂。     

REUSY-EX的酸性和催化性能的研究

用高真空重量吸附、~(29)SiMAS NMR、NH_3-TPD、P_y-IR和正庚烷裂解等方法研究稀盐酸萃取REUSY样品后,对该沸石的孔和骨架结构、酸性和催化裂化功能的影响。吸附及~(29)SiMASNMR的测定结果表明,稀盐酸可以萃取出一部分填充在沸石二次孔中的非骨架铝(EFAl)碎片。NH_3-TPD和P_y-IR的试验结果表明,稀盐酸萃取后,该沸石强、弱酸中心的强度和数目均有所增加。正康烷裂解反应的数据指出,REUSYEX的裂解活性和抗氮性能均较其母体REUSY为高。     

同晶置换改性FAU分子筛结构及吸附性能的密度泛函理论研究

采用密度泛函理论(DFT)方法,考察了八面沸石(FAU)型分子筛β笼孔道结构内含氧化合物(甲醇、二甲醚、丙醛)的吸附,并进一步计算研究了Zn,Ca同晶置换改性的作用机理.研究结果表明,β笼孔道结构内,Al原子为甲醇、二甲醚和丙醛的吸附活性位,Si原子无吸附活性.Zn,Ca掺杂的β笼结构内,正2价的Zn和Ca掺杂替换正3价的Al,导致邻近的Si原子位置形成缺电子空穴,增强了甲醇、二甲醚和丙醛的吸附,而杂原子Zn和Ca本身并没有吸附活性.     

脱铝丝光沸石的吸附性能研究

丝光沸石是优良的吸附剂和工业生产对二甲苯的实用催化剂。脱铝是使丝光沸石改性的有效方法。Chen报道了脱铝丝光沸石对环己烷的吸附量在硅铝比为15～50范围内随硅铝比增加而减少,而在50～90范围内变化很小。张红浪等用高温水蒸气处理结合酸洗的方法脱铝,得到不同硅铝比的丝光沸石,并研究了脱铝对其结构、酸性和催化性能的影响。本     

Evaluation of the Secondary Pore Structure of Hydrothermally- and Acid-treated Faujasite Type Zeolites

With regard to H-Y type zeolites dealuminated by hydrothermal and acid treatments, their physical properties were characterized by measurements of 29Si- and 27Al-MAS-NMR, IR, and X-ray diffraction. The secondary pores were quantitatively analyzed by the t-plot method for nitrogen adsorption isotherm at liquid nitrogen temperature and were then compared with the results of samples dealuminated by SiCl4 treatment.The plateau region of the nitrogen adsorption isotherm diminished as hydrothermal and acid treatments proceeded, with the result that the shape of the t-plot changed to that of three straight sections. This t-plot shape suggested that the secondary pores with relatively consistent sizes could develop with the progress of the treatment. On the other hand, SiCl4 treatment was found to produce less secondary pores than hydrothermal and acid treatments. The surface area of micropores calculated from the t-plots gave a considerably higher value than values obtained from the BET equation and from that calculated geometrically. This is attributable to the micropore filling effect.     

气体超临界吸附研究进展

综述了近年来国内外学者对超临界气体在固体表面吸附的研究情况。指出了气体在临界温度以上吸附与临界温度以下吸附的不同之处;对现行的关于超临界气体的吸附理论研究进行了讨论,并在此基础上提出了研究中存在的总是及进一步的研究方向。     

聚丙烯酰胺在硅胶表面上的吸附及其抑制的研究

聚丙烯酰胺(PAM)具有强极性,对硅胶等极性固体表面具有强烈的吸附作用,陈九顺等用4％的NaCl水溶液为淋洗液和Adamson用0.1mol/L的吗啡啉水溶液为淋洗液虽能部分解决硅胶担体对PAM样品的吸附,但他们对吸附的实质问题未进行研究,PAM等高分子化合物在固体表面上的吸附问题的研究尚处于初级阶段。     

三维全碳多孔结构对亚甲基蓝吸附性能的动力学探究

采用低温-烧结法,以碳纳米管(CNTs)为基本骨架,聚甲基丙烯酸甲酯(PMMA)微球为造孔剂,制备了一种孔径可调的三维全碳多孔结构(ACPs);利用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、X射线衍射分析(XRD)、拉曼光谱(Raman)、比表面积及孔结构分析等对ACPs的形貌、组成、结构及比表面积进行了表征;考察了ACPs对模拟污染物亚甲基蓝的吸附效果.结果表明,该ACPs为内部含有大孔、介孔及微孔的三维连通孔隙结构,具有较大的比表面积.ACPs对亚甲基蓝的吸附过程符合伪二级动力学模型,对亚甲基蓝的平衡吸附量qe与亚甲基蓝溶液的平衡浓度ce的关系满足Langmuir等温吸附模型,由Langmuir模型计算得到ACPs对亚甲基蓝的最大吸附容量为151.3 mg/g.     

炭化温度对烟杆基活性炭孔结构及电化学性能的影响研究

以烟杆为原料, 氢氧化钾为活化剂, 通过调节炭化温度(500～800 ℃温度范围)在相同活化条件下制备了具有不同孔隙结构的活性炭材料. N₂吸附测试表明随着炭化温度降低, 活性炭的比表面积和总孔容先增大后减小, 中孔比表面积和平均孔径却一直增大. 其中600 ℃炭化样品经KOH活化后可制得比表面积为3333 m²•g^－1, 总孔容为2.47 cm³• g^－1, 中孔孔容达2.11 cm³•g^－1的高中孔率高比表面积活性炭材料. 采用直流充放电法、交流阻抗法和循环伏安法测定上述多孔炭为电极材料的双电层电容器的电化学性能, 结果表明: 炭化温度不同的烟杆基活性炭电极均表现出良好的功率特性, 充放电流增大50倍, 容量保持率均在80%左右, 其中TS-AC-600活性炭电极在有机电解液中1 mA•cm^－2充放电时, 比电容达到190 F•g^－1. 较高的中孔率和较大的平均孔径使得烟杆基活性炭电极具有良好的高倍率充放电性能.     

孔结构对活性炭吸附水溶液中铅离子的影响

选取三种表面化学性质相近的活性炭(AC),通过等温吸附实验考察活性炭对水溶液中铅离子的吸附性能,利用扫描电子显微镜(SEM)观察活性炭的表面微观形貌,通过低温(77 K)液氮吸附测定活性炭的比表面积和孔容,并分别以密度泛函理论(DFT)和Barrett-Joyner-Halenda (BJH)法计算微孔和中孔的孔径分布.结果表明:选用的三种活性炭AC1、AC2、AC3在比表面积和总孔容上呈依次下降的趋势,但表面开放孔均匀分布的AC2,具有最高的饱和吸附量,孔结构类似颗粒堆积孔的AC3,具有与表面开放孔分布集中的AC1相近的饱和吸附量;通过对孔结构与吸附量的关联分析可知,在活性炭吸附铅离子的过程中, 0.4-0.6 nm的孔是有效吸附孔, 10.5-20.6 nm、20.6-55.6 nm、5.2-10.5 nm三个区间的孔则会对吸附产生阻碍作用.     

螯合树脂研究（XXVI）氮杂冠醚型树脂的合成及其吸附性能