Flux growth of PbMg1/3Ta2/3O3 single crystals

Single crystals of PbMg_1/3Ta_2/3O₃ (PMT) were grown by the flux method. The PbO–Pb₃O₄–B₂O₃ system was used as a solvent. Transparent and light yellow PMT single crystals of rectangular shape and dimensions up to 10×6×4 mm³ were obtained. For the applied growth conditions only, the crystals of the perovskite structure were grown. X-ray diffraction tests showed that at room temperature PMT exhibits cubic symmetry with lattice parameter a=4.042(1) Å. Dielectric studies pointed to relaxor properties of PMT. The characteristic broad and frequency-dependent maximum of dielectric permittivity was observed at 179.7 K (1 kHz).     

Ambient-condition growth of superconducting YBa2Cu4O8 single crystals using KOH flux

YBa₂Cu₄O₈ is a stoichiometric oxide superconductor of T_c80 K. Unlike YBa₂Cu₃O_7−δ, this compound is free from oxygen vacancy or twin formation and does not have any microscopic disorder in the crystal. Doping with Ca raises its T_c to 90 K. The compound is a promising superconductor for technological application. Up to now, single crystals have not been grown without using specialized apparatus with extremely high oxygen pressure up to 3000 bar and at over 1100 °C due to the limited range of reaction kinetics of the compound. This fact has delayed the progress in the study of its physical properties and potential applications. We present here a simple growth method using KOH as flux that acts effectively for obtaining high-quality single crystals in air/oxygen at the temperature as low as 550 °C. As-grown crystals can readily be separated from the flux and exhibit a perfect orthorhombic morphology with sizes up to 0.7×0.4×0.2 mm³. Our results are reproducible and suggest that the crystals can be grown using a conventional flux method under ambient condition.     

Flux growth of BPO4 crystals

Single crystals of BPO₄ with sizes up to 15×10×12 mm³ were grown by top-seeded solution growth method using Li₂O–Li₄P₂O₇ as fluxes. The components volatilized from the melt were characterized by the method of X-ray powder diffraction. The defects of grown crystals have also been investigated. The measured ultraviolet cutoff edge of BPO₄ was about 130 nm. Its density was 2.82 g/cm³ determined using drainage method.     

Floating zone growth of high-quality SrTiO3 single crystals

Strontium titanate single crystals 15–20 mm in diameter and 40–80 mm in length were grown by a floating zone method with radiation heating. Additional crystal heating just below the molten zone by an in-growth annealing furnace was applied in order to lower the temperature gradients and to achieve slower cooling of the grown crystal. The crystal perfection was studied with X-ray topography and double-crystal diffractometry. The most perfect crystals were grown in [0 0 1] direction with single grain rocking curve widths of about 30″ and subgrain misorientations of 1′–3′ over 10×10 mm² areas of the boule cross-section for both (0 0 1)-, (1 1 0)- and (1 1 1)-oriented slices. Such high-quality crystal can be grown reproducibly with starting materials of 4N grade quality.     

Growth and properties of Pb[(Zn1/3Nb2/3)0.91Ti0.09]O3 single crystals directly from melt

Pb[(Zn_1/3Nb_2/3)_0.91Ti_0.09]O₃ (PZNT91/9) single crystals were grown by a modified Bridgman method directly from melt using an allomeric Pb[(Mg_1/3Nb_2/3)_0.69Ti_0.31]O₃ (PMNT69/31) single crystal as a seed. X-ray diffraction (XRD) measurement confirmed that the as-grown PZNT91/9 single crystals are of pure perovskite structure. Electrical properties and thermal stabilization of PZNT91/9 crystals grown directly from melt exhibit different characters from those of PZNT91/9 crystals grown from flux, although segregation and the variation of chemical composition are not seriously confirmed by X-ray fluorescence analysis (XPS). The [0 0 1]-oriented PZNT91/9 crystals cut from the middle part of the as-grown crystal boules exhibit broad dielectric-response peaks at around 105 °C, accompanied by apparent frequency dispersion. The values of piezoelectric constant d₃₃, remnant polarization P_r, and induced strain are about 1800–2200 pC/N, 38.8 μC/cm², and 0.3%, respectively, indicating that the quality of PZNT crystals grown directly from melt can be comparable to those of PZNT91/9 single crystals grown from flux. However, further work deserves attention to improve the dielectric properties of PZNT crystals grown directly from melt. Such unusual characterizations of dielectric properties of PZNT crystals grown directly from melt are considered as correlating with defects, microinhomogeneities, and polar regions.     

Influence of cooling rate on the liquid-phase epitaxial growth of Zn3P2

We report the liquid-phase epitaxial growth of Zn₃P₂ on InP (1 0 0) substrates by conventional horizontal sliding boat system using 100% In solvent. Different cooling rates of 0.2–1.0 °C/min have been adopted and the influence of supercooling on the properties of the grown epilayers is analyzed. The crystal structure and quality of the grown epilayers have been studied by X-ray diffraction and high-resolution X-ray rocking measurements, which revealed a good lattice matching between the epilayers and the substrate. The supercooling-induced morphologies and composition of the epilayers were studied by scanning electron microscopy and energy dispersive X-ray analysis. The growth rate has been calculated and found that there exists a linear dependence between the growth rate and the cooling rate. Hall measurements showed that the grown layers are unintentionally doped p-type with a carrier mobility as high as 450 cm²/V s and a carrier concentration of 2.81×10¹⁸ cm⁻³ for the layers grown from 6 °C supercooled melt from the cooling rate of 0.4 °C/min.     

Large-size β-Ga2O3 single crystals and wafers

Large-size single crystals of β-Ga₂O₃ with 1 inc in diameter have been grown by the floating zone technique. The stable growth conditions have been determined by the examination of the crystal structure. Wafers have been cut and fine polished in the (1 0 0), (0 1 0) and (0 0 1) planes. These were highly transparent in the visible and near UV, as well as electrically conductive, indicating the potential use of β-Ga₂O₃ as a substrate for optoelectic devices operating in the visible/near UV and with vertical current flow.     

Growth of NaBi(WO4)2 crystal by modified-Bridgman method

NaBi(WO₄)₂ (NBW) crystals have been grown for the first time by modified-Bridgman method. Influences of some factors on the crystal growth process are discussed. X-ray powder diffraction experiments show that the unit cell parameters of NBW crystal are a=b=0.5284 nm, c=1.1517 nm, and V=0.3215 nm³. The differential thermal analysis shows that the NBW crystal melts at 923°C.     

Growth of large dimension BaWO4 crystal by the Czochralski method

In this paper, polycrystalline materials of BaWO₄ were synthesized by solid-state phase method, and a single crystal of BaWO₄ was successfully grown along a and c-axis direction by using the Czochralski method. Up to 20×22×80 mm³ BaWO₄ crystal was obtained, and X-ray powder diffraction results show that the as-grown BaWO₄ crystal belongs to the scheelite structure. The effective segregation coefficients of Ba and W of the BaWO₄ crystal were measured by the X-ray fluorescence method, and the effective segregation coefficients of Ba and W were near 1. The rocking curve from (2 0 0) diffraction plane of as-grown BaWO₄ single crystal was measured on the High-resolution X-ray diffractometer D5005, and the full-width at half-maximum value was found to be 26.64′′ The density and hardness of the BaWO₄ crystal was measured, the measured density was in agreement with the calculated result, and the Mohs hardness was about 4.     

Growth and spectral properties of Nd-doped Sr3Y(BO3)3 crystal

A new crystal of Nd³⁺:Sr₃Y(BO₃)₃ with dimension up to 25×35 mm² was grown by Czochralski method. Absorption and emission spectra of Nd³⁺: Sr₃Y(BO₃)₃ were investigated . The absorption band at 807 nm has a FWHM of 18 nm. The absorption and emission cross sections are 2.17×10⁻²⁰ cm² at 807 nm and 1.88×10⁻¹⁹ cm² at 1060 nm, respectively. The luminescence lifetime τ_f is 73 μs at room temperature     

Growth and spectroscopic properties of Er single doped and Er–Yb co-doped YAl3(BO3)4 crystals

Er³⁺-doped and Er³⁺–Yb³⁺ co-doped yttrium aluminum borate (YAB) single crystals have been grown by the top-seeded solution growth method using a new flux system, namely NaF–MoO₃–B₂O₃. The Er³⁺ concentrations were 1.3 mol% for both single doped and co-doped crystals and the Yb³⁺ concentration in the Er³⁺–Yb³⁺ co-doped crystal was 20.0 mol% in the raw materials. The distribution coefficients of Er³⁺ single doped and Er³⁺–Yb³⁺ co-doped crystals were measured. The polarized absorption and fluorescence spectra of Er³⁺–Yb³⁺ co-doped crystal were recorded and compared with those of Er³⁺ single doped crystal. The results demonstrate that Er³⁺–Yb³⁺ co-doped YAB crystal is a potential candidate for 1.55 μm laser materials.     

Growth and spectral properties of Nd:LaVO4 crystal

This paper reports the growth and spectral properties of 3.5 at% Nd³⁺:LaVO₄ crystal with diameter of 20×15 mm² which has been grown by the Czochralski method. The spectral parameters were calculated based on Judd–Ofelt theory. The intensity parameters Ω_λ are: Ω₂=2.102×10⁻²⁰ cm², Ω₄=3.871×10⁻²⁰ cm², Ω₆=3.235×10⁻²⁰ cm². The radiative lifetime τ_r is 209 μs and calculated fluorescence branch ratios are: β₁(0.88μm)=45.2, β₂(1.06μm)=46.7, β₃(1.34μm)=8.1. The measured fluorescence lifetime τ_f is 137 μm and the quantum efficiency η is 65.6%. The absorption band at 808 nm wavelength has an FWHM of 20 nm. The absorption and emission cross sections are 3×10⁻²⁰ and 6.13×10⁻²⁰ cm², respectively.     

Improved growth of PbI2 single crystals

The phase equilibrium and the crystallization process of lead iodide (PbI₂) melt have been primarily investigated according to the lead–iodine phase diagram. It is found that the iodine evaporation and the segregated lead deposition are the two important factors that affect the PbI₂ crystal quality. The new method of Pulling U-type quartz growth ampoule has been made to impede the decomposition of PbI₂ and the vaporization and condensation of iodine. An orange and translucent PbI₂ single crystal of large size was obtained by the improved growth method, i.e. U-type ampoule pulling. Resistivity of the as-grown crystal is up to 4×10¹¹ Ω cm, and IR transmission is up to 45% in the region from 7800 to 450 cm⁻¹. Therefore, the improved growth method is a promising convenient new method for the growth of high quality PbI₂ crystals.     

Growth, dielectric, ferroelectric and optical properties of Ca0.28Ba0.72Nb2O6 single crystals

Calcium barium niobate Ca_0.28Ba_0.72Nb₂O₆ (CBN-28) crystals were grown by the Czochralski method. The effective segregation coefficients of Ca, Ba, Na elements in CBN-28 crystal growth were measured, and the rocking curve from 0 0 2 reflection of CBN-28 wafer was also measured by the high-resolution X-ray diffractometer D5005, and the full-width at half-maximum value was measured to be 70.6″. The measured dependence of dielectric constants on temperature showed the Curie temperature of the CBN-28 crystals is between 246.8 and 260 °C. Typical polarization–electric field (P–E) hysteresis loops were measured at room temperature. Ferroelectric 180° domains were observed by scanning electron microscopy (SEM) on the etched (0 0 1) surface of the CBN-28 crystals. The transmittance of [0 0 1]-oriented CBN-28 crystals was measured and the result shows that optical properties of CBN-28 crystal are almost the same as those of SBN for wavelengths between 2500 and 7500 nm.     

Synthesis, growth, thermal, optical, dielectric and mechanical properties of semi-organic NLO crystal: Potassium hydrogen malate monohydrate

Potassium hydrogen malate monohydrate (PHMM), a semi-organic nonlinear optical material, has been synthesized and single crystals were grown from aqueous solution. Single crystals of PHMM have been grown by slow evaporation of solvent at room temperature up to dimensions of 22 mm×16 mm×14 mm. Single-crystal X-ray diffraction study on grown crystals shows that they belong to monoclinic system and non-centrosymmetry spacegroup Cc. The structural perfection of the grown crystals has been analyzed by high-resolution X-ray diffraction (HRXRD) rocking curve measurements. Fourier transform infrared (FTIR) spectroscopic study was performed for the identification of different modes of functional groups present in the compound. The UV–Vis transmission spectrum has been recorded in the range 200–1100 nm. The thermal stability of the compound has been determined by TG-DTA curves. The dielectric studies were performed. From the microhardness measurements, Vicker's hardness number (H_v), Stiffness constant (C₁₁), fracture toughness (k_c), Brittle index (B_i) and yield strength (σ_y) have been calculated. The Young's modulus was calculated using the Knoop hardness measurement. The SHG relative efficiency of PHMM crystal was found to be 1.2 times higher than that of KDP.     

Structural, thermal and dielectric studies on a new solution grown 4-dimethylaminopyridinium dihydrogen phosphate crystal

Single crystals of 4-dimethylaminopyridinium dihydrogen phosphate (DMAPDP) (C₇H₁₃N₂PO₄) were grown by the solvent evaporation method. The three-dimensional structure was solved by the single-crystal X-ray diffraction method which belongs to triclinic crystal system and the molecular arrangements in the crystal were studied. The thermal behaviour was investigated using differential scanning calorimetry (DSC) and no phase transition was identified in the temperature region −150 to 230 °C. The thermal parameters—thermal diffusivity (), thermal effusivity (e), thermal conductivity (K) and heat capacity (C_p) of DMAPDP were measured by an improved photopyroelectric technique at room temperature. Dielectric constant and dielectric loss of the grown crystal were evaluated for the frequency range 1–200 KHz in the temperature region 28–135 °C. The Vicker's hardness was measured as 42.2 for a load of 98.07 mN. The laser induced surface damage threshold of DMAPDP crystal was found to be 4.8 GW/cm² with nanosecond Nd:YAG laser.     

Growth and characterization of CdSe single crystals by modified vertical vapor phase method

Good quality, large single crystals of CdSe were grown by the modified growth method (i.e., vertical unseeded vapor phase growth with multi-step purification of the starting material in the same quartz ampoule without any manual transfer between the steps). Lower temperature gradients (8–9°C/cm) at the growth interface were used for the crystal growth. As-grown CdSe crystals was characterized by X-ray diffraction, scanning electron microscopy, energy dispersive analyzer of X-rays, high-resistance instrument measurement, and etch-pit observation. It is found that there are two cleavage faces of (1 0 0) and (1 1 0) orientations on the crystal, the resistivity is about 10⁸ Ω cm, and the density of etch pits is about 10^3–4/cm². The crystal was cut into wafers and was fabricated into detectors. The detectors were tested using an ²⁴¹Am radiation source. γ-ray spectra at 59.5 keV were obtained. The results demonstrated that the quality of the as-grown crystals was good. The crystals were useful for fabrication of room-temperature-operating nuclear radiation detectors. Therefore, the modified growth technique is a promising, convenient, new method for the growth of high-quality CdSe single crystals.     

Crystal growth of Ce: PrF3 by micro-pulling-down method

Micro-pulling-down (μ-PD) growth apparatus was modified for fluoride crystals. PrF₃ was grown with various concentrations of Ce³⁺ from 0–100%. The crystals were transparent and colorless (CeF₃) or greenish and 3 mm in diameter and 15–50 mm in length. Neither visible inclusions nor cracks were observed. Radioluminescence spectra and decay kinetics were measured for the sample set at room temperature. In comparison to the Czochralski or Bridgman method, the μ-PD method allows to produce single crystalline material in a faster thus more economic way. Once it is established for the fluoride crystals, it is an efficient tool for exploring the field of new functional fluorides.     

Phase diagram of the SrS–Ga2S3 system and its application to the single-crystal growth of SrGa2S4

Ce-doped SrGa₂S₄ compound is expected as a new host material of blue EL devices. However, the basic properties of bulk single crystals have not been fully clarified, since this compound has been mostly synthesized in the form of polycrystals or thin films. Here, we firstly present the pseudo-binary phase diagram of the SrS–Ga₂S₃ system constructed in accordance with our DTA data for single-crystal growth of SrGa₂S₄. It is shown that SrGa₂S₄ compound has a congruent melting point and a eutectic reaction in the side of excess of Ga₂S₃ concentration. On the basis of the phase diagram, single crystals of SrGa₂S₄ are grown using Ga₂S₃ as a self-flux in a horizontal Bridgman furnace. Colorless and transparent crystals having a typical size 2×2×2 mm³ are obtained.     

The growth and spectroscopic characteristics of Ca3Y2(BO3)4:Er laser crystal

The Ca₃Y₂(BO₃)₄:Er³⁺ crystal with a size up to 20 mm×30 mm was grown by the Czochralski method. The absorption spectrum was measured and its absorption peaks were assigned to the corresponding transitions between the Er³⁺ energy levels. A broad emission spectrum from 1429.4 to 1662.8 nm was exhibited from 530 nm wavelength pumping. This crystal is promising as a tunable infrared laser crystal.