丙烯酸及其接枝物对纳米CaCO3/PP结晶与熔融行为的影响

制备了丙烯酸(AA)及其接枝聚丙烯(PP—g-AA)改性的纳米CaC03／PP复合材料。用DSC研究了纳米CaCO3对PP、PP-g-A和AA对纳米CaCO3／PP中PP结晶与熔融行为的影响。结果表明：随纳米CaCO3用量增加，PP结晶与熔融温度提高，PP—g—AA加入使PP结晶温度进一步提高，PP的结晶温度也随从用量增加而提高；在过氧化二异丙苯(DCP)存在下，少量AA能明显提高PP的结晶温度，但增加从用量对结晶温度的影响较小；WAXD证实纳米CaCO3／PP复合材料中存在β晶。     

多组分单体接枝聚丙烯/尼龙6反应共混物结晶行为研究

用多组分熔融接枝的方法将甲基丙烯酸缩水甘油酯 (GMA)和苯乙烯 (St)共同接枝到聚丙烯 (PP)上 ,制得具有较高GMA接枝率的多单体接枝聚丙烯 ,PP g (GMA co St) .将PP g (GMA co St)与尼龙 6 (PA6 )进行共混 ,利用扫描电镜 (SEM) ,差示扫描量热计 (DSC)和广角X射线衍射 (WAXD)对共混物的形态和结晶进行了研究 .在共混过程中 ,PP g (GMA co St)与PA6反应原位生成了PP g PA6 ,有效改善了共混物的相容性 ,分散相尺寸明显减小 .在PP g (GMA co St) PA6为 3 7的体系中 ,PP g (GMA co St)出现分级结晶现象 ,其在较低温度下的结晶属于均相成核结晶 .在PP g (GMA co St) PA6为 7 3的体系中 ,由于PA6相分散细微 ,在通常结晶温度下不结晶 ,而是在低温下均相成核与PP g (GMA co St)同时结晶 .WAXD证实体系中接枝PP ,PA6为分别结晶 ,无共晶或新的晶型产生     

马来酸酐接枝热塑性弹性体在PP/PA6共混物中的作用

研究了马来酸酐接枝热塑性弹性体 (TPEg )作为增容剂对聚丙烯 (PP) 尼龙 6 (PA6 )共混体系的相容性、相态以及物理力学性能的影响 .研究结果表明TPEg的加入大大改善了PP PA6共混体系的相容性 ,且随TPEg含量的增大分散相粒径明显降低 ,共混物的韧性以及延展性大大提高 ,同时拉伸强度及模量仍保持较好的水平 .TPEg增容的PP PA6共混物的非等温结晶行为的研究表明 ,共混物中PP和PA6的结晶行为不同于各自纯的聚合物 ,PA6作为成核剂使PP的结晶温度提高 ;而PA6由于TPEg的加入 ,出现分级结晶现象 ,一级结晶温度略低于纯PA6的结晶温度 ,且随TPEg含量增大结晶受阻 ,二级结晶温度与PP的接近 .由于PP、PA 6以及TPEg之间存在较强的相互作用 ,三元共混物中PP及PA6的玻璃化转变温度分别较其纯聚合物升高 .基于上述结果 ,提出了本共混体系的结构模型     

多组份聚丙烯共混物的微观结构及共混纤维的染色性能

研究了PP GPET、PP GPET EVA、PP GPET EVA PS共混物的结构和性能 .研究表明 ,PP GPET体系属于非相容共混体系 ,共混物呈典型海岛型两相结构 ,EVA的加入可以改善体系相容性 ;共混物的结晶度比纯聚丙烯低 ,PS有增大共混物晶粒尺寸的作用 ;改性聚丙烯纤维的染色性有明显提高 ,用分散染料E EX可染成深蓝色     

大分子相容剂改性Mg(OH)2/PP阻燃材料的性能

用双螺杆挤出机熔融挤出法制备了相容剂改性氢氧化镁/聚丙烯[Mg(OH)2/PP]阻燃材料。研究了马来酸酐接枝聚丙烯(PP-g-MA),马来酸酐接枝(乙烯/辛烯)共聚物(POE-g-MA)和马来酸酐接枝聚醋酸乙烯酯(EVA-g-MA)3种大分子相容剂对阻燃材料的熔体流动性、结晶行为、力学性能和断口形态的影响。结果表明:相容剂PP-g-MA和POE-g-MA的加入使阻燃材料的熔体流动速率降低,PP结晶温度提高,EVA-g-MA的加入使阻燃材料熔体流动速率数提高;Mg(OH)2对PP结晶存在异相成核作用,Mg(OH)2的加入使PP的冲击强度、拉伸强度和断裂伸长率降低,杨氏模量提高;相容剂改性后Mg(OH)2/PP阻燃材料的拉伸强度提高,其中以PP-g-MA最为明显,而POE-g-MA则提高了阻燃材料的冲击强度。     

PP—g—（GMA—co—St）对PA6—PC共混合的反应增容作用

用红外、扫描电镜、熔体流动速率和力学性能等测试方法,研究了甲基丙烯酸缩水甘油酯（GMA）和苯乙烯（St）多单体熔融接枝聚丙烯PP－g-(GMA-co-St)对PA6－PC共混合的反应增容作用。研究结果表明,在熔融共混过程中,PP－g-(GMA-co-St)中的环氧基与PA6的端氨基及PC的端羟基原位生成的接枝共聚物就有效地降低了共混物相间的界面张力,明显提高了共混物相界面的粘着力。少量的PP－g-(GMA-co-St)就能使PA6和PC的相容性得到显著改善。当PP－g-(GMA-co-St)的质量分数为10％时,共混物分散相的相区尺寸细化到0．2μm,其力学性能也有较大提高。PA6／PC／PP－g-(GMA-co-St)共混物的力学性能均衡,达到了弹性体增韧体系难以达到的效果。即使PP－g-(GMA-co-St)组分含量为20％时,共混物仍能保持较好的力学性能,特别是在共混物地韧性得以提高的同时,其强度和伸长率也提高。     

PP-g-MAEu离聚物的合成与表征

以过氧化二异丙苯(DCPO)为引发剂,将马来酸铕(MAEu)熔融接枝到聚丙烯上,合成不同接枝率的PP-g-MAEu离聚物,考察了反应时间、引发剂浓度、单体用量对接枝率的影响,在离聚物的1540～1643 cm-1之间的宽峰说明MAEu与PP发生了接枝反应;利用WAXD, POM和DSC考察了PP及其接枝物的结晶行为, PP-g-MAEu能促进β-型结晶的形成,接枝物的起始结晶温度移向高温,结晶速率加快,接枝物形成的球晶尺寸变小,而且球晶不规整;荧光光谱的结果表明PP-g-MAEu离聚物是一种单色性好、亮度高的稀土高分子光致发光材料.     

聚丙烯/插层改性水滑石纳米复合材料结构与性能研究

采用离子交换法制备了十二烷基磺酸钠和衣康酸共同改性水滑石(LDHs2),FTIR、XRD分析表明,十二烷基磺酸钠和衣康酸能够同时进入水滑石片层之间,层间距有很大提高。利用改性水滑石,通过马来酸酐-苯乙烯共接枝改性聚丙烯相容剂的熔融共混和聚丙烯与水滑石溶液共混制备母粒,然后与聚丙烯分别熔融共混两种方法制备聚丙烯/水滑石纳米复合材料。TEM分析表明,马来酸酐-苯乙烯共接枝改性聚丙烯作相容剂可以使水滑石在聚丙烯基体中达到更好分散。DSC、XRD分析表明,水滑石、相容剂以及短链共聚聚丙烯对聚丙烯晶型没有影响,但对其结晶速率、结晶度以及晶粒大小有所改变,复合材料中聚丙烯的起始结晶温度、结晶峰温度、结晶速率、结晶度均比纯聚丙烯高,晶粒粒径分布也更均匀。     

纳米碳酸钙微粒填充改性聚丙烯复合材料的力学性能和结晶行为研究

研究了两种不同粒径的纳米碳酸钙(Nano-CaCO3)熔融共混改性均聚聚丙烯(PP)材料的力学性能和结晶行为，结果表明，两种纳米CaCO3填料对PP的B晶形成均有不同程度的诱导作用，并可提高基体结晶温度和结晶速率，从而提高材料的冲击韧性．     

马来酸酐-苯乙烯熔融接枝聚丙烯的影响因素及其性能研究

用单螺杆挤出机制备了马来酸酐 (MAH) 苯乙烯 (St)对聚丙烯 (PP)的多组分单体自由基熔融接枝体系 .研究证实了当两种单体物质的量比约为 1∶1时 ,接枝物的接枝率最高 ,而熔体流动速率 (MFR)最大 .对反应体系影响因素的研究表明单体用量和引发剂用量对不同单体用量比的系列接枝物的接枝率会产生不同的影响 ;另外 ,单体用量增加 ,接枝物的MFR减小 ,过氧化二异丙苯 (DCP)用量增加 ,接枝物的MFR增加 .对多单体熔融接枝聚丙烯PP g (MAH co St)的力学性能研究发现 ,选用合适的单体用量比、单体用量和DCP用量时 ,所制备的接枝物可具有与纯PP相当或更佳的力学性能     

The effect of organoclay and graphene on the crystallization of PP in ABS/PP blends

In the present research, the isothermal and non-isothermal crystallization of polypropylene (PP) phase in PP-rich poly(acrylonitrile–butadiene–styrene)/polypropylene (ABS/PP) blends was studied. The effect of nanofillers’ incorporation and specialty of organically modified montmorillonite (OMMT) and graphene, into the prepared blends on the isothermal and non-isothermal crystallization of PP phase, were investigated. Moreover, kinetic study of their isothermal crystallization process was carried out, by applying the Avrami equation. The addition of ABS to the PP matrix increased the crystallization rate of PP at 130 °C. The incorporation of OMMT in pure PP accelerated slightly the crystallization process, whereas in ABS/PP blends, it seemed to retard crystallization, due to interactions between ABS phase and organoclay. The incorporation of graphene in pure PP accelerated impressively its isothermal crystallization, while the addition of ABS in graphene/PP nanocomposite slowed down the crystallization rate of PP. The effect of ABS and nanofillers, separately or in combination, on the crystallization of PP phase was reflected on the kinetic parameters of the Avrami equation. Regarding the non-isothermal crystallization, ABS/PP blends presented higher crystallization temperature (T _c) compared to pure PP. The organoclay reinforcement did not have any obvious effect on this temperature, whereas graphene caused significant increase, acting as nucleating agent. The presence of ABS to PP increased the concentration of the β-crystalline phase, reaching its maximum value at 30 mass% ABS content. The organoclay decreased the β-PP in ABS/PP blends, whereas graphene eliminated it.     

Studies on partial compatibility of PP and PS

<正>Blends of polystyrene(PS) and polypropylene(PP) were prepared through melt compounding.With an increase of PS content up to 30 wt%,the tensile strength of PP/PS blends increased from 37.4 MPa to 42.2 MPa,although the blends were widely regarded as immiscible.The DSC results showed that there's slight decrease in melting temperature of PP, showing insufficient evidence for partial compatibility between PP and PS.Almost no variation of distinct characterization peaks were observed in FTIR spectra of PS/PP blends compared with those of neat PP and PS,indicating there is no chemical interactions between PP and PS.Since the morphology investigation showed a droplet structure as PS content was up to 30 wt%,the improvement of tensile strength could be simply considered as due to the reinforcing effect of dispersed rigid PS particles on the PP,combining with partial compatibility between them as evaluated by change of C_p at glass transition for both PS and PP.More interestingly,DSC and DMA results showed that the blending of PS and PP could lead to a substantial decrease of the glass transition temperature(T_g) of PP,and increase of T_g of PS.The annealing experiment was carried out to understand the change of T_g in PP/PS blends.It is believed that the compressive stress generated by the contracting PP should be the dominant mechanism for the T_g elevation of PS.On the other hand,the T_g decrease of PP is likely owing to the creation of a large amount free interface of PP and the dilatation of the PP phase resulting from the corresponding tension exerted by PS during cooling.     

Modification of PP by blending with PS and reactive polymers

In this paper a polypropylene (PP) resin with controlled rheology was selected as polymer matrix and modified by melt mixing with polystyrene (PS) which has certain processing compatibility with PP. The effect of the addition of polyperoxide (PPX), peroxide modified PS particles (PS‐PPX), and maleic anhydride (MAH) to the PP/PS blend during melt mixing on the rheological behavior and morphology of the PP/PS blends has been carefully studied.     

Thermogravimetric analysis and differential scanning calorimetric studies on nanoclay-filled TPU/PP blends

Thermal stability of ester-thermoplastic polyurethane (TPU)/polypropylene (PP) and ether-TPU/PP blends was evaluated by thermogravimetric studies. Thermal studies were made as a function of blend ratio. Effects of compatibilization using MA-g-PP and nanoclay addition on thermal stability were evaluated. Mass loss at 400 °C was found to decrease with increasing PP content were determined. Finally the compatibility and crystallization behavior of the blends were studied by differential scanning calorimetry. Compared to the ether-TPU blend nanocomposites, the ester-TPU blends showed better compatibility and thermal stability.     

HIPS／PP熔融反应共混及其动态力学性质

研究了高抗冲聚苯乙烯（HIPS）／聚丙烯（PP）共混物在过氧化二异丙苯（DCP）存在下的熔融反应过程及其动态力学性质．HIPS在DCP存在下以聚苯乙烯（PS）的降解为主，伴随着聚丁二烯（PB）的交联和接枝，PP在DCP存在下以降解为主，HIPS／PP在DCP存在下以PP同HIPS的反应接枝为主，这种原位生成的增容剂显著地改善了HIPS／PP两组份间的相容性，其分子运动特征较前两者发生明显变化，PS的Tg下降，PB和PP的Tg升高．     

Synthesis and characterization of polyethylene‐g‐polystyrene as the compatibilizer for polypropylene/ Polystyrene blends

Polyethylene‐g‐polystyrene (PE‐g‐PS) was synthesized as a compatibilizer for polypropylene/polystyrene­(PP/PS) blends by the living radical polymerization of styrene with polyethylene‐co‐glycidylmethacrylate (PE‐co‐GMA). The compatibilizer effect of PE‐g‐PS on the morphology and thermal properties of PP/PS blends was investigated. The crystalline temperature of PP in PP/PS blends decreased with increasing PE‐g‐PS contents. Morphologies of PP/PE‐g‐PS/PS blends showed much better dispersion of each domain for higher PE‐g‐PS contents. The molecular weight of PS segment in PP/PE‐g‐PS/PS blend was increased by addition of styrene monomer during the post melt blending process where post living radical polymerization reaction proceeded. Copyright © 2003 John Wiley & Sons, Ltd.     

1,6-己二醇二丙烯酸酯和苯乙烯多单体熔融接枝制备长支链聚丙烯研究

采用哈克转矩流变仪制备了1,6-己二醇二丙烯酸酯(HDDA)和苯乙烯(St)多单体熔融接枝聚丙烯(PP)体系.红外测试结果表明St的加入能够促进HDDA接枝到PP主链,提高接枝率.动态流变行为研究结果也表明采用多单体熔融接枝PP更有利于体系在熔融接枝中生成长支链(LCB).随着St单体添加量的增加,HDDA的接枝率增大...     

超细CaCO_3的粒子尺寸对PP结晶行为的影响

The effects of CaCO3 on the crystallization behavior of polypropylene (PP) were studied by means of DSC and WAXD.The average sizes of the CaCO3 powders used were 0.1μm (UC) and 0.5μm (GC),respectively.The PP/CaCO3 composites at compositions of 1phr and 10 phr were investigated.The results showed that the addition of CaCO3 reduced the supercooling,the rate of nucleation and the overall rate of crystallization (except for the 10phr UC/PP sample).The crystallinity of PP was increased and the size distribution of the crystallites of α-PP was broadened.On the other hand,the crystallization rate of 10phr UC/PP is 1.5 times higher than that of neat PP.It has an overall rate of crystallization 2 times as much as that of the neat PP and has the maximum crystallinity.The sizes of crystallites and the unit cell parameters of α-PP were varied by the addition of CaCO3.β-PP was formed by addition of GC and was not detected by addition of UC.The differences of crystallization behaviors of PP might be attributed to the combined effects of the content and size of CaCO3 filled.