A novel method to fabricate lithium-ion polymer batteries based on LiMn<Subscript>2</Subscript>O<Subscript>4</Subscript>/NG electrodes

A novel method to fabricate lithium-ion polymer batteries (LiPBs) has been developed. The LiPBs was fabricated without microporous polyolefin separators, taking spinel lithium manganese oxide (LiMn₂O₄) and natural graphite (NG) as the electrodes. The thicknesses of the cathodes and the anodes are 190 and 110 μm, respectively. The NG anode was coated with a microporous composite polymer film (20 μm thick) which composed of polymer and ultrafine particles. The coating process was effective and simple to be used in practical application, and ensured the composite polymer film to act as a good separator in the LiPB. The LiPBs assembled with the coated NG anodes and pristine LiMn₂O₄ cathodes presented better electrochemical performances than liquid lithium-ion battery counterparts, proving that the microporous composite polymer film can improve the performance of the coated NG anode. In this paper, the spinel LiMn₂O₄/(coated)NG-based LiPBs exhibited high rate capability, compliant temperature reliability, and significantly, excellent cycling performance under the elevated temperature (55°C).     

Analysis of the temperature dependence of the high-frequency EMR spectra of Mn ions in the lithium-ion battery material LiMn<Subscript>2</Subscript>O<Subscript>4</Subscript>

This paper deals with the analysis of the temperature dependence of high-frequency EMR (HF-EMR) spectra due to Mn³⁺ and Mn⁴⁺ ions in the lithium manganese spinel LiMn₂O₄. A range of powder samples obtained by the sol-gel method with calcinations in several temperature ranges were prepared for this study. Based on the initial characterization carried out by a number of techniques, the physicochemical and structural properties of the samples were earlier determined. Independently, temperature magnetization and HF-EMR measurements were carried out. The EMR spectra vary strongly between samples, indicating possible structural or chemical changes. Quantitative analysis of the temperature dependence of the HF-EMR spectra due to Mn³⁺ and Mn⁴⁺ ions in LiMn₂O₄ is presented in this paper. The spectral analysis concerns the line shape, linewidth, intensity and g-factors. Fittings using the Lorentzian spectral shape and, to a certain extent, the Gaussian spectral shape have been carried out in order to parameterize the temperature dependence of the HF-EMR spectra. This parameterization of the HF-EMR experimental data enables a deeper characterization of the samples. Subsequently, a better insight into the role of the Mn³⁺ and Mn⁴⁺ ions in accounting for the characteristics most suitable for application of LiMn₂O₄ as a cathode material may be gained.     

LiMn<Subscript>2</Subscript>O<Subscript>4</Subscript> and LiCoO<Subscript>2</Subscript> composite cathode materials obtained by mechanical activation

New composite cathode materials xLiMn₂O₄/(1 ? x) LiCoO₂(x = 0.7, 0.6, 0.5 и 0.4) were obtained by mechanical activation. According to scanning electron microscopy data, the process was accompanied by pronounced dispersion and fine mixing of the initial components. In the course of the preparation and electrochemical cycling of the composites, LiMn₂O₄ and LiCoO₂ partially reacted, leading to the replacement of manganese with cobalt in the structure of spinel, which was detected by powder X-ray diffraction (XRD), IR and X-ray photoelectron spectroscopy (XPS), and cyclic chronopotentiometry. The specific discharge capacity of composites was ～100 mAh/g.     

Synthesis and electrochemical properties of yttrium-doped LiMn<Subscript>0.98</Subscript>Y<Subscript>0.02</Subscript>O<Subscript>2</Subscript> for lithium secondary batteries

Yttrium-doped lithium manganese oxide (LiMn_0.98Y_0.02O₂) was prepared by ion exchange of lithium for sodium in NaMn_0.98Y_0.02O₂ precursors obtained by using rheological phase reaction method. This material had small particle size, which was composed of grain size of about 100 nm. Especially, LiMn_0.98Y_0.02O₂ delivered the initial discharge capacity of about 191 mA h g⁻¹ at room temperature when cycled between 2.0 and 4.4 V vs Li/Li⁺. Moreover, it showed an excellent cycling behavior, its specific capacity remained above 173 mA h g⁻¹ after 20 cycles, and the material did not transform into spinel structure during the electrochemical cycling according to the cyclic voltammograms and X-ray powder diffraction. The electrochemical results revealed that the doping of Y³⁺ improved the performance of LiMnO₂ considerably.     

Effects of Ni-ion doping on electrochemical characteristics of spinel LiMn<Subscript>2</Subscript>O<Subscript>4</Subscript> powders prepared by a spray-drying method

Spinel LiMn_2−x Ni _x O₄ compounds doped with a range of Ni (x=0–0.06) were synthesized by a spray-drying method. The structure and morphology characteristics of the powders were studied in detail by means of X-ray diffraction (XRD), scanning electron microscopy, and transmission electron microscopy. The XRD data reveal that all the samples have well-defined spinel structure, but, with the increase in Ni content, the doped lithium manganese spinels have smaller lattice constant. The undoped and doped spinel LiMn₂O₄ particles are fine, narrowly distributed, and well crystallized. The electrochemical characteristics of the samples are measured in the coin-type cells in a potential range of 3.2–4.35 V vs Li/Li⁺. All cyclic voltammogram curves exhibit two pairs of redox reaction peaks, but, among them, there are some differences about the peak split. With the increase in the Ni content, the specific capacities of the samples decrease slightly, but their cyclic ability increases.     

Preparation and characterization of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript>composite particles

Using Fe₃O₄ nano-particles as seeds, a new type of Fe₃O₄/Au composite particles with core/shell structure and diameter of about 170 nm was prepared by reduction of Au³⁺ with hydroxylamine in an aqueous solution. Particle size analyzer and transmission electron microscope were used to analyze the size distribution and microstructure of the particles in different conditions. The result showed that the magnetically responsive property and suspension stability of Fe₃O₄ seeds as well as reduction conditions of Au³⁺to Au⁰are the main factors which are crucial for obtaining a colloid of the Fe₃O₄/Au composite particles with uniform particle dispersion, excellent stability, homogeneity in particle sizes, and effective response to an external magnet in aqueous suspension solutions. UV-Vis analysis revealed that there is a characteristic peak of Fe₃O₄/Au fluid. For particles with d(0.5)=168 nm, the λmax is 625 nm.     

Preparation of novel visible-light-driven In<Subscript>2</Subscript>O<Subscript>3</Subscript>–CaIn<Subscript>2</Subscript>O<Subscript>4</Subscript> composite photocatalyst by sol–gel method

Novel visible-light-activated In₂O₃–CaIn₂O₄ photocatalysts were developed in this paper through a sol–gel method. The photocatalytic activities of In₂O₃–CaIn₂O₄ composite photocatalysts were investigated based on the decomposition of methyl orange under visible light irradiation (λ > 400 nm). The obtained samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectrum (EDS), X-ray photoelectron spectroscopy (XPS) and UV–vis diffused reflectance spectroscopy (DRS). The results revealed that the In₂O₃–CaIn₂O₄ composite samples with different In₂O₃ and CaIn₂O₄ content can be obtained by controlling the synthesis temperature, and the composite photocatalysts extended the light absorption spectrum toward the visible region. The photocatalytic tests indicated that the composite samples demonstrated high visible-light activity for decomposition of methyl orange. The significant enhancement in the In₂O₃–CaIn₂O₄ photo-activity under visible light irradiation can be ascribed to the efficient separation of photo-generated carriers in the In₂O₃ and CaIn₂O₄ coupling semiconductors.     

Hydrothermal synthesis and thermodynamic properties of 2CaO·3B<Subscript>2</Subscript>O<Subscript>3</Subscript>·H<Subscript>2</Subscript>O

2CaO·3B₂O₃·H₂O which has non-linear optical (NLO) property was synthesized under hydrothermal condition and identified by XRD, FTIR and TG as well as by chemical analysis. The molar enthalpy of solution of 2CaO·3B₂O₃·H₂O in HCl·54.572H₂O was determined. From a combination of this result with measured enthalpies of solution of H₃BO₃ in HCl·54.501H₂O and of CaO in (HCl+H₃BO₃) solution, together with the standard molar enthalpies of formation of CaO(s), H₃BO₃(s), and H₂O(l), the standard molar enthalpy of formation of −(5733.7±5.2) kJ mol⁻¹ of 2CaO·3B₂O₃·H₂O was obtained. Thermodynamic properties of this compound were also calculated by a group contribution method.     

2-pyrrolidone - capped Mn<Subscript>3</Subscript>O<Subscript>4</Subscript> nanocrystals

Water-soluble Mn₃O₄ nanocrystals have been prepared through thermal decomposition in a high temperature boiling solvent, 2-pyrrolidone. The final product was characterized with XRD, SEM, TEM, FTIR and Zeta Potential measurements. Average crystallite size was calculated as ∼15 nm using XRD peak broadening. TEM analysis revealed spherical nanoparticles with an average diameter of 14±0.4 nm. FTIR analysis indicated that 2-pyrrolidone coordinates with the Mn₃O₄ nanocrystals only via O from the carbonyl group, thus confining their growth and protecting their surfaces from interaction with neighboring particles.      

Thermal oxide synthesis and characterization of Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> nanorods and Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> nanowires

Fe₃O₄ nanorods and Fe₂O₃ nanowires have been synthesized through a simple thermal oxide reaction of Fe with C₂H₂O₄ solution at 200–600°C for 1 h in the air. The morphology and structure of Fe₃O₄ nanorods and Fe₂O₃ nanowires were detected with powder X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The influence of temperature on the morphology development was experimentally investigated. The results show that the polycrystals Fe₃O₄ nanorods with cubic structure and the average diameter of 0.5–0.8 μm grow after reaction at 200–500°C for 1 h in the air. When the temperature was 600°C, the samples completely became Fe₂O₃ nanowires with hexagonal structure. It was found that C₂H₂O₄ molecules had a significant effect on the formation of Fe₃O₄ nanorods. A possible mechanism was also proposed to account for the growth of these Fe₃O₄ nanorods. Supported by the Fund of Weinan Teacher’s University (Grant No. 08YKZ008), the National Natural Science Foundation of China (Grant No. 20573072) and the Doctoral Fund of Ministry of Education of China (Grant No. 20060718010)     

Synthesis and characterization of submicron size particles of LiMn<Subscript>2</Subscript>O<Subscript>4</Subscript> by microemulsion route

Among the various positive electrode materials investigated for Li-ion batteries, spinel LiMn₂O₄ is one of the most important materials. Small particles of the active materials facilitate high-rate capability due to large surface to mass ratio and small diffusion path length. The present work involves the synthesis of submicron size particles of LiMn₂O₄ in a quaternary microemulsion medium. The precursor obtained from the reaction is heated at different temperatures in the range from 400 to 900 °C. The samples heated at 800 and 900 °C are found to possess pure spinel phase with particle size <200 nm, as evidenced from XRD, SEM, and TEM studies. The electrochemical characterization studies provide discharge capacity values of about 100 mAh g⁻¹ at C/5 rate, and there is a moderate decrease in capacity by increasing the rate of charge–discharge cycling. Studies also include charge–discharge cycling and ac impedance studies in temperature range from −10 to 40 °C. Impedance data are analyzed with the help of an equivalent circuit and a nonlinear least squares fitting program. From temperature dependence of charge-transfer resistance, a value of 0.62 eV is obtained for the activation energy of Mn³⁺/Mn⁴⁺ redox process, which accompanies the intercalation/deintercalation of the Li⁺ ion in LiMn₂O₄.     

An electrochemical investigation on (MoO<Subscript>3</Subscript>+PVP+PVA) nanobelts for lithium batteries

Molybdenum trioxide (MoO₃) xerogel films modified with poly(vinyl alcohol)+poly(vinyl pyrrolidone) (PVP+PVA) polyblends were obtained by ion-exchange method with sol-gel technique. Investigations were conducted using X-ray “diffractometry”, Fourier transform infrared spectroscopy, and cyclic voltammetry. The results show that the H atoms in polyblend are H-bonded with the O atoms in the Mo=O bonds of MoO₃ xerogel, which effectively shield the electrostatic interaction between MoO₃ interlayer and Li⁺ ions when MoO₃ xerogel is modified by the intercalation of (PVP+PVA). The reversibility of the insertion/extraction of Li⁺ ions is greatly improved by the modification with polyblend of MoO₃ nanocomposite films. MoO₃ and (PVP+PVA) _x MoO₃ (x = 0, 0.5) nanobelts were obtained by a simple hydrothermal process from MoO₃ sol. The electrochemical cells with configuration Li/(LiPF₆+EC+DMC)/MoO₃ modified by (PVP+PVA) were fabricated and their discharge profiles studied.     

Preparation of Ca<Subscript>3</Subscript>Co<Subscript>4</Subscript>O<Subscript>9</Subscript> by polyacrylamide gel processing and its thermoelectric properties

Ca₃Co₄O₉ powder was prepared by a polyacrylamide gel route in this paper. The effect of the processing on microstructure and thermoelectric properties of Ca₃Co₄O₉ ceramics via spark plasma sintering were investigated. Electrical measurement shows that the Seebeck coefficient and conductivity are 170 μV/K and 128 S/cm, respectively, at 700 °C, yielding a power factor value of 3.70 × 10⁻⁴ W m⁻¹ K⁻² at 700 °C, which is larger than that of Ca₃Co₄O₉ ceramics via solid-state reaction processing. The polyacrylamide gel processing is a fast, cheap, reproducible and easily scaled up chemical route to improve the thermoelectric properties of Ca₃Co₄O₉ ceramics by preparing the homogeneous and pure Ca₃Co₄O₉ phase.     

Phase relations in the CoO–V<Subscript>2</Subscript>O<Subscript>5</Subscript>–Fe<Subscript>2</Subscript>O<Subscript>3</Subscript> system in subsolidus area

Thermal properties of Co₂FeV₃O₁₁ have been reinvestigated. It has been proved that this compound does not exhibit polymorphism. It melts incongruently at the temperature of 770±5°C and the phase with lyonsite type structure is the solid product of this melting. Phase relations in the whole subsolidus area of the CoO–V₂O₅–Fe₂O₃ system have been determined. The solidus area projection onto the component concentration triangle plane of this system has been constructed using the DTA and XRD methods. 15 subsidiary subsystems can be distinguished in this system.     

Synthesis and electrochemical properties of Ca-doped LiNi<Subscript>0.8</Subscript>Co<Subscript>0.2</Subscript>O<Subscript>2</Subscript> cathode material for lithium ion battery

LiNi_0.8Co_0.2O₂ and Ca-doped LiNi_0.8Co_0.2O₂ cathode materials have been synthesized via a rheological phase reaction method. X-ray diffraction studies show that the Ca-doped material, and also the discharged electrode, maintains a hexagonal structure even when cycled in the range of 3.0–4.35 V (vs Li⁺/Li) after 100 cycles. Electrochemical tests show that Ca doping significantly improves the reversible capacity and cyclability. The improvement is attributed to the formation of defects caused by the partial occupancy of Ca²⁺ ions in lithium lattice sites, which reduce the resistance and thus improve the electrochemical properties.     

Li<Subscript>0.99</Subscript>Ti<Subscript>0.01</Subscript>FePO<Subscript>4</Subscript>/C composite as cathode material for lithium ion battery

Three kinds of LiFePO₄ materials, mixed with carbon (as LiFePO₄/C), doped with Ti (as Li_0.99Ti_0.01FePO₄), and treated both ways (as Li_0.99Ti_0.01FePO₄/C composite), were synthesized via ball milling by solid-state reaction method. The crystal structure and electrochemical behavior of the materials were investigated using X-ray diffraction, SEM, TEM, cyclic voltammetry, and charge/discharge cycle measurements. It was found that the electrochemical behavior of LiFePO₄ could be increased by carbon coating and Ti-doping methods. Among the materials, Li_0.99Ti_0.01FePO₄/C composite presents the best electrochemical behavior, with an initial discharge capacity of 154.5 mAh/g at a discharge rate of 0.2 C, and long charge/discharge cycle life. After 120 cycles, its capacity remains at 92% of the initial capacity. The Li_0.99Ti_0.01FePO₄/C composite developed here can be used as the cathode material for lithium ion batteries.     

Magnetorheological characteristics of aqueous suspensions that contain Fe<Subscript>3</Subscript>O<Subscript>4</Subscript> nanoparticles

This investigation examines the magnetorheological (MR) characteristics of Fe₃O₄ aqueous suspensions. Magnetite particles (Fe₃O₄) were synthesized using a colloidal process and their sizes were determined to be normally distributed with an average of 10 nm by TEM. Experimental results reveal that the MR effect increases with the magnetic field and suspension concentration. The yield stress increases by up to two orders of magnitude when the sample is subjected to a magnetic field of 146 Oe/mm. In comparison with other published results, concerning a concentration of approximately 10–15% v/v, this study demonstrates that the same increase can be obtained with a concentration of nano-scale particles as low as 0.04% by volume. The viscosity was increased by an order of magnitude while the shear rate remained low; however, the increase decayed rapidly as the shear rate was raised. Finally, the MR effect caused by DC outperformed that caused by AC at the same current.     

Electronic structure and chemical bonding in K<Subscript>2</Subscript>V<Subscript>3</Subscript>O<Subscript>8</Subscript>

The calculations of the electronic structure of layered polyvanadate K₂V₃O₈ were made employing the spin-polarized tight-binding LMTO method. Calculated magnetic moment for K₄V₆O₁₆ compound phase equals 1.97 μ_B. V-O interactions were established to be dominating in the chemical bonding generation in this polyvanadate according to the estimated crystal orbital overlap population. The covalent bonds V(2)-V(2) in V(2)₂O₇ groups and electron density localization on vanadium atoms in isolated pyramids V(1)O₅ were found.     

Quantum-chemical modelling of nanotubes of titanium silicocarbides Ti<Subscript>2</Subscript>SiC,Ti<Subscript>3</Subscript>SiC<Subscript>2</Subscript>, and Ti<Subscript>4</Subscript>SiC<Subscript>3</Subscript>

Atomic models are proposed for nanotubes of the titanium silicocarbides Ti₂SiC, Ti₃SiC₂, and Ti₄SiC₃, and their electronic structure and interatomic interactions are investigated by the density functional tight-binding method (DFTB) in comparison with the corresponding crystalline phases. Translated from Teoreticheskaya i éksperimental’naya Khimiya, Vol. 45, No. 2, pp. 88-92, March-April, 2009.     

Electrochemical properties of nano-crystalline LiNi<Subscript>0.5</Subscript>Mn<Subscript>1.5</Subscript>O<Subscript>4</Subscript> synthesized by polymer-pyrolysis method

LiNi_0.5Mn_1.5O₄ powders were prepared through polymer-pyrolysis method. XRD and TEM analysis indicated that the pure spinel structure was formed at around 450 °C due to the very homogeneous intermixing of cations at the atomic scale in the starting precursor in this method, while the well-defined octahedral crystals appeared at a relatively high calcination temperature of 900 °C with a uniform particle size of about 100 nm. When cycled between 3.5 and 4.9 V at a current density of 50 mA/g, the as prepared LiNi_0.5Mn_1.5O₄ delivered an initial discharge capacity of 112.9 mAh/g and demonstrated an excellent cyclability with 97.3% capacity retentive after 50 cycles.