BaB_2O_4低温相单晶体的生长及其相关体系相图的研究

本文用差热分析和X射线衍射等方法研究了BaO-Na_2O-B_2O_3三元系的两个截面:BaB_2O_4-Na_2B_2O_4和BaB_2O_4-Na_2O赝二元系的相平衡关系。BaB_2O_4-Na_2B_2O_4属共晶体系,其共晶温度为826±3℃。在BaB_2O_4-Na_2O体系中发现一个新化合物BaB_2O_4·Na_2O,该化合物在846±3℃同成分熔化。BaB_2O_4·Na_2O对BaB_2O_4和Na_2O均为共晶体系,其共晶温度分别为755±3℃和573±3℃。并根据所得的结果,分别以15mol％Na_2O和13mol％Na_2B_2O_4为助熔剂,用提拉法培养出2×4×6mm~3和2×4×8mm~3的低温相BaB_2O_4单晶体。     

BaB2O4-K2O和BaB2O4-K2B2O4赝二元系相图的研究

用X射线衍射和差热分析方法研究了BaB₂O₄-K₂O和BaB₂O₄-K₂B₂O₄赝二元系的相平衡关系。BaB₂O₄-K₂B₂O₄属共晶体系,共晶温度为850±3℃,共晶点成分为45mol％K₂O。在Ba 关键词：     

BaO-Li2O-B2O3三元系中BaB2O4-Li2B2O4和BaB2O4-Li2O截面相平衡关系的研究

本文用X射线和差热分析方法对BaO-Li₂O-B₂O₃三元系中的两个截面:BaB₂O₄-Li₂B₂O₄和BaB₂O₄-Li₂O作了研究。在BaB₂O₄-Li₂B₂O₄赝二元系中发现了一个新的化合物4BaB₂O₄·Li₂B₂O₄。化合物在930±3℃由包晶反应形成,并与Li₂B₂O₄形成共晶反应。共晶温度为797±3℃,共晶点组分为79mol％Li₂B₂O₄。在BaB₂O₄-Li₂O截面中也存在化合物4BaB₂O₄·Li₂B₂O₄,其包晶反应温度从930±3℃随Li₂O含量增加下降到908±3℃。在组分60mol％Li₂O处形成另一个新的化合物2BaB₂O₄·3Li₂O。该化合物在630±3℃也是由包晶反应形成,并与Li₂O和Li₂CO₃分别形成共晶反应,共晶温度分别为400±3℃和612±3℃。在BaB₂O₄-Li₂B₂O₄和BaB₂O₄-Li₂O体系中都没有观察到固溶体。用计算机程序分别对化合物4BaB₂O₄·Li₂B₂O₄和2BaB₂O₄·3Li₂O的X射线粉末衍射图案进行了指标化,其结果:4BaB₂O₄·Li₂B₂O₄的空间群为Pmma,a=13.033?,b=14.630?,c=4.247?,每个单胞包含两个化合式单位;2BaB₂O₄·3Li₂O的空间群为Pmmm,a=4.814?,b=9.897?,c=11.523?,每个单胞也含有两个化合式单位。 关键词：     

β─BaB2O4晶体生长母液结构的分子动力学模拟研究

采用分子动力学模拟方法，研究了β-BaB₂O₄晶体生长母液BaB₂O₄-Na₂O二元系熔体的结构，Na₂O摩尔浓度分别为12.5%，20%，25%，30%．模拟给出的不同组分比下的B-O径向分布函数表明，随着Na₂O浓度的增加，第一峰峰值更高，峰形更尖锐．在模拟产生的一系列瞬态构型基础上，采用键序参数方法，结合环链统计，研究了母液溶体的局部结构．结果表明 关键词：     

CoFe2O4和MnFe2O4纳米复合介质的制备及其磁性研究

采用热分解法制备了分散程度高且平均晶粒尺寸为20 nm的CoFe₂O₄和MnFe₂O₄复合介质.低温磁化曲线测量显示,制备的复合介质具有软-硬磁交换弹性耦合效应,且合成温度以及软磁和硬磁相的成分比例对磁交换弹性耦合的强度有很大的影响.变温磁测量显示,温度为20K时,复合纳米介质的表面自旋冻结效应导致饱和磁化强度显著增加.Henkel测量显示,对分散的CoFe₂O₄和MnFe₂O₄复合介质,磁偶极相互作用占主导作用.     

Li2SO4—Li2B2O4,Li2SO4—(NH4)2SO4赝二元系相图及离子导电性研究

本文用差热分析和X射线衍射方法对Li₂SO₄-Li₂B₂O₄和Li₂SO₄-[NH₄]₂SO₄两个赝二元系相图进行了研究。Li₂SO₄-Li₂B₂O₄是共晶体系,共晶温度为720℃ 关键词：     

低温相偏硼酸钡(β-BaB2O4)晶体倍频系数的计算

本文从“离子基团理论”出发,并考虑A位离子晶格电场对(B₃O₆)^3-环的影响,采用CNDO/S近似计算了(B₃O₆)^3-基团的分子轨道,进而求得低温相偏硼酸钡(β-BaB₂O₄)晶体的倍频系数。计算结果与实验值符合,由此进一步证实了这一论点:β-BaB₂O₄晶体的倍频系数主要来自(B关键词：     

PbFe12O19单晶体中的位错蚀斑研究

应用50％HCl作为浸蚀剂,对助熔法生长的PbFe₁₂O₁₉单晶体的(0001)解理面进行了浸蚀,以显示位错蚀斑。根据蚀斑所具有的形态,将其进行了分类,并确定了各自对应的位错类型。应用Mathews等人提出的机制,解释了在(0001)基面上所观察到的位错蚀斑阵列。 关键词：     

ZnFe2O4的固相法和水热法制备及其电化学性能研究

本文用固相反应法和水热法制备了ZnFe₂O₄材料,X射线衍射(X-ray diffraction, XRD)表明制备出来的ZnFe₂O₄为尖晶石结构,表面形貌测试 (scanning electron microscopy, SEM) 显示两种方法制备的材料的平均粒径分别为500 nm和200 nm.比表面积测试结果表明,两种方法制备的样品的比表面积分别为136.7 m² g^{-1关键词： 2O₄')" href="#">ZnFe₂O₄ 尖晶石结构 电化学性能 锂离子电池}     

低维Bi2Fe4O9晶体的控制生长及其光催化性能研究

Low-dimensional Bi₂Fe₄O₉ nanosheets and microrods have been selectively prepared by a solvothermal method, from which the growth of the Bi₂Fe₄O₉ crystals can be controlled by the variation of reaction conditions. Structure determination showed that the nanosheets are mainly exposed by {001} facets while the microrods are exposed by {110} facets. Ab- sorption spectra revealed that there are two bandgaps observed for both nanosheets (at 1.9 and 1.55 eV) and microrods (1.7 and 1.45 eV), and they both would be available for the sunlight photocatalysis e ciently due to the intensive absorption ability in a wide region. Photocatalytic investigation demonstrated that the overall photocatalytic performance of the microrods is prior to that of the nanosheets due to the variation of bandgaps and exposed facets. The present report provides a useful alternative strategy for the controlling growth of nanostructures and/or microcrystals besides the present demonstration of the Bi₂Fe₄O₉ crystals with diflerent bandgaps and facets that would be able to tune the corresponding photocatalytic ability selectively.     

偏硼酸钡低温相的晶体结构

本文报道了新型信频材料——偏硼酸钡[Ba₃(B₃O₆)₂]低温相的晶体结构。晶体属三方晶系,空间群为C₃⁴-R3,取六方坐标系,晶胞参数为a=b=12.532?,c=12.717?,z=6。在PhilipsPW-1100四圆衍射仪上收集到独立衍射693个。采用重原子法通过三维帕特逊和三维傅里叶合成测定结构,并用对角矩阵最小二乘法修正至R=0.046。该晶体是一个由Ba²⁺和(B₃O₆)^3-环交错组成的层状阶梯式结构。其阴离子(B₃O₆)^3-环基本上是平面状的。基团平面垂直于三次轴;Ba²⁺近邻有7个氧原子。将此结构与偏硼酸钡高温相比较表明,由于钡阳离子的非中心对称分布改变了阴离子硼氧环共轭基团的电子云密度,这一结构上的变化对该晶体的倍频效应做了主要贡献。 关键词：     

Ni2+:BeAl2O4晶体发光性质的研究

用时间分辨的激光诱导荧光光谱方法测量了10—300K温度范围内Ni²⁺:BeAl₂O₄晶体的红外荧光光谱和荧光寿命。通过荧光寿命的温度变化特性分析,得出³T_2g态的内禀辐射衰减寿命为123±7.2μs。无辐射弛豫的Mott激活能为1147cm^-1,并导出了此晶体发光量子效率随温度的变化关系式。Ni²⁺:BeAl₂O_{4关键词：}     

LaxBi2-xTi4O11的合成及相变研究

合成了Ｌａ_xＢｉ_2-xＴｉ₄Ｏ₁₁系列样品，并完成了它们的喇曼光谱和ｘ射线衍射测量；结果表明，该体系在Ｘ＝１．２经历了一次相变，且相变与最低频声子模随Ｘ的变化有关。Ｌａ_0.2Ｂｉ_1.8·Ｔｉ₄Ｏ₁₁的相变温度为２００℃。初步获得Ｌａ₂Ｔｉ₄Ｏ₁₁的结构为正交结构。 关键词：     

LaNi5-NdNi5,LaNi5-CeNi5赝二元系相图和吸氢性能的研究

本文用X射线衍射和差热分析的方法测定了LaNi₅-NdNi₅,LaNi₅-CeNi₅两个赝二元系相图。用X射线衍射线宽化法测定了活化后LaNi₅-NdNi₅体系的样品晶粒尺寸的各向异性。考查了吸氢性能和第二相存在对LaNi₅吸氢性能的影响。测定和计算了两个体系中样品的点阵常数、单胞体积、原了间距吸氢前后的变化。从结构的观点,解释了LaNi₅-NdNi₅体系中活化后样品晶粒尺寸各向异性的原因。用本实验的结果,解释了RmNi₅(Rm代表混合稀土金属)的吸氢量和平台压力的差异。 关键词：     

2LiIO3·HIO3的晶体结构与相变

本文用差热分析、热失重以及X射线衍射等方法,对LiIO₃·HIO₃二元系的相平衡进行了研究,观察了以α-LiIO₃为基的固溶体和以2LiIO₃·HIO₃为基的固溶体的热学性质和晶体结构。2LiIO₃·HIO₃属六方晶系,空间群为P6₃,是α-LiIO₃的同晶型结构。20℃的点阵常数为:α=5.555?,c=4. 关键词：     

LiKSO4低温相变的核磁共振研究

研究了LiKSO₄中⁷Li的核磁共振谱与温度及晶体取向的关系。证实了在T_c=195K存在一个结构相变,并由实验数据推导出在这一温度以下,晶体的对称性低于P31c,每单胞至少含有六个分子式。没有证据说明有一个无公约相存在。测得181K的四极耦合常数为38.9kHz,不对称因子η=0.46,电场梯度主轴方向z与原c轴成11.6°角。 关键词：     

LiKSO4的旋光性和相变

室温下测量了LiKSO₄单晶的旋光频散特性,用“晶体”旋光模型可以很好地拟合实验结果。在-180℃到680℃温度范围内,测量了LiKSO₄的旋光度,观测到四个相交:低温相变具有显著的温度迴线,相变温度随样品而异。讨论了上述相变模式与目前已报道的LiKSO₄相变资料之间的关系。 关键词：