Optical and structural properties of Ge–Se bulk glasses and Ag–Ge–Se thin films

The optical and structural properties of Ge₂₀Se₈₀, Ge₂₅Se₇₅ and Ge₃₀Se₇₀ bulk glasses and Ag_x(Ge_0.20Se_0.80)_100−x thin films, where x = 0, 6, 11, 16, 20 and 23 at.% were studied. All samples were confirmed as amorphous according to XRD. The Raman spectra showed increase in 260 cm⁻¹ and 237 cm⁻¹ and decrease in 198 cm⁻¹ and 216 cm⁻¹ bands with different Se content in the bulk samples. The optical bandgap energy of bulk samples decreased (2.17–2.08 eV) and refractive index increased (2.389–2.426 at 1550 nm) with increasing Se content in bulk glasses. The Ge₂₀Se₈₀ thin films were prepared by vacuum thermal evaporation from Ge₃₀Se₇₀ bulk glasses. The Raman spectra of the films showed that peaks at 260 cm⁻¹ and 216 cm⁻¹ decreased their intensities with increasing Ag content in the thin films. The significant red shift of bandgap energy occurred upon different Ag content. The optically induced dissolution and diffusion resulted in graded refractive index profile along the film thickness caused by different Ag concentration. The refractive index increased from the substrate side to the top of thin films. The graded profile was getting more uniform with increasing content of silver in the thin film.     

Crystallization processes of Ag–Ge–Se superionic glasses

The interest in superionic systems has increased in recent years because of the potential application of these materials as solid electrolytes. In this field, amorphous materials present important advantages when compared to the crystalline solids: larger conductivity, isotropy and absence of grain boundaries. In this work, amorphous alloys of compositions (Ge₂₅Se₇₅)_100−yAg_y with y=10, 15, 20 and 25 at.% have been studied. Amorphous samples in bulk were obtained from the liquid by water quenching (melt-quenching technique). The crystallization kinetics of the amorphous alloys have been studied under continuous heating and isothermal conditions by means of differential scanning calorimetry. A glass transition and two exothermic transformations were observed in all the samples. The quenched samples and the crystallization products have been characterized by X-ray diffraction. The primary crystallization of the ternary phase Ag₈GeSe₆ and the secondary phase GeSe₂ was observed. The glass and crystallization temperatures, the activation energy and the crystallization enthalpy are reported. The first step of the crystallization of the Ag₈GeSe₆ phase in all the (Ge₂₅Se₇₅)_100−yAg_y samples is modelled taking into account the Johnson–Mehl–Avrami–Kolmogorov theory and considering that the changes in the composition only modify the viscosity of the undercooled liquid. The transformation diagrams (TTT and THRT) are calculated and the glass forming ability is analyzed. The experimental results are discussed and correlated with the structures proposed for the glass. The present results and conclusions are also compared with those reported by other authors.     

Rapid quenching and glass formation in chalcogenide glasses: Preparation and properties of Ge–As–Te glasses over an extended composition ranges

In Ge–As–Te system, the glass forming region determined by normal melt quenching method has two regions (GFR I and GFR II) separated by few compositions gap. With a simple laboratory built twin roller apparatus, we have succeeded in preparing Ge_7.5As_xTe_92.5−x glasses over extended composition ranges. A distinct change in T_g is observed at x = 40, exactly at which the separation of the glass forming regions occur indicating the changes in the connectivity and the rigidity of the structural network. The maximum observed in glass transition (T_g) at x = 55 corresponding to the average coordination number (Z_av) = 2.70 is an evidence for the shift of the rigidity percolation threshold (RPT) from Z_av = 2.40 as predicted by the recent theories. The glass forming tendency (K_gl) and ΔT (=T_c−T_g) is low for the glasses in the GFR I and high for the glasses in the GFR II.     

Influence of Ga incorporation on photoinduced phenomena in Ge–S based glasses

To study the influence of Ga addition on photoinduced effect, GaGeS glasses with constant atomic ratio S/Ge = 2.6 have been prepared. Using Raman spectroscopy, we have reported the effect of Ga on the structural behavior of these glasses. An increase of the glass transition temperature T_g, the linear refractive index and the density have been observed with increasing gallium content. The photoinduced phenomena have been examined through the influence of time exposure and power density, when exposed to above light bandgap (3.53 eV). The correlation between photoinduced phenomena and Ga content in such glasses are shown hereby.     

Study of microstructure in Agx(As0.33Se0.67)100−x chalcogenide glasses

Glasses with general formula Ag_x(As_0.33Se_0.67)_100−x were studied by means of modulated differential scanning calorimetry (MDSC), conductivity and permittivity measurements and atomic force acoustic microscopy (AFAM). In the whole range of doping (x = 2–12 at.% Ag) a phase separation was supposed. The proportional amount of the ion-conductive Ag rich phase increased with the Ag content. A rapid increase (almost four orders of magnitude) in the conductivity was observed in the Ag concentration range 4–8 at.%, which could be associated with the interconnection of this ion-conductive phase. The transition from a hole conductivity (at low Ag concentration) to a mixed ionic-hole conductivity at higher Ag concentration was studied by permittivity measurements.     

Local structural environment and intra-4f transition of rare-earth ion in chalcogenide glass: Comparison between Dy-doped Ge–As–S and Ge–Ga–S glasses

We have employed Dy L₃-edge extended X-ray absorption fine structure measurements to investigate the local structures of Dy doped in Ge–As–S and Ge–Ga–S glasses. It turned out that Dy–S distance on average is conspicuously longer in Ge–Ga–S glass despite the number of the nearest neighboring S atoms being nearly identical with each other. The enhanced rare-earth solubility of Ge–Ga–S glass is then explained in connection with decrease in covalence of Ga–S bonds compared with Ge–S or As–S bonds, and structural correlation between GaS₄ tetrahedra and Dy. The discrepancy in the local structural environments of trivalent Dy, however, results in no significant changes in the spectral lineshape and the mean energy of its intra-4f-configurational transitions.     

Effect of silver doping on the structure and phase separation of sulfur-rich As–S glasses: Raman and SEM studies

We report on the structural details and microphase separation of the bulk glasses Ag_x·(As₃₃S₆₇)_100-x for 0x25. Glass–glass phase separation occurs over a wide range of Ag content, i.e. 4x20. An off-resonant polarized Raman spectroscopic study has been carried out to elucidate structural aspects at the short- and medium-range structural order of the glasses. Analysis of Raman spectra revealed quantitative changes of the sulfur-rich microenvironments that reduce upon adding Ag. Scanning electron microscopy combined with X-rays microanalysis have been utilized to examine the type and extent of phase separation, and to provide quantitative details on the atomic concentrations in the Ag-poor and Ag-rich phases. It has been shown that at 7 at.% Ag the Ag-rich phase percolates through the structure; this effect can be associated with an ionic-to-superionic behavior of these glasses in accordance with similar studies on the stoichiometric arsenic sulfide glass; although the phase separation observed in the present glasses is qualitatively different.