Spectroscopic Characteristics of Differently Produced Single‐Walled Carbon Nanotubes

Single‐walled carbon nanotubes (SWNTs) synthesized with different methods are investigated by using multiple characterization techniques, including Raman scattering, optical absorption, and X‐ray absorption near edge structure, along with X‐ray photoemission by following the total valence bands and C 1s core‐level spectra. Four different SWNT materials (produced by arc discharge, HiPco, laser ablation, and CoMoCat methods) contain nanotubes with diameters ranging from 0.7 to 2.8 nm. The diameter distribution and the composition of metallic and semiconducting tubes of the SWNT materials are strongly affected by the synthesis method. Similar sp² hybridization of carbon in the oxygenated SWNT structure can be found, but different surface functionalities are introduced while the tubes are processed. All the SWNTs demonstrate stronger plasmon resonance excitations and lower electron binding energy than graphite and multiwalled carbon nanotubes. These SWNT materials also exhibit different valence‐band X‐ray photoemission features, which are considerably affected by the nanotube diameter distribution and metallic/semiconducting composition.     

Bundling and diameter selectivity in HiPco SWNTs poly(p-phenylene vinylene-co-2,5-dioctyloxy-m-phenylene vinylene) composites

Temperature-dependent (TD) Raman measurements at laser excitation 514.5 nm were performed at different concentrations. The spectral profile of the radial breathing modes were investigated up to a polymer concentration of 1 g/L and were found to be dominated by approximately 1.2-1.4 nm diameter tubes at room temperature. Upon heating above the glass transition of the polymer (60 degrees C) the smaller tubes around approximately 0.9 nm increased significantly in relative intensity. This suggests that below the glass transition of the polymer (60 degrees C) RBMs within the composite are damped and spectral changes cannot be interpreted as diameter selective solubilization. The observed RBM damping at room temperature only occurred up to a concentration of approximately 1.2 x 10(-4) g/L and below this no damping was observed. Photoluminescence intensity (PL) measurements were taken for a range of PmPV concentrations, in which HiPco single walled carbon nanotubes (SWNTs) at 100%, 10%, 1%, 0.1%, 0.01%, and 0% mass fractions were added. Fitting of the concentration dependence to a dynamic absorption/desorption model indicates that the polymer interacts with nanotube bundles until a critical concentration of approximately 1.2 x 10(-4) g/L is reached, below which the nanotubes are isolated. The polymer and or solvent has a significant effect on the debundling and aggregation within these systems. Aggregation and/or interaction with the polymer at higher concentrations can effect the RBM profile in the composite at ambient temperatures, providing an incomplete representation of the selection of diameters present within composites at a particular wavelength.     

Tuning the Raman resonance behavior of single-walled carbon nanotubes via covalent functionalization

We present a systematic Raman study over a range of excitation energies of arc discharge single-walled carbon nanotubes (SWCNTs) covalently functionalized according to two processes, esterification and reductive alkylation. The SWCNTs are characterized by resonance Raman spectroscopy at each step of the functionalization process, showing changes in radial breathing mode frequencies and transition energies for both semiconducting and metallic tubes. Particular attention is given to a family of tubes clearly identified in the Kataura plot for which we continuously tune the excitation energy from 704 to 752 nm. This allows us to quantify the energy shift occurring in the spacing of the van Hove singularities. We demonstrate that, independently of the functionalization technique, the type of chain covalently bound to the tubes plays an important role, notably when oxygen atoms lie close to the tubes, inducing a larger shift in transition energy as compared to that of other carbonaceous chains. The study shows the complexity of interpreting Raman data and suggests many interpretations in the literature may need to be revisited.     

On the origin of preferential growth of semiconducting single-walled carbon nanotubes

A correlation is observed between the diameters (d) of single-walled carbon nanotubes and the percentages of metallic and semiconducting tubes synthesized at 600 degrees C by plasma-assisted chemical vapor deposition. Small tubes (d approximately 1.1 nm) show semiconductor percentages that are much higher than expected for a random chirality distribution. Density functional theory calculations reveal differences in the heat of formation energies for similar-diameter metallic, quasi-metallic, and semiconducting nanotubes. Semiconducting tubes exhibit the lowest energies and the stabilization scales with approximately 1/d(2). This could be a thermodynamic factor in the preferential growth of small semiconducting nanotubes.     

Anisotropic Photoluminescence of Poly(3-hexyl thiophene) and Their Composites with Single-Walled Carbon Nanotubes Highly Separated in Metallic and Semiconducting Tubes

In this work, the effect of the single-walled carbon nanotubes (SWNTs) as the mixtures of metallic and semiconducting tubes (M + S-SWNTs) as well as highly separated semiconducting (S-SWNTs) and metallic (M-SWNTs) tubes on the photoluminescence (PL) of poly(3-hexyl thiophene) (P3HT) was reported. Two methods were used to prepare such composites, that is, the chemical interaction of the two constituents and the electrochemical polymerization of the 3-hexyl thiophene onto the rough Au supports modified with carbon nanotubes (CNTs). The measurements of the anisotropic PL of these composites have highlighted a significant diminution of the angle of the binding of the P3HT films electrochemical synthetized onto Au electrodes covered with M + S-SWNTs. This change was attributed to metallic tubes, as was demonstrated using the anisotropic PL measurements carried out on the P3HT/M-SWNTs and P3HT/S-SWNTs composites. Small variations in the angle of the binding were reported in the case of the composites prepared by chemical interaction of the two constituents. The proposed mechanism to explain this behavior took into account the functionalization process of CNTs with P3HT. The experimental arguments of the functionalization process of CNTs with P3HT were shown by the UV-VIS-NIR and FTIR spectroscopy as well as surface-enhanced Raman scattering (SERS). A PL quenching process of P3HT induced both in the presence of S-SWNTs and M-SWNTs was reported, too. This process origins in the various de-excitation pathways which can be developed considering the energy levels diagram of the two constituents of each studied composite.     

Ultrafast energy transfer of one-dimensional excitons between carbon nanotubes: a femtosecond time-resolved luminescence study

Excitation energy transfer has long been an intriguing subject in the fields of photoscience and materials science. Along with the recent progress of photovoltaics, photocatalysis, and photosensors using nanoscale materials, excitation energy transfer between a donor and an acceptor at a short distance (≤1-10 nm) is of growing importance in both fundamental research and technological applications. This Perspective highlights our recent studies on exciton energy transfer between carbon nanotubes with interwall (surface-to-surface) distances of less than ～1 nm, which are equivalent to or shorter than the size of one-dimensional excitons in carbon nanotubes. We show exciton energy transfer in bundles of single-walled carbon nanotubes with the interwall distances of ～0.34 and 0.9 nm (center-to-center distances ～1.3-1.4 and 1.9 nm). For the interwall distance of ～0.34 nm (center-to-center distance ～1.3-1.4 nm), the transfer rate per tube from a semiconducting tube to adjacent semiconducting tubes is (1.8-1.9) × 10(12) s(-1), and that to adjacent metallic tubes is 1.1 × 10(12) s(-1). For the interwall distance of ～0.9 nm (center-to-center distance ～1.9 nm), the transfer rate per tube from a semiconducting tube to adjacent semiconducting tubes is 2.7 × 10(11) s(-1). These transfer rates are much lower than those predicted by the F?rster model calculation based on a point dipole approximation, indicating the failure of the conventional F?rster model calculations. In double-walled carbon nanotubes, which are equivalent to ideal nanoscale coaxial cylinders, we show exciton energy transfer from the inner to the outer tubes. The transfer rate between the inner and the outer tubes with an interwall distance of ～0.38 nm is 6.6 × 10(12) s(-1). Our findings provide an insight into the energy transfer mechanisms of one-dimensional excitons.     

Aqueous dispersion, surface thiolation, and direct self-assembly of carbon nanotubes on gold

We report the efficient aqueous dispersion of pristine HiPco single-walled carbon nanotubes (SWNTs) with ionic liquid (IL)-based surfactants 1-dodecyl-3-methylimidazolium bromide (1) and 1-(12-mercaptododecyl)-3-methylimidazolium bromide (2), the thiolation of nanotube sidewalls with 2, and the controlled self-assembly of positively charged SWNT-1,2 composites on gold. Optical absorption spectra and resonance Raman (RR) data of obtained aqueous SWNT-1,2 dispersions are consistent with debundled and noncovalently functionalized nanotubes whose electronic properties have not been disturbed. Additionally, the dispersion of pristine nanotube material with surfactants 1 and 2 leads to a high degree of purification from carbonaceous particles. The chiralities of the 14 smallest semiconducting HiPco SWNTs in resonance with Raman excitation at 1064 nm (1.165 eV) were determined in SWNT-2 aqueous dispersion using UV-vis-NIR and RR spectra. X-ray photoelectron spectroscopy (XPS) and surface-enhanced resonance Raman scattering (SERRS) spectroscopy of SWNT-2 submonolayers on gold verified the encapsulation of individualized SWNTs with IL surfactants, the cleavage of S-S disulfide bonds formed in aqueous SWNT-2 suspensions, and the direct chemisorption of the SWNT-2 composite on bare gold via the Au-S bond. Aqueous dispersions of SWNTs with IL-based surfactants add biofunctionality to carbon nanotubes by imparting the positive surface charge necessary for interactions with cell membranes. Our technique, which purifies pristine nanotube material and produces water-soluble, positively charged nanotubes with pendent surface-active thiol groups, may also be translated to other carbon nanotubes and carbon nanostructures. Self-assembled, positively charged submonolayers of SWNTs can be further used for applications in cell biology and sensor technology.     

Adsorption of gases in carbon nanotubes: are defect interstitial sites important?

Molecular simulations are used to shed light on an ongoing controversy over where gases adsorb on single walled carbon nanotube bundles. We have performed simulations using models of carbon nanotube bundles composed of tubes of all the same diameter (homogeneous) and tubes of different diameters (heterogeneous). Simulation data are compared with experimental data in an effort to identify the best model for describing experimental data. Adsorption isotherms, isosteric heats of adsorption, and specific surface areas have been computed for Ar, CH 4, and Xe on closed, open, and partially opened homogeneous and heterogeneous nanotube bundles. Experimental data from nanotubes prepared from two different methods, electric arc and HiPco, were examined. Experimental adsorption isotherms and isosteric heats for nanotubes prepared by the electric arc method are in best agreement with simulations for heterogeneous bundles of closed nanotubes. Models including adsorption in defect interstitial channels are required to achieve good agreement with experiments. Experimental isosteric heats and specific surface areas on HiPco nanotubes are best described by a model consisting of heterogeneous bundles with approximately 11% of the nanotubes opened.     

活性碳纤维阴极电芬顿反应降解微囊藻毒素研究

以具有高比表面积的活性碳纤维作为阴极,通过电芬顿反应降解水中微囊藻毒素(MCRR,MCLR)的电化学方法系统考察了电流密度、pH值和Fe2+浓度等因素对微囊藻毒素降解效果的影响.实验结果表明,在Fe2+浓度为1.0mmol/L和电流密度为6.6mA/cm2条件下,电化学处理60min,MCRR(8.81mg/L)去除率为75%,MCLR(6.36mg/L)去除率为94%.证明过氧化氢可以通过电化学还原在活性碳纤维阴极表面高效产生,微囊藻毒素可被高效降解去除.     

A route for bulk separation of semiconducting from metallic single-wall carbon nanotubes

Substantial separation of single-wall carbon nanotubes (SWNTs) according to type (metallic versus semiconducting) has been achieved for HiPco and laser-ablated SWNTs. We presently argue that stable dispersions of SWNTs with octadecylamine (ODA) in tetrahydrofuran (THF) originate from the physisorption and organization of ODA along the SWNT sidewalls in addition to the originally proposed zwitterion model. Furthermore, the reported affinity of amine groups for semiconducting SWNTs, as opposed to their metallic counterparts, contributes additional stability to the physisorbed ODA. This provides a venue for the selective precipitation of metallic SWNTs upon increasing dispersion concentration, as indicated by Raman investigations.     

Raman spectroscopy of individual single-walled carbon nanotubes from various sources

Resonance Raman spectroscopy/microscopy was used to study individualized single-walled carbon nanotubes (SWNTs) both in aqueous suspensions as well as after spin-coating onto Si/SiO2 surfaces. Four different SWNT materials containing nanotubes with diameters ranging from 0.7 to 1.6 nm were used. Comparison with Raman data obtained for suspensions shows that the surface does not dramatically affect the electronic properties of the deposited tubes. Raman features observed for deposited SWNTs are similar to what was measured for nanotubes directly fabricated on surfaces using chemical vapor deposition (CVD) methods. In particular, individual semiconducting tubes could be distinguished from metallic tubes by their different G-mode line shapes. It could also be shown that the high-power, short-time sonication used to generate individualized SWNT suspensions does not induce defects in great quantities. However, (additional) defects can be generated by laser irradiation of deposited SWNTs in air, thus giving rise to an increase of the D-mode intensity for even quite low power densities (approximately 10(4) W/cm2).     

Insights on charge transfer doping and intrinsic phonon line shape of carbon nanotubes by simple polymer adsorption

Doping of individual single-walled carbon nanotubes via noncovalent adsorption of polyethylenimine which converts p-type semiconducting nanotubes into n-type is examined by micro-Raman studies. Distinctively different responses are observed in metallic and in semiconducting nanotubes. Very little or no changes in the radial breathing and the disorder modes are observed upon polymer adsorption on semiconducting carbon nanotubes indicating noncovalent nature of this process. Tangential G-band spectral downshift of up to approximately 10 cm(-)(1) without line broadening is observed for semiconducting tubes suggesting similar magnitude of electron transfer as commonly observed in electrochemical doping with alkali metals. Strong diameter dependence is also observed and can be explained by thermal ionization of charge carriers with activation barrier that scales as the energy gap of the semiconducting nanotubes. In contrast, metallic nanotubes exhibit very different behavior with significant line broadening of the G-band and concurrent enhancement of the disorder mode. In certain cases, initially symmetric Lorentzian line shapes of the G-band features with narrow line widths similar to semiconducting tubes are converted to a broad, asymmetric Breit-Wigner-Fano line shape. Implications on the effects of electron injection and the local chemical environment on the intrinsic line shape of isolated carbon nanotubes are discussed.     

Assessment of chemically separated carbon nanotubes for nanoelectronics

It remains an elusive goal to obtain high performance single-walled carbon-nanotube (SWNT) electronics such as field effect transistors (FETs) composed of single- or few-chirality SWNTs, due to broad distributions in as-grown materials. Much progress has been made by various separation approaches to obtain materials enriched in metal or semiconducting nanotubes or even in single chiralties. However, research in validating SWNT separations by electrical transport measurements and building functional electronic devices has been scarce. Here, we performed length, diameter, and chirality separation of DNA functionalized HiPco SWNTs by chromatography methods, and we characterized the chiralities by photoluminescence excitation spectroscopy, optical absorption spectroscopy, and electrical transport measurements. The use of these combined methods provided deeper insight to the degree of separation than either technique alone. Separation of SWNTs by chirality and diameter occurred at varying degrees that decreased with increasing tube diameter. This calls for new separation methods capable of metallicity or chirality separation of large diameter SWNTs (in the approximately 1.5 nm range) needed for high performance nanoelectronics. With most of the separated fractions enriched in semiconducting SWNTs, nanotubes placed in parallel in short-channel (approximately 200 nm) electrical devices fail to produce FETs with high on/off switching, indicating incomplete elimination of metallic species. In rare cases with a certain separated SWNT fraction, we were able to fabricate FET devices composed of small-diameter, chemically separated SWNTs in parallel, with high on-/off-current (I(on)/I(off)) ratios up to 105 owing to semiconducting SWNTs with only a few (n,m) chiralities in the fraction. This was the first time that chemically separated SWNTs were used for short channel, all-semiconducting SWNT electronics dominant by just a few (n,m)'s. Nevertheless, the results suggest that much improved chemical separation methods are needed to produce nanotube electronics at a large scale.     

Interaction of narrow carbon nanotubes with nitronium tetrafluoroborate salts

Density functional calculations have been performed to investigate the destruction of narrow carbon nanotubes (CNTs) under the attack of nitronium tetrafluoroborate salts. The dissociation of these salts in a solvent produces nitronium and tetrafluoroborate ions which coadsorb on the external surface of the tubes. It is shown that the ions bind strongly to both metallic and semiconducting narrow nanotubes, although stronger to the metallic ones. The nitronium cations bind to the CNTs through a charge transfer mechanism, whereas the tetrafluoroborate anions remain negatively charged upon adsorption on the nanotubes. The surface of the nanotubes gets substantially deformed around the adsorption site of the nitronium ion, but it is hardly changed around the adsorption site of the tetrafluoroborate ion. These results are the theoretical basis to explain the destruction of the narrow CNTs found in the experiments and also to unravel, in agreement with the experimental interpretation, the distinct role played by the nitronium and the tetrafluoroborate ions. The tetrafluoroborate ions contribute to separate the CNTs from the bundles into individual tubes, without affecting the tubes. The nitronium ions, in contrast, modify the electronic and geometrical structures of the narrow tubes leading eventually to their destruction. The implications for the selective removal of intermediate diameter metallic CNTs found in the experiments are also discussed. The adsorption of the neutral nitrogen dioxide molecule is also studied, and the results show that the weak interactions of this molecule with both metallic and semiconducting tubes cannot be used as a model for the strong attack of the nitronium ions to the narrow tubes. The sensor effect of the nanotubes toward adsorption of nitrogen dioxide is also discussed.     

On the applicability of cluster models to study the chemical reactivity of carbon nanotubes

We have performed a comparative study on the reactivity of metallic and semiconducting nanotubes using infinite and finite models. Infinite models were created using periodic boundary conditions while finite ones were constructed by means of hydrogen terminated nanotubes sections. Cluster models systematically underestimate the reactivity of metallic single wall carbon nanotube (SWCNT)s. We have confirmed that metallic nanotubes are more reactive than semiconducting species, in disagreement with previous works. The differences can be attributed to the presence of an instability in the singlet ground state of the wavefunction corresponding to semiconducting nanotubes clusters. When lower electronic states of the pristine cluster are considered, semiconducting nanotubes become less reactive as compared with metallic SWCNTs. Particularly, if an antiferromagnetic solution is considered for the semiconducting (10,0) SWCNT cluster, it becomes less reactive than the (5,5) SWCNT, as observed for infinite models. Because semiconducting nanotubes are less reactive than metallic counterparts, their reaction energies converge faster to the values observed for graphene. For a 1.6-nm diameter semiconducting nanotube, the addition energy is comparable with graphene. Thus, semiconducting nanotubes with diameters larger than 1.6 nm are going to be as reactive as graphene and the effects of curvature will be unimportant.     

Selective polycarboxylation of semiconducting single-walled carbon nanotubes by reductive sidewall functionalization

The efficient and controllable synthesis, the detailed characterization, and the chemical postfunctionalization of polycarboxylated single-walled carbon nanotubes SWCNT(COOH)(n) are reported. This innovative covalent sidewall functionalization method is characterized by (a) the preservation of the integrity of the entire σ-framework of SWCNTs; (b) the possibility of achieving very high degrees of addition; (c) control of the functionalization degrees by the variation of the reaction conditions (reaction time, ultrasonic treatment, pressure); (d) the identification of conditions for the selective functionalization of semiconducting carbon nanotubes, leaving unfunctionalized metallic tubes behind; (e) the proof that the introduced carboxylic acid functionalities can serve as versatile anchor points for the coupling to functional molecules; and (f) the application of a subsequent thermal degradation step of the functionalized semiconducting tubes leaving behind intact metallic SWCNTs. Functional derivatives have been characterized in detail by means of Raman, UV-vis/nIR, IR, and fluorescence spectroscopy as well as by thermogravimetric analysis combined with mass spectrometry, atomic force microscopy, and zeta-potential measurements.     

Purity assessment of single-wall carbon nanotubes, using optical absorption spectroscopy

A demand currently exists for a method of assessing the purity of single-wall carbon nanotubes (SWNTs), which will allow for meaningful material comparisons. An established metric and protocol will enable accurate and reproducible purity claims to be substantiated. In the present work, the ability to accurately quantify the mass fraction of SWNTs in the carbonaceous portion of a given sample is demonstrated, using optical absorption spectroscopy on both laser and arc discharge-generated SWNT-N,N-dimethylacetamide (DMA) dispersions. Verification of purity assessment protocols is based upon constructed sample sets comprising designed mass fractions of purified SWNTs and representative carbonaceous synthesis byproducts. Application of a previously reported method based on a ratio of the areal absorbance from linear subtractions of the second interband electronic transitions of semiconducting SWNTs ((S)E(22)) has shown a severe overestimation of SWNT purity (average error >24%). Instead, the development of a nonlinear pi-plasmon model, which considers overlap of electronic transitions and peak broadening, has dramatically improved the purity assessment accuracy (average error <7%), derived from a strong correlation to the constructed sample sets. This approach has enabled corroboration of rapid assessment procedures, such as absorbance peak maxima ratio and Beer's law analysis, directed at purification monitoring and synthesis sample screening. Specifically, a simple protocol for purity assessment of laser and arc-discharge SWNTs has been established that can be extended to other synthetic types (i.e. CVD, HiPco, etc.) and diameter distributions.     

The luminescent carbon-bearing microinclusion enigma in the Kimi Unit, Rhodope, Greece: Raman microscopic point analyses and mapping with different lasers

The Kimi Unit of the Rhodope Metamorphic Province (RMP), NE Greece, experienced ultrahigh-pressure metamorphism (UHPM), as documented by the unequivocal presence of diamond microinclusions in metapelitic garnet porphyroblasts. Certain peculiar lozenge-shaped 2-8 microm sized inclusions in diamond-bearing garnets reveal a broad composite and asymmetric triplet band (phase XXX) at approximately 1331 cm(-1) in their Raman spectra acquired with a 632.8 nm He-Ne laser, initially attributed to an sp(3)-hybridized C-polymorph. These have been meticulously re-investigated by means of combined 2-wavelength (514.5 nm/632.8 nm laser) Raman microscopy. Raman mapping has been extensively employed in order to examine the spatial distribution of phase XXX and of other phases in these polyphase inclusions and to explore for additional Raman bands. The triplet band at approximately 1331 cm(-1) measured with the 632.8 nm laser shifts to much higher wavenumbers ( approximately 4966 cm(-1)) when excited with a 514.5 nm Ar(+) laser, proving that the XXX triplet is not a real Raman band but a luminescence one at approximately 691.1 nm. Numerous hypotheses on the nature of the mysterious phase XXX (e.g. Cr(3+)-bearing mineral, carbonate, C polymorph, gas, organic phase) are explored and discussed but all are shown to be unsatisfactory. It is suggested that XXX occurs as nanocrystals that luminesce strongly giving the appearance (in Raman maps) of being larger.     

Preferred functionalization of metallic and small-diameter single-walled carbon nanotubes by nucleophilic addition of organolithium and -magnesium compounds followed by reoxidation

Covalent sidewall addition to single-walled nanotubes (SWNTs) of a series of organolithium and organomagnesium compounds (nBuLi, tBuLi, EtLi, nHexLi, nBuMgCl, tBuMgCl) followed by reoxidation is reported. The functionalized R(n)-SWNTs were characterized by Raman and NIR emission spectroscopy. The reaction of SWNTs with organolithium and magnesium compounds exhibits pronounced selectivity: in general, metallic tubes are more reactive than semiconducting ones. The reactivity of SWNTs toward the addition of organometallic compounds is inversely proportional to the diameter of the tubes. This was determined simultaneously and independently for both metallic and semiconducting SWNTs. The reactivity also depends on the steric demands of the addend. Binding of the bulky t-butyl addend is less favorable than addition of primary alkyl groups. Significantly, although tBuLi is less reactive than, for example, nBuLi, it is less selective toward the preferred reaction with metallic tubes. This unexpected behavior is explained by fast electron transfer to the metallic SWNTs having low-lying electronic states close to the Fermi level, a competitive initial process. The NIR emission of weakly functionalized semiconducting SWNTs, also reported for the first time, implies interesting applications of functionalized tubes as novel fluorescent reporter molecules.     

磺化碳纳米管改性聚苯胺复合材料的合成与超级电容特性

运用重氮化技术制备了水溶性磺化碳纳米管,在此基础上,以不同直径的磺化碳纳米管(1～2 nm,<8 nm,10～20 nm,30～50 nm)为载体,采用原位氧化聚合方法合成了一系列磺化碳纳米管改性聚苯胺复合材料.红外和紫外-可见光谱分析表明,聚苯胺与磺化碳纳米管之间存在π-π相互作用,并形成了电荷转移复合物;且随着碳纳...