添加聚乙二醇对CuZnAl浆状催化剂结构和性能的影响

首先利用共沉淀沉积法制备CuZnAl催化剂前驱体,并且通过添加聚乙二醇(PEG600)对其进行改性,最后采用完全液相法对前驱体进行热处理制得浆状催化剂,考察了其在浆态床合成气一步法制二甲醚反应中的催化性能,采用X射线粉末衍射、程序升温还原、氨程序升温脱附和X射线光电子能谱对其进行了表征.结果表明,PEG600的添加促进了催化剂中铜组分在热处理过程中被还原成低价铜,提高了催化剂中Cu2O的分散性,改变了催化剂表面酸量和酸强度的分布,同时PEG600的添加方式对催化剂的甲醇合成和甲醇脱水能力有显著影响.在硝酸铜和硝酸锌水溶液中添加0.5 wt%的PEG600时,在热处理过程中形成的Cu2O最稳定,不易被还原,其晶粒度小,进而使CO转化率大幅度提高.     

Effect of Polyethylene Glycol on Structure and Performance of CuZnAI Slurry Catalyst

首先利用共沉淀沉积法制备CuZnAl催化剂前驱体,并且通过添加聚乙二醇（PEG600）对其进行改性,最后采用完全液相法对前驱体进行热处理制得浆状催化剂,考察了其在浆态床合成气一步法制二甲醚反应中的催化性能,采用X射线粉末衍射、程序升温还原、氨程序升温脱附和X射线光电子能谱对其进行了表征.结果表明,PEG600的添加促进了催化剂中铜组分在热处理过程中被还原成低价铜,提高了催化剂中Cu2O的分散性,改变了催化剂表面酸量和酸强度的分布,同时PEG600的添加方式对催化剂的甲醇合成和甲醇脱水能力有显著影响.在硝酸铜和硝酸锌水溶液中添加0.5 wt%的PEG600时,在热处理过程中形成的Cu2O最稳定,不易被还原,其晶粒度小,进而使CO转化率大幅度提高.     

La和Mn助剂对完全液相法制备的CuZr浆状催化剂结构和性能的影响

利用完全液相法分别制备了CuZr和La,Mn促进的CuZr浆状催化剂,考察了催化剂在合成气一步合成二甲醚反应中的催化性能,并采用NH3程序升温脱附、X射线粉末衍射、N2吸附-脱附、X射线光电子能谱和程序升温还原等对其进行了表征.结果表明,在利用完全液相法制备的La-Mn-CuZr催化剂中,La和Mn的加入可促进催化剂活...     

Zn、Mo对CuCo基催化剂合成低碳醇性能的促进作用

采用超声辅助的反相共沉淀法制备CO加氢合成低碳醇用CuCo基催化剂,研究过渡金属Zn、Mo助剂对CuCo基催化剂结构与性能的影响,借助N2吸附（BET）、X射线衍射（XRD）、程序升温还原（H2-TPR）和程序升温脱附（CO-TPD）等测试技术对催化剂进行表征.结果表明,Zn、Mo均在一定程度上增加了催化剂的比表面积、...     

Pt/CeO2-ZrO2-La2O3柴油车尾气氧化催化剂活性及抗硫性能

采用两种方法制备了三种Pt/CeO2-ZrO2-La2O3柴油车尾气氧化催化剂,并用X射线衍射、N2物理吸附、程序升温还原、程序升温脱附、X射线荧光光谱和红外光谱等方法对其进行了表征.结果发现,制备方法对催化剂的结构、织构、抗硫性能及催化性能的影响非常大.对其进行硫中毒,导致起燃温度明显升高.将ZrO2和La2O3沉积...     

载体焙烧温度对Ru/MgAl2O4催化剂液相苯部分加氢性能的影响

采用水热合成法制备了镁铝尖晶石(MgAl2O4)材料,制备了其负载的Ru催化剂,研究了MgAl2O4焙烧温度对Ru/MgAl2O4催化剂上液相苯部分加氢催化性能的影响.采用X射线粉末衍射、27A1固体核磁共振、傅里叶变换红外光谱、H2-程序升温还原、H2-程序升温脱附、N2物理吸附、透射电子显微镜和X射线光电子能谱等手...     

CoMoS/ZrO2催化4-甲基苯酚加氢脱氧中C−O键的选择性断裂

采用饱和浸渍法制备了不同Co-Mo原子比(0.25,0.30,0.35,0.40,0.45)和Co-Mo负载量(2.35％,4.36％,7.48％和10.79％)的CoMoS/ZrO2催化剂.用X射线衍射(XRD)、程序升温还原(H2-TPR)、氮气吸附和X射线光电子能谱(XPS)对催化剂进行了表征.以4-甲基苯酚为模...     

Mn-Al和Cu-Mn-Al复合氧化物催化苯甲醇选择氧化反应

用溶胶-凝胶法制备了不同组成的Mn-Al和Cu-Mn-Al复合氧化物两组催化剂,用于苯甲醇选择氧化反应.用X射线衍射(XRD)、N2物理吸附(BET)、扫描电镜(SEM)、H_2程序升温还原(H_2-TPR)、O_2程序升温脱附(O_2-TPD)和X射线光电子能谱(XPS)技术对催化剂进行了结构表征,考察了催化剂组成对催化活性的影响.结果表明:以甲苯为溶剂,O_2为氧化剂,353 K反应5 h,Mn_2Al和Cu_(0.3)Mn_(0.7)Al_2催化剂上的苯甲醇转化率分别为36.6%和40.9%,苯甲醛选择性均为100%.进一步研究表明:催化剂活性与其H2还原性和O_2吸附性有关,高活性的催化剂吸附氧多,生成的活性氧易参与反应.     

丙烷选择氧化催化剂Mo-V-Zr-O的研究

研究了Zr添加量对Mo-V-O基催化剂丙烷选择氧化制丙烯醛催化性能的影响.对催化剂的BET、X射线衍射、H2-程序升温还原、NH3-程序升温脱附和异丙醇分解表征结果表明,Zr的添加改变了催化剂的物相结构、氧化还原性和酸碱性质,从而影响催化剂的催化性能,其中Mo2VZr0.5Ox催化剂表现出较好的催化活性和丙烯醛选择性.     

超声浸渍对费托合成Co/Zr/SiO2催化剂性能的影响

采用超声浸渍法制备了费托合成Co/Zr/SiO2催化剂,考察了超声波功率对催化剂费托反应性能的影响,并运用N2物理吸附、X射线衍射、H2程序升温脱附、H2程序升温还原和透射电子显微镜对催化剂进行了表征,结果表明,超声波处理可以增大催化剂的比表面积,减小金属Co的粒径,并使其较为均匀地分散于载体表面,其中以高功率超声波作...     

氧化铝载体对Pt-Sn/Al2O3催化剂上苯胺和苯甲醇一步合成N-苯基苄胺催化反应性能的影响

以基于借氢策略的苯甲醇和苯胺一步合成N-苯基苄胺为模型反应,研究了三种不同表面结构的氧化铝对其负载的Pt-Sn催化剂上N-烷基化合成仲胺反应性能的影响.采用N₂吸附-脱附法、压汞法、X射线衍射、透射电镜、扫描电镜、CO脉冲吸附、H₂-程序升温还原及NH₃-程序升温脱附等技术对载体和Pt-Sn/Al₂O₃催化剂进行了表征.结果表明,与Al₂O₃相互作用较弱且高度分散的Pt颗粒具有很高的催化活性,Al₂O₃载体较大的孔体积和大孔分布的孔结构有助于反应物扩散和吸附到催化剂表面并提高反应活性.同时也有利于反应产物从催化剂表面离开,从而提高催化剂的稳定性.然而Al₂O₃较强的酸性及酸性分布降低了产物仲胺的选择性和催化剂稳定性.     

Cr掺杂的丙烷选择氧化制丙烯酸高效催化剂

在丙烷选择氧化制丙烯酸催化剂MoVTeNbOx的活性相M1基础上掺杂一定量的Cr,当Cr/Nb摩尔比为0.002时,催化剂具有很高的丙烯酸选择性(78.3%)和收率(50.7%);并采用X射线衍射、X射线光电子能谱、程序升温还原、O2程序升温脱附、NH3程序升温脱附和异丙醇氧化等手段对催化剂的构效关系进行了探讨.结果表明,适量Cr的添加可调节催化剂表面Mo6+,V5+和Te4+等物种含量,提高催化剂的氧化能力,使丙烷转化率增加.同时,适量Cr的添加使得催化剂表面酸强度下降,酸性位点数量减少,从而抑制丙烯酸的深度氧化,提高了丙烯酸选择性.     

Zr 改性MnOx/MWCNTs催化剂的结构特征与低温SCR活性

以ZrO（NO₃）₂·2H₂O为前驱体对多壁碳纳米管（MWCNTs）进行了改性并负载MnO_x制备了MnO_x/ZrO₂/MWCNTs 催化剂. 考察了Zr 对催化剂低温选择性催化还原（SCR）反应活性的影响,并通过多种分析手段对催化剂的结构进行了表征. 结果表明Zr 的添加对催化剂的低温SCR活性具有显著的促进作用,当Zr 负载量为30%时,催化剂活性最佳. X射线衍射（XRD）、拉曼（Raman）光谱、透射电镜（TEM）、N₂吸附-脱附的表征结果分析表明,适量的Zr 改性促进了MnO_x在载体表面的分散,增强金属氧化物与MWCNTs 之间的作用,也能增加催化剂的比表面积、孔容和孔径. X 射线光电子能谱（XPS）、H₂程序升温还原（H₂-TPR）和NH₃程序升温脱附（NH₃-TPD）的分析结果则显示,Zr 能提高催化剂表面化学吸附氧浓度,促进Mn³⁺转化为Mn⁴⁺,从而使催化剂表面的活性位点增多,氧化还原能力增强,同时还提高了催化剂表面酸性位点的数量和强度,促进了NH₃的吸附,是MnO_x/ZrO₂/MWCNTs 催化剂低温SCR活性提高的主要原因.     

Synthesis of Higher Alcohols via Syngas on Cu/Zn/Si Catalysts. Effect of Polyethylene Glycol Content

Cu/Zn/Si catalysts with different polyethylene glycol (PEG) content were prepared by a complete liquid-phase method, and characterized by XRD, H₂-TPR, N₂-adsorption, and XPS. The influence of PEG content on the higher alcohols synthesis from syngas was investigated. The results showed that addition of PEG can influence the texture and surface properties of the catalysts, and therefore affect their activity and product distribution. With an increase in PEG content, BET surface area, Cu crystallite size and surface active ingredient content of the catalysts first increased and then decreased, the CO conversion had similar variation tendency. However, the pore volume and pore diameter of the catalyst increased, and the binding energy of the active component and the content of Cu₂O decreased, which resulted in higher catalyst selectivity towards higher alcohols. The highest C²⁺OH selectivity in total alcohols was 60.6 wt %.     

氧化铝载体和氧化钡助剂对钌基氨合成催化剂结构和性能的影响

采用不同来源γ-Al2O3(市售Al2O3-1,合成Al2O3-2)作为钌基氨合成催化剂载体,利用浸渍法制备了一系列添加不同BaO助剂含量的Ba-Ru/Al2O3催化剂.通过X射线衍射(XRD)、N2-低温物理吸附、X射线荧光光谱(XRF)、透射电镜(TEM)、H2程序升温还原(H2-TPR)、NH3程序升温脱附(NH3-TPD)和X射线光电子能谱(XPS)等方法研究了不同来源的Al2O3以及BaO助剂含量对负载型钌基催化剂的物相结构、织构性质、微观形貌、表面性质和催化剂的氨合成活性等方面的影响.结果表明,载体的物理化学性质对制备的钌基氨合成催化剂的结构以及活性有较大影响.BaO助剂对催化剂的影响主要表现在两个方面:添加量不同导致BaO与γ-Al2O3的作用力不同,从而进一步影响催化体系的比表面积和孔结构性质;BaO助剂会对体系的Ru物种还原性质以及催化剂表面酸碱性质进行调节,适量BaO的加入能够极大提高反应活性,而这种最佳量与载体性质密切相关.     

Ni/SiO2-ZrO2催化剂焙烧温度对其催化愈创木酚加氢脱氧性能的影响简

采用化学沉淀法合成了SiO₂-ZrO₂复合氧化物载体,并以浸渍法制备了Ni/SiO₂-ZrO₂双功能催化剂,考察了焙烧温度对催化剂结构及其催化愈创木酚加氢脱氧制环己烷性能的影响. 结果表明,经500℃焙烧催化剂的加氢脱氧活性最高,在Ni金属中心和SiO₂-ZrO₂载体材料的协同作用下,愈创木酚转化率为100%,环己烷选择性为96.8%. 对催化剂进行N₂物理吸附、H₂化学吸附、X射线衍射分析、H₂程序升温还原、NH₃程序升温脱附与Raman光谱等表征后发现,合成的SiO₂-ZrO₂为无定形的酸碱两性氧化物;经500℃焙烧的催化剂样品的有效比表面积和孔体积均明显增大,表面酸量最多,硝酸镍分解成小颗粒的NiO较易被H₂还原,这些特性是该催化剂样品具有高效加氢脱氧活性的原因.     

Influences of pore size on production of 2-methylpyrazine over bifunctional CuO/ZnO/meso-SiO2 catalysts

Controllable crystallite size of CuO in CuO/ZnO/meso-SiO₂ catalysts was successfully realized by impregnation method using mesoporous silica with different pore diameters as support. Characterization techniques such as N₂ adsorption/desorption, X-ray diffraction, H₂ temperature-programmed reduction, and potentiometric titration were employed to investigate the influences of pore size on textural properties, crystalline phases, reducibility, and acidity. Catalytic evaluation of synthesis of 2-methylpyrazine was carried out at 380 °C under atmospheric conditions. The best catalytic performance was achieved over catalyst CZ/S1 supported on the carrier with smallest pore size.     

MnOx/MWCNTs低温氨选择性催化还原NOx硫中毒机理

以经过浓硝酸和等离子体放电预处理后的多壁碳纳米管(MWCNTs)为载体, 锰氧化物(MnO_x)为活性组分, 采用等体积浸渍法制备MnO_x/MWCNTs 催化剂. 利用热重分析(TGA)、扫描电子显微镜(SEM)、X射线衍射(XRD)、X射线光电子能谱(XPS)、程序升温还原/脱附(TPR/TPD)以及傅里叶变换红外(FTIR)光谱对催化剂进行表征, 探讨SO₂对催化剂低温氨选择性催化还原(SCR)NO_x活性的影响及SO₂中毒机理. 结果表明, 低温下SO₂对MnO_x/MWCNTs 催化剂活性有明显毒化作用. 反应温度越高, SO₂浓度越大, 催化剂SCR活性下降越快. 活性中心Mn原子硫酸化是催化剂失活的主要原因. 另外, 催化剂表面生成硫酸铵盐以及SO₂对NO吸附的抑制作用也一定程度上造成了催化剂的失活.     

不同聚合物分散剂对Pt/SAPO-11催化剂性能的影响

采用浸渍法制备了经过不同聚合物分散剂处理的Pt/SAPO-11催化剂，并通过X射线衍射(XRD)、透射电子显微镜(TEM)、N₂吸附-脱附和NH₃程序升温脱附(TPD)等对催化剂的组织结构进行了表征。结果表明，分散剂不会破坏催化剂的结构，反而提高了其孔体积、孔径和比表面积，同时改变了沸石的酸强度和酸量，其中以聚乙烯吡咯烷酮处理的Pt/SAPO-11催化剂孔体积、孔径和酸性分布最佳。在固定床反应器上对不同分散剂处理的Pt/SAPO-11催化剂催化性能进行评价，结果表明聚乙烯吡咯烷酮处理的Pt/SAPO-11催化剂也表现出最佳的催化性能，麻风树油的加氢脱氧率高达99.45%，生物航空煤油组分收率和异构烷烃组分(C₈~C₁₆)的选择性分别达到了44.67%和56.37%。     

不同聚合物分散剂对Pt/SAPO-11催化剂性能的影响

采用浸渍法制备了经过不同聚合物分散剂处理的Pt/SAPO-11催化剂,并通过X射线衍射(XRD)、透射电子显微镜(TEM)、N₂吸附-脱附和NH₃程序升温脱附(TPD)等对催化剂的组织结构进行了表征。结果表明,分散剂不会破坏催化剂的结构,反而提高了其孔体积、孔径和比表面积,同时改变了沸石的酸强度和酸量,其中以聚乙烯吡咯烷酮处理的Pt/SAPO-11催化剂孔体积、孔径和酸性分布最佳。在固定床反应器上对不同分散剂处理的Pt/SAPO-11催化剂催化性能进行评价,结果表明聚乙烯吡咯烷酮处理的Pt/SAPO-11催化剂也表现出最佳的催化性能,麻风树油的加氢脱氧率高达99.45%,生物航空煤油组分收率和异构烷烃组分(C₈~C₁₆)的选择性分别达到了44.67%和56.37%。