Defect structure and optical damage resistance of Hf:Fe:LiNbO3 crystals with various [Li]/[Nb] ratios

Hf:Fe:LiNbO₃ crystals were grown in air by the Czochralski technique with various ratios of [Li]/[Nb]=0.94, 1.05, 1.20 in melt. The defect structure and location of doped ions were analyzed by the UV‐visible and infrared spectroscopy. The optical damage resistance ability of Hf:Fe:LiNbO₃ crystals was measured by the photo‐induced birefringence change and the transmitted light spot distortion method. The results show that the optical damage resistance ability of Hf:Fe:LiNbO₃ crystals is enhanced with the increase of the [Li]/[Nb] ratio. The dependence of the optical damage resistance of Hf:Fe:LiNbO₃ crystals on the defect structure is discussed in detail. (© 2010 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Defect structure and optical damage resistance of In:Fe:Cu:LiNbO3 crystals with various [Li]/[Nb] ratios

In:Fe:Cu:LiNbO₃ crystals were grown in air by the Czochralski technique with various [Li]/[Nb] ratios of 0.946, 1.050, 1.200, and 1.380 in melt. Based on the ICP‐AES (inductively coupled plasma atomic emission spectrometry) analyzed results, the chemical formula of the triple‐doped In:Fe:Cu:LiNbO₃ crystals were obtained. It can be seen that the near‐stoichiometric ratio value is between 1.050 and 1.200 for our samples. The optical damage resistance of In:Fe:Cu:LiNbO₃ crystals was characterized by changes in light‐induced birefringence and it increases with the increasing of [Li]/[Nb] ratios. The dependence of the optical damage resistance on the defect structure of In:Fe:Cu:LiNbO₃ crystals is discussed in detail based on the obtained chemical formulas. (© 2011 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Optical damage resistance of Mg:Ce:Fe:LiNbO3 crystals

Mg:Ce:Fe:LiNbO₃ crystals were prepared with fixed concentrations of Fe₂O₃ and CeO₂, and differing concentrations of MgO by the Czochralski technique. Their infrared transmission spectra were measured in order to investigate their defect structures and their optical damage resistance was characterized by the photoinduced birefringence change and transmission facula distortion method. The optical damage resistance of Mg:Ce:Fe:LiNbO₃ crystals increases remarkably when the concentration of MgO exceeds a threshold concentration. The dependence of the optical damage resistance on the defect structure of Mg:Ce:Fe:LiNbO₃ crystals is discussed in detail. (© 2010 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Influence of microscopic defects on optical damage resistance of Zn:Fe:LiNbO3 crystals

Influence of defect structure on the infrared transmission spectra of OH^‐ in Zn:Fe:LiNbO₃ crystals with various ZnO concentration and different Li/Nb ratios was investigated. It indicates that above the Zn concentration threshold the OH^‐ absorptions bands successively shift from 3482cm^‐1 to 3504cm^‐1 and 3529cm^‐1. The intensity of the 3504cm^‐1 band increases with ZnO concentration increasing. The optical damage resistance of the Zn:Fe:LiNbO₃ crystals increases rapidly when the ZnO concentration exceeds a threshold value. This result contributed to the site alteration from the Li sites to Nb sites due to Zn‐doping in crystal. © 2006 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim     

Defect structure and spectroscopic characteristics of codoped Hf: Er: LiNbO3 crystals

Codoped Hf: Er: LiNbO₃ crystals have been grown by the Czochralski technique. Defect structures of the crystals were analyzed by IR absorption spectra, and the compositions of the crystals were measured by X‐ray fluorescent spectrograph. A new OH^–‐associated vibrational peak at 3492 cm^–1 was revealed in 6 mol % Hf: 1 mol % Er: LiNbO₃ crystal. It was attributed to (Hf_Nb)^–‐OH^–‐(Er_Nb)^2– defect centers. The Er³⁺ concentrations in crystals gradually decreased with the increase of the codoped Hf⁴⁺ concentrations in the melts. The emission characteristics of the crystals were investigated by the fluorescence spectrum. It was found that the luminescent intensity in codoped 6 mol % Hf: 1 mol % Er: LiNbO₃ crystal was 3.5 times stronger than that in single doped 1 mol % Er: LiNbO₃ crystal. The luminescent enhancement effect was successfully explained on the basis of defect structure of the crystals. (© 2009 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Growth and optical damage resistance of Sc,Er Co‐doped LiNbO3 crystals

A series of Sc:Er:LiNbO₃ crystals have been grown by Czochralski method. Their ultraviolet‐visible (UV‐Vis) absorption spectra was measured and discussed to investigate their defect structure. The optical damage resistance of Sc:Er:LiNbO₃ crystals was characterized by the transmitted beam pattern distortion method. It increases remarkably when the concentration of Sc₂O₃ exceeds a threshold concentration. The optical damage resistance of Sc (3.0mol %):Er:LiNbO₃ is much higher than that of the Er:LiNbO₃. The intrinsic and extrinsic defects were discussed to explain the enhance of the optical damage resistance in the Sc:Er:LiNbO₃ crystals. (© 2005 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Structure and optical damage resistance of In:Yb:Er:LiNbO3 crystals

A series of In:Yb:Er:LiNbO₃ crystals have been grown. The UV‐Vis absorption spectra and Infrared (IR) transmission spectra were measured and discussed in terms of the spectroscopic characterizations and the defect structure of the In:Yb:Er:LiNbO₃ crystals. The optical damage resistance was characterized by the transmitted beam pattern distortion method. The optical damage resistance of In (3.0mol %):Yb:Er:LiNbO₃ crystal is one order of magnitude higher than that of other crystal. The dependence of the optical damage resistance on the defect structure was studied. (© 2007 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Photorefractive features of non‐stoichiometry codoped Hf:Fe:LiNbO3 single crystals

Hf(2mol%):Fe(0.05wt%):LiNbO₃ crystals with various [Li]/[Nb] ratios of 0.94, 1.05, 1.2 and 1.38 have been grown. The photorefractive resistant ability increases with the accretion of [Li]/[Nb] ratio. When the ratio of [Li]/[Nb] is 1.20 or 1.38, the OH^‐ absorption band shifts to about 3477cm^‐1. The mechanisms of the photorefractive resistant ability increase and the absorption band shift have been discussed. The exponential gain coefficient (Γ) of the crystals was measured with two‐beam coupling method and the effective charge carrier concentration (N_eff) was calculated. The results show that Γ and N_eff increase with the accretion of [Li]/[Nb] ratio. The temperature effect of codoped Hf:Fe:LiNbO₃ crystals was also studied, it was found that the exponential gain coefficient increase dramatically at about 55°C, 70°C and 110°C, this is due to the inner electric field which is resulted from structure phase change. (© 2007 WILEY ‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Microstructure and optical properties of Zn:Mn:Fe:LiNbO3 crystals

Zn:Mn:Fe:LiNbO₃ crystals were prepared by Czochralski technique. Its microstructure was measured and analyzed by UV‐Vis absorption spectra. The optical damage resistance of Zn:Mn:Fe:LiNbO₃ crystals was characterized by the transmitted beam pattern distortion method. It increases remarkably when the concentration of ZnO is over a threshold concentration. Its value in Zn(7.0 mol%):Mn:Fe:LiNbO₃ crystal is about three orders of magnitude higher that in the Mn:Fe:LiNbO₃ crystal. The dependence of the defects on the optical damage resistance was discussed. The non‐volatile holographic storage was realized in all crystals, and the sensitivity of the Zn(7.0 mol%):Mn:Fe:LiNbO₃ crystal is much higher than that of others. (© 2006 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

[Li]/[Nb]比对Ce:LiNbO3晶体结构及光折变性能的影响

在铌酸锂(LiNbO3,LN)中掺入摩尔分数为0.1;的CeO2,以提拉法从不同[Li]/[Nb]摩尔比([Li]/[Nb]=0.750,0.850,0.946,1.100)的熔体中生长出了Ce:LN晶体.测试了晶体的晶格常数、红外光谱和居里温度.结果表明:随着[Li]/[Nb]比的增加,晶体仍为三方的LN晶体,且晶格常数和晶胞体积没有发生大的变化,v(OH-)振动峰的位置依次向长波方向移动,居里温度依次增加,结构缺陷减少.由于Ce和[Li]/[Nb]比的协同作用,[Li]/[Nb]比为1.100的Ce:LN晶体已接近化学计量比,[Li]/[Nb]比为0.850的Ce:LN晶体的居里温度近似等于纯LN晶体.利用二波耦合光路测试了晶体的衍射效率、写入时间和擦除时间,计算了晶体的光折变灵敏度及动态范围.测试了晶体的抗光致散射能力,结果表明:[Li]/[Nb]比越高的Ce:LN晶体的光折变性能越好.并分析了不同[Li]/[Nb]比Ce:LN晶体光折变性能增强的机理.     

Structure defects and optical damage resistance in doubly doped In:Nd:LiNbO3 crystal waveguide substrates

A series of In:Nd:LiNbO₃ crystals were grown by Czochralski technique and were made into waveguide substrates. The optical damage resistance of the In:Nd:LiNbO₃ waveguide substrates was characterized by measurement of the holographic method. The optical damage resistance of In (3.0 mol%):Nd:LiNbO₃ was much higher than that of other In:Nd:LiNbO₃. The ultraviolet‐visible (UV‐Vis) absorption spectra the In:Nd:LiNbO₃ crystals were measured and investigated. The structure defects were discussed in this paper to explain the enhance of the optical damage resistance in the In:Nd:LiNbO₃ crystals. (© 2003 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

In doping effect on optical properties in Zn:In:Fe:LiNbO3 crystals

A series of Zn:In:Fe:LiNbO₃ crystals were prepared by Czochralski method. The crystal composition and defect structure were analyzed by ICP‐OE/MS, UV–vis and IR spectroscopy. The results show that with increasing In³⁺ doping concentration in melt, the segregation coefficients of both Zn and In ions decrease. The optical damage resistance of Zn:In:Fe:LiNbO₃ crystals was studied by the transmitted beam pattern distortion method. It is found that the optical damage resistance of Zn:In(3mol%):Fe LiNbO₃ crystals is two orders of magnitude higher than that of Zn:Fe:LiNbO₃. (© 2009 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

不同Li/Nb比Mg:In:Fe:LiNbO3晶体的光折变性能研究

采用提拉法生长了不同Li/Nb比(Li/Nb=0.85,0.94,1.05,1.20,1.38)的Mg:In:Fe:LiNbO3(LN)单晶.测试了Mg:In:Fe:LN晶体的红外透射光谱,紫外吸收光谱,抗光致散射能力,响应时间和指数增益系数.实验结果显示:Li/Nb=0.85晶体的OH-吸收峰在3481cm-1附近, Li/Nb=0.94、1.05、1.20的晶体的OH-吸收峰在3505cm-1附近,而Li/Nb=1.38晶体的OH-吸收峰有三个,分别在3466cm-1、3481cm-1和3518cm-1附近.随着Li/Nb比的增大,晶体的紫外吸收边发生紫移,抗光致散射能力增强,响应速度加快,指数增益系数增大.结果表明:Li/Nb=1.38的晶体是性能最为优良的光折变晶体材料.     

Investigation on the blue photorefractive properties varied with MgO codoping in Ru:Fe:LiNbO3 crystals

Mg:Ru:Fe:LiNbO₃ crystals with various doping concentration of MgO have been grown by Czochralski method. The type of charge carriers and photorefractive properties in Mg:Ru:Fe:LiNbO₃ crystals were measured by two‐wave coupling method using Kr⁺ laser (476 nm) and He‐Ne laser (633 nm) as light sources. We found that holes were the dominant charge carriers under blue light irradiation while electrons were the dominant charge carriers under red light irradiation. Mg²⁺ ions behaved no longer as damage resistant, but promoter to the photorefractive properties at 476 nm wavelength. The photorefractive properties under blue light improved with the increase concentration of Mg²⁺ ions. The enhancement mechanisms of the blue photorefractive were suggested. Experimental results definitely showed that Mg‐doped two‐centre Ru:Fe:LiNbO₃ was a promising blue photorefraction material for holographic volume storage.     

Influence of Zn2+ ions concentration on the optical properties of Zn/Er:LiNbO3 crystals

Congruent Er³⁺(3 mol%):LiNbO₃ crystals codoped with ZnO (X mol %, X=0, 3, 6 and 7) were grown by the Czochralski technique. The Er contents in the crystals were measured by an inductively coupled plasma atomic emission spectrometer (ICP‐AES). Under 800 nm excitation, the upconversion emission spectra reveal an enhancement of the green emission with respect to the red emission when the Zn²⁺ ions are introduced into Er:LiNbO₃ crystal. The effect of Zn²⁺ ions concentration on the intensity ratio of the green to red emission has been investigated. Two cross‐relaxation processes (²H_11/2 + ⁴I_13/2 → ⁴I_11/2 + ⁴F_9/2 and ⁴F_7/2 + ⁴I_11/2 → ⁴F_9/2 + ⁴F_9/2) are involved in populating the ⁴F_9/2 state, which bypass the green‐emitting states. The OH^‐ absorption spectra indicate that the Zn²⁺ codoping leads to a decreased concentration of Er³⁺ cluster sites contributing to the enhancement of the green emission. The studies on UV‐vis absorption spectra show that the heavily codoped with Zn²⁺ results in the reformation of the Er³⁺ cluster sites in Er:LiNbO₃. (© 2011 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Improved blue photorefractive properties of near‐stoichiometric LiNbO3:Mn:Fe:Zr crystal

Near‐stoichiometric LiNbO₃ single crystal tri‐doped with ZrO₂, MnO and Fe₂O₃ was grown from Li‐riched melt by Czochralski method. The defect structures and composition of these crystals were analyzed by means of ultraviolet‐visible and infrared transmittance spectra. The appearance of 3466 cm^‐1 peak in infrared spectra showed that the crystal grown from Li‐riched melt was near stoichiometric. The photorefractive properties at the wavelength of 488 nm and 633 nm were investigated with two‐beam coupling experiment, respectively. The experimental results showed that the response speed and sensitivity were enhanced significantly and the high diffraction efficiency was obtained at 488 nm wavelength. This manifested that near‐stoichiometric LiNbO₃:Mn:Fe:Zr crystal was an excellent candidate for holographic storage. (© 2010 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Zn:Fe:LiNbO3晶体的生长及其光学性能的研究

在LiNbO3中掺进ZnO和Fe2O3,以Czochralski技术生长Zn(7mol;):Fe(0.03;):LiNbO3,Zn(3mol;):Fe(0.03;):LiNbO3和Fe(0.03;):LiNbO3晶体.测试晶体的吸收光谱,Zn:Fe:LiNbO3晶体的吸收边相对Fe:LiNbO3晶体发生紫移.测试晶体的红外光谱,Zn(7mol;):Fe:LiNbO3晶体OH-吸收峰移到3529cm-1.测试晶体抗光致散射能力,Zn(3mol;):Fe:LiNbO3晶体抗光致散射能力比Fe:LiNbO3晶体提高一个数量级,Zn(7mol;):Fe:LiNbO3晶体比Fe:LiNbO3晶体高二个数量级.测试晶体的衍射效率和响应时间,Zn:Fe:LiNbO3晶体响应时间缩短,衍射效率降低.对吸收边和OH-吸收峰移动的机理,以及Zn:Fe:LiNbO3晶体抗光致散射能力增强的机理进行了研究.     

Effect of reduction/oxidation treatment on blue photorefraction in In:Fe:Cu:LiNbO3 crystals

In:Fe:Cu:LiNbO₃ crystals with reduced/oxidized treatments were prepared by the Czochralski method. The defect structure was analyzed by the UV‐Visible absorption spectra. The blue photorefractive properties, such as the refractive index change, response time, recording sensitivity, dynamic range as well as two‐wave coupling gain coefficient, were also investigated at 488 nm wavelength using the two‐wave coupling experiment. Comparing the as‐grown and oxidized In:Fe:Cu:LiNbO₃ crystals, the reduced sample has the highest recording sensitivity and largest dynamic range. Meanwhile, the high diffraction efficiency is still maintained. Experimental results definitely show that reduction treatment is an effective method to improve the blue photorefractive performance of In:Fe:Cu:LiNbO₃ crystals. (© 2010 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Double‐frequency properties of In:LiNbO3 crystals

1 mol%, 2 mol%, 3 mol%, 4 mol% and 5 mol% In³⁺ doped LiNbO₃ crystals were grown by the Czochralski method, respectively. Oxidized treatment of some crystals was carried out. The infrared transmission spectra and photo‐damage resistance of the samples were measured. The results showed that the OH^‐ absorption peaks of In(3mol%):LiNbO₃, In(4mol%):LiNbO₃ and In(5mol%):LiNbO₃ crystals were located at about 3508 cm^‐1, while those of In(1mol%):LiNbO₃ and In(2mol%):LiNbO₃ crystals were located at about 3484cm^‐1. When the doped In³⁺ concentration reached its threshold in LiNbO₃ crystal, photo‐damage resistance of In:LiNbO₃ crystals was two orders of magnitude higher than that of pure LiNbO₃ crystal. The experimental results of the second harmonic generation (SHG) showed that the phase matching temperatures of In:LiNbO₃ crystals were lower than those of Zn:LiNbO₃ and Mg:LiNbO₃ crystals and the SHG efficiency reached 38%. Oxidization treatment was also found to make the dark trace resistance of crystals increase. (© 2005 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Growth and optical damage properties of In:Zn:LiNbO3 waveguide substrate

In:Zn:LiNbO₃ crystals doped with different indium concentrations were grown by Czochralski technique. The optical damage threshold value and ultraviolet‐visible absorption spectra of the In:Zn:LiNbO₃ crystals were measured. The In:Zn:LiNbO₃ crystals were made into optical waveguide substrates using hexanedioic acid as proton exchange agent. The optical damage resistant ability of those optical waveguide substrates was investigated by the m‐line method. The optical damage threshold values of In(2mol.%):Zn(3mol.%):LiNbO₃ crystal and optical waveguide substrate are two orders of magnitude higher than those of pure LiNbO₃. (© 2007 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)