Poly(vinylpyrrolidone)‐stabilized silver nanoparticles for strained‐silicon surface enhanced Raman spectroscopy

Poly(vinylpyrrolidone)‐stabilized silver nanoparticles deposited onto strained‐silicon layers grown on graded Si_1−xGe_x virtual substrates are utilized for selective amplification of the Si–Si vibration mode of strained silicon via surface‐enhanced Raman scattering spectroscopy. This solution‐based technique allows rapid, highly sensitive and accurate characterization of strained silicon whose Raman signal would usually be overshadowed by the underlying bulk SiGe Raman spectra. The analysis was performed on strained silicon samples of thickness 9, 17.5 and 42 nm using a 488 nm Ar⁺ micro‐Raman excitation source. The quantitative determination of strained‐silicon enhancement factors was also made. Copyright © 2011 John Wiley & Sons, Ltd.     

A comparative study of surface‐enhanced Raman scattering from silver‐coated anodic aluminum oxide and porous silicon

Three types of Ag‐coated arrays from porous anodic aluminum oxide (AAO) were prepared and studied as substrates for surface‐enhanced Raman scattering (SERS). They were compared with Ag‐coated porous silicon (PSi) samples. AAO‐based substrates were prepared by the vapor deposition of silver directly onto the surface of porous AAO with different morphologies of the pores, whereas SERS‐active island films on the PSi were prepared by immersion plating. The resulting metallic nanostructures were characterized by UV‐vis absorption spectroscopy and scanning electron microscopy (SEM). Thermal evaporation leads to the formation of granular arrays of Ag nanoparticles on the surface of AAO. SERS activity of the substrates was tested using water‐soluble cationic Zn(II)‐tetrakis (4‐N‐methylpyridyl) porphyrin (ZnTMPyP4) as a probe molecule. The results indicate that all AAO‐based substrates studied here exhibit some degree of SERS activity. Noteworthy, for excitation at 532 nm, signals from AAO‐based substrates were comparable with those from the PSi‐based ones, whereas for 441.6 nm excitation they were about twice higher. The strongest SERS‐enhancement at 441.6 nm excitationwas provided by the AAO substrates with silver deposited on the monolith (originally nonporous) side of AAO. Preferential SERS‐enhancement of the bands ascribed to the vibrations of the N‐methylpyridinium group of ZnTMPyP4 when going to blue excitation was found. Copyright © 2010 John Wiley & Sons, Ltd.     

Gold‐coated zinc oxide nanowire‐based substrate for surface‐enhanced Raman spectroscopy

Zinc oxide nanowires with two distinct morphologies were synthesized on silicon substrates using a simple thermal evaporation and vapor transport method in an oxidizing environment. The as‐synthesized nanowires were coated with gold to allow excitation of surface plasmons over a broad frequency range. SERS studies with near‐IR excitation at 785 nm showed significant enhancement (average enhancement > 10⁶) with excellent reproducibility to detect monolayer concentrations of 4‐methylbenzenethiol (4‐MBT) and 1,2‐benzendithiol (1,2‐BDT) probe molecules. The Raman enhancement showed a strong dependence on the gold film thickness, and the peak enhancement was observed for a ∼40‐nm‐thick film. The Raman enhancement was stronger for randomly oriented nanowires compared to aligned ones suggesting the importance of contributions from the junctions of nanowires. Copyright © 2009 John Wiley & Sons, Ltd.     

Surface‐enhanced Raman scattering from gold‐coated germanium oxide nanowires

We utilized bulk‐synthesized nanowires (NWs) of germanium dioxide as nanoscale structures that can be coated with noble metals to allow the excitation of surface plasmons over a broad frequency range. The NWs were synthesized on substrates of silicon using gold‐catalyst‐assisted vapor–liquid–solid (VLS) growth mechanism in a simple quartz tube furnace setup. The resulting NWs have diameters of ∼100–200 nm, with lengths averaging ∼10–40 µm and randomly distributed on the substrate. The NWs are subsequently coated with thin films of gold, which provide a surface‐plasmon‐active surface. Surface‐enhanced Raman scattering (SERS) studies with near‐infrared (NIR) excitation at 785 nm show significant enhancement (average enhancement > 10⁶) with good uniformity to detect submonolayer concentrations of 4‐methylbenzenethiol (4‐MBT), trans‐1,2‐bis(4‐pyridyl)ethylene (BPE), and 1,2‐benzendithiol (1,2‐BDT) probe molecules. We also observed an intense, broad continuum in the Raman spectrum of NWs after metal coating, which tended to diminish with the analyte monolayer formation. Copyright © 2008 John Wiley & Sons, Ltd.     

Microwave monitoring of silver nanoparticle sintering for surface‐enhanced Raman scattering substrates

One of the most widely used methods for surface‐enhanced Raman scattering (SERS) employs silver or gold nanoparticles either in colloidal suspension or in the dry‐drop form. In such substrates the SERS amplification factors depend critically on the interparticle distances. Here, we report that microwave absorption as a function of temperature in dry‐drop substrates can be used as a probe to demarcate temperature regions for thermal annealing to produce SERS substrates with very high amplification factors. Copyright © 2011 John Wiley & Sons, Ltd.     

Analysis of alizarin by surface‐enhanced and FT‐Raman spectroscopy

This paper presents the application of Raman spectroscopy (RS) for the structural study of alizarin adsorbed on a metallic surface. As a biologically active molecule, alizarin has remarkable antigenotoxic activity like other anthraquinone dyes. Alizarin is highly fluorescent and that limits the application of RS as an investigation method; however, the Fourier transform‐RS (FTRS) can be applied since the near‐infrared excitation line lies far away from the absorption region of alizarin. The surface enhanced‐RS (SERS) technique also makes the fluorescence quenching possible. In this work, monolayers of alizarin were deposited on the surface of an electrode by the immersion of silver substrates in methanolic solution of the analyte. From such prepared samples, by using the excitation of 488, 514.5 and 647.1 nm the Raman spectra were registered. Depending on the excitation line, SERS or surface‐enhanced resonance Raman scattering (SERRS) spectra of alizarin were observed. The interpretation of experimental data was supported by theoretical calculations. Copyright © 2008 John Wiley & Sons, Ltd.     

Silver‐capped silicon nanopillar platforms for adsorption studies of folic acid using surface enhanced Raman spectroscopy and density functional theory

The study of the interactions of folic acid (FA) with surface enhanced Raman scattering substrates is relevant for understanding its adsorption mechanism and for fabricating analytical devices for detection of malignant cells over‐expressing folate receptors. This paper presents a study of the adsorption of FA on silver‐capped silicon nanopillar substrates employing surface enhanced Raman scattering spectroscopy and density functional theory calculations. The experimentally observed vibrations from free FA and FA bound to the Ag surface display different vibrational spectra indicating chemical interaction of the molecule with the metal surface. Density functional theory calculations show that the Ag–FA interaction is primarily through the nitrogen from the pteridine ring anchoring to the Ag metal surface. To investigate the Ag–FA binding behavior further, the adsorption isotherm of FA on the silver‐capped silicon nanopillar surface is estimated. The results show a positive cooperative Ag–FA binding mechanism. That is, adsorbed FA increases the affinity of new incoming FA molecules. Copyright © 2015 John Wiley & Sons, Ltd.     

SERS active Ag nanoparticles in mesoporous silicon: detection of organic molecules and peptide–antibody assays

Ag nanoparticles synthesized on porous silicon samples were studied and applied as substrates for surface‐enhanced Raman scattering (SERS). The metallic nanostructures prepared by immersion plating were characterized by UV–Vis reflectance spectroscopy and scanning electron microscopy. SERS activity of the substrates was tested using Cyanine dye 1,3,3,1′,3′,3′‐esamethyl‐5,5′‐dimethoxyindodicarbocyanine iodide (Cy5‐OCH₃) as a probe molecule. The Raman spectra obtained for different excitation wavelengths indicate amplifications ascribed to plasmonic resonances with an enhancement factor up to 10⁷. CGIYRLRS peptides were chemisorbed on the Ag nanoparticles with the plasmonic resonance tuned at the excitation energy. Such oligopeptides were used as baits for a specific polyclonal antibody. The overall Raman enhancement allowed to evidence a good selectivity to the target analyte as required by most of the SERS applications on biological assays. Copyright © 2011 John Wiley & Sons, Ltd.     

Use of atomic layer deposition to improve the stability of silver substrates for in situ,high‐temperature SERS measurements

A method to stabilize silver surface‐enhanced Raman spectroscopy (SERS) substrates for in situ, high‐temperature applications is demonstrated. Silver island films grown by thermal evaporation were coated with a thin layer (from 2.5 to 5 nm) of alumina by atomic layer deposition (ALD), which protects and stabilizes the SERS‐active substrate without eliminating the Raman enhancement. The temporal stability of the alumina‐coated silver island films was examined by measurement of the Raman intensity of rhodamine 6G molecules deposited onto bare and alumina‐coated silver substrates over the course of 34 days. The coated substrates showed almost no change in SERS enhancement, while the uncoated substrates exhibited a significant decrease in Raman intensity. To demonstrate the feasibility of the alumina‐coated silver substrate as a probe of adsorbates and reactions at elevated temperatures, an in situ SERS measurement of calcium nitrate tetrahydrate on bare and alumina‐coated silver was performed at temperatures ranging from 25 to 400 °C. ALD deposition of an ultrathin alumina layer significantly improved the thermal stability of the SERS substrate, thus enabling in situ detection of the dehydration of the calcium nitrate tetrahydrate at an elevated temperature. Despite some loss of Raman signal, the coated substrate exhibited greater thermal stability compared to the uncoated substrate. These experiments show that ALD can be used to synthesize stable SERS substrates capable of measuring adsorbates and processes at high temperature. Copyright © 2009 John Wiley & Sons, Ltd.     

Microstructured polymer‐based substrates with broadband absorption for surface‐enhanced Raman scattering

Large area (3 × 3 cm²) substrates for surface‐enhanced Raman scattering were fabricated by combining femtosecond laser microstructuring and soft lithography techniques. The fabrication procedure is as follows: (i) femtosecond laser machining is used to create a silicon master copy, (ii) replicates from polydimethylsiloxane are made, and (iii) a 50‐nm‐thick gold film is deposited on the surface of the replicates. The resulting substrates exhibit strongly enhanced absorption in the spectral region of 350 ∼ 1000 nm and generate enhanced Raman signal with enhancement factor of the order of 10⁷ for 10^{‐ 6} M rhodamine 6G. The main advantages of our substrates are low cost, large active area, and possibility for mass replication. Copyright © 2013 John Wiley & Sons, Ltd.     

Study of Raman spectrum of uranium using a surface‐enhanced Raman scattering technique

Raman spectroscopic investigation on weak scatterers such as metals is a challenging scientific problem. Technologically important actinide metals such as uranium and plutonium have not been investigated using Raman spectroscopy possibly due to poor signal intensities. We report the first Raman spectrum of uranium metal using a surface‐enhanced Raman scattering‐like geometry where a thin gold overlayer is deposited on uranium. Raman spectra are detected from the pits and scratches on the sample and not from the smooth polished surface. The 514.5‐ and 785‐nm laser excitations resulted in the Raman spectra of uranium metal whereas 325‐nm excitation did not give rise to such spectra. Temperature dependence of the B_3g mode at 126 cm⁻¹ is also investigated. Copyright © 2011 John Wiley & Sons, Ltd.     

Drop‐coating deposition Raman spectroscopy of porphyrins

We report an improvement of the Raman detection sensitivity of porphyrins by factor of 10⁵ using drop‐coating deposition Raman spectroscopy (DCDR). We were able to obtain Raman spectra from ~20 nM initial (deposited) concentrations of cationic and anionic porphyrin. This detection limit is comparable with or even better than that of surface‐enhanced Raman scattering spectroscopy using Ag nanoparticles. Moreover, DCDR spectrum of protoporphyrin IX, which is known as a marker in clinical diagnostics of cancer, was also obtained from 10 nM deposited concentration. To our knowledge, it is the first demonstration of the resonance DCDR spectroscopy. Copyright © 2015 John Wiley & Sons, Ltd.     

Glass‐embedded silver nanoparticle patterns by masked ion‐exchange process for surface‐enhanced Raman scattering

Glass‐embedded silver nanoparticle patterns were fabricated by masked silver–sodium ion‐exchange process followed by etching to reveal the particles for surface‐enhanced Raman scattering (SERS). The intensity of the enhanced Raman signal is comparable to that of the fluorescence, and the detection limit of 1 nM for Rhodamine 6G has been achieved. Raman images at different etching depths and corresponding morphological images are compared to find optimal SERS signal. Our results demonstrate that silver nanoparticle patterns embedded in glass can be used as SERS‐active substrates. Nanoparticles can be formed in a glass of high optical quality and have potential to be integrated with optical waveguides for a sensor chip. Copyright © 2010 John Wiley & Sons, Ltd.     

A hybrid substrate for surface‐enhanced Raman scattering spectroscopy: coupling metal nanoparticles to strong localised fields on a micro‐structured surface

Electromagnetic coupling between localised plasmons on metal nanoparticles and the strong localised fields on a micro‐structured surface is demonstrated as a means to increase the enhancement factor in surface‐enhanced Raman scattering (SERS) spectroscopy. Au nanoparticles of diameter 20 nm were deposited on a micro‐structured Au surface consisting of a periodic array of square‐based pyramidal pits (Klarite). The spectra of 4‐aminothiophenol (4‐ATP) were compared before and after deposition of Au nanoparticles on the micro‐structured surface. The addition of Au nanoparticles is shown to provide significantly higher signal intensities, with improvements of the order of ∼10³ per molecule compared with spectra obtained from the micro‐structured substrate alone. This hybrid approach offers promise for combining nanoparticles with micro‐ and nano‐structured surfaces in order to design SERS substrates with higher sensitivities. Copyright © 2011 John Wiley & Sons, Ltd.     

Nanostructured gold surfaces as reproducible substrates for surface‐enhanced Raman spectroscopy

Raman spectroscopy is a common tool for the qualitative and quantitative chemical analysis of molecules. Although the unique identification of molecules is possible via their vibrational lines, high concentrations (mmol/l) are needed for their nonresonant excitation owing to their low scattering cross section. The intensity of the Raman spectra is amplified by the use of the surface‐enhanced Raman scattering (SERS) technique. While the use of silver sols results only in a limited reproducibility of the Raman line intensities, lithographically designed, nanostructured gold surfaces used as SERS‐active substrates should, in principle, combine the high sensitivity with better reproducibility. For this purpose, we have produced gratings of gold dots on Si(001) surfaces by means of electron beam lithography. Qualitative and quantitative investigations of crystal violet (CV) performed using nanostructured surfaces give high reproducibility and enhancement of the Raman lines. The substrates are reusable after cleaning; all results presented could be obtained from a single SERS substrate. For the experiments very low laser powers were used. Copyright © 2006 John Wiley & Sons, Ltd.     

Photonic nanojet‐mediated SERS technique for enhancing the Raman scattering of a few molecules

We report a two‐step enhancement of Raman scattering signal (η) of a few dye molecules. In the first step, high‐quality surface‐enhanced Raman scattering (SERS) substrates have been used. The SERS substrates were fabricated by direct current sputtering of Au followed by thermal annealing. The role of thermal annealing of the SERS substrates and numerical aperture of Raman microscopic objective lens on the enhancement has been studied for optimizing the enhancement in the SERS technique. In the second step, the value of η obtained with conventional SERS technique has been improved significantly with the help of photonic nanojet (PNJ) of an optical microsphere (PNJ‐mediated SERS technique). The signal to noise ratio and reproducibility of the experimental results have been found to be very high. Based on our theoretical simulations on PNJ, a few suitable parameters have been proposed for obtaining better enhancement using this technique. To the best of our belief, this report will enable the SERS community to improve η value with ease. Copyright © 2016 John Wiley & Sons, Ltd.     

Preparation of silver nanoparticles on zinc oxide nanowires by photocatalytic reduction for use in surface‐enhanced Raman scattering measurements

To increase the sensitivity in surface‐enhanced Raman scattering (SERS) measurements, the high surface area of zinc oxide nanowires (ZnO NWs) was used. ZnO NWs on silicon substrates were prepared and used as substrates for further growth of silver nanoparticles (AgNPs). Ultraviolet (UV) irradiation was used to reduce silver ions to AgNPs on the ZnO wires. With proper growth conditions for both ZnO NWs and AgNPs, the substrates exhibit SERS enhancement factors greater than 10⁶. To understand the influences of the morphologies of the ZnO NWs on the growth of AgNPs, the growing time and temperature were varied. The concentration of silver nitrate and irradiation time of UV radiation were also varied. The resulting AgNPs were probed with para‐nitrothiophenol to quantify the SERS enhancements obtained from the varying conditions. The results indicate that ZnO NWs could be grown at temperatures higher than 490 °C and higher growth temperatures result in smaller diameter of the formed ZnO NWs. Also, the morphologies of ZnO NWs did not significantly alter the SERS signals. The concentration of silver nitrate affects the SERS signals significantly and the optimal concentration was found to be in the range of 10–20 mM. With irradiation times longer than 90 s, the resulting AgNPs showed similar SERS intensities. With optimized conditions, the AgNPs/ZnO substrates are highly suitable for SERS measurements with a typical enhancement factor of higher than 10⁶. Copyright © 2010 John Wiley & Sons, Ltd.     

Surface‐enhanced Raman scattering and DFT calculations studies of 3,3′‐diethylthiatri‐ carbocyanine iodide

As an infrared Raman probe, the molecule 3,3′‐diethylthiatricarbocyanine iodide (DTTC) has received much attention in the past decades due to its potential applications in Raman imaging, single‐cell detection, cancer diagnosis, and surface‐enhanced Raman scattering (SERS). In this work, ordinary Raman, SERS, and theoretical Raman spectra were investigated to estimate the DTTC suspension. More specifically, the original gold nanospheres (60 nm diameter) and gold nanorods were encoded with DTTC and stabilized with a layer of thiol–polyethylene glycol as Raman reporter; SERS data were also obtained from the samples. Hartree–Fock theory and density functional theory (DFT) calculation were applied to calculate the optimized Raman spectra of DTTC in water on the B3LYP/6‐31G level. Subsequently, the obtained experimental spectra from DTTC were carefully compared with the theoretically calculated spectra, and good agreement was obtained between the theoretical and experimental results.The bands between 500 and 3100 cm⁻¹ in the ordinary Raman and SERS spectra were assigned as well. This work will facilitate the development of ultrasensitive SERS probes for advanced biomedical imaging applications. Copyright © 2011 John Wiley & Sons, Ltd.     

Stamping plasmonic nanoarrays on SERS‐supporting platforms

The dielectric property of a nanoparticle‐supporting film has recently garnered attention in the fabrication of plasmonic surfaces. A few studies have shown that the localized surface plasmon resonance (LSPR), and hence surface‐enhanced Raman scattering (SERS), strongly depends on the substrate refractive index. In order to create higher efficiency SERS‐active surfaces, it is therefore necessary to consider the substrate property along with nanoparticle morphology. However, due to certain limitations of conventional lithography, it is often not feasible to create well‐defined plasmonic nanoarrays on a substrate of interest. Here, an additive nanofabrication technique, i.e., nanotransfer printing (nTP), is implemented to integrate electron beam lithography (EBL) defined high‐aspect‐ratio nanofeatures on a variety of SERS‐supporting surfaces. With the aid of suitable surface chemistries, a wide range of plasmonic particles were successfully integrated on surfaces of three physically and chemically distinct dielectric materials, namely, polydimethyl siloxane (PDMS), SU‐8 photoresist, and glass surfaces, using silicon‐based relief pillars. These nTP‐created metal nanoparticles strongly amplify the Raman signal and complement the selection of suitable substrates for better SERS enhancement. Our experimental observations are also supported by theoretical calculations. The implementation of nTP to stamp out metal nanoparticles on a multitude conventional/unconventional substrates has novel applications in designing in‐built plasmonic microanalytical devices for SERS sensing and other related photonic studies. Copyright © 2011 John Wiley & Sons, Ltd.     

Surface‐enhanced Raman scattering investigations on silver nanoparticles deposited on alumina and titania nanotubes: influence of the substrate material on surface‐enhanced Raman scattering activity of Ag nanoparticles

Silver nanoparticles deposited on various ‘inert’ porous materials (mainly Al₂O₃ and TiO₂) are often used as substrates for surface‐enhanced Raman scattering (SERS) measurements. In this study, we used the sputter deposition technique to cover tubular arrays of Al₂O₃ and TiO₂ with Ag nanoparticles. Raman spectra of pyridine (as a probe molecule) and of two selected dyes (5‐(4‐dimethylaminobenzylidene)rhodanine and 5‐(4‐(dimethylamino)benzylidene)‐3‐(3‐methoxypropyl)rhodanine) adsorbed on fabricated Ag/TiO₂‐n/Ti and Ag/Al₂O₃‐n/Al substrates were measured. We found that the SERS spectra of pyridine adsorbed on Ag nanoparticles deposited on an Al₂O₃‐n/Al substrate are distinctly different from those measured for an Ag/TiO₂‐n/Ti composite. Similar effects were observed for dyes adsorbed on the surface of both composites. The spectral differences between two kinds of composites (Ag/TiO₂‐n/Ti and Ag/Al₂O₃‐n/Al) are discussed in terms of (1) the modified electronic structure of the Ag nanoparticles due to their interaction with different substrate materials and (2) the different atomic topology of the metal particles thus deposited on the surfaces of the substrates. Composite samples were also studied with the aid of scanning electron microscopy (SEM) and Auger electron spectroscopy (AES) to reveal their characteristic morphological and chemical features. Copyright © 2012 John Wiley & Sons, Ltd.