High-yield synthesis and characterization of monodisperse sub-microsized CoFe2O4 octahedra

In this study, sub-microsized CoFe₂O₄ octahedra with a high yield are synthesized via a simple hydrothermal route under mild conditions. The as-prepared products are characterized by conventional techniques of XRD, SEM, TEM, ED and HR-TEM. The results show that the as-synthesized sample exhibits octahedral morphology with a narrow size distribution. The edge size of CoFe₂O₄ octahedra is estimated to be about 0.10-0.14 μm. The growth process is also monitored by time and temperature-dependent observation. It is found that the reaction temperature has no obvious influence on the product morphology but a significant effect on the size of CoFe₂O₄ octahedra, while the reaction time determines the final morphology of the product. Moreover, it is displayed that the citrate ions play a key role in the formation of CoFe₂O₄ octahedra. Furthermore, the possible growth mechanism of the sub-microsized CoFe₂O₄ octahedra is discussed on the basis of a series of experiments. Magnetic measurements show that sub-micro-sized CoFe₂O₄ octahedra exhibit obvious ferromagnetic behaviors. The saturation magnetization (M_s), remanent magnetization (M_r), and coercivity (H_c) are determined to be 85.8, 29.2 emu/g and 892 Oe, respectively.     

Preparation of magnetic CoFe2O4-functionalized graphene sheets via a facile hydrothermal method and their adsorption properties

Magnetic CoFe₂O₄-functionalized graphene sheets (CoFe₂O₄-FGS) nanocomposites have been synthesized by hydrothermal treatment of inorganic salts and thermal exfoliated graphene sheets. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) observations show that cobalt ferrite nanoparticles with sizes of 10-40 nm are well dispersed on graphene sheets. OH⁻ was recognized as a tie to integrate the inorganic salts with the graphene sheets, which made reaction started and developed on the surface of graphene sheets and formed cobalt ferrite nanoparticles on graphene sheets. The adsorption kinetics investigation revealed that the adsorption of methyl orange from aqueous solution over the as-prepared CoFe₂O₄-FGS nanocomposites followed pseudo-second-order kinetic model and the adsorption capacity was examined as high as 71.54 mg g⁻¹. The combination of the superior adsorption of FGS and the magnetic properties of CoFe₂O₄ nanoparticles can be used as a powerful separation tool to deal with water pollution.     

β−cyclodextrins-based inclusion complexes of CoFe2O4 magnetic nanoparticles as catalyst for the luminol chemiluminescence system and their applications in hydrogen peroxide detection

β−cyclodextrins (β−CD)-based inclusion complexes of CoFe₂O₄ magnetic nanoparticles (MNPs) were prepared and used as catalysts for chemiluminescence (CL) system using the luminol-hydrogen peroxide CL reaction as a model. The as-prepared inclusion complexes were characterized by XRD (X-ray diffraction), TGA (thermal gravimetric analysis) and FT-IR. The oxidation reaction between luminol and hydrogen peroxide in basic media initiated CL. The effect of β−CD-based inclusion complexes of CoFe₂O₄ magnetic nanoparticles and naked CoFe₂O₄ magnetic nanoparticles on the luminol-hydrogen peroxide CL system was investigated. It was found that inclusion complexes between β−CD and CoFe₂O₄ magnetic nanoparticles could greatly enhance the CL of the luminol-hydrogen peroxide system. Investigation on the kinetic curves and the chemiluminescence spectra of the luminol-hydrogen peroxide system demonstrates that addition of CoFe₂O₄ MNPs or inclusion complexes between β−CD and CoFe₂O₄ MNPs does not produce a new luminophor of the chemiluminescent reaction. The luminophor for the CL system was still the excited-state 3-aminophthalate anions (3-APA*). The enhanced CL signals were thus ascribed to the possible catalysis from CoFe₂O₄ MNPs or inclusion complexes between β−CD and CoFe₂O₄ nanoparticles. The feasibility of employing the proposed system for hydrogen peroxide sensing was also investigated. Experimental results showed that the CL emission intensity was linear with hydrogen peroxide concentration in the range of 1.0 × 10⁻⁷ to 4.0 × 10⁻⁶ mol L⁻¹ with a detection limit of 2.0 × 10⁻⁸ mol L⁻¹ under optimized conditions. The proposed method has been used to determine hydrogen peroxide in water samples successfully.     

Synthesis of MnOOH nanorods by cluster growth route from [Mn12O12(RCOO)16(H2O)n] (R=CH3, C2H5). Rational conversion of MnOOH into Mn3O4 or MnO2 Nanorods

Single-crystalline nanorods of γ-MnOOH (manganite) phase with diameters of 120 nm and lengths of 1100 nm have been prepared using a new cluster growth route under low-temperature hydrothermal conditions starting from [Mn₁₂O₁₂(CH₃COO)₁₆(H₂O)₄]·2CH₃COOH·4H₂O or [Mn₁₂O₁₂(C₂H₅COO)₁₆(H₂O)₃]·4H₂O without any catalyst or template agents. The so-obtained nanorods were studied by X-ray diffraction (XRD), infrared (IR) spectroscopy, Raman spectroscopy and high resolution transmission electron microscopy (HRTEM). Their thermal conversion opens an access to Mn₃O₄ (hausmannite) and β-MnO₂ (pyrolusite) nanorods, respectively, under argon or air atmosphere. A coercive field of 12.4 kOe was obtained for the Mn₃O₄ nanorods.     

Fabrication, characterization and magnetic behaviour of alumina-doped zinc ferrite nano-particles

Zinc ferrite nano-powders with a nominal composition of ZnFe₂O₄ were prepared by combustion synthesis using mixture of urea and ammonium nitrate as fuel. The influence of alumina-doping on the structural, morphological and magnetic properties of ZnFe₂O₄ nano-particles was investigated by means of X-ray powder diffraction (XRD), infrared (IR) spectroscopy, scanning and transmission electron microscopy (SEM and TEM) and vibrating sample magnetometer (VSM). XRD and IR analyses confirm the cubic spinel phase of ZnFe₂O₄ nano-particles. The Zn ferrite presented a uniform microstructure with grain size in nano-scale. Alumina-doping brought about a change in the morphology of the as prepared ferrite from sphere-like to regular hexagon. Al₂O₃-treatment led to a decrease in the coercivity (H_c), magnetization (M_s) and magnetic moment (n_B) of the investigated system. The maximum decrease in the values of H_c, M_s and n_B due to the treatment with 1.5 wt% Al₂O₃ attained 13.5, 17.4 and 13.5%, respectively. The observed results can be explained on the basis of particle size and the Fe³⁺ concentration in the octahedral and tetrahedral sites involved in the cubic spinel structure.     

Ultrasonic-assisted synthesis of PMMA/Ni0.5Zn0.5Fe2O4 nanocomposite in mixed surfactant system

PMMA/Ni_0.5Zn_0.5Fe₂O₄ nanocomposite with superparamagnetic behavior was synthesized by in situ emulsion polymerization of methylmethacrylate (MMA) monomer in the presence of Ni_0.5Zn_0.5Fe₂O₄ colloidal suspension assisted by ultrasonic irradiation. The obtained samples were characterized by X-ray diffraction (XRD), Fourier transform infrared spectra (FT-IR), transmission electron microscopy (TEM) and vibrating sample magnetometer (VSM). XRD and FT-IR spectra confirmed the formation of PMMA/Ni_0.5Zn_0.5Fe₂O₄ nanocomposite. TEM images showed that Ni_0.5Zn_0.5Fe₂O₄ nanoparticles with the particle sizes of about 12 nm were well dispersed in the polymer matrix. The nanocomposite at room temperature exhibited superparamagnetic behavior under applied magnetic field. The formation mechanism of PMMA/Ni_0.5Zn_0.5Fe₂O₄ nanocomposite was proposed as well.     

Series of compositions Bi2(M′xM1−x)4O9 (M′, M=Al, Ga, Fe; 0≤x≤1) with mullite-type crystal structure: Synthesis, characterization and O/O exchange experiment

Series of compositions Bi₂(M′_xM_1−x)₄O₉ with x=0.0, 0.1,…, 1.0 and M′/M=Ga/Al, Fe/Al and Fe/Ga were synthesized by dissolving appropriate amounts of corresponding metal nitrate hydrates in glycerine, followed by gelation, calcination and final heating at 800 °C for 24 h. The new compositions with M′/M=Ga/Al form solid-solution series, which are isotypes to the two other series M′/M=Fe/Al and Fe/Ga. The XRD data analysis yielded in all cases a linear dependence of the lattice parameters related on x. Rietveld structure refinements of the XRD patterns of the new compounds, Bi₂(Ga_xAl_1−x)₄O₉ reveal a preferential occupation of Ga in tetrahedral site (4 h). The IR absorption spectra measured between 50 and 4000 cm⁻¹ of all systems show systematic shifts in peak positions related to the degree of substitution. Samples treated in ¹⁸O₂ atmosphere (16 h at 800 °C, 200 mbar, 95% ¹⁸O₂) for ¹⁸O/¹⁶O isotope exchange experiments show a well-separated IR absorption peak related to the M-¹⁸O_c-M vibration, where O_c denotes the common oxygen of two tetrahedral type MO₄ units. The intensity ratio of M-¹⁸O_c/M-¹⁶O_c IR absorption peaks and the average crystal sizes were used to estimate the tracer diffusion coefficients of polycrystalline Bi₂Al₄O₉ (D=2×10⁻²² m²s⁻¹), Bi₂Fe₄O₉ (D=5×10⁻²¹ m²s⁻¹), Bi₂(Ga/Al)₄O₉ (D=2×10⁻²¹ m²s⁻¹) and Bi₂Ga₄O₉ (D=2×10⁻²⁰ m²s⁻¹).     

Synthesis, structure and magnetic properties of the S=1/2, one-dimensional antiferromagnet, Y5Re2O12

Single crystals of Y₅Re₂O₁₂ have been grown, and the crystal structure has been determined by X-ray diffraction. This compound crystallizes in space group C2/m with cell dimensions of a=12.4081(10) Å b=5.6604(5)Å, c=7.4951(6) Å, β=107.837(3)°, Z=2. The final refinement led to R1=0.0238, WR2=0.0459 for 1053 observed reflections with F>4σ(F₀). Edge-sharing ReO₆ octahedra form infinite linear [ReO₂O_4/2]_n chains along the b direction with alternating short and long Re-Re distances. Three crystallographically independent yttrium atoms surround O2 to form OY₄ tetrahedra, which share edges and corners in the ab plane to form a two-dimensional Y₅O₄ network which separates the [ReO₂O_4/2]_n magnetic chains. This compound is therefore isostructural with the series Ln₅Re₂O₁₂Ln=Gd-Lu, which have been known since 1969. The average Re oxidation state is +4.5 in the chains and a reasonable, if qualitative MO scheme results in one unpaired electron per Re dimer. Consistent with this, magnetic susceptibility data can be fitted to the one-dimensional antiferromagnetic Heisenberg model with S=1/2 and parameters J^intra/k=−89(1)K, g=2.15(4) and χ(TIP)=5(1)×10⁻⁴ emu/mol. There is no sign of long-range magnetic order down to 2 K. These results are contrasted with those for the isostructural Y₅Mo₂O₁₂.     

Magnetic and charge transport properties of the Na-based Os oxide pyrochlore

The Na-based osmium oxide pyrochlore was synthesized for the first time by an ion-exchange method using KOs₂O₆ as a host. The composition was identified as Na_1.4Os₂O₆·H₂O by electron probe micro-analysis, thermogravimetric analysis, and structural analysis using synchrotron X-ray diffraction. Na_1.4Os₂O₆·H₂O crystallizes in a regular pyrochlore structure with some defects (space group: Fd-3m, a=10.16851(1) Å). Electrical resistivity, heat capacity, and magnetization measurements clearly showed absence of superconductivity down to 2 K, being in large contrast to what was found for the β-type pyrochlore superconductor AOs₂O₆ (A=Cs, Rb, and K). The Sommerfeld coefficient is 22 mJ K⁻² mol⁻¹, being the smallest among AOs₂O₆. A magnetic anomaly at ∼57 K and associated magneto-resistance (+3.7% at 2 K in 70 kOe) were found.     

Controlled assembly of superparamagnetic iron oxide nanoparticles on electrospun PU nanofibrous membrane: A novel heat-generating substrate for magnetic hyperthermia application

A facile method of fabricating novel heat-generating membranes composed of electrospun polyurethane (PU) nanofibers decorated with superparamagnetic iron oxide nanoparticles (NPs) is reported. Electrospinning was used to produce polymeric nanofibrous matrix, whereas polyol immersion technique allowed in situ assembly of well-dispersed Fe₃O₄ NPs on the nanofibrous membranes without any surfactant, and without sensitizing and stabilizing reagent. The assembly phenomena can be explained by the hydrogen-bonding interactions between the amide groups in the PU matrix and the hydroxyl groups capped on the surface of the Fe₃O₄ NPs. The prepared nanocomposite fibers showed acceptable magnetization value of 33.12 emu/g, after measuring the magnetic hysteresis loops using SQUID. Moreover, the inductive heating property of electrospun magnetic nanofibrous membranes under an alternating current (AC) magnetic field was investigated. We observed a progressive increase in the heating rate with the increase in the amount of magnetic Fe₃O₄ NPs in/on the membranes. The present electrospun magnetic nanofibrous membrane may be a potential candidate as a novel heat-generating substrate for localized hyperthermia cancer therapy.     

Growth of La2CuO4 nanofibers under a mild condition by using single walled carbon nanotubes as templates

La₂CuO₄ nanofibers (ca. 30 nm in diameter and 3 μm in length) have been grown in situ by using single walled carbon nanotubes (SWNTs; ca. 2 nm in inner diameter; made via cracking CH₄ over the catalyst of Mg_0.8Mo_0.05Ni_0.10Co_0.05O_x at 800 °C) as templates under mild hydrothermal conditions and a temperature around 60 °C. During synthesis, the surfactant poly(ethylene glycol)-block-poly(propylene glycol)-block-poly(ethylene glycol) and H₂O₂ were added to disperse SWNTs and oxidize the reactants, respectively. The structure of La₂CuO₄ nanofibers was confirmed by powder X-ray diffraction (XRD) and their morphologies were observed with field emission scanning electron microscope (FESEM) at the hydrothermal synthesis lasting for 5, 20 and 40 h, respectively. The La₂CuO₄ crystals grew from needle-like (5 h) through stick-like (20 h) and finally to plate-like (40 h) fibers. Twenty hours is an optimum reaction time to obtain regular crystal fibers. The La₂CuO₄ nanofibers are probably cubic rather than round and may capsulate SWNTs.     

A chitosan–polypyrrole magnetic nanocomposite as μ-sorbent for isolation of naproxen

An extracting medium based on chitosan–polypyrrole (CS–PPy) magnetic nanocomposite was synthesized by chemical polymerization of pyrrole at the presence of chitosan magnetic nanoparticles (CS-MNPs) for micro-solid phase extraction. In this work, magnetic nanoparticles, the modified CS-MNPs and different types of CS–PPy magnetic nanocomposites were synthesized. Extraction efficiency of the CS–PPy magnetic nanocomposite was compared with the CS-MNPs and Fe₃O₄ nanoparticles for the determination of naproxen in aqueous samples, via quantification by spectrofluorimetry. The scanning electron microscopy images obtained from all the prepared nanocomposites revealed that the CS–PPy magnetic nanocomposite possess more porous structure. Among different synthesized magnetic nanocomposites, CS–PPy magnetic nanocomposite showed a prominent efficiency. Influencing parameters on the morphology of CS–PPy magnetic nanocomposite such as weight ratio of components was also assayed. In addition, effects of different parameters influencing the extraction efficiency of naproxen including desorption solvent, desorption time, amount of sorbent, ionic strength, sample pH and extraction time were investigated and optimized. Under the optimum condition, a linear calibration curve in the range of 0.04–10 μg mL⁻¹ (R² = 0.9996) was obtained. The limits of detection (3S_b) and limits of quantification (10S_b) of the method were 0.015 and 0.04 μg mL⁻¹ (n = 3), respectively. The relative standard deviation for water sample spiked with 0.1 μg mL⁻¹ of naproxen was 3% (n = 5) and the absolute recovery was 92%. The applicability of method was extended to the determination of naproxen in tap water, human urine and plasma samples. The relative recovery percentages for these samples were in the range of 56–99%.     

Structure and properties of the CaFe2O4-type cobalt oxide CaCo2O4

The calcium cobalt oxide CaCo₂O₄ was synthesized for the first time and characterized from a powder X-ray diffraction study, measuring magnetic susceptibility, specific heat, electrical resistivity, and thermoelectric power. CaCo₂O₄ crystallizes in the CaFe₂O₄ (calcium ferrite)-type structure, consisting of an edge- and corner-shared CoO₆ octahedral network. The structure of CaCo₂O₄ belongs to an orthorhombic system (space group: Pnma) with lattice parameters, a=8.789(2) Å, b=2.9006(7) Å and c=10.282(3) Å. Curie-Weiss-like behavior in magnetic susceptibility with the nearly trivalent cobalt low-spin state (Co³⁺, 3d, S=0), semiconductor-like temperature dependence of resistivity (ρ=3×10⁻¹ Ω cm at 380 K) with dominant hopping conduction at low temperature, metallic-temperature-dependent large thermoelectric power (Seebeck coefficient: S=+147 μV/K at 380 K), and Schottky-type specific heat with a small Sommerfeld constant (γ=4.48(7) mJ/Co mol K²), were observed. These results suggest that the compound possesses a metallic electronic state with a small density of states at the Fermi level. The doped holes are localized at low temperatures due to disorder in the crystal. The carriers probably originate from slight off-stoichiometry of the phase. It was also found that S tends to increase even more beyond 380 K. The large S is possibly attributed to residual spin entropy and orbital degeneracy coupled with charges by strong electron correlation in the cobalt oxides.     

Transition metal tetramolybdate dihydrates MMo4O13·2H2O (M=Co,Ni) having a novel pillared layer structure

Hydrothermal synthesis in the M/Mo/O (M=Co,Ni) system was investigated. Novel transition metal tetramolybdate dihydrates MMo₄O₁₃·2H₂O (M=Co,Ni), having an interesting pillared layer structure, were found. The molybdates crystallize in the triclinic system with space group P−1, Z=1 with unit cell parameters of a=5.525(3) Å, b=7.058(4) Å, c=7.551(5) Å, α=90.019(10)°, β=105.230(10)°, γ=90.286(10)° for CoMo₄O₁₃·2H₂O, and a=5.508(2) Å, b=7.017(3) Å, c=7.533(3) Å, α=90.152(6)°, β=105.216(6)°, γ=90.161(6)° for NiMo₄O₁₃·2H₂O The structure is composed of two-dimensional molybdenum-oxide (2D Mo-O) sheets pillared with CoO₆ octahedra. The 2D Mo-O sheet is made up of infinite straight ribbons built up by corner-sharing of four molybdenum octahedra (two MoO₆ and two MoO₅OH₂) sharing edges. These infinite ribbons are similar to the straight ones in triclinic-K₂Mo₄O₁₃ having 1D chain structure, but are linked one after another by corner-sharing to form a 2D sheet structure, like the twisted ribbons in BaMo₄O₁₃·2H₂O (or in orthorhombic-K₂Mo₄O₁₃) are.     

Metallic Re-Re bond formation in different MRe2O6 (MFe, Co, Ni) rutile-like polymorphs: The role of temperature in high-pressure synthesis

Different polymorphs of MRe₂O₆ (MFe, Co, Ni) with rutile-like structures were prepared using high-pressure high-temperature synthesis. For syntheses temperatures higher than ∼1573 K, tetragonal rutile-type structures (P4₂/mnm) with a statistical distribution of M- and Re-atoms on the metal position in the structure were observed for all three compounds, whereas rutile-like structures with orthorhombic or monoclinic symmetry, partially ordered M- and Re-ions on different sites and metallic Re-Re-bonds within Re₂O₁₀-pairs were found for CoRe₂O₆ and NiRe₂O₆ at a synthesis temperature of 1473 K. According to the XPS measurements, a mixture of Re⁺⁴/Re⁺⁶ and M²⁺/M³⁺ is present in both structural modifications of CoRe₂O₆ and NiRe₂O₆. The low-temperature forms contain more Re⁺⁴ and M³⁺ than the high-temperature forms. Tetragonal and monoclinic modifications of NiRe₂O₆ order with a ferromagnetic component at ∼24 K, whereas tetragonal and orthorhombic CoRe₂O₆ show two magnetic transitions: below ∼17.5 and 27 K for the tetragonal and below 18 and 67 K for the orthorhombic phase. Tetragonal FeRe₂O₆ is antiferromagnetic below 123 K.     

Synthesis, structure and magnetic properties of porous magnetic composite, based on MCM-41 molecular sieve with Fe3O4 nanoparticles

Porous magnetic composites were prepared by the synthesis of molecular sieve MCM-41 in the presence of Fe₃O₄ nanoparticles with average diameter of 15 nm. Nanoparticles were captured by porous silica matrix MCM-41, which resulted in their incorporation, as it was confirmed by TEM, SEM and X-ray diffraction. The materials possessed high surface area (392-666 m² g⁻¹), high pore volume (0.39-0.73 cm³ g⁻¹) along with high magnetic response (M_S up to 28.4 emu g⁻¹ at 300 K). Calcination of samples resulted in partial oxidation of Fe₃O₄ to α-Fe₂O₃. The influence of nanoparticles content on sorption and magnetic properties of the composites was shown. No hysteresis was found for the samples at 300 K; at 5 K, H_C was in the range 370-385 G for non-calcinated samples and 350-356 G for calcinated ones.     

Characterization and magnetic exchange observation for CoFe2O4–CoFe2 nanocomposite microfibers

The magnetic hard-soft CoFe₂O₄–CoFe₂ nanocomposite microfibers have been synthesized by the sol–gel and partial reduction process, where CoFe₂O₄ ferrite is the hard phase with a grain size range from 43 to 62 nm and CoFe₂ alloy the soft phase with grain sizes around 30 nm. These nanocomposite microfibers exhibit the magnetization behavior like a single phase magnetic material, and the magnetic exchange coupling effects are observed between the hard and soft phases. The specific saturation magnetization of CoFe₂O₄–CoFe₂ nanocomposite microfibers shows an increase tendency with the increasing weight fraction of CoFe₂, while the coercivity is consequently reduced. The nanocomposite microfibers have a maximum remanence 51.7 Am²/kg when the phase contents of CoFe₂ around 28 wt% and CoFe₂O₄ about 72 wt%.     

The formation and physicochemical characterization of Al2O3-doped manganese ferrites

Mn/Fe mixed oxide solids doped with Al₂O₃ (0.32-1.27 wt.%) were prepared by impregnation of manganese nitrate with finely powdered ferric oxide, then treated with different amounts of aluminum nitrate. The obtained samples were calcined in air at 700-1000 °C for 6 h. The specific surface area (S_BET) and the catalytic activity of pure and doped precalcined at 700-1000 °C have been measured by using N₂ adsorption isotherms and CO oxidation by O₂. The structure and the phase changes were characterized by DTA and XRD techniques. The obtained results revealed that Mn₂O₃ interacted readily with Fe₂O₃ to produce well-crystallized manganese ferrite (MnFe₂O₄) at temperatures of 800 °C and above. The degree of propagation of this reaction increased by Al₂O₃-doping and also by increasing the heating temperature. The treatment with 1.27 wt.% Al₂O₃ followed by heating at 1000 °C resulted in complete conversion of Mn/Fe oxides into the corresponding ferrite phase. The catalytic activity and S_BET of pure and doped solids were found to decrease, by increasing both the calcination temperature and the amount of Al₂O₃ added, due to the enhanced formation of MnFe₂O₄ phase which is less reactive than the free oxides (Mn₂O₃ and Fe₂O₃). The activation energy of formation (ΔE) of MnFe₂O₄ was determined for pure and doped solids. The promotion effect of aluminum in formation of MnFe₂O₄ was attributed to an effective increase in the mobility of reacting cations.     

Layer by layer assembly of catalase and amine-terminated ionic liquid onto titanium nitride nanoparticles modified glassy carbon electrode: Study of direct voltammetry and bioelectrocatalytic activity

A novel, simple and facile layer by layer (LBL) approach is used for modification of glassy carbon (GC) electrode with multilayer of catalase and nanocomposite containing 1-(3-Aminopropyl)-3-methylimidazolium bromide (amine terminated ionic liquid (NH₂-IL)) and titanium nitride nanoparticles (TiNnp). First a thin layer of NH₂-IL is covalently attached to GC/TiNnp electrode using electro-oxidation method. Then, with alternative self assemble positively charged NH₂-IL and negatively charged catalase a sensitive H₂O₂ biosensor is constructed, whose response is directly correlated to the number of bilayers. The surface coverage of active catalase per bilayer, heterogeneous electron transfer rate constant (k_s) and Michaelis–Menten constant (K_M) of immobilized catalase were 3.32 × 10⁻¹² mol cm⁻², 5.28 s⁻¹ and 1.1 mM, respectively. The biosensor shows good stability, high reproducibility, long life-time, and fast amperometric response with the high sensitivity of 380 μA mM⁻¹ cm⁻² and low detection limit of 100 nM at concentration range up to 2.1 mM.     

Comparative study of the synthesis of CoFe<Subscript>2</Subscript>O<Subscript>4</Subscript> and NiFe<Subscript>2</Subscript>O<Subscript>4</Subscript> in silica through the polymerized complex route of the sol–gel method

In this work the synthesis of CoFe₂O₄-SiO₂ and NiFe₂O₄-SiO₂ nanocomposites was studied via the sol–gel method, using the polymerized complex route. The polymerized precursors obtained by the reaction of citric acid, ethylene glycol, tetraethylorthosilicate, ferric nitrate, and cobalt nitrate or nickel chloride were characterized by nuclear magnetic resonance (NMR) and infrared (IR) spectroscopy. NMR and IR spectra of the precursors, without and with metallic ions, show the formation of polymeric chains with ester and ether groups and complexes of metal-polymeric precursor. The nanocomposites were obtained by the thermal decomposition of the organic fraction and characterized by X-ray diffraction (XRD) and vibrating sample magnetometry (VSM). XRD patterns show the formation of CoFe₂O₄ and NiFe₂O₄ in an amorphous silica matrix above 400 °C in both cases. When the calcination temperature was 800 °C the particle size of the crystalline phases, calculated using the Scherrer equation, reached ∼35 nm for the two oxides. VSM plots show the ferrimagnetic behavior that is expected for this type of magnetic material; the magnetization at 12.5 KOe of the CoFe₂O₄-SiO₂ and NiFe₂O₄-SiO₂ compounds was 29.5 and 17.4 emu/g, respectively, for samples treated at 800 °C.