用穆斯堡尔谱研究Eu2O3在载体表面上的分散度

用穆斯堡尔谱研究了Eu₂O₃在不同载体表面上的分散度。随着铕含量的变化引起的穆斯堡尔参数的差别表明了Eu₂O₃与不同载体之间作用上的差别。在γ-Al₂O₃表面上,当Eu含量增加时,用质异能位移增加,逐渐接近于体相Eu₂O₃相应值,说明在逐步形成Eu₂O₃晶相。与此不同,在两种SiO_关键词：     

Eu_2O_3在η-Al_2O_3和SiO_2上固体-固体表面相互作用的研究

用穆斯堡尔谱和X射线衍射技术研究了Eu_2O_3在η-Al_2O_3和硅胶上的固体表面吸附。     

Influence of hydrothermally modified γ-Al2O3 on the properties of NiMo/γ-Al2O3 catalyst

The influence of hydrothermal modification of γ-Al₂O₃ on the properties of NiMo/γ-Al₂O₃ catalyst was investigated in this paper. The experimental results showed that the use of the modified γ-Al₂O₃ in the preparation of the NiMo/γ-Al₂O₃ catalyst led to the increase of the dispersion of the surface Mo and Ni oxides, favored the formation of the poly-molybdates and promoted the reduction of the active Mo oxides owing to the increase of the surface acidity of the modified γ-Al₂O₃. Therefore, the NiMo/γ-Al₂O₃ catalyst supported on the modified γ-Al₂O₃ exhibited a higher hydrodenitrogenation (HDN) activity than that supported on the untreated γ-Al₂O₃ in the temperature range of 300-340 °C.     

共沉淀ZnO/γ-Al2O3体系EXAFS研究

用XRD和EXAFS研究了200°C,300°C,450°C,800°C焙烧的共沉淀ZnO/γ-Al₂O₃体系.通过EXAFS分析得到了Zn原子的径向分布函数,并针对第一配位层做了定量的拟合,结果是体系中第一层锌氧Zn-O保持ZnO中的四配位结构.文中还对第二层配位峰的变化趁势做了分析.     

α-Al2O3(0001)基片表面结构与能量研究

对α-Al₂O₃(0001)晶体表层三种不同终止原子结构的计算模型， 在三维周期边界条件下 的κ空间中，采用超软赝势平面波函数描述多电子体系.应用基于密度泛函理论的局域密度 近似，计算了不同表层结构的体系能量，表明最表层终止原子为单层Al的表面结构最稳定. 对由10个原子组成的菱形原胞进行了结构优化，得到晶胞参数值(a₀＝0.48178n m)与实验 报道值误差小于1.3%.进一步计算了超晶胞(2×2)表面弛豫，弛豫后原第2层O原子层成为最 表层； 对不同表层O，Al原子最外层电子进行了布居分析，表面电子有更大的概率被定域在 O原子的周围，表面明显地表现出O原子的电子表面态. 关键词： 2O₃(0001)')" href="#">α-Al₂O₃(0001) 超软赝势 表面结构 表面态     

α-Al2O3单晶的热释光和光释光特性

研究了纯α-Al₂O₃单晶的热释光发光曲线和三维发光谱，以及光释光衰变曲线，对它们的发光机理和剂量学特性进行了分析和讨论.实验观察到α-Al₂O₃单晶β射线照射后立即测量的热释光发光曲线，有峰温为76℃和207℃两个发光峰.经γ射线照射数小时后测量的三维发光谱，只有峰温207℃波长为416 nm发光峰，它与α-Al₂O₃:C晶体的发光波长基本相同，是受热激发到导带的电子与F< 关键词： 2O₃')" href="#">α-Al₂O₃ 三维发光谱 TL/OSL剂量响应     

用自由正电子固体表面态湮没技术研究2%PdO/Al2O3

用²²Na的e⁺研究2%PdO/Al₂O₃中PdO空间结构与热处理的关系,利用e⁺湮没参数计算PdO颗粒度,说明自由e⁺固体表面态湮没技术可以应用于催化剂的研究。 关键词：     

Ce3+掺杂SiO2-Al2O3-Gd2O3玻璃的闪烁性能

通常, Ce离子掺杂的低密度玻璃有较高的发光效率, 而高密度的Ce离子掺杂玻璃其发光效率很低. 为了解释这一现象, 采用高温熔融法获得了SiO₂-Al₂O₃-Gd₂O₃三元系统的玻璃形成区, 并在还原气氛下制备了Ce³⁺掺杂SiO₂-Al₂O₃-Gd₂O₃以及SiO₂-Al₂O₃-Gd₂O₃-Ln₂O₃ (Ln=Y, La, Lu)闪烁玻璃, 研究了其光谱和闪烁性能. 测试结果显示: 随着Gd₂O₃含量增加, 玻璃紫外截止波长发生红移, 荧光强度降低, 衰减时间缩短; 加入Lu₂O₃, La₂O₃, Y₂O₃后, 紫外截止波长发生红移, 荧光强度降低, 衰减时间变短; 当Gd₂O₃超过10% mol时, X射线荧光积分光产额从相当于锗酸铋 晶体的61%降低到13%. 荧光强度降低、衰减时间缩短的原因是随着玻璃的紫外截止波长红移玻璃的能带宽度变窄, 使得Ce³⁺离子的d电子轨道开始接近玻璃的导带, Ce³⁺离子受辐射后跃迁到d电子轨道的电子会通过导带与玻璃中的空穴复合, 产生电荷迁移猝灭效应.     

α-Al2O3(0001)表面原子缺陷对ZnO吸附影响

采用基于密度泛函理论的分子动力学方法，对α-Al₂O₃(0001)表面 Al，O原子空位缺陷及其对ZnO吸附进行了理论计算.电子局域函数显示了表面空位处的电子密度变化，表面Al原子空缺处有非常明显的缺电子区域，悬挂键临近O的电子密度增大，有利于对Zn的吸附；O原子空缺处的Al原子处存在孤立电子，其ELF值为005—03，将有利于同电负性较大的O或O^2-结合.通过吸附动力学模拟与体系能量的计算发现，表面缺陷显著增强了表面 的化学吸附，空缺原子处都被吸附原子填补，吸附结合能远大于单晶表面的情况.在Al空缺的表面，由于ZnO的O与表面O形成双键，破坏了α-Al₂O₃(0001)表面O六 角对称结构，减小了 O的表面扩散，从而不利于规则的ZnO薄膜生长.相反，O的空缺表面，弥补了α-Al_{2O3(0001)表面O空位缺陷，不影响基片表面O六角对称结构.}     

用于α-Al2O3分子动力学模拟的长程Finnis-Sinclair势函数

用金属势函数描述氧化物是实现金属-氧化物界面分子动力学模拟的关键.基于此,通过拟合α-Al₂O₃的晶格能、晶格常数、弹性常数,获得了一套用于描述α-Al₂O₃的长程Finnis-Sinclair（F-S）势.通过与已报道的描述α-Al₂O₃的EAM势、Glue势和modified Matsui（m-Matsui）势的比较,结果达到或优于前人的结果.进而,在300 K的温度下对 关键词： 长程F-S势 2O₃')" href="#">α-Al₂O₃ 2O₃界面')" href="#">Fe-Al₂O₃界面 2O₃界面')" href="#">Al-Al₂O₃界面     

Preparation and characteristics of?a?BaO–Al2O3–B2O3–SiO2–La2O3 glass ceramic via spray pyrolysis

The characteristics of a BaO–Al₂O₃–B₂O₃–SiO₂–La₂O₃ glass ceramic prepared by spray pyrolysis were studied. Glass powders with spherical shape and amorphous phase were prepared by complete melting at a preparation temperature of 1 500°C. The mean size and geometric standard deviation of the powders prepared at the temperature of 1 500°C were 0.6 μm and 1.3. The glass powders had similar composition to that of the spray solution. The glass transition temperature (T _g) of the glass powders was 600.3°C. Two crystallization exothermic peaks were observed at 769.3 and 837.8°C. Densification of the specimen started at a sintering temperature of 600°C, in which Ba₄La₆O(SiO₄)₆ as main crystal structure was observed. Complete densification of the specimen occurred at a sintering temperature of 800°C. The specimens sintered at temperatures above 800°C had main crystal structure of BaAl₂Si₂O₈.     

磁载光催化剂ZnO/ SiO2/γ-Fe2O3的光催化性能

本文采用液相沉积法制备出了纳米SiO2/γ-Fe2O3复合粒子,在其表面负载ZnO, 从而得到了易于磁性固液分离的磁载光催化剂ZnO/SiO2/γ-Fe2O3, 并通过XRD和TEM等测试技术对样品进行了表征。以可溶性染料亚甲基兰等为降解对象, 研究了磁载光催化剂ZnO/SiO2/γ-Fe2O3在紫外光下的光催化活性。结果表明, 在γ-Fe2O3和ZnO之间包覆一层无定形SiO2可使催化剂降佳率由20.76%提高到95.63%,并且该磁载光催化剂对染料有较好的降解效果, 在三次循环使用后仍能保持较好的光催化性能.     

MoO3在多孔γ-Al2 O3中固熔分散的研究

用MoO₃与多孔γ-Al₂O₃载体以机械混合法制备了一系列MoO₃/γ-Al₂O₃样品.用扫描电子显微镜、X射线衍射、X射线光电子能谱分析、综合热分析(TG/DTA)和正电子湮没谱学研究了MoO₃加载于γ-Al₂O₃后固熔分散过程.分别测量了不同含量的MoO₃/γ-Al_{2关键词： 正电子湮没谱学 三氧化钼 分散 逐次加载}     

Adsorption of methyl orange on mesoporous γ-Fe2O3/SiO2 nanocomposites

Mesoporous γ-Fe₂O₃/SiO₂ nanocomposite containing 30 mol% of γ-Fe₂O₃ was prepared by a template-free sol-gel method, and its removal ability for methyl orange (MO) was investigated. The nanocomposite was characterized using X-ray powder diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscope (SEM), Fourier transform infrared (FTIR) absorption measurements, nitrogen adsorption-desorption measurements, and magnetic measurements. The synthesized γ-Fe₂O₃/SiO₂ nanocomposite has a mesoporous structure with an average pore size of 3.5 nm and a specific surface area of 245 m²/g, and it exhibits ferrimagnetic characteristics with the maximum saturation magnetization of 20.9 emu/g. The adsorption of MO on the nanocomposite reaches the maximum adsorbed percentage of ca. 80% within a few minutes, showing that most of MO can be removed in a short time. The MO adsorption data fit well with both Langmuir and Freundlich adsorption isotherms. The maximum adsorption capacity of MO is estimated to be 476 mg/g.     

Broadband near-IR emission and temperature dependence in Er/Tm co-doped Bi2O3–SiO2–Ga2O3 glasses

The broadband near-IR emission has been investigated in a series of Er/Tm co-doped Bi₂O₃–SiO₂–Ga₂O₃ (BSG) glasses with 800 nm laser diode as an excitation source. A broadband emission extending from 1350 to 1650 nm with a full width at half maximum (FWHM) around 165 nm is obtained in 0.2 wt% Er₂O₃ and 1.0 wt% Tm₂O₃ co-doped BSG glass. The fluorescence decay curves of glasses are measured and maximum energy transfer efficiency from Er³⁺ to Tm³⁺ reaches 71% when Tm³⁺ concentration is 1.0 wt%. The temperature dependence of the broadband emission spectra in Er³⁺–Tm³⁺ co-doped BSG glass is also recorded to further understand the energy-transfer processes between Er³⁺ and Tm³⁺. The present work suggests that Er/Tm co-doped BSG glasses can be a potential candidate for broadband integrated amplifier.     

α-Al2O3: Mn单晶的三维热释发光谱研究

测量了α-Al2O3: Mn单晶中子辐照前后的三维热释发光谱.观察到α-Al2O3: Mn:Mn单晶γ射线照射后测量的三维热释发光谱中，峰温在350℃波长为680nm处有一宽发光峰，这可能与Mn2+离子有关；波长为695nm峰温在170℃和350℃的线状光谱，叠加在680nm宽发光峰上，是Cr3+离子的发光谱线,其中可能有Mn4+离子的贡献.与纯α-Al2O3单晶的热释发光谱相比，掺入Mn杂质后，γ射线照射的三维热释发光谱中完全地抑制了波长为416nm的α-Al2O3的F心发光峰.经1017cm-2中子注量辐照和退火后，γ射线照射后测量的三维热释发光谱中，在150℃出现了波长为416和695nm的发光峰，以及在250℃波长为680和695nm的发光峰，其中695nm新发光峰的强度略超过了中子辐照前α-Al2O3:Mn在350℃波长为695nm的发光峰，说明中子辐照产生了大量浅陷阱能级和F心.然而，经1018cm-2中子注量辐照和退火后，γ射线照射后测量的三维热释发光谱中，出现了峰温150℃，190℃和250℃波长为520nm的Mn2+离子发光峰，以及300℃波长为680和695nm的Cr3+（或Mn4+）的发光峰，表明增高中子注量的辐照，产生了温度为190℃，250℃和300℃深陷阱能级和F心，并使Mn2+离子发光峰明显加强. 关键词： α-Al2O3:Mn 三维发光谱 缺陷结构 发光机理     

Stability and electronic properties of carbon in α-Al2O3

The stability and electronic properties of carbon in α-Al₂O₃ are investigated using density functional theory. In the host lattice, the substitutional C prefers the Al site under the O-rich conditions, whereas the O site is preferred by carbon under the Al-rich conditions. The calculated results predict a direct relationship between the thermodynamic and optical transition levels with the degree of the local distortion induced by C in the alumina lattice. We also find C at the O site acts as a charge compensator to stabilize the F⁺ center, thereby enhancing the TL signal at 465 K. Also, C at Al site can serve as electron traps for TL emission process in α-Al₂O₃.     

α-Al2O3:C晶体的热释光和光释光特性

以高纯α-Al₂O₃和石墨为原料,采用温梯法生长了α-Al₂O₃：C晶体,使用Ris TL/OSL-DA-15型热释光和光释光仪研究了其热释光和光释光特性.α-Al₂O₃：C晶体在462K附近有单一热释光峰,发射波长位于410nm.随着辐照剂量的增加,热释光强度逐渐增强,462K的热释光特征峰位置保持不变.α-Al₂O₃：C晶体的 关键词： 2O₃：C')" href="#">α-Al₂O₃：C 热释光 光释光     

含碳Na-β(β")-Al2O3的导电性能

本文研究了含碳(1—10)wt％的Na-β(β″)-Al₂O₃,指出含碳6wt％以下仍是良好的快离子导体,而且由于混入了碳,离子电导率比纯的Na-β(β″)-Al₂O₃提高一到两个数量级。样品的体电阻,晶界电阻,双电层电容及其漏电阻等参量都随含碳量的不同而变化。文中详细地讨论了碳的影响。在-40℃到80℃温度范围测量了纯样品与含碳样品的电导温度特性,指出含碳的Na-β(β″)-Al₂O₃是做双电层电容器的良好材料。 关键词：     

Y2O3·Cr2O3复合氧化物热力学性质的研究

在1182—1386K温度范围内,用固体电解质氧浓差电池:Mo|Cr,Y₂O₃,Y₂O₃·Cr₂O₃|ZrO₂(+MgO)|Cr,Cr₂O₃|Mo测定了复合氧化物Y₂O₃·Cr₂O₃的热力学性质。对于反应Y_{2关键词：}