Pt/SAPO-34在低温H2选择催化还原NO反应中的催化活性

考察了贫燃条件下Pt/SAPO-34催化剂低温(60～260℃)选择催化还原(H2-SCR)消除NO的催化性能,研究了载体、金属负载量和反应条件对催化性能的影响.结果表明,0.5%Pt/SAPO-34催化剂的活性高于相同金属负载量的Pt/SiO2和Pt/ZSM-5,其在高空速(80000h-1)时的最高NO转化率可达78.8%,N2选择性为75.2%,而在空速降低到10000h-1时,其NO转化率可达到100%.通过原外漫反射红外光谱初步研究了H2-SCR反应的机理,发现反应的中间物种主要是-NO3-.     

载体性质对Pt催化剂H2选择催化还原NOx活性和选择性的影响

研究了Pt/MgO, Pt/γ-Al2O3, Pt/ZrO2和Pt/HZSM-5催化剂上H2选择催化还原消除NOx(H2-SCR)反应。结果发现, H2-SCR活性和N2生成选择性受催化剂中Pt的金属性以及载体的氮氧化物吸附能力影响很大。 HZSM-5的表面酸性使载体对NOx吸附能力较小,使担载Pt以较高的金属性存在,从而导致Pt/HZSM-5催化剂的高活性和高选择性。相反, Pt/MgO和Pt/γ-Al2O3催化剂较差的活性和选择性可归因于其载体的碱性表面、催化剂中Pt较低的金属性以及载体对氮氧化物较大的吸附能力。结合反应的原位红外光谱结果可以认为,在Pt/载体界面处亚硝酸根/硝酸根物种被还原为N2或N2O,取决于该处参与反应的活性H与这些含氮物种的相对数目。     

载体性质对Pt催化剂H2选择催化还原NOx活性和选择性的影响

研究了Pt/MgO, Pt/γ-Al2O3, Pt/ZrO2和Pt/HZSM-5催化剂上H2选择催化还原消除NOx(H2-SCR)反应。结果发现, H2-SCR活性和N2生成选择性受催化剂中Pt的金属性以及载体的氮氧化物吸附能力影响很大。 HZSM-5的表面酸性使载体对NOx吸附能力较小,使担载Pt以较高的金属性存在,从而导致Pt/HZSM-5催化剂的高活性和高选择性。相反, Pt/MgO和Pt/γ-Al2O3催化剂较差的活性和选择性可归因于其载体的碱性表面、催化剂中Pt较低的金属性以及载体对氮氧化物较大的吸附能力。结合反应的原位红外光谱结果可以认为,在Pt/载体界面处亚硝酸根/硝酸根物种被还原为N2或N2O,取决于该处参与反应的活性H与这些含氮物种的相对数目。     

Pd基催化剂上H2快速选择催化还原 NOx

 首次研究了 Pd 基催化剂上氢快速选择催化还原 NOx 反应 (快速 H2-SCR 反应). 结果表明, Pd/Al2O3 和 Pd/SiO2 催化剂表现出极高的活性, 在 200 oC 以上时 NOx 转化率可达 100%; 但 Pd/MgO 催化剂在整个考察温度范围均没有活性, 这表明载体对催化剂快速 H2-SCR 活性有决定性作用. 与常规 H2-SCR 反应相比, 快速 H2-SCR 反应明显提高了 NOx 的消除效率. 原位漫反射红外光谱结果表明, 快速 H2-SCR 反应活性的提高来源于加速生成的氨物种以及后续反应速率的加快.     

Pt/ZSM-35/MCM-49催化剂上H2选择还原NO

将共结晶分子筛作为催化剂载体应用于富氧条件下的氮氧化物消除反应.在体积分数为0.1%NO,0.5%H2,6.7%O2,He气为平衡气,反应空速8×104h-1条件下对比考察了Pt/ZSM-35/MCM-49,Pt/ZSM-35和Pt/MCM-49催化剂在氢气选择催化还原氮氧化物反应中的活性.结果表明,Pt/ZSM-35/MCM-49催化剂上的活性较其它2个催化剂有一定程度的提高,NO转化率最高达到84%,N2选择性最高达到74%.通过X射线衍射(XRD)、氨气程序升温脱附(NH3-TPD)、氢气程序升温还原(H2-TPR)、CO吸附红外和原位漫反射红外对3种催化剂进行了表征.结果发现,Pt/ZSM-35/MCM-49催化剂活性的提高源于共结晶有利于生成和稳定重要的中间物种——氨物种.     

负载型磷钨酸催化剂的制备及催化合成ＥＴＢＥ的性能研究

采用水热法合成纯硅介孔分子筛Si-MCM-41, 并用浸渍法将磷钨酸(PWA)负载到介孔分子筛Si-MCM-41上, 制得了磷钨酸负载量不同的催化剂x%PWA/MCM-41. 利用XRD, FT-IR, Py-IR, BET, TEM对载体和催化剂进行分析. 结果表明, 负载后的PWA颗粒粒径明显减小, 粒径约为10个纳米, PWA在载体表面实现了均匀分布, 通过叔丁醇和乙醇在高压反应釜内生成乙基叔丁基醚的反应测试催化剂的催化性能. 结果表明, 负载型催化剂和纯PWA相比, 前者使叔丁醇(TBA)的转化率、ETBE的选择性有很大提高, 当磷钨酸负载量为30%时TBA的转化率最大. 最优的催化剂制备及反应条件是: 载体550 ℃煅烧脱模, PWA负载量为30%, 催化剂煅烧温度为300 ℃, 醚化反应温度为120 ℃, 乙醇与叔丁醇的摩尔比为2∶ 1, 催化剂的用量为1.4 g.     

氨法选择性还原氮氧化物 V2O5/TiO2-PILC催化剂的抗硫性能

选择性催化还原(SCR)是目前去除氮氧化物最有效的方法之一. V2O5/TiO2催化剂被广泛应用于氨法选择性还原氮氧化物(NH3-SCR)反应,但该催化剂存在工作温度高(300–400oC)及 SO2氧化率高引起设备腐蚀和管路堵塞等问题,开发低温 SCR催化剂具有重要意义.过渡金属氧化物(如 Fe2O3, MnOx和 CuO等)催化剂用于低温SCR先后见诸文献报道,但这些催化剂在 SO2和 H2O存在下易失活.近年来柱撑黏土(PILC)引起科学家广泛关注, Yang等首次将 V2O5/TiO2-PILC催化剂应用于 NH3-SCR反应,发现其催化活性高于传统 V2O5/TiO2催化剂.柱撑黏土基催化剂在 NH3-SCR反应中也显示出良好抗硫性能,但 V2O5/TiO2-PILC催化剂的抗硫机理至今尚未见深入研究.因此我们制备了一系列 V2O5/TiO2-PILC催化剂,采用原位漫反射红外等方法详细研究了其抗硫性能较好的原因.
　　首先采用离子交换法制备出 TiO2-PILC载体,之后采用浸渍法制备了不同钒含量(质量分数x/%=0,3,4,5)的xV2O5/TiO2-PILC催化剂.同时,制备了传统 V2O5/TiO2和 V2O5-MoO3/TiO2催化剂作为对比.活性评价结果显示,4V/TiO2-PILC催化剂具有最高的催化活性,其催化性能与传统钒钛催化剂相当.在160oC时, NO转化率可达80%以上.同时,4V/TiO2-PILC催化剂还具有较宽的反应温度窗口,在260–500oC范围内, NO转化率保持在90%以上.向反应体系中加入0.05% SO2和10% H2O后,在低温(160oC以下)时所有催化剂的反应活性都有一定提高,可能是由于 SO2的加入提高了催化剂的表面酸性.继续升高温度,4V/TiO2和4V6Mo/TiO2催化剂活性均明显下降,而4V/TiO2-PILC催化剂的活性则未出现明显下降.原位漫反射红外光谱结果显示, SO2在三种催化剂表面的吸附以表面硫酸盐或亚硫酸盐物种以及离子态 SO42–物种形式存在,而在4V/TiO2-PILC催化剂表面离子态 SO42–物种的量最少. X射线光电子能谱及 O2程序升温脱附结果显示,在4V/TiO2-PILC催化剂上,表面吸附氧(Oads)的量最少.综合上述分析可以得出,在 SO2气氛下,离子态 SO42–物种在 SCR催化剂表面的累积可能是导致其失活的主要原因,而离子态 SO42–物种的形成可能与催化剂表面吸附氧的量有关.     

一步水热合成Cu-SAPO-34选择性催化丙烯还原氮氧化物（英文）

采用一步法水热合成不同Cu/Al比的Cu-SAPO-34催化剂,并对其丙烯选择性催化还原NO(C3H6-SCR)性能进行了研究。通过N2吸附-脱附、X射线衍射(XRD)、X射线光电子能谱(XPS)、程序升温还原(H2-TPR)和原位漫反射傅里叶变换红外光谱(In situ DRIFTS)等研究手段对催化剂进行表征,考察Cu-SAPO-34中Cu物种含量对催化剂的物理化学性质和反应活性的影响。结果表明,当铜负载量为2.76%～4.12%(w/w)时,Cu-SAPO-34催化剂在富氧条件下300～400℃内表现出非常有吸引力的C_3H_6-SCR活性,可实现～100%的脱硝效率和～100%的N_2选择性。原位红外光谱研究表明,Cu-SAPO-34分子筛骨架上孤立的Cu~(2+)离子是NO吸附和活化形成NO_2~-/NO_3~-中间物种的主要活性位,并通过C_3H_6-SCR反应过程中Cu~(2+)/Cu~+氧化还原循环来实现Cu~(2+)离子的持续供给。     

CeO2表面分散态WO3的氨选择性催化还原性能

铈基材料在氨选择性催化还原氮氧化物(NH3-SCR)的研究中备受关注,亦被认为是潜在的新型环境友好型催化剂.CeO2具有独特的氧化还原性能和优良的储释氧性能,易与其它金属氧化物发生协同催化而有利于提高催化剂的催化反应性能,而WO3可以改善催化剂的表面酸性.研究亦报道了WO3可以改善CeO2的NH3-SCR反应的高温活性和N2选择性,其原因在于WO3增加了铈基催化剂NH3的吸附性能且抑制了NH3非选择性氧化成NOx.我们采用浸渍法制备了一系列负载型WO3/CeO2催化剂,并利用XRD,Raman,XPS,H2-TPR,NH3-TPD和in situ DRIFT对其理化性质进行了表征,系统研究了WO3负载量对WO3/CeO2催化剂NH3-SCR催化性能的影响,主要研究的内容包括:(1)WO3/CeO2催化剂中WO3的状态与催化性能之间的关系;(2)WO3负载量对WO3/CeO2催化剂的NH3和NO吸附行为的影响.NH3-SCR反应测试表明WO3负载量对WO3/CeO2催化剂有显著影响,优化的WO3/CeO2催化剂在200–450℃具有良好的脱硝性能,且在300℃通入SO2+H2O条件下依然保持优异的催化活性.XPS和H2-TPR结果表明,WO3分散在CeO2表面抑制了CeO2表面活性氧和表面晶格氧的氧化能力,这导致催化剂对NO的氧化以及对硝酸盐的吸附性能相比于纯CeO2显著降低,同时,in situ DRIFT也证实,随着WO3负载量的增加,WO3/CeO2催化剂表面吸附硝酸盐能力下降.因此,我们认为,由于低活性的晶相WO3覆盖在催化剂表面,阻碍了催化剂的表面活性位,降低了催化剂的氧化还原能力和表面酸量,从而晶相WO3抑制了WO3/CeO2催化剂的催化活性.同时,我们发现在70℃下采用氨水可以洗掉WO3/CeO2催化剂中的晶相WO3,且洗涤后的样品催化活性有所提升,这进一步验证了晶相WO3对催化活性的抑制作用.In situ DRIFT结果表明WO3/CeO2催化剂上NH3-SCR反应是通过Eley-Rideal机理进行,即吸附NH3物种与气相NO之间发生反应.随着WO3负载量的增加,WO3/CeO2催化剂中NH3的吸附能力先增强后减弱,而NO吸附能力持续减弱,这有利于表面酸位在反应过程中不被硝酸盐阻碍,当WO3负载量在分散容量附近时,这种吸附特性的效果发挥到最大,从而最大限度地促进NH3-SCR反应按照Eley-Rideal机理顺利进行.     

硫化CoMo/Al2O3催化剂上H2同时催化还原SO2和NO(Ⅰ)——催化剂的制备、表征及性能

用浸渍法制备了CoMo/Al2O3催化剂,并对其进行了XRD、低温氮吸附-脱附和TPR表征.结果表明,随着Co负载量的增加,催化剂表面活性物种增加,但同时催化剂的比表面积和孔容逐渐减小;硫化后的催化剂比未经硫化处理的催化剂表面具有更多更易还原的活性物种.将所制得的催化剂硫化后用于NO分解和H2还原NO反应,NO均完全转化,但催化剂最终会因为晶格硫的大量流失而活性下降.在H2还原NO反应体系中,H2的存在使得催化剂晶格硫的流失速率极大变缓,催化剂活性下降较慢;在H2同时还原SO2和NO体系中,由于晶格硫能够得到外界源源不断的补充,因此,SO2和NO能同时在催化剂表面实现稳定的还原,反应温度、空速、进料气中H2的配比、催化剂中Co负载量以及硫化预处理方式对催化剂的活性有显著影响.活性测试结果表明,在500℃,空速12000 h-1,n(H2)/n(SO2 NO)=2时,5%Co10%Mo/Al2O3上SO2和NO转化率均为100%,单质硫产率达96.6%.     

Influences of Mesoporous Structure on the NO+H2+O2 Low Temperature Reaction over Pt/Si-MCM-41 Catalyst

It was found that Si-MCM-41 mesoporous molecular sieves as a support of noble metal Pt could be used for the selective catalytic reduction of NO by hydrogen (H₂-SCR) under lean-burn conditions. Pt/Si-MCM-41, together with Pt/Si-ZSM-5 and Pt/SiO₂, was characterized by X-ray diffraction analysis (XRD), nitrogen adsorption/desorption, hydrogen adsorption, and transmission electron microscopy (TEM). The results indicated that Pt/Si-MCM-41 had the best H₂-SCR activity in comparison with Pt/Si-ZSM-5 and Pt/SiO₂ catalysts and that the maximum conversion of NO was up to 60.1% at 100 °C and a gas hourly space velocity (GHSV) of 80000 h_-1 under lean-burn conditions. Characterization showed that the large surface area and pore volume of MCM-41 favored the dispersion of Pt. The maximum NO conversion of Pt/Si-MCM-41 catalyst decreased obviously to 15% at 120 °C when the pore structure of Si-MCM-41 support was destroyed. The reaction mechanism over Pt/Si-MCM-41 was investigated using in situ diffuse reflectance infrared spectroscopy (DRIFTS), which revealed that the main reaction intermediates should be nitrate species during NO reduction.     

Detection of homogeneous distribution of functional groups in mesoporous silica by small angle neutron scattering and in situ adsorption of nitrogen or water

The distribution of SO(3)H-functional groups attached to the ordered inner pore walls of mesoporous Si-MCM-41 materials based on SiO(2) was investigated by gas adsorption combined with in situ small angle neutron scattering (SANS). The functionalization was performed by two different methods, (i) grafting and (ii) co-condensation. The adsorbates N(2) at 77 K or a H(2)O/D(2)O mixture of 42:58 at 298 K possess neutron scattering length densities (SLD) similar to that of SiO(2) and therefore quench the diffraction signals of the nonmodified silica. SANS measurements show that N(2) matches completely not only with the pristine mesoporous Si-MCM-41 but also with Si-MCM-41-SO(3)H functionalized by grafting. Thus, full access of adsorbate into the entire length of the pores is proven. For the analysis of the distribution of functional groups within the pores in dependence on the used functionalization method, grafting or co-condensation, however, the more specific adsorbate H(2)O/D(2)O (42:58) is necessary, because it reacts more sensitively toward small changes in the SLD of the host material. For grafted Si-MCM-41-SO(3)H materials, an incomplete quenching was observed, indicating that only some regions, probably the pore mouths, have been modified. For a sample functionalized by co-condensation, almost no quenching of the neutron diffraction was found, indicating a very homogeneous distribution of the functional groups along the entire pores.     

焙烧温度对CuO/γ-Al2O3和CeO2-CuO/γ-Al2O3催化剂NO还原活性的影响

用浸渍法制备了CuO/γ-Al2O3催化剂和CeO2改性的CeO2-CuO/γ-Al2O3催化剂,考察了焙烧温度对CuO/γ-Al2O3和CeO2-CuO/γ-Al2O3催化剂C3H6还原NO反应活性的影响,以及CeO2的添加量对CeO2-CuO/γ-Al2O3催化剂C3H6还原NO反应活性的影响。结果表明,在200 ℃～500 ℃的焙烧温度范围内,焙烧温度对CuO/γ-Al2O3催化剂的活性影响很小；在500 ℃～800 ℃的焙烧温度范围内,随着焙烧温度的升高CuO/γ-Al2O3催化剂的活性急剧下降,由XRD物相测定结果可知,归因于对反应表现惰性的尖晶石CuAl2O4相的生成。当焙烧温度为500 ℃时,CeO2的添加对CuO/γ-Al2O3催化剂的活性影响很小；当焙烧温度为800 ℃时,CeO2的添加对CuO/γ-Al2O3催化剂有明显的助催化作用,当Ce和Cu的摩尔比为1∶10时,NO转化率较为理想。     

Cu交换度对贫燃条件下 Cu-Al-MCM-41上NO选择性催化还原的影响

利用程序升温反应技术考察了cu交换度对Cu-Al-MCM-41上NO选择性还原反应性能的影响,同时结合XRD,N2吸附等温线,NMR,ICP-AES,TPD和TPR等技术对催化剂的结构特征和化学吸附性能进行了表征．结果表明,经Cu离子交换的Al-MCM-41并未改变载体的结构特征,仍保持长程有序的中孔结构．影响Cu-Al-MCM-41催化剂选择性还原活性的主要因素是Cu交换度,而不是Cu含量,前者决定了活性中心(主要是Cu^2 )的浓度．当Cu交换度低于100％时,随着Cu交换度的增加,NO最大转化率增加．当交换度超过100％后,催化剂的还原活性下降,此时出现的CuO起完全氧化的催化作用而非选择性还原的催化作用．在n(Si)／n(Al)=10,Cu交换度接近100％的Cu-Al-MCM-41上360℃时可获得79％的NO最大转化率．     

Cl–改性对Ag/Al2O3催化剂结构及其催化C3H6-SCR和H2/C3H6-SCR反应性能的影响

以烯烃为还原剂的NOx选择性催化还原(HC-SCR)是重要的环境催化反应之一.Ag/Al2O3催化剂(SA)因在HC-SCR反应中表现高活性、高N2选择性及中等H2O和SO2耐受性等优点,而被广泛研究.SA催化剂中存在不同的Ag物种,包括孤立Ag+离子,带部分正电荷Agnδ+团簇和金属态Agn0团簇.文献研究结果表明,SA催化剂中Agnδ+团簇是催化HC-SCR反应的活性Ag物种,而Ag物种类型与Ag的负载量密切相关.因此文献中研究SA催化HC-SCR反应的结构-性能关系主要是通过改变Ag负载量来开展的,最优Ag负载量约为1％～2％.本文以Cl–改性的γ-Al2O3作为载体,采用传统的浸渍法制备了Ag/Al2O3-Cl催化剂(SA-Cl),通过XRD、TEM、H2-TPR、UV-Vis DRS以及XPS对催化剂进行了结构表征,并结合C3H6-SCR和H2/C3H6-SCR活性测试,建立催化剂结构-催化性能关系;同时利用原位傅里叶变换红外光谱(DRIFTS)和在线同步辐射单光子电离质谱(SVUV-PIMS)研究了SA催化HC-SCR的反应机理.结构表征结果表明,在SA催化剂中,Ag负载量的提高主要是增加了Agn0物种,而在SA-Cl催化剂中,Ag负载量的提高主要是增加了Agnδ+物种,因此Cl?改性能促进SA催化剂中Agnδ+物种的形成.活性测试结果表明,在相同Ag负载量下,SA-Cl催化剂表现出比SA催化剂更好的HC-SCR催化性能.Cl?改性对SA催化剂中Ag物种的调控作用和HC-SCR催化性能的促进作用随Ag负载量的增加变得更为明显.原位DRIFTS结果表明,γ-Al2O3载体(Al位点)是NO氧化形成硝酸盐物种的主要活性位点;Agnδ+物种催化丙烯适度氧化主要生成乙酸盐类物种,可以还原表面硝酸盐物种;而Agn0催化丙烯过度氧化主要生成羧酸盐类物种,进而生成CO2,不能还原表面硝酸盐物种.由此可见,Agnδ+是催化HC-SCR反应的活性Ag物种,而Agn0是催化烃类完全氧化反应的活性Ag物种;Cl–改性能有效促进Agnδ+的形成,进而提高HC-SCR催化反应活性.在线SVUV-PIMS结果检测到H2/C3H6-SCR反应中存在气态中间物种丙烯腈(CH2=CHCN).–CN和–NCO物种被认为是HC-SCR反应的关键中间物种,能够直接与气相NO+O2反应生成N2.因此,CH2=CHCN的存在说明HC-SCR反应涉及到气相反应机理.基于SA和SA-Cl催化剂,进一步研究了H2对C3H6-SCR低温活性的促进作用.结果表明,H2的促进作用是通过作用于Agnδ+物种,而不是通过Agn0物种来实现的;H2的引入有利于低温下强吸附硝酸盐物种的脱附或分解以及中间体向–NCO和–CN物种的转化,从而提高HC-SCR低温催化活性.综上,基于Cl–改性的Ag/Al2O3-Cl催化剂,本文成功证实了Agnδ+物种是催化HC-SCR反应的活性Ag物种,并结合原位DRIFTS在线SVUV-PIMS谱分别鉴定了催化反应表面中间物种和气相中间物种.这些结果加深了对SA催化HC-SCR反应构-效关系和反应机理的基础理解.     

Selective catalytic reduction of NO by C2H2 over Ce-Al2O3 catalyst with rate-determining step of NO oxidation

Ce-Al2O3 catalysts prepared by co-precipitation are investigated both in NO oxidation by O2 and in selective catalytic reduction of NO by C2H2(C 2 H 2-SCR).It is found that C2H2-SCR is initiated and controlled by NO oxidation to NO 2 over Al2O3.Ce loading on Al2O3 is almost inactive for NO oxidation below 350 C,since NO2 strongly adsorbs on cerium oxide,leading to the active sites being blocked,which was characterized by temperature-programmed desorption of NO and NO 2 and Fourier transform infrared spectroscopy after NO+O 2 coadsorption over the samples.However,in the case of C2H2-SCR,Ce loading on Al 2 O 3 significantly improves the reaction by accelerating the NO oxidation step in the temperature range of 250-450 C,since the nitrate species produced by NO 2 adsorption is an active intermediate required by C2H 2-SCR.     

BaFeO_(3-x)与Cu-ZSM-5耦合催化剂的NO_x储存还原性能

为替代传统的贵金属基NOx储存还原(NSR)催化剂,本文设计并制备了不含贵金属的BaFeO3-x+CuZSM-5耦合催化剂,用于催化消除稀燃发动机尾气中的NOx.在稀燃阶段,NO在BaFeO3-x催化剂上发生了氧化和储存反应;在富燃阶段,从BaFeO3-x催化剂中脱附出来未能消除的NOx被置于其后的Cu-ZSM-5催化剂进一步催化消除.实验结果表明,BaFeO3-x+Cu-ZSM-5耦合催化剂的工作温度窗口被拓宽到250-400°C,同时NOx消除性能得到了显著提高:NOx转化率最高可达98%,N2选择性接近100%.     

表面Mo修饰提高CeTiO_x催化剂低温脱硝性能（英文）

近年来,以雾霾为代表的大气污染问题严重影响到经济社会的可持续发展.其中,氮氧化物(NOx)的大量排放是导致雾霾天气的重要原因之一.氨选择性催化还原(NH3-SCR)是目前消除氮氧化物的主流技术,低温NH3-SCR更是广泛应用于钢铁、焦化、水泥、玻璃、陶瓷和垃圾焚烧等行业的烟气排放治理.传统的V2O5-WO3/Ti O2催化剂活性温度高(300–400 oC)且钒具有生物毒性,因此亟待开发环境友好的低温非钒基脱硝催化剂.最近, Ce Ti Ox基催化剂由于在中高温段(250–400 oC)表现出优异的脱硝性能而得到广泛关注.然而,该催化剂仍面临低温活性差及抗硫性能差的问题,制约了其工业化应用.研究显示,添加过渡金属可提高Ce Ti Ox基催化剂的脱硝活性和抗硫中毒性能,这主要是因为过渡金属的添加可以有效改善催化剂的氧化还原性能和表面酸性.Mo O3作为一种可以提供大量酸性位的氧化物,常被用作助剂改善钒钨钛催化剂的活性.研究显示, Mo O3的引入可以促进催化剂中钒物种的分散度以及提高表面酸性.基于此,我们制备了一系列不同Mo含量的Mo O3/Ce Ti Ox催化剂,以期提高Ce Ti Ox催化剂的低温脱硝性能及抗SO2中毒能力,并着重研究表面Mo的修饰对Ce Ti Ox催化剂物理化学性质的影响.研究发现,表面Mo修饰可以显著提高Ce Ti Ox的低温催化活性,其脱硝效率在150 oC即可达到80%,同时抗SO2中毒能力也得到增强.进一步借助X射线衍射、比表面积测定、氢气程序升温还原、氨气程序升温脱附和X射线光电子能谱等方法对催化剂进行了全面表征分析.结果显示,表面Mo修饰对Ce Ti Ox催化剂物理化学性质的影响与其脱硝性能有着密不可分的关系.首先,钼物种主要是以Mo O3的形式存在于Ce Ti Ox表面,其最佳的负载量为4wt.%.其次,表面Mo的沉积显著提高了催化剂的表面酸量,尤其是Br?nsted酸位的数量,而表面酸位的增加有利于催化剂吸附与活化反应物种NH3;同时,表面Mo修饰还减弱了硝酸盐在催化剂表面的吸附,进一步促使NH3-SCR反应按照Eley-Rideal机理顺利进行.最后,该催化剂在H2O和SO2存在的条件下仍具有最佳的脱硝性能,因而有望用于实际含SO2的低温烟气脱硝.     

富氧条件下氢气选择催化还原氮氧化物研究的进展

 富氧条件下, 氢气选择催化还原 (H2-SCR) 是消除氮氧化物的有效方法. 本文介绍了 H2-SCR 反应特点及其研究现状, 重点总结和评述了应用于 H2-SCR 反应的氧化物和分子筛负载的 Pt 或 Pd 催化剂, 以及 H2-SCR 反应机理, 并展望了今后 H2-SCR 研究的方向.