Mg0.9Ti0.1Ni1－xCox (x＝0.05, 0.1, 0.15, 0.2)合金的合成及电化学性能研究

采用机械合金化法合成了Mg_0.9Ti_0.1Ni_1－xCo_x (x＝0.05, 0.1, 0.15, 0.2)系列四元合金, 并对该系列合金的结构和电化学性能等方面进行了研究. 球磨100 h的该系列合金, XRD结果表明, X射线衍射峰均呈现宽化趋势, 基本呈非晶态. 充放电结果表明, 该系列合金具有较好的活化性能, 它们的循环稳定性明显好于MgNi合金, 其中Mg_0.9Ti_0.1Ni_0.8Co_0.2最大放电容量最高, 为427.5 mAh•g^－1. 在充放电循环过程中, Mg在合金表面形成了Mg(OH)₂是合金电极衰减的主要原因. 腐蚀曲线的测试结果表明, Co的添加可以提高合金电极在碱液中的抗腐蚀能力, 从而提高了电极的循环稳定性.     

四元Mg0.9Ti0.1Ni0.9X0.1(X=Mn,Zn,Co,Fe)系列合金的制备及性能研究

用机械合金化法合成了Mg0.9Ti0.1Ni0.9X0.1(X=Mn,Zn,Co,Fe)系列合金.X射线衍射(XRD)结构分析表明,用X部分替代Ni后,促进了Mg0.9Ti0.1Ni合金的非晶化过程.用Co和Fe部分替代Ni提高了合金的放电容量,但却降低了合金的循环稳定性.用Zn和Mn部分替代Ni提高了合金电极的循环寿命,尤其是Mg0.9Ti0.1Ni0.9Zn0.1合金电极经10个充放电循环后,其放电容量仍可达到313.8mA.h/g.对添加Co后的合金进行p-c-T测试发现,Mg0.9Ti0.1Ni0.9Co0.1合金的吸放氢容量明显比Mg0.9Ti0.1Ni合金高,这与电化学所测到的结果一致.     

四元Mg0.9Ti0.1Ni0.9X0.1(X=Mn,Zn,Co,Fe)系列合金的制备及性能研究

用机械合金化法合成了Mg0.9Ti0.1Ni0.9X0.1(X=Mn, Zn, Co, Fe)系列合金. X射线衍射(XRD)结构分析表明, 用X部分替代Ni后, 促进了Mg0.9Ti0.1Ni合金的非晶化过程. 用Co和Fe部分替代Ni提高了合金的放电容量, 但却降低了合金的循环稳定性. 用Zn和Mn部分替代Ni提高了合金电极的循环寿命, 尤其是Mg0.9Ti0.1Ni0.9Zn0.1合金电极经10个充放电循环后, 其放电容量仍可达到313.8 mA·h/g. 对添加Co后的合金进行p-c-T测试发现, Mg0.9Ti0.1Ni0.9Co0.1合金的吸放氢容量明显比Mg0.9Ti0.1Ni合金高, 这与电化学所测到的结果一致.     

Mg0.9Ti0.1Ni0.85Co0.15合金的石墨粉及镍粉球磨表面包覆性能

选用非晶态的Mg0.9Ti0.1Ni0.85Co0.15合金粉末与石墨粉及镍粉进行球磨表面包覆。SEM分析结果表明,己包覆石墨和镍粉的合金表面上吸附着一层小的颗粒,形成薄层将原来的合金表面包覆起来。使用XPS分析了合金表面元素。结果表明,包覆石墨粉后,合金表面碳元素的质量分数和原子分数均增加,Mg的质量分数从22.74%减小至22.23%,原子分数从36.43%减小到32.94%,从而减小了Mg在碱液中的腐蚀几率,提高合金的抗腐蚀性能;包覆镍粉后,合金表面Ni的质量分数由59.89%增加到60.04%,原子分数由40.63%增加到41.02%,形成合金表面富Ni的保护层,提高了合金的抗腐蚀性能。充放电循环测试表明,循环30周后,包覆石墨粉的合金电极容量保持率为32.05%,包覆镍粉的合金电极容量保持率为41.26%,而未包覆的电极容量保持率仅为17.88%。合金电极极化曲线测试结果表明,石墨或镍粉的包覆提高了Mg0.9Ti0.1Ni0.85Co0.15合金电极的循环稳定性和在KOH碱液中的抗腐蚀性能。     

钛和锆的添加对MgNi型合金电极电化学性能的影响

用机械球磨法（MA）成功合成了镁基储氢合金MgNi, Mg0.9Ti0.1Ni和Mg0.9Ti0.1Ni0.9Co0.1。研究了其结构和电化学性能。X射线衍射（XRD）和扫描电镜（SEM）结果表明合金为非晶结构，并有少量的Ni衍射峰存在。充放电测试结果表明这一系列合金具有很好的电化学活性。Ti和Co的替代使合金的循环稳定性好于MgNi合金。50周充放电循环后，Mg0.9Ti0.1Ni0.9Co0.1合金的放电容量明显好于MgNi合金，Mg0.9Ti0.1Ni0.9Co0.1的放电容量比MgNi合金高102.8%，比Mg0.9Ti0.1Ni合金高45.49%。在充放电循环过程中，合金电极容量衰减的主要原因是在合金电极表面Mg变成了Mg(OH)2。Tafel极化测试表明Ti和Co的添加可以提高合金电极在碱液中的抗腐蚀性能和提高合金电极的循环稳定性。EIS测试结果表明Ti和Co的替代可以明显提高MgNi型合金表面的电催化活性。     

四元Mg0.9Ti0.1Ni0.9X0.1(X=Mn,Zn,Co,Fe)系列合金的制备及性能研究

用机械合金化法合成了Mg0·9Ti0·1Ni0·9X0·1(X=Mn,Zn,Co,Fe)系列合金.X射线衍射(XRD)结构分析表明,用X部分替代Ni后,促进了Mg0·9Ti0·1Ni合金的非晶化过程.用Co和Fe部分替代Ni提高了合金的放电容量,但却降低了合金的循环稳定性.用Zn和Mn部分替代Ni提高了合金电极的循环寿命,尤其是Mg0·9Ti0·1Ni0·9Zn0·1合金电极经10个充放电循环后,其放电容量仍可达到313·8mA·h/g.对添加Co后的合金进行p-c-T测试发现,Mg0·9Ti0·1Ni0·9Co0·1合金的吸放氢容量明显比Mg0·9Ti0·1Ni合金高,这与电化学所测到的结果一致.     

Mg1-xTixNi(0≤x≤0.4)系列合金的合成及性能研究

采用机械合金化法成功制备了Mg1-xTixNi(0≤x≤0.4)系列三元合金.XRD结构分析表明,不同成分的合金在相同的球磨时间下非晶化程度有所区别,并且合金的非晶化程度随着球磨时间的增加而趋于完全.少量Ti的加入使得该系列合金的电化学性能及循环稳定性都有所提高.在球磨120h的该系列合金中,Mg0.9Ti0.1Ni合金的最大初始放电容量达到356.85mA·h·g-1(100mA·g-1,-0.5Vvs.Hg/HgO),而Mg0.7Ti0.3Ni合金的循环稳定性最好.Ti的加入亦提高了合金的抗腐蚀性能,使其腐蚀电位正移.     

MgNi-x% TiNi0.5Mn0.5 (x＝10, 30, 50)贮氢合金的制备与电化学性能

用机械合金化法成功制备出MgNi和TiNi0.5Mn0.5合金, 并将不同质量的TiNi0.5Mn0.5与MgNi合金球磨复合10 h制备MgNi-x% TiNi0.5Mn0.5 (x＝10, 30, 50)合金. XRD结果表明球磨后几种合金均为非晶体, TiNi0.5Mn0.5均匀分散到MgNi合金主相中; 充放电结果表明MgNi-TiNi0.5Mn0.5复合合金的初始容量比纯MgNi合金(443.12 mAh/g)低, MgNi- 10% TiNi0.5Mn0.5首次放电容量是394.46 mAh/g, 但循环寿命有较大的改善, 50次循环后容量保持在232.57 mAh/g, 保持率达59%; 动电位扫描结果表明复合后合金电极抗腐蚀能力提高; 循环伏安法和电化学阻抗谱法研究结果表明: 复合后电极表面的电化学催化性能增强, H原子在合金电极内部的扩散阻抗减小.     

新型镁基储氢合金的合成及电化学性能的研究

用扩散法成功地合成了Mg_1.5Al_0.5-xNiV_x(x=0,0.1,0.2,0.3,0.4)系列合金。XRD结构分析表明,合金中出现一个新的物相,其化学式为Mg₃AlNi₂,属立方晶系,Fd3m空间群,新相具有很好的电化学性能。钒的添加使合金的容量进一步提高。未经任何预处理的Mg_1.5Al_0.3V_0.2Ni合金的最大放电容量达到333mA·h·g^-1(50mA·g^-1,-0.5Vvs.Hg/HgO).Al对六方晶系Mg₂Ni合金结构中Mg的部分取代对于延长合金的循环寿命有重要作用。     

非金属与金属的协同作用对镁基储氢合金电化学性能的影响

用机械球磨法分别以Ti、B、复合物TiB对非晶态Mg45Ti3V2Ni50储氢合金进行了表面修饰.实验结果表明,恰当比例的TiB球磨修饰对镁基储氢合金循环稳定性远好于Ti、B同比例单独修饰合金电极的效果.Mg45Ti3V2Ni50与TiB质量比为2∶1的Mg45Ti3V2Ni50-TiB(2∶1)复合合金电极的初始放电容量为529.4mAh·g-1,第50次循环放电容量仍为277.1mAh·g-1.复合物TiB中Ti、B元素之间和复合合金中合金元素与TiB之间产生了金属与非金属的协同作用,导致复合合金新的立体褶皱结构的生成,增强了修饰层与合金间的作用,Mg45Ti3V2Ni50-TiB(2∶1)合金电极表面活性增强,循环稳定性显著提高.     

Electrochemical Characteristics of Mg0.9Ti0.1-xZrxNi （x=0.02, 0.04, 0.06） Alloys

Mg-based hydrogen storage alloys Mg0.9Ti0.1-xZrxNi (x=0.02, 0.04, 0.06) were successfully prepared by means of mechanical alloying (MA). The effects of Zr addition on the discharge capacity and the cycle performance of the Mg-based electrodes were also studied. It was found that the discharge capacities were improved with addition of a small amount of Zr and the cycle performances of the alloy were stabilized with the addition of Ti. The effects of surface modification or coating on the properties of Mg0.9Ti0.06Zr0.04Ni were also studied. The results indicated that coating with graphite improved both the discharge capacity and cycle life of the amorphous Mg0.9Ti0.06Zr0.04Ni electrode.     

Effects of Ti and Co on the Electrochemical Characteristics of MgNi-Based Alloy Electrodes

Mg-based hydrogen storage alloys MgNi, Mg0.9Ti0.1Ni and Mg0.9Ti0.1Ni0.9Co0.1 were successfully prepared by means of mechanical alloying （MA）. The structure and the electrochemical characteristics of these Mg-based materials were also studied. The results of X-ray diffraction （XRD） and scanning electron microscopy （SEM） show that the main phases of the alloys exhibit amorphous structures, and trace of Ni co-exists. The charge-discharge cycle tests indicate these alloys have good electrochemical active characteristics. And the cycle stability of Ti and Co doped alloy was better than that of MgNi alloy. After 50 cycle charge-discharge, the discharge capacity of the Mg0.9Ti0.1Ni0.9Co0.1 alloy was much better than that of MgNi and Mg0.9Ti0.1Ni alloys. The discharge capacity of Mg0.9Ti0.1Ni0.9Co0.1 was 102.8% higher than that of MgNi alloy, and 45.49% higher than that of the Mg0.9Ti0.1Ni alloy. During the process of charge-discharge cycle test, the main reason for the electrode capacity fading is the corrosion of Mg to Mg（OH）2 on the surface of alloys. The Tafel polarization test indicates Ti and Co improve the anticorrosion in an alkaline solution. The EIS results suggest that proper amount of Ti and Co doping improve the electrochemical catalytical activity on the Mg-based alloy surface significantly.     

La0.7Mg0.3(Ni1-xCox)3.5 (0≤x≤0.5)储氢合金电化学性能

近年来,具有AB2和AB5复合结构的LaNi3系和La2Ni7系储氢材料由于具有较高的储氢量而引起了人们的关注[1]. 它们可在较温和条件下快速吸放氢, 且理论吸氢量分别为LaNi5的1.25倍及1.11倍.     

CeMn1-xAl1-xNi2x(x=0.00, 0.25, 0.50和0.75)合金的结构和电化学性能研究

研究了镍部分取代AB2型CeMnAl金属间化合物B侧Mn,Al形成的化学计量比合金的结构和电化学性能。XRD分析,SEM形貌观察和电化学性能测试结果表明:镍的部分取代使合金发生了相变化,形成了新相,CeMn1-xAl1-xNi2x(x=0.0,0.25,0.50和0.75)合金电极的电化学活性得到很大提高,298K时的放电容量从x=0时的17.93mAh.g-1提高到x=0.75时的118.3mAh.g-1,328 K时的放电容量从x=0时的68.42mAh.g-1提高到x=0.75时的216.1mAh.g-1。合金的电化学P-C-T曲线表明:无Ni的CeMnAl合金几乎没有平衡氢压平台,随Ni取代量的增加,合金的平衡氢压平台斜率变小,宽度增大。     

La_(0.7)Pr_(0.15)Nd_(0.05)Mg_(0.3)Ni_(3.3-x)Co_(0.2)Al_(0.1)(Co_(0.75)Mn_(0.25))_x(x=0.0,0.2,0.4,0.6)的电化学性能研究

在Ar气保护下用悬浮熔炼制备La0.7Pr0.15Nd0.05Mg0.3N i3.3-xCo0.2A l0.1(Co0.75Mn0.25)x(x=0.0,0.2,0.4,0.6)合金,系统研究了Co和Mn对合金储氢性能和电化学性能的影响。XRD相分析表明,合金相主要由(La,Pr)(N i,Co)5,LaMg2N i9,(La,Nd)2N i7和LaN i3相组成;添加Co和Mn后合金中(La,Pr)(N i,Co)5,(La,Nd)2N i7和LaN i3相晶胞体积增加,LaMg2N i9相晶胞体积变小。合金放氢PCT曲线测试表明,随着合金中Co和Mn含量的增加,合金吸氢量先减小后增加,放氢平台压下降,合金氢化物稳定性增加。合金电极电化学性能测试表明,添加Co和Mn使合金电极放电容量减小,容量保持率S100从53.2%(x=0.0)增加到63.0%(x=0.6),合金电极的电循环稳定性增强,高倍率放电性能HRD1500先增加后减小。此外,合金电极的极化电阻先减小后增加,交换电流密度、循环伏安特性阳极峰电流密度和极限电流密度先增加后减小,合金内氢原子扩散系数先增加后减小,表明添加适量的Co和Mn可以提高合金电...     

La0.8-xPrxMg0.2Ni3.2Co0.4Al0.2(x=0～0.4)储氢合金的相结构与电化学性能

研究了Pr替代La对La0．8-xPrxMg0．2Ni3．2Co0．4Al0．2（X=0～0．4）储氢合金相结构与电化学性能的影响。XRD及Rietveld全谱拟合方法分析表明，合金主要由PrsCo-9，Ce5Co-9及CaCu5型物相组成。随着Pr含量x值的增加，合金中A5B19型物相（Pr5Co19＋Ce5Co19）逐渐增多，同时各物相的晶胞参数（a，c）和晶胞体积（y）均减小。电化学测试表明，x值的增加对合金电极的活化性能影响不大，但可显著提高合金电极的循环稳定性。合金的高倍率放电性能（HRD）随着x的增加呈增加趋势，在x=0．3时存在最大值（HRD900=89．6％）；合金电极的HRD主要由合金电极表面的电荷迁移速率所控制。     

储氢合金La0.7-xCexMg0.3Ni2.4Co0.6(x=0～0.4)电化学性能研究

研究了以Ce部分取代La对AB3型储氢合金La0.7-xCexMg0.3Ni2.4Co0.6(x=0~0.4)结构和电化学性能的影响.实验表明,该系列合金主要包含LaNi3相和LaNi5相.随着Ce含量的增加,合金电极的最大放电容量逐渐降低,但循环稳定性得到了明显改善.