球磨辅助高温固相法制备Li1.0Na0.2Ni0.13Co0.13Mn0.54O2正极材料及其性能

以乙酸盐(乙酸锂、乙酸钠、乙酸钴、乙酸镍、乙酸锰等)为原材料,采用球磨辅助高温固相法制备Li_(1.0)Na_(0.2)Ni_(0.13)Co_(0.13)Mn_(0.54)O_2正极材料。借助XRD、SEM等表征材料的结构和形貌,利用循环伏安、恒流充放电、交流阻抗等方法研究材料的电化学性能。结果表明,钠的掺杂导致颗粒表面光滑度降低,形成Na_(0.77)Mn O_(2.05)新相。0.05C活化过程中,掺钠样品和未掺钠样品首次放电比容量分别为258.4 m Ah·g~(-1)和215.8 m Ah·g~(-1),库伦效率分别为75.2%和72.8%;2C放电比容量分别为116.3 m Ah·g~(-1)和106.2 m Ah·g~(-1)。研究发现,掺钠可减小首次充放电过程的不可逆容量,提高容量保持率;改善倍率性能与容量恢复特性;降低SEI膜阻抗和电荷转移阻抗;掺钠后样品首次循环就可以基本完成Li_2Mn O_3组分向稳定结构的转化,而未掺杂的样品需要两次循环才能逐步完成该过程;XPS结果表明,掺钠样品中Ni~(2+)、Co~(3+)、Mn~(4+)所占比例明显提高,改善了样品的稳定性和电化学性能;循环200次后的XRD结果表明掺钠与未掺钠材料在脱嵌锂反应中的相变化过程基本一致,良好有序的层状结构遭到破坏是循环过程中容量衰减的主要原因。     

钠离子电池正极材料Na3V2(PO4)2O2F的控制合成与电化学性能优化

采用简单的水热合成法制备氟磷酸钒氧钠(Na_3V_2(PO_4)_2O_2F,简写为NVPOF),通过调节水热反应溶液的pH值和反应温度等关键参数,有效调节NVPOF的颗粒尺寸和均匀性,优化其电化学性能。研究结果显示,性能最优的NVPOF的合成条件是:pH值为7.00±0.05,水热反应温度为170℃。在该条件下合成的NVPOF正极材料具有优异的电化学性能,表现为0.1C(1C=130 mA·g~(-1))的倍率下放电比容量可达123.2 mAh·g~(-1),且在20C的高倍率下仍可实现85.9 mAh·g~(-1)的比容量,在1C下循环200圈后其容量保持率为96.2%,表明该材料具有高容量、优异的倍率和循环性能。所制备的NVPOF颗粒为纳米尺度且具有很高的均匀性,可缩短Na~+的传输路径从而缩短其传输时间,且NVPOF晶体结构具有高稳定性,是一类具有高性能的钠离子电池正极材料。     

LiNi0.8Co0.15Al0.05O2制备过程中聚乙烯吡咯烷酮的加入对其电化学性能的影响

为提高LiNi_(0.8)Co_(0.15)Al_(0.05)O_2(NCA)材料的电化学性能,在NCA材料的制备过程中加入聚乙烯吡咯烷酮(PVP),通过调控所得NCA材料的形貌来提高其电化学性能。所得材料采用X射线衍射仪和扫描电子显微镜进行形貌结构表征,电化学性能经组装成纽扣电池,用电池程控测试仪和电化学工作站进行测试。研究结果表明:由于PVP的空间效应和静电作用,PVP改性的NCA材料拥有更完整的棒状结构、发育出更好的层状结构,电化学储能性能得到较大的提升。在0.1C下,材料的首次放电比容量和充放电效率分别从143.36 mAh·g~(-1)、78.25%提高到了170.24 mAh·g~(-1)、89.20%;在0.2C的实验室条件下循环50次后,容量保持率为94.28%。     

石墨烯修饰改性制备锂离子电池LiFePO4/LiNi0.8Co0.15Al0.05O2复合正极材料及其性能

采用两步干混-球磨方法制备了石墨烯掺杂改性的锂离子电池LiFePO_4/LiNi_(0.8)Co_(0.15)Al_(0.05)O_2复合正极材料,实现LiNi_(0.8)Co_(0.15)Al_(0.05)O_2材料的高容量和高安全性。借助X射线衍射(XRD)、扫描电镜(SEM)、透射电镜(TEM)、X射线光电子能谱(XPS)以及电化学测试等表征手段对材料的晶体结构、微观形貌和电化学性能进行了较系统的研究。结果表明,石墨烯的存在实现了Li Fe PO4材料在LiNi_(0.8)Co_(0.15)Al_(0.05)O_2材料表面的完全包覆,形成致密的包覆层,进一步抑制LiNi_(0.8)Co_(0.15)Al_(0.05)O_2与电解液之间的副反应,提高活性材料利用率和循环性能。三者之间构成导电网络,加快电子渗透和传输,提高倍率性能。Li Fe PO4质量分数为20%的Li Fe PO4-Graphene/LiNi_(0.8)Co_(0.15)Al_(0.05)O_2样品具有最佳的容量性能和长循环性能,0.1C时放电容量达到202.5 m Ah·g~(-1),3C时放电容量仍然可保持在160.5 m Ah·g~(-1)。50℃在2.8~4.3 V,0.5C下循环100次后,容量保持率为91.9%,优于LiNi_(0.8)Co_(0.15)Al_(0.05)O_2和LiFePO_4/LiNi_(0.8)Co_(0.15)Al_(0.05)O_2样品的72.9%和82.0%。     

CuO表面修饰锐钛矿TiO2纳米管阵列及其电化学嵌锂性能

以(CH_2OH)_2、NH4F和HCl为电解液,纯Ti片、CuCl_2和Na NO3为主要原料,联用阳极氧化和水热法制备CuO表面修饰锐钛矿TiO_2纳米管阵列锂离子电池负极材料(CuO/TiO_2)。使用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、能谱仪(EDS)、X射线光电子能谱仪(XPS)和X射线衍射(XRD),研究样品的形貌特征、元素分布、价态和微观物相组成。利用电池充放电测试仪和电化学工作站,探讨材料的电化学嵌锂性能。结果表明,表面修饰后的锐钛矿TiO_2纳米管阵列外侧出现了大量绒毛状纳米CuO,单个绒毛结构的宽度约4 nm,长度约10 nm。在0.3C的电流密度下进行恒电流充放电测试,首次放电容量为550 m Ah·g~(-1),充电容量为490 m Ah·g~(-1)。50次循环后,可逆电流容量仍保持在320 m Ah·g~(-1),具有良好的循环稳定性和电化学特性。     

高容量梯度锂离子电池正极材料Li[Ni0.85Co0.08Mn0.07]O2的制备

通过改变金属离子的浓度比例,采用连续控制结晶法制备出镍钴锰金属元素连续浓度梯度变化的前驱体[Ni_(0.85)Co_(0.08)Mn_(0.07)](OH)_2。再与LiOH·H_2O混合,通过高温固相法得到全梯度材料Li[Ni_(0.85)Co_(0.08)Mn_(0.07)]O_2。XRD结果表明该梯度材料阳离子混排程度比纯相Li[Ni_(0.85)Co_(0.08)Mn_(0.07)]O_2更低,具有更好的层状结构。扫描电镜结果显示Li[Ni_(0.85)Co_(0.08)Mn_(0.07)]O_2具有球形形貌,粒径分布比较集中,颗粒平均粒径分布在11.5～12μm,切面元素扫描显示沿着球径方向从球心到外壳,镍含量越来越低,而钴锰的含量越来越高。越靠近颗粒表面,镍的含量越低,而钴锰的含量越高。电材料在0.1C放电倍率下首次放电比容量可达204.3 mAh·g~(-1),1C放电倍率的首次放电比容量为185.3 mAh·g~(-1),循环100次后,仍有164.7 mAh·g~(-1),容量保持率达89.17%。在高温55℃环境下,1C首次放电比容量可达202.7 mAh·g~(-1),容量保持率为85.84%,性能均好于纯相Li[Ni_(0.85)Co_(0.08)Mn_(0.07)]O_2。     

高电化学活性SnO2/TiO2空心微球的制备及其性能

采用一种简便的无模板溶剂热法合成了尺寸在1μm左右、具有堆叠结构的SnO_2/TiO_2空心微球。合成过程的研究结果表明:SnO_2/TiO_2空心微球在形成过程中经历了空心、被填充、分裂到再次形成空心结构的过程。随后,SnO_2/TiO_2空心微球作为锂离子电池负极材料的电化学性能测试结果表明:SnO_2/TiO_2空心微球在0.1 A·g~(-1)的电流密度下,其首次放电容量达到1 484.9mAh·g~(-1),库伦效率为49.0%。经过600次循环后,其放电容量依然可以达到565.6 mAh·g~(-1),显示了高的容量和循环稳定性。     

钨掺杂对锂离子电池LiNiO2正极材料性能的影响

采用溶胶-凝胶法制备了钨掺杂镍酸锂正极材料(LiNi_(1-x)W_xO_2,x=1%、3%),研究了钨掺杂对LiNiO_2正极材料电化学性能的影响。结果表明,钨掺杂明显地改善了LiNiO_2的充放电循环性能,在100 mA·g~(-1)的电流密度和2.5～4.5 V电压范围的测试条件下,LiNi_(0.99)W_(0.01)O_2材料循环400次后的容量保持率为62.51%,而LiNiO_2在相同循环条件下的保持率仅为47.06%。同时,钨掺杂也提升了LiNiO_2的充放电倍率性能,掺杂材料在每一个倍率下放电比容量均高于未掺杂材料。     

δ-MnO2改性石墨烯气凝胶的制备及电化学性能

通过对还原石墨烯气凝胶(RGOA)进行δ-MnO_2纳米颗粒改性制备出锂离子电池负极,并获得了良好的电化学性能。同时研究了δ-MnO_2的负载量对三维复合RGOA/δ-MnO_2负极材料电化学性能的影响,发现随着δ-MnO_2负载量的增加,锂离子电池性能先增后减,在δ-MnO_2负载量合适时(160 mg)比容量达到最大值(1 701.9 mAh·g~(-1)),该值明显高于δ-MnO_2负极的理论容量1 230 m Ah·g~(-1)。此外,该RGOA/δ-MnO_2-160 mg负极即便在5 A·g~(-1)的大电流下经历600次循环后仍能保持210.5 mAh·g~(-1)的比容量。如此优异的电化学性能归因于RGOA的大比表面积和高导电性,以及δ-MnO_2颗粒的高比容量和高催化活性。此外,三维石墨烯气凝胶中大量的孔洞有利于提供足够的空间负载超细δ-MnO_2颗粒,避免了δ-MnO_2在嵌锂过程中的体积膨胀以及抑制了固液界面保护膜(SEM)的加厚。通过计算赝电容对锂离子电池比容量的贡献,证实RGOA/δ-MnO_2电极的充放电过程为赝电容行为所主导,这也是取得良好比容量和循环性能的另一重要原因。     

掺F影响LiNi0.8Co0.1Mn0.1O2结构和性能的微观机制

以氟化锂为氟源,通过高温固相法合成了F掺杂的LiNi_(0.8)Co_(0.1)Mn_(0.1)O_2。采用X射线衍射仪(XRD)、扫描电镜(SEM)、X射线光电子能谱(XPS)和电化学测试等手段研究F影响LiNi_(0.8)Co_(0.1)Mn_(0.1)O_2结构和性能的微观机制。结果表明:适量F掺杂可以提高正极材料的放电比容量,改善其倍率性、循环性和热稳定性。当F掺杂量(物质的量分数)为1.5%时,材料的综合电化学性能最优,初始放电比容量(0.2C)和50周循环容量保持率(1C)分别由原始的174.0 mAh·g~(-1)(78.7%)提高到178.6 mAh·g~(-1)(85.7%)。LiNi_(0.8)Co_(0.1)Mn_(0.1)O_2材料性能的改善可归因于F能够增强过渡金属层、锂层与氧层之间的结合力,提高材料的结构稳定性。此外,F掺杂还有利于降低电化学反应中的界面电阻和电荷转移阻抗。     

TiO2/SnO2复合光催化剂的耦合效应

采用改进的sol gel技术制备TiO2/SnO2耦合型半导体光催化剂,利用XRD、气相色谱 仪、粒度仪和表面光电压装置等研究了耦合型半导体光催化机理和光催化效率的影响因素, 并通过降解甲醛探讨其在空气污染治理中的作用.实验结果表明,添加20 ％(mol) SnO2的复 合半导体光催化剂,其光催化效率比纯TiO2高一倍以上.据实验结果和粒子紧密堆积原理,提 出强耦合效应和弱耦合效应的光催化反应模型,并用此模型较好地解释了TiO2/SnO2复合型半 导体光催化剂的光催化效率随SnO2含量变化规律.     

CeO2改性Ag-V2O5/TiO2催化剂的甲基吡啶氧化脱甲基性能

以锐钛矿TiO_2为载体,考察了CeO_2改性对Ag-CeO_2-V_2O_5/TiO_2催化3-甲基吡啶氧化脱甲基性能的影响,并优化了催化剂组成与制备条件.结果表明:Ce掺杂改性不仅能够与V物种作用形成Ce VO_4,而且促进V_2O_5分散,改善活性组分的氧化还原性能,从而提高3-甲基吡啶脱甲基转化率与选择性,改善Ag-V_2O_5/TiO_2催化性能.适宜的催化剂组成为V_2O_5负载量15%,Ce/V的摩尔比0.33,Ag质量分数1.0%.过高的焙烧温度将导致TiO_2载体向金红石型转变,Ag-CeO_2-V_2O_5/TiO_2适宜制备条件为450℃焙烧4 h.     

Conversion of NO in NO/N2, NO/O2/N2, NO/C2H4/N2 and NO/C2H4/O2/N2 Systems by Dielectric Barrier Discharge Plasmas

An experimental study on the conversion of NO in the NO/N₂, NO/O₂/N₂, NO/C₂H₄/N₂ and NO/C₂H₄/O₂/N₂ systems has been carried out using dielectric barrier discharge (DBD) plasmas at atmospheric pressure. In the NO/N₂ system, NO decomposition to N₂ and O₂ is the dominating reaction; NO conversion to NO₂ is less significant. O₂ produced from NO decomposition was detected by an on-line mass spectrometer. With the increase of NO initial concentration, the concentration of O₂ produced decreases at 298 K, but slightly increases at 523 K. In the NO/O₂/N₂ system, NO is mainly oxidized to NO₂, but NO conversion becomes very low at 523 K and over 1.6% of O₂. In the NO/C₂H₄/N₂ system, NO is reduced to N₂ with about the same NO conversion as that in the NO/N₂ system but without NO₂ formation. In the NO/C₂H₄/O₂/N₂ system, the oxidation of NO to NO₂ is dramatically promoted. At 523 K, with the increase of the energy density, NO conversion increases rapidly first, and then almost stabilizes at 93–91% of NO conversion with 61–55% of NO₂ selectivity in the energy density range of 317–550 J L⁻¹. It finally decreases gradually at high energy density. A negligible amount of N₂O is formed in the above four systems. Of the four systems studied, NO conversion and NO₂ selectivity of the NO/C₂H₄/O₂/N₂ system are the highest, and NO/O₂/C₂H₄/N₂ system has the lowest electrical energy consumption per NO molecule converted.     

Li2O-TiO2-SiO2-P2O5和Li2O-TiO2-Al2O3-P2O5体系锂离子固体电解质的制备及性能研究

一些具有NASICON型网格结构的固体电解质具有高的电导率和好的稳定性,NASICON的意思是Na Super Ionic Conductor[1]。当NaZr2(PO4)3中P5 被Si4 部分取代时便可以得到具有NASICON结构的Na1 xZr2SixP3-xO12体系,其具有高的钠离子电导率。然而有相同结构的Li1 xZr2SixP3-xO12体系的离子电导率却很低,这是因为Li 半径太小,而NASICON三维网格结构的离子通道太大,两者不匹配而使电导率下降[2]。但当LiZr2(PO4)3中Zr4 被离子半径小些的Ti4 取代,所得LiTi2(PO4)3的通道就与Li 半径相匹配,适合于锂离子的迁移,从而使其电导率…     

Energetics of copper diphosphates – Cu2P2O7 and Cu3(P2O6OH)2

Differential scanning calorimetry and high temperature oxide melt solution calorimetry are used to study enthalpy of phase transition and enthalpies of formation of Cu₂P₂O₇ and Cu₃(P₂O₆OH)₂. α-Cu₂P₂O₇ is reversibly transformed to β-Cu₂P₂O₇ at 338–363 K with an enthalpy of phase transition of 0.15 ± 0.03 kJ mol⁻¹. Enthalpies of formation from oxides of α-Cu₂P₂O₇ and Cu₃(P₂O₆OH)₂ are −279.0 ± 1.4 kJ mol⁻¹ and −538.8 ± 2.7 kJ mol⁻¹, and their standard enthalpies of formation (enthalpy of formation from elements) are −2096.1 ± 4.3 kJ mol⁻¹ and −4302.7 ± 6.7 kJ mol⁻¹, respectively. The presence of hydrogen in diphosphate groups changes the geometry of Cu(II) and decreases acid–base interaction between oxide components in Cu₃(P₂O₆OH)₂, thus decreasing its thermodynamic stability.     

Cr2(WO4)3和Cr2(MoO4)3的负热膨胀特性研究

用液相反应-前驱物烧结法制备了Cr₂(WO₄)₃和Cr₂(MoO₄)₃粉体。298～1 073 K的原位粉末X射线衍射数据表明Cr₂(WO₄)₃和Cr₂(MoO₄)₃的晶胞体积随温度的升高而增大, 本征线热膨胀系数分别为(1.274±0.003)×10^-6 K^-1和(1.612±0.003)×10^-6 K^-1。用热膨胀仪研究了Cr₂(WO₄)₃和Cr₂(MoO₄)₃在静态空气中298～1 073 K范围内热膨胀行为，即开始表现为正热膨胀，随后在相转变点达到最大值，最后表现为负热膨胀，其负热膨胀系数分别为(-7.033±0.014)×10^-6 K^-1和(-9.282±0.019)×10^-6 K^-1。     

g-C3N4/Bi2O2CO32D纳米片复合材料的制备及可见光催化性能研究

采用自组装和化学沉淀法分别制得两种可见光驱动复合材料石墨相氮化碳/碳酸氧铋(g-C_3N_4/Bi_2O_2CO_3).采用X射线衍射光谱(XRD),紫外可见光谱、扫描电镜(SEM)、N_2吸附、电化学阻抗谱(EIS)和X射线光电子能谱(XPS)等分析手段对制备的催化剂进行了表征.结果表明,制备方法对纳米复合材料的晶相、形态及光学性能没有影响,但是影响g-C_3N_4和Bi_2O_2CO_3之间的相互作用力,导致光生电子-空穴对的分离速率存在显著差异.以可见光驱动苯酚和罗丹明B的降解实验为探针反应检测催化剂的光催化性能.实验结果表明自组装法得到的异质结催化剂中相互作用力更强,催化效果最高.O_2-是罗丹明B降解反应的主要活性物种,染料的光敏化、Bi_2O_2CO_3与g-C_3N_4综合效应,导致光生载流子电荷分离效率更高.     

EuZn2Si2 and EuZn2Ge2 Grown from Zn or Ga(ln)/Zn Flux

Single crystals of the novel ternary compounds EuZn₂Si₂ and EuZn₂Ge₂ were grown from pure gallium, indium, or zinc metal used as a flux solvent. Crystal properties were characterized using X-ray single-crystal analyses via Gandolfi and Weissenberg film techniques and by four-circle X-ray single-crystal diffractometry. The new compounds crystallize with ternary derivative structures of BaAl₄, i.e., EuZn₂Si₂ with ThCr₂Si₂-type (a=0.42607(2) nm, c=1.03956(5) nm, I4/mmm, R₁=0.038) and EuZn₂Ge₂ with CaBe₂Ge₂-type (a=0.43095(2) nm, c=1.07926(6) nm, P4/nmm, R₁=0.067). XAS and magnetic measurements on EuZn₂Si₂ and EuZn₂Ge₂ revealed in both compounds the presence of Eu²⁺ ions carrying large magnetic moments, which order magnetically at low temperatures. The magnetic phase transition occurs at T_N=16 and 7.5 K for the silicide and the germanide, respectively. In EuZn₂Si₂ there occurs a spin reorientation at 13 K and furthermore some canting of antiferromagnetically ordered moments below about 10 K. In EuZn₂Ge₂ a canted antiferromagnetic structure is formed just at T_N.     

Mn-Na2WO4/SiO2催化剂表面活性中心结构的DFT研究

Mn Na2WO4/SiO2 is one of the best catalysts for oxidative coupling of methane.To investigate the nature of active centers and the reaction mechanism,the structure of possible metal sites formed by tungsten and manganese over the silica surface were studied using molecular simulation method and ab initio DFT calculations.Silica support exists in the catalyst as 岐瞔ristobalite and its (111) face exposes preferentially to the surface.The calculated results show that tungsten interacts with the silica surface by three or one bridge oxygen atoms to form tetrahedral [WO4],and manganese interacts with single bridge oxygen to form dispersed [MnO4] or exists as oxide clusters.The nature of the molecular orbitals and the electronic structure suggest that the tetrahedral [WO4] site with single bridge oxygen is the most probable active center responsible for methane activation.     

Preparation of ZrO2-TiO2-CeO2 and Its Application in the Selective Catalytic Reduction of NO with NH3

TiO₂,ZrO₂-TiO₂,andZrO₂-TiO₂-CeO₂ were prepared by co-precipitation method and characterized by X-ray diffraction (XRD), specific surface area measurements (BET), temperature programmed desorption (NH₃-TPD), oxygen storage capacity (OSC), and temperature programmed reduction (H₂-TPR). The results showed that ZrO₂-TiO₂-CeO₂ exhibited large number of surface strong acid, possessed some oxygen storage capacity, and strong redox property. The three materials were used as supports and the monolith catalysts were prepared with 1% (w) V₂O₅ and 9% (w)WO₃ for selective catalytic reduction (SCR) of NO with ammonia in the presence of excessive O₂, and the results of catalytic activity showed that the catalyst used ZrO₂-TiO₂-CeO₂ as support yielded nearly 100% NO conversion at 275 °C at a gas hourly space velocity (GHSV) of 10000 h⁻¹, and it had the best catalytic activity and showed great potential for practical application.