Magnetic properties and magnetoresistance effect of Y1-xGdxMn6Sn6 (x=0－1) compounds

The magnetic properties and magnetoresistance effect of Y_1-xGd_xMn₆Sn₆ (x=0－1) compounds have been investigated by magnetization and resistivity measurements in the applied field range (0－5 T). Compounds with x=0.4－1 display ferrimagnetic behaviours in the whole magnetic ordering temperature range, while compounds with x=0－0.2 display a field-induced metamagnetic transition, and the threshold fields decrease with increasing Gd content. The compounds with x=0.1－0.2 undergo an antiferromagnetic to ferromagnetic transition with increasing temperature. The cell-parameter a and c and cell-volume V of compounds (x=0－1) increase with increasing Gd content. It was found that the saturation magnetization M_s of the compounds (x=0.4－1) decreases, while the ordering points of the compounds (x=0－1)increase with increasing Gd content. A large MR effect was observed in the compound with x=0.2, and the maximum absolute value of MR at 5 K under 3 T is close to 19.3%.     

Magnetic Properties and Magnetoresistance of HfFe6Ge6—Type Er1—xGdxMn6Ge6 and Ho1—xGdxMn6Ge6（0.2≤x≤0.9） Compounds

Magnetic properties and magnetoresistance effects of the Er1-xGdxMn6Ge6 and Ho1-xGdxMn6Ge6 (0.2≤x≤0.9) compounds have been studied by magnetic property and resistivity measurements in applied magnetic field up to 5T. For increasing Gd content, two series display a transition from the antiferromagnetic state to the ferrimagnetic state. The Er1-xGdxMn6Ge6 (x=0.2 and 0.5) and Ho1-xGdxMn6Ge6(x=0.2 and 0.4) compounds order antiferromagnetically at 430,432,423 and 425K, respectively. The Er1-xMn6Ge6 (x=0.8 and 0.9) and Ho1-xGdxMn6Ge6(x=0.7,0.8 and 0.9) compounds order ferrimagnetically at 462, 471, 450, 463 and 470K, respectively. The Er1-xGdxMn6Ge6 and Ho1-xGdxMn6Ge6 compounds undergo the second transitions below 71 and 82K, respectively. The magnetoresistance curves of the Er0.1Gd0.9Mn6Ge6 and Ho0.1Gd0.9Mn6Ge6 compounds in a field of 5T are presented and the magnetoresistance effects are related to the metamagnetic transistions.     

Magnetic properties and magnetoresistance of HfFe2Ge2-type Dy1-xGdxMn6Ge6 (x=0.1－0.6) compounds

The magnetic properties and magnetoresistance effects of Dy_{1-x}Gd_xMn_6Ge_6 (x=0.1－0.6) compounds have been studied by magnetic properties and resistivity measurements in applied magnetic fields up to 5T. The compounds with x=0.1, 0.2, 0.4 and 0.5 order antiferromagnetically at 425, 428, 430 and 432K, respectively, and there are second magnetic phase transitions below 100K. The compound with x=0.6 exhibits a transition from ferrimagnetic to antiferromagnetic, then to ferrimagnetic state again with decreasing temperature. Furthermore, it displays a field-induced metamagnetic transition, and its threshold field decreases with increasing temperature. The magnetoresistance curve of the compound with x=0.6 in applied magnetic fields up to 5T is presented and the magnetoresistance effects are related to the metamagnetic transitions.     

Magnetic Transitions and Magnetoresistance of Y1—xDyxMn6Sn6（x=0.2 and 0.3）

Magnetic transitions and magnetoresistance of HfFe6Ge6-type Y1-xDyxMn6Sn6 (x=0.2 and 0.3) have been investigated in the temperature range of 5-380K. It was found that the strong exchange interaction between the Dy and Mn sublattices results in incomplete ferromagnetism at low temperatures. At higher temperatures, the metamagnetic transition from an antiferromagnetic state to a ferrimagnetic state can be induced by a fairly small threshold field or by increasing temperature. The magnetic transition is accompanied by a large magnetoresistance effect of about -29% and -16% at 5K for x=0.2 and 0.3, respectively.     

Magnetic entropy change and magnetic phase transition of LaFe11.4Al1.6Cx （x=0-0.8） compounds

The unit cell volume and phase transition temperature of LaFe11.4Al1.6Cx compounds have been studied. The magnetic entropy change, refrigerant capacity and the type of magnetic phase transition are investigated in detail for LaFe11.4Al1.6Cx with x=0.1, All the LaFe11.4Al1.6Cx （x=0-0.8） compounds have the cubic NaZn13-type structure. The addition of carbon atoms brings about a considerable increase in the lattice parameter. The bulk expansion results in the change of phase transition temperature （Tc）, Tc increases from 187K to 269 K with x varying from 0.1 to 0.8, Meanwhile an increase in the lattice parameter can also cause a change of the magnetic ground state from antiferromagnetic to ferromagnetic. Large magnetic entropy change IASI is found over a large temperature range around Tc and the refrigerant capacity is about 322J/kg for LaFe11.4Al1.6C0.1. The magnetic phase transition belongs in weakly first-order one for x=0.1.     

Magnetoresistances and magnetic entropy changes associated with negative lattice expansions in NaZn13-type compounds LaFeCoSi

Magnetoresistances and magnetic entropy changes in NaZn13-type compounds La（Fel-xCox）11.9Si1.1 （x=0.04, 0.06, and 0.08） with Curie temperatures of 243 K, 274 K, and 301 K, respectively, are studied. The ferromagnetic ordering is accompanied by a negative lattice expansion. Large magnetic entropy changes in a wide temperature range from ～230 K to ～320 K are achieved. Raising Co content increases the Curie temperature but weakens the magnetovolume effect, thereby causing a decrease in magnetic entropy change. These materials exhibit a metallic character below Tc, whereas the electrical resistance decreases abruptly and then recovers the metal-like behaviour above Tc. Application of a magnetic field retains the transitions via increasing the ferromagnetic ordering temperature. An isothermal increase in magnetic field leads to an increase in electrical resistance at temperatures near but above Tc, which is a consequence of the field-induced metamagnetic transition from a paramagnetic state to a ferromagnetic state.     

Effect of Cu doping on the magnetic and electrical properties of n=2 Ruddlesden-Popper manganates

A series of polycrystalline Cu-doped n=2 Ruddlesden-Popper manganates La1.2Sr1.8CuzMn（2-x）O7 （x=0, 0.04, 0.13） were synthesized by the solid state reaction method. The effect of Cu doping on the magnetic and transport properties has been studied. It is found that Cu substitution for Mn greatly affects the magnetic and electrical properties of the parent phase La1.2Sr1.8Mn2O7. With the increase of Cu content, the system undergoes a transition from longrange ferromagnetic order to the spin glass state and further to an antiferromagnetic order. A little of Cu dopant can lead to the samples showing semiconductor or insulator behaviour in the whole observed temperature range while the parent phase has a metal-insulator transition. These samples show colossal magnetoresistance at low temperatures and the value of it decreases with increasing Cu content.     

STRUCTURE, MAGNETIC PROPERTIES AND GIANT MAGNETORESISTANCE OF YMn6Sn6-xGax (x=0-0.6) COMPOUNDS

Structure, magnetic and transport properties of YMn₆Sn_6-xGa_x (0≤x≤0.6) compounds with a HfFe₆Ge₆-type structure were investigated. It was found that the Ga substitution leads to a contraction of the unit-cell volume. A transition from an antiferromagnetic to a ferromagnetic (or ferrimagnetic) state can be observed for samples (0.1≤x≤0.2) with increasing temperature. The antiferro-ferromagnetic transition for samples with x≤0.2 can also be induced by an external field. The required field is very low, and decreases with increasing Ga concentration. More Ga concentration (x≥0.3) leads to the samples being ferromagnetic in the whole temperature range below the Curie temperature. The Ga substitution weakens the interlayer magnetic coupling between the Mn spins. Corresponding to the metamagnetic transition, a magnetoresistance as large as 32% under a field of 5 T was observed at 5 K for the sample with x=0.2.     

Influences of P doping on magnetic phase transition and structure in MnCoSi ribbon

The structure and magnetic properties of Mn Co Si1-xPx(x = 0.05–0.50) are systematically investigated.With P content increasing,the lattice parameter a increases monotonically while both b and c decrease.At the same time,the temperature of metamagnetic transition from a low-temperature non-collinear ferromagnetic state to a high-temperature ferromagnetic state decreases and a new magnetic transition from a higher-magnetization ferromagnetic state to a lowermagnetization ferromagnetic state is observed in each of these compounds for the first time.This is explained by the changes of crystal structure and distance between Mn and Si atoms with the increase of temperature according to the hightemperature XRD result.The metamagnetic transition is found to be a second-order magnetic transition accompanied by a low inversed magnetocaloric effect(1.0 J·kg-1·K-1at 5 T) with a large temperature span(190 K at 5 T) compared with the scenario of Mn Co Si.The changes in the order of metamagnetic transition and structure make P-doped Mo Co Si compounds good candidates for the study of magnetoelastic coupling and the modulation of magnetic phase transition.     

Magnetism and magnetoresistance of Er1-xSmxMn6Ge6(x=0.2－1.0) compounds

Magnetic and transport properties of Er_{1-x}Sm_xMn_6Ge_6(x=0.2-1.0) have been investigated by x-ray diffraction (XRD) and magnetization measurement. Analysis of the XRD patterns indicates that the samples with x≤0.4 mainly consist of HfFe_6Ge_6-type phase and the samples with 0.6≤x≤1.0 mainly consist of YCo_6Ge_6-type phase (P6/mmm). The lattice constants and the unit cell volume increase with increasing Sm content. The antiferro－ferri－ferromagnetic transitions can be observed with increasing Sm content. The samples with x=0.2 and 0.4 order antiferromagnetically at 420 and 425K, respectively. The samples with x=0.6, 0.8 and 1.0 order from ferri- to ferromagnetically over the whole magnetic ordering temperature range. The corresponding Curie temperatures are 435, 441 and 446K, respectively. The magnetoresistance (MR) isotherms of the sample with x=0.8, measured at various temperatures, are analysed. The magnitude of MR is found to be positive below 55K and gradually increases to a relatively large value of about 5.02% at 5K in a field of 5T as the temperature is lowered. A possible explanation for the positive MR is given.     

Coexistence of positive and negative magnetic entropy changes in CeMn_2(Si_(1-x)Ge_x)_2 compounds

A series of CeMn2(Si1-xGex)2(x = 0.2, 0.4, 0.6, 0.8) compounds are prepared by the arc-melting method. All the samples primarily crystallize in the Th Cr2Si2-type structure. The temperature dependences of zero-field-cooled(ZFC) and FC magnetization measurements show a transition from antiferromagnetic(AFM) state to ferromagnetic(FM) state at room temperature with the increase of the Ge concentration. For x = 0.4, the sample exhibits two kinds of phase transitions with increasing temperature: from AFM to FM and from FM to paramagnetic(PM) at around TN~197 K and T C~300 K,respectively. The corresponding Arrott curves indicate that the AFM–FM transition is of first-order character and the FM–PM transition is of second-order character. Meanwhile, the coexistence of positive and negative magnetic entropy changes can be observed, which are corresponding to the AFM–FM and FM–PM transitions, respectively.     

Magnetic properties of Nd0.5Pb0.5—xSrxMnO3 materials

The structure and magnetic properties of Nd_{0.5}Pb_{0.5-x}Sr_xMnO_3 (0≤x≤0.4) manganites were systematically investigated. Significant changes in Curie temperature and metal-insulator (MI) transition temperature of the samples were observed. All samples exhibited a transition from paramagnetic semiconducting to ferromagnetic metallic state. Curie temperature T_C and the MI transition temperature T_p increased with increasing Sr content. We attributed these behaviours to the enhancing of both the double exchange mechanism and the Jahn－Teller electron－phonon coupling.     

Magnetic properties of Nd0.5Pb0.5-xSrxMnO3 materials

The structure and magnetic properties of Nd0.5Pb0.5-xSrxMnO3 (0≤x≤0.4) manganites were systematically investigated. Significant changes in Curie temperature and metal-insulator (MI) transition temperature of the samples were observed. All samples exhibited a transition from paramagnetic semiconducting to ferromagnetic metallic state.Curie temperature Tc and the MI transition temperature Tp increased with increasing Sr content. We attributed these behaviours to the enhancing of both the double exchange mechanism and the Jahn-Teller electron-phonon coupling.     

Change in the magnetic ground state of LaFe11.4Al1.6 compound by the substitution of Mn for Fe

The structure and magnetic properties of La(Fe_{1-x}Mn_x)_{11.4}Al_{1.6} (0≤x≤0.25)compounds have been studied. The NaZn_{13}-type structure is preserved and the lattice parameter increases linearly with increasing the Mn concentration. The magnetic ground state changes from the antiferromagnetic to the spin-glass or the cluster-glass state by the substitution of Mn for Fe. Furthermore, a field-induced transition from cluster glass to ferromagnet is found for the samples with x=0.05 and 0.10.     

Effects of the Mn/Co ratio on the magnetic transition and magnetocaloric properties of Mn1+xCo1-xGe alloys

We have investigated the magnetic transition and magnetocaloric effects of Mn 1+x Co 1 x Ge alloys by tuning the ratio of Mn/Co.With increasing Mn content,a series of first-order magnetostructural transitions from ferromagnetic to paramagnetic states with large changes of magnetization are observed at room temperature.Further increasing the content of Mn (x=0.11) gives rise to a single second-order magnetic transition.Interestingly,large low-field magnetic entropy changes with almost zero magnetic hysteresis are observed in these alloys.The effects of Mn/Co ratio on magnetic transition and magnetocaloric effects are discussed in this paper.     

Crystal structure and magnetic properties of Nd（Mn1-xFex）2Si2 compounds

X-ray powder diffraction,resistivity and magnetization studies have been performed on polycrystalline Nd(FexMn1-x)2Si2 (0 ≤ x ≤ 1) compounds which crystallize in a ThCr2Si2-type structure with the space group I4/mmm.The field-cooled temperature dependence of the magnetization curves shows that,at low temperatures,NdFe2Si2 is antiferromagnetic,while the other compounds show ferromagnetic behaviour.The substitution of Fe for Mn leads to a decrease in lattice parameters a,c and unit-cell volume V .The Curie temperature of the compounds first increases,reaches a maximum around x = 0.7,then decreases with Fe content.However,the saturation magnetization decreases monotonically with increasing Fe content.This Fe concentration dependent magnetization of Nd(FexMn1-x)2Si2 compounds can be well explained by taking into account the complex effect on magnetic properties due to the substitution of Mn by Fe.The temperature’s square dependence on electrical resistivity indicates that the curve of Nd(Fe0.6Mn0.4)2Si2 has a quasi-linear character above its Curie temperature,which is typical of simple metals.     

Phase separation and abnormal transport behaviours in La0.7-xGdxSr0.3MnO3 system

The magnetic and transport behaviours of the La_{0.7-x}Gd_xSr_{0.3}MnO_3 (0≤x≤0.70) system are investigated. The experimental results indicate that with increasing Gd doping content, the magnetism of the system changes from the long-range ferromagnetic order state to the cluster-spin glass state, then to the antiferromagnetic (AFM) state. It is interesting that the phase separation appears at x=0.30 and 0.40 and disappears for x≥0.50 where the AFM state occurs. At high doping content, the transport behaviours exhibit abnormality, e.g. there are two temperature ranges in which the ρ－T curves can be well fitted by a variable-range hopping (VRH) model. We suggest that the VRH does not come from the hopping of carriers between clusters, but from the different magnetic backgrounds in the clusters.     

First-principle investigation on perovskite La_(1-x)Eu_xGaO_3

The pseudopotential method has been used to investigate the structural, electronic and magnetic properties of La_(1-x)Eu_xGaO_3(x = 0, 0.25, 0.5, 0.75, and 1) within the scheme of generalized gradient approximation. The spin-polarized calculations demonstrate that the ground state is an antiferromagnetic insulator for x ≤ 0.5, while it is ferromagnetic halfmetal at x 0.5. The substitutions of magnetic Eu ions for non-magnetic La ions produce and strength spin polarization,which forcefully urges the system from the insulator to the half metal. Meanwhile, Eu doping strengthens a stoner mechanism for ferromagnetism of La_(1-x)Eu_xGaO_3(x = 0.75 and 1), which may lead to a rapid increasing in the total magnetic moment and therefore, antiferromagnetic–ferromagnetic transition happens.     

Pressure induced magnetic and semiconductor–metal phase transitions in Cr_2MoO_6

We investigate magnetic ordering and electronic structures of Cr_2MoO_6under hydrostatic pressure. To overcome the band gap problem, the modified Becke and Johnson exchange potential is used to investigate the electronic structures of Cr_2MoO_6. The insulating nature at the experimental crystal structure is produced, with a band gap of 1.04 eV, and the magnetic moment of the Cr atom is 2.50 μB, compared to an experimental value of about 2.47 μB. The calculated results show that an antiferromagnetic inter-bilayer coupling–ferromagnetic intra-bilayer coupling to a ferromagnetic inter-bilayer coupling–antiferromagnetic intra-bilayer coupling phase transition is produced with the pressure increasing. The magnetic phase transition is simultaneously accompanied by a semiconductor–metal phase transition. The magnetic phase transition can be explained by the Mo–O hybridization strength, and ferromagnetic coupling between two Cr atoms can be understood by empty Mo-d bands perturbing the nearest O-p orbital.     

Large magnetoresistance in metamagnetic CoMnSi0.88Ge0.12 alloy

The magneto-transport properties are investigated in metamagnetic CoMnSi0.88Ge0.12 alloy.By applying a magnetic field or increasing temperature,a metamagnetic phase transition from antiferromagnetic to ferromagnetic is observed in this alloy.Around the metamagnetic phase transition,CoMnSi0.88Ge0.12 alloy exhibits a large and negative magnetoresistance effect(～32%) under a magnetic field of 20 kOe(1 Oe = 79.5775 A/m),which is ascribed to the spin-dependent scattering of conduction electrons.