PVA-g-PS复合微球的制备与粒径控制研究

由链转移自由基聚合与端基置换反应法,合成了苯乙稀基单封端的聚醋酸乙烯酯(PVAc)大分子单体,使其与苯乙烯在乙醇/水的混合介质中进行自由基分散共聚,得到了表面以PVAc为接枝链的聚苯乙烯(PVAc-g-PSt)微球。将所得微球在碱性条件下醇解,形成了以亲水性聚乙烯醇(PVA)为壳、聚苯乙烯为核的复合微球(PVAc-g-PSt)。用核磁共振对聚合物的结构进行表征,定出了PVAc末端双键的含量;并用激光光散射、扫描电子显微镜对微球的粒径与形态进行了表征。研究结果表明,在共聚反应体系中大分子单体的分子量与浓度、苯乙烯浓度、引发剂浓度及溶剂的组成对微球的形态和粒径大小有明显影响。     

无规-类接枝共聚物自组装制备交联纳米微球

无规-类接枝共聚物(SFG)由大分子单体-己内酯改性丙烯酸酯(FA)、亲油性单体苯乙烯和甲基丙烯酸缩水甘油酯(GMA)共聚所得，SFG与聚苯乙烯在甲醇溶液中进行自组装，形成核壳结构纳米胶束，进一步对PGMA壳进行化学交联。最终得到具有核壳结构的纳米微球。动态激光光散射和透射电子显微镜表征结果显示SFG自组装形成了窄分布的纳米微球，微球粒径在100～200nm之间。     

结合表面引发的原子转移自由基聚合和气/固反应制备CdS纳米微粒/聚苯乙烯核壳微球

结合表面引发的原子转移自由基聚合和气/固反应制备CdS纳米微粒/聚苯乙烯核壳微球. 以表面富含环氧基团的聚苯乙烯微球为基底, 利用开环反应在水相中一步接枝表面引发剂, 然后在聚苯乙烯微球表面引发甲基丙烯酸镉的原子转移自由基聚合, 最后通入H2S气体原位生成CdS纳米微粒. 生成的CdS纳米微粒复合的核壳微球呈草莓状形貌, 且具有良好的光学性能.     

原位聚合法制备具有温敏PNIPAM壳的核-壳结构聚合物纳米微球的研究

结合大分子自组装和原位自由基聚合方法,采用油溶性引发剂偶氮二异丁腈(AIBN),在聚(ε-已内酯)(PCL)纳米粒子表面引发聚合单体N-异丙基丙烯酰胺(NIPAM)和交联剂亚甲基双(丙烯酰胺)(MBA),制备得到了核-壳结构的PCL/PNIPAM聚合物纳米微球.系统研究了单体和交联剂用量、壳层目标交联度、初始PCL/DMF溶液的浓度及引发剂AIBN含量4个反应参数对核-壳结构PCL/PNIPAM纳米微球的PNIPAM壳层得率、微球尺寸、温敏性能及电镜形貌的影响.结果表明,在制备核-壳结构PCL/PNIPAM纳米微球的反应过程中,PCL粒子表面的聚合和水中的聚合二者之间相互竞争.适当增加引发剂AIBN的添加量,有利于制备得到核/壳比例可控的PCL/PNIPAM纳米微球;交联剂MBA较高的反应活性导致形成了非均匀交联的PNIPAM壳层.     

纳米氧化硅表面阴离子接枝聚合苯乙烯

通过正丁基锂(BL)引发甲基丙烯酰氧丙基纳米氧化硅(MAMSN)与苯乙烯共聚,制备了聚苯乙烯表面接枝纳米氧化硅(PS—g—Silica),并考察了正丁基锂加入量对苯乙烯转化率(C)、接枝率(PG)以及聚苯乙烯分子量(Mn)的影响。实验结果表明,阴离子聚合可以获得比自由基聚合更大的分子量和更高的转化率以及接枝率。     

制备方法对模板法制备SiO_2中空微球形貌的影响

模板法是制备无机中空微球的重要方法之一.首先通过苯乙烯和甲基丙烯酸的无皂乳液聚合法制得表面含羧基、粒径为360nm的单分散聚苯乙烯(PSt)乳胶粒,并以此为模板,分别采用表面改性-前驱体水解法(PHC)和SiO2纳米颗粒层层自组装法(LBL),制备出了不同壳层厚度的PSt/SiO2核壳结构复合微球,然后经500℃煅烧4h,得到SiO2中空微球.利用透射电镜和扫描电镜对微球结构形态进行了表征.研究表明,首先利用γ-氨丙基三乙氧基硅烷(KH-550)对PSt模板微球进行表面改性、然后再在乙醇-水混合介质中进行原硅酸乙酯(TEOS)水解与缩合反应的PHC法,是制备PSt/SiO2核壳结构复合微球的简便方法,复合微球经煅烧可制得表面均匀、结构致密、壳层厚度和形貌可控的SiO2中空微球;而LBL法制备PSt/SiO2核壳结构复合微球的工艺复杂,煅烧后所得SiO2中空微球结构疏松,易于破碎.     

Pickering乳液聚合制备核-壳结构PS-SiO2复合微球

用二氯二甲基硅烷对纳米SiO2粒子进行疏水改性,当其表面Zeta电位由-54.8 mV变成-25.8 mV时,SiO2粒子就能在苯乙烯-水界面自组装,形成稳定的Pickering乳液,即以胶体粒子为乳化剂的乳液.利用Pickering乳液聚合制备了以聚苯乙烯(PS)为核、纳米SiO2为壳的PS-SiO2复合微球.用FT-IR、XPS、SEM、偏光显微镜等对复合微球进行了表征.结果表明:复合微球由聚苯乙烯和纳米二氧化硅粒子组成,二氧化硅粒子以单层、六方密排的方式分布在聚苯乙烯微球表面.     

Fe3O4表面原位引发可控/“活性”聚合制备磁性聚苯乙烯纳米粒子

采用化学共沉淀方法合成了Fe3O4纳米粒子, 用3-甲基丙烯酰氧基丙基三甲氧基硅烷(3-MPS)对其进行表面接枝修饰, 然后以苯乙烯(St)为单体, 过氧化苯甲酰(BPO)为引发剂, 4-羟基-2,2,6,6-四甲基哌啶-1-氧化物自由基(HTEMPO·)为稳定自由基介质, 采用可控/“活性”自由基聚合技术在修饰后的Fe3O4纳米粒子表面原位引发聚合, 制备了粒径小、分布窄、磁含量高的磁性聚苯乙烯（PS）纳米粒子. X射线衍射(XRD)研究表明, 所合成的Fe3O4粒子为尖晶石结构. 凝胶渗透色谱(GPC)分析表明, 聚苯乙烯的分子量与反应时间呈较好的线性关系. 透射电镜(TEM)观察表明, 所制备的磁性聚苯乙烯纳米粒子的粒径在20-30 nm之间. 热重(TG)分析得到磁性聚苯乙烯纳米粒子的磁含量为62.6%. 振动样品磁强计(VSM)测试结果表明, 磁性聚苯乙烯纳米粒子的比饱和磁化强度为31.7 emu·g-1, 呈现单磁畴结构.     

纳米Fe3O4/聚苯乙烯均匀分散体系的制备及结构

用化学共沉淀法制备了Fe3O4纳米颗粒,以油酸为表面活性剂,苯乙烯为载液,制备了稳定的纳米Fe3O4可聚合磁流体,将可聚合磁流体经自由基引发聚合制成纳米Fe3O4/聚苯乙烯均匀分散体系,用WAXRD研究了Fe3O4纳米粒子的结晶情况;用FTIR研究了油酸表面改性前后Fe3O4粒子表面官能团的变化;用TEM研究了Fe3O4颗粒的粒径大小及其在苯乙烯单体和聚苯乙烯中的分散情况;用DSC和TGA研究了纳米Fe3O4/聚苯乙烯均匀分散体系的玻璃化转变温度(Tg)和热稳定性,结果表明,合成的纳米Fe3O4为立方晶型,平均粒径在10nm左右,油酸分子在Fe3O4表面是化学吸附,经表面处理的Fe3O4超细颗粒在苯乙烯和聚苯乙烯基体中分散较均匀.界面粘结较好,含1.8％Fe3O4纳米颗粒的聚苯乙烯的最大热失重温度比聚苯乙烯提高了13K,Fe3O4/聚苯乙烯复合体系的饱和磁化强度σs为17.43emu/g.     

分散聚合法制备单分散聚苯乙烯微球

以苯乙烯为单体,偶氮二异丁腈为引发剂,聚乙烯吡咯烷酮为分散稳定剂,在乙醇/水的极性反应体系中,使用分散聚合法制备了聚苯乙烯(PS)微球。研究了制备工艺对微球分子量等远程结构参数的影响。研究结果表明:在适合微球形成的单体用量、引发剂和分散稳定剂的浓度、反应温度、时间和乙醇/水的比例等参数下,克服了以往存在的粒径不均匀、分子量较低、微球表面圆整光洁度较低和产率偏低等主要问题,制备了粒径在1.5~3μm之间、粒径分布1.05~1.08、分子量80×104左右、最高得率达97%、球体表面光洁、球形对称均匀且相互不粘连的单分散PS微球。     

Graft copolymers having hydrophobic backbone and hydrophilic branches. XXIII. Particle size control of poly(ethylene glycol)-coated polystyrene nanoparticles prepared by macromonomer method

Monodisperse polymeric nanospheres, which consist of polystyrene cores and poly(ethylene glycol) (PEG) branches on their surfaces, were prepared by the dispersion copolymerization of styrene (St) with PEG macromonomers that had a methacryloyl (MMA-PEG) or p-vinylbenzyl (St-PEG) end group in various organic solvent/water media. Electron spectroscopy for chemical analysis (ESCA) of the nanosphere surfaces indicated that PEG macromonomer chains were favorably located on their surfaces. The morphologies of the nanospheres were observed via a scanning electron micrograph (SEM), and particle sizes were estimated by a submicron particle analyzer. When both the concentration of macromonomers and molecular weight were higher, small nanospheres in diameter were obtained. Larger nanospheres in diameter were obtained using macromonomers with low molecular weight at lower concentration. The functions that correlate the diameter (D_n) on different concentration units were D_n = K[St]^0.64[MMA-PEG]^{−0.53±0.01}[I]^−0.49 and D_n = K[St]^0.80[St-PEG]^{−0.69±0.01}[I]^−0.22, where [I], [St], [MMA-PEG], and [St-PEG] are initiator, styrene, MMA-PEG, and St-PEG macromonomer concentration in feed, respectively. When the reaction parameters such as the molecular weight of the macromonomers were properly chosen, the particle size could be controlled in a range from ca. 80 to 3100 nm. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 2155–2166, 1999     

ARGET ATRP 与ROP 结合制备pH 响应两亲性聚合物分子刷及其自组装研究

结合电子转移活化剂再生-原子转移自由基聚合(ARGET ATRP)和开环聚合(ROP)法合成了一种具有无规疏水/ pH 响应结构的两亲性聚合物分子刷聚(甲基丙烯酸聚丙交酯酯-co-甲基丙烯酸)-b-聚甲基丙烯酸单甲氧基聚乙二醇酯 [P(PLAMA-co-MAA)-b-PPEGMA]. 通过核磁共振氢谱(¹H NMR)和凝胶渗透色谱(GPC)表征了聚合物的结构、分子量及分子量分布. 优化了反应条件并合成出分子量可控、分子量分布窄的聚合产物. 采用动态光散射法(DLS)、扫描电子显微镜(SEM)研究了聚合物分子刷在水溶液中自组装胶束的粒径、形貌及pH 响应行为. P(PLAMA-co-MAA)-b-PPEGMA 自组装形成粒径分布均匀的球形胶束. 且随着溶液pH 值从7 降低至3, 胶束中的PMAA 逐渐去离子化, 溶胀的胶束逐渐收缩, 粒径由200～300 nm 减小至150 nm 左右; 但当pH 值减小到2 以下, 胶束表面电荷量非常小, 胶束聚集, 使得粒径增大.     

PSt种子与“花瓣”形PSt/PAN复合颗粒的制备

以过硫酸钾为引发剂,在乙醇/水的混合介质中使苯乙烯进行无皂乳液聚合,得到了单分散亚微米级聚苯乙烯(PSt)微球.用扫描电子显微镜研究了引发剂浓度、单体浓度、反应温度和溶剂组成对PSt微球粒径的影响.结果表明,改变上述条件能明显影响其粒径.以所得单分散聚苯乙烯微球为种子,在丙烯酸单封端聚乙二醇大分子单体存在的条件下,使丙烯腈和少量苯乙烯进行新的无皂种子乳液聚合,在合适的条件下制得到了“花瓣”形的聚合物复合颗粒,为深入探讨这类特殊形态聚合物颗粒的形成机理提供了新的佐证.     

Polymerizable Molecular Silsesquioxane Cage Armored Hybrid Microcapsules with In Situ Shell Functionalization

We prepared core–shell polymer–silsesquioxane hybrid microcapsules from cage‐like methacryloxypropyl silsesquioxanes (CMSQs) and styrene (St). The presence of CMSQ can moderately reduce the interfacial tension between St and water and help to emulsify the monomer prior to polymerization. Dynamic light scattering (DLS) and TEM analysis demonstrated that uniform core–shell latex particles were achieved. The polymer latex particles were subsequently transformed into well‐defined hollow nanospheres by removing the polystyrene (PS) core with 1:1 ethanol/cyclohexane. High‐resolution TEM and nitrogen adsorption–desorption analysis showed that the final nanospheres possessed hollow cavities and had porous shells; the pore size was approximately 2–3 nm. The nanospheres exhibited large surface areas (up to 486 m² g^?1) and preferential adsorption, and they demonstrated the highest reported methylene blue adsorption capacity (95.1 mg g^?1). Moreover, the uniform distribution of the methacryloyl moiety on the hollow nanospheres endowed them with more potential properties. These results could provide a new benchmark for preparing hollow microspheres by a facile one‐step template‐free method for various applications.     

Production of micron-sized polystyrene particles containing PEG near the particles surface

Polystyrene (PS) particles in the size range of 1-7 µm, containing poly(ethylene glycol) or PEG on the particles surface, were prepared by multi-step seeded polymerizations. Micron-sized PS particles were first prepared by dispersion polymerization using 2,2'-azobisisobutyronitrile as initiator and polyvinyl pyrrolidone as stabilizer. Conventional swelling method was then used to increase the size of the PS particles with a large amount of styrene in presence of oil soluble initiator, benzoyl peroxide. In the final step, the PS particles have been used to carry out seeded polymerization with small amount of styrene in presence of poly(ethylene glycol)-azo or PEGA initiator with average molecular weights of the PEG chains of 200 and 3000 g mol^-1 , respectively. The average size, size distribution, and surface morphology indicate that seeded polymerization in the final step with small amount of styrene in presence of PEGA is the best way to produce monodisperse polystyrene particles containing PEG near the particles surface.     

原子转移自由基聚合制备聚(丙二醇-g-苯乙烯)

以氯甲基化苯氧基聚丙二醇 (CMPOPPG)为大分子引发剂 ,由CuCl/bpy催化的苯乙烯原子转移自由基聚合反应合成了聚 (丙二醇 g 苯乙烯 ) .CMPOPPG经环氧丙烷 (PO)与缩水甘油苯基醚 (GPE)的开环聚合和氯甲基化反应制得 .接枝聚合反应具有可控性 .用1H NMR和微库仑分析法对接枝共聚物进行了表征 .结果表明 ,支链分子量可控 ,接枝率可达 8.6.     

Block copolymers prepared by emulsion polymerization with poly(ethylene oxide)–azo-initiators

Poly(ethylene oxide)-b-poly(styrene) block copolymers were prepared in the form of latex particles by emulsion polymerization of styrene with poly(ethylene glycol)–azo-initiators as well as with the redox initiation system poly(ethylene glycol)/Ce⁴⁺. The emulsion polymerization can be carried out in the absence of additional stabilizers if the chain length of the poly(ethylene glycol) is greater than 40. The latex particles as well as the copolymers were characterized by capillary hydrodynamic fractionation, ¹³C-nuclear magnetic resonance (NMR) spectroscopy and Fourier transform infrared spectroscopy. By ¹³C-NMR spectroscopy a side reaction of the primary radicals arising from the azo-initiator was found which can contribute to the low efficiency of azo-initiators in emulsion polymerization.     

Brush macro‐RAFT agent mediated dispersion polymerization of styrene in the alcohol/water mixture

Dispersion RAFT polymerization of styrene in the alcohol/water mixture mediated with the brush macro‐RAFT agent of poly[poly(ethylene oxide) methyl ether vinylphenyl‐co‐styrene] trithiocarbonate [P(mPEGV‐co‐St)‐TTC] with similar molecular weight but different chemical composition is investigated. Well‐controlled RAFT polymerization including an initial slow homogeneous polymerization and a subsequent fast heterogeneous polymerization at almost complete monomer conversion is achieved. The molecular weight of the synthesized block copolymer increases linearly with the monomer conversion, and the polydispersity is relatively narrow (PDI < 1.3). The RAFT polymerization kinetics is dependent on the chemical composition in the brush macro‐RAFT agents, and those with high content of hydrophobic segment lead to fast RAFT polymerization. The growth of the block copolymer nano‐objects during the RAFT polymerization is explored, and various block copolymer nano‐objects such as nanospheres, worms, vesicles and large‐compound‐micelle‐like particles are prepared. The parameters such as the chemical composition in the brush macro‐RAFT agent, the chain length of the solvatophobic block, the concentration of the feeding monomer and the solvent character affecting the size and morphology of the block copolymer nano‐objects are investigated. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013, 51, 3177–3190     

悬浮-乳液复合聚合聚苯乙烯-聚甲基丙烯酸甲酯复合粒子的颗粒特性和成粒机理

采用在苯乙烯 (St)悬浮聚合过程中滴加甲基丙烯酸甲酯 (MMA)乳液聚合组分的悬浮 乳液复合聚合方法 ,制备大粒径聚苯乙烯 聚甲基丙烯酸甲酯 (PS PMMA)复合粒子 .研究聚合物粒径分布和颗粒形态的变化发现 ,在St悬浮反应中期滴加MMA乳液聚合组分后 ,聚合体系逐渐由悬浮粒子与乳胶粒子并存向形成单峰分布复合粒子转变 ,最终形成核 壳结构完整的大粒径PS PMMA复合粒子 ;在St悬浮反应初期滴加MMA乳液聚合组分 ,St与MMA一起分散成更小液滴 ,反应后期凝并成非核 壳结构复合粒子 ;在St悬浮反应后期滴加MMA乳液聚合组分 ,PMMA乳胶粒子与PS悬浮粒子基本独立存在 .根据以上结果 ,提出了St MMA悬浮 乳液复合聚合的成粒机理 .     

Surface properties of styrene–ethylene oxide block copolymers

Hydrophobic–hydrophilic block copolymers were prepared by “living” anionic polymerization. They consist of polystyrene and poly(ethylene oxide) blocks, and are soluble in water. Their interfacial properties were investigated, employing aqueous solutions. The block copolymers lowered the surface tension of water in analogy with the low molecular weight surfactants such as sodium lauryl sulfate and heptaethylene oxide n-dodecyl ether. Their aqueous solutions exhibited solubilization properties differing from those of polyethylene glycol. Therefore, it is thought that the polystyrene blocks produce solubilization phenomena. In samples of the same styrene content, the precipitation temperature of a high molecular weight copolymer in water was lower than that of a low molecular weight copolymer at the same concentration in the same solvent. The surface tension and precipitation temperature of aqueous solutions seem to be influenced by molecular weight and composition.