1.
Cr 助剂对 Fe 基催化剂结构和费托合成性能的影响 总被引:1,自引:0,他引:1
采用 N2 吸附-脱附、X 射线衍射、穆斯堡尔谱、X 射线光电子能谱、程序升温还原和热重分析等技术研究了助剂 Cr 含量对 Fe 基费托合成催化剂的织构性质、还原行为以及物相变化的影响. 在 H2/CO = 2.0, 260~300 oC, 1.5 MPa 和 2 000 ml/(g•h) 条件下, 在固定床反应器中考察了 Cr 含量对 Fe 基催化剂费托合成反应活性和产物烃选择性的影响. 结果表明, 在氧化态催化剂中, Cr 助剂与 Fe 物相存在较强的相互作用, 形成固溶体相 α-(Cr1-xFex)2O3; 随着 Cr 含量的增加, 逐渐由单一的富 Fe 相 α-(Fe1-xCrx)2O3 向富 Fe 相和富 Cr 相 α-(Cr1-yFey)2O3 两相过渡. Fe-Cr 固溶体的生成显著抑制了催化剂的还原, 导致催化剂还原度降低, 因而催化剂活性下降. 同时, Cr 的添加提高了甲烷和轻质烃选择性, 但抑制了水煤气变换活性. 相似文献
2.
3.
采用连续共沉淀和喷雾干燥相结合的方法制备了微球形 Fe 基催化剂, 采用 N2 吸附-脱附、X 射线衍射和穆斯堡尔谱等手段, 考察了催化剂在不同还原条件下铁物相的转变, 并在浆态床反应器中评价了催化剂的费-托合成 (FTS) 反应性能. 结果表明, Fe 基催化剂在合成气气氛下首先从α-Fe2O3 转变为 Fe3O4, 然后转变为铁碳化物 (FexC); 还原压力的增大有利于 α-Fe2O3 向 Fe3O4 的转变, 而抑制 Fe3O4 向 FexC 的转变; 还原空速的增加则促进 Fe3O4 转变为 FexC. 催化剂的 FTS 反应活性随着催化剂中 Fe3O4 含量的增加而逐渐下降, 而随着 FexC 含量的增加而逐渐上升. 相似文献
4.
Zn助剂对铁基催化剂费托合成制低碳烯烃性能的影响 总被引:3,自引:0,他引:3
低碳烯烃(C2=–C4=)是十分重要的基础化工原料,目前主要采用热裂解或催化裂解石脑油、蜡油等工艺路线生产。近年来,针对全球范围的石油危机及我国富煤贫油这一基本的国情,以煤、天然气(页岩气)和生物质等丰厚的碳资源,经合成气制取低碳烯烃的工艺路线备受关注。其中,合成气经由甲醇或二甲醚间接制取烯烃技术(MTO/MTP)已经工业化;与之相比,费托合成直接生产低碳烯烃(FTO)工艺流程短、投资和操作费用低,具有良好的工业发展前景。目前,费托合成催化剂活性组分的研究主要集中于Fe, Co, Ni和Ru等元素,其中Fe基催化剂具有较高低碳烯烃选择性、较低甲烷选择性和制造廉价等优势,更适合于FTO反应。最近,人们大多聚焦于对负载型铁基催化剂的研究,但传统非负载型铁催化剂由于其制备简单、价格低廉,仍然具有巨大的开发前景。近来,我们组报道了采用微波水热法制备的Zr助剂改性Fe-Zr催化剂应用于CO加氢研究,提高了催化剂的活性,与传统Mn改性铁基催化剂相比, CO2选择性明显降低。目前,已有研究小组对Zn助剂提高铁基催化剂烯烃选择性进行报道,但反应过程中的严重积碳问题却少有研究。我们在Fe-Zr催化剂的基础上,进一步研究了Zn助剂在提高铁基催化剂低碳烯烃选择性、改善产物分布和降低反应过程积碳方面的作用。
我们分别采用微波水热法和浸渍法对铁基催化剂进行了Zn改性,并将其用于费托合成制取低碳烯烃反应。运用扫描电镜(SEM)、X射线衍射(XRD)、N2物理吸附(BET)、H2程序升温还原(H2-TPR)和X射线光电子能谱(XPS)技术手段对催化剂的物理和化学性质进行了表征。结果表明,两种方法改性后的铁基催化剂具有高低碳烯烃选择性和稳定性,重质烃(C5+)含量降低,且保持低CO2选择性。此外,采用两种方法Zn改性的铁基催化剂展现出了不同的特性。 XRD结果表明,反应前两种方法制备的样品α-Fe2O3物相晶粒大小均为15–18 nm,反应后浸渍法制备的样品对应物相(ZnFe2O4)晶粒大小约为25 nm、而微波水热法制备的样品约为20 nm,说明微波水热法改性的催化剂有效分散了Fe活性组分; H2-TPR结果显示,两种Zn助剂加入方法对催化剂Fe组分的还原行为有不同程度影响,体现了活性组分间不同的相互作用; XPS结果表明, Zn助剂改变了催化剂Fe活性位的化学性质,在微波水热法制得催化剂的表面Zn含量更低、分散度更高,而Zn助剂的加入对Zr组分没有明显影响。所有催化剂经200 h在线活性测试后,采用传统浸渍法制备的催化剂表面有大量积碳生成;而采用微波水热改性铁基催化剂积碳量明显减少,表现出更高的催化活性与稳定性。 相似文献
我们分别采用微波水热法和浸渍法对铁基催化剂进行了Zn改性,并将其用于费托合成制取低碳烯烃反应。运用扫描电镜(SEM)、X射线衍射(XRD)、N2物理吸附(BET)、H2程序升温还原(H2-TPR)和X射线光电子能谱(XPS)技术手段对催化剂的物理和化学性质进行了表征。结果表明,两种方法改性后的铁基催化剂具有高低碳烯烃选择性和稳定性,重质烃(C5+)含量降低,且保持低CO2选择性。此外,采用两种方法Zn改性的铁基催化剂展现出了不同的特性。 XRD结果表明,反应前两种方法制备的样品α-Fe2O3物相晶粒大小均为15–18 nm,反应后浸渍法制备的样品对应物相(ZnFe2O4)晶粒大小约为25 nm、而微波水热法制备的样品约为20 nm,说明微波水热法改性的催化剂有效分散了Fe活性组分; H2-TPR结果显示,两种Zn助剂加入方法对催化剂Fe组分的还原行为有不同程度影响,体现了活性组分间不同的相互作用; XPS结果表明, Zn助剂改变了催化剂Fe活性位的化学性质,在微波水热法制得催化剂的表面Zn含量更低、分散度更高,而Zn助剂的加入对Zr组分没有明显影响。所有催化剂经200 h在线活性测试后,采用传统浸渍法制备的催化剂表面有大量积碳生成;而采用微波水热改性铁基催化剂积碳量明显减少,表现出更高的催化活性与稳定性。 相似文献
5.
以FeCuK/SiO2为母体催化剂,用不同浓度的NH4HSO4水溶液进行等体积浸渍,制备了不同SO2-4含量的费托合成(FTS)铁基催化剂.采用原子发射光谱、低温N2吸附、 X射线光电子能谱、程序升温还原和穆斯堡尔谱等技术对催化剂进行了表征,并在H2/CO摩尔比0.67,WHSV=2 000 h-1,压力1.5 MPa和温度250 ℃条件下进行了浆态床FTS反应.结果表明,少量SO2-4能促进催化剂在H2中的还原;在合成气还原过程中,少量SO2-4对催化剂的碳化程度影响不大,但大量SO2-4严重抑制催化剂的碳化.在约500 h的运行实验中,各催化剂样品表现出的催化活性有所差异,但均呈现较好的稳定性.SO2-4可抑制水煤气变换反应活性,且随着SO2-4含量的增加,抑制作用愈加明显;同时,催化剂上浸渍少量SO2-4可有效抑制CH4的生成,提高低碳烯烃的选择性. 相似文献
6.
采用沉淀法和喷雾干燥技术制备了一个典型的费托合成铁基催化剂(100Fe/3K/6SiO_2,质量比)所得样品在不同温度下焙烧5 h.分别利用N_2吸附和穆斯保尔谱表征了催化剂的织构和物相性质,同时利用热重分析仪记录了催化剂在H2气氛中的还原过程,并利用气固反应模型对还原曲线进行了动力学模拟.结果表明,300~600℃焙烧后催化剂的还原过程可用相同的模型拟合,其中由α-Fe_2O_3还原为Fe_3O_4的过程可用一维晶相形成与生长模型或三维相界面反应模型描述,Fe_3O_4还原为α-Fe的过程受二维晶相形成与生长模型控制.而对于700℃焙烧后的催化剂,其还原过程可能受晶相形成与生长模型和收缩核模型共同影响.随着焙烧温度的提高,催化剂的还原能力减弱,还原过程活化能升高.这可能是由于焙烧温度的提高导致晶粒尺寸增大和晶格缺陷减少所致. 相似文献
7.
以FeCuK/SiO2为母体催化剂,用不同浓度的NH4HSO4水溶液进行等体积浸渍,制备了不同SO42-含量的费托合成(FTS)铁基催化剂.采用原子发射光谱、低温N2吸附、X射线光电子能谱、程序升温还原和穆斯堡尔谱等技术对催化剂进行了表征,并在H2/CO摩尔比0.67,WHSV=2 000 h-1,压力1.5 MPa和温度250℃条件下进行了浆态床FTS反应.结果表明,少量SO42-能促进催化剂在H2中的还原;在合成气还原过程中,少量SO42-对催化剂的碳化程度影响不大,但大量SO42-严重抑制催化剂的碳化.在约500 h的运行实验中,各催化剂样品表现出的催化活性有所差异,但均呈现较好的稳定性.SO42-可抑制水煤气变换反应活性,且随着SO42-含量的增加,抑制作用愈加明显;同时,催化剂上浸渍少量SO42-可有效抑制CH4的生成,提高低碳烯烃的选择性. 相似文献
8.
研究了 Mo 和 Cu 助剂对 FeK/SiO2 催化剂的性质及费托 (F-T) 合成性能的影响. 采用 N2 物理吸附、H2 程序升温还原、X 射线衍射、穆斯堡尔谱和 X 射线光电子能谱技术对催化剂进行了表征. 结果表明, Mo 加入后与 Fe 产生了较强的相互作用, 抑制了催化剂的还原和碳化; Cu 助剂的加入促进了催化剂的还原和碳化; 当 Mo 和 Cu 共同加入后, 催化剂的还原和碳化行为与单独加入 Cu 助剂时相似. 催化剂 F-T 合成性能在固定床上于 280 oC, 1.5 MPa, 2 000 h-1, H2/CO = 2.0 的合成气中测试. 结果表明, Mo 的加入降低了催化剂活性, 但提高了重质烃 (C5+) 的选择性; Cu 的添加提高了催化剂的活性, 但对稳定 C5+选择性作用不明显. Mo 和 Cu 共同加入后, 催化剂既表现出较为稳定的 C5+选择性, 同时其活性也没有降低. 相似文献
9.
Mn和Zr助剂对介孔碳负载钴基催化剂费托合成反应性能的影响 《燃料化学学报》2017,45(6):682-688
采用浸渍法制备了Mn和Zr改性的介孔碳负载钴基催化剂,采用X射线衍射(XRD)、比表面积测定、H2程序升温还原(H2-TPR)、H2/CO程序升温脱附(TPD)及X射线光电子能谱(XPS)等手段对催化剂的物化性质进行了表征,采用固定床反应器对其F-T反应性能进行了研究。结果表明,Mn或Zr助剂的添加均降低了CH4的选择性。其中,Mn助剂的添加提高了C2-4的选择性,提高了烯烷比,而Zr的添加提高了钴物种的分散度,增加了反应活性位点,显著提高了钴基催化剂的F-T反应活性和C5+选择性。 相似文献
10.
费托合成钴基催化剂的研究进展 总被引:1,自引:0,他引:1
费托合成油技术是煤炭、天然气等含碳资源清洁优化利用的重要途径, 其关键问题之一是催化剂选择性的调控, 即抑制甲烷生成和提高馏分油含量. 近 10 年来, 中国科学院山西煤炭化学研究所系统地开展了钴基费托合成催化剂及制备放大的工程基础研究, 包括钴分散度、还原度与甲烷生成之间的关系, 载体表面疏水性对催化剂性能的影响, 以及采用孔道限域等手段初步实现了产物的选择性调控. 同时, 初步阐明了甲烷生成的结构基础, 并指明了新型馏分油催化剂研发方向. 在此基础上, 研制了新型钴基催化剂, 其具有低甲烷选择性、高重质烃选择性和良好稳定性的特点. 目前, 对 I 型催化剂完成了实验室稳定性验证并实现了工业示范; 对 II 型催化剂 (甲烷选择性约 2%~3%) 完成了稳定性验证. 相似文献
11.
Novel cobalt Fischer-Tropsch synthesis(FTS) catalysts were prepared from natural halloysite nanotubes(HNT) by double-solvent and wetimpregnation methods,and characterized by TEM,XRD,TPR and N2 adsorption-desorption.Comparing with the catalyst prepared by wetimpregnation method,the catalyst prepared by double-solvent method reduces Co3O4 particle migration and agglomeration due to size-induced effect,thus showing higher catalytic activity for Fischer-Tropsch synthesis. 相似文献
12.
Ali Nakhaei Pour Mohammad Reza Housaindokht Sayyed Faramarz Tayyari Jamshid Zarkesh 《天然气化学杂志》2010,19(3):284-292
Effects of nanoscale iron oxide particles on textural structure, reduction, carburization and catalytic behavior of precipitated iron catalyst in Fischer-Tropsch synthesis (FTS) are investigated. Nanostructured iron catalysts were prepared by microemulsion method in two series. Firstly, Fe2O3, CuO and La2O3 nanoparticles were prepared separately and were mixed to attain Fe/Cu/La nanostructured catalyst (sep-nano catalyst); Secondly nanostructured catalyst was prepared by co-precipitation in a water-in-oil microemulsion method (mix-nano catalyst). Also, conventional iron catalyst was prepared with common co-precipitation method. Structural characterizations of the catalysts were performed by TEM, XRD, H2 and CO-TPR tests. Particle size of iron oxides for sep-nano and mix-nano catalysts, which were determined by XRD pattern (Scherrer equation) and TEM images was about 20 and 21.6 nm, respectively. Catalyst evaluation was conducted in a fixed-bed stainless steel reactor and compared with conventional iron catalyst. The results revealed that FTS reaction increased while WGS reaction and olefin/paraffin ratio decreased in nanostructured iron catalysts. 相似文献
13.
研究了还原温度对Fe-Mo催化剂性质及费托(F-T)合成性能的影响。采用N2物理吸附、X射线衍射、穆斯堡尔谱和H2程序升温脱附技术对催化剂进行了表征。结果表明,随还原温度升高,金属铁晶粒粒径增大,金属铁上的H2吸附量先升后降;催化剂还原度提高,反应态催化剂碳化铁含量递增。催化剂F-T合成性能在280 ℃、1.5 MPa、2 000 h-1、合成气H2/CO比为2.0条件下在固定床反应器中测试。反应结果表明,随还原温度提高,催化剂接近稳态时的活性和重质烃选择性(C5+)先升后降,而甲烷选择性则先降后升。350 ℃还原催化剂具有最佳F-T合成反应性能。 相似文献
14.
考察了不同还原气氛处理CoFe/SBA-15催化剂对F-T反应性能的影响。结果表明,H2气氛下有利于六方钴的生成;催化剂的活性取决于钴含量,随着钴含量的增加,F-T反应中CO转化率增加,C5+选择性增加。随着铁含量的增加,催化剂表现了较高的CO2选择性。CO还原有利于立方钴的生成,导致催化活性相比H2还原的催化剂活性要低。同时CO还原容易产生积炭使催化剂的钴活性位被覆盖,导致甲烷选择性随着钴含量增加而升高。但碳化铁的生成有利于提高20Fe/SBA-15催化剂的活性,有利于低碳烃生成及C2~4烃烯烷比增加。 相似文献
15.
高温沉淀铁基催化剂上费托合成含氧化合物生成机理的研究 总被引:1,自引:0,他引:1
采用漫反射原位红外光谱法及化学捕获方法,考察了费托合成过程中高温沉淀铁基催化剂表面吸附物种的变化,并探讨了含氧化合物的生成机理。结果表明,CO在高温沉淀铁基催化剂上有线式和桥式两种吸附态存在,同时,CO的吸附在催化剂表面生成大量含氧化合物前驱体。费托原位实验捕获到了一些较关键的中间产物:表面乙酸盐、表面酰基、甲氧基等。同时发现高温沉淀铁基催化剂表面具有以下反应共性:醇类可与表面羟基结合生成烷氧基团;催化剂表面的吸附分子具有氧化性;一些基础化学物质如OH-、晶格氧等可以与甲醇或乙醛分子发生反应。对CH3OH + CO及CH3I + CO + H2两个反应的化学捕获实验表明,酰基是C2+含氧化合物的重要中间产物,酰基加氢是形成C2+含氧化合物的关键步骤。根据表面中间产物及反应特性,得到了高温沉淀铁基催化剂上费托合成含氧化合物的生成机理。 相似文献
16.
Effect of operating conditions and potassium content on Fischer-Tropsch liquid products produced by potassium-promoted iron catalysts
下载免费PDF全文
![点击此处可从《天然气化学杂志》网站下载免费的PDF全文](/ch/ext_images/free.gif)
The dependencies of Fischer-Tropsch synthesis liquid hydrocarbon product distribution on operating pressure and temperature have been studied over three potassium-promoted iron catalysts with increasing potassium molar content. The study followed an experimental planning and the results were analyzed based on surface response methodology. The effects of different operating conditions and potassium contents on the liquid product distribution were compared based on number average carbon number and dispersion. Results showed that high pressures (25 to 30 arm) favored the production of waxes that could be converted into liquid fuels through hydrocracking, while greater direct selectivity towards diesel was favored by low pressure (20 arm) using catalysts with low potassium to iron molar ratios. The liquid product distribution produced using an iron catalyst with high potassium content presented higher number-average number of carbons when compared to the distribution obtained using an iron catalyst with low potassium content. 相似文献
17.
18.
Wenping Ma Yunjie Ding Jing Yang Xing Liu Liwu Lin 《Reaction Kinetics and Catalysis Letters》2005,84(1):11-19
Summary Characterization (BET and TPD) and reaction studies were conducted with activated carbon supported iron catalysts (Fe/AC) used for the Fischer-Tropsch synthesis (FTS). The TPD study showed that there existed interactions between metals and the AC surface. Greater association of Cu and K promoters with the AC surface resulted in stronger promoter to surface interaction, which enhanced the H2 desorption ability of the Cu and K promoted Fe/AC catalyst prepared under vacuum impregnation (VI). Catalytic behavior of a Fe/AC catalyst (VI-15 Fe/2 Cu/2 K/81 AC, in parts per weight) was studied in a 1-liter slurry phase continuous stirred tank reactor. The catalyst presented moderate syngas conversion (44.3-60.6%) and high gaseous selectivity (CH4, 12.8-15.1% and C2-C4, 42.4-46.1%) under 304oC, 3.0 MPa, 1.1 L(STP)/g-cat/h, and H2/CO = 2.0 during 166 h of testing. Detectable hydrocarbons up to C18 were formed on the Fe/AC catalyst. 相似文献
19.
以SBA-15分子筛为载体,采用等体积浸渍法制备了负载量为20%的钴基催化剂,采用TEM、XRD、H2-TPR和N2物理吸附-脱附等方法对催化剂进行了表征,并在浆态床反应器中考察了水的加入对费-托合成反应性能的影响.结果表明,金属钴物种进入到SBA-15载体的孔道中;产物在孔道中的滞留以及水促进的金属钴物种的团聚,引起了催化剂活性的降低;水的加入有利于反应物和产物在孔道中的传输,增加CO的转化率;在SBA-15负载的钴基催化剂中,产物在孔道中的滞留对催化剂活性影响较大,引起的扩散限制是催化剂活性降低的重要原因. 相似文献
20.
Ali Nakhaei Pour Mohammad Reza Housaindokht Sayyed Faramarz Tayyari Jamshid Zarkesh 《天然气化学杂志》2010,19(3):333-340
A nano-structured iron catalyst for syngas conversion to hydrocarbons in Fischer-Tropsch synthesis (FTS) was prepared by micro-emulsion method. Compositions of bulk iron phase and phase transformations of carbonaceous species during catalyst deactivation in FTS reaction were characterized by temperature-programmed surface reaction with hydrogen (TPSR-H2), and XRD techniques. Many carbonaceous species on surface and bulk of the nano-structured iron catalysts were completely identified by combined TPSR-H2 and XRD spectra and which were compared with those recorded on conventional co-precipitated iron catalyst. The results reveal that the catalyst deactivation results from the formation of inactive carbide phases and surface carbonaceous species like graphite, and it will be increased when the particle size of iron oxides was reduced in FTS iron catalyst. 相似文献