Influence of oxygen, hydrogen, helium, argon and vacuum on the surface behavior of molten InSb, other semiconductors, and metals on silica

Sessile drop experiments were performed on molten indium antimonide on clean quartz (fused silica) surfaces. A cell was constructed through which argon, helium, oxygen, hydrogen or a mixture of these was flowed at 600 °C. Some of the InSb was doped with 0.1% Ga. The surface tension σ of oxide-free molten InSb was smaller in Ar than in He, may have increased with increasing O₂ in the gas, and was not influenced by Ga or H₂. The contact angle θ on silica was higher in the presence of Ar, was lowered by O₂, and was not influenced by H₂ or Ga. The work of adhesion W and the surface energy σ_sv of the silica were higher in He than in Ar. The surface remained free of solid oxide only in flowing gas containing 0.8 ppm O₂. This behavior is attributed to reaction of O₂ at the surface of the melt to form In₂O gas. When solid oxide formed on Ga-doped material, it was strongly enriched in Ga, with the Ga/In ratio increasing with the concentration of O₂ in the gas.

Examination of published sessile-drop results for liquid metals and semiconductors on silica revealed that W and σ_sv were highest for reactive melts, in which SiO₂ dissolves. For non-reactive melts, W and σ_sv were lower and θ higher in a gas than in a vacuum, regardless of whether the experiments had been carried out in sealed ampoules, a flowing gas, or dynamic vacuum. The implication is that the surface of silica was different in a vacuum than in a gas at 1 bar.     

Oriented growth of large size calcium fluoride single crystals for optical lithography

We report (1 1 1), (1 1 0) and (1 0 0) growth of CaF₂ by the vertical Bridgman method. Crystals up to 250 mm diameter were grown and various growth parameters such as growth rate, temperature gradient and post-growth cooling rate were studied. It was found that the growth rate and the cooling rate are slower for the larger diameter crystals with a fixed temperature gradient. These growth parameters were optimized for growing the crystals along specific orientation after realizing that CaF₂ has a tendency to grow along an orientation close to 1 1 0. Degradation in optical transmittance was evaluated by irradiating the crystal to γ-rays up to a dose of 10⁵ rad. Optimized scavenger addition resulted in crystals with better radiation resistance and excellent VUV transmittance.     

Crystallization of calcium oxalate monohydrate at dipalmitoylphosphatidylcholine monolayers in the presence of chondroitin sulfate A

The growth and aggregation of calcium oxalate monohydrate (COM) crystals beneath dipalmitoylphosphatidylcholine (DPPC) monolayers in the presence of chondroitin sulfate A (C₄S) was systematically examined under different surface pressure. The results indicated that the addition of C₄S can inhibit the crystal growth and prevent the aggregation of COM crystals. Under a DPPC monolayer, well-defined three-dimensional hexagonal prisms and three-dimensional rhombus prisms with sharply angled tips were obtained. The DPPC monolayer at a surface pressure of 10 mN/m can match the Ca²⁺ distance of the face of COM better than at 20 mN/m. The addition of C₄S could cooperatively modulate the interaction strength between the monolayer (or itself) with the specific morphology determining faces such as and (0 2 0), and thus results in remarkable stabilization of the faces. The dramatic changes in morphological details were due to the strong electrostatic interactions between the Ca²⁺-rich crystal faces of COM and the polyanionic polysaccharide C₄S together with the negatively charged sites of the zwitterionic DPPC monolayers. The increase of the concentration of C₄S can further enhance the stabilization of the face.     

The effect of calcium cations on the precipitation of barium sulfate 2: calcium ions in the presence of organic additives

Calcium ions have been implicated in changing the precipitation of barium sulfate when organic additives are present, although whether it inhibits or promotes nucleation and/or growth has been disputed in the literature. We conducted a thorough investigation into the effect of calcium when additives are present and show that calcium cations do indeed promote nucleation of barium sulfate particles when compared to the appropriate control. This result is independent of the analytical method (conductivity or turbidity) used to assess precipitation. The nucleation promotion produces no change in the crystal morphology, thus morphology is not always a good indicator of nucleation or growth behavior. The extent of nucleation promotion depends on the functional group of the additive.     

Synthesis of calcium carbonate polymorphs in the presence of polyacrylic acid

Calcium carbonate precipitates are prepared from a solution of CaCl₂ and K₂CO₃ in the presence of polyacrilic acid. The effect of polyacrilic acid incorporation in the [25–80 °C] temperature range on crystal morphologies and CaCO₃ precipitated polymorph concentrations are investigated using scanning electron microscopy and X-ray diffraction quantitative microstructural and phase analysis. Large changes in morphology and phase proportions are observed in the presence of polyacrylic acid, which strongly depend on the solution temperature. While crystallization of vaterite is favoured in the presence of polyacrilic acid up to 50 °C, it is largely destabilized at higher temperatures. Our process also enables the elaboration of particles in the range 10–20 nm.     

Growth of calcium carbonate in polyacrylamide hydrogel: Investigation of the influence of polymer content

The growth of calcium carbonate crystals has attracted growing attention as a model system for biomineralisation processes. Organic molecules and gelatinous matrices are known to play an essential role in the formation of hard tissues. For the investigation of the function of specific influence factors, a model experiment is necessary. Several hydrogels were previously tested as growth matrices for calcium carbonate.

For laboratory experiments, a double diffusion set-up for the growth of crystals in gels was established earlier. Calcium carbonate crystals were grown in polyacrylamide hydrogels.

Here the influence of the polymer content in the hydrogels on the crystallisation behaviour is reported. Time-resolved and spatially resolved crystallisation experiments were conducted. The collected calcium carbonate precipitates were analysed by light microscopy, scanning electron microscopy and X-ray diffraction.

The morphology of the developing crystals was found to be dependent on the polymer content of the hydrogels.     

Defect characterization and composition distributions of mercury indium telluride single crystals

A mercury indium telluride (MIT) ingot was grown by the vertical Bridgman method. The defects in MIT crystals were characterized by the chemical etching method. A defect etchant for MIT crystals was developed. The etch pits of dislocations, microcracks and boundary was observed by scanning electron microscopy. It was elucidated that the etch pits density of dislocations of MIT wafers was about 4×10⁵ cm⁻². Te and In reduced at the grain boundaries, but were homogeneously distributed within the grains in the as-grown MIT crystals. The distribution of In in MIT crystals along the growth direction and radial direction was analyzed by electronic probe microscopy. It was found that In concentration was higher in the initial part and lower in the final part of the MIT ingot, which indicated that the segregation coefficient of In in MIT crystals was 1.15. The radial In concentration increased from the center to edge of the wafers and homogeneous in the middle part.     

Study of effects of polishing and etching processes on Cd1−xZnxTe surface quality

The effect of surface preparation on CdZnTe properties was investigated. Surface etching using bromine solutions enhances Te elemental composition, resulting in a Te rich surface layer that is prone to oxidize. This oxidation degrades the performance of the fabricated CZT gamma detector. Roughness results were identical for samples polished with 1 and 3 μm and subsequently etched in 2% Br-MeOH. The optimal concentration of etching was 2% Br-MeOH.     

Facile preparation of diversified patterns of calcium carbonate in the presence of DTAB

Nano- and micro-sized calcium carbonate (CaCO₃) with various morphologies including multi-petal-flower-shaped, multi-step-cube-shaped, coral-shaped, dendrite-shaped and multi-antenna-shaped was successfully prepared using dodecyltrimethylammonium bromide (DTAB) micellar vevulsant. The effects of temperature, pH and the concentration of DTAB micellar solution on the morphology and crystalline form of CaCO₃ were systematically investigated. The prepared CaCO₃ was characterized by Scanning Electron Microscope (SEM), Transmission Electron Microscopy (TEM), X-ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FTIR). The concentration of DTAB micelle, pH and reaction temperature are found to play crucial roles in the morphology, size and crystalline form of the final products. On the base of the characterizations, a possible self-assembled mechanism was proposed. The novel multi-petal-flower-shaped and multi-antenna-shaped CaCO₃ may have some unique properties and potential applications in the future.     

Reconstruction of the -GaO (1 0 0) cleavage surface to hexagonal GaN after NH nitridation

The potential use of β-Ga₂O₃ wafers as transparent conductive substrates for compounds with hexagonal structure, in particular the GaN-system, is shown. Nitridation of the main cleavage plane under high temperature and NH₃ gas results in the substitution of O by N on the surface, and a simultaneous surface reconstruction. The 2-fold symmetry of the initial (1 0 0) plane changes to a 6-fold symmetry, keeping the [0 1 0] azimuth as a symmetry direction. The RHEED pattern suggests the formation of GaN on the β-Ga₂O₃ surface, with the b-axis of β-Ga₂O₃ parallel to the direction of GaN, so that β-Ga₂O₃ can be used as a substrate with no lattice mismatch to GaN.     

Influence of some foreign metal ions on crystal growth kinetics of brushite (CaHPO4·2H2O)

Brushite, CaHPO₄·2H₂O, has been precipitated at 25 °C in the presence of Mg²⁺, Ba²⁺ or Cu²⁺ at concentrations up to 0.5 mM. When initial pH is sufficiently low to exclude nanocrystalline apatite as the initial solid phase, overall crystal growth rate may be determined from simple mass crystallization by recording pH as function of time. A combination of surface nucleation (birth-and-spread) and spiral (BCF) growth was found. Edge free energy was determined from the former contribution and was found to be a linear function of chemical potential of the additive, indicating constant adsorption over a wide range of additive concentrations. Average distances between adsorbed additive ions as calculated from slopes of plots are compatible with lattice parameters of brushite: 0.54 nm for Mg²⁺, 0.43 nm for Ba²⁺ and 0.86 nm for Cu²⁺. With the latter a sharp decrease in growth rate occurred early in the crystallization process, followed by an equally sharp increase to the previous level. When interpreted in terms of the Cabrera–Vermilyea theory of crystal growth inhibition, the results are consistent with an average distance between Cu ions of 0.88 nm, in perfect agreement with the above value.     

Synthesis and optical properties of high-purity CoO nanowires prepared by an environmentally friendly molten salt route

CoO nanowires with diameters of 50^_80 nm, and lengths of up to more than 5 μm have been successfully synthesized by a simple environmentally friendly molten salt route, in which the precursor CoCO₃ nanoparticles are decomposed to form high-purity CoO nanowires in NaCl flux. The structure features and morphology of the as-prepared CoO nanowires were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), and selected area electron diffraction (SAED). The chemical composition and oxidation state of the prepared nanowires were systemically studied by X-ray photoelectron spectra (XPS) and laser Raman spectroscopy. The results indicated that the as-prepared CoO nanowires were composed of pure cubic CoO phase. The growth mechanism of the synthesized nanowires was also discussed in detail based on the experimental results.     

Growth of aragonite calcium carbonate nanorods in the biomimetic anodic aluminum oxide template

In this study, a biomimetic template was prepared and applied for growing calcium carbonate (CaCO₃) nanorods whose shape and polymorphism were controlled. A biomimetic template was prepared by adsorbing catalytic dipeptides into the pores of an anodic aluminum oxide (AAO) membrane. Using this peptide-adsorbed template, mineralization and aggregation of CaCO₃ was carried out to form large nanorods in the pores. The nanorods were aragonite and had a structure similar to nanoneedle assembly. This aragonite nanorod formation was driven by both the AAO template and catalytic function of dipeptides. The AAO membrane pores promoted generation of aragonite polymorph and guided nanorod formation by guiding the nanorod growth. The catalytic dipeptides promoted the aggregation and further dehydration of calcium species to form large nanorods. Functions of the AAO template and catalytic dipeptides were verified through several control experiments. This biomimetic approach makes possible the production of functional inorganic materials with controlled shapes and crystalline structures.     

Growth and properties of Pb[(Zn1/3Nb2/3)0.91Ti0.09]O3 single crystals directly from melt

Pb[(Zn_1/3Nb_2/3)_0.91Ti_0.09]O₃ (PZNT91/9) single crystals were grown by a modified Bridgman method directly from melt using an allomeric Pb[(Mg_1/3Nb_2/3)_0.69Ti_0.31]O₃ (PMNT69/31) single crystal as a seed. X-ray diffraction (XRD) measurement confirmed that the as-grown PZNT91/9 single crystals are of pure perovskite structure. Electrical properties and thermal stabilization of PZNT91/9 crystals grown directly from melt exhibit different characters from those of PZNT91/9 crystals grown from flux, although segregation and the variation of chemical composition are not seriously confirmed by X-ray fluorescence analysis (XPS). The [0 0 1]-oriented PZNT91/9 crystals cut from the middle part of the as-grown crystal boules exhibit broad dielectric-response peaks at around 105 °C, accompanied by apparent frequency dispersion. The values of piezoelectric constant d₃₃, remnant polarization P_r, and induced strain are about 1800–2200 pC/N, 38.8 μC/cm², and 0.3%, respectively, indicating that the quality of PZNT crystals grown directly from melt can be comparable to those of PZNT91/9 single crystals grown from flux. However, further work deserves attention to improve the dielectric properties of PZNT crystals grown directly from melt. Such unusual characterizations of dielectric properties of PZNT crystals grown directly from melt are considered as correlating with defects, microinhomogeneities, and polar regions.     

Direct observation of sublimation process on a CdTe(1 1 1) surface using an ultrafine particle

A particle with a CdTe core and carbon mantle was produced by the advanced carbon-coating method which enables direct coverage with a carbon layer using an electron microscope. The coagulated particles containing approximately 30–200 CdTe particles produced by the gas evaporation method were covered with a carbon layer of about 7 nm thickness at 300°C. By heating these particles above 500°C, the sublimation process of a part of the CdTe particle can be directly captured by high-resolution transmission electron microscopy and recorded in real time on videotape. Sublimation on the CdTe(1 1 1) surfaces occurred in the step flow mode of two (1 1 1) layers. It was observed that two (1 1 1) zinc-blende layers changed to the (0 0 0 2) würtzite configuration unit just before sublimation. The condensation of CdTe on the sublimated particle surface and growth of CdTe in the carbon layers were also captured in the video image. These sublimation processes were discussed in terms of the existence of the polarity of II–VI compounds.     

Instability of the melt flow in VGF growth with a traveling magnetic field

The linear instability of a thermally stratified melt flow in the VGF configuration driven by a traveling magnetic field (TMF) is considered numerically and experimentally. The dependency of the instability threshold on the governing parameters is found for several cuts through the parameter space covering a wide range of possible applications. In a first approximation the linear instability occurs when the dimensionless TMF forcing parameter reaches the magnitude of the Grashof number. This is particularly true in a medium-sized crucible where the first instability is axisymmetric and sub-critical. As the Grashof number increases the flow develops self-similar boundary layers and the instability becomes three-dimensional. The instability originates in the bottom boundary layer where the convection tends to suppress the imposed temperature gradient in the central part of the melt zone. It is shown that the TMF may serve as a tool to control the phase interface shape without causing flow instationarity when the crucible diameter exceeds a certain value. This value is estimated to be around 6 cm for GaAs. The flow stays stable if the TMF is used for a reversal of the meridional flow with the aim to remove a possible dopant concentration peak on the axis.     

Growth of nanofibrous barium carbonate on calcium carbonate seeds

Fibrous barium carbonate (BaCO₃/witherite) crystals 50–100 nm in diameter and several microns in length were grown on calcium carbonate (CaCO₃) seeds at temperatures as low as 4 °C. The BaCO₃ fibers were deposited onto calcite rhombs or CaCO₃ films using the polymer-induced liquid-precursor (PILP) process, which was induced with the sodium salt of polyacrylic acid (PAA). The structure and morphology of the resultant fibers were investigated using scanning electron microscopy (SEM), transmission electron microscopy (TEM), selected-area electron diffraction (SAED), and polarized light microscopy (PLM). Fibers were successfully grown on calcite seeds of various morphologies, with a range of barium concentrations, and PAA molecular weight and concentration. Two categories of fibers were grown: straight and twisted. Both types of fibers displayed single-crystalline SAED diffraction patterns, but after examining high-resolution TEM lattice images, it was revealed that the fibers were in fact made up of nanocrystalline domains. We postulate that these nanocrystalline domains are well aligned due to a singular nucleation event (i.e., each fiber propagates from a single nucleation event on the seed crystal) with the nanocrystalline domains resulting from stresses caused by dehydration during crystallization of the highly hydrated precursor phase. These BaCO₃ fibers grown on calcite substrates further illustrate the robustness and non-specificity of the PILP process.     

Role of non-stoichiometry in the cracking of oxide crystals

The cracking and stoichiometric deviations frequently observed in crystals of mixed oxides have generally been perceived to be unrelated phenomena. The present study pertains to the cracking in Czochralski grown crystals of three different materials, viz. CdWO₄, PbWO₄ and ZnWO₄. The results obtained on the single-crystal growth as well as on the thermal stability of melts of these materials and of their constituent oxides demonstrate, for the first time, that stoichiometric deviations manifest as cracks in the crystals. An important outcome of this investigation is that materials exhibiting a small degree of super-cooling with stable melting and solidification temperatures should be less prone to cracking.