Preparation and characterization of SiO2/TiO2 composite microspheres with microporous SiO2 core/mesoporous TiO2 shell

SiO₂/TiO₂ composite microspheres with microporous SiO₂ core/mesoporous TiO₂ shell structures were prepared by hydrolysis of titanium tetrabutylorthotitanate (TTBT) in the presence of microporous silica microspheres using hydroxypropyl cellulose (HPC) as a surface esterification agent and porous template, and then dried and calcined at different temperatures. The as-prepared products were characterized with differential thermal analysis and thermogravimetric (DTA/TG), scanning electron microscopy (SEM), X-ray diffraction (XRD), nitrogen adsorption. The results showed that composite particles were about 1.8 μm in diameter, and had a spherical morphology and a narrow size distribution. Uniform mesoporous titania coatings on the surfaces of microporous silica microspheres could be obtained by adjusting the HPC concentration to an optimal concentration of about 3.2 mmol L⁻¹. The anatase and rutile phase in the SiO₂/TiO₂ composite microspheres began to form at 700 and 900 °C, respectively. At 700 °C, the specific surface area and pore volume of the SiO₂/TiO₂ composite microspheres were 552 and 0.652 mL g⁻¹, respectively. However, at 900 °C, the specific surface area and pore volume significantly decreased due to the phase transformation from anatase to rutile.     

TiO2-SiO2复合气凝胶：常压干燥制备及性能表征

以廉价的四氯化钛和工业水玻璃为原料,通过溶胶-凝胶法制得TiO2-SiO2复合湿凝胶,用三甲基氯硅烷(TMCS)/乙醇(EtOH)/正己烷(Hexane)混合溶液对湿凝胶进行改性,常压干燥制备了TiO2-SiO2复合气凝胶.利用扫描电子显微镜(SEM)、透射电子显微镜(TEM)、红外光谱(FTIR)、X射线衍射(XRD)及N2吸附/脱附法对复合气凝胶的形貌和性质进行了分析.结果表明,TiO2-SiO2复合气凝胶具有连续多孔结构,150℃干燥后复合气凝胶的比表面积为1 076 m2·g-1,孔体积为4.96 cm3·g-1;经550 ℃热处理后,复合气凝胶仍然具有高的孔隙率,比表面积为856 m2·g-1,孔体积为3.46 cm3·g-1.吸附和光催化降解罗丹明B的结果表明,复合气凝胶同时具有较好的吸附和光催化性能,其吸附/光催化协同作用活性优于纯SiO2气凝胶和锐钛矿TiO2粉末;且重复利用四次降解率仍然可达到89%.     

Preparation of porous TiO2/silica composites without any surfactants

TiO₂-SiO₂ composites, with high specific surface area (up to 308 m²/g), large pore volume, and narrow distribution with average pore sizes of 3.2 nm, have been synthesized from wollastonite and titanium sulfate in the absence of any surfactants. Calcium sulfate, a microsolubility salt, plays an important role in the formation of pores in this porous TiO₂/silica composite. The microstructure and chemical composition of composite were characterized by X-ray diffractometry (XRD), transmission electron microscopy (TEM) equipped with energy-dispersive X-ray spectroscopy (EDX), X-ray photoelectron spectrometer (XPS) and N₂ adsorption and desorption analysis. The as-prepared porous titanium dioxide-silicon dioxide composites with high specific surface area and well-crystallized anatase contents were used as an efficient photocatalyst.     

Preparation and characterization of porous TiO_2/ZnO composite nanofibers via electrospinning

<正>Porous TiO_2/ZnO composite nanofibers have been successfully prepared by electrospinning technique for the first time.It was generated by calcining TiO_2/ZnCl_2/PVP[PVP:polyvinyl pyrrolidone)]nanofibers,which were electrospun from a mixture solution of TiO_2,ZnCl_2 and PVP.Transmission electron microscopy(TEM) and X-ray diffraction(XRD) analyses were used to identify the morphology of the TiO_2/ZnO nanofibers and a formation of inorganic TiO_2/ZnO fibers.The porous structure of the TiO_2/ZnO fibers was characterized by N_2 adsoption/desorption isotherm.Surface photovoltage spectroscopy(SPS) and photocatalytic activity measurements revealed advance properties of the porous TiO_2/ZnO composite nanofibers and the results were compared with pure TiO_2 nanofibers,pure ZnO nanofibers and TiO_2/ZnO nanoparticles.     

氧化铝-g-聚丙烯酰胺复合磨粒的制备及表征

为提高α-Al₂O₃磨粒在水基介质中的分散稳定性，采用接枝聚合方法制备了Al₂O₃-g-聚丙烯酰胺复合粒子。采用FTIR、XPS、TOF-SIMS、激光粒度仪、SEM、沉降试验等对氧化铝复合粒子结构及分散性能等进行了表征。结果表明，聚丙烯酰胺以化学键形式接枝到Al₂O₃粒子表面，形成聚丙烯酰胺为壳，Al₂O₃为核的复合磨粒;接枝改性后的Al₂O₃粒子分散性明显提高，并且其分散性与Al₂O₃表面接枝量密切相关。     

SO2气氛下半焦负载Zn/Fe/Ce高温煤气脱硫剂的再生行为研究

以共沉淀法制备了半焦负载Zn/Fe/Ce（物质的量比1.0：2.0：0.6）高温煤气脱硫剂,在固定床装置上研究了再生反应温度、进口SO₂浓度以及再生气空速对再生性能的影响,并进行三次硫化-再生循环测试。采用XRD、SEM、BET等测试手段对脱硫剂的新鲜样、硫化样及再生样进行了表征。实验结果表明,半焦负载Zn/Fe/Ce高温煤气脱硫剂在SO₂气氛下600 ℃就能发生再生反应,且再生后的主要产物为ZnFe₂O₄、CeO₂和单质硫;最佳再生条件为,再生温度700 ℃、进口SO₂体积分数为12%、再生气空速为5 000 h^-1。脱硫剂经过多次硫化-再生循环后,脱硫剂仍能保持较好的硫化活性。     

Preparation of monodispersed microporous SiO2 microspheres with high specific surface area using dodecylamine as a hydrolysis catalyst

A novel and simple method for the synthesis of monodispersed microporous SiO₂ microspheres with high specific surface area was developed by hydrolysis of tetraethoxysilane (TEOS) in a water-ethanol mixed solution and using dodecylamine (DDA) as hydrolysis catalyst and template. The as-prepared products were characterized with differential thermal analysis-thermogravimetry, scanning electron microscopy, high-resolution transmission electron microscopy, small angle X-ray diffraction and nitrogen adsorption. The effects of experimental conditions including hydrolysis temperatures, calcination temperature and concentrations of TEOS and DDA on the morphology and pore parameters of the as-prepared SiO₂ microspheres were investigated and discussed. The results showed that hydrolysis temperature and concentrations of TEOS and DDA are important parameters for the control of size and morphology of particles. The specific surface area and specific pore volume of the as-prepared SiO₂ microspheres increased with increasing DDA concentration and calcination temperature. DDA may act not only as a good hydrolysis catalyst but also as a template for the formation of monodispersed SiO₂ microspheres with high specific surface area. This research may provide new insight into the synthesis of monodispersed microporous SiO₂ microspheres.     

Thermal Stability of Pt/Al2O3 Catalysts Prepared by Sol-Gel

A series of Pt/Al₂O₃ catalysts were prepared using a sol-gel method. The influence of several parameters used in the synthesis including: metal content, identity of the metal precursor, and the water/alkoxide ratio on the structural properties of the fresh (dried) and calcined samples were studied. It was found that the BET surface area decreased with an increase in the platinum content. A surface area of 500 m²/g was obtained following calcination at 773 K. The structure of fresh samples as determined by FTIR corresponded to that of a pseudoboehmite structure. Samples prepared using a water/alkoxide ratio (H₂O/ATB) of 9 showed a well-defined, uniform pore size distribution following calcination at 773 K. Metal dispersions comparable to those obtained using impregnation methods were obtained. Aging studies (calcination at 873 K for 24 h) performed on these catalysts, exhibited sintering behavior which were similar to Pt/Al₂O₃ catalysts prepared by other methods. The sample prepared using a H₂O/ATB ratio of 9 had the highest surface area and was more thermally resistant towards metal sintering. A bimodal metal particle size distribution was observed: some particles exhibited sintering while others of similar size showed a greater thermal stability to sintering. The sample having the largest surface area and the highest thermal stability following thermal treatment was a consequence of a more condensed structure and a higher pore roughness obtained after drying the gel. This enabled the formation of an alumina structure which was more amorphous and limited aggregation of platinum particles due to surface diffusion within the pore structure.     

不同铈添加量对CeO2-ZrO2-Al2O3材料性能的影响

采用共沉淀法制备了一系列不同铈添加量的CeO2-ZrO2-Al2O3(CZA)储氧材料,并通过XRD、低温N2吸附-脱附、氧脉冲吸附(OSC)和H2-TPR等手段进行了表征。XRD结果表明,在1 000和1 100℃高温焙烧后,当CeO2添加量为8%时样品具有最好的结构稳定性能。N2吸附-脱附结果表明,CeO2添加量为8%时样品具有最好的织构性能,1 000℃时,比表面积和孔容分别为:136.6 m2.g-1和0.38 mL.g-1;1 100℃时,比表面积和孔容分别为:83.7 m2.g-1和0.23 mL.g-1。OSC结果显示,CeO2添加量为8%时样品具有最大的储氧量,1 000℃和1 100℃分别为70μmol.g-1和31μmol.g-1。H2-TPR结果表明,CeO2添加量为8%时样品具有最佳的还原性能。     

球形TiO2-Al2O3的制备、结构和理化性能研究

将Ti(SO₄)₂溶于稀盐酸合成酸性钛溶胶，再将其与铝溶胶和六次甲基四胺溶液混合后采用油柱成型法制备了球形TiO₂-Al₂O₃复合氧化物。通过XRD、低温氮吸附-脱附与NH₃-TPD等手段对样品进行表征，结果表明600 ℃焙烧得到的球形TiO₂-Al₂O₃中TiO₂以无定型形式存在;随TiO₂含量的增加，球形TiO₂-Al₂O₃的比表面积、孔容和平均孔径呈增加趋势;TiO₂的引入没有对球形TiO₂-Al₂O₃的强酸和弱酸中心的强度产生影响，弱酸中心数量显著增加，强酸中心数量稍有增加;球形TiO₂-Al₂O₃的堆密度和压碎强度随TiO₂含量的增加而减小，颗粒直径基本保持不变。     

TiO2微粒功能化多孔Al2O3膜的光电化学研究

用恒电位法制备了多孔Al₂O₃薄膜, 通过在Al₂O₃薄膜孔内水蒸汽水解钛酸异丙酯生成了锐钛矿型TiO₂微粒, 制备出了Al₂O₃与TiO₂微粒的复合薄膜. 用XRD, SEM, 光电化学方法进行了研究. 实验表明: 该复合薄膜具有光电转换特性, 在光催化、光电化学太阳能转换中具有应用价值.     

氨基功能化SBA-16对CO_2的动态吸附特性

采用浸渍法将四乙烯五胺(TEPA)负载到介孔分子筛SBA-16的孔道内,形成功能化的介孔材料用于CO2的吸附.利用X射线衍射(XRD)、透射电镜(TEM)、氮气物理吸附-脱附和热重分析(TGA)等方法对样品进行了表征.通过动态吸附对不同TEPA浸渍量的SBA-16的CO2吸附性能和再生性能进行研究.结果表明:修饰后的SBA-16仍然保持有序的孔道结构,但样品的孔道有序度降低,比表面积、孔容、平均孔径都减小.样品对CO2的饱和吸附容量和穿透吸附容量随着TEPA浸渍量的增加而增加.60℃时,30%TEPA浸渍量的样品的穿透吸附容量和饱和吸附容量达到最大,分别为0.625和0.973mmol·g-1.在60-80℃,样品的动态吸附性能稳定.经过20次吸附-脱附循环后,样品的饱和吸附容量仅降低了6.45%.采用失活模型对CO2的吸附穿透曲线进行模拟,该模型能够很好地模拟样品对CO2的吸附过程.     

以氨水和碳酸铵为沉淀剂制备氧化铝的对比研究

γ-Al2O3，是一种常用的催化剂载体，它具有比表面大和价廉易得等优点。但对于很多高温反应体系，如汽车尾气催化净化，其热稳定性在很大程度上影响了汽车尾气净化催化剂的活性和稳定性，因此提高γ-Al2O3的高温热稳定性对保持汽车尾气净化催化剂的反应活性、延长催化剂的使用寿命非常重要。     

Structural Characterization and Property Study on the Activated Alumina-activated Carbon Composite Material

AlCl3,NH3·H2O,HNO3 and activated carbon were used as raw materials to prepare one new type of activated alumina-activated carbon composite material.The influence of heat treatment conditions on the structure and property of this material was discussed;The microstructures of the composite material were characterized by XRD,SEM,BET techniques;and its formaldehyde adsorption characteristic was also tested.The results showed that the optimal heat treatment temperature of the activated alumina-activated carbon composite material was 450 ℃,iodine adsorption value was 441.40 mg/g,compressive strength was 44 N,specific surface area was 360.07 m2/g,average pore size was 2.91 nm,and pore volume was 0.26 m3/g.According to the BET pore size distribution diagram,the composite material has dual-pore size distribution structure,the micro-pore distributes in the range of 0.6-1.7 nm,and the meso-pore in the range of 3.0-8.0 nm.The formaldehyde adsorption effect of the activated alumina-activated carbon composite material was excellent,much better than that of the pure activated carbon or activated alumina,and its saturated adsorption capacity was 284.19 mg/g.     

Zinc oxide nanowires in chemical bath on seeded substrates: Role of hexamine

Ceria-doped alumina sol-gel materials were obtained by two synthesis methods at low temperature; using method A, 2-propanol-diluted cerium precursor was slowly added at the time of the aluminum sol formation in acidic environment; using method B, the cerium salt was mixed with the aluminum alkoxide before sol formation in a basic environment. The supports were characterized by N₂ physisorption, thermogravimetric and thermal differential analyses (TGA and DTA), X-ray diffraction (XRD), ²⁷Al Magic Angle Spinning-Nuclear Magnetic Resonance (MAS-NMR), 2-propanol reactions, and ammonia temperature-programmed desorption (NH₃-TPD). The samples obtained by Method B present similar values in properties such as specific areas, pore volumes, pore size distribution, and acidity compared to those of pure alumina; the alumina structure was not modified, but segregated crystallites of CeO₂ were found in samples calcined at 1000 ^∘C, as observed by XRD. The ceria-containing materials synthesized by method A show a thermal behavior similar to that of alumina, with no appreciable segregation of CeO₂ detected by XRD and modifications in the amounts of tetra, penta, and octa-hedral aluminum coordination as determined by NMR. 2-propanol reactions showed a good correlation with acid density determined by NH₃-TPD. As the percentage of ceria in the material increases, surface area, pore volume, and acidity decrease. These changes can be correlated with an increase of pentacoordinated aluminum content. The results indicate that CeO₂ is well dispersed in the alumina framework when method A is used, but synthesis method B does not have the same effect on the CeO₂incorporation.     

Improvement of the Pd/Al2O3 Catalyst by the Control of the Sol-Gel Preparative Parameters

In this work, the metal dispersion of the Pd/Al₂O₃ catalyst prepared by sol-gel method is improved by an adequate optimisation of the preparative variables. First, the gelation temperature and the ageing time are selected, in order to avoid the reduction of the metal precursor (palladium acetylacetonate, Pd(acac)₂) by the solvent (sec-butanol, sB). The metal sintering effect on the catalysts treated in oxygen at 500°C is then minimized when the alumina pore size is controlled by the variation of the alumium alkoxide (AsB) concentration and the acetic acid amount ([AcA]/[AsB]). The appearance of new palladium particles on the alumina surface and the matching between the particle diameters and the pore sizes were also effective for the metallic surface area improvement on the samples treated in oxygen at 800°C. Compared to the reference catalysts, the higher metal dispersion obtained on the sol-gel ones was the determinant factor for their higher catalytic activity in methane combustion.     

SO42-/TiO2-ZrO2复合氧化物固体酸催化剂的长叶烯芳构化催化性能

本工作用溶胶-凝胶法制备不同组成的SO42-/TiO2-ZrO2复合氧化物固体酸催化剂,用微型催化反应评价结合X-射线粉末衍射(XRD)、孔结构/BET表面积测试和NH3-程序升温脱附(NH3-TPD)等表征了SO42-/TiO2-ZrO2复合氧化物固体酸催化剂结构、表面酸性和长叶烯芳构化催化性能。复合氧化物固体酸SO42-/TiO2-ZrO2催化剂具有优良的长叶烯芳构化催化性能,并且其芳构化催化性能与催化剂组成和表面酸性密切相关。随催化剂中nZr/(nZr+nTi)增加,催化剂表面中等强度的酸中心量增加,芳构化产物选择性和收率明显增加,在nZr/(nZr+nTi)=0.5时达极大值。随nZr/(nZr+nTi)进一步增加,不仅催化剂表面酸中心量减少、原料转化率明显下降,而且催化剂酸强度增强,导致芳构化产物选择性和收率下降。催化长叶烯芳构化的二元复合氧化物固体酸SO42-/TiO2-ZrO2催化剂适宜的组成为nZr/(nZr+nTi)=0.5。     

Preparation of TiO2 nano-particle photocatalysts by a multi-gelation method: the effect of pH change

TiO₂ photocatalysts were prepared by a multi-gelation method and the effect of the changes in the pH during the pH swing times, i.e., by a controlled pH swing, on the morphology of the TiO₂ particles was investigated. The photocatalytic properties of the TiO₂ catalysts prepared by controlled pH swing were compared with TiO₂ particles prepared without adjusting the pH during the swing times. The photocatalytic degradation reaction of these TiO₂ catalysts was investigated by comparing their effectiveness in 2-propanol oxidation. The experimental results showed that the TiO₂ photocatalysts prepared without adjusting the pH performed better in controlling the important parameters of the catalysts such as particle size, surface area, anatase/rutile phase ratio and pore size, as well as pore volume than the TiO₂ photocatalysts prepared by a controlled pH swing method. Deceased.     

纳米TiO2-SiO2复合氧化物的制备与性质

采用溶胶-凝胶结合CO2超临界干燥方法制备了比表面积大、热稳定性好的纳米TiO2-SiO2复合氧化物.考察了原料组成和焙烧温度对复合氧化物比表面积、热稳定性和酸性的影响,通过加氢脱硫反应考察了该复合氧化物作为加氢精制催化剂载体的可行性.结果表明,采用该方法制备的复合氧化物为纳米颗粒,在n(Ti)/n(Si)=1时,其比表面积和孔容最大;与纯TiO2相比,引入SiO2明显提高了复合氧化物的热稳定性和晶型稳定性;以此复合氧化物为载体的加氢精制催化剂具有很好的低温脱硫活性,TiO2-SiO2复合氧化物载体的酸性特征影响了催化剂的加氢脱硫活性.     

Structure and properties of polymer modified TiO2 pillared montmorillonite

With the aim of improving the microstructures and properties of TiO₂ pillared montmorillonite (MMT), a long-chain polymer (polyoxypropylenediamine, PPO-D 2000) was used as a template to synthesize composite pillared MMT. The materials were characterized by X-ray powder diffraction (XRD), Fourier transform infrared (FT-IR) spectrophotometer, Fourier Raman (FT-Raman) spectrophotometer, thermo-gravimeter/differential thermogravimeter (TG/DSC), transmission electron microscopy (TEM), and Brunauer-Emmett-Teller (BET) methods. The results show that as compared to low-molecular weight surfactant, this polymer significantly expanded the interlayer spacing and thus more TiO₂ could be intercalated into MMT. The specific surface area of polymer/TiO₂ pillared MMT was increased by 13% with comparison to TiO₂ pillared MMT and rose to 241.52 m²/g. Both the pore diameter and volume are doubled, and thus the pore structure is optimized markedly. The investigation on the photo-catalytic degradation of methyl orange in aqueous solution show that the modulation of polymer molecules raise the adsorption content of montmorillonite and improve the photo-catalytic activity. Therefore, this process provides a novel alternative to design and prepare the advanced eco-catalytic materials with high adsorption capacity and photo-catalytic activity. __________ Translated from Huaxue Tongbao, 2007, 12: 936–941 [译自: 化学通报]