X-ray multiple diffraction in the characterization of TiNO and TiO2 thin films grown on Si(0 0 1)

TiO₂ and TiN_xO_y thin films grown by low pressure metal-organic chemical vapor deposition (LP-MOCVD) on top of Si(0 0 1) substrate were characterized by X-ray multiple diffraction. X-ray reflectivity analysis of TiO₂[1 1 0] and TiNO[1 0 0] polycrystalline layers allowed to determine the growth rate (−80 Å/min) of TiO₂ and (−40 Å/min) of TiNO films. X-ray multiple diffraction through the Renninger scans, i.e., ?-scans for (0 0 2)Si substrate primary reflection is used as a non-conventional method to obtain the substrate lattice parameter distortion due to the thin film conventional deposition, from where the information on film strain type is obtained.     

Optical and hydrophilic properties of Cr doped TiO2-SiO2 nanostructure thin film

Cr doped TiO₂-SiO₂ nanostructure thin film on glass substrates was prepared by a sol-gel dip coating process. X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) were used to characterize the structural and chemical properties of the films. A UV-vis spectrophotometer was used to measure the transmittance spectra of the thin film. The hydrophilicity of the thin film during irradiation and storage in a dark place was measured by a contact angle analyzer. The results indicated that Cr doping has a significant effect on the transmittance and super-hydrophilicity of TiO₂-SiO₂ thin film.     

Electrochemical properties of thin TiO2 electrode on Li1 + xAlxGe2 − x(PO4)3 solid electrolyte

A fabrication of all-solid-state thin-film rechargeable lithium ion batteries by sol-gel method is expected to achieve both the simplification and cost reduction for fabrication process. TiO₂ thin film electrode was prepared by PVP (polyvinylpyrrolidone) sol-gel method combined with spin-coating on Li_1 + xAl_xGe_2 − x(PO₄)₃ (LAGP) solid electrolyte which has wide electrochemical window. The thin film was composed of anatase TiO₂ that is the most active phase for Li insertion and extraction and contacted well with LAGP substrate. In the cyclic voltammogram, a redox couple was observed at 1.8 V vs. Li/Li⁺ assigned to Li insertion/extraction into/from anatase TiO₂, indicating that the thin film worked as electrode for lithium battery. The charge and discharge test in various charge and discharge rates revealed that the discharge process (delithiation) is thought to be faster than charge process (lithiation). It is attested that the sol-gel process, which derives both simplification and cost reduction for fabrication process, can be applied to thin film battery using LAGP solid electrolyte.     

Correlation between microstructure and optical properties of nano-crystalline TiO2 thin films prepared by sol-gel dip coating

Titanium dioxide thin films have been prepared from tetrabutyl-orthotitanate solution and methanol as a solvent by sol-gel dip coating technique. TiO₂ thin films prepared using a sol-gel process have been analyzed for different annealing temperatures. Structural properties in terms of crystal structure were investigated by Raman spectroscopy. The surface morphology and composition of the films were investigated by atomic force microscopy (AFM). The optical transmittance and reflectance spectra of TiO₂ thin films deposited on silicon substrate were also determined. Spectroscopic ellipsometry study was used to determine the annealing temperature effect on the optical properties and the optical gap of the TiO₂ thin films. The results show that the TiO₂ thin films crystallize in anatase phase between 400 and 800 °C, and into the anatase-rutile phase at 1000 °C, and further into the rutile phase at 1200 °C. We have found that the films consist of titanium dioxide nano-crystals. The AFM surface morphology results indicate that the particle size increases from 5 to 41 nm by increasing the annealing temperature. The TiO₂ thin films have high transparency in the visible range. For annealing temperatures between 1000 and 1400 °C, the transmittance of the films was reduced significantly in the wavelength range of 300-800 nm due to the change of crystallite phase and composition in the films. We have demonstrated as well the decrease of the optical band gap with the increase of the annealing temperature.     

Influence of annealing process on conductive properties of Nb-doped TiO2 polycrystalline films prepared by sol-gel method

Nb-doped TiO₂ (TNO) thin films were prepared by sol-gel dip-coating method with Nb content in a wide range of 0-20 at.%. The prepared films were preheated at 400 °C and then undertaken by two different post-annealing processes: (a) three times vacuum annealing and (b) multi-round annealing. The designed multi-round annealing was shown to be an effective way to improve the conductive properties of the films, compared to the traditional vacuum annealing process. The minimum resistivity reached approximately 0.5 Ω cm with Nb doping concentration around 12 at.%, and the carrier density increased with Nb-doping concentration until the critical point of 12 at.%, which might be the optimal doping content for our TNO films prepared by sol-gel method.     

Preparation and optical properties of ZnGa2O4:Cr thin films derived by sol-gel process

ZnGa₂O₄:Cr³⁺ thin films with bright red emission were synthesized using a sol-gel process, characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), Auger electron spectroscopy (AES) and UV-vis and fluorescence spectrophotometry measurements. Effects of calcining temperature, film thickness, calcining duration and substrates on the crystal structure and photoluminescent property have been investigated. It is found that the crystallinity, Ga/Zn ratio and band gap energy (E_g) are significant factors influencing optical characteristics, while the nature of substrates affect the surface morphologies of ZnGa₂O₄:Cr³⁺ thin films.     

Influences of space charge and electrode on the electrical transport through (Ba,Sr)TiO3 thin film capacitors

The combined model of thermionic emission and carrier drift-diffusion is derived to simulate the electrical transport through BST thin film capacitors. In the model the field-dependent permittivity is obtained from the derivative of the polarization distinguished with the traditional characterization. The simulated currents show the hysteresis. The influences of space charges and electrode materials on the current density-applied voltage characteristics have been studied. The simulation results suggest that the current densities can be greatly influenced by the space charges at the cathode interface and the barrier height at the electrode/BST interface. It is expected that this work can provide some useful guidelines to the design and performance improvement of BST thin film capacitors and other BST thin film devices.     

Theoretical study of CO adsorption on the illuminated TiO2 (0 0 1) surface

A quantum modeling of the CO adsorption on illuminated anatase TiO₂ (0 0 1) is presented. The calculated adsorption energy and geometries of illuminated case are compared with the ground state case. The calculations were achieved by using DFT formalism and the BH and HLYP. Upon photoexcitation, an electron-hole pair is generated. Comparing of natural population in the ground state and the exited state, shows that an electron is trapped in a Ti⁴⁺ ion and a hole is localized in an oxygen ion. The photoelectron helps generation of a CO₂ molecule on the TiO₂ surface. As shown by optimization of these systems, the CO molecule adsorbed vertically on the TiO₂ (0 0 1) surface in the ground state case while the CO molecule made an angle of 134.3° to this surface at the excited state case. Based on the here used model the obtained adsorption energy was 0.36 eV which is in excellent agreement with the reported experimental value. In the present work the C-O stretch IR frequencies are calculated which are 1366.53 and 1423.16 cm⁻¹. These results are in good agreement with the earlier reported works for the surface carbonaceous compounds, and oxygenated carbon species.     

Influence of heating rate on the crystalline properties of 0.7BiFeO3-0.3PbTiO3 thin films prepared by sol-gel process

0.7BiFeO₃-0.3PbTiO₃ (BFPT7030) thin films were deposited on SiO₂/Si substrates by sol-gel process. The influence of heating rate on the crystalline properties of BFPT7030 thin films were studied by X-ray diffraction (XRD), scanning electron microscope (SEM), atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS). XRD patterns of the films showed that a pure perovskite phase exists in BFPT7030 films annealed by rapid thermal annealing (RTA) technique. SEM and AFM observations demonstrated that the BFPT7030 films annealed by RTA at 700 °C for 90 s with the heating rate of 1 °C s⁻¹ could show a dense, crack-free surface morphology, and the films’ grains grow better than those of the films annealed by RTA at the same temperature with other heating rates. XPS results of the films indicated that the ratio of Fe³⁺:Fe²⁺ is about 21:10 and 9:5 for the films annealed by RTA at 700 °C for 90 s with the heating rate of 1 and 20 °C s⁻¹, respectively. That means the higher the heating rate, the higher the concentration of Fe²⁺ in the BFPT7030 thin films.     

Vapor phase modification of sol-gel derived titania (TiO2) surfaces

Chemical vapor deposition (CVD) method was used in titania surface modification. Titania layers were obtained in sol-gel process and prepared as thin films on silicon wafers in dip-coating method. In order to define the influence of modification on titania surface properties (e.g., friction), various types of fluoroalkylsilanes were used. The effectiveness of the modification was monitored by FT-IR spectroscopy. The topography and frictional measurements were investigated with the use of atomic force microscopy (AFM).     

Preparation and photo-induced superhydrophilicity of composite TiO2-SiO2-In2O3 thin film

In this work, TiO₂-SiO₂-In₂O₃ composite thin films on glass substrates were prepared by the sol-gel dip coating process. X-ray diffraction (XRD), X-ray fluorescence spectroscopy (XRF) and X-ray photoelectron spectroscopy (XPS) were used to evaluate the structural and chemical properties of the films. UV-vis spectrophotometer was used to measure the transmittance spectra of thin films. The water contact angle (WCA) of thin films during UV/vis irradiation and storage in a dark place was measured by a contact angle analyzer. The results indicated that fabrication of composite film has a significant effect on transmittance and superhydrophilicity of TiO₂ films.     

Structural, optical and electrical properties of ZnO/Zn2GeO4 porous-like thin film and wires

Zinc oxide/zinc germanium oxide (ZnO/Zn₂GeO₄) porous-like thin film and wires has been fabricated by simple thermal evaporation method at temperature about 1120 °C for 2.5 h. The structural and optical properties of the porous-like-thin film and wires have been investigated by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD) and photoluminescence (PL) spectroscopy. Metal semiconductor metal (MSM) photodetector structure was used to evaluate the electrical characteristics by using current-voltage (I-V) measurements. Room temperature photoluminescence spectrum of the sample shows one prominent ultraviolet peak at 378 nm and a shoulder at 370 nm. In addition, broad visible blue emission peak at wavelength 480 nm and green emission peak at 500 nm are also observed. Strong photoelectric properties of the MSM in the UV demonstrated that the porous-like-thin film and wires contribute to its photosensitivity and therefore making ZnO/Zn₂GeO₄ wires potential photodetector in the shorter wavelength applications.     

(Mo + N) codoped TiO2 for enhanced visible-light photoactivity

A series of Ti_1−xMo_xO_2−yN_y samples were prepared by using sol-gel method and characterized by X-ray diffraction, transmission electron microscopy and UV-vis absorption spectroscopy. All Ti_1−xMo_xO_2−yN_y samples are anatase phase. It is found that Mo, N mono-doping can increase visible light absorption, while (Mo + N) co-doping can greatly enhance absorption in whole visible region. Results of our first-principles band structure calculations reveal that (Mo + N)-doping, especially passivated co-doping can increase the up-limit of dopant concentration and create more impurity bands in the band gap of TiO₂, which leads to a greatly increase of its visible-light absorption without a decrease of its redox potential. It reveals that (Mo + N) co-doped TiO₂ is promising for a photocatalyst with high photocalystic activity under visible light.     

Structural, electrical and optical properties of TiO2 doped WO3 thin films

TiO₂ doped WO₃ thin films were deposited onto glass substrates and fluorine doped tin oxide (FTO) coated conducting glass substrates, maintained at 500 °C by pyrolytic decomposition of adequate precursor solution. Equimolar ammonium tungstate ((NH₄)₂WO₄) and titanyl acetyl acetonate (TiAcAc) solutions were mixed together at pH 9 in volume proportions and used as a precursor solution for the deposition of TiO₂ doped WO₃ thin films. Doping concentrations were varied between 4 and 38%. The effect of TiO₂ doping concentration on structural, electrical and optical properties of TiO₂ doped WO₃ thin films were studied. Values of room temperature electrical resistivity, thermoelectric power and band gap energy (E_g) were estimated. The films with 38% TiO₂ doping in WO₃ exhibited lowest resistivity, n-type electrical conductivity and improved electrochromic performance among all the samples. The values of thermoelectric power (TEP) were in the range of 23-56 μV/K and the direct band gap energy varied between 2.72 and 2.86 eV.     

Photocatalytic reduction of oxygen molecules at the (1 0 0) TiO2 anatase surface

The adsorption, photoreduction and chemical activity of oxygen molecules on the (1 0 0) anatase surface have been investigated here together with the effects that surface oxygen vacancies (V_O) can have on these O₂-related processes. We use an original approach by treating molecules on the TiO₂ surface like surface defects in the same framework successfully used for defects in semiconductors. The achieved results: (i) give the first theoretical evidence of an acceptor behaviour of an adsorbed O₂ molecule, which is at the origin of its photoreduction; (ii) show that the V_O donor character is strongly affected by the interaction with O₂; and (iii) suggest that the release of radicals as well as the formation of O₂-related radicals may be favoured by photogenerated electrons in presence of surface V_O’s.     

Effect of TiO2/Al2O3 film coated diamond abrasive particles by sol-gel technique

The diamond abrasive particles were coated with the TiO₂/Al₂O₃ film by the sol-gel technique. Compared with the uncoated diamonds, the TiO₂/Al₂O₃ film was excellent material for the protection of the diamonds. The results showed that the incipient oxidation temperature of the TiO₂/Al₂O₃ film coated diamonds in air atmosphere was 775 °C, which was higher 175 °C than that of the uncoated diamonds. And the coated diamonds also had better the diamond's single particle compressive strength and the impact toughness than that of uncoated diamonds after sintering at 750 °C. For the vitrified bond grinding wheels, replacing the uncoated diamonds with the TiO₂/Al₂O₃ film coated diamonds, the volume expansion of the grinding wheels decreased from 6.2% to 3.4%, the porosity decreased from 35.7% to 25.7%, the hardness increased from 61.2H_RC to 66.5H_RC and the grinding ratio of the vitrified bond grinding wheels to carbide alloy (YG8) increased from 11.5 to 19.1.     

Epitaxial MoOx nanostructures on TiO2(1 1 0) obtained using thermal decomposition of Mo(CO)6

Stoichiometric and highly-defective TiO₂(1 1 0) surfaces (called as yellow and blue, respectively) were exposed to Mo(CO)₆ vapours in UHV and in a reactive O₂ atmosphere. In the case of yellow-TiO₂, an O₂ reactive atmosphere was necessary to obtain the Mo(CO)₆ decomposition at 450 °C with deposition of MoO_x nanostructures where, according to core level photoemission data, the Mo⁺⁴ state is predominant. In the case of blue-TiO₂ it was possible to obtain Mo deposition both in UHV and in an O₂ atmosphere. A high dose of Mo(CO)₆ in UHV on blue-TiO₂ allowed the deposition of a thick metallic Mo layer. An air treatment of this sample at 580 °C led to the elimination of Mo as MoO₃ and to the formation of a transformed layer of stoichiometry of Ti_(1−x)Mo_xO₂ (where x is close to 0.1) which, according to photoelectron diffraction data, can be described as a substitutional near-surface alloy, where Mo⁺⁴ ions are embedded into the titania lattice. This embedding procedure results in a stabilization of the Mo⁺⁴ ions, which are capable to survive to air exposure for a rather long period of time. After exposure of the blue-TiO₂(1 1 0) substrate to Mo(CO)₆ vapours at 450 °C in an O₂ atmosphere it was possible to obtain a MoO₂ epitaxial ultrathin layer, whose photoelectron diffraction data demonstrate that is pseudomorphic to the substrate.     

A photoemission study of molybdenum hexacarbonyl adsorption and decomposition on TiO2(1 1 0) surface

The adsorption and decomposition of molybdenum hexacarbonyl on (1 1 0) TiO₂ surfaces were studied using both core levels and valence band photoemission spectroscopies. It was found that after an adsorption at 140 K, when going back to room temperature, only a small part of molybdenum compounds, previously present at low temperature, remained on the TiO₂ surface. This indicates that the desorption temperature on such a surface is lower than the decomposition one. The use of photon irradiation to decompose the hexacarbonyl molecule was also studied. It was shown that during such a decomposition molecular fragments were chemisorbed on the surface allowing a higher amount of metal to remain on the surface. It was also shown that it was possible to get rid of adsorbed subcarbonyl groups and to organize the metal atoms by thermal treatments at temperatures as low as 400 K, i.e. much lower than the one needed to obtain the same structures using physical vapour deposition (PVD). Moreover, due to lower used temperatures, this chemical way of deposition allows a better control of the interface than during PVD growth.     

Molecular dynamics study on surface structure and surface energy of rutile TiO2 (1 1 0)

The formula for surface energy was modified in accordance with the slab model of molecular dynamics (MDs) simulations, and MD simulations were performed to investigate the relaxed structure and surface energy of perfect and pit rutile TiO₂(1 1 0). Simulation results indicate that the slab with a surface more than four layers away from the fixed layer expresses well the surface characteristics of rutile TiO₂ (1 1 0) surface; and the surface energy of perfect rutile TiO₂ (1 1 0) surface converges to 1.801±0.001 J m⁻². The study on perfect and pit slab models proves the effectiveness of the modified formula for surface energy. Moreover, the surface energy of pit surface is higher than that of perfect surface and exhibits an upper-concave parabolic increase and a step-like increase with increasing the number of units deleted along [0 0 1] and [1 1 0], respectively. Therefore, in order to obtain a higher surface energy, the direction along which atoms are cut out should be chosen in accordance with the pit sizes: [] direction for a small pit size and [0 0 1] direction for a big pit size; or alternatively the odd units of atoms along [1 1 0] direction are removed.     

Synthesis and photocatalytic properties of porous TiO2 films prepared by ODA/sol-gel method

Porous TiO₂ films were deposited on SiO₂ pre-coated glass-slides by sol-gel method using octadecylamine (ODA) as template. The amount of ODA in the sol played an important role on the physicochemical properties and photocatalytic performance of the TiO₂ films. The films prepared at different conditions were all composed of anatase titanium dioxide crystals, and TiO₂ crystalline size got larger with increasing ODA amount. The maximum specific surface area of 41.5 m²/g was obtained for TiO₂ powders prepared from titanium sol containing 2.0 g ODA. Methyl orange degradation rate was enhanced along with increasing ODA amount and reached the maximal value at 2.0 g addition of ODA. After 40 min of UV-light irradiation, methyl orange degradation rate reached 30.5% on the porous film, which was about 10% higher than that on the smooth film. Porous TiO₂ film showed almost constant activity with slight decrease from 30.5% to 28.5% after 4 times of recycles.