CdSe nanoparticles stabilized with the amphiphilic diblock copolymer polystyrene‐block‐poly(4‐vinylpyridine) were spread from toluene dispersion on the water surface. Monolayers could be transferred onto solid substrates using the Langmuir‐Blodgett technique. By means of atomic force and scanning electron microscopy highly symmetric ring and disk‐like structures with diameters ranging between 150 nm and 1200 nm were observed.
AFM image of a mixed monolayer of copolymer 12 and CdSe nanoparticles stabilized with polystyrene‐block‐poly(4‐vinylpyridine). 相似文献
Summary: Tetraaniline‐block‐poly(L ‐lactide) diblock oligomers are synthesized via ring‐opening polymerization. The diblock oligomers cast from an L ‐lactide selective solvent (chloroform) show spherical aggregates for the leucoemeraldine state, and ring‐like structures that are composed of much smaller spherical aggregates for the emeraldine state. The formation mechanisms of the two different surface morphologies are discussed in detail.
Surface morphology changes induced by oxidation of the aniline segment of tetraaniline‐block‐poly(L ‐lactate) and drying effects. 相似文献
This paper aims to report the fabrication of biodegradable thin films with micro‐domains of cylindrical nanochannels through the solvent‐induced microphase separation of poly(L ‐lactide)‐block‐poly(ethylene glycol)‐block‐poly(L ‐lactide) (PLA‐b‐PEG‐b‐PLA) triblock copolymers with different block ratios. In our experimental scope, an increase in each of the block lengths of the PLA and PEG blocks led to both a variation in the average number density (146 to 32 per 100 µm2) and the size of the micro‐domains (140 to 427 nm). Analyses by atomic force microscopy (AFM) and fluorescence microscopy indicated that the hydrophilic PEG nanochannels were dispersed in the PLA matrix of the PLA‐b‐PEG‐b‐PLA films. We demonstrated that the micro‐domain morphology could be controlled not only by the block length of PEG, but also by the solvent evaporation conditions.
A dielectric elastomer derived from a polystyrene‐block‐poly(ethylene‐co‐butylene)‐block‐polystyrene triblock copolymer swollen with a midblock‐selective solvent is reported to show promise as a nanostructured organic actuator requiring no pre‐strain. This might provide an attractive alternative to conventional acrylic, siloxane, and polyurethane elastomers since the electromechanical properties are composition‐tunable.
Here, we show that a poly(ethylene oxide) polymer can be physically cross‐linked with silicate nanoparticles (Laponite) to yield highly extensible, bio‐nanocomposite fibers that, upon pulling, stretch to extreme lengths and crystallize polymer chains. We find that both, nanometer structures and mechanical properties of the fibers respond to mechanical deformation by exhibiting strain‐induced crystallization and high elongation. We explore the structural characteristics using X‐ray scattering and the mechanical properties of the dried fibers made from hydrogels in order to determine feasibility for eventual biomedical use and to map out directions for further materials development.
We propose a theoretical explanation of the parallel and perpendicular lamellar orientations in free surface films of symmetric polystyrene‐block‐polybutadiene diblock copolymers on silicon substrates (with a native SiOx layer). Two approaches are developed: A correction to the strong segregation theory and a qualitative analysis of the intermediate segregation regime. We show that the perpendicular orientation of the lamellae formed by the molecules of high molecular weight is stabilized by A–B interfacial interactions. They are weaker in the case of the perpendicular orientation of the lamellae, whereas the surface tension coefficient of the A–B interface decreases with the increase of the molecular weight.
Poly(N‐isopropylacrylamide)‐block‐poly{6‐[4‐(4‐pyridyazo)phenoxy] hexylmethacrylate} (PNIPAM‐b‐PAzPy) was synthesized by successive reversible addition‐fragmentation chain transfer (RAFT) polymerization. In a water/tetrahydrofuran (H2O/THF) mixture, amphiphilic PNIPAM‐b‐PAzPy self‐assembles into giant micro‐vesicles. Upon alternate ultraviolet (UV) and visible light irradiation, obvious reversible swelling‐shrinking of the vesicles was observed directly under an optical microscope. The maximum percentage increase in volume, caused by the UV light, reached 17%. Moreover, the swelling could be adjusted using the UV light power density. The derivation of this effect is due to photoinduced reversible isomerization of azopyridine units in the vesicles.
Summary: Plasma‐initiated controlled/living radical polymerization of methyl methacrylate (MMA) was carried out in the presence of 2‐cyanoprop‐2‐yl 1‐dithionaphthalate. Well‐defined poly(methyl methacrylate) (PMMA), with a narrow polydispersity, could be synthesized. The polymerization is proposed to occur via a RAFT mechanism. Chain‐extension reactions were also successfully carried out to obtain higher molecular weight PMMA and PMMA‐block‐PSt copolymer.
Dependence of ln([M]0/[M]) on post‐polymerization time (above), and \overline M _{\rm n} and PDI against conversion (below) for plasma initiated RAFT polymerization of MMA at 25 °C. 相似文献
Regioregular poly(3‐hexylthiophene) has been successfully incorporated into a novel amphiphilic block copolymer. The amphiphilic nature of poly(3‐hexylthiophene)‐block‐poly(acrylic acid) has been investigated using spectroscopic methods and has yielded solvatochromic behavior in several solvents of varying polarity. Evidence suggests that a supramolecular, long range ordering of block copolymer occurs in polar solvents, resulting in the formation of aggregates. Despite relatively large amounts of non‐conductive blocks, the poly(3‐hexylthiophene) diblock copolymer yields a high conductivity of 1 S · cm−1, and atomic force microscopy shows the formation of a highly organized nanofibrilar morphology in the solid state.
Well‐defined diblock copolymers composed of poly(N‐octylbenzamide) and polystyrene were synthesized by reversible addition‐fragmentation chain transfer (RAFT) polymerization of styrene with a polyamide chain transfer agent (CTA) prepared via chain‐growth condensation polymerization. Synthesis of a dithioester‐type macro‐CTA possessing the polyamide segment as an activating group was unsatisfactory due to side reactions and incomplete introduction of the benzyl dithiocarbonyl unit. On the other hand, a dithiobenzoate‐CTA containing poly(N‐octylbenzamide) as a radical leaving group was easily synthesized, and the RAFT polymerization of styrene with this CTA afforded poly(N‐octylbenzamide)‐block‐polystyrene with controlled molecular weight and narrow polydispersity.
Magnetic nanomaterials have been studied in order to generate novel nanocomposites that display both the magnetic properties of the nanoparticles and the ability to self‐assemble of the amorphous block copolymer matrix. Towards this goal, iron oxide magnetic nanoparticles have been modified with PS brushes by ATRP in order to improve both the dispersion and the affinity of the nanoparticles with one of the blocks of a polystyrene‐block‐polybutadiene‐block‐polystyrene block copolymer. This method of preparation of nanocomposites opens new strategies for the generation of magnetic nanomaterials. The samples are characterized using DSC and atomic and magnetic force microscopies.
Summary: Experimental and modeling studies of addition–fragmentation chain transfer (AFCT) during radical polymerization of methyl methacrylate in the presence of poly(methyl methacrylate) macromonomer with 2‐carbomethoxy‐2‐propenyl ω‐ends (PMMA‐CO2Me) at 60 °C are reported. The results revealed that AFCT involving PMMA‐CO2Me formed in situ during methyl methacrylate polymerization has a negligible effect on the molecular weight distribution.
A novel approach is employed to produce core–corona nanospheres, which introduces a stereoregular hydrophilic part to an amphiphilic block copolymer. The resultant morphology is reported using isotactic‐poly(methacrylic acid)‐block‐poly(butyl acrylate). Infrared spectroscopy revealed a supramolecular interaction, and X ray diffraction revealed the crystallization of the outer isotactic‐poly(methacrylic acid) part. The nanostructure, which looks like a nanosized ‘grape’, was formed when nanospheres and nanofibers coexisted simultaneously and partially fused.
Aliphatic polyesters containing thioester linkages were enzymatically prepared by both the copolymerization of lactone with mercaptoalkanoic acid and by the transesterification of polyesters with mercaptoalkanoic acids. The enzymatic copolymerization of ε‐caprolactone with 11‐mercaptoundecanoic acid (11MU) and 3‐mercaptopropionic acid (3MP) was performed under reduced pressure using an immobilized lipase from Candida antarctica (CA). The transesterification of poly(ε‐caprolactone) and poly[(R)‐3‐hydroxybutyrate] was carried out with 11MU and 3MP using lipase CA under reduced pressure.
The carbon nitride poly(triazine imide) with intercalated bromide ions is a layered, graphitic material of 2D covalently bonded molecular sheets with an exceptionally large gallery height of 3.52 Å due to the intercalated bromide anions. The material can be cleaved both mechanically and chemically into thin sheets and scrolls analogous to the carbon‐only systems graphite and graphene.
A new synthesis of amphiphilic biodegradable copolymers consisting of hydrophobic poly(3‐hydroxyalkanoate) (PHA) backbone and hydrophilic poly(ethylene glycol) (PEG) units as side chains is described. Poly[(3‐hydroxyoctanoate)‐co‐(3‐hydroxyundecenoate)] (PHOU) was first methanolyzed and its unsaturated side chains were quantitatively oxidized to carboxylic acid. Esterification with propargyl alcohol led to an alkyne‐containing “clickable” PHA in 71% conversion. Its reactivity was successfully demonstrated by grafting azide‐terminated PEG chains of 550 and 5 000 g · mol−1, respectively. All products were fully characterized using GPC, 1H, and COSY NMR.
A novel helical poly(macromonomer) [poly(M‐PS): absolute = 82 800–252 000, determined by GPC/RALLS] with a polyacetylene main chain and polystyrene (PS) side chains was synthesized by the polymerization of acetylene‐terminated M‐PS [ = 2 000, / = 1.20, = 18] with an Rh catalyst. M‐PS was prepared by ATRP of styrene using the acetylene‐containing initiator 2‐bromo‐2‐methylpropionic acid (S)‐1‐methylpropargyl ester ( l ). In solutions, poly(M‐PS) exhibited an intense CD signal at 345–355 nm, indicating that it possessed a predominantly one‐handed helical conformation. Poly(M‐PS) had a stable helical conformation irrespective of solvents and temperature.
A polymer system based on polydiacetylene (PDA) supramolecules that emits red, green, and blue fluorescence has been constructed. The three‐color emitting system is comprised of red‐fluorescent PDA vesicles in which green‐fluorescent fluorescein molecules are encapsulated. Finally, the blue‐fluorescence component is introduced by reacting terminal amine groups on the PDA vesicle surfaces with fluorescamine. Thin PDA‐polymer‐containing poly(vinyl alcohol) films formed by using this strategy display red, green, and blue fluorescence upon excitation with light at specific wavelengths.