Surface modifications of PET in argon atmospheric pressure plasma: Gas flow rate effect

The correlation between plasma optical properties and the treated polyethylene terephthalate (PET) surface characteristics have been studied at various Ar flow rate. The rotational T_rot and vibrational T_vib temperatures of APPJ were determined from SPS emission band. The pristine and plasma-treated PET surfaces were characterized by several techniques including X-ray photoelectrons spectroscopy (XPS), Raman spectroscopy, contact angle (CA), and atomic force microscope (AFM). The CA decreased rapidly in the flow rate range 1–3 L/min and weakly dependent as flow rate > 3 L/min. XPS results showed that C 1s % of plasma-treated PET surfaces decreases and has a minimum for samples treated at 3–4 L/min, while O 1s has a maximum at the same flow rate range. The carbon C 1s peak of pristine and plasma treated PET samples resolved into five subcomponents: C–C, C–O, C=O, O–C=O, and π–π bonds with variable percentage ratio accordance to the plasma gas flow rate. Raman data revealed a partial loss in the crystallinity of the treated PET samples and also confirm the incremental of C–O band at Ar flow rate of 3 L/min. AFM images showed that the surface roughness of treated PET films increases as Ar flow rate increases.     

Surface modification of titanium with thermally treated polydimethylsiloxane coating and the effect on resin to titanium adhesion

In this study, titanium surface modification by a thermal treatment using a polydimethylsiloxane (PDMS) coating was investigated. The surfaces of four titanium samples were surface treated by polishing, sandblasting, and coating with a PDMS with a thermal treatment at 800 and 1100 °C. The titanium surfaces were characterized by X‐ray photoelectron spectroscopy (XPS) and atomic force microscopy. The effect of the surface treatments on adhesion of resin to titanium was assessed by shear adhesion strength test. XPS analysis showed that there was a change of elemental composition of titanium surfaces after surface treatment. Binding energy shifts for Si2p and O1s were observed after sandblasting and thermally treated PDMS. Therefore, chemical states of Si and O were changed. Atomic force microscopy analysis revealed that the surface topography of the Ti samples was different, and surface roughness was increased after sandblasting and thermal treatment of PDMS coating. Shear adhesion strength test results showed that the adhesion between resin and titanium is affected by the treatment temperature of PDMS coating. The highest adhesion is obtained at 1100 °C (14.7 ± 1.57 MPa). Copyright © 2014 John Wiley & Sons, Ltd.     

Effect of thermal dehydration and rehydration on Na-magadiite structure

The effect caused by dehydration and rehydration of the synthetic Na-magadiite was investigated by TGA, XRD, SEM, and ²⁹Si NMR. Thermal analysis of Na-magadiite presented two well-defined loss mass stages between 20 and 150 °C and another between 270 and 310 °C, both related to the removal of interlayer water. The swelling behavior of Na-magadiite was studied by thermal dehydration data obtained at 150 and 300 °C, and respective rehydration by water addition. X-ray patterns showed that the dehydration of Na-magadiite at 150 and 300 °C provoked the basal spacing decrease. The XRD also showed that only the material treated at 150 °C returned to the original structure with the rehydration. ²⁹Si NMR spectra showed that after rehydration, the Q₃/Q₄ relationship presented the same value for Na-magadiite treated at 150 °C. However, this Q₃/Q₄ value decreased when the treatment was done at 300 °C. Kinetic studies of thermal decomposition showed that the dehydration of magadiite is based on a phase boundary-controlled reaction, caused by contracting areas. The exfoliation of lamellas with thermal treatment can explain this behavior, as observed in SEM images.     

The influence of dodecylamine hydrochloride on the dissolution kinetics of heat-treated hydroxyapatite samples

The influence of dodecylamine hydrochloride (DAC) on the dissolution rate behavior of hydroxyapatite (HAP) samples prepared by digestion at 100°C and heated to various temperatures was investigated. The dissolution rates of HAP samples heated to temperatures of 300, 500, 750, 900, 1000, and 1200°C were determined at various levels of DAC in an acetate buffer having a pH of 4.50 and an ionic strength of 0.10. DAC adsorption isotherms for these different HAP samples and the specific surface areas were also determined. The initial dissolution rates (IDR) for all preparations generally decreased with increasing DAC levels with an approximately inverse relationship between IDR and DAC adsorption. For HAP samples heated at 1000°C and higher, the dissolution rates at 3.0 mM DAC were completely inhibited, while for samples heated at 900°C or less, there was a significant residual IDR at 3.0 mM DAC. This residual rate was approximately 20% of the zero DAC rate for all samples treated between 300 and 900°C. These results are in agreement with the concept that HAP prepared by precipitation and digestion at 100°C has two or more kinds of sites for dissolution and that heat treatment at around 1000°C or greater causes the elimination of one or more of these sites.     

Polyol-mediated synthesis of Li4Ti5O12 nanoparticle and its electrochemical properties

Li₄Ti₅O₁₂ nanoparticles were precipitated from ethylene glycol solution of titanium tetra isopropoxide (Ti(O-iPr)₄) and Li₂O₂ by refluxing at 197 °C for 12 h. The obtained particles were filtered and dried at 100 °C for 12 h, and the dried powder samples were heated at 320, 500 and 800 °C for 3 h. The X-ray diffraction patterns of the obtained samples exhibited a good fit with the spinel phase. The field emission-SEM images of the dried powder sample and the samples heated at 320, 500 and 800 °C for 3 h showed a uniform spherical morphology with a particle size of 5, 8, 10 and 400 nm, respectively. According to the results of electrochemical testing, the dried powder sample and the samples heated at 320, 500, and 800 °C for 3 h showed initial capacities of 200, 310, 320, and 260 mA h/g, respectively, at a current density of 0.05 mA/cm². Nanosized (6–8 nm) particles with good crystallinity were obtained by controlling the synthesis conditions. The sample heated at 500 °C for 3 h exhibited a high capacity and an excellent rate capability over 60 cycles.     

Surface modification of polyester by oxygen‐ and nitrogen‐plasma treatment

In this paper, we present a study on the surface modification of polyethyleneterephthalate (PET) polymer by plasma treatment. The samples were treated by nitrogen and oxygen plasma for different time periods between 3 and 90 s. The plasma was created by a radio frequency (RF) generator. The gas pressure was fixed at 75 Pa and the discharge power was set to 200 W. The samples were treated in the glow region, where the electrons temperature was about 4 eV, the positive ions density was about 2 × 10¹⁵ m^?3, and the neutral atom density was about 4 × 10²¹ m^?3 for oxygen and 1 × 10²¹ m^?3 for nitrogen. The changes in surface morphology were observed by using atomic force microscopy (AFM). Surface wettability was determined by water contact angle measurements while the chemical composition of the surface was analyzed using XPS. The stability of functional groups on the polymer surface treated with plasma was monitored by XPS and wettability measurements in different time intervals. The oxygen‐plasma‐treated samples showed much more pronounced changes in the surface topography compared to those treated by nitrogen plasma. The contact angle of a water drop decreased from 75° for the untreated sample to 20° for oxygen and 25° for nitrogen‐plasma‐treated samples for 3 s. It kept decreasing with treatment time for both plasmas and reached about 10° for nitrogen plasma after 1 min of plasma treatment. For oxygen plasma, however, the contact angle kept decreasing even after a minute of plasma treatment and eventually fell below a few degrees. We found that the water contact angle increased linearly with the O/C ratio or N/C ratio in the case of oxygen or nitrogen plasma, respectively. Ageing effects of the plasma‐treated surface were more pronounced in the first 3 days; however, the surface hydrophilicity was rather stable later. Copyright © 2008 John Wiley & Sons, Ltd.     

The effect of heat treatment of PES and PVDF ultrafiltration membranes on morphology and performance for milk filtration

The flat sheet polyethersulfone (PES) and poly(vinylidene fluoride) (PVDF) membranes were prepared by immersion precipitation technique. The influence of hot air and water treatment on morphology and performance of membranes were investigated. The membranes were characterized by AFM, SEM, cross-flow filtration of milk and fouling analysis. The PES membrane turns to a denser structure with thick skin layer by air treatment at various temperatures during different times. This diminishes the pure water flux (PWF). However the milk permeation flux (MPF) was considerably improved at 100 °C air treatment for 20 min with no change in protein rejection. The smooth surface and slight decrease in surface pore size for air treated PES membrane at 100 °C compared to untreated membrane may cause this behavior for the membrane. The water treatment of PES membranes at 55 and 75 °C declines the PWF and MPF and increases the protein rejection. This is due to slight decrease in membrane surface pore size. The treatment of PES membrane with water at higher temperature results in a porous structure with superior performance. The fouling analysis of 20 min treated membrane indicates that the surface properties of 100 °C air treated and 95 °C water treated PES membranes are improved compared to untreated membrane. The SEM observation depicts that the morphology of air and water treated PVDF membranes was denser and smoother with increasing the heat treatment temperature. The 20 min air treated PVDF membranes at 100 °C and water treated at 95 °C exhibited the highest performance and antifouling properties.     

Electrothermal Atomic Absorption Determination of Chromium in Sediments

An electrothermal atomic absorption spectrometric method has been developed to determine total chromium concentration in natural sediment samples. Samples were mineralized by dry ashing at 550°C and fused at 1100°C for 30 min with lithium metaborate. Dissolved samples were injected in graphite tubes, mineralized at 1100°C, and atomized at 2600°C. Standard addition calibration made unnecessary the use of chemical modifiers. The method provided a limit of detection from 23 to 45 ng liter⁻¹. The relative standard deviation for chromium determination was between 3 and 14%. Results obtained for a standard reference material agree well with the certified value. A series of natural samples were analyzed by the developed procedure and also directly by neutron activation analysis without any pretreatment and comparable results were obtained by both procedures.     

甲醇气相羰基化Ni-Pd/AC催化剂失活机理的研究

采用连续流动固定床反应装置,Ni Pd/AC为催化剂,在260℃、1.5MPa、CO/CH3OH/CH3I摩尔比为20/19/1、W/F为7.5g·h·mol－1下考察了催化剂的稳定性,并对失活前、后Ni-Pd/AC催化剂进行了比表面积、热解-红外分析（Py FTIR）和XPS表征。结果表明,反应初期反应产物乙酸或乙酸甲酯与催化剂之间强吸附堵塞了催化剂孔道,导致扩散受到限制。随着反应时间的延长,羰基化活性中心Ni不断迁移并富集在催化剂表面上,使Ni晶粒增大,成为积炭的活性中心,积炭堵塞了催化剂孔道,导致催化剂失活。进一步对积炭类型进行研究,发现形成的碳物种主要是类石墨型碳。     

Preparation and electrocatalytic activities of platinum nanoclusters deposited on modified multi-walled carbon nanotubes supports

Multi-walled carbon nanotubes (MWNTs) were modified by oxyfluorination treatment at several different temperatures of 20, 100, 200, and 300 °C. The changes of surface properties of oxyfluorinated MWNTs were investigated using X-ray photoelectron spectroscopy (XPS) method. As a result, it was found that surface fluorine contents were varied with changing an oxyfluorination temperature and showed a maximum value at 100 °C. By changing the treatment temperature in the process of oxyfluorination for carbon supports, the surface characteristics of MWNTs had been modified, resulting that the size and loading content of deposited Pt on the modified carbon supports could be changed. Consequently, Pt deposited MWNTs that were treated at 100 °C (Pt/100-MWNTs) showed the best electroactivity among samples. The enhanced electroactivity was dependent on the higher surface area of electrochemical reaction for metal catalyst, which was related to the particle size and the morphology of the deposited particle catalysts.     

Cobalt–silicon mixed oxide nanocomposites by modified sol–gel method

Cobalt–silicon mixed oxide materials (Co/Si=0.111, 0.250 and 0.428) were synthesised starting from Co(NO₃)₂·6H₂O and Si(OC₂H₅)₄ using a modified sol–gel method. Structural, textural and surface chemical properties were investigated by thermogravimetric/differential thermal analyses (TG/DTA), XRD, UV–vis, FT-IR spectroscopy and N₂ adsorption at −196 °C. The nature of cobalt species and their interactions with the siloxane matrix were strongly depending on both the cobalt loading and the heat treatment. All dried gels were amorphous and contained Co²⁺ ions forming both tetrahedral and octahedral complexes with the siloxane matrix. After treatment at 400 °C, the sample with lowest Co content appeared amorphous and contained only Co²⁺ tetrahedral complexes, while at higher cobalt loading Co₃O₄ was present as the only crystalline phase, besides Co²⁺ ions strongly interacting with siloxane matrix. At 850 °C, in all samples crystalline Co₂SiO₄ was formed and was the only crystallising phase for the nanocomposite with the lowest cobalt content. All materials retained high surface areas also after treatments at 600 °C and exhibited surface Lewis acidity, due to cationic sites. The presence of cobalt affected the textural properties of the siloxane matrix decreasing microporosity and increasing mesoporosity.     

Structure Evolution Process of Ce0.65Zr0.25Y0.1O1.95 Prepared by Oxidation-Coprecipitation Method

Ce_0.65Zr_0.25Y_0.1O_1.95 oxides were prepared by oxidation-coprecipitation method using ammonia and salvolatile as precipitators. The as-prepared samples were thermally treated at different temperatures and characterized by thermogravimetry-differential scanning calorimetry (TG-DSC), Fourier transform-infrared (FT-IR) spectrometry, X-ray diffraction (XRD), and specific surface area measurements (BET). The results showed that the hydroxyl and carboxyl groups coexisted in the precipitate and a perfect solid solution was gradually formed with an increase in calcination temperature. The physisorbed water was lost from 100 to 170 °C, hydroxyl groups were removed from 250 to 300 °C, and the carboxyl groups were eliminated from 420 to 500 °C. A structure model was further proposed to understand the Ce_0.65Zr_0.25Y_0.1O_1.95 structure evolution process in depth.     

Adsorption mechanism of Cu from aqueous solution by chitosan-coated magnetic nanoparticles modified with α-ketoglutaric acid

In order to better understand the adsorption mechanism of chitosan-coated magnetic nanoparticles modified with α-ketoglutaric acid (α-KA-CCMNPs), the removal of Cu²⁺ by α-KA-CCMNPs from aqueous solution was investigated in a batch system at 18, 35 and 50 °C. Different experimental approaches were applied to show mechanistic aspects, such as adsorption isotherms, kinetics and thermodynamics studies. Adsorption equilibrium studies showed that Cu²⁺ adsorption followed Langmuir model. The kinetics of the interactions was best described by pseudo-second-order mechanism. The thermodynamic parameters (ΔG°, ΔH° and ΔS°) analysis predicted that the adsorption process was strongly dependent on temperature of medium, and spontaneous and endothermic process. The XPS combined with FT-IR spectra revealed that N atom of –NH– group and O atom of carboxyl group in α-KA-CCMNPs coordinated with Cu²⁺. Experimental results from this study provide data that would be required if this heavy metal adsorption system was to be “scaled up” for industrial application.     

Catalytic methanol decomposition to carbon monoxide and hydrogen over Pd/CeO2-ZrO2-La2O3 with different Ce/Zr molar ratios

The catalytic behaviors of Pd (1.4 wt%) catalysts supported on CeO₂-ZrO₂-La₂O₃ mixed oxides with different Ce/Zr molar ratios were investigated for methanol decomposition. Nitrogen adsorption-desorption (BET), X-ray photoelectron spectroscopy (XPS), H₂ temperature-programmed reduction (H₂-TPR), X-ray diffraction (XRD) and Pd dispersion analysis were used for their characterization. Pd/Ce_0.76Zr_0.18 La_0.06O_1.97 catalyst showed the highest BET surface area, best Pd dispersion capability and strongest metal-support interaction. Moreover, XPS showed that there was lattice defect oxygen or mobile oxygen. According to the result of O 1s measurements the lattice defect oxygen or mobile oxygen helped to maintain Pd in a partly oxidized state and increased the activity for methanol decomposition. The Pd/Ce_0.76Zr_0.18La_0.06O_1.97 catalyst exhibited the best activity. A 100% conversion of methanol was achieved at around 260 °C, which was about 20-40 °C lower than other catalysts     

A facile preparation of nanocrystalline Mo2C from graphite or carbon nanotubes

Nanocrystalline Mo₂C powders were successfully synthesized at 500 °C by reacting molybdenum chloride (MoCl₅) with C (graphite or carbon nanotube) in metallic sodium medium. X-ray powder diffractometer (XRD), transmission electron microscope (TEM), X-ray photoelectron spectroscope (XPS) and surface area analyzer (BET method) were used to characterize the samples. Experiments reveal that the carbon source used for the carbide synthesis has a great effect on the particle size and the surface area of the samples. When micro-sized graphite was used as C source the obtained nanocrystalline Mo₂C powder consists of particles of 30∼100 nm, with a surface area of 2.311 m²/g. When carbon nanotubes were used as C source, the as-synthesized Mo₂C sample is composed of particles of 20∼50 nm, with a surface area of 23.458 m²/g, which is an order of magnitude larger than that of the carbide prepared from the graphite.     

A novel method of surface modification on thin-film-composite reverse osmosis membrane by grafting hydantoin derivative

Membrane degradations by biofouling and free chlorine oxidation are the major obstacles for aromatic polyamide thin-film-composite (TFC) reverse osmosis (RO) membranes to realize high performance over a long period of operation. In this work, a hydantoin derivative, 3-monomethylol-5,5-dimethylhydantoin (MDMH), was grafted onto the nascent aromatic polyamide membrane surfaces by the reactions with active groups (e.g., acyl chloride groups) in the surfaces. The grafted MDMH moieties with high reaction activity and free chlorine could play as sacrificial pendant groups when membranes suffer from chlorine attacks, and the chlorination products N-halamines with strong antimicrobial function could sterilize microorganisms on membrane surfaces and then regenerate to MDMH. This was designed as a novel means to improve both chlorine resistances and anti-biofouling properties of the aromatic polyamide TFC RO membranes.Attenuated total reflectance mode Fourier transform infrared spectroscopy (ATR-FTIR) revealed that the MDMH-modified membranes had two characteristic bands at 1772 and 1709 cm⁻¹ corresponding to two carbonyl groups in hydantoin ring. This suggested the successful grafting of MDMH onto the membrane surfaces, which was further confirmed and quantified by X-ray photoelectron spectroscopy (XPS) analysis. After modification with MDMH, the membrane surface hydrophilicity increased obviously as contact angles decreased from 57.7° to 50.4–31.5°. But, there was no obvious change in membrane surface roughness after modification. The MDMH-modified membranes were shown to possess high chlorine resistances with small changes in water fluxes and salt rejections after chlorination with 100–2000 ppm h chlorine at pH 4. The chlorinated MDMH-modified membranes demonstrated obvious sterilization effects on Escherchia coli and substantial preventions against microbial fouling. Therefore, the MDMH-modified membranes offer a potential use as a new type of chlorine resistance and anti-biofouling TFC RO membranes.     

Oxidation of propane over substituted Keggin phosphomolybdate salts

Ammonium salts, (NH₄)₆HPMo₁₁MO₄₀ (M = Ni, Co, Fe), have been investigated for the oxidation of propane, with molecular oxygen, at temperature ranging between 380 °C and 420 °Cafter in-situ pre-treatment performed at two heating rate of 5 or 9 °C/min. They were characterized by BET method, XRD, ³¹P NMR, UV-Vis and IR techniques. The catalysts were found active in the propane oxidation and selective to propene or acrolein, in particular for samples pre-treated with the heating rate of 9 °C/min.     

Chromium doped γ-Al2O3 powders. Features of the electrical double layer and state of the surface species

γ-Al₂O₃ samples, both pure and Cr doped, were prepared by heating at 470°C sol–gel precursors obtained by using aluminum tri-sec-butoxide [Al(OC₄H₉)₃] as the starting compound. The samples were characterised for phase composition (X-ray diffraction) and surface area (BET). Electrochemical determinations of the double layer reactivity of the pure and doped oxides were performed both by surface charge and by electrokinetic sonic amplitude (ESA) determinations. The interfacial electrostatic response is discussed and analysed also with reference to the sample surface state obtained by X-ray photoelectron spectroscopy (XPS).     

Low energy electron diffraction and cyclic voltammetry studies of flame-annealed platinum single crystals

Low energy electron diffraction (LEED) and cyclic voltammetry were used to examine the surface structure of flame-annealed platinum (100), (110), and (111) electrodes. Well-defined LEED patterns were obtained for these surfaces but only after heat treatment in vacuo at 400°C in order to remove surface contaminants. The cyclic voltammograms correspond to those expected for these low index platinum surfaces from prior studies.     

Preparation and characterization of the catalytically active forms of rare earth oxides

Catalytically active forms of the rare earth oxides Ln₂O₃(Ln = La, Sm, Eu, Dy, Ho, and Yb), Pr₆O₁₁, and CeO₂ have been prepared. The dehydration behavior of the precursors of these oxides has been studied by XRD, TG, DTA, TPD-MS, IR, and adsorption-desorption isotherms of N₂ at −196°C. Thermal analyses show that in most cases the dehydration takes place through an intermediate oxyhydroxide LnO (OH) that decomposes to the respective oxide at around 400°C. Strongly held difficult to remove carbonates were present on the surface, e.g., for Yb₂O₃ it was necessary raise the outgassing temperature to 700°C to achieve carbonate decomposition. At temperatures around 500°C these oxides are well crystallized and have moderate specific surface areas (10–40 m²g⁻¹). As a representative of the series, a detailed study of the dehydration and surface decarbonation of Yb₂O₃ was carried out by means of TPD-MS and infrared spectroscopy.