钛表面含硅羟基磷灰石涂层的电化学合成和表征

在含有Ca2+,PO43-以及SiO32-的电解液中,通过电化学恒电位方法,在工作电压为3 V温度为85℃的条件下沉积1 h,于钛表面上制得含硅羟基磷灰石涂层。通过电感耦合等离子体原子发射光谱(ICP)、扫描电镜(SEM)、X-射线衍射(XRD)、探针式轮廓仪(SP)、红外光谱(FTIR)对涂层进行分析。结果表明:电化学恒电位方法可制得Si饱和含量为0.55wt%左右的Si-HA涂层,Si以SiO44-形式取代PO43-进入HA晶格,造成羟基磷灰石中OH-减小以维持电荷平衡。另外,电解液中Si元素的存在抑制涂层中HA晶体的生长,使涂层变薄,且当电解液中nSi/(nSi+nP)达到20%时Si-HA晶体形貌由单独的棒状转变为根部相连的树枝状。     

吡咯聚合调控脉冲电沉积制备球形羟基磷灰石和银纳米粒子复合涂层

借助聚吡咯(PPy)的调控,采用脉冲电沉积法在生物医用金属钛表面制备出均匀的纳米HA/PPy/Ag抗菌复合涂层.考察了电解液中Py浓度、Ag~+浓度、钙磷盐浓度等对复合涂层的形貌及成分的影响.探讨了PPy聚合过程形成球形HA-NPs和Ag-NPs的形成机理,并对复合涂层的生物活性、生理稳定性及抗菌性能进行研究.研究结果表明,电解液中Py浓度的高低影响涂层的形貌,Py浓度为0.03 mol/L时有利于复合涂层的沉积.电解液中Ag~+浓度影响涂层的形貌、结晶,电解液中Ag~+浓度为0.3 mmol/L左右比较适合.电解液中Ca~(2+)浓度影响涂层的形貌及结晶,其浓度过高颗粒尺寸增大,Ca~(2+)浓度为5.0 mmol/L左右较适合.复合涂层能够诱导磷灰石的生成,使其沿着(002)晶面出现择优生长,具有较好的生物活性.PPy的加入大大降低了复合涂层中Ca~(2+)和Ag~+的释放速度,提高了复合涂层的生理稳定性.抗菌检测表明复合涂层具有良好的抗菌性.     

钛基多孔HA/SiO2复合涂层的制备及性能研究

为了制得表面多孔且与基材结合强度高的羟基磷灰石(HA)涂层,实验中以正丁醇为分散介质,以SiO2粉末为添加剂,纯钛片为基材,电泳沉积制备羟基磷灰石/二氧化硅/壳聚糖/(HA/SiO2/CS)复合涂层,经后续热处理得到多孔HA/SiO2复合涂层,采用扫描电镜(SEM)、傅立叶红外光谱仪(FT-IR)、X射线衍射仪(XRD)、万能材料试验机对涂层的表面形貌、组成、结构和结合强度进行测试和表征,并通过模拟体液(SBF)浸泡法对复合涂层的生物活性进行评价.结果表明:当悬浮液中的HA/SiO2/CS质量比为1∶1∶1时,制得的HA/SiO2/CS涂层经700℃热处理后获得的HA/SiO2复合涂层孔洞分布均匀,大孔孔径在10～15μm,小孔孔径在1～5μm;涂层与基材的结合强度达到25.5 MPa;多孔HA/SiO2复合涂层在SBF中浸泡7 d后,涂层表面碳磷灰石化;说明实验中添加SiO2所制得的多孔HA/SiO2复合涂层与钛基材结合强度高,且具有良好的生物活性.     

电诱导牙釉质表面羟基磷灰石涂层形成的研究

以含Ca(NO₃)₂、NH₄H₂PO₄和NaNO₃组成的溶液作为电解液,在人牙釉质表面电诱导制备了羟基磷灰石(HA)涂层。应用X射线衍射(XRD)﹑扫描电镜(SEM)和能谱分析(EDS)对形成涂层后的牙釉质样品进行分析和表征,研究了电解液初始pH值﹑电流密度和温度的变化对涂层的组成﹑结构和形貌的影响。研究结果表明这些因素对涂层的组分(HA)没有显著影响,而对涂层中HA晶体c轴的择优取向度的影响则较显著。当控制电解液的初始pH值为6﹑电流密度为0.5 mA·cm^-2﹑温度为55 ℃的时候,涂层中HA晶体沿c轴方向择优取向生长,且择优取向度和牙釉柱的HA较为接近。     

水热电沉积羟基磷灰石/Ti复合涂层的研究

在水热电沉积羟基磷灰石（Hydroxyapatite，简称HA）涂层的电解液中加入Ti粉，制备了HA/Ti复合涂层，探讨了Ti粉的加入对涂层结合强度和生物活性的影响，并研究了涂层的热稳定性。结果表明，500 ℃焙烧2 h后，HA/Ti复合涂层的结合强度为18.4 MPa，明显高于纯HA涂层的11.2 MPa；模拟体液浸泡7 d后，涂层表层形成一层碳磷灰石。Ti粉的加入明显提高了涂层的结合强度，又不降低涂层的生物活性。500 ℃焙烧不改变涂层的相组成，焙烧温度高于600 ℃时，HA部分发生分解，Ti氧化为金     

HA/CuO/SrCO3梯度复合涂层的制备及体外生物活性

在羟基磷灰石(HA)悬浮液中, 以正丁醇为分散介质, 三乙醇胺为乳化剂, 成骨微量元素化合物CuO 和SrCO₃作为添加剂, Ti片为基材, 壳聚糖(CS)为造孔剂, 依次通过区带电泳分布并在反向电场作用下电 泳沉积, 得到HA/CS/CuO/SrCO₃复合涂层, 经700 ℃高温煅烧2 h后, 制得HA/CuO/SrCO₃复合涂层. 通过X射线衍射(XRD)、 傅里叶变换红外光谱(FTIR)、 场发射扫描电子显微镜(FESEM)、 能量色散光谱仪(EDS)、 劳埃德万能材料试验机、 电化学工作站、 模拟体液培养和抑菌实验等手段对复合涂层进行测试与表征. 结果表明, Ca, Cu和Sr 元素含量在HA/CuO/SrCO₃复合涂层的径向上均呈现梯度分布; 复合涂层与钛基材的结合强度达33.0 MPa; 循环伏安(CV)曲线和Tafel极化曲线测试表明, 复合涂层在N-2-羟乙基哌嗪-N′-2-乙磺酸(HEPES)模拟体液(H-SBF)中电化学性能稳定, 耐腐蚀性较强; 在H-SBF中培养24 d后, 复合涂层表面完全碳磷灰石化; 抑菌实验发现, 复合涂层粉末对大肠杆菌和金黄色葡萄球菌的抑菌率分别为81.82%和71.86%.     

造孔剂对电泳沉积制备多孔HA涂层及其生物活性的影响

采用水热法制得的羟基磷灰石(HA)纳米粉体,分别与造孔剂葡萄糖(Glu)、壳聚糖(CS)、炭粉(C)3种微粒(＜38.5 μm)配置成质量比1∶1的悬浮液,电泳沉积 烧结制备钛基多孔HA涂层,并对制得的3种多孔HA涂层在模拟体液浸泡前后的表面形貌、化学组成及物相变化进行表征。 结果表明,经700 ℃烧结处理后制得的3种多孔HA涂层在1.5倍人体模拟体液中浸泡5 d后,多孔HA涂层表面均被层状生长的碳磷灰石颗粒完全覆盖,颗粒直径在5~25 μm,说明这些多孔HA涂层均具有良好的生物活性。 其中以CS为造孔剂制得的多孔HA涂层结合强度最高,达19.5 MPa,有望开发成为新型的人骨植入生物陶瓷材料。     

电化学共沉积HA/胶原复合涂层及其生物性能初探

应用电化学恒电流共沉积法在医用纯钛基底上制备羟基磷灰石(HA)/胶原(collagen)复合涂层.SEM和XPS等测试表明:复合涂层呈特定有序的纳-微米二级多孔结构,化学组分为HA和胶原的有机-无机复合.借助体外细胞的培养实验观察种植于不同材料表面的细胞贴壁及生长形态,显示电化学共沉积的复合涂层具有比纯HA或纯钛表面更好的生物相容性.     

羟基磷灰石/氧化铁复合涂层的制备及其诱导骨生长的生物活性

用电泳沉积法制得羟基磷灰石/壳聚糖/氧化铁(HA/CS/Fe2O3)复合涂层,经700 ℃烧结处理得到HA/Fe2O3复合涂层。 通过SEM、EDS、XRD、FT-IR、电化学和万能材料试验机等对复合涂层的表面形貌、物相组成、抗腐蚀性和结合强度进行了表征和测试,最后采用1.5SBF浸泡法对复合涂层的生物活性进行了评价。 结果表明,当悬浮液中的HA、CS与Fe2O3质量比为100∶100∶1时,所制得的HA/Fe2O3复合涂层表面粗糙,抗腐蚀性强,具有良好的诱导骨生长生物活性,基体与复合涂层结合强度可达27.5 MPa。     

水热电沉积羟基磷灰石涂层的研究

在0.0105mol/LCa(NO₃)₂,0.0063mol/LNH₄H₂PO₄,0.1mol/LNaNO₃,pH=4.6的电解液中,控制温度60～200℃,恒电流0.4mA/cm²,通过水热电沉积法制备羟基磷灰石涂层.实验结果表明,涂层晶体端面呈六边形棒状结构,涂层组分为缺钙磷灰石Ca_10-x(HPO₄)_x(PO₄)_6-x(OH)_2-x.经800℃烧结后涂层分解为HA和β-TCP的混合物.随温度升高,涂层n(Ca)/n(P)不断增大,涂层组分逐渐接近计量比的HA.涂层质量和结合强度随温度升高先增后减,在160℃时达到最大值16.7MPa     

Near infrared study of aqueous rare-earth ethylsulfates

The near infrared spectra of aqueous solutions of the ethylsulfates of La, Nd, Gd, Tb, Er, Yb, Lu, Y, and Na have been determined from about 0.2 mol-dm^–3 to nearly saturation. The extinction coefficients of water have been calculated taking into account the absorption of ethylslfate anions determined in separate experiments. Their values appeared to be nearly the same as that of pure water. The relative contents of free OH groups in 0.5 and 0.7M solutions have been estimated from the absorbances at 1160 nm. They were lower in solutions of the heavy rare-earth ethylsulfates (Tb, Er, Yb, Lu) than in equimolar solutions of the lighter ones (La, Nd), confirming our previous view that secondary hydration of the heavy trivalent rare-earth cations is distinctly stronger than that of the lighter ones. A comparison of the spectra of these aqueous ethylsulfates with those of perchlorates shows that the structure-breaking ability of the C₂H₅SO ₄ ^– ion is much smaller than that of perchlorate anion.     

Microstructures of Some Bi-W-Nb-O Phases

Microstructures of three Bi-W-Nb-O phases have been examined by using high-resolution transmission electron microscopy. Bi₁₇W₂Nb₃O₃₉ and Bi₁₇WNb₃O₃₆ have incommensurate superstructures derived from the defect fluorite-type δ-Bi₂O₃ and can be regarded as intermediate phases between the type II solid solutions in the Bi-Nb-O and Bi-W-O systems. Bi₈W₂Nb₂O₂₃ has a Bi₂WO₆-like subunit cell with a stepped superstructure. Formation mechanisms of various superstructures are discussed.     

Reactivity of Binary Mixtures of La(III) Oxide and Cu(II) Oxalate or Nitrate and Synthesis of La(III) Cuprate

Reactivity of mixtures of La(III) oxide and Cu(II) oxalate/nitrate in hydrated as well as anhydrous state was studied using TG, DTA and XRD. Cu(II) oxide formed in the endothermic decomposition of mixture containing hydrated Cu(II) nitrate and La(III) oxide could not form La₂CuO₄ while Cu(II) oxide formed in the exothermic decomposition of mixture containing hydrated/anhydrous Cu(II) oxalate and La(III) oxide reacts with La(III) oxide and develops the phases CuLaO₃ and La₂CuO₄. The maximum reactivity with respect to the formation of La₂CuO₄phase was observed in mixture containing anhydrous Cu(II) oxalate. This revised version was published online in July 2006 with corrections to the Cover Date.     

Preparation of ZrO2-TiO2-CeO2 and Its Application in the Selective Catalytic Reduction of NO with NH3

TiO₂,ZrO₂-TiO₂,andZrO₂-TiO₂-CeO₂ were prepared by co-precipitation method and characterized by X-ray diffraction (XRD), specific surface area measurements (BET), temperature programmed desorption (NH₃-TPD), oxygen storage capacity (OSC), and temperature programmed reduction (H₂-TPR). The results showed that ZrO₂-TiO₂-CeO₂ exhibited large number of surface strong acid, possessed some oxygen storage capacity, and strong redox property. The three materials were used as supports and the monolith catalysts were prepared with 1% (w) V₂O₅ and 9% (w)WO₃ for selective catalytic reduction (SCR) of NO with ammonia in the presence of excessive O₂, and the results of catalytic activity showed that the catalyst used ZrO₂-TiO₂-CeO₂ as support yielded nearly 100% NO conversion at 275 °C at a gas hourly space velocity (GHSV) of 10000 h⁻¹, and it had the best catalytic activity and showed great potential for practical application.     

α-Fe2O3掺杂对In2O3电导和气敏性能的影响

用化学共沉淀法制备了α Fe2O3掺杂的In2O3纳米晶微粉,研究了α Fe2O3掺杂对In2O3电导和气敏性能的影响. 结果表明, α Fe2O3和In2O3间可形成有限固溶体In2－xFexO3(0≤x≤0.40); Fe3＋对In2O3晶格中In3＋格位的部分取代,大大增强了阴阳离子间的结合力,导致材料中氧空位VO×数骤降、 自由电子的浓度变稀和电导下降. n(Fe3＋):n(In3＋)=5 :5的共沉淀粉于800 ℃下灼烧4 h所得的α Fe2O3掺杂In2O3传感器元件,对45 μmol•L－1 C2H5OH的灵敏度达54.0,为相同浓度干扰气体汽油的8倍多.     

电感耦合等离子体光谱法测定铜冶炼烟尘中锌

本实验介绍了电感耦合等离子体光谱法测定铜冶炼烟尘中锌含量的分析方法。针对样品碳,硅含量高的特点,有针对性的研究了样品的消解方法,确定采用盐酸、硝酸、氢氟酸、高氯酸对铜冶炼烟尘样品进行消解。同时进行了干扰试验,确定样品中高含量的铜,铅,砷等对样品测定结果没有影响。并对仪器的工作参数进行了优化。方法检出限为为0.011 mg/L,测定下限为0.019 mg/L,3个样品的相对标准偏差在0.54%~0.92%之间,加标回收率在96%~101.14%之间。该方法样品消解完全,流程短,操作简单,快速,测定准确度高,可以满足铜冶炼烟尘中锌含量的测定。     

B2O3-Bi2O3-ZnO-Al2O3玻璃助烧剂对BaTiO3陶瓷烧结条件、晶体结构和介电性能的影响

通过调节B₂O₃-Bi₂O₃-ZnO-Al₂O₃(BBZA)玻璃的添加量研究其对钛酸钡(BaTiO₃)陶瓷烧结条件、晶体结构和介电性能的影响。结果表明：添加适量的BBZA玻璃能够有效地将BaTiO₃陶瓷烧结温度由1 350℃降至950℃,并使其致密化。同时,添加BBZA玻璃后,BaTiO₃的晶体结构随着烧结温度的升高而发生转变(立方相→四方相)。另外,BBZA玻璃的引入使BaTiO₃陶瓷的居里峰得到了有效的抑制和拓宽。陶瓷微观形貌显示,玻璃相均匀分布在BaTiO₃晶粒表面。优化的BaTiO₃陶瓷制备条件如下：BBZA添加量(质量分数)为2.0%,烧结温度为950℃。在该条件下制备的BaTiO₃陶瓷介电常数达到1 364,介电损耗低至1.2%。     

电感耦合等离子体光谱法(ICP-AES)测定银精矿中铜、铅、锌、砷、镉、钙、镁、锰含量

针对银精矿样品复杂,难消解的特点,研究了不同酸溶法和碱熔法对样品的消解情况,建立了硝酸,盐酸,氢氟酸,高氯酸消解银精矿的方法。根据元素灵敏度和抗干扰性,选定各元素的测定波长。通过酸溶样和碱熔样测定结果比对,验证了方法准确性。建立了四酸消解-电感耦合等离子体光谱法测定银精矿中铜、铅、锌、砷、镉、钙、镁、锰含量的方法,元素的线性相关系数均在0.9999以上。通过共存元素干扰实验,确定了银精矿中高含量元素(铜、铅、锌、铁、锑、铋等)对测定元素结果没有影响。方法检出限：Cu 0.0063 mg/L, Pb 0.0159 mg/L ,Zn 0.0090 mg/L,As 0.0192 mg/L, Cd 0.0093 mg/L ,Ca 0.0084 mg/L, Mg 0.0075 mg/L, Mn 0.0081 mg/L。测定下限：Cu 0.0105mg/L,Pb 0.0265 mg/L, Zn 0.0150 mg/L, As 0.0320 mg/L, Cd 0.0155 mg/L, Ca 0.0140 mg/L, Mg 0.0125 mg/L,Mn 0.0135 mg/L。3个样品的相对标准偏差在0.87%~3.56%之间,加标回收率在95.00%~103.56%之间。方法流程短,操作简单,快速,灵敏度和再现性高,结果准确可靠,可以满足银精矿中铜、铅、锌、砷、镉、钙、镁、锰含量的测定。     

Li_(1.3)Ti_(1.7)Al_(0.3)(PO_4)_3,Na_(1.3)Ti_(1.7)Al_(0.3)(PO_4)_3的离子交换研究

研究了在不同温度下的NaNO3和AgNO3水溶液中Li1.3Ti1.7Al0.3(PO4)3和Na1.3Ti1.7Al0.3(PO4)3离子交换行为.实验表明Li1.3Ti1.7Al0.3(PO4)3和Na1.3Ti1.7Al0.3(PO4)3均显示出了高选择性与Na+和Ag+进行离子交换的特征,且对Ag+的选择性高于Na+.升高温度可显著提高Ag/Li和Ag/Na的交换反应速度.     

Reactivity of Zn3V2O8 Towards ZnMoO4 in the Solid State

The reactivity of Zn₃ V₂ O₈ towards ZnMoO₄ was investigated by using DTA and XRD methods. A new compound of the formula Zn_2.5 VMoO₈ was found. It crystallises in an orthorhombic system. The melting temperature was determinated to be 845±5°C. This revised version was published online in August 2006 with corrections to the Cover Date.