Characterization of microarc oxidation coatings formed on AM60B magnesium alloy in silicate and phosphate electrolytes

Microarc oxidation coatings on AM60B magnesium alloy were prepared in silicate and phosphate electrolytes. Structure, composition, mechanical property, tribological, and corrosion resistant characteristics of the coatings was studied by scanning electron microscope (SEM), X-ray diffraction (XRD) and microhardness analyses, and by ball-on-disc friction and potentiodynamic corrosion testing. It is found that the coating produced from the silicate electrolyte is compact and uniform and is mainly composed of MgO and forsterite Mg₂SiO₄ phases, while the one formed in phosphate electrolyte is relatively porous and is mainly composed of MgO phase. The thick coating produced from a silicate electrolyte possesses a high hardness and provides a low wear rate (3.55 × 10⁻⁵ mm³/Nm) but a high friction coefficient against Si₃N₄ ball. A relatively low hardness and friction coefficient while a high wear rate (8.65 × 10⁻⁵ mm³/Nm) is recorded during the testing of the thick coating produced from a phosphate electrolyte. Both of these types of coatings provide effective protection for the corrosion resistance compared with the uncoated magnesium alloy. The coating prepared from the silicate electrolyte demonstrates better corrosion behavior due to the compacter microstructure.     

Preparation of anti-corrosion films by microarc oxidation on an Al-Si alloy

Thick ceramic films over 140 μm were prepared on Al-7% Si alloy by ac microarc oxidation in a silicate electrolyte. The film growth kinetics was determined by an eddy current technique and film growth features in different stages were discussed. The microstructure and composition profiles for different thick films were analyzed by scanning electron microscopy and energy dispersive X-ray spectroscopy. Their phase components were determined by X-ray diffraction. The electrochemical corrosion behaviors of bare and coated alloys were evaluated using potentiodynamic polarization curves, and their corrosion morphologies were observed. In the initial stage of oxidation, the growth rate is slow with 0.48 μm/min due to the effect of Si element though the current density is rather high up to 33 A/dm². After the current density has decreased to a stable value of 11 A/dm², the film mainly grows towards the interior of alloy. The film with a three-layer structure consists of mullite, γ-Al₂O₃, α-Al₂O₃ and amorphous phases. By microarc discharge treatment, the corrosion current of the Al-Si alloy in NaCl solution was significantly reduced. However, a thicker film has to be fabricated in order to obtain high corrosion-resistant film of the Al-Si alloy. Microarc oxidation is an effective method to form an anti-corrosion protective film on Si-containing aluminum alloys.     

Microstructure and corrosion behavior of coated AZ91 alloy by microarc oxidation for biomedical application

Magnesium and its alloy currently are considered as the potential biodegradable implant materials, while the accelerated corrosion rate in intro environment leads to implant failure by losing the mechanical integrity before complete restoration. Dense oxide coatings formed in alkaline silicate electrolyte with and without titania sol addition were fabricated on magnesium alloy using microarc oxidation process. The microstructure, composition and degradation behavior in simulated body fluid (SBF) of the coated specimens were evaluated. It reveals that a small amount of TiO₂ is introduced into the as-deposited coating mainly composed of MgO and Mg₂SiO₄ by the addition of titania sol into based alkaline silicate electrolytic bath. With increasing concentration of titania sol from 0 to 10 vol.%, the coating thickness decreases from 22 to 18 μm. Electrochemical tests show that the E_corr of Mg substrate positively shifted about 300500 mV and i_corr lowers more than 100 times after microarc oxidation. However, the TiO₂ modified coatings formed in electrolyte containing 5 and 10 vol.% titania sol indicate an increasing worse corrosion resistance compared with that of the unmodified coating, which is possibly attributed to the increasing amorphous components caused by TiO₂ involvement. The long term immersing test in SBF is consistent with the electrochemical test, with the coated Mg alloy obviously slowing down the biodegradation rate, meanwhile accompanied by the increasing damage trends in the coatings modified by 5 and 10 vol.% titania sol.     

Effect of potassium fluoride in electrolytic solution on the structure and properties of microarc oxidation coatings on magnesium alloy

Oxide coatings were produced on AM60B magnesium alloy substrate making use of microarc oxidation (MAO) technique. The effect of KF addition in the Na₂SiO₃-KOH electrolytic solution on the microarc oxidation process and the structure, composition, and properties of the oxide coatings was investigated. It was found that the addition of KF into the Na₂SiO₃-KOH electrolytic solution caused increase in the electrolyte conductivity and decrease in the work voltage and final voltage in the MAO process. Subsequently, the pore diameter and surface roughness of the microarc oxidation coating were decreased by the addition of KF, while the coating compactness was increased. At the same time, the phase compositions of the coatings also varied after the addition of KF in the electrolytic solution, owing to the participation of KF in the reaction and its incorporation into the oxide coating. Moreover, the coating formed in the electrolytic solution with KF had a higher surface hardness and better wear-resistance than that formed in the solution without KF, which was attributed to the changes in the spark discharge characteristics and the compositions and structures of the oxide coatings after the addition of KF.     

Effect of current density on the microstructure and corrosion behaviour of plasma electrolytic oxidation treated AM50 magnesium alloy

Plasma electrolytic oxidation (PEO) of an AM50 magnesium alloy was accomplished in a silicate-based electrolyte using a DC power source. Coatings were produced at three current densities, i.e. 15 mA cm⁻², 75 mA cm⁻², and 150 mA cm⁻² and were characterised for thickness, roughness, microstructural morphology, phase composition, and corrosion resistance. Even though the 15 min treated coatings produced at higher current density levels were thicker, they showed poor corrosion resistance when compared to that of the coatings obtained at 15 mA cm⁻². Short-term treatments (2 min and 5 min) at 150 mA cm⁻² yielded coatings of thickness and corrosion resistance comparable to that of the low current density coatings. The superior corrosion resistance of the low thickness coatings is attributed to the better pore morphology and compactness of the layer.     

Plasma electrolytic oxidation coating on AZ91 magnesium alloy modified by neodymium and its corrosion resistance

Ceramic coatings on the surfaces of Mg-9Al-1Zn (AZ91) magnesium alloy and Mg-9Al-1Zn-1Nd magnesium alloy (AZ91 magnesium alloy modified by neodymium, named as AZ91Nd in this paper) are synthesized in aluminate electrolyte by plasma electrolytic oxidation (PEO) process, respectively. X-ray diffraction and X-ray photoelectron spectroscopy analyses show the PEO coating on the Mg-9Al-1Zn-1Nd alloy comprises not only MgO and Al₂O₃, which are found in the coating on the AZ91 alloy, but also a trace amount of Nd₂O₃. Microstructure observations indicate the addition of Nd can decrease the sizes of β phases and form Al₂Nd intermetallics in the AZ91 alloy. The fine β phases can effectively restrain the formation of unclosed-holes and greatly decrease the sizes of pores in the coating during the PEO process. In addition, the Al₂Nd intermetallics can be completely covered due to the lateral growth of the PEO coatings formed on the α and β phases. As a result, the coating on the AZ91Nd alloy possesses a dense microstructure compared with that on the AZ91 alloy. The following corrosion tests indicate the corrosion resistance of the PEO coating on the AZ91Nd alloy is evidently higher than that of the PEO coating on the AZ91 alloy.     

Effect of microarc oxidation coating on fatigue performance of Ti-Al-Zr alloy

Ceramic coatings of different thickness were fabricated on Ti6Al2Zr1Mo1V alloy by microarc oxidation (MAO), and the effect of the coating on fatigue life was evaluated by 810 Material Test System. The microstructure, phase and chemical composition of the coatings were determined by SEM, XRD and EDS techniques. The coating mainly consists of rutile and a small amount of anatase TiO₂. With oxidation time ranging from 10 to 30 min, the coating thickness increases from 13 to 25 μm, while the interface between coating and substrate becomes more zigzag, characterized by increasing overgrowth regions of coating into substrate. Under the same cyclic stress of 750 MPa, the fatigue life decreases from 2.08 × 10⁶ cycles for uncoated specimen to about 3 × 10⁴ cycles for microarc oxidized specimen. Under the cyclic stress, the thicker the coating, the more cracks initiate in the overgrowth regions of coating into substrate near the interface, which are considered as the notch sites of stress concentration to induce the crack initiation, also is the key factor to cause the facture.     

Preparation and properties of super-hydrophobic coating on magnesium alloy

The super-hydrophobic coating was successfully fabricated on the surface of magnesium alloy AZ31 by chemical etching and surface modification. The surface morphologies, compositions, wettability and corrosion resistance of the coating were investigated with SEM, XPS, contact angle measurement and electrochemical method, respectively. It shows that the rough and porous micro-nano-structure was presented on the surface of magnesium alloy, and the contact angle could reach up to 157.3 ± 0.5° with sliding angle smaller than 10°. The super-hydrophobic coating showed a long service life. The results of electrochemical measurements showed that anticorrosion property of magnesium alloy was improved. The super-hydrophobic phenomenon of the prepared surface was analyzed with Cassie theory, and it finds that only about 10% of the water surface is contacted with the metal substrate and the rest 90% is contacted with the air cushion.     

Corrosion resistant properties of polyaniline-acrylic coating on magnesium alloy

The performance of the paint coating based on acrylic-polyaniline on magnesium alloy ZM 21 has been studied by electrochemical impedance spectroscopy in 0.5% NaCl solution. The polyaniline was prepared by chemical oxidative method of aniline with ammonium persulphate in phosphoric acid medium. The phosphate-doped polyaniline was characterized by FTIR and XRD methods. Acrylic paint containing the phosphate-doped polyaniline was prepared and coated on magnesium ZM 21 alloy. The coating was able to protect the magnesium alloy and no base metal dissolution was noted even after 75 days exposure to sodium chloride solution.     

Electroless deposition of Ni-W-P coating on AZ91D magnesium alloy

Ternary Ni-W-P alloy coating was deposited directly on AZ91D magnesium alloy by using an alkaline-citrate-based baths. Nickel sulfate and sodium tungstate were used as metal ion sources, respectively, and sodium hypophosphite was used as a reducing agent. The pH value of the electroless bath was tailored for magnesium alloy. The coating was characterized for its structure, morphology, microhardness and the corrosion properties. SEM observation showed the presence of dense and coarse nodules in the ternary coating. EDS analysis showed that the content of tungsten in the Ni-W-P alloy was 4.5 wt.%. Both the electrochemical analysis and the immersion test in 10% HCl solution revealed that the ternary Ni-W-P coating exhibited good corrosion resistance properties in protecting the AZ91D magnesium alloy.     

电流密度对铝合金微弧氧化膜物理化学特性的影响

利用微弧氧化(MAO)技术，在LYl2铝合金上沉积了显微硬度达42.14GPa的超硬陶瓷膜.采用x射线衍射仪和显微硬度计研究了阳极电流密度j_a和阴极、阳极电流密度比j_c/j_a对MAO膜相构成和力学特性的影响.此外，利用扫描电子显微镜和恒电位仪分别对膜的微结构和抗点腐蚀特性进行了分析.结果表明，高j_a制备的膜主要含α-Al₂O₃相，低j_a制备的膜主要含γ-Al₂O₃相.显微硬度测试表明，这类膜有较高的硬度，但以j_a=15A/dm²和j_c/j_a=0.7制备的陶瓷膜硬度最高.抗点腐蚀测试表明，j_c/j_a对陶瓷膜的微结构有很强的影响. 关键词： 微弧氧化 显微硬度 电流密度 抗点腐蚀     

Interface adhesion properties of functional coatings on titanium alloy formed by microarc oxidation method

Three functional coatings (namely Al-C, Si-P-Al and P-F-Al coating) were fabricated by microarc oxidation method on Ti6Al4V alloy in different aqueous solutions. The microstructure, phase and chemical composition of coatings were investigated using scanning electron microscope, X-ray diffraction and energy dispersive spectroscopy. The interface adhesion failure mode of the coating is revealed by shear, tensile and thermal shock methods. The coatings exhibit high adhesion strength by the quantitative shearing test, registering as 110, 70, and 40 MPa for Al-C, Si-P-Al and P-F-Al coating, respectively. The tensile test of the coated samples shows that microarc oxidation treatment does not significantly deteriorate mechanical properties of substrate titanium alloy. The observations of the coating failure after subjected to the identical tensile elongation of 3.0% are well in agreement with those results of the shear test. The thermal cycle test indicates that all the coatings have good anti-thermal shocking properties.     

Characterization of calcium containing plasma electrolytic oxidation coatings on AM50 magnesium alloy

An attempt was made to produce calcium containing plasma electrolytic oxidation (PEO) coatings on AM50 magnesium alloy using an alkaline electrolyte. This study was performed in three alkaline electrolytes containing calcium hydroxide and sodium phosphate with three different mass ratios viz., 1:2.5, 1:5 and 1:7.5. All the three coatings produced were found to contain Ca and P in appreciable amounts. The concentration of P was found to be higher in the coatings obtained in the electrolytes with higher concentration of phosphate ions. Even though all the three coatings were found to be constituted with magnesium oxide and magnesium phosphate phases, X-ray diffraction analyses revealed that the phase composition was influenced by the phosphate ion concentration/conductivity of the electrolyte. Further, the PEO coating obtained in the 1:7.5 ratio electrolyte was found to contain di-calcium phosphate (monetite) and calcium peroxide phases, which were absent in the other two coatings. Potentiodynamic polarization studies performed in 0.1 M NaCl solution showed that the coatings obtained from the 1:5 ratio electrolyte possessed a superior corrosion resistance, which is attributed to the combined effect of thickness, compactness and phase/chemical composition of this coating.     

Electrodeposition of high corrosion resistance Cu/Ni-P coating on AZ91D magnesium alloy

High corrosion resistance Cu/Ni-P coatings were electrodeposited on AZ91D magnesium alloy via suitable pretreatments, such as one-step acid pickling-activation, once zinc immersion and environment-friendly electroplated copper as the protective under-layer, which made Ni-P deposit on AZ91D Mg alloy in acid plating baths successfully. The pH value and current density for Ni-P electrodeposition were optimized to obtain high corrosion resistance. With increasing the phosphorous content of the Ni-P coatings, the deposits were found to gradually transform to amorphous structure and the corrosion resistance increased synchronously. The anticorrosion ability of AZ91D Mg alloy was greatly improved by the amorphous Ni-P deposits, which was investigated by potentiodynamic polarization curve and electrochemical impedance spectroscopy (EIS). The corrosion current density (I_corr) of the coated Mg alloy substrate is about two orders of magnitude less than that of the uncoated.     

Preparation and properties of titanium oxide film on NiTi alloy by micro-arc oxidation

Titanium oxide ceramic coatings were prepared by micro-arc oxidation (MAO) in galvanostatic regime on biomedical NiTi alloy in H₃PO₄ electrolyte using DC power supply. The surface of the coating exhibited a typical MAO porous and rough structure. The XPS analysis indicated that the coatings were mainly consisted of O, Ti, P, and a little amount of Ni, and the concentration of Ni was greatly reduced compared to that of the NiTi substrate. The TF-XRD analysis revealed that MAO coating was composed of amorphous titanium oxide. The coatings were tightly adhesive to the substrates with the bonding strength more than 45 MPa, which was suitable for medical applications. The curves of potentiodynamic porlarization indicated that the corrosion resistance of NiTi alloy was significantly improved due to titanium oxide formation on NiTi alloy by MAO.     

Fretting wear behaviour of microarc oxidation coatings formed on titanium alloy against steel in unlubrication and oil lubrication

Ceramic coatings were formed on Ti6Al4V alloy surface by microarc oxidation (MAO) in a Na₂SiO₃ system solution. Unlubricated, smear oil and oil bath lubricated fretting tests were performed on MAO coatings against 52100 steel on a fretting wear tester. Microstructural investigation of the worn surfaces was performed and the wear mechanisms were studied. The results show that the coatings are mainly composed of rutile and a small amount of anatase TiO₂, both in nano grain structure. Friction coefficient of microarc oxidation coatings under oil bath lubrication was significantly reduced, favorable stable at 0.15, which indicates that the coatings with oil lubricated lowered the shear and adhesive stresses between contact surfaces, consequently alleviating the possibility of initiation and propagation of cracks in the inner layer of the coating or titanium alloy substrate.     

Effect of pulse frequency on the microstructure, phase composition and corrosion performance of a phosphate-based plasma electrolytic oxidation coated AM50 magnesium alloy

An AM50 magnesium alloy was plasma electrolytic oxidation treated using a pulsed DC power supply at three different pulse frequencies viz., 10 Hz, 100 Hz and 1000 Hz with a constant pulse ratio for 15 min in an alkaline phosphate electrolyte. The resultant coatings were characterized by X-ray diffraction, energy dispersive spectroscopy and scanning electron microscopy for their phase composition and microstructural features. The 10 Hz condition yielded relatively thick and rough coatings, which was attributed to the higher energy input per individual pulse during the PEO processing. The phase composition was also found to be influenced by the processing frequency. Electrochemical impedance spectroscopy studies performed in 0.1 M NaCl solutions revealed that the coatings produced at 10 Hz condition had a better corrosion resistance, which was attributed to the higher thickness, more compact microstructural features and a relatively stable phase composition.     

A method to select the optimal equivalent electrical circuit applied to study corrosion system of composite coating on magnesium alloy

Mg-Al layered double hydroxides/micro-arc oxidation (Mg-Al LDHs/MAO) composite coating on AZ31 magnesium alloy is fabricated by hydrothermal treatment. Corrosion system is described by ideal equivalent circuit, in which each layer or interface is regarded as the corresponding electronic component. The optimal equivalent circuit is determined by the minimum total error area of electrical parameters. Error areas of phase angle and modulus for experimental and fitting data are calculated for the selected four different kinds of circuit models such as EC1, EC2, EC3 and EC4. The results show that circuit model EC2 is the best because its total error is 1/2, 2/19 and 1/15 of error values for other three kinds of circuit models, respectively. This work reveals that the optimal equivalent electrical circuit can well reflect corrosion system of Mg-Al LDHs/MAO composite coating with the help of electrochemical impedance spectroscopy (EIS) and scanning electron microscope (SEM).     

Electrodeposition of Al-Mn alloy on AZ31B magnesium alloy in molten salts

The Al-Mn alloy coatings were electrodeposited on AZ31B Mg alloy in AlCl₃-NaCl-KCl-MnCl₂ molten salts at 170 °C aiming to improve the corrosion resistance. However, in order to prevent AZ31B Mg alloy from corrosion during electrodeposition in molten salts and to ensure excellent adhesion of coatings to the substrate, AZ31B Mg alloy should be pre-plated with a thin zinc layer as intermediate layer. Then the microstructure, composition and phase constituents of the coatings were investigated by scanning electron microscopy (SEM), energy-dispersive X-ray spectrometry (EDX), and X-ray diffraction (XRD). It was indicated that, by adjusting the MnCl₂ content in the molten salts from 0.5 wt% to 2 wt%, the Mn content in the alloy coating was increased and the phase constituents were changed from f.c.c Al-Mn solid solution to amorphous phase. The corrosion resistance of the coatings was evaluated by potentiodynamic polarization measurements in 3.5% NaCl solution. It was confirmed that the Al-Mn alloy coatings exhibited good corrosion resistance with a chear passive region and significantly reduced corrosion current density at anodic potentiodynamic polarization. The corrosion resistance of the alloy coatings was also related with the microstructure and Mn content of the coatings.     

In situ formation of Al2O3-SiO2-SnO2 composite ceramic coating by microarc oxidation on Al-20%Sn alloy

In situ formation of Al₂O₃-SiO₂-SnO₂ composite ceramic coating on Al-20%Sn alloy was successfully fabricated in aqueous Na₂SiO₃ electrolyte by microarc oxidation technology. The compositions, structure, mechanical and tribological properties of the composite coating were detailed studied by scanning electron microscope, energy dispersive spectroscopy, X-ray diffraction, hardness tester and ball-on-disc friction tester. It is found that the species originating from the Al-20%Sn alloy substrate and the electrolyte solution both participate in reaction and contribute to the composition of the coating, which results in the generated coating firmly adherent to the substrate. The composite ceramic coating can greatly improve the microhardness and tribological property of Al-20%Sn alloy.