Spray pyrolysis deposition of YSZ and YSZ-Pt composite films

In the present paper procedures are described for spray pyrolysis deposition of YSZ films (0.1-30 μm in thickness) with 8 or 15 mole % of YO_1.5 on different substrates. Aqueous or ethylene glycol solutions of Y-Zr-citrates were used as starting material and O₂ as carrier gas. The crystal structure and the morphology of the films were studied.The optimal deposition and post-deposition annealing conditions were defined, taking into account the desired film thickness and characteristics. Substrate temperatures of 250 °C during the deposition followed by heating for 10 min to 400 °C after every spraying and to 590 °C after every three sprayings with final annealing at 590 °C for 2 h in static air atmosphere were found to be suitable for the production of dense, uniform and cracks-free films.     

Influence of substrate temperature and post-treatment on the properties of ZnO:Al thin films prepared by pulsed laser deposition

Highly transparent conductive Al₂O₃ doped zinc oxide (AZO) thin films have been deposited on the glass substrate by pulsed laser deposition technique. The effects of substrate temperature and post-deposition annealing treatment on structural, electrical and optical properties of AZO thin films were investigated. The experimental results show that the electrical resistivity of films deposited at 240 °C is 6.1 × 10⁻⁴ Ω cm, which can be further reduced to as low as 4.7 × 10⁻⁴ Ω cm by post-deposition annealing at 400 °C for 2 h in argon. The average transmission of AZO films in the visible range is 90%. The optical direct band gap of films was dependent on the substrate temperature and the annealing treatment in argon. The optical direct band gap value of AZO films increased with increasing annealing temperature.     

Synthesis and characterization of porous crystalline SiC thin films prepared by radio frequency reactive magnetron sputtering technique

Hexagonal SiC thin films have been deposited using radio frequency reactive magnetron sputtering technique by varying the substrate temperature and other deposition conditions. Prior to deposition surface modification of the substrate Si(1 0 0) played an important role in deposition of the hexagonal SiC structure. The effect of substrate temperature during deposition on structure, composition and surface morphology of the SiC films has been analyzed using atomic force microscopy, Fourier transform infrared spectroscopy and spectroscopic ellipsometry. X-ray diffraction in conventional θ-2θ mode and omega scan mode revealed that the deposited films were crystalline having 8H-SiC structure and crystallinity improved with increase of deposition temperature. The bonding order and Si-C composition within the films showed improvement with the increase of deposition temperature. The surface of thin films grew in the shape of globes and columns depending upon deposition temperature. The optical properties also showed improvement with increase of deposition temperature and the results obtained by ellipsometry reinforced the results of other techniques.     

Investigation of thermal annealing effects on microstructural and optical properties of HfO2 thin films

In the present paper, we investigate the effect of thermal annealing on optical and microstructural properties of HfO₂ thin films (from 20 to 190 nm) obtained by plasma ion assisted deposition (PIAD). After deposition, the HfO₂ films were annealed in N₂ ambient for 3 h at 300, 350, 450, 500 and 750 °C. Several characterisation techniques including X-ray reflectometry (XRR), X-ray diffraction (XRD), spectroscopic ellipsometry (SE), UV Raman and FTIR were used for the physical characterisation of the as-deposited and annealed HfO₂ thin films. The results indicate that as-deposited PIAD HfO₂ films are mainly amorphous and a transition to a crystalline phase occurs at a temperature higher than 450 °C depending on the layer thickness. The crystalline grains consist of cubic and monoclinic phases already classified in literature but this work provides the first evidence of amorphous-cubic phase transition at a temperature as low as 500 °C. According to SE, XRR and FTIR results, an increase in the interfacial layer thickness can be observed only for high temperature annealing. The SE results show that the amorphous phase of HfO₂ (in 20 nm thick samples) has an optical bandgap of 5.51 eV. Following its transition to a crystalline phase upon annealing at 750 °C, the optical bandgap increases to 5.85 eV.     

Influence of temperature annealing on optical properties of SrTiO3/BaTiO3 multilayered films on indium tin oxide

We have prepared SrTiO₃/BaTiO₃ thin films with multilayered structures deposited on indium tin oxide (ITO) coated glass by a sol-gel deposition and heating at 300-650 °C. The optical properties were obtained by UV-vis spectroscopy. The films show a high transmittance (approximately 85%) in the visible region. The optical band gap of the films is tunable in the 3.64-4.19 eV range by varying the annealing temperature. An abrupt decrease towards the bulk band gap value is observed at annealing temperatures above 600 °C. The multilayered film annealed at 650 ° C exhibited the maximum refractive index of 2.09-1.91 in the 450-750 nm wavelength range. The XRD and AFM results indicate that the films annealed above 600 ° C are substantially more crystalline than the films prepared at lower temperatures which were used to change their optical band gap and complex refractive index to an extent that depended on the annealing temperature.     

The effect of heat treatment on the physical properties of sol-gel derived ZnO thin films

Zinc oxide (ZnO) thin films were deposited on microscope glass substrates by sol-gel spin coating method. Zinc acetate (ZnAc) dehydrate was used as the starting salt material source. A homogeneous and stable solution was prepared by dissolving ZnAc in the solution of monoethanolamine (MEA). ZnO thin films were obtained after preheating the spin coated thin films at 250 °C for 5 min after each coating. The films, after the deposition of the eighth layer, were annealed in air at temperatures of 300 °C, 400 °C and 500 °C for 1 h. The effect of thermal annealing in air on the physical properties of the sol-gel derived ZnO thin films are studied. The powder and its thin film were characterized by X-ray diffractometer (XRD) method. XRD analysis revealed that the annealed ZnO thin films consist of single phase ZnO with wurtzite structure (JCPDS 36-1451) and show the c-axis grain orientation. Increasing annealing temperature increased the c-axis orientation and the crystallite size of the film. The annealed films are highly transparent with average transmission exceeding 80% in the visible range (400-700 nm). The measured optical band gap values of the ZnO thin films were between 3.26 eV and 3.28 eV, which were in the range of band gap values of intrinsic ZnO (3.2-3.3 eV). SEM analysis of annealed thin films has shown a completely different surface morphology behavior.     

Magnetoelectrical properties of W doped ZnO thin films

ZnO thin films were deposited on the Si(100) substrate by rf sputtering using a 99.999% pure commercially bought and a home made target under 100 W power. The home made ZnO target, including 1–2% tungsten, was synthesized via solid state reaction. Thin films were deposited under a flow of 70% argon and 30% O₂ gas mixture followed by post-deposition annealing under 1 Torr oxygen atmosphere. Both deposition and post-deposition annealing were done at 420±1 °C. The structural analyses show that the films were in the [0002] preferred direction and that W atoms are bound to the oxygen atoms by replacing the Zn host atoms. Although no specific change was observed in the magnetic properties as a result of W doping, significant changes in the electrical properties were observed, as determined by the longitudinal and transversal magneto-electrical measurements. It was found that the W impurities induce better insulating properties due to lower carrier concentration and higher resistivity values. On the other hand, the enhanced positive magnetoresistivity and the existence of polarized spin currents, which were not specific for pure ZnO thin films, were observed in W doped ZnO films below 10 K.     

Highly thermal stable transparent conducting SnO2:Sb epitaxial films prepared on α-Al2O3 (0 0 0 1) by MOCVD

Antimony-doped tin oxide (SnO₂:Sb) single crystalline films have been prepared on α-Al₂O₃ (0 0 0 1) substrates by metal organic chemical vapor deposition (MOCVD). The antimony doping was varied from 2% to 7% (atomic ratio). Post-deposition annealing of the SnO₂:Sb films was carried out at 700-1100 °C for 30 min in atmosphere ambient. The effect of annealing on the structural, electrical and optical properties of the films was investigated in detail. All the SnO₂:Sb films had good thermal stability under 900 °C, and the 5% Sb-doped SnO₂ film exhibited the best opto-electrical properties. Annealed above 900 °C, the 7% Sb-doped SnO₂ film still kept high thermal stability and showed good electrical and optical properties even at 1100 °C.     

Thermal stability of alumina thin films containing γ-Al2O3 phase prepared by reactive magnetron sputtering

The paper reports on thermal stability of alumina thin films containing γ-Al₂O₃ phase and its conversion to a thermodynamically stable α-Al₂O₃ phase during a post-deposition equilibrium thermal annealing. The films were prepared by reactive magnetron sputtering and subsequently post-deposition annealing was carried out in air at temperatures ranging from 700 °C to 1150 °C and annealing times up to 5 h using a thermogravimetric system. The evolution of the structure was investigated by means of X-ray diffraction after cooling down of the films. It was found that (1) the nanocrystalline γ-Al₂O₃ phase in the films is thermally stable up to 1000 °C even after 5 h of annealing, (2) the nanocrystalline θ-Al₂O₃ phase was observed in a narrow time and temperature region at ≥1050 °C, and (3) annealing at 1100 °C for 2 h resulted in a dominance of the α-Al₂O₃ phase only in the films with a sufficient thickness.     

Effect of deposition temperature on the microstructure and surface morphology of c-axis oriented AlN films deposited on sapphire substrate by RF reactive magnetron sputtering

In this paper, c-axis oriented AlN films were prepared on sapphire substrate by RF reactive magnetron sputtering at various deposition temperatures (30–700 °C). The influences of deposition temperature on the chemical composition, crystalline structure and surface morphology of the AlN films were systematically investigated. The as-deposited films were characterized by X-ray photoelectron spectroscopy (XPS), two-dimensional X-ray diffraction (2D-XRD) and atomic force microscopy (AFM). The experimental results show that it can be successfully grown for high-purity and near-stoichiometric (Al/N = 1.12:1) AlN films except for the segregation of a few oxygen impurities exist in the form of Al–O bonding. The chemical composition of as-deposited films is almost independent of substrate temperature in the range of 30–700 °C. However, the crystalline structure and surface morphology of the deposited AlN films are strongly influenced by the deposition temperature. The optimum deposition temperature is 300 °C, giving a good compromise between crystalline structure and surface morphology to grow AlN films.     

Fabrication and vacuum annealing of transparent conductive Ga-doped Zn0.9Mg0.1O thin films prepared by pulsed laser deposition technique

In this study, highly transparent conductive Ga-doped Zn_0.9Mg_0.1O (ZMO:Ga) thin films have been deposited on glass substrates by pulsed laser deposition (PLD) technique. The effects of substrate temperature and post-deposition vacuum annealing on structural, electrical and optical properties of ZMO:Ga thin films were investigated. The properties of the films have been characterized through Hall effect, double beam spectrophotometer and X-ray diffraction. The experimental results show that the electrical resistivity of film deposited at 200 °C is 8.12 × 10⁻⁴ Ω cm, and can be further decreased to 4.74 × 10⁻⁴ Ω cm with post-deposition annealing at 400 °C for 2 h under 3 × 10⁻³ Pa. In the meantime, its band gap energy can be increased to 3.90 eV from 3.83 eV. The annealing process leads to improvement of (0 0 2) orientation, wider band gap, increased carrier concentration and blue-shift of absorption edge in the transmission spectra of ZMO:Ga thin films.     

The effect of post-annealing on surface acoustic wave devices based on ZnO thin films prepared by magnetron sputtering

Zinc oxide (ZnO) thin films were deposited on unheated silicon substrates via radio frequency (RF) magnetron sputtering, and the post-deposition annealing of the ZnO thin films was performed at 400 °C, 600 °C, 800 °C, and 1000 °C. The characteristics of the thin films were investigated by X-ray diffractometry (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM). The films were then used to fabricate surface acoustic wave (SAW) resonators. The effects of post-annealing on the SAW devices are discussed in this work. Resulting in the 600 °C is determined as optimal annealing temperature for SAW devices. At 400 °C, the microvoids exit between the grains yield large root mean square (RMS) surface roughness and higher insertion losses in SAW devices. The highest RMS surface roughness, crack and residual stress cause a reduction of surface velocity (about 40 m/s) and increase dramatically insertion loss at 1000 °C. The SAW devices response becomes very weak at this temperature, the electromechanical coupling coefficient (k²) of ZnO film decrease from 3.8% at 600 °C to 1.49% at 1000 °C.     

Pulsed laser deposition and characterization of multilayer metal-carbon thin films

Cobalt-DLC multilayer films were deposited with increasing content of cobalt, keeping carbon content constant by pulsed laser deposition technique. A cobalt free carbon film was also deposited for comparison. Excimer laser was employed to ablate the materials onto silicon substrate, kept at 250 °C, while post-deposition annealing at 400 °C was also performed in situ. The formation of cobalt grains within the carbon matrix in Co-DLC films can be seen through scanning electron and atomic force micrographs while no grains on the surface of the cobalt-free DLC film were observed. Raman spectra of all the films show D- and G-bands, which is a confirmation that the films are DLC in nature. According to Vibrating sample magnetometer (VSM) measurements, the DLC films with cobalt revealed ferromagnetic behaviour whereas the cobalt free DLC film exhibited diamagnetic behaviour. The pure DLC film also shows ferromagnetic nature when diamagnetic background is subtracted. Spectroscopic Ellipsometry (SE) analysis showed that the optical band gaps, refractive indices and extinction coefficients of Co-DLC films can be effectively tuned with increasing content of cobalt.     

Crystallization of hydrogenated amorphous silicon carbon films with laser and thermal annealing

The crystallization of silicon rich hydrogenated amorphous silicon carbon films prepared by Plasma Enhanced Chemical Vapor Deposition technique has been induced by excimer laser annealing as well as thermal annealing. The excimer laser energy density (E_d) and the annealing temperature were varied from 123 to 242 mJ/cm² and from 250 to 1200 °C respectively. The effects of the two crystallization processes on the structural properties and bonding configurations of the films have been studied. The main results are that for the laser annealed samples, cubic SiC crystallites are formed for E_d ≥ 188 mJ/cm², while for the thermal annealed samples, micro-crystallites SiC and polycrystalline hexagonal SiC are observed for the annealing temperature of 800 and 1200 °C respectively. The crystallinity degree has been found to improve with the increase in the laser energy density as well as with the increase in the annealing temperature.     

Evolution of magnetic and microstructural properties of thick sputtered NdFeB films with processing temperature

Ta (100 nm)/NdFeB (5 μm)/Ta (100 nm) films have been deposited onto Si substrates using triode sputtering (deposition rate ∼18 μm/h). A 2-step procedure was used: deposition at temperatures up to 400 °C followed by ex-situ annealing at higher temperatures. Post-deposition annealing temperatures above 650 °C are needed to develop high values of coercivity. The duration of the annealing time is more critical in anisotropic samples deposited onto heated substrates than in isotropic samples deposited at lower temperatures. For a given set of annealing conditions (750 °C/10′), high heating rates (?2000 °C/h) favour high coercivity in both isotropic and anisotropic films. The shape and size of Nd₂Fe₁₄B grains depend strongly on the heating rate.     

Magnetic properties of MnO nanocrystals dispersed in a silica matrix

Magnetic nanocrystalline MnO particles have been synthesized in a silica glass matrix by the sol-gel method at calcination temperatures up to 1000 °C. EPR spectra of 0.1 mol% MnO doped silica gel and glasses studied in the temperature range 10-290 K show with the exception of those samples calcined at 900 and 1000 °C 6-line characteristic Mn(II) hyperfine (HF) lines. Additionally five spin-forbidden doublets have been observed at 100 K and below. Small spreads in spin Hamiltonian parameters (D and E) imply that the ligand field environments of Mn(II) ions embedded in the silica glass are nearly uniform. Monotonous decrease in HF linewidth in going from 120 °C gel to 800 °C calcined glass has been interpreted as the continuous decrease in population of isolated Mn²⁺ ions in silica glass matrix resulting in the decrease of magnetic dipolar interactions leading to the observed decrease in HF linewidth. XRD and TEM of sample calcined at 1000 °C shows the presence of nanocrystals of MnO having orthorhombic crystalline phase and sizes about 10 nm. The thermal behavior of magnetization (zero-field-cooled and field-cooled) and magnetic hysteresis of MnO nanocrystals in the 5-300 K temperature interval have demonstrated that the MnO nanocrystals display superparamagnetic-ferromagnetic transition at low temperatures. X-band EPR linewidth data plotted versus inverse of temperature (1/T) for samples calcined at 900 and 1000 °C (EPR recorded in the vicinity of 0.35 T applied field) depict similar transitions.     

Initial study on the structure and photoluminescence properties of SiC films doped with Al

SiC films doped with aluminum (Al) were prepared by the rf-magnetron sputtering technique on p-Si substrates with a composite target of a single crystalline SiC containing several Al pieces on the surface. The as-deposited films were annealed in the temperature range of 400-800 °C under nitrogen ambient. The thin films have been characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). The results show that the introduction of Al into films hinders crystalline formation process. And with the increase of annealing temperature, more Si particles are formed in the films, which strongly affect the optical absorption properties. The photoluminescence (PL) spectra of the samples show two peaks at 370 nm and 412 nm. The intensities of the PL peaks are evidently improved after Al doped. We attribute the origin of the two PL peaks to a kind of Si-related defect centres. The obtained results are expected to have important applications in modern optoelectronic devices.     

Magnetic and spectroscopic characteristics of ZnMnO system

We report on the observation of room-temperature ferromagnetism in epitaxial (Zn,Mn)O films grown by a pulsed-laser deposition technique using high-density targets. The X-ray, microscopic, spectroscopic and magnetic properties of target material containing 6 at.% of Mn and films were compared. The target shows the presence of large clusters exhibiting paramagnetic behavior. However, ferromagnetic properties were observed in (Zn,Mn)O films grown at a substrate temperature of 500 °C and with an oxygen partial pressure of 1 mTorr. Although, crystalline quality of the film improves with increasing substrate temperature, the ferromagnetism becomes weaker.     

ZnO thin films on Si(1 1 1) grown by pulsed laser deposition from metallic Zn target

ZnO thin films with highly c-axis orientation have been fabricated on p-type Si(1 1 1) substrates at 400 °C by pulsed laser deposition (PLD) from a metallic Zn target with oxygen pressures between 0.1 and 0.7 mbar. Experimental results indicate that the films deposited at 0.3 and 0.5 mbar have better crystalline and optical quality and flatter surfaces than the films prepared at other pressures. The full width at half maximum (FWHM) of (0 0 0 2) diffraction peak decreases remarkably from 0.46 to 0.19° with increasing annealing temperature for the film prepared at 0.3 mbar. In photoluminescence (PL) spectra at room temperature, the annealed film at 700 °C exhibits a smaller ultraviolet (UV) peak FWHM of 108 meV than the as-grown film (119 meV). However, an enhanced deep-level emission is observed. Possible origins to above results are discussed.     

Layer structure variations of ultra-thin HfO2 films induced by post-deposition annealing

To meet challenges for a smaller transistor feature size, ultra-thin HfO₂ high-k dielectric has been used to replace SiO₂ for the gate dielectric. In order to accurately analyze the ultra-thin HfO₂ films by grazing incidence X-ray reflectivity (GIXRR), an appropriate material model with a proper layer structure is required. However, the accurate model is difficult to obtain, since the interfaces between layers of the ultra-thin HfO₂ films are not easily identified, especially when post-deposition annealing process is applied. In this paper, 3.0 nm HfO₂ films were prepared by atomic layer deposition on p-type silicon wafer, and annealed in Ar environment with temperatures up to 1000 °C. The layer structures and the role of the interfacial layer of the films in the post-deposition annealing processes were evaluated by X-ray diffraction and X-ray photoelectron spectroscopy (XPS). The experimental results and analysis showed that layer thicknesses, crystal phases and chemical structures of the ultra-thin HfO₂ films were significantly dependent on annealing temperatures. The binding energy shifts of Hf 4f, O 1s, and Si 2p elements revealed the formation of Hf silicate (Hf-O-Si bonding) with increasing annealing temperatures. Due to the silicate formation and increasing silicon oxide formation, the interface broadening is highly expected. The structure analysis of the GIXRR spectra using the modified material structure model from the XPS analysis confirmed the interfacial broadening induced by the post-deposition annealing.