Epitaxially grown ZnO thin films on 6H-SiC(0 0 0 1) substrates prepared by spin coating-pyrolysis

Epitaxially grown ZnO thin film on 6H-SiC(0 0 0 1) substrate was prepared by using a spin coating-pyrolysis with a zinc naphthenate precursor. As-deposited film was pyrolyzed at 500 °C for 10 min in air and finally annealed at 800 °C for 30 min in air. In-plane alignment of the film was investigated by X-ray pole-figure analysis. Field emission-scanning electron microscope, scanning probe microscope, and He-Cd laser (325 nm) was used to analyze the surface morphology, the surface roughness and photoluminescence of the films. In the photoluminescence spectra, near-band-edge emission with a broad deep-level emission was observed. The position of the near-band-edge peak was around 3.27 eV.     

Influence of substrate temperature on the texture of barium ferrite film by magnetron sputtering

Barium ferrite thin films have been prepared by radio frequency magnetron sputtering on a sapphire (0 0 1) substrate at substrate temperature of 500 °C and 650 °C, respectively. The films were further annealed in air at 1000 °C for 5 h. X-ray diffraction shows that the films at the lower substrate temperatures have a good epitaxial relation with respect to the substrate, while the samples under the higher substrate temperatures have (1 0 9) planes parallel to the substrate. The remanence ratio decreases from 0.82 to 0.47 when the substrate temperature is increased. We attribute the variation of the growth direction to the enhanced vertical mobility of the deposited atoms when the substrate temperature is increased.     

Effect of thermal treatment on linear optical properties of Cu nanoclusters

Silica glass was implanted with 50 keV Cu⁺ ions at various fluences from 6×10¹⁵ to 8×10¹⁶ ions/cm² and thermally-annealed in air between room temperature to 1200 °C. UV/visible spectroscopy measurements reveal absorption bands at characteristics surface plasmon resonance (SPR) frequencies, signifying the formation of copper colloids in silica, even without thermal treatments. Such copper nanoclusters can be attributed to the relatively high mobility of copper atoms, even at ambient conditions. Using the equation derived from the framework of free-electron theory, the average radii of the Cu particles were found to be in the range 2-4 nm from the experimental surface plasmon absorption peaks. Radioluminescence (RL) spectra exhibited broad bands at 410 and 530 nm, associated with the presence of Cu⁺ ions in the as-implanted samples. The effect of thermal annealing in air on absorption and emission spectra of these Cu-implanted samples, as well as the formation of copper nanoclusters from original Cu⁺ ions, is discussed.     

Substrate temperature influence on the properties of nanostructured ZnO transparent ultrathin films grown by PLD

Zinc oxide films of 40 nm thickness have been deposited on glass substrates by pulsed laser deposition using an excimer XeCl laser (308 nm) at different substrate temperatures ranging from room temperature to 650 °C. Surface investigations carried out by using atomic force microscopy have shown a strong influence of temperature on the films surface topography. UV-VIS transmittance measurements have shown that our ZnO films are highly transparent in the visible wavelength region, having an average transmittance of ∼90%. The optical band gap of the films was found to be 3.26 eV, which is lower than the theoretical value of 3.37 eV. Besides the normal absorption edge related to the transition between the valence and the conduction band, an additional absorption band was also recorded in the wavelength region around 364 nm (∼3.4 eV). This additional absorption band may be due to excitonic, impurity, and/or quantum size effects. Photoreduction/oxidation in ozone of the ZnO films lead to larger conductivity changes for higher deposition temperature. In conclusion, the ozone sensing characteristics as well as the optical properties of the ZnO thin films deposited by pulsed laser deposition are strongly influenced by the substrate temperature during growth. The sensitivity of the films towards ozone might be enhanced significantly by the control of the films deposition parameters and surface characteristics.     

Mixing and magnetic properties of surface alloys: The role of the substrate

In this paper, we have performed ab initio density functional theory calculations to compare the miscibility and magnetic properties of two-dimensional binary surface alloys of the form M_xN_1−x (M = Fe or Co; N = Pt, Au, Ag, Cd or Pb) on two different substrates - Rh(1 1 1) and Ru(0 0 0 1). The trends in miscibility for the two substrates are found to be strikingly similar. The magnetic moments show qualitatively similar behavior, but their magnitudes differ: surface alloys on Rh(1 1 1) have larger magnetic moments than on Ru(0 0 0 1). We infer that strain plays the determining role in stabilizing these two-dimensional alloys, whereas the differences in magnetic moments can be ultimately attributed to the different number of d-electrons in Rh and Ru.     

Influence of substrate morphology on Pb growth

The crystallographic structure and morphology of Pb layers in their early stage of growth on Si(3 3 5) surface are studied with Reflection High Electron Energy Diffraction (RHEED) and specific resistivity techniques. The vicinal Si(3 3 5), with different surface morphology controlled by the amount of predeposited Au, was used as a substrate. Changes in the substrate morphology, from disordered step distribution through a perfectly ordered Si(3 3 5) to a hill-and-valley structure consisting of wide (1 1 1) terraces and high Miller index facets, cause switching between one- and two-dimensional growth of the Pb structures.     

Growth of oriented crystalline Ag nanoislands on air-exposed Si(0 0 1) surfaces

Growth of Ag islands under ultrahigh vacuum condition on air-exposed Si(0 0 1)-(2 × 1) surfaces has been investigated by in-situ reflection high energy electron diffraction (RHEED). A thin oxide is formed on Si via exposure of the clean Si(0 0 1)-(2 × 1) surface to air. Deposition of Ag on this oxidized surface was carried out at different substrate temperatures. Deposition at room temperature leads to the growth of randomly oriented Ag islands while well-oriented Ag islands, with (0 0 1)_Ag||(0 0 1)_Si, [1 1 0]_Ag||[1 1 0]_Si, have been found to grow at substrate temperatures of ≥350 °C in spite of the presence of the oxide layer between Ag islands and Si. The RHEED patterns show similarities with the case of Ag deposition on H-passivated Si(0 0 1) surfaces.     

Effect of calcination temperature on the morphology and surface properties of TiO2 nanotube arrays

Well-ordered TiO₂ nanotube arrays were prepared by electrochemical anodization of titanium in aqueous electrolyte solution of H₃PO₄ + NH₄F at a constant voltage of 20 V for 3 h, followed by calcined at various temperatures. X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), X-ray photoelectron spectroscopy (XPS) and Photoluminescence (PL) were used to characterize the samples. The results showed that the as-prepared nanotube arrays before being calcined were amorphous and could transform to anatase phase at a heat treatment temperature higher than 400 °C. As the calcination temperatures increased, crystallization of anatase phase enhanced and rutile phase appeared at 600 °C. However, further increasing the calcination temperature would cause the collapse of nanotube arrays. PL intensity of the nanotube arrays annealed at 500 °C was the lowest, which was probably ascribed to better crystallization together with fewer surface defects of the nanotube arrays.     

AlF3 film deposited by IAD with end-Hall ion source using SF6 as working gas

A novel and effective process to fabricate high quality fluoride thin films was presented. Aluminum fluoride films deposited by a conventional thermal evaporation with an ion-assisted deposition (IAD) using SF₆ as a working gas at around room temperature were investigated. In this study, the optimal voltage and current, 50 V and 0.25 A, were found according to the optical properties of the films: high refractive index (1.489 at 193 nm), low optical absorption and extinction coefficient (<10⁻⁴ at 193 nm) in the UV range. The physical properties of the film are high packing density and amorphous without columnar structure. It was proved that using SF₆ working gas in IAD process is a good choice and significantly improves the quality of AlF₃ films.     

Influence of crystallization on the spectral features of nano-sized ferroelectric barium strontium titanate (Ba0.7Sr0.3Tio3) thin films

Ferroelectric barium strontium titanate (Ba_0.7Sr_0.3TiO₃)(BST) thin films have been prepared from barium 2-ethylhexanoate [Ba[CH₃(CH₂)₃CH(C₂H₅)CO₂]₂]_, strontium 2-ethylhexanoate [Sr[CH₃(CH₂)₃CH(C₂H₅)CO₂]₂] and titanium(IV) isopropoxide [TiOCH(CH₃)₂]₄ precursors using a modified sol-gel technique. The precursor except [TiOCH(CH₃)₂]₄ were synthesized in the laboratory. Transparent and crack-free films were fabricated on pre-cleaned quartz substrates by spin coating. The structural and optical properties of films annealed at different temperatures have been investigated. The as-fired films were found to be amorphous that crystallized to the tetragonal phase after annealing at 550 °C for 1 h in air. The lattice constants “a” and “c” were found to be 3.974 A and 3.990 A, respectively. The grain sizes of the films annealed at 450, 500 and 550 °C were found to be 30.8, 36.0 and 39.8 nm respectively. The amorphous film showed very high transparency (∼95%), which decreases slightly after crystallization (∼90%). The band gap and refractive index of the amorphous and crystalline films were estimated. The optical dispersion data are also analyzed in the light of the single oscillator model and are discussed.     

Thickness-dependent magnetization reversal in CoZrNb amorphous films

Structure and magnetization of CoZrNb amorphous films prepared by DC magnetron sputtering have been studied as a function of film thickness (t), from 35 to 840 nm. Using comprehensive characterization, we show that the CoZrNb amorphous films possess a single phase and no nanocrystalline can be detected. The magnetic measurements indicate that the magnetization reversal of CoZrNb films is strongly dependent on t. That is, the coercivity is abruptly reduced to be lower than 4 Oe with t increasing from 35 to 105 nm, and then gradually decreases to ∼0.2 Oe as t increases. This coercivity transition versus t is accompanied by the strong magnetization reversal when t is larger than 105 nm. The results reveal that CoZrNb amorphous films with comparatively large film thickness (>100 nm) are suitable for sensors and anti-faked materials.     

Comparative photoemission study of the electronic properties of L-CVD SnO2 thin films

In this work we present the results of comparative XPS and PYS studies of electronic properties of the space charge layer of the L-CVD SnO₂ thin films after air exposure and subsequent UHV annealing at 400 °C, with a special emphasis on the interface Fermi level position.From the centre of gravity of binding energy of the main XPS Sn 3d_5/2 line the interface Fermi level position E_F − E_v in the band gap has been determined. It was in a good correlation with the value estimated from the offset of valence band region of the XPS spectrum, as well as from the photoemission yield spectroscopy (PYS) measurements. Moreover, from the valence band region of the XPS spectrum and PYS spectrum two different types of filled electronic band gap states of the L-CVD SnO₂ thin films have been derived, located at 6 and 3 eV with respect to the Fermi level.     

Synthesis and electrochemical characteristics of Ta-N thin films fabricated by cathodic arc deposition

Ta-N thin films were deposited on AISI 317L stainless steel (SS) substrates by cathodic arc deposition (CAD) at substrate biases of −50 and −200 V. The as-deposited films were characterized using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and energy dispersive X-ray analysis (EDX). The results show that stoichiometric TaN with hexagonal lattice (3 0 0) preferred orientation was achieved at the bias of −200 V. On the other hand, Ta-rich Ta-N thin film deposited at −50 V shows amorphous nature. According to the XPS result, Ta element in the films surface exist in bonded state, including the Ta-N bonds characterized by the doublet (Ta 4f_7/2 = 23.7 eV and Ta 4f_5/2 = 25.7 eV). Electrochemical properties of the Ta-N coated stainless steel systems were investigated using potentiodynamic polarization and electrochemical impedance spectroscope (EIS) in Hank's solution at 37 °C. For the Ta-N coated samples, the corrosion current (i_corr) is two or three orders of magnitude lower than that of the uncoated ones, indicating a significantly improved corrosion resistance. Growth defects in the Ta-N thin films produced by CAD, however, play a key role in the corrosion process, especially the localised corrosion. Using the polarization fitting and the EIS modelling, we compared the polarization resistance (R_p) and the porosity (P) of the Ta-N coatings deposited at different biases. It seems that Ta-N film with comparatively lower bias (−50 V) shows better corrosion behavior in artifical physiological solution. That may be attributed to the effect of ion bombarding, which can be modulated by the substrate bias.     

Optical characterization of PLD grown nitrogen-doped TiO2 thin films

Nitrogen-doped TiO₂ thin films were prepared by pulsed laser deposition (PLD) by ablating metallic Ti target with pulses of 248 nm wavelength in reactive atmospheres of O₂/N₂ gas mixtures. The layers were characterized by UV-VIS spectrophotometry and variable angle spectroscopic ellipsometry with complementary profilometry for measuring the thickness of the films. Band gap and extinction coefficient values are presented for films deposited at different substrate temperatures and for varied N₂ content of the gas mixture. The shown tendencies are correlated to nitrogen incorporation into the TiO_2-xN_x layers. It is shown that layers of significantly increased visible extinction coefficient with band gap energy as low as 2.89 eV can be obtained. A method is also presented how the spectroscopic ellipsometric data should be evaluated in order to result reliable band gap values.     

The influence of substrate temperature variation on tungsten oxide thin film growth in an HFCVD system

Tungsten oxide (WO₃) thin films were deposited by a modified hot filament chemical vapor deposition (HFCVD) technique using Si (1 0 0) substrates. The substrate temperature was varied from room temperature to 430 °C at an interval of 100 °C. The influence of the substrate temperature on the structural and optical properties of the WO₃ films was studied. X-ray diffraction and Raman spectra show that as substrate temperature increases the film tends to crystallize from the amorphous state and the surface roughness decreases sharply after 230 °C as confirmed from AFM image analysis. Also from the X-ray analysis it is evident that the substrate orientation plays a key role in growth. There is a sharp peak for samples on Si substrate due to texturing. The film thickness also decreases as substrate temperature increases. UV-vis spectra show that as substrate temperature increases the film property changes from metallic to insulating behavior due to changing stoichiometry, which was confirmed by XPS analysis.     

The effect of heat treatment on the physical properties of sol-gel derived ZnO thin films

Zinc oxide (ZnO) thin films were deposited on microscope glass substrates by sol-gel spin coating method. Zinc acetate (ZnAc) dehydrate was used as the starting salt material source. A homogeneous and stable solution was prepared by dissolving ZnAc in the solution of monoethanolamine (MEA). ZnO thin films were obtained after preheating the spin coated thin films at 250 °C for 5 min after each coating. The films, after the deposition of the eighth layer, were annealed in air at temperatures of 300 °C, 400 °C and 500 °C for 1 h. The effect of thermal annealing in air on the physical properties of the sol-gel derived ZnO thin films are studied. The powder and its thin film were characterized by X-ray diffractometer (XRD) method. XRD analysis revealed that the annealed ZnO thin films consist of single phase ZnO with wurtzite structure (JCPDS 36-1451) and show the c-axis grain orientation. Increasing annealing temperature increased the c-axis orientation and the crystallite size of the film. The annealed films are highly transparent with average transmission exceeding 80% in the visible range (400-700 nm). The measured optical band gap values of the ZnO thin films were between 3.26 eV and 3.28 eV, which were in the range of band gap values of intrinsic ZnO (3.2-3.3 eV). SEM analysis of annealed thin films has shown a completely different surface morphology behavior.     

High temperature STM/STS investigations of resonant image states on Au(1 1 1)

Scanning tunneling microscopy (STM) and spectroscopy (STS) were used to study the electronic structure of Au(1 1 1) surface in the range of 2-5.5 eV above the Fermi level. In this paper, we concentrate firstly on the position of the upper band gap edge (BE) existing in [1 1 1] direction in Au(1 1 1) and secondly on the position of the resonant image potential surface state (RIS) located in the bulk states approximately 1.1 eV above BE. The experiment was carried out in UHV at two temperatures 294 K and 580 K. Our high temperature STS (HT-STS) results clearly show the presence of RIS and BE local maxima at both temperatures. What is more, a slight shift towards the Fermi level of BE and RIS was observed. Those shifts were the consequence of the change of [1 1 1] band gap and lowering gold work function due to the thermal extension of interatomic distances. Finally, estimation of the work function was given at 294 K and 580 K.     

Surface electronic structure of the (3 × 2) reconstruction induced by Yb on a Si(1 1 1) surface

We have investigated the electronic structure of the Yb/Si(1 1 1)-(3 × 2) surface using angle-resolved photoelectron spectroscopy. Five surface states have been identified in the gap of the bulk band projection. Among these five surface state, the dispersions of three of them agree well with those of the surface states of monovalent atom adsorbed Si(1 1 1)-(3 × 1) surfaces. The dispersions of the two other surface states agree well with those observed on the Ca/Si(1 1 1)-(3 × 2) surface, whose basic structure is the same as that of monovalent atom adsorbed Si(1 1 1)-(3 × 1) surfaces. Taking these results into account, we conclude that the five surface states observed in the band gap originate from the orbitals of Si atoms that form a honeycomb-chain-channel structure.     

Structural and optical characterization of Ce-doped Gd2SiO5 films by sol-gel technique

Cerium-doped Gd₂SiO₅ (GSO:Ce) films have been prepared on (1 1 1) silicon substrates by the sol-gel technique. Annealing was performed in the temperature range from 400 to 1000 °C. X-ray diffraction (XRD), and atomic force microscopy (AFM) were used to investigate the structure and morphology of GSO:Ce films. Results showed that GSO:Ce film starts to crystallize at about 600 °C, GSO:Ce films have a preferential (0 2 1) orientation, as the annealing temperature increase, the (0 2 1) peak intensity increases, the full width of half maximum (FWHM) decreases, and the grain size of GSO:Ce films increases. Emission spectra of GSO:Ce films were measured, results exhibit the characteristic blue emission peak at 427 nm.     

Modeling the influence of the porosity of laser-ablated silicon films on their photoluminescence properties

Nanostructured porous Si-based films produced by pulsed laser ablation (PLA) from a silicon target in residual helium gas can exhibit both size-dependent (1.6-3.2 eV) and fixed photoluminescent (PL) bands (1.6 and 2.2 eV) with their relative contributions depending on the film porosity. We study the influence of prolonged oxidation in ambient air on properties of the fixed PL bands, associated with oxidation phenomena, and their correlation with structural properties of the films. In addition, we propose a model describing the appearance of surface radiation states for oxidized films of various porosities. Our experiments and numerical simulations led to a conclusion that the 1.6 eV PL is due to a mechanism involving a recombination through the interfacial layer between Si core and an upper oxide of nanocrystals. This mechanism gives the optimal porosity of 73% for the most efficient production of 1.6 eV PL centers that is in excellent agreement with our experimental results.