采用浸渍法制备了MnO_x/Al_2O_3低温脱硝催化剂,研究了Mn的含量对MnO_x/Al_2O_3催化剂低温烟气中NOx脱除率的影响,并通过XRD、SEM、BET、XPS、NH_3-TPD和H_2-TPR等手段对催化剂进行了表征.结果表明,当Mn含量为9%,空速为45 000 h-1时,MnO_x/Al_2O_3催化剂NO_x脱除率最高,在220℃时达79%;9MnO_x/Al_2O_3催化剂表面MnO_x氧化物分散较均匀,且稳定性及抗H_2O性能较好,但抗SO_2性能有待提高;MnO_x/Al_2O_3催化剂孔径主要分布在4~20 nm范围内,Mn含量对催化剂孔径变化影响较小;催化剂中活性组分Mn主要以Mn~(3+)和Mn~(4+)的形式存在;Mn~(4+)和Oα含量增加有利于NO_x的脱除;且添加Mn后,活性酸位点的数量增长,增强了催化剂还原能力,促进了NO_x脱除率的增加.     

焙烧温度对Mn/Al2O3-TiO2催化剂结构及氧化NO性能的影响

采用溶胶凝胶法和浸渍法制备10% Mn/Al₂O₃-TiO₂催化剂,借助TPO、XRD、O₂-TPD、Raman、XPS等手段,考察焙烧温度(450~650 ℃)对催化剂结构以及氧化NO性能的影响。TPO结果表明催化剂活性随焙烧温度的升高先增后减,其中焙烧温度为550 ℃时催化剂活性最好。XPS结果显示随着焙烧温度的升高(450~550 ℃),催化剂表面Mn³⁺的含量逐渐升高,与催化剂活性的强弱成对应关系,并且催化剂晶格氧含量下降,而表面化学吸附氧从40.9%增加到64.8%。Raman分析显示550 ℃焙烧时,催化剂表面存在丰富的Mn₂O₃活性物种,并且O₂-TPD分析也表明随着焙烧温度的升高,晶格氧向表面化学吸附氧流动,提高了化学吸附态氧物种的含量。这些结果表明Mn₂O₃可能是NO氧化起主要作用的活性Mn物种,释放更多的表面化学吸附氧物种,将有助于促进NO的催化氧化。     

预处理条件对Pt/Al2O3催化还原NO的活性影响

用溶胶-凝胶法制备Al2O3载体,浸渍法制备质量分数为0.5%的Pt/Al2O3催化剂.研究焙烧气氛和温度对选择性催化还原NO反应活性和Pt价态的影响.结果表明,H2焙烧的活性温度区间最宽,随着焙烧温度的升高,温度区间变化很小,523K下O2焙烧的催化剂活性最好,且活性区间向高温方向移动.活性现象用程序升温脱附实验(NO-TPD,NO-O2-TPD)进行了解释.XPS研究表明,523K下O2用焙烧Pt的主要价态是Pt2+,而523K下H2和N2焙烧Pt的主要价态为Pt0.     

富氧条件下Cu/Al2O3催化剂上C3H6选择性还原NO的研究

以Cu/Al2O3为催化剂,对富氧条件下C3H6为还原剂选择性催化还原NO反应进行了研究.活性评价结果表明,与高活性的Ag/Al2O3催化剂相比,Cu/Al2O3催化剂选择性还原NO的活性较低,NO的最高转化率仅为40%.在所考察的温度范围(473～723K)内,红外谱图中不存在有机含氮化合物(R—ONO和R—NO2)的特征振动吸收峰.作为反应中间体—NCO的前驱体,有机含氮化合物在Cu/Al2O3催化剂表面难以生成是造成催化剂选择性还原NO活性低的直接原因.在Cu/Al2O3催化剂上,NO2吸附能够优先发生,并以NO3-物种的形式覆盖在大部分催化剂表面.动态原位红外光谱实验发现,这种NO3-表面物种与C3H6的反应性较差,使生成有机含氮化合物的关键反应难以发生,但此时的催化剂表面有利于C3H6和O2的完全氧化反应,这是导致Cu/Al2O3催化剂选择性较低的根本原因.     

K2CO3含量对Ni-Cu-Mn-K/Al2O3水煤气变换催化剂结构和性能的影响

以γ-Al₂O₃为载体，采用等体积浸渍法，制备了不同K₂CO₃含量的Ni-Cu-Mn-K/Al₂O₃水煤气变换催化剂，采用低温N₂吸附、XRD、TPD和TPR，考察了K₂CO₃含量对催化剂结构和性能的影响。结果表明:K₂CO₃的加入使催化剂的还原温度有所提高，适量的K₂CO₃能增加活性组分的电子密度，从而增强其给电子活化CO的能力，提高催化剂的活性。但过量的K₂CO₃使得催化剂比表面积和孔容降低，且导致催化剂对CO吸附过强，催化活性降低。当Ni-Cu-Mn-K/γ-Al₂O₃催化剂中K₂CO₃的添加量为7.5%时，且催化剂经530 ℃耐热15 h后，在350 ℃时水煤气变换反应中CO转化率达62.29%。     

不同金属负载对Cr/Al2O3-TiO2催化剂结构及氧化NO性能的影响

采用溶胶-凝胶法和浸渍法制备Cr/Al_2O_3-TiO_2催化剂,在考察不同Cr负载量的基础上,研究不同金属负载与焙烧温度对Cr/Al_2O_3-TiO_2催化剂结构与性能影响。程序升温氧化(TPO)结果表明,当Cr负载量为10%(w/w)时具有较好的催化活性;不同金属负载Cr/Al_2O_3-TiO_2时,负载Co及在焙烧温度为550℃时催化剂具有较好的活性。通过程序升温还原(H_2-TPR)表征发现,Co的负载使催化剂的低温氧化还原能力逐渐提高,表明Co-Cr具有较好的协同催化作用。X射线光电子能谱(XPS)表征表明,Co增加了Cr~(6+)和表面吸附氧(O_β)含量,随着焙烧温度的升高(450～550℃),晶格氧不断向催化剂表面流动,表面化学吸附氧O_β比例逐渐增加,导致催化活性不断升高,说明Cr~(6+)和O_β是催化氧化NO的重要活性物种。     

Ce0.67Zr0.33O2对CH4燃烧催化剂Fe2O3/Al2O3的改性作用

固定n(Ce)/n(Zr)比为0.67/0.33,用共沉淀法制得一系列CeO2-ZrO2-Al2O3固溶体.采用这些固溶体作载体,以Fe2O3为活性组分,用浸渍法制备了一系列催化剂.BET结果显示,将适量Ce0.67Zr0.33O2引入到Al2O3载体中有助于催化剂保持较高的比表面积.TPR结果显示,载体中引入适量的Ce0.67Zr0.33O2可以改善催化剂的氧化还原性能.XRD结果表明,Fe2O3在CeO2-ZrO2-Al2O3载体上呈现出良好的分散状况,老化前后催化剂的晶相结构基本无明显变化.特别是当载体中m(Ce0.67Zr0.33O2)∶m(Al2O3)的值为1∶2时,Fe2O3/CeO2-ZrO2-Al2O3催化剂在甲烷催化燃烧中显示出最佳的催化性能和抗高温老化性能.     

有机配体修饰纳米Al2O3的合成及性质研究

合成了以β-二酮配体3-甲基-1-苯基-4-(十八烷基酰基)吡唑啉酮-5(PMOP)修饰的Al2O3纳米粒子,并用IR、UV光谱、NMR和荧光光谱等手段进行了表征.修饰后的Al2O3纳米粒子能溶于氯仿、乙醇和甲苯等常见有机溶剂,并有较强的蓝色荧光.表明在一些无机纳米粒子的表面键合上有机配体后,可以产生新的光物理性质.修饰后的Al2O3纳米粒子还可作为支架材料用于准固态染料敏化纳米晶太阳能电池中.     

Fe2O3/Al2O3二元气凝胶合成高质量单壁纳米碳管

通过溶胶和超临界干燥方法制得了Fe₂O₃/Al₂O₃二元气凝胶，其比表面积和孔隙体积分别为246 m²·g^-1和1.89 cm³·g^-1，并具有较宽的孔径分布。以Fe₂O₃/Al₂O₃二元气凝胶作催化剂，通过甲烷催化裂解成功地合成了高质量的单壁纳米碳管。利用FESEM、TEM和HRTEM、Raman光谱等分析手段研究了反应温度对单壁纳米碳管生长的影响。结果表明在900 ℃时合成单壁纳米碳管的质量较高，并且合成的炭产物为毡状，该炭产物主要为高质量的单壁纳米碳管。     

TiO2微粒功能化多孔Al2O3膜的光电化学研究

用恒电位法制备了多孔Al₂O₃薄膜, 通过在Al₂O₃薄膜孔内水蒸汽水解钛酸异丙酯生成了锐钛矿型TiO₂微粒, 制备出了Al₂O₃与TiO₂微粒的复合薄膜. 用XRD, SEM, 光电化学方法进行了研究. 实验表明: 该复合薄膜具有光电转换特性, 在光催化、光电化学太阳能转换中具有应用价值.     

Thermal Stability of Pt/Al2O3 Catalysts Prepared by Sol-Gel

A series of Pt/Al₂O₃ catalysts were prepared using a sol-gel method. The influence of several parameters used in the synthesis including: metal content, identity of the metal precursor, and the water/alkoxide ratio on the structural properties of the fresh (dried) and calcined samples were studied. It was found that the BET surface area decreased with an increase in the platinum content. A surface area of 500 m²/g was obtained following calcination at 773 K. The structure of fresh samples as determined by FTIR corresponded to that of a pseudoboehmite structure. Samples prepared using a water/alkoxide ratio (H₂O/ATB) of 9 showed a well-defined, uniform pore size distribution following calcination at 773 K. Metal dispersions comparable to those obtained using impregnation methods were obtained. Aging studies (calcination at 873 K for 24 h) performed on these catalysts, exhibited sintering behavior which were similar to Pt/Al₂O₃ catalysts prepared by other methods. The sample prepared using a H₂O/ATB ratio of 9 had the highest surface area and was more thermally resistant towards metal sintering. A bimodal metal particle size distribution was observed: some particles exhibited sintering while others of similar size showed a greater thermal stability to sintering. The sample having the largest surface area and the highest thermal stability following thermal treatment was a consequence of a more condensed structure and a higher pore roughness obtained after drying the gel. This enabled the formation of an alumina structure which was more amorphous and limited aggregation of platinum particles due to surface diffusion within the pore structure.     

焙烧温度对Mn/Al2O3-TiO2催化剂结构及氧化NO性能的影响

采用溶胶凝胶法和浸渍法制备10%Mn/Al_2O_3-TiO_2催化剂,借助TPO、XRD、O_2-TPD、Raman、XPS等手段,考察焙烧温度(450~650℃)对催化剂结构以及氧化NO性能的影响。TPO结果表明催化剂活性随焙烧温度的升高先增后减,其中焙烧温度为550℃时催化剂活性最好。XPS结果显示随着焙烧温度的升高(450~550℃),催化剂表面Mn~(3+)的含量逐渐升高,与催化剂活性的强弱成对应关系,并且催化剂晶格氧含量下降,而表面化学吸附氧从40.9%增加到64.8%。Raman分析显示550℃焙烧时,催化剂表面存在丰富的Mn_2O_3活性物种,并且O_2-TPD分析也表明随着焙烧温度的升高,晶格氧向表面化学吸附氧流动,提高了化学吸附态氧物种的含量。这些结果表明Mn_2O_3可能是NO氧化起主要作用的活性Mn物种,释放更多的表面化学吸附氧物种,将有助于促进NO的催化氧化。     

Fischer-Tropsch synthesis over Ru/Al2O3 catalysts

Fischer-Tropsch syntheses (FTS) were carried out in a slurry phase over Ru/Al₂O₃ catalysts using hexadecane as a solvent. The outcome of the FTS was dependent on the oxide support, calcination temperature, synthesis gas composition and sulfur content. The addition of Mn/Na to Ru/Al₂O₃ was effective in raising the initial activity and C5+ selectivity, but after 20 hours, the performance of the modified catalyst was similar to that of the unmodified catalyst. An additional investigation involving the use of fresh vs used catalysts demonstrated that an agglomeration of the metallic Ru, at least in part, does occur during the reaction.     

改性介孔Al_2O_3负载的高分散铜基催化剂的结构与催化性能

采用浸渍法制备了LaCeZr或YCeZr改性的γ-Al2O3负载的系列Cu基催化剂,运用XRD、BET、EXAFS、XPS和H2-TPR等技术对催化剂的结构进行了详细表征,探讨了催化剂中Cu物种的存在形式及其还原性能,并与CO的氧化性能相关联。氮气吸附-脱附测试结果表明,催化剂具有很高的比表面积以及较均一的介孔结构。XRD结果表明,未改性的γ-Al2O3负载的Cu基催化剂经800℃高温焙烧后,Cu物种与载体作用强烈,形成了CuAl2O4尖晶石相,而EXAFS结果显示,助剂改性后的γ-Al2O3负载的Cu基催化剂上Cu物种主要以高分散的CuO形式存在,促进了催化剂对CO的低温氧化性能。H2-TPR结果表明,同一系列样品随焙烧温度提高,CuO的还原温度升高,晶格氧的活动度降低,导致活性的下降。LaCeZr改性的γ-Al2O3负载的铜基催化剂于650℃焙烧后显示出了较强的抗硫和抗水性能。     

纳米膜组装介孔Al2O3：合成及Pt/Al2O3的硝基苯催化加氢性能

以"乙酸乙酯(EA)-偏铝酸钠-水"体系在室温下合成了纳米膜组装介孔Al2O3。研究发现:合成反应时间、静置前搅拌时间、NaAlO2用量、EA用量及反应温度等对合成产物的形貌有影响;另外,与用商品γ-Al2O3制备的Pt/γ-Al2O3催化剂相比,纳米膜组装介孔Al2O3制备的Pt/Al2O3催化剂含有部分易被还原的PtOx物种。在硝基苯催化加氢反应中,用合成Al2O3为载体制备的Pt/Al2O3催化剂,比用商品γ-Al2O3制备的Pt/γ-Al2O3催化剂具有更好的催化活性。