The inhibitive effect of bipyrazolic derivatives on the corrosion of steel in hydrochloric acid solution

The effect of two pyrazole-type organic compounds, namely ethyl 5,5′-dimethyl-1′H-1,3′-bipyrazole-3 carboxylate (P1) and 3,5,5′-trimethyl-1′H-1,3′-bipyrazole (P2) on the corrosion behaviour of steel in 1 M hydrochloric acid (HCl) solution is investigated at 308 K by weight loss measurements, potentiodynamic polarisation and impedance spectroscopy (EIS) methods. The inhibition efficiencies obtained from cathodic Tafel plots, gravimetric and EIS methods are in good agreement. Results obtained show that the compound P2 is the best inhibitor and its efficiency reaches 84% at 10⁻³ M. Potentiodynamic polarisation studies show that pyrazolic derivatives are cathodic-type inhibitors and these compounds act on the cathodic reaction without changing the mechanism of the hydrogen evolution reaction. The inhibition efficiency of P2 is temperature-dependent in the range from 308 to 353 K and the associated activation energy has been determined. P2 adsorbs on the steel surface according to Langmuir adsorption model. The calculation of the total partial charge of inhibitor atoms is computed.     

Investigation of the inhibitive effect of triphenyltin 2-thiophene carboxylate on corrosion of steel in 2 M H3PO4 solutions

A new organic compound was synthesised and tested as corrosion inhibitor of steel in phosphoric acid medium using gravimetric, electrochemical polarisation and electrochemical impedance spectroscopy (EIS) measurements. Results obtained show that the inhibitor studied is a good cathodic inhibitor. EIS results show that the change in the impedance parameters (R_T and C_dl) with concentration of triphenyltin 2-thiophene carboxylate (TTC) is indicative of the adsorption of molecules leading to the formation of a protective layer on the surface of steel. The effect of the temperature on the steel corrosion in 2 M H₃PO₄ and with addition of various concentrations of TTC in the range of temperature 298-348 K was studied. The associated apparent activation corrosion energy has been determined.     

Inhibition of steel corrosion in 2 M H3PO4 by artemisia oil

Artemisia oil (Ar) is extracted from artemisia herba alba collected in Ain es-sefra-Algeria, and tested as corrosion inhibitor of steel in 2 M H₃PO₄ using weight loss measurements, electrochemical polarisation and EIS methods. The naturally oil reduces the corrosion rate. The inhibition efficiency was found to increase with oil content to attain 79% at 6 g/l. Ar acts as a cathodic inhibitor. The effect of temperature on the corrosion behaviour of steel indicates that inhibition efficiency of the natural substance decreases with the rise of temperature. The adsorption isotherm of natural product on the steel has been determined.     

Electrochemical and quantum chemical studies of some Schiff bases on the corrosion of steel in H2SO4 solution

The efficiency, as steel-corrosion inhibitors in 0.1 M and 1 M H₂SO₄, of two Schiff bases, 2-{[(4-methoxyphenyl)imino]methyl}phenol and 1-{[(4-methoxyphenyl)imino]methyl}-2-naphthol, (abbreviated SB-1 and SB-2, respectively) was investigated by Tafel extrapolation and linear polarization methods. Corrosion parameters and adsorption isotherms were determined from current-potential curves. It was found that the percent inhibition efficiencies (η%) and surface coverage (θ) increase with an increases in the concentrations of inhibitors. The results showed that these compounds act as good corrosion inhibitors especially at high concentrations. The adsorption of used compounds on the steel surface obeys Langmuir's isotherm. Obvious correlation was found between corrosion inhibition efficiency and quantum chemical parameters obtained by B3LYP/6-31g(d) method. The obtained theoretical results have been compared with the experimental findings.     

Enhanced corrosion resistance of mild steel in normal sulfuric acid medium by 2,5-bis(n-thienyl)-1,3,4-thiadiazoles: Electrochemical, X-ray photoelectron spectroscopy and theoretical studies

The inhibitive action of some thiadiazole derivatives, namely 2,5-bis(2-thienyl)-1,3,4-thiadiazole (2-TTH) and 2,5-bis(3-thienyl)-1,3,4-thiadiazole (3-TTH) against the corrosion of mild steel in 0.5 M H₂SO₄ solution has been investigated using weight loss measurements, Tafel polarisation and electrochemical impedance spectroscopy (EIS) techniques. The experimental results obtained revealed that these compounds inhibited the steel corrosion in acid solution. The protection efficiency increased with increasing inhibitors concentration and the ability of the molecule to adsorb on the steel surface was dependent on the position of the sulphur atom on the thienyl substituent. Inhibition efficiency values obtained from various methods employed were in reasonable agreement. Potentiodynamic polarisation studies clearly showed that 2-TTH and 3-TTH acted as mixed inhibitors. Adsorption of these inhibitors on steel surface obeyed to Langmuir adsorption isotherm. X-ray photoelectron spectroscopy and the thermodynamic data of adsorption showed that inhibition of steel corrosion in normal sulphuric solution by n-TTH is due to the formation of a chemisorbed film on the steel surface. Molecular modelling was used to gain some insight, about structural and electronic effects in relation to the inhibiting efficiencies.     

Berberine as a natural source inhibitor for mild steel in 1 M H2SO4

Berberine was abstracted from coptis chinensis and its inhibition efficiency on corrosion of mild steel in 1 M H₂SO₄ was investigated through weight loss experiment, electrochemical techniques and scanning electronic microscope (SEM) with energy disperse spectrometer (EDS). The weight loss results showed that berberine is an excellent corrosion inhibitor for mild steel immersed in 1 M H₂SO₄. Potentiodynamic curves suggested that berberine suppressed both cathodic and anodic processes for its concentrations higher than 1.0 × 10⁻⁴ M and mainly cathodic reaction was suppressed for lower concentrations. The Nyquist diagrams of impedance for mild steel in 1 M H₂SO₄ containing berberine with different concentrations showed one capacitive loop, and the polarization resistance increased with the inhibitor concentration rising. A good fit to Flory-Huggins isotherm was obtained between surface coverage degree and inhibitor concentration. The surface morphology and EDS analysis for mild steel specimens in sulfuric acid in the absence and presence of the inhibitor also proved the results obtained by the weight loss and electrochemical experiments. The correlation of inhibition effect and molecular structure of berberine was then discussed by quantum chemistry study.     

Inhibition of copper corrosion by bis-(1,1′-benzotriazoly)-α,ω-diamide compounds in aerated sulfuric acid solution

Three kinds of novel corrosion inhibitors, bis-(1,1′-benzotriazoly)-α,ω-succinyldiamide (BSU), bis-(1,1′-benzotriazoly)-α,ω-adipoyldiamide (BAD), and bis-(1,1′-benzotriazoly)-α,ω-azelayldiamide (BAZ) were synthesized and certified by IR and ¹H NMR. Their corrosion inhibition effects for copper in 0.5 M H₂SO₄ were evaluated by weight-loss method. It shows that among the three compounds, only BSU behaves better compared with BTA. The inhibition efficiency (IE) increased with increasing BSU concentration to 85.2% at the 5 × 10⁻⁴ M level. Polarization studies showed that BSU suppressed both anodic and cathodic corrosion reactions. The minimum energy conformation of these compounds was obtained by MM2 force field program. The two benzotriazoly moieties in BSU molecule are more parallel than in other compounds. This is benefit to increase the inhibition effects of BSU.     

Inhibiting effects of some oxadiazole derivatives on the corrosion of mild steel in perchloric acid solution

The efficiency of 3,5-bis(n-pyridyl)-1,3,4-oxadiazole (n-POX, n = 1, 2, 3), as corrosion inhibitors for mild steel in 1 M perchloric acid (HClO₄) have been determined by weight loss measurements and electrochemical studies. The results show that these inhibitors revealed a good corrosion inhibition even at very low concentrations. Comparison of results among those obtained by the studied oxadiazoles shows that 3-POX was the best inhibitor. Polarisation curves indicate that n-pyridyl substituted-1,3,4-oxadiazoles are mixed type inhibitors in 1 M HClO₄. The adsorption of these inhibitors follows a Langmuir isotherm model. The electronic properties of n-POX, obtained using the AM1 semi-empirical quantum chemical approach, were correlated with their experimental efficiencies using the linear resistance model (LR).     

Synergistic effect between 4-(2-pyridylazo) resorcin and chloride ion on the corrosion of cold rolled steel in 0.5 M sulfuric acid

The corrosion inhibition of 1-(2-pyridylazo)-2-naphthol (PAR) on the corrosion of cold rolled steel in 0.5 M sulfuric acid (H₂SO₄) was studied using weight loss method and potentiodynamic polarization method. Results obtained revealed that together with chloride ion, PAR is an effective corrosion inhibitor for steel corrosion in sulfuric acid. It was found that for steel corrosion inhibition in the presence of single PAR in sulfuric acid the Temkin adsorption isotherm may be used to explain the adsorption phenomenon. For the mixture of PAR and NaCl used as corrosion inhibitor, however, the Langmuir adsorption isotherm can be used to satisfactorily elucidate the adsorption of mixture of PAR and NaCl. Potentiodynamic polarization studies showed that single PAR mainly acts as a cathodic inhibitor for the corrosion of steel in 0.5 M sulfuric acid. The mixture of PAR and chloride ion, however, acts as a mixed type inhibitor that mainly inhibits cathodic reaction of the steel corrosion in sulfuric acid. By means of electrochemical polarization tests, a desorption potential at ca. −370 mV was observed for the adsorption of mixture of PAR and chloride ion, when potential reaches this value, adsorbed inhibitor molecule heavily departs from the steel surface. For the mixture of PAR and chloride ion, thermodynamic parameters such as adsorption heat, adsorption entropy and adsorption free energy were obtained from experimental data of the temperature studies of the inhibition process at four temperatures ranging from 30 to 45 °C, the kinetic data such as apparent activation energies and pre-exponential factors at different concentrations of the inhibitor were calculated, and the effect of the apparent activation energies and pre-exponential factors on the corrosion rates of cold rolled steel was discussed. The most suitable range of inhibitor concentration was discussed. The inhibitive action was satisfactorily explained by using both thermodynamic and kinetic models. Synergism between chloride ion and PAR was proposed. The results obtained from weight loss and potentiodynamic polarization were in good agreement.     

Synergistic effect of iodide ions on the corrosion inhibition of steel in 0.5 M H2SO4 by new chalcone derivatives

The effect of addition of 4′,4-dihydroxychalcone (P₁), 4-aminochalcone (P₂) and 4-bromo, 4′-methoxychalcone (P₃) on the corrosion of steel in 0.5 M sulphuric acid has been studied by weight loss measurements, potentiodynamic and EIS measurements. We investigate the synergistic effect of iodide ions on the corrosion inhibition of steel in the presence of chalcone derivatives. The corrosion rates of the steel decrease with the increase of the chalcones concentration, while the inhibition efficiencies increase. The addition of iodide ions enhances the inhibition efficiency considerably. The presence of iodide ions increases the degree of surface coverage. The synergism parameters S_Θ and S_I, calculated from surface coverage and the values of inhibition efficiency, in the case of chalcone derivatives are found to be larger than unity. The enhanced inhibition efficiency in the presence of iodide ions is only due to synergism and there is a definite contribution from the inhibitors molecules. E (%) obtained from the various methods is in good agreement. Polarisation measurements show also that the compounds act as cathodic inhibitors.     

Electrochemical, SEM/EDS and quantum chemical study of phthalocyanines as corrosion inhibitors for mild steel in 1 mol/l HCl

The inhibition effect of metal-free phthalocyanine (H₂Pc), copper phthalocyanine (CuPc) and copper phthalocyanine tetrasulfuric tetrasodium salt (CuPc·S₄·Na₄) on mild steel in 1 mol/l HCl in the concentration range of 1.0 × 10⁻⁵ to 1.0 × 10⁻³ mol/l was investigated by electrochemical test, scanning electron microscope with energy dispersive spectrometer (SEM/EDS) and quantum chemical method. The potentiodynamic polarization curves of mild steel in hydrochloric acid containing these compounds showed both cathodic and anodic processes of steel corrosion were suppressed, and the Nyquist plots of impedance expressed mainly as a capacitive loop with different compounds and concentrations. For all these phthalocyanines, the inhibition efficiency increased with the increase in inhibitor concentration, while the inhibition efficiencies for these three phthalocyanines with the same concentration decreased in the order of CuPc·S₄·Na₄ > CuPc > H₂Pc according to the electrochemical measurement results. The SEM/EDS analysis indicated that there are more lightly corroded and oxidative steel surface for the specimens after immersion in acid solution containing 1.0 × 10⁻³ mol/l phthalocyanines than that in blank. The quantum chemical calculation results showed that the inhibition efficiency of these phthalocyanines increased with decrease in molecule's LUMO energy, which was different from the micro-cyclic compounds.     

Synthesis and electrochemical characteristics of Ta-N thin films fabricated by cathodic arc deposition

Ta-N thin films were deposited on AISI 317L stainless steel (SS) substrates by cathodic arc deposition (CAD) at substrate biases of −50 and −200 V. The as-deposited films were characterized using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and energy dispersive X-ray analysis (EDX). The results show that stoichiometric TaN with hexagonal lattice (3 0 0) preferred orientation was achieved at the bias of −200 V. On the other hand, Ta-rich Ta-N thin film deposited at −50 V shows amorphous nature. According to the XPS result, Ta element in the films surface exist in bonded state, including the Ta-N bonds characterized by the doublet (Ta 4f_7/2 = 23.7 eV and Ta 4f_5/2 = 25.7 eV). Electrochemical properties of the Ta-N coated stainless steel systems were investigated using potentiodynamic polarization and electrochemical impedance spectroscope (EIS) in Hank's solution at 37 °C. For the Ta-N coated samples, the corrosion current (i_corr) is two or three orders of magnitude lower than that of the uncoated ones, indicating a significantly improved corrosion resistance. Growth defects in the Ta-N thin films produced by CAD, however, play a key role in the corrosion process, especially the localised corrosion. Using the polarization fitting and the EIS modelling, we compared the polarization resistance (R_p) and the porosity (P) of the Ta-N coatings deposited at different biases. It seems that Ta-N film with comparatively lower bias (−50 V) shows better corrosion behavior in artifical physiological solution. That may be attributed to the effect of ion bombarding, which can be modulated by the substrate bias.     

Electrochemical and theoretical investigation on the corrosion of aluminium in acidic solution containing some Schiff bases

The effect of newly synthesised three Schiff bases—2-[2-aza-2-(5-methyl(2-pyridly))vinyl]phenol, 2-[2-aza-2-(5-methyl(2-pyridly))vinyl]-4-bromophenol, 2-[2-aza-2-(5-methyl(2-pyridly))vinyl]-4-chlorophenol—on the corrosion behaviour of aluminium in 0.1 M HCl were investigated using potentiodynamic polarisation, electrochemical impedance spectroscopy and linear polarisation methods. Polarisation curves indicate that all studied Schiff bases were acting as mixed type inhibitors. All measurements show that inhibition efficiencies increase with increase in inhibitor concentration. This reveals that inhibitive actions of inhibitors were mainly due to adsorption on aluminium surface. Adsorption of these inhibitors follows Langmuir adsorption isotherm. Thermodynamic parameters of adsorption (K_ads, ΔG_ads) of studied Schiff bases were calculated using Langmuir adsorption isotherm. The variation in inhibition efficiency values depends on the type of functional groups substituted on benzene ring. It was found that the presence of bromine and chlorine atoms in the molecular structure of studied Schiff bases facilitate the adsorption of molecule on aluminium surface.The correlation between the inhibition efficiencies of studied Schiff bases and their molecular structure has been investigated using quantum chemical parameters obtained by MNDO semi-empirical SCF-MO methods. These results indicate that adsorption of studied Schiff bases depends on the charge density of adsorption centres and dipole moments.     

Understanding the adsorption of 4H-1,2,4-triazole derivatives on mild steel surface in molar hydrochloric acid

This study examines the use of some 4H-triazole derivatives, namely 3,5-diphenyl-4H-1,2,4-triazole (DHT), 3,5-bis(4-pyridyl)-4H-1,2,4-triazole (4-PHT) and 3,5-bis(4-methyltiophenyl)-4H-1,2,4-triazole (4-MTHT) for corrosion and dissolution protection of mild steel in normal hydrochloric acid solution. The inhibiting efficiency of the different additives is evaluated by means of weight loss and electrochemical techniques such as ac impedance measurements and polarisation curves. The experimental results obtained reveal that 4-MTHT is the best effective inhibitor and the inhibition efficiency is found to be in the following order: 4-MTHT > 4-PHT > DHT. The variation in inhibitive efficiency mainly depends on the type and nature of the substituents present in the inhibitor molecule. Polarisation curves show that theses triazoles are mixed-type inhibitors in 1 M HCl. The inhibition efficiency increases with 4H-triazole derivatives concentration and attains the maximum value of 99.6% in the case of 4-MTHT at 5 × 10⁻⁴ M. The results obtained from weight loss electrochemical studies were in reasonable agreement. The adsorption of 4H-triazole derivatives on the steel surface obeys to the Langmuir isotherm model. The thermodynamic data of adsorption and activation are determined and discussed. The fundamental thermodynamic functions were used to glean important information about the 4H-triazoles inhibitory behaviour. Molecular modeling was used to get better insight, about structural and electronic effects in relation to the inhibition efficiencies.     

Corrosion inhibition of steel in 0.5 M H2SO4 by [(2-pyridin-4-ylethyl)thio]acetic acid

The influence of [(2-pyridin-4-ylethyl)thio]acetic acid (P1) and pyridine (P2) on the corrosion inhibition of steel in sulphuric acid solution is studied using weight loss, potentiodynamic polarisation and linear polarisation resistance (R_p) and electrochemical impedance spectroscopy (EIS) measurements. Results obtained show that P1 is the best inhibitor and its inhibition efficiency (E%) increases with the increase of concentration. The highest E% of 82% is observed at 5 × 10⁻³ M. Potentiodynamic polarisation studies clearly reveal that P1 acts as a mixed inhibitor. The inhibitor studied reduces the corrosion rates. E% values obtained from various methods used are in good agreement. Adsorption of P1 on steel surface obeys to Langmuir adsorption isotherm. Effect of temperature indicates that E% decreases with temperature between 298 and 353 K.     

The inhibited effect of some tetrazolic compounds towards the corrosion of brass in nitric acid solution

The effect of the addition of some tetrazolic type organic compounds: 1-phenyl-5-mercapto-1,2,3,4-tetrazole (PMT), 1,2,3,4-tetrazole (TTZ), 5-amino-1,2,3,4-tetrazole (AT) and 1-phenyl-1,2,3,4-tetrazole (PT) on the corrosion of brass in nitric acid is studied by weight loss, polarisation and electrochemical impedance spectroscopy (EIS) measurements. The explored methods gave almost similar results. Results obtained reveal that PMT is the best inhibitor and the inhibition efficiency (E%) follows the sequence: PMT > PT > AT > TTZ. Polarization measurements also indicated that tetrazoles acted as mixed-type inhibitors without changing the mechanism of the hydrogen evolution reaction. Partial π-charge on atoms has been calculated. Correlation between the highest occupied molecular orbital energy E_HOMO and inhibition efficiencies was sought. The adsorption of PMT on the brass surface followed the Langmuir isotherm. Effect of temperature is also studied in the (25-50 °C) range.     

Analysis of EIS characteristics of CO2 corrosion of well tube steels with corrosion scales

The electrochemical impedance spectroscopy (EIS) was used to study the characteristics of CO₂ corrosion of N80 and 4Cr steels with corrosion scales. The results indicated that CO₂ corrosion scale on tube steel could prevent the rate of mass transfer remarkably, corrosion rate was controlled by ions diffusion in corrosion scale, which led to finite length diffusion impedance occurred in electrochemical impedance spectra. Additionally, pitting of N80 steel could lead to additional capacitive reactance in impedance spectrum. The ion diffusion coefficient in corrosion scale and porosity of corrosion scale could be calculated by Warburg impedance coefficient, the results shown that the value of H⁺ diffusion coefficient in N80 and 4Cr corrosion scale is (3.46 and 1.76) × 10⁻¹⁰ m² s⁻¹, respectively. The protective ability of 4Cr corrosion scale was better than that of N80 corrosion scale.     

Inhibition of iron corrosion in 0.5 M sulphuric acid by metal cations

Corrosion inhibitors are widely used in acid solutions during pickling and descaling. Mostly organic compounds containing N, O, and S groups are employed as inhibitors. In this study, the inhibition performance of metal cations such as Zn²⁺, Mn²⁺ and Ce⁴⁺ ions in the concentration range 1-10 × 10⁻³ M has been found out. The corrosion behaviour of iron in 0.5 M H₂SO₄ in the presence of metal cations is studied using polarization and impedance methods. It is found that the addition of these metal cations inhibits the corrosion markedly. The inhibition effect is in the following order Ce⁴⁺ ? Mn²⁺ > Zn²⁺.     

Influence of treating frequency on microstructure and properties of Al2O3 coating on 304 stainless steel by cathodic plasma electrolytic deposition

Alumina ceramic coatings were fabricated on 304 stainless steel by cathodic plasma electrolytic deposition (CPED). Influence of treating frequency of the power supply on the microstructure and properties of the coatings were studied. The results indicated that coatings obtained at various frequencies on 304 stainless steels were all composed of α-Al₂O₃ and γ-Al₂O₃, and α-Al₂O₃ was the dominant phase. The contents of α-Al₂O₃ decreased gradually in a very small rate with increasing the frequency and γ-Al₂O₃ gradually increased. The surface of alumina ceramic coating was porous. With increasing the frequency, the coating surface gradually became less rough and more compact, resulting in low surface roughness. The bonding strength of Al₂O₃ coating was higher than 22 MPa and was not strongly affected by treating frequency. With increasing the frequency, the alumina coated steels showed better and gradually increasing corrosion resistance than the uncoated one in 3.5% NaCl solution. The coating steel with desirable corrosion resistance was obtained at 800 Hz whose corrosion current potential and corrosion density were −0.237 V and 7.367 × 10⁻⁸ A/cm², respectively.     

Influence of Ni deposition and subsequent N ion implantation at different substrate temperatures on nano-structure and corrosion behaviour of type 316 and 304 stainless steels

Ni thin films of 250 nm thicknesses were coated on type 304 and 316 stainless steels and post N⁺ ion implanted at 15 keV energy with a fluence of 5 × 10¹⁷ N⁺ cm⁻² at different substrate temperatures. Surface nano-structure of the samples were analysed using X-ray diffraction (XRD), atomic force microscopy (AFM) before corrosion test and scanning electron microscopy (SEM) after corrosion test. Corrosion behaviour of the samples in 1.0 M H₂SO₄ solution was investigated by means of potentiodynamic technique. Nano-structure and crystallography of the films showed the development of Ni₃N(1 1 1) and Ni₄N(2 0 0) orientations with a minimum surface roughness and grain size at 400 K substrate temperature. The highest corrosion resistance with a corrosion current of 0.01 μA cm⁻² (for SS(316)) and 0.56 μA cm⁻² (for SS(304)) was achieved in case of samples which were N⁺ ion implanted at 400 K. Results for both types of stainless steels showed good agreement and the better performance of SS(316) was attributed to the 2% molybdenum contents in the alloy composition of this type of stainless steel, which enhances the effectiveness of nitrogen in retarding the corrosion process.