Ag对Pd/CeO2-ZrO2-La2O3-Al2O3催化氧化甲醇性能的影响

采用等体积共浸渍法制备了一系列Pd-Ag/CeO2-ZrO2-La2O3-Al2O3催化剂。运用N2吸附-脱附,X射线衍射(XRD),H2程序升温还原(H2-TPR),紫外-可见漫反射光谱(UV-Vis DRS),X射线光电子能谱(XPS)对催化剂进行表征,并考察其对甲醇的催化氧化性能。活性测试结果表明,Ag的添加可显著改善Pd催化剂对甲醇的催化氧化活性,T50、T90以及ΔT分别为125℃,150℃和25℃,具有较好的应用前景。H2-TPR表明,引入Ag可明显改善催化剂的还原性能,使表面易还原氧物种量增多,还原速率加快;UV-Vis DRS及XPS表明,Pd、Ag金属之间以及金属与载体之间存在电子效应,这种效应促使金属与载体界面产生大量具有活性的氧物种,不仅提高了催化剂的低温活性,还提高了催化剂的氧化速率。     

浸渍/共沉淀法对BaO改性单Pd催化剂净化甲醇汽油车尾气性能的影响(英文)

采用浸渍和共沉淀两种方法分别制备了Ba O改性的Pd/CeO2-ZrO2-La2O3-Al2O3催化剂。运用N2吸附-脱附,X射线衍射(XRD),H2程序升温还原(H2-TPR),NH3程序升温脱附(NH3-TPD),透射电子显微镜(TEM)和X射线光电子能谱(XPS)对催化剂进行表征,并考察其对甲醇,CO,C3H8和NO的催化性能。活性测试结果表明,Ba O的引入可明显改善Pd催化剂对甲醇,CO,C3H8和NO的催化活性,且浸渍法最佳,起燃温度(T50)分别降低了43,31,45和35℃。XRD,H2-TPR及XPS结果表明,浸渍法引入Ba O主要通过表面改性方式,强化Pd-Ce界面间的相互作用,改善催化剂的还原性能,进而提高催化剂的低温活性;而共沉淀法则是通过结构改性方式增加CeO2晶格缺陷,加速活性氧物种的流动,Ce3+浓度的增加是促使CO氧化活性显著提高的主要原因。     

贫燃条件 In-Ag/TiO2-γ-Al2O3催化 CO选择性还原NO

汽车尾气中主要污染成分 CO和 NOx可导致酸雨、光化学烟雾和臭氧空洞效应,对生物、环境及生态系统造成重大危害。污染源中 CO是性能优良的还原剂,如能不添加还原剂实现 CO催化还原 NOx,将成为最具经济技术优势的 NOx脱除技术。在富氧、低温条件下,利用 CO选择性催化还原 NOx为 N2,是目前选择性催化还原研究中的热点和难点。催化 CO还原 NOx常用的贵金属 Ir, Rh, Pt和Pd矿藏稀少,价格昂贵,有氧条件下活性急降,而分子筛催化剂和一些金属氧化物催化剂普遍存在反应温度高,尤其对 N2选择性差等问题。为解决上述问题,需寻找新的适合我国矿产资源的催化体系。研究发现,稀散金属基催化剂对氮氧化物的净化具有一定效果,因而可将我国的稀散金属资源优势转化为技术优势和经济优势。因此,本文以 TiO2-γ-Al2O3(TA)为载体, In/Ag为活性组分,采用等体积浸渍法制备了 InAg/TA以及 In/TA, Ag/TA和InAg/Al (γ-Al2O3为载体)催化剂,考察了贫燃条件下 CO选择性还原NO的催化活性。研究表明,双金属催化剂InAg/Al和 InAg/TA的活性比单金属催化剂In/TA和 Ag/TA高, In/TA催化剂中引入 Ag物种能降低起燃温度;另外,相比于InAg/Al催化剂, InAg/TA催化剂具有较高的催化活性,550?600°C时 N2产率超过60%,说明载体中引入TiO2可以提高催化剂活性。为了深入研究 InAg/TA催化剂中 Ag物种和TiO2对 In物种的作用,通过比表面测定、X射线衍射(XRD)、透射电子显微镜(TEM)、X射线光电子能谱、紫外-可见光吸收光谱、氢气程序升温还原、傅立叶变换红外线光谱等方法分析了催化剂结构和表面形态。结果表明, Ag物种可以提高 In物种的分散性, In和 Ag物种在 TA载体表面可以很好地分散,从而有利于提高催化活性。 In和 Ag物种在 TA载体表面以氧化态形式存在,并且 Ag物种可以提高 In物种表面含量,表面 In和 Ag物种含量越高,吸附活性位越多,催化活性越高;同时, TiO2也可以促进 NO吸附,从而提高 InAg/TA催化剂活性。 InAg/TA催化剂在450°C连续反应72 h进行稳定性测试,测试前后分别在50?600°C进行活性测试,并用 XRD和 TEM对反应后的催化剂进行表征测试。结果表明, InAg/TA催化剂具有较好的稳定性,连续反应前后催化剂活性基本保持不变,推测可能由于在有 CO和O2存在的体系中, Ag物种利用自身 Ag+与 Ag0之间的氧化还原反应抑制了活性组分 In2O3的还原和聚集,稳定了 In物种乃至催化剂活性。 InAg/TA催化剂用于贫燃条件下CO还原NO具有较好的催化效果,主要归因于催化剂活性组分分散性好,稳定性高,对NO吸附能力强。 Ag物种可以稳定In物种并提高其分散性, TiO2可以改善In物种和Ag物种的分散性并促进NO吸附。     

CO在纳米CeO2负载的Pd-Cu催化剂上的低温催化氧化

用溶胶-凝胶法制得了平均晶粒度为15nm的CeO2粉体,并用浸渍法制备了Pd-Cu/纳米CeO2催化剂;通过XRD、SEM和HRTEM等表征手段研究了纳米CeO2粉体和Pd-Cu/纳米CeO2催化剂的性能;考察了催化剂对CO的低温催化氧化活性.结果表明纳米CeO2粉体负载的Pd-Cu催化剂对CO的低温催化氧化活性明显优于一般CeO2颗粒负载的Pd-Cu催化剂,其CO完全氧化的最低温度比Pd-Cu/热分解法CeO2催化剂低约70℃,比Pd-Cu/工业CeO2催化剂低约130℃.因此,纳米CeO2粉体作载体可极大地提高Pd-Cu催化剂的CO氧化性能.     

CO在纳米CeO2负载的Pd-Cu催化剂上的低温催化氧化

用溶胶一凝胶法制得了平均晶粒度为15nm的CeO2粉体,并用浸渍法制备了Pd-Cu/纳米CeO2催化剂;通过XRD、SEM和HRTEM等表征手段研究了纳米CeO：粉体和Pd-Cu/纳米CeO2催化剂的性能;考察了催化剂对CO的低温催化氧化活性。结果表明：纳米CeO2粉体负载的Pd-Cu催化剂对CO的低温催化氧化活性明显优于一般CeO2颗粒负载的Pd-Cu催化剂,其CO完全氧化的最低温度比Pd-Cu,热分解法CeO2催化剂低约70℃,比Pd-Cu,工业CeO：催化剂低约130℃。因此,纳米CeO2粉体作载体可极大地提高Pd-Cu催化剂的CO氧化性能。     

贫燃条件In-Ag/TiO_2-γ-Al_2O_3催化CO选择性还原NO（英文）

汽车尾气中主要污染成分CO和NO_x可导致酸雨、光化学烟雾和臭氧空洞效应,对生物、环境及生态系统造成重大危害.污染源中CO是性能优良的还原剂,如能不添加还原剂实现CO催化还原NO_x,将成为最具经济技术优势的NO_x脱除技术.在富氧、低温条件下,利用CO选择性催化还原NO_x为N_2,是目前选择性催化还原研究中的热点和难点.催化CO还原NO_x常用的贵金属Ir,Rh,Pt和Pd矿藏稀少,价格昂贵,有氧条件下活性急降,而分子筛催化剂和一些金属氧化物催化剂普遍存在反应温度高,尤其对N_2选择性差等问题.为解决上述问题,需寻找新的适合我国矿产资源的催化体系.研究发现,稀散金属基催化剂对氮氧化物的净化具有一定效果,因而可将我国的稀散金属资源优势转化为技术优势和经济优势.因此,本文以TiO_2-γ-Al_2O_3(TA)为载体,In/Ag为活性组分,采用等体积浸渍法制备了InAg/TA以及In/TA,Ag/TA和InAg/Al(γ-Al_2O_3为载体)催化剂,考察了贫燃条件下CO选择性还原NO的催化活性.研究表明,双金属催化剂InAg/Al和InAg/TA的活性比单金属催化剂In/TA和Ag/TA高,In/TA催化剂中引入Ag物种能降低起燃温度;另外,相比于InAg/Al催化剂,InAg/TA催化剂具有较高的催化活性,550-600°C时N_2产率超过60%,说明载体中引入TiO_2可以提高催化剂活性.为了深入研究InAg/TA催化剂中Ag物种和TiO_2对In物种的作用,通过比表面测定、X射线衍射(XRD)、透射电子显微镜(TEM)、X射线光电子能谱、紫外-可见光吸收光谱、氢气程序升温还原、傅立叶变换红外线光谱等方法分析了催化剂结构和表面形态.结果表明,Ag物种可以提高In物种的分散性,In和Ag物种在TA载体表面可以很好地分散,从而有利于提高催化活性.In和Ag物种在TA载体表面以氧化态形式存在,并且Ag物种可以提高In物种表面含量,表面In和Ag物种含量越高,吸附活性位越多,催化活性越高;同时,TiO_2也可以促进NO吸附,从而提高InAg/TA催化剂活性.InAg/TA催化剂在450°C连续反应72 h进行稳定性测试,测试前后分别在50-600°C进行活性测试,并用XRD和TEM对反应后的催化剂进行表征测试.结果表明,InAg/TA催化剂具有较好的稳定性,连续反应前后催化剂活性基本保持不变,推测可能由于在有CO和O_2存在的体系中,Ag物种利用自身Ag~+与Ag~0之间的氧化还原反应抑制了活性组分In_2O_3的还原和聚集,稳定了In物种乃至催化剂活性.InAg/TA催化剂用于贫燃条件下CO还原NO具有较好的催化效果,主要归因于催化剂活性组分分散性好,稳定性高,对NO吸附能力强.Ag物种可以稳定In物种并提高其分散性,TiO_2可以改善In物种和Ag物种的分散性并促进NO吸附.     

络合浸渍法制备Ag/Al2O3-TiO2催化剂及其催化燃烧丙烷性能

研究了制备过程中不同络合剂乙醇胺（ETA）、二乙醇胺（DTA）、三乙醇胺（TEA）及柠檬酸（CA）等对Ag/Al₂O₃-TiO₂催化剂理化性质的影响,并考察了其催化丙烷燃烧的活性。结果表明,络合浸渍法能够显著提高催化剂催化活性,其活性顺序依次为：Ag/Al₂O₃-TiO₂(IM,传统浸渍法) < Ag/Al₂O₃-TiO₂(TEA) < Ag/Al₂O₃-TiO₂(DTA) < Ag/Al₂O₃-TiO₂(ETA) < Ag/Al₂O₃-TiO₂(CA),表明CA作为络合剂效果最好。当CA与Ag的物质的量比为1:1时,催化剂的催化活性最佳。与Ag/Al-Ti(IM)催化剂相比,Ag/Al₂O₃-TiO₂催化剂的T₉₀（丙烷转化率为90%的反应温度）下降了81 ℃。由催化剂的结构分析发现,络合浸渍法制备的催化剂银物种的粒径明显变小、银的分散度提高、表面Ag⁰物种和表面吸附氧的含量增加,进而促进了丙烷催化燃烧性能的提升。      

Pt-CeO2/SiO2催化剂用于室温湿空气中CO氧化反应

开发室温CO氧化催化剂的主要挑战是CO自中毒和慢的表面动力学,同时湿气的存在也可导致催化剂失活.本文开发了高活性CeO2促进的Pt基催化剂4%Pt-12%CeO2/SiO2,用于室温湿气(湿度10%?90%,25°C)中CO氧化反应,在低CO浓度(<500 ppm)和高CO浓度(>2500 ppm)时,CO转化率高于99%.优化了催化剂制备变量,如Pt和CeO2负载量、CeO2沉积方法、CeO2和Pt前驱体的干燥和焙烧条件.采用CO/H2化学吸附、O2-H2滴定、X射线衍射和BET比表面积测定表征了催化剂的表面特性,并将其与催化剂活性相关联.结果表明,CeO2沉积方法对催化剂活性影响显著,当用浸渍法沉积CeO2时,所得催化剂的反应速率(5.77μmol/g/s)比用沉积沉淀法(1.96μmol g?1 s?1)或CeO2嫁接法(1.31μmol g?1 s?1)制得催化剂的高3倍.O2-H2滴定结果表明,当用浸渍法沉积CeO2时,CeO2和Pt的紧密结合导致了催化剂的高活性.催化剂载体的选择也非常重要,硅胶负载的催化剂活性(5.77μmol g?1 s?1)是氧化铝负载的(1.05μmol g?1 s?1)5倍.当反应受内扩散控制时,催化剂载体的粒径和孔结构影响非常大.另外,CeO2和Pt前驱体的干燥和焙烧条件对催化剂活性的影响至关重要.当Pt和CeO2含量分别大于2.5和15 wt%时,所得催化剂在室温条件下活性高(TOF>0.02 s?1),稳定性好(反应15 h,CO转化率≥99%).     

固相浸渍法制备NiO/CeO2催化剂及其在CO氧化反应中的应用

采用固相浸渍法制备了一系列NiO/CeO2催化剂,并通过与常规湿浸渍法比较,考察了制备方法对催化剂和CO氧化反应性能的影响.同时结合X射线衍射(XRD),N2吸附-脱附(BET),透射电镜(TEM),氢气-程序升温还原(H2-TPR),拉曼(Raman)光谱,X射线光电子能谱(XPS)等手段对催化剂的结构和表面物种分散状态进行了表征.CO氧化活性测试结果表明,当镍负载量相同时,固相浸渍法制备的催化剂相比于湿浸渍法表现出更好的催化性能.TEM、XPS、H2-TPR结果表明,固相浸渍法更有利于加强镍铈间的相互作用和得到高分散的镍物种,从而促进镍物种的还原.Raman结果表明固相浸渍法相比于湿浸渍法能产生更多氧空位,这有利于氧气在催化剂表面的活化,使得CO氧化反应更容易进行.     

（Ag／Al2O3＋Cu／Ce（x）／Al2O3）组合催化剂催化乙醇选择性还原NO工及其副产物的消除

制备了Cu／Ce（x）／Al2O3（X为Ce与Al的摩尔比）系列氧化催化剂,并考察了（Ag／Al2O3＋Cu／Ce（x）／Al2O3）组合体系催化乙醇还原NO,以及氧化去除反应副产物（CO和未完全燃烧的碳氧化合物）的活性．在200～350℃温度区间,组合催化剂具有与Ag／Al2O3相似的NO,去除效率．随着Ce／Al比增加,氧化催化剂去除CO的活性逐渐提高．Cu／CeO2催化剂具有最好的氧化活性,但其对NOx的去除有较大影响．综合考虑NOx转化率以及CO和HC的去除效果,（Ag/Al2O3＋Cu／Ce（0．15）／Al2O3）是最佳的催化剂组合体系．通过对此系列氧化催化剂的BET比表面积、XRD、H2-TPR以及XPS等表征结果的分析,发现Cu和Ce之间的相互作用是催化剂氧化CO能力提高的主要原因．     

CO Selective Oxidation in Hydrogen-Rich Gas over Copper-Series Catalysts

The performances of CO selective oxidation in hydrogen-rich gas over four catalytic systems of CuO/ZrO2, CuO/MnO2, CuO/CoO and CuO/CeO2 were compared. The reducibility of these catalysts and the effect of CuO and CeO2 molar ratio of CuO/CeO2 catalysts on the activity of selective CO oxidation are investigated by XRD and TPR methods. The results show that the catalysts with the exception of CuO/ZrO2 have the interactions between CuO and CoO, CeO2 or MnO2, which result in a decrease in the reduction temperature. Among the catalysts studied, CuO/ZrO2 catalyst shows the lowest catalytic activity while CuO/CeO2 catalyst exhibits the best catalytic performance. The CuO(10%)/CeO2 catalyst attains the highest CO conversion and selectivity at 140 and 160℃. The addition of 9% H2O in the reactant feed decreases the activity of CuO/CeO2 catalyst but increases its CO selectivity.     

Low-temperature CO oxidation over CuO-CeO2/SiO2 catalysts：Effect of CeO2 content and carrier porosity

The effects of CeO2 contents and silica carder porosity with their pore diameters ranging from 5.2 nm to 12.5 nm of CuO-CeO2/SiO2 catalysts in CO oxidation were investigated. The catalysts were characterized by N2 adsorption/desorption at low temperature, X-ray diffraction (XRD), temperature-programmed reduction by H2 (H2-TPR), oxygen temperature programmed desorption (O2-TPD) and X-ray photoelectron spectroscopy (XPS). The results suggested that, the ceria content and the porosity of SiO2 carder possessed great impacts on the structures and catalytic performances of CuO-CeO2/SiO2 catalysts. When appropriate content of CeO2(Ce content ≤8 wt%) was added, the catalytic activity was greatly enhanced. In the catalyst supported on silica carrier with larger pore diameter, higher dispersion of CuO was observed, better agglomeration-resistant capacity was displayed and more lattice oxygen could be found, thus the CuO-CeO2 supported on Si-1 showed higher catalytic activity for low-temperature CO oxidation.     

Low-temperature CO oxidation over CuO-CeO_2/SiO_2 catalysts:Effect of CeO_2 content and carrier porosity

The effects of CeO2 contents and silica carrier porosity with their pore diameters ranging from 5.2 nm to 12.5 nm of CuO-CeO2/SiO2 cata-lysts in CO oxidation were investigated.The catalysts were characterized by N2 adsorption/desorption at low temperature,X-ray diffraction (XRD),temperature-programmed reduction by H2 (H2-TPR),oxygen temperature programmed desorption (O2-TPD) and X-ray photoelectron spectroscopy (XPS).The results suggested that,the ceria content and the porosity of SiO2 carrier possessed great impacts on the structures and catalytic performances of CuO-CeO2/SiO2 catalysts.When appropriate content of CeO2 (Ce content 8 wt%) was added,the catalytic activity was greatly enhanced.In the catalyst supported on silica carrier with larger pore diameter,higher dispersion of CuO was observed,better agglomeration-resistant capacity was displayed and more lattice oxygen could be found,thus the CuO-CeO2 supported on Si-1 showed higher catalytic activity for low-temperature CO oxidation.     

还原剂对Au-Pd/CeO2催化剂甲醇部分氧化性能的影响

以PVP为保护剂,乙醇(ER)、乙二醇(GR)和水合肼(HR)为还原剂制备了一系列Au-Pd/CeO2催化剂,考察了还原剂对甲醇部分氧化性能的影响,并运用XRD、TPD和TPR等手段对催化剂进行了表征。结果表明,Au-Pd/CeO2(ER)催化剂具有较大的比表面积,形成的AuxPdy量较多、粒径较小、分散度较高、活性组分与载体的相互作用较强,同时对甲醇的吸附量较大和吸附温度较低。因此,该催化剂具有较高的催化活性和氢气选择性以及较低的CO质量分数。     

Ir/CeO2催化剂的表征和CO氧化性能

采用浸渍法制备了Ir/CeO2催化剂,考察了催化剂的CO氧化活性。随着Ir负载量的增加,Ir/CeO2催化剂的CO氧化活性先上升后下降,当Ir的负载量为1%时,催化剂的活性最高。Ir/CeO2催化剂中Ir以IrO2的形式存在,当低负载量(≤1%)时以高分散形式存在;高负载量(>1%)时以晶相IrO2的形式存在。随着Ir负载量增加,Ir粒子逐渐变大,反应比速率和反应转换频率(TOF)逐渐下降,表明小粒子上具有更高的CO反应活性。同时也发现金属态Ir催化剂的CO氧化活性高于氧化态IrOx催化剂。     

Effect of Addition of Base on Ceria and Reactivity of CuO/CeO2 Catalysts for Low-Temperature CO Oxidation

In this work, we have reported the influence of the addition of base (KOH) on the physicochemical property of ceria synthesized by alcohothermal process, and the alcohothermal mechanism was also put forward. Furthermore, the prepared CeO2 was used as the support to prepare CuO/CeO2 catalysts via the wet impregnation method. The samples were characterized by N2 adsorption-desorption, X-ray powder diffraction (XRD), high resolution transmission electron microscopy (HRTEM), and temperature-programmed reduction by H2 (H2-TPR). The catalytic properties of the CuO/CeO2 catalysts for low-temperature CO oxidation were studied using a microreactor-GC system. The crystal size of CeO2-A was much smaller than that of CeO2-B, and the corresponding copper oxide catalysts exhibited higher catalytic activity than that of the CeO2-B-supported catalysts under the same reaction conditions. The alcohothermal mechanism indicated that KOH plays a key role in determining the physicochemical and catalytic properties of ceria-based materials.     

K/CeO2催化剂上碳黑催化燃烧性能及稳定性（英文）

采用不同的钾盐前体制备了一系列K/CeO2催化剂,利用热重和程序升温氧化(TPO)等技术考察了其催化性能及稳定性.结果表明,K/CeO2催化剂可使碳黑完全燃烧温度降低近200oC.钾盐前体对催化活性和稳定性具有较大影响,由于硝酸钾熔点低,金属在载体上的流动性强,有利于催化剂与碳黑的有效接触,因而表现了较高的活性,三次TPO循环试验中催化活性稳定.碳酸钾的熔点高且碱性较强,使碳黑燃烧生成的CO2不可逆吸附在其表面,导致反应活性低,TPO循环实验表明其反应速率降低,失活明显.     

CuO／CeO2和CuO／Al2O3催化剂的催化性能

本文以ＣＯ氧化为模式反应考察了ＣｅＯ２和Ａｌ２Ｏ３负载氧化铜催化剂的氧化活性，运用ＸＲＤ和ＴＰＲ技术研究了催化剂的还原性能和物相结构，结果表明：载体性质对负载ＣｕＯ催化剂的ＣＯ氧化活性有很大影响，ＣｕＯ／ＣｅＯ２催化剂活性明显高于ＣｕＯ／Ａｌ２Ｏ３催化剂．催化剂的还原特性随载体不同而不同．同时发现，热处理对催化剂铜物种的存在形式，晶粒大小、还原特性及其催化活性有明显影响，ＣｕＯ／Ａｌ２Ｏ３催化剂活性下降的主要因素是生成了活性较低的ＣｕＡｌ２Ｏ４相，而ＣｕＯ／ＣｅＯ２催化剂活性下降是由于ＣｕＯ和ＣｅＯ２发生烧结，晶粒变大     

CeO2添加量对催化剂Cu-Ni-Ce／SiO2性能的影响

采用浸渍法在不同Ce掺杂量时制备了用于湿式H2O2降解吡虫啉农药废水的Cu-Ni-Ce/SiO2催化剂, 利用BET、 SEM、 XRD和XPS等对其进行了表征, 并研究了Ce掺杂量对催化剂表面形态的影响以及催化剂表面形态与活性及稳定性之间的关系.结果表明: 适量添加Ce后, 催化剂晶粒尺寸减小, 比表面积增加, Cu、 Ni固溶体量和催化剂表面化学吸附氧量增加, 而且活性组分的分散性增加. 湿式H2O2降解吡虫啉农药废水时, 在催化剂用量10 g/L、反应温度110 ℃、双氧水用量为理论需用量、进水pH为9.0、反应60 min条件下, 0.16%Ce掺杂量的Cu-Ni-Ce/SiO2的催化剂的活性比相同工艺条件的无Ce添加的催化剂活性提高了7.2%, 活性组分溶出量也大为减少.     

锰掺入对CeO2催化氧化CO性能的影响