Stability of Zn–Ni–TiO<Subscript>2</Subscript> and Zn–TiO<Subscript>2</Subscript> nanocomposite coatings in near-neutral sulphate solutions

Zn–Ni–TiO₂ and Zn–TiO₂ nanocomposites were prepared by galvanostatic cathodic square wave deposition. X-ray diffraction analysis and scanning electron microscopy revealed that the occlusion of TiO₂ nanoparticles (spherical shaped with diameter between 19.5 and 24.2 nm) promotes the formation of the γ-Ni₅Zn₂₁ phase, changes the preferred crystallographic orientation of Zn from (101) and (102) planes to (002), and decreases the particle size of the metallic matrices. The stability of the nanocomposites immersed in near-neutral 0.05 mold m⁻³ Na₂SO₄ solution (pH 6.2) was investigated over 24 h. The initial open circuit potential for the Zn–Ni–TiO₂ and Zn–TiO₂ coatings were −1.32 and −1.51 V (vs. Hg/Hg₂SO₄), respectively, and changed to −1.10 and –1.49 V (vs. Hg/Hg₂SO₄) after 24 h of immersion. Data extracted from the steady state polarization curves demonstrated that the metal–TiO₂ nanocomposites have, with respect to the metal coatings, a higher corrosion potential in the case of the Zn–Ni alloy composite; a lower corrosion potential in the case of Zn-based nanocomposite albeit the predominant (002) crystallographic orientation; and a lower initial corrosion resistance due to the smaller grain size and higher porosity in the Zn–Ni–TiO₂ and Zn–TiO₂ nanocomposites. Morphological and chemical analyses showed that a thicker passive layer is formed on the surface of the Zn–Ni–TiO₂ and Zn–TiO₂ deposits. After 24 h of immersion in the sulphate solution, the Zn–Ni–TiO₂ coating has the highest corrosion stability due to the double-protective action created by the deposit’s surface enrichment in Ni plus the higher amount of corrosion products.     

Phase formation in the BaCO<Subscript>3</Subscript>–PbO–Fe<Subscript>2</Subscript>O<Subscript>3</Subscript>–Nb<Subscript>2</Subscript>O<Subscript>5</Subscript> system

Features of the formation of lead-ferroniobate compounds in the xBaCO₃–(1 – x)PbO–Fe₂O₃–Nb₂O₅ system by solid-phase synthesis are investigated. For perovskite-type lead-ferroniobate solid solution, a single-phase concentration region is revealed at 1233 K. The crystalline structures of the synthesized compounds are refined using Rietveld analysis and the Pm3?m and R3m space groups. Ceramic samples of lead ferroniobate are studied by scanning electron microscopy.     

Deep metastable eutectic nanometer-scale particles in the MgO–Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–SiO<Subscript>2</Subscript> system

Laboratory vapor phase condensation experiments systematically yield amorphous, homogeneous, nanoparticles with unique deep metastable eutectic compositions. They formed during the nucleation stage in rapidly cooling vapor systems. These nanoparticles evidence the complexity of the nucleation stage. Similar complex behavior may occur during the nucleation stage in quenched-melt laboratory experiments. Because of the bulk size of the quenched system many of such deep metastable eutectic nanodomains will anneal and adjust to local equilibrium but some will persist metastably depending on the time–temperature regime and melt/glass transformation.     

Magnetic and magnetoresistive properties of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>–Sr<Subscript>2</Subscript>FeMoO<Subscript>6–δ</Subscript>–Al<Subscript>2</Subscript>O<Subscript>3</Subscript> nanoheterostructures

A method has been developed for fabricating nanoporous matrices based on anodic aluminum oxide for the deposition of ferromagnetic nanoparticles in them. The modes of deposition of strontium ferromolybdate thin films prepared by the ion-plasma method have been worked out, and the magnetic and magnetoresistive properties, structure, and composition of the films have been investigated. It has been revealed that the microstructure and properties of the strontium ferromolybdate films deposited by ionplasma sputtering depend on the deposition rate and the temperature of the substrate. Based on the measurement of the electrical resistivity of nanoheterostructures in a magnetic field, it has been found that the magnetoresistance reaches 14% at T = 15 K and B = 8 T, which is due to the manifestation of tunneling magnetoresistance.     

Elastic properties of TeO<Subscript>2</Subscript>–B<Subscript>2</Subscript>O<Subscript>3</Subscript>–Ag<Subscript>2</Subscript>O glasses

A series of glasses [(TeO₂) _x (B₂O₃)_1−x ]_1−y [Ag₂O] _y with x = 70 and y = 10, 15, 20, 25 and 30 mol% were synthesised by rapid quenching. Longitudinal and shear ultrasonic velocity were measured at room temperature and at 5 MHz frequency. Elastic properties, Poisson's ratio, microhardness, softening temperature and Debye temperature have been calculated from the measured density and ultrasonic velocity at room temperature. The experimental results indicate that the elastic constants depend upon the composition of the glasses and the role of the Ag₂O inside the glass network is discussed. Estimated parameters based on Makishima–Mackenzie theory and bond compression model were calculated in order to analyse the experimental elastic moduli. Comparison between the experimental elastic moduli data obtained in the study and the calculated theoretically by the mentioned above models has been discussed.     

Influence of Matrix Nature on the Structural Characteristics of In<Subscript>2</Subscript>O<Subscript>3</Subscript>–CeO<Subscript>2</Subscript> and SnO<Subscript>2</Subscript>–CeO<Subscript>2</Subscript> Composites Fabricated by the Impregnation Method

The structural characteristics, valence states, and distribution of cerium ions between the components in In₂O₃–CeO₂ and SnO₂–CeO₂ nanocomposites fabricated using the impregnation method were studied. X-ray photoelectron spectroscopy (XPS) and energy-dispersive X-ray spectroscopy (EDX) were used to show that, during impregnation, cerium ions are not included into In₂O₃ crystals and are disposed only on their surface in the form of nano-sized crystallites or amorphous clusters. On the other side, under the contact of CeO₂ clusters with a surface of SnO₂ matrix crystals, cerium ions penetrate into the surface layer of these crystals. In contrast to an In₂O₃–CeO₂ system, where the addition of CeO₂ does not affect the conduction activation energy, where cerium oxide is added to SnO₂, the observed increase in the resistance of a SnO₂–CeO₂ composite is accompanied by a sufficient increase in activation energy. These data and the XPS spectra confirm the modification of the surface layers of conductive SnO₂ crystals as, a result of the penetration of cerium ions into these layers.     

Sol–gel synthesis and characterization of Li<Subscript>2</Subscript>CO<Subscript>3</Subscript>–Al<Subscript>2</Subscript>O<Subscript>3</Subscript> composite solid electrolytes

Composite solid electrolytes in the system (1???x)Li₂CO₃–xAl₂O₃, with x?=?0.0–0.5 (mole), were synthesized by a sol–gel method. The synthesis carried out at low temperature resulted in voluminous and fluffy products. The obtained materials were characterized by X-ray diffraction, differential scanning calorimetry, scanning electron microscopy/energy-dispersive X-ray, Fourier transform infrared spectroscopy and AC impedance spectroscopy. Structural analysis of the samples showed an amorphous feature of Li₂CO₃ and traces of α-LiAlO₂, γ-LiAlO₂ and LiAl₅O₈. The prepared composite samples possess high ionic conductivities at 130–180 °C on account of the presence of lithium aluminates as well as the formation of a high concentration of an amorphous phase of Li₂CO₃ via this sol–gel preparative technique.     

Electrical switching in the MoO<Subscript>3</Subscript>–WO<Subscript>3</Subscript>–P<Subscript>2</Subscript>O<Subscript>5</Subscript> and MoO<Subscript>3</Subscript>–P<Subscript>2</Subscript>O<Subscript>5</Subscript> glasses

High field electrical switching on blown films of MoO₃(60%)–P₂O₅(40%), MoO₃(50%)–WO₃(10%)–P₂O₅(40%), and MoO₃(45%)–WO₃(15%)–P₂O₅(40%) having different thicknesses was studied and compared. Switching was observed using two terminal samples. S-type current–voltage characteristic (current-controlled negative resistance—CCNR) with memory was observed in molybdenum–phosphate glasses, but N-type characteristic (voltage-controlled negative resistance—VCNR) with threshold in tungsten–molybdenum–phosphate glasses was observed. The important observation was that with the addition of WO₃ to binary MoO₃–P₂O5 led to a change of I–V characteristic from CCNR with memory to VCNR with threshold. The measurements of density and molar volume showed linear relation between MoO₃ content and density which decreased with the increase of MoO₃ content. The samples’ thickness had no significant effect on threshold voltage. The attained results also indicated that the electrode material had no effect on switching property of devices. The switching behavior of the devices did not show any dependence on the polarity of the applied voltage. In terms of the effect of heat on the switching behavior of molybdenum–phosphate glasses, it was found that threshold voltage decreases with increasing of temperature. Finally, the switching phenomenon was explained by thermal (formation of crystalline filaments) and electronic models.     

Fortification of Ni–Y<Subscript>2</Subscript>O<Subscript>3</Subscript> nanocomposite coatings prepared by pulse and direct current methods

Ni–Y₂O₃ nanocomposite coatings were prepared under direct current (DC) and pulse current (PC) using acetate bath. The microstructure and corrosion resistance of the coatings were characterized by means of XRD, SEM, AFM, and EIS. The results showed that the microstructure and performances of the coatings were greatly affected by Y₂O₃ content on the deposits prepared by DC and PC methods. The microhardness and corrosion resistance were enhanced in the optimum percentage of Y₂O₃ composite coatings. The PC composite coatings were exhibited compact surface, higher microhardness, and good corrosion resistance compared with that of the DC composite coatings.     

Production of ultrafine particles of high-temperature tetragonal WO<Subscript>3</Subscript> by dc arc discharge in Ar–O<Subscript>2</Subscript> gases

Ultrafine particles of WO₃ are successfully produced by dc arc discharge in Ar-O₂ gases. Particle sizes are distributed from 10 nm to 1 m depending on production conditions: gas pressure, collection position and discharge current. Observations of the cooled particles by electron microscopy indicate that the WO₃ particles are tetragonal, a phase that is usually only stable above 725 °C. The octahedral crystals are bounded by eight {1 0 1} faces and occasionally truncated by {1 0 0} and/or {0 0 1} faces. This method of producing WO₃ by dc arc discharge therefore affords a high-temperature phase that is preserved upon cooling to room temperature.     

Specific heat of the [NH<Subscript>2</Subscript>(CH<Subscript>3</Subscript>)<Subscript>2</Subscript>]<Subscript>2</Subscript>ZnCl<Subscript>4</Subscript> crystal in the temperature region 80–300 K

The specific heat of [NH₂(CH₃)₂]₂ZnCl₄ was measured calorimetrically in the temperature region 80–300 K. As the temperature T decreases, the C _p (T) dependence indicates a phase transition sequence, with the phase transition at T₆=151 K observed for the first time. The thermodynamic characteristics of the crystal were refined. The transformation occurring at T₂=298.3 K is shown to be an incommensurate-commensurate phase transition.     

Effect of the humidity on the uptake of NO<Subscript>3</Subscript> on coatings composed of MgCl<Subscript>2</Subscript> · 6H<Subscript>2</Subscript>O and MgBr<Subscript>2</Subscript> · 6H<Subscript>2</Subscript>O and mixtures thereof with NaCl

The reactive uptake of NO₃ radicals on the surface of wetted individual X salts and of wetted X-NaCl salts (X = MgCl₂ · 6H₂O and MgBr₂ · 6H₂O) at [H₂O] = 2 × 10¹²−2 × 10¹⁵ cm⁻³ and NO₃ (4.8 × 10¹² cm⁻³) was studied using a reactor with a movable insert covered with a salt coating in combination with a mass spectrometer for monitoring the initial reactant and products. The probabilities of NO₃ uptake γ on X-NaCl binary salts as functions of the content of doping salt were determined. A parametric approximation of the experimental data was proposed, which makes it possible to quantitatively predict the extent of surface enrichment of a wetted binary salt coating in doping salt and its dependence on the humidity and the content of this salt in the binary mixture. It was established that the relative surface density σ_X of X doping salt depends on its mole fraction μ_X in the X-NaCl binary salt as σ_X = aμ_X (a = 2.2 for MgBr₂ and 13.1 for MgCl₂) over the entire humidity range covered. The contributions of the X salts to the overall uptake of NO₃ at NO₃ concentration typical of the tropospheric conditions ([NO₃] ∼ 10⁷ cm⁻³ and relative humidities of RH ≤ 20%) were estimated.     

Reactions of initiation of the autoignition of H<Subscript>2</Subscript>–O<Subscript>2</Subscript> mixtures in shock waves

The initiation of the autoignition of hydrogen–oxygen–argon mixtures behind reflected shock waves is studied by absorption and emission spectrophotometry in the temperature range of 960 < T < 1670 K at pressures of ~0.1 MPa. Introduction of Mo(CO)₆ additive in an amount of ~80 ppm made it possible to study the effect of O atoms on the shortening of the ignition delay time of H₂–O₂–Ar mixtures. A kinetic modeling of our own and published experimental data at temperatures of 930 < T < 2500 K and pressures of 0.05 < P < 8.7 MPa enabled to establish how the initiation reactions influence the process of self-ignition and to evaluate the rate constant for one of the initiation reactions: k(H₂ + O₂ → 2OH) = (3 ± 1) × 10¹¹exp(–E _a/RT), cm³ mol^–1 s^–1, where E _a = (40 ± 2) kcal/mol.     

Microwave dielectric properties of the 5.5Li<Subscript>2</Subscript>O–Nb<Subscript>2</Subscript>O<Subscript>5</Subscript>–7TiO<Subscript>2</Subscript> ceramics

A new Li₂O–Nb₂O₅–TiO₂ (LNT) ceramic with the Li₂O:Nb₂O₅:TiO₂ mole ratio of 5.5:1:7 was prepared by solid state reaction route. The phase and structure of the ceramic were characterized by X-ray diffraction and scanning electron microscopy (SEM). The microwave dielectric properties of the ceramics were studied using a network analyzer. The microwave dielectric ceramic has low sintering temperature (∼1075°C) and good microwave dielectric properties of ε _r=42, Q×f=16900 GHz (5.75 GHz), and τ _f =63.7 ppm/°C. The addition of B₂O₃ can effectively lower the sintering temperature from 1075 to 875°C and does not induce degradation of the microwave dielectric properties. Obviously, the LNT ceramics can be applied to microwave low temperature-cofired ceramics (LTCC) devices.     

High-Temperature Heat Capacity of Zn<Subscript>2</Subscript>V<Subscript>2</Subscript>O<Subscript>7</Subscript>–Cu<Subscript>2</Subscript>V<Subscript>2</Subscript>O<Subscript>7</Subscript> Solid Solutions

Differential scanning calorimetry has been used to study the influence of temperature on the heat capacity of synthesized vanadates Zn₂V₂O₇, (Cu_0.56Zn_1.44)V₂O₇, and (Cu_1.0Zn_1.0)V₂O₇. It is found that dependences C_p = f(T) have extremes. The thermodynamic properties of Zn₂V₂O₇ have been determined.     

AC Conductivity,XRD and transport properties of melt quenched PbI<Subscript>2</Subscript>–Ag<Subscript>2</Subscript>O–Cr<Subscript>2</Subscript>O<Subscript>3</Subscript> system

Composite materials used for electrode and electrolyte materials have been intensely studied in view of their advantages such as higher conductivity and better operational performance compared to their single-phase counterparts. The present work aims at studying the electrical and structural characteristics of a new composite electrolyte namely, (PbI₂) _x  − (Ag₂O–Cr₂O₃)_100−x where x = 5, 10, 15, 20, and 25 mol%, respectively, prepared by the melt quenching technique. The room temperature X-ray diffraction spectra revealed certain crystalline phases in the samples. AC conductivity analysis for all the prepared samples was carried out over the frequency range 1 MHz–20 Hz and in the temperature window 297–468 K. The room temperature conductivity values were calculated to be in the order of 10⁻⁵–10⁻³ Scm⁻¹. An Arrhenius dependence of temperature with conductivity was observed, and the activation energies calculated were found to be in the range 0.27–0.31 eV. Furthermore, the total ionic transport number (t _i) values obtained for all these indicated the ionic nature of this system. Paper presented at the Third International Conference on Ionic Devices (ICID 2006), Chennai, Tamilnadu, India, Dec. 7–9, 2006.     

Preparation and characterization of organic–inorganic hybrid compound [N(C<Subscript>4</Subscript>H<Subscript>9</Subscript>)<Subscript>4</Subscript>]<Subscript>2</Subscript>Cu<Subscript>2</Subscript>Cl<Subscript>6</Subscript>

Organic–inorganic hybrid sample [N(C₄H₉)₄]₂Cu₂Cl₆ was prepared via the reaction between copper chloride and tetrabutylammonium chloride. The compound was characterized by X-ray powder diffraction, IR, Raman, differential scanning calorimetry (DSC), DTA-TGA analysis and electrical impedance spectroscopy. DSC studies indicate a presence of one-phase transition at 343 K. The complex impedance of compound [N(C₄H₉)₄]₂Cu₂Cl₆ have been investigated in temperature and frequency ranges 300–380 K and 200 Hz–5 MHz, respectively. The Z′ and Z″ versus frequency plots are well fitted to an equivalent circuit model. The circuits consist of the parallel combination of bulk resistance R _p and constant phase elements CPE. The frequency dependence of the conductivity is interpreted in term of Jonscher's law: s(w) = s_dc + Awⁿ \sigma (\omega ){ } = {\sigma_{\rm{dc}}} + { }A{\omega^n} . The conductivity follows the Arrhenius relation. The variation of the value of these elements with temperatures confirmed the availability of the phase transition at 343 K detected by DSC and electrical measurements.     

The role of structural and nonstructural water in oxyfluoride K<Subscript>2</Subscript>WO<Subscript>2</Subscript>F<Subscript>4</Subscript> · H<Subscript>2</Subscript>O

X-ray structural and polarization optical investigations have been performed, and birefringence and rotation angles of the optical indicatrix φ _b and φ _c of the K₂WO₂F₄ · H₂O crystal have been measured in the temperature range of 100–600 K. The structure and symmetry of compounds at room temperature have been refined. It has been established that the layered crystal K₂WO₂F₄ · H₂O can exist in two states (A and B) depending on the atmospheric humidity and undergoes the sequence of reversible and irreversible phase transformations G ₃ ↔ G ₂ → G ₁ → G ₀. The sequences of changes in the phase symmetry P [`1]\bar 1 ↔ C2/m → P4/nmm for samples A and m ↔ C2/m → P4/nmm for samples B have been found. The second-order proper ferroelastic phase transition (P [`1]\bar 1 ↔ C2/m) at T ₀₃ = 270–290 K (G ₃ ↔ G ₂) is accompanied by twinning and appearance of the shift deformation x ₆. The crystal system of the substance for the B crystals remains invariable after the second-order phase transition G ₃ ↔ G ₂. The irreversible first-order phase transition G ₂ → G ₁ occurs in a temperature range T ₀₂ ≈ 350–380 K; it is accompanied by the loss of the crystallization water, which then is reduced easily from the atmosphere for a day. The substance decomposes at T ₀₁ ≈ 510 K (G ₁ → G ₀). The distinction between the A and B crystals has been explained by the presence or absence of free water in interlayer spacings.     

Characterization and transport properties of 10BaO–xAg<Subscript>2</Subscript>O–(85-x)V<Subscript>2</Subscript>O<Subscript>5</Subscript>–5TeO<Subscript>2</Subscript> glass system

Silver-based quaternary glasses were prepared by splat quenching technique. X-ray diffraction and differential scanning calorimetry were done for confirming their amorphous nature. The conductivity of the glasses was measured in the frequency range from 1 Hz to 32 MHz from room temperature to 373 K. Conductivity data, which obeys the Arrhenius type behavior, shows minimum at 30 mol% Ag₂O, suggesting that the conductivity mechanisms are different above and below these two regions. The minimum in conductivity is accompanied by an inverse behavior of activation energy. Experimental data suggests that a polaron hopping mechanism operates in the electronically conducting domain of 20 ≤ × ≤ 30, and an interstitial pair mechanism operates in the ionically conducting domain of 35 ≤ × ≤ 55.