Structural, magnetic and transport properties of Ni-doped ZnO films

In this work, Ni-doped ZnO (Zn_1−xNi_xO, x=0, 0.03, 0.06, 0.11) films were prepared using magnetron sputtering. X-ray diffraction (XRD), X-ray absorption spectroscopy (XAS), temperature dependence electrical resistance, Hall and magnetic measurements were utilized in order to study the properties of the Ni-doped ZnO films. XRD and XAS results indicate that all the samples have a ZnO wurtzite structure and Ni atoms incorporated into ZnO host matrix without forming any secondary phase. The Hall and electrical resistance measurements revealed that the resistivity increased by Ni doping, and all the Ni-doped ZnO films exhibited n-type semiconducting behavior. The magnetic measurements showed that for the samples with x=0.06 and 0.11 are room-temperature ferromagnetic having a saturation magnetization of 0.33 and 0.39 μ_B/Ni, respectively. The bound-magnetic-polaron mediated exchange is proposed to be the possible mechanism for the room-temperature ferromagnetism in this work.     

Structural and photoluminescent properties of Ni doped ZnO nanorod arrays prepared by hydrothermal method

Self-assembled Ni-doped zinc oxide (Zn_1−xNi_xO, x = 0.05, 0.10, 0.15, i.e., ZnNiO, nominal composition) nanorod arrays vertically grown on the ZnO seed layer covered glass along [0 0 1] direction were synthesized by hydrothermal method. Their images and structures have been characterized by scan electron microscope (SEM), X-ray diffraction (XRD) and Raman spectra, showing that Ni doping is beneficial to the formation of ZnO nanorods with hexagonal cross section and the enhancement of ZnO crystal quality. X-ray photoemission spectroscopy (XPS) study further demonstrated that Ni atoms were successfully doped into ZnO lattices. The photoluminescence (PL) spectra of ZnNiO samples show near bandedge emission (NBE) peaks at about 380 nm at a low excitation power and the NBE peak position redshifts while its intensity continuously increases with the increase of Ni doping concentration. With the excitation power increasing, the NBE peak redshifts from 380 nm to about 400 nm for ZnNiO nanorod arrays. The NBE mechanisms for ZnNiO nanorod arrays have been discussed, which is helpful for understanding their room temperature ferromagnetisms.     

Synthesis and magnetic properties of Ni-doped zinc oxide powders

Polycrystalline Zn_1−xNi_xO diluted magnetic semiconductors have been successfully synthesized by an auto-combustion method. X-ray diffraction measurements indicated that the 5 at% Ni-doped ZnO had the pure wurtzite structure. Refinements of cell parameters from powder diffraction data revealed that the cell parameters of Zn_0.95Ni_0.05O were a little bit larger than ZnO. Transmission electron microscopy observation showed that the as-synthesized powders were of the size ∼60 nm. Magnetic investigations showed that the nanocystalline Zn_0.95Ni_0.05O possessed room temperature ferromagnetism with the saturation magnetic moment of 0.1 emu/g (0.29 μ_B/Ni²⁺).     

Structural and optical properties of ZnO nanorods grown on MgxZn1−xO buffer layers

ZnO nanorod arrays were synthesized by chemical-liquid deposition techniques on Mg_xZn_1−xO (x = 0, 0.07 and 0.15) buffer layers. It is found that varying the Mg concentration could control the diameter, vertical alignment, crystallization, and density of the ZnO nanorods. The X-ray diffraction (XRD), transmission electron microscopy (TEM), and selected area electron diffraction (SAED) data show the ZnO nanorods prefer to grow in the (0 0 2) c-axis direction better with a larger Mg concentration. The photoluminescence (PL) spectra of ZnO nanorods exhibit that the ultraviolet (UV) emission becomes stronger and the defect emission becomes weaker by increasing the Mg concentration in Mg_xZn_1−xO buffer layers.     

Structural and magnetic properties of Co1−xZnxFe2O4 nanoparticles by co-precipitation method

Co_1−xZn_xFe₂O₄ nanoparticles were prepared by co-precipitation method with x varying from 0 to 1.0. The powder samples were characterized by X-ray diffraction (XRD), vibrating sample magnetometer (VSM) and Fourier transform infrared spectroscopy (FTIR). The average crystallite sizes of the particles were determined from XRD. X-ray analysis showed that the samples were cubic spinel. The average crystallite size (D_aveXR) of the particles precipitated was found to vary from 6.92 to 12.02 nm decreasing with the increase in zinc substitution. The lattice constant (a_o) increased with the increase in zinc substitution. The specific saturation magnetization (M_S) of the particles was measured at room temperature. The magnetic parameters such as M_S, H_c, and M_r were found to decrease with the increase in zinc substitution. FTIR spectra of the Co_1−xZn_xFe₂O₄ with x varying from 0 to 1.0 in the range 400–4000 cm⁻¹ were reported. The spinel structure and the crystalline water adsorption of Co_1−xZn_xFe₂O₄ nanoparticles were studied by using FTIR.     

Solvothermal synthesis and magneto-optical properties of Zn1−xNixO hierarchical microspheres

Zn_1−xNi_xO (x=0-0.25) hierarchical microspheres were synthesized via a solvothermal process in ethylene glycol. The magnetic microspheres were characterized by X-ray powder diffraction, field-emission scanning electron microscopy, energy-dispersive X-ray spectra, X-ray photoelectron spectroscopy, room-temperature photoluminescence spectra, and vibrating sample magnetometer. The as-prepared samples take on a well-defined spherical architecture following the processes of spontaneous aggregation and localized Ostwald ripening. Dependence of the magnetization and morphology on Ni²⁺ content was observed. Magnetic hysteresis loops reveal that the Ni-doped ZnO microspheres exhibit ferromagnetic loops at room temperature.     

Influence of Co doping content on its valence state in Zn1−xCoxO (0 ≤ x ≤ 0.15) thin films

Zn_1−xCo_xO (0 ≤ x ≤ 0.15) thin films grown on Si (1 0 0) substrates were prepared by a sol-gel technique. The effects of Co doped on the structural, optical properties and surface chemical valence states of the Zn_1−xCo_xO (0 ≤ x ≤ 0.15) films were investigated by X-ray diffraction (XRD), ultraviolet-visible spectrometer and X-ray photoelectron spectroscopy (XPS). XRD results show that the Zn_1−xCo_xO films retained a hexagonal crystal structure of ZnO with better c-axis preferred orientation compared to the undoped ZnO films. The optical absorption spectra suggest that the optical band-gap of the Zn_1−xCo_xO thin films varied from 3.26 to 2.79 eV with increasing Co content from x = 0 to x = 0.15. XPS studies show the possible oxidation states of Co in Zn_1−xCo_xO (0 ≤ x ≤ 0.05), Zn_0.90Co_0.10O and Zn_0.85Co_0.15O are CoO, Co₃O₄ and Co₂O₃, with an increase of Co content, respectively.     

Production of bulk dilute ferromagnetic semiconductor by mechanical milling

We tried to prepare the bulk dilute ferromagnetic semiconductor (DMS) by mechanical milling (MM). Experimental results were as following: (1) The observation of X-ray diffraction and transmitting electron microscopy showed that the particle diameter of host ZnO powder were reduced to about 10 nm by MM. (2) The MM for the mixtures of V₂O₅/ZnO or γ-Fe₂O₃/ZnO realizes the V- or Fe-doped ZnO nano-powders. (3) The values of magnetization under the field of 5 kOe were nearly saturated to 0.8×10⁻³ to 3×10⁻³ μ_B/V-ion for V_xZn_1−xO (x=0.05, 0.1 and 0.2), and 0.2–0.3 μ_B/Fe-ion for Fe_xZn_1−xO (x=0.05 and 0.1) at room temperature. The above results show that the ferromagnetic DMS powder of V_xZn_1−xO and Fe_xZn_1−xO were successfully prepared by MM method.     

Synthesis and characterization of Ni-doped ZnO: A transparent magnetic semiconductor

We report synthesis of a transparent magnetic semiconductor by incorporating Ni in zinc oxide (ZnO) matrix. ZnO and nickel-doped zinc oxide (ZnO:Ni) thin films (∼60 nm) are prepared by fast atom beam (FAB) sputtering. Both undoped and doped films show the presence of ZnO phase only. The Ni concentration (in at%) as determined by energy dispersive X-ray (EDX) technique is ∼12±2%. Magnetisation measurement using a SQUID magnetometer shows that the Ni-doped films are ferromagnetic, having coercivity (H_c) values 192, 310 and 100 Oe and saturation magnetization (M_s) values of 6.22, 5.32 and 4.73 emu/g at 5, 15 and 300 K, respectively. The Ni-doped film is transparent (>80%) across visible wavelength range. Resistivity of the ZnO:Ni film is ∼2.5×10⁻³ Ω cm, which is almost two orders of magnitude lower than the resistivity (∼4.5×10⁻¹ Ω cm) of its undoped counterpart. Impurity d-band splitting is considered to be the cause of increase in conductivity. Interaction between free charges generated by doping and localized d spins of Ni is discussed as the reason for ferromagnetism in the ZnO:Ni film.     

Low-field transport properties of (1−x)La0.7Ca0.2 Sr0.1MnO3+x(ZnO) composites

Composite samples (1−x)La_0.7Ca_0.2Sr_0.1MnO₃(LCSMO)+x(ZnO) with different ZnO doping levels x have been investigated systematically. The structure and morphology of the composites have been studied by the X-ray diffraction (XRD) and scanning electronic microscopy (SEM). The XRD and SEM results indicate that no reaction occurs between LCSMO and ZnO grains, and that ZnO segregates mostly at the grain boundaries of LCSMO. The magnetic properties reveal that the ferromagnetic order of LCSMO is weakened by addition of ZnO. The results also show that ZnO has a direct effect on the resistance of LCSMO/ZnO composites, especially on the low-temperature resistance. With increase of the ZnO doping level, T_P shifts to a lower temperature and the resistance increases. It is interesting to note that an enhanced magnetoresisitance (MR) effect for the composites is found over a wide temperature range from low temperature to room temperature in an applied magnetic field of 3 kOe. The maximum MR appears at x=0.1. The low field magnetoresistance (LFMR) results from spin-polarized tunneling. However, around room temperature, the enhanced MR of the composites is caused by magnetic disorder.     

Effect of ZnO on phase emergence, microstructure and surface modifications of calcium phosphosilicate glass/glass-ceramics having iron oxide

The effect of ZnO on phase emergence and microstructure properties of glass and glass-ceramics with composition 25SiO₂-50CaO-15P₂O₅-(10 − x)Fe₂O₃-xZnO (where x = 0, 2, 5, 7 mol%) has been studied. They have been characterized using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and scanning electron microscopy (SEM). Surface modifications of these glass-ceramics in simulated body fluid have been studied using Fourier transform infrared reflection spectroscopy (FTIR), XPS and SEM. Results have shown a decrease in the fraction of non-bridging oxygen with increase in zinc oxide content. Emergence of crystalline phases in glass-ceramics at different heat treatment temperatures was studied using XRD. When glass is heat treated at 800 °C calcium phosphate, hematite and magnetite are developed as major phases in the glass-ceramics samples with ZnO up to 5 mol%. In addition to these, calcium silicate (Ca₃Si₂O₇) phase is also observed when glass is heat treated at 1000 °C. The microstructure of the glass-ceramics heat treated at 800 °C exhibits the formation of nano-size (40-50 nm) grains. On heat treatment at 1000 °C crystallites grow to above 50 nm size and more than one phase are observed in the microstructure. The formation of thin flake-like structure with coarse particles is observed at high zinc oxide concentration (x = 7 mol%). In vitro studies have shown the surface modifications and formation of Ca-P-rich layer on the glass-ceramics when immersed in simulated body fluids (SBF) for different durations. The bioactive response was found to depend on ZnO content.     

In vitro evaluation of bioactivity of CaO-SiO2-P2O5-Na2O-Fe2O3 glasses

Glasses with compositions 41CaO(52 − x)SiO₂4P₂O₅·xFe₂O₃3Na₂O (2 ≤ x ≤ 10 mol.%) were prepared by melt quenching method. Bioactivity of the different glass compositions was studied in vitro by treating them with simulated body fluid (SBF). The glasses treated for various time periods in SBF were evaluated by examining apatite formation on their surface using grazing incidence X-ray diffraction, Fourier transform infrared reflection spectroscopy, scanning electron microscopy and energy dispersive spectroscopy techniques. Increase in bioactivity with increasing iron oxide content was observed. The results have been used to understand the evolution of the apatite surface layer as a function of immersion time in SBF and glass composition.     

Influence of annealing temperature on structural, optical and magnetic properties of Mn-doped ZnO thin films prepared by sol-gel method

Thin films of Zn_1−xMn_xO (x=0.01) diluted magnetic semiconductor were prepared on Si (1 0 0) substrates by the sol-gel method. The influence of annealing temperature on the structural, optical and magnetic properties was studied by X-ray diffraction (XRD), atom force microscopy (AFM), photoluminescence (PL) and SQUID magnetometer (MPMS, Quantum Design). The XRD spectrum shows that all the films are single crystalline with (0 0 2) preferential orientation along c-axis, indicating there are not any secondary phases. The atomic force microscopy images show the surfaces morphologies change greatly with an increase in annealing temperature. PL spectra reveal that the films marginally shift the near band-edge (NBE) position due to stress. The magnetic measurements of the films using SQUID clearly indicate the room temperature ferromagnetic behavior, and the Curie temperature of the samples is above room temperature. X-ray photoelectron spectroscopy (XPS) patterns suggest that Mn²⁺ ions were successfully incorporated into the lattice position of Zn²⁺ ions in ZnO host. It is also found that the post-annealing treatment can affect the ferromagnetic behavior of the films effectively.     

Characterization, sintering and dielectric properties of nanocrystalline zinc oxide prepared by a citric acid-based combustion route

Nanosized zinc oxide has been synthesized through a novel single step solution combustion route using citric acid as fuel. The X-ray diffraction (XRD) analysis revealed that the synthesized ZnO nanopowder has the pure wurtzite structure. The phase purity of the nanopowder has been confirmed using differential thermal analysis (DTA), thermogravimetric analysis (TGA) and Fourier transform infrared spectroscopy (FT-IR). The morphology and crystalline size of the as-prepared nanopowder characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM) revealed that the powder consisted of a mixture of nanoparticles and nanorods. The nanocrystalline ZnO could be sintered to ∼97% of the theoretical density at 1200 °C in 4 h. The dielectric constant (ε_r) and dielectric loss (ε_i) of sintered ZnO pellets at 5 MHz were 1.38 and 9×10⁻², respectively, at room temperature.     

Studies of structural and morphological characteristics of flower-like ZnO thin film and its application as photovoltaic material

In this work a new method has been employed to synthesize nanocrystalline ZnO powder under hydrothermal conditions at 80 °C using aqueous Zn(NO₃)₂·6H₂O solution and diethylamine (DEA) as the starting materials. The ZnO powder prepared by this novel method was characterized by XRD, energy dispersive X-ray spectroscopy (EDX), FTIR and UV–vis techniques. Calculation based on XRD data revealed ZnO particles to be of nanometer size (∼33 nm). The ZnO powder was subsequently used to make its thin film which exhibited flower like morphology when examined by SEM. Thin ZnO films were sensitized with N719 dye, (Bu₄N)₂[Ru(dcbpyH)₂(NCS)₂], and used as photo-anode to construct sandwich type dye-sensitized solar cell (DSSC). With such cells, V_OC = 0.680 V, J_SC = 0.61 mA cm⁻², fill factor = 0.43 and overall conversion efficiency η = 0.23% were achieved on illumination with visible light (80 mW cm⁻²).     

Effect of a LaSrCoO3 buffer layer on Pb1 − xLaxTi1 − x/4O3 films studied by polarized Raman spectroscopy

A confocal Raman investigation of Pb_1 − xLa_xTi_1 − x/4O₃ (PLT) thin films grown by RF magnetron sputtering on PbO_x/Pt/Ti/SiO₂/Si substrates with an intermediate LaSrCoO₃ (LSCO) layer was performed. The influence of the LaSrCoO₃ buffer layer was analyzed taking advantage of the observed Raman spectral band variation, which varied according to different manufacturing procedures. In the presence of a LSCO layer, the A1(1TO) Raman mode, which was indicative of tetragonal distortion, was pronouncedly enhanced, and a slight deviation from the (0 0 1) plane of the film was observed from the angular dependence of the polarized Raman spectral intensity. Furthermore, the spectral band variation as well as the residual stress along the in-depth direction was measured in the film from cross-sectional spectral line scans. This latter measurement showed a relaxation of the lattice mismatch in the presence of LSCO and PbO layers.     

Synthesis and characterization of room-temperature ferromagnetism in Fe- and Ni-co-doped In2O3

Observation of room-temperature ferromagnetism in Fe- and Ni-co-doped In₂O₃ samples (In_0.9Fe_0.1−xNi_x)₂O₃ (0?x?0.1) prepared by citric acid sol-gel auto-igniting method is reported. All of the samples with intermediate x values are ferromagnetic at room-temperature. The highest saturation magnetization (0.453 μ_B/Fe+Ni ions) moment is reached in the sample with x=0.04. The highest solubility of Fe and Ni ions in the In₂O₃ lattice is around 10 and 4 at%, respectively. The 10 at% Fe-doped sample is found to be weakly ferromagnetic, while the 10 at% Ni-doped sample is paramagnetic. Extensive structure including Extended X-ray absorption fine structure (EXAFS), magnetic and magneto-transport including Hall effects studies on the samples indicate the observed ferromagnetism is intrinsic rather than from the secondary impurity phases.     

Structural and photoluminescence analysis of Zn1 − xMnxO nanocrystalline powders

This Letter reports on structural and photoluminescence properties of Zn_1 − xMn_xO nanocrystalline powders, which were synthesized by using oxalate precursor decomposition method. From the XRD features, we have noticed that all samples exhibit wurtzite crystal structure. The origin of photoluminescence properties of Mn doped and undoped ZnO have been discussed.     

Photosensitivity of nanocrystalline ZnO films grown by PLD

We have studied the properties of ZnO thin films grown by laser ablation of ZnO targets on (0 0 0 1) sapphire (Al₂O₃), under substrate temperatures around 400 °C. The films were characterized by different methods including X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and atomic force microscopy (AFM). XPS analysis revealed that the films are oxygen deficient, and XRD analysis with θ-2θ scans and rocking curves indicate that the ZnO thin films are highly c-axis oriented. All the films are ultraviolet (UV) sensitive. Sensitivity is maximum for the films deposited at lower temperature. The films deposited at higher temperatures show crystallite sizes of typically 500 nm, a high dark current and minimum photoresponse. In all films we observe persistent photoconductivity decay. More densely packed crystallites and a faster decay in photocurrent is observed for films deposited at lower temperature.     

EPR and magnetic properties of MgO-CaO-SiO2-P2O5-CaF2-Fe2O3 glass-ceramics

Glass-ceramics have been derived from 4.5MgO(45−x)CaO34SiO₂16P₂O₅0.5CaF₂xFe₂O₃ (x=5, 10, 15, 20 wt%) glasses by heat treatment. Room temperature electron paramagnetic resonance (EPR) spectra and temperature-dependent magnetic susceptibility (χ) of the glass-ceramics have been obtained. The EPR absorption line centered at g≈4.3 disappeared at higher concentrations of iron oxide. The intensity and line width of the EPR absorption line centered at g≈2.1 increased as the iron oxide concentration was increased. Temperature-dependent magnetization of samples with low iron oxide content revealed ferrimagnetic as well as paramagnetic contributions. Information about the structural changes involving iron ions, their valence state and the type of magnetic interactions between the Fe ions as a function of composition was obtained using EPR and χ studies.