Effect of Cr doping on the magnetic and electrical transport properties of charge-ordered Bi0.5Ca0.5MnO3

An experimental study on the magnetic and electrical transport properties of the manganites Bi_0.5Ca_0.5Mn_1−xCr_xO₃ (BCMCO) (0≤x≤0.12) is carried out. The results show that Cr doping can suppress the charge-ordering transition, favoring the ferromagnetic clusters. For x=0.12, the charge-ordering transition disappears but a very broad paramagnetic-ferromagnetic-like transition is detected at the Curie temperature T_C=72.6 K. It is caused by phase separation or coexistence of the charge-ordering and ferromagnetic phase. Moreover, the critical Cr content to destroy charge ordering phase in BCMCO does not match the general monotonous tendencies shown by Cr-doped Re_0.5Ca_0.5MnO₃ (Re-rare-earth). These differences are ascribed to the fact that the ground state in BCMCO differs markedly from the ferromagnetic metallic phase in Cr-doped Re_0.5Ca_0.5MnO₃ compounds.     

Spin glass ordering of Zn0.75Co0.25Fe0.5Cr1.5O4 cubic spinel

The linear and nonlinear low field AC susceptibilities of Zn_0.75Co_0.25Fe_0.5Cr_1.5O₄ show peaks due to non-critical contributions, which mask the peak due to spin glass ordering. They extend into the region of temperatures in which Mössbauer spectra do not show any magnetic component. When a DC field of 200 Oe suppresses the non-critical contributions, peak due to spin glass ordering is clearly visible. The spin glass ordering is thus shown to be a thermodynamic transition. The critical exponent is found to fall within the range found using other spin glasses. Mössbauer spectra in zero fields provide T_SG, which agrees with the peak temperature of AC susceptibilities in the absence of non-critical contributions. 〈S_Z〉 determined using Mössbauer spectra does not show any anomaly. In the presence of a field of 5 T, the spectra show SG ordering at 4.2 K, which converts into ferrimagnetic ordering at higher temperatures.     

Charge order melting and magnetic transition in Nd0.5(1+x)Ca0.5(1−x)Mn(1−x)CrxO3 system

The magnetic property of double doped manganite Nd_0.5(1+x)Ca_0.5(1−x)Mn_(1−x)Cr_xO₃ with a fixed ratio of Mn³⁺:Mn⁴⁺=1:1 has been investigated. For the undoped sample, it undergoes one transition from charge disordering to charge ordering (CO) associated with paramagnetic (PM)-antiferromagnetic (AFM) phase transition at T<250 K. The long range AFM ordering seems to form at 35 K, rather than previously reported 150 K. At low temperature, an asymmetrical M-H hysteresis loop occurs due to weak AFM coupling. For the doped samples, the substitution of Cr³⁺ for Mn³⁺ ions causes the increase of magnetization and the rise of T_c. As the Cr³⁺ concentration increases, the CO domain gradually becomes smaller and the CO melting process emerges. At low temperature, the FM superexchange interaction between Mn³⁺ and Cr³⁺ ions causes a magnetic upturn, namely, the second FM phase transition.     

Li0.5Fe2.5−xMnxO4 ferrite sintered from microwave-induced combustion

Li_0.5Fe_2.5−xMn_xO₄ (0≦x≦1.0) powders with small and uniformly sized particles were successfully synthesized by microwave-induced combustion, using lithium nitrate, ferric nitrate, manganese nitrate and carbohydrazide as the starting materials. The process takes only a few minutes to obtain as-received Mn-substituted lithium ferrite powders. The resultant powders annealed at 650 ^°C for 2 h and were investigated by thermogravimeter/differential thermal analyzer (TG/DTA), X-ray diffractometer (XRD), transmission electron microscopy (TEM), vibrating sample magnetometer (VSM), and thermomagnetic analysis (TMA). The results revealed that the Mn content were strongly influenced the magnetic properties and Curie temperature of Mn-substituted lithium ferrite powder. As for sintered Li_0.5Fe_2.5−xMn_xO₄ specimens, substituting an appropriate amount of Mn for Fe in the Li_0.5Fe_2.5−xMn_xO₄ specimens markedly improved the complex permeability and loss tangent.     

Spin-glass like behaviour in a concentrated chromium spinel: Zn0.5Cd0.5Cr2S4

Low field d.c. and a.c. susceptibility measurements are reported for the non magnetically diluted spinel Zn_0.5Cd_0.5Cr₂S₄. A spin-glass like behaviour is observed at low temperature (T_F = 15.4Katv = 198 Hz).This is the result of the presence of competing interactions (ferromagnetic between nearest-neighbours and antiferromagnetic between higher order neighbours) and of the disorder of their distribution due to the substitution between non-magnetic zinc and cadmium ions in the tetrahedral sites of the spinel lattice.     

Preparation of substituted barium ferrite BaFe12−x(Ti0.5Co0.5)xO19 by citrate precursor method and compositional dependence of their magnetic properties

As a possible candidate for the left-handed metamaterial with negative permeability, a series of Ti, Co-substituted M-type barium hexaferrite BaFe_12−x(Ti_0.5Co_0.5)_xO₁₉ (x=0, 1, 2, 3, 4 and 5) was prepared by citrate precursor method. The formation processes of the substituted barium hexaferrite compounds from the precursors were followed by the measurements of powder X-ray diffraction (XRD), Infrared absorption spectra (FT-IR), and thermogravimetry and differential thermal analysis (TG/DTA) coupled with mass spectroscopy (MS). In the case of the non-substituted sample, the formation of the barium hexaferrite is regulated by the thermal decomposition of BaCO₃ and the solid-state reactions of BaO and Fe₂O₃ in the temperature range from 800 to 1100 K. The formation temperature of the substituted BaFe_12−x(Ti_0.5Co_0.5)_xO₁₉ is higher than that for the non-substituted sample and increases with the value of x, due to the effects of carbonate ions incorporated by the partial substitution of Fe³⁺ by (Ti_0.5Co_0.5)³⁺. On heating up to ca. 1200 K, all the substituted samples transform into the magenetoplumbite phase as is the non-substituted sample. The compositional dependence of the magnetic properties of the substituted barium hexaferrite was investigated by the magnetization measurement. The decrease in the magnetic anisotropy was confirmed by the change in the magnetization curve and coercivity H_C with the composition x. A negative permeability spectrum was observed in the BaFe₉(Ti_0.5Co_0.5)₃O₁₉ in the frequency range from 2 to 4 GHz.     

Antiferromagnetism and spin-glass transition in the FeInxCr2−xSe4 series of selenides

The magnetic behavior of the FeIn_xCr_2−xSe₄ system (with x=0.0, 0.2 and 0.4) has been investigated by magnetic and Mössbauer spectroscopy. Hyperfine parameters indicate that iron is in the Fe²⁺ oxidation state, with a minor (∼9%) Fe³⁺ fraction, located at different layers in the structure. Low-field magnetization curves as a function of temperature showed that the antiferromagnetic (AFM) order temperature is T_N=208(2) K for FeCr₂Se₄ and decreases to 174(3) K for FeIn_0.4Cr_1.6Se₄. The effective magnetic moment μ_eff decreases with increasing In contents, and shows agreement with the expected values from the contribution of Fe²⁺ (⁵D) and Cr³⁺ (⁴F) electronic states. A second, low-temperature transition is observed at T_G∼13 K, which has been assigned to the onset of a glassy state.     

Heat capacity and magnetic properties of pyrochlore Hg2Os2O7

Hg₂Os₂O₇, which has the cubic pyrochlore structure, remains metallic down to the liquid helium temperature unlike its isostructural counterpart Cd₂Os₂O₇, which shows metal-insulator transition at 226 K. Magnetization and heat capacity data for Hg₂Os₂O₇ are presented. The magnetic anomaly at T_N=88 K shares many characteristics in common with the metal-insulator transition in Cd₂Os₂O₇, though Hg₂Os₂O₇ remains metallic below T_N. The heat capacity C_p shows no or very little change in the magnetic entropy around T_N, supporting the view that there is no long-range ordering of localized spins. The measured value of electronic heat-capacity coefficient γ=21 mJ K⁻²mol⁻¹ is comparable to the value obtained from band-structure calculation on Cd₂Os₂O₇, suggesting that mass-enhancement is small in Hg₂Os₂O₇. There is a pronounced peak in C_p/T³ at 13.1 K, which corresponds to a peak in the phonon density of states at 40 cm⁻¹.     

Magnetic structure of the manganites heavily doped by Fe and Cr ions

Powder neutron diffraction and magnetic studies have been performed for NdMn_0.5Fe_0.5O₃ and NdMn_0.5Cr_0.5O₃ manganites. In NdMn_0.5Cr_0.5O₃, magnetic structure has been revealed consisting of ferromagnetic and G-type antiferromagnetic components as result of a 3d-ions magnetic moments ordering. Magnetic moments of Nd-ions are parallel to the ferromagnetic component. In NdMn_0.5Fe_0.5O₃ only the antiferromagnetic G-type structure has been found whereas Nd-sublattice was not ordered. In the both compounds, magnetic moments of 3d-ions are significantly less than one can expect, what is interpreted in terms of intrinsic chemical inhomogeneity. Magnetic phase diagrams have been constructed for the Nd(Mn_1−xM_x)O₃ (M=Fe, Cr) systems, interpreted assuming superexchange interactions Mn³⁺–O–Cr³⁺ to be positive, Mn³⁺–O–Fe³⁺ negative and taking into account a disordered arrangement of Mn and Cr ions in the crystal structure sublattice as well as interplay between Jahn–Teller effect and superexchange interactions.     

Effect of SnO2 coating on the magnetic properties of nanocrystalline CuFe2O4

Nanocrystalline CuFe₂O₄ and CuFe₂O₄/xSnO₂ nanocomposites (x=0, 1, 5 wt%) have been successfully synthesized by one-pot reaction of urea-nitrate combustion method. The transmission electron microscope study reveals that the particle size of the as synthesized CuFe₂O₄ and CuFe₂O₄/5 wt%SnO₂ are 10 and 20 nm, respectively. The SnO₂ coating on the nanocrystalline CuFe₂O₄ was confirmed from HRTEM studies. The resultant products were sintered at 1100 °C and characterized by XRD and SQUID for compound formation and magnetic studies, respectively. The X-ray diffraction pattern shows the well-defined sharp peak that confirms the phase pure compound formation of tetragonal CuFe₂O₄. The zero field cooled (ZFC) and field cooled (FC) magnetization was performed using SQUID magnetometer from 2 to 350 K and the magnetic hysteresis measurement was carried out to study the magnetic properties of nanocomposites.     

Growth temperature dependence of the hysteretic behavior of Ni0.5Zn0.5Fe2O4 thin films

Herein, a discussion of the effect of deposition temperature on the magnetic behavior of Ni_0.5Zn_0.5Fe₂O₄ thin films. The thin films were grown by r.f. sputtering technique on (1 0 0) MgO single-crystal substrates at deposition temperatures ranging between 400 and 800 °C. The grain boundary microstructure was analyzed via atomic force microscopy (AFM). AFM images show that grain size (φ∼70-112 nm) increases with increasing deposition temperature, according to a diffusion growth model. From magneto-optical Kerr effect (MOKE) measurements at room temperature, coercive fields, H_c, between 37and 131 Oe were measured. The coercive field, H_c, as a function of grain size, reaches a maximum value of 131 Oe for φ ∼93 nm, while the relative saturation magnetization exhibits a minimum value at this grain size. The behaviors observed were interpreted as the existence of a critical size for the transition from single- to multi-domain regime. The saturation magnetization (21 emu/g<M_s<60 emu/g) was employed to quantify the critical magnetic intergranular correlation length (L_c≈166 nm), where a single-grain to coupled-grain behavior transition occurs. Experimental hysteresis loops were fitted by the Jiles-Atherton model (JAM). The value of the k-parameter of the JAM fitted by means of this model (k/μ_o∼50 A m²) was correlated to the domain size from the behavior of k, we observed a maximum in the density of defects for the sample with φ∼93 nm.     

Effect of 3d metal ion doping on the structure and superconductivity of (Tl0.5Pb0.5)Sr2CaCu2O7

(Tl_0.5Pb_0.5)Sr₂Ca(Cu_2−xM_x)O₇ (M=Co, Ni and Zn) have been synthesized and investigated by means of X-ray diffraction, scanning electron microscope, electrical resistivity and magnetic susceptibility measurements. X-ray diffraction patterns show that all studied samples contain the nearly single ‘1212’ phase. They crystallize in a tetragonal unit cell with a=3.8028-3.8040 Å and c=12.0748-12.1558 Å. In (Tl_0.5Pb_0.5)Sr₂Ca(Cu_2−xM_x)O₇ system (M=Co or Ni), the superconducting critical temperature T_c decreases linearly with both Co and Ni concentrations and the rate of T_c decrease is around −6.5 and −7.0 K/at%, respectively. For (Tl_0.5Pb_0.5)Sr₂Ca (Cu_2−xZn_x)O₇ system, the dependence of T_c on the Zn dopant concentration deviates from a linear behavior and the Zn substitution suppresses T_c much less (−2.5 K/at%) than the Co and Ni substitutions. The suppression in T_c in Co and Ni doped samples are attributed to the magnetic pair-breaking mechanism and the reduction in the carrier concentration. The suppression of T_c in Zn doped samples is not caused by the reduction in carrier concentration which should remain constant, but rather due to nonmagnetic pair-breaking mechanism induced by disorder as well as the filling of the local Cu d_x²−y² state due to the full d band of Zn ions.     

Giant strain associated with microstructure control by magnetic field in Fe-31.2Pd, CoO and Nd0.5Sr0.5MnO3

We have made in situ optical microscope observation for the microstructure control driven by magnetic field in Fe-31.2Pd (at%), CoO and Nd_0.5Sr_0.5MnO₃. These materials exhibit structural transitions, and their low-temperature phases are composed of several crystallographic domains (variants), which are separated by twinning planes. In the case of ferromagnetic Fe-31.2Pd and antiferromagnetic CoO, the magnetic field promotes the twinning plane movement. This movement gives a large strain of several percent and is essentially explained by the fact that the magnetic shear stress, which corresponds to the magnetic anisotropy energy divided by the twinning shear, is larger than the twinning stress. In the case of Nd_0.5Sr_0.5MnO₃, the twinned microstructure of the charge-ordered phase disappears under a magnetic field in association with the melting of the charge-ordered phase.     

Spin-glass-like behaviour and magnetic order in Mn[Cr0.5Ga1.5]S4 spinels

Magnetization and susceptibility were investigated as a function of temperature and magnetic field in polycrystalline Mn[Cr_0.5Ga_1.5]S₄ spinel. The dc susceptibility measurements at 919 Oe showed a disordered ferrimagnetic behaviour with a Curie-Weiss temperature θ_CW=−55 K and an effective magnetic moment of 5.96 μ_B close to the spin-only value of 6.52 μ_B for Cr³⁺ and Mn²⁺ ions in the 3d³ and 3d⁵ configurations, respectively. The magnetization measured at 100 Oe revealed the multiple magnetic transitions with a sharp maximum at the Néel temperature T_N=3.9 K, a minimum at the Yafet-Kittel temperature T_YK=5 K, a broad maximum at the freezing temperature T_f=7.9 K, and an inflection point at the Curie temperature T_C=48 K indicating a transition to paramagnetic phase. A large splitting between the zero-field-cooled (ZFC) and field-cooled (FC) magnetizations at a temperature smaller than T_C suggests the presence of spin-glass-like behaviour. This behaviour is considered in a framework of competing interactions between the antiferromagnetic ordering of the A(Mn) sublattice and the ferromagnetic ordering of the B(Cr) sublattice.     

The effect of pressure on the spin density wave transition in the layered cobaltites [Ca2CoO3]0.62[CoO2] and [Ca2Co4/3Cu2/3O4]0.62[CoO2]

In order to investigate the pressure effect on the magnetism in the layered cobaltites, positive muon spin rotation and relaxation μ⁺SR experiments have been carried out up to 1.3 GPa using c-aligned polycrystalline samples of [Ca₂CoO₃]_0.62[CoO₂] and [Ca₂Co_4/3Cu_2/3O₄]_0.62[CoO₂]. A transverse field μ⁺SR experiment indicates that the transition temperature to an incommensurate spin density wave IC-SDW state is independent of hydrostatic pressure up to 1.3 GPa for the both compounds. Furthermore, there are no changes in the spontanious muon precession frequency in zero field at 5 K even under 1.3 GPa. These results strongly suggest that the IC-SDW exists not in the rocksalt-type block ([Ca₂CoO₃] and/or [Ca₂Co_4/3Cu_2/3O₄]) but in the CoO₂ plane.     

Crystal field analysis of energy level structure of the Cr2O3 antiferromagnet

A detailed analysis of the energy level structure of the six-fold coordinated Cr³⁺ ion in the chromium oxide Cr₂O₃ is performed using the exchange charge model of the crystal field theory. Parameters of the crystal field acting on the Cr³⁺ optical electrons are calculated from the crystal structure data for the [CrO₆]⁹⁻ impurity center. The energy levels obtained are compared with the experimental absorption spectra for the considered crystal; a good agreement with experimental data is demonstrated. One possible explanation for the ultraviolet p₁ absorption band is proposed based on the results of crystal field calculations.     

Research on charge-ordering state in La0.5Sr0.5MnO2.88 and La0.5Sr0.5Mn0.5Ti0.5O3 systems

The structural, magnetic and transport properties of La_0.5Sr_0.5MnO_2.88 and La_0.5Sr_0.5Mn_0.5Ti_0.5O₃ samples have been investigated systematically. Indeed, this series has been considered to understand the influence of physical parameters such as oxygen deficiency and titanium doping effect in undoped La_0.5Sr_0.5MnO₃ sample. Ceramic material based on La_0.5Sr_0.5MnO_2.88 exhibits interesting behaviours of charge-ordering (CO), ferromagnetic (FM) states and a good conductivity down to the lowest temperatures. The substitution of Ti for Mn destroyed drastically the CO, damaged the motion of itinerant e_g electrons and changed the local parameters of perovskite cell. A change of the structure from tetragonal to rhombohedral symmetry is observed causing a weakening of double-exchange interaction. The experiment results show that the suppression of the CO is sensitive to the variety of Mn³⁺/Mn⁴⁺ ratio. In a field of 8 T at 10 K, FM and CO phase can be evaluated to be ∼20:80 according to the μ_exp/μ_cal ratio for La_0.5Sr_0.5MnO_2.88, whereas the CO state is suppressed for La_0.5Sr_0.5Mn_0.5Ti_0.5O₃ sample, FM and anti-ferromagnetic (AFM) phase are coexisted and evaluated to be ∼54:46, respectively.     

Microstructure characterization and magnetic behavior of NiAlxFe2−xO4 and Ni1−yMnyAl0.2Fe1.8O4 ferrites

NiAl_xFe_2−xO₄ and Ni_1−yMn_yAl_0.2Fe_1.8O₄ ferrites were prepared by the conventional ceramic method and were characterized by X-ray diffraction, scanning electron microscopy, and magnetic measurements. The single spinel phase was confirmed for all prepared samples. A proper explanation of data is possible if the Al³⁺ ions are assumed to replace Fe³⁺ ions in the A and B sites simultaneously for NiAl_xFe_2−xO₄ ferrites, and if the Mn²⁺ ions are assumed to replace Ni²⁺ ions in the B sites for Ni_1−yMn_yAl_0.2Fe_1.8O₄ ferrites. Microstructural factors play an important role in the magnetic behavior of Ni_1−yMn_yAl_0.2Fe_1.8O₄ ferrites with large Mn²⁺ content.     

Suitability of water based magnetic fluid with CoFe2O4 particles in hyperthermia

Magnetic susceptibility of the magnetic fluid with CoFe₂O₄ particles was measured in the low-frequency range in order to determine mean values of the magnetic grain size and the saturation magnetisation. The volume concentration of the solid phase (CoFe₂O₄) was also found. Results of the calorimetric measurements, in the range from 70 kHz to 1.7 MHz, confirmed the suitability of use of the medium studied in magnetic fluid hyperthermia, especially in the frequency region 600–800 kHz. The H²–law-type dependence of the specific absorption rate on the square amplitude of the magnetic field testified to the presence of superparamagnetic particles in the magnetic fluid. The minimum magnetic field intensity needed for successful hyperthermal treatment was experimentally determined.     

Surface magnetic disorder in nanostructured Ni0.5Zn0.5Fe2O4 particles

Nanostructured ferroxide particles with initial formula Ni_0.5Zn_0.5Fe₂O₄ are investigated. The aim was to explore the monodomain and the superparamagnetic states of the ferrospinel and the impact of the surface magnetic disorder on the magnetization processes. Mössbauer spectroscopy (MöS) demonstrated that the ion distribution follows the general formula (Zn_0.5Fe_0.5)_A[Ni_0.5Fe_1.5]_BO₄, where A is the tetrahedral and B, the octahedral sublattice. MöS in an external magnetic field (5 T) at 4.2 K shows non-collinearity of the sublattices’ magnetic moments and deviations in the hyperfine magnetic field that could be related to a canting effect. Magnetic measurements were applied to characterize the temperature behavior of the magnetic properties and the a.c. complex magnetic susceptibility.