Cr2O3和CrO3/Cr2O3催化剂的2-氯-1,1,1-三氟乙烷气相氟化反应的活性物种和失活

采用沉淀法和浸渍法制备了2种铬基（Cr₂O₃和CrO₃/Cr₂O₃）催化剂,用于气相氟化2-氯-1,1,1-三氟乙烷合成1,1,1,2-四氟乙烷。研究发现含有低价铬（Cr³⁺）物种的Cr₂O₃催化剂上2-氯-1,1,1-三氟乙烷的稳态转化率为18.5%,而含有高价铬（Cr⁶⁺）物种和低价铬（Cr³⁺）物种的CrO₃/Cr₂O₃催化剂初始转化率达到30.6%,然而存在明显的失活。含有Cr⁶⁺物种的CrO₃/Cr₂O₃催化剂的2-氯-1,1,1-三氟乙烷氟化反应初始TOF值为1.71×10^-4 mol_HCFC-133a·mol_Cr（Ⅵ）^-1·s^-1,高于含有Cr³⁺物种的Cr₂O₃催化剂（4.16×10^-5 mol_HCFC-133a·mol_Cr（Ⅲ）^-1·s^-1）。Cr₂O₃催化剂在氟化反应前后催化剂的物相结构保持不变;而含有高价铬物种的CrO₃/Cr₂O₃催化剂经HF反应后生成了CrO_xF_y活性物种。然而,CrO_xF_y物种在反应中挥发或转化成稳定但无活性的CrF₃,从而导致催化剂失活。     

Cr3+掺杂Ca4HfGe3O12宽带近红外荧光粉的发光特性及应用

近红外荧光粉在生物活体成像领域展现出重要的应用前景。但活体成像用近红外荧光粉存在种类匮乏、耐温性差等瓶颈问题。采用固相法合成了宽带近红外Ca₄HfGe₃O₁₂∶ xCr³⁺(0≤x≤0.09)荧光粉。X射线衍射和能谱分析的结果表明Cr³⁺离子成功进入Ca₄HfGe₃O₁₂晶格。在469 nm蓝光激发下,Ca₄HfGe₃O₁₂∶xCr³⁺荧光粉发射出690~1 200 nm的宽带近红外光,峰值波长为825 nm (⁴T₂-⁴A₂),半高宽达到141 nm,Cr³⁺掺杂最佳浓度为0.03。依据激发光谱峰形和寿命衰减行为,证实Cr³⁺仅占据基质中一种阳离子格位。Ca₄HfGe₃O₁₂∶0.03Cr³⁺荧光粉的荧光量子效率为33.63%,该荧光粉发射光谱在400 K下的积分面积为室温下的60.5%,表明该样品具有优良的热稳定性。采用自制近红外荧光粉转换器件照射人手掌和滤波片遮挡的水果,观察到清晰地静脉血管和遮挡水果的轮廓。     

电荷补偿对Ba2ZnGe2O7：Bi3+荧光粉发光性质的影响

采用高温固相法制备了2个系列的荧光粉样品：Ba_2-xZnGe₂O₇：xBi³⁺（系列Ⅰ）和Ba_1.994-yK_yZnGe₂O₇：0.006Bi³⁺（系列Ⅱ）。X射线衍射（XRD）测试结果表明,少量Bi³⁺、K⁺的掺杂不会明显改变材料的物相结构。样品的荧光光谱测试结果表明,虽然2个系列样品的发光光谱都随组成成分变化有少量变化,但发光颜色基本上均为黄绿色。在358 nm的激发下,荧光粉的发射光谱呈现一个峰值在500 nm的宽发射带,归属于³P₁→¹S₀能级跃迁。在500 nm监测下,荧光粉的最强激发峰位于358 nm,归属于¹S₀→³P₁能级跃迁,此外还有一个位于320 nm的肩峰归属于O^2--Bi³⁺电荷转移带。系列Ⅰ样品的光谱数据结果指出,Bi³⁺的最佳掺杂量x为0.006。在该基质中,Bi³⁺掺杂取代Ba²⁺属于不等价取代,会在晶格中产生Ba²⁺空位或间隙O^2-,对材料的发光强度产生负面影响。对此,采用K⁺与Bi³⁺协同掺杂起到电荷补偿的作用,填补Ba²⁺空位或捕获间隙O^2-缺陷。空位被填补或间隙被捕获均减少了晶格畸变,从而使发光强度明显提高。系列Ⅱ样品的光谱数据表明,完全电荷补偿的荧光粉样品相比于没有掺K⁺的样品,其发光强度提高了约2.5倍。     

CrOx/SiO2催化剂上丙烷在CO2气氛中脱氢反应的研究

采用XRD、UV-vis DRS、ESR和微分吸附量热等技术,考察了铬担载量分别为2.5、5和10wt%的CrO_x/SiO₂催化剂的结构、表面性质和氧化还原性能。结果表明,催化剂表面上存在多种Cr的氧化态和聚集形式。随着Cr担载量从2.5wt%到10wt%的逐渐增大,催化剂表面占主导地位的Cr物种由CrO₃单体转为多聚CrO₃和Cr₂O₃晶相。在CO₂气氛中催化剂对丙烷转化率和丙烯选择性的大小顺序为2.5wt%CrO_x/SiO₂>5wt%CrO_x/SiO₂>10wt%CrO_x/SiO₂,反应过程中的原位ESR和UV-visDRS测定结果表明,催化剂表面的反应活性中心为Cr⁵⁺,Cr⁵⁺可由催化剂预处理过程中Cr³⁺的氧化及丙烷反应过程中CrO₃单体的还原产生,在反应中CO₂可使Cr³⁺重新氧化为Cr⁵⁺.     

面向异丁烷脱氢介孔γ-Al2O3基催化剂的合成及其高催化性能

采用溶剂蒸发自组装法调控载体形貌及孔道结构,成功制备了有序介孔氧化铝载体。以铬氧物种为活性组分,碱金属钾为助剂,采用浸渍法制备负载型催化剂,用于异丁烷催化脱氢反应,研究了反应温度、原料流速、催化剂粒径等因素对催化性能的影响。采用X射线粉末衍射、透射电子显微镜、N₂物理吸附、氢气程序升温还原及热重等表征方法探讨了载体形貌、孔道结构与催化性能的构效关系,结果表明,低温下有利于控制异丙醇铝的水解和缩合及介孔γ-Al₂O₃的研制。与常规的γ-Al₂O₃相比,所制备的介孔γ-Al₂O₃的有更大的比表面积和良好的有序性,在600℃、101.325kPa、GHSV=1 000 h^-1的条件下,10%（w/w）Cr₂O₃/γ-Al₂O₃催化剂性能最佳,异丁烷的转化率达63.1%,异丁烯的选择性达到85.5%。与传统的催化剂相比,介孔Cr₂O₃/γ-Al₂O₃催化剂具有大的比表面积,高度分散的活性组分,优良的催化性能和良好的抗积碳能力。     

MOF-1和Tb@MOF-1荧光探针的设计、合成及对痕量Cr2O72-、S2O82-离子的识别

采用5-（（4-吡啶基）甲氧基）-异烟酸（H₂PLIA）、1,3,5-三（1-咪唑基）-苯（TIB）合成了金属有机骨架[Cd （PLIA）（TIB）]_n （MOF-1）。MOF-1是具有理想一维孔道的二维结构化合物,其一维孔道由柔性三角形PLIA^2-配体和刚性三角形TIB配体间隔形成。利用MOF-1易掺杂的优势,采用后修饰合成策略制备了Tb@MOF-1。对MOF-1和Tb@MOF-1进行了基本表征及荧光探针性能研究。2种探针材料具有相同的结构。MOF-1和Tb@MOF-1分别对水溶液中的Cr₂O₇^2-和S₂O₈^2-离子具有较强荧光识别能力,均有响应时间快,稳定性、选择性、灵敏度高的特点。研究了MOF-1和Tb@MOF-1对Cr₂O₇^2-和S₂O₈^2-的荧光识别机理,其不同可能与Tb³⁺离子掺杂有关。     

CaSb2O6:Bi3+,Eu3+荧光粉的制备和发光性质

采用共沉淀法及1 200 ℃后续煅烧4 h,成功制备了CaSb₂O₆:Bi³⁺,Eu³⁺荧光粉,并对其结构及发光性能进行了研究。所制备荧光粉颗粒为六边形类圆饼状,平均尺寸在100~600 nm之间。对CaSb₂O₆:Bi³⁺,Eu³⁺发光的机理分析表明,Bi³⁺对Eu³⁺的发光存在高效的敏化与能量传递。当Bi³⁺和Eu³⁺的掺杂浓度分别为0.5%和8%,Eu³⁺位于580 nm(⁵D₀→⁷F₀ )处的荧光发射显著增强,Bi³⁺,Eu³⁺共掺样品的荧光强度是CaSb₂O₆:Eu³⁺的10倍左右。调节Bi³⁺/Eu³⁺离子掺杂比,色坐标呈现了从蓝、白光到红光的变化,表明该荧光粉可分别作为蓝或红色荧光粉使用,甚至可实现从蓝、白光到红光的自由调控,这为白光LED荧光粉的发展提供了参考。     

α-Ti(HPO4)2微球负载型催化剂的合成及其烯烃聚合催化性能

2种茂金属催化剂及1种后过渡金属催化剂分别被固载于经过甲基铝氧烷处理后的α-Ti（HPO₄）₂微球表面,制备得到3种微球负载型催化剂。在烯烃聚合反应过程中,3种负载型催化剂均表现出比硅胶负载型催化剂更高的催化活性。2种茂金属负载型催化剂在乙烯、丙烯聚合反应中的活性分别高达6.8×10⁷ g_PE·（mol_Zr·h）^-1和5.0×10⁷ g_PP·（mol_Zr·h）^-1,所产生的烯烃聚合产物分子量分布较窄（M_w/M_n<2.3）,表现出良好的单中心催化特性,而且丙烯聚合产物的等规度高达96.5%。负载型后过渡金属催化剂在乙烯聚合反应中的活性稍低,但也能够达到8.3×10⁶ g_PE·（mol_Fe·h）^-1。3种负载型催化剂催化烯烃聚合产物均成微球型,能够很好地复制载体的形貌。     

MOF-1和Tb@MOF-1荧光探针的设计、 合成及对痕量Cr2O72-、 S2O82-离子的识别

采用5-((4-吡啶基)甲氧基)-异烟酸(H₂PLIA)、1,3,5-三(1-咪唑基)-苯(TIB)合成了金属有机骨架[Cd(PLIA)(TIB)]_n (MOF-1),MOF-1是具有理想一维孔道的二维结构化合物,其一维孔道由柔性三角形PLIA^2-配体和刚性三角形TIB配体间隔形成。利用MOF-1 易掺杂的优势,采用后修饰合成策略制备了Tb@MOF-1。对MOF-1 和Tb@MOF-1 进行了基本表征及荧光探针性能研究。2种探针材料具有相同的结构。MOF-1和Tb@MOF-1分别对水溶液中的Cr₂O₇^2-和S₂O₈^2-离子具有较强荧光识别能力,均有响应时间快,稳定性、选择性、灵敏度高的特点。研究了MOF-1和Tb@MOF-1对Cr₂O₇^2-和S₂O₈^2-的荧光识别机理,其不同可能与Tb³⁺离子掺杂有关。     

Li1.2Mn0.54Ni0.13Co0.13O2正极材料的Ga2O3包覆改性及电化学性能

首先采用共沉淀方法制备富锂锰基正极材料Li_1.2Mn_0.54Ni_0.13Co_0.13O₂原始样品(P-LRMO),然后通过简单的湿化学法以及低温煅烧方法对其进行不同含量Ga₂O₃原位包覆。透射电子显微镜(TEM)以及X射线光电子能谱(XPS)结果表明在P-LRMO表面成功合成了Ga₂O₃包覆层。电化学测试结果表明：含有3%Ga₂O₃的改性材料G3-LRMO具有最优的电化学性能,其在0.1C倍率(电流密度为25 mA·g^-1)下首圈充放电比容量可以达到270.1 mAh·g^-1,在5C倍率下容量仍能保持127.4 mAh·g^-1,优于未改性材料的90.7 mAh·g^-1,表现出优异的倍率性能。G3-LRMO在1C倍率下循环200圈后仍有190.7 mAh·g^-1的容量,容量保持率由未改性前的72.9%提升至85.6%,证明Ga₂O₃包覆改性能有效提升富锂锰基材料的循环稳定性。并且,G3-LRMO在1C倍率下循环100圈后,电荷转移阻抗(R_ct)为107.7 Ω,远低于未改性材料的251.5 Ω,表明Ga₂O₃包覆层能提高材料的电子传输速率。     

Cr2(WO4)3和Cr2(MoO4)3的负热膨胀特性研究

用液相反应-前驱物烧结法制备了Cr₂(WO₄)₃和Cr₂(MoO₄)₃粉体。298～1 073 K的原位粉末X射线衍射数据表明Cr₂(WO₄)₃和Cr₂(MoO₄)₃的晶胞体积随温度的升高而增大, 本征线热膨胀系数分别为(1.274±0.003)×10^-6 K^-1和(1.612±0.003)×10^-6 K^-1。用热膨胀仪研究了Cr₂(WO₄)₃和Cr₂(MoO₄)₃在静态空气中298～1 073 K范围内热膨胀行为，即开始表现为正热膨胀，随后在相转变点达到最大值，最后表现为负热膨胀，其负热膨胀系数分别为(-7.033±0.014)×10^-6 K^-1和(-9.282±0.019)×10^-6 K^-1。     

Cr2O3-modified ZnO thick film resistors as LPG sensors

Thick films of pure ZnO were obtained by screen-printing technique. Surface functionalized ZnO thick films by Cr₂O₃ were obtained by dipping pure ZnO thick films into 0.01 M aqueous solution of chromium trioxide (CrO₃). The dipped films were fired at 500 °C for 30 min. Upon firing, the CrO₃ would reduce to Cr₂O₃. Cr₂O₃-activated (0.47 mass%) ZnO thick films resulted in LPG sensor. Upon exposure to 100 ppm LPG, the barrier height between Cr₂O₃ and ZnO grains decreases markedly, leading to a drastic decrease in resistance. The sensor was found to sense LPG at 350 °C and no cross sensitivity was observed to other hazardous, polluting and inflammable gases. The quick response (∼18 s) and fast recovery (∼42 s) are the main features of this sensor. The effects of microstructures and dopant concentrations on the gas sensing performance of the sensor were studied and discussed.     

B2O3-Bi2O3-ZnO-Al2O3玻璃助烧剂对BaTiO3陶瓷烧结条件、晶体结构和介电性能的影响

通过调节B₂O₃‐Bi₂O₃‐ZnO‐Al₂O₃(BBZA)玻璃的添加量研究其对钛酸钡(BaTiO₃)陶瓷烧结条件、晶体结构和介电性能的影响。结果表明：添加适量的BBZA玻璃能够有效地将BaTiO₃陶瓷烧结温度由1350℃降至950℃,并使其致密化。同时,添加BBZA玻璃后,BaTiO₃的晶体结构随着烧结温度的升高而发生转变(立方相→四方相)。另外,BBZA玻璃的引入使BaTiO₃陶瓷的居里峰得到了有效的抑制和拓宽。陶瓷微观形貌显示,玻璃相均匀分布在BaTiO₃晶粒表面。优化的BaTiO₃陶瓷制备条件如下：BBZA添加量(质量分数)为2.0%,烧结温度为950℃。在该条件下制备的BaTiO₃陶瓷介电常数达到1364,介电损耗低至1.2%。     

B2O3-Bi2O3-ZnO-Al2O3玻璃助烧剂对BaTiO3陶瓷烧结条件、晶体结构和介电性能的影响

通过调节B₂O₃-Bi₂O₃-ZnO-Al₂O₃(BBZA)玻璃的添加量研究其对钛酸钡(BaTiO₃)陶瓷烧结条件、晶体结构和介电性能的影响。结果表明：添加适量的BBZA玻璃能够有效地将BaTiO₃陶瓷烧结温度由1 350℃降至950℃,并使其致密化。同时,添加BBZA玻璃后,BaTiO₃的晶体结构随着烧结温度的升高而发生转变(立方相→四方相)。另外,BBZA玻璃的引入使BaTiO₃陶瓷的居里峰得到了有效的抑制和拓宽。陶瓷微观形貌显示,玻璃相均匀分布在BaTiO₃晶粒表面。优化的BaTiO₃陶瓷制备条件如下：BBZA添加量(质量分数)为2.0%,烧结温度为950℃。在该条件下制备的BaTiO₃陶瓷介电常数达到1 364,介电损耗低至1.2%。     

BaO-Al2O3-B2O3系密封玻璃的结构与性质

The BaO-Al₂O₃-B₂O₃ glasses manufactured for solid oxide fuel cell(SOFC) sealing were studied. The effect of different n_BaO/n_B2O3 on crystal, thermal properties, density and infrared spectra of this system has been discussed. The results show that the trends of crystallization, glass transformation temperature, dilatometric softening temperature and density increase with n_BaO/n_B2O3 values. But a typical property deviation occurs when n_BaO/n_B2O3 is 0.875, and its coefficient of thermal expansion has the maximum at this point. The changes of properties can attribute to the conversion of boron from tetrahedral coordination to trigonal, breakage of the local glass network and interaction between the network modifiers. These can be proved by infrared spectra of glasses. Thermal properties of some studied samples are suitable for the sealing of SOFC using Sm doped ceria electrolyte and operating at 400～600 ℃.     

Fe2O3/Al2O3二元气凝胶合成高质量单壁纳米碳管

通过溶胶和超临界干燥方法制得了Fe₂O₃/Al₂O₃二元气凝胶，其比表面积和孔隙体积分别为246 m²·g^-1和1.89 cm³·g^-1，并具有较宽的孔径分布。以Fe₂O₃/Al₂O₃二元气凝胶作催化剂，通过甲烷催化裂解成功地合成了高质量的单壁纳米碳管。利用FESEM、TEM和HRTEM、Raman光谱等分析手段研究了反应温度对单壁纳米碳管生长的影响。结果表明在900 ℃时合成单壁纳米碳管的质量较高，并且合成的炭产物为毡状，该炭产物主要为高质量的单壁纳米碳管。     

La2O3对Ni/γ-Al2O3甲烷化催化剂的助催化作用

我国将稀土作为助剂引入镍基甲烷化催化剂,大大提高了催化剂的活性和热稳定性,并已投入工业应用［1－3］．稀土对不同镍催化剂反应性能及其作用机理的研究已有一些报导［3－7］．谢有畅等观察到镍负载在经单层La2O3改性的γ－Al2O3表面,其晶粒要比没有La2O3时小得多．Rotgerink等认为添加La后反应速率的增加不只是由于几何效应,而是La对甲烷化本身有促进作用,单位镍表面的活性是随La含量不同而改变的,活性增加的同时表观活化能也增加［5］．作为助剂的La2O3在氢还原和反应过程中的变化及其作用的研究和讨论较少,目前一般认为添…     

The Al2O3-Fe2O3 Mixed Oxidic System, I. Preparation and Characterization

A series of Al₂O₃-Fe₂O₃ mixed oxidic solids with composition ranging from 0 to 100% of Fe₂O₃ were prepared and examined for structural characteristics. XRD diagrams showed the presence of α-Al₂O₃ and hematite phases. The analysis of M?ssbauer spectra revealed the existence of two iron containing phases. The specific surface area of the mixture decreases by the addition of iron and depends on the crystal phases of the mixture. This revised version was published online in June 2006 with corrections to the Cover Date.     

The Ternary System Li2O-Al2O3-B2O3: Compounds and Phase Relations

The ternary system Li₂O-Al₂O₃-B₂O₃ is reinvestigated with solid-state reaction and X-ray powder diffraction technique to clarify some long-standing uncertainties. The phase relations are constructed based on the phase identifications of 51 ternary samples. Six ternary compounds, Li₂AlB₅O₁₀, LiAlB₂O₅, Li₃AlB₂O₆, Li₂AlBO₄, LiAl₇B₄O₁₇ and a compound with a composition close to 0.66Li₂O·0.06Al₂O₃·0.28B₂O₃, are observed or confirmed in this system, and the thermal stability of these ternary compounds is also discussed on the basis of DTA experimental results.