Ba1-xSrxMyTi1-yO3(M=Zr, Sn)纳米材料的软化学合成、结构与介电特性

用软化学方法,在１００℃以下合成了一系列Ｂａ_(１－ｘ)Ｓｒ_ｘＭ_ｙＴｉ_(１－ｙ)Ｏ_３固溶体纳米粉末（Ｍ＝Ｚｒ,Ｓｎ,０ ≤ｘ≤０．４,０≤ｙ≤０．３）,经ＸＲＤ物相分析和ｄ－间距－组成图证明,产品为立方晶系的完全互溶取代固溶体,结果符合Ｖｅｇａｒｄ定律．ＴＥＭ形貌观察,粒子为均匀球形,平均粒径７０ｎｍ．通过制陶实验,分别测定了该系列固溶体的室温介电常数以及介电常数随温度的变化．结果发现,用软化学方法在ＢａＴｉＯ_３中掺入适量锶和锆或锡,由于掺杂离子均匀进入母体晶格,引起Ｔｃ降低,介电性能改善显著．当ｘ＝０．２,ｙ＝０．１时,室温介电常数达 １１ ０００,比 ＢａＴｉＯ_３纯相提高 ８倍,而介电损失却下降 ３倍．     

Ba1-xSrxTi1-yMyO3固溶体的湿化学法合成与介电特性

A series of Ba_1-xSr_xTi_1-yM_yO₃ (M=Zr,Sn, 0≤ x≤ 0.5,0≤ y≤ 0.3) solid solutions were synthesized by chemical method at below 100℃ . XRD and cell parameters component figures of the series of the solid solutions powder demonstrated that the compounds are mutually miscible in the solid solutions. The particls size is about 70nm with spherical shape and uniform distribution. The result of preparing ceramics showed that after adulterating with Sr²⁺ and Zr⁴⁺ or Sn⁴⁺ in pure BaTiO₃ phase, the dielectric constant increased eight times while the dielectric loss decreased three times at room temperature.     

纳米钛酸钡基介电材料的水热合成、结构与性能

采用低温-低压水热法, 在170℃, 0.8 MPa以下合成了一系列Ba_1-xSr_xTi_1-yZr_yO₃ (0≤x≤0.5, 0≤y≤0.3)和Ba_1-xZn_xTi_1-ySn_yO₃(0≤x≤0.3, 0≤y≤0.3)固溶体纳米粉末. 经XRD物相分析和d-间距-组成图证明, 产物为立方钙钛矿结构的完全互溶取代固溶体, 结果符合Vegard 定律. TEM形貌观察, 粒子为均匀球形, 平均粒径70 nm. 通过制陶实验, 分别测定了两个系列固溶体纳米粉末的室温介电常数、介电损失以及介电常数随温度的变化, 结果发现, 用软化学方法在BaTiO₃中掺入适量锶、锌和锆、锡, 由于掺杂离子均匀进入母体晶格, 引起T_C降低, 室温介电常数达18000, 比BaTiO₃纯相提高12倍, 而介电损失却降低至1/6.     

Ba1-1.5yLayZrxTi1-xO3固溶体的合成、结构与介电特性

用软化学合成方法在100℃以下制备了一系列Ba_1-1.5yLa_yZr_xTi_1-xO₃(0<x<0.3, 0≤y≤0.08)固溶体纳米粉末。XRD物相分析及晶间距-组成图表明，产品为完全互溶取代固溶体。用TEM观察可知其粒子为均匀球形，平均粒径为60纳米。通过制陶实验，对该系列固溶体的介电特性分别进行了测试。结果表明：采用化学掺杂方法在BaTiO₃中掺入适量锆、镧后，样品的室温介电常数可提高到30，000以上，并呈现出规律性。     

BaZrxTi1-xO3·yLa2O3固溶体的合成、结构与性能

在100℃以下用软化学合成方法制备了一系列BaZrxTi1-xO3·yLa2O3O(0≤x≤0.3,0≤y≤0.04)固溶体纳米粉末.XRD物相分析及d-间隔-组成图证明,产品为完全互溶取代固溶体.从TEM谱图观察,粒子为均匀球形,平均粒径60nm.通过制陶实验对该系列固溶体的介电特性进行了测试,结果表明,采用化学掺杂方法在BaTiO3中掺入适量锆和镧后,样品的室温介电常数可提高20倍.     

BaZrxTi1-xO3·yLa2O3固溶体的合成、结构与性能

以１００℃以下用软化学合成方法制备了系列ＢａＺｒｘＴｉ１－ｘＯ３．ｙＬａ２Ｏ３固溶体纳米粉末，ＸＲＤ物相分析有ｄ－间隔－组成图证明，产品为完全互溶取代固溶体。从ＴＥＭ谱图观察，粒子为均匀球形，平均粒径６０ｎｍ。通过制陶实验对系列固溶体的介电特性进行了测试，结果表明，采用化学掺杂方法在ＢａＴｉＯ３中掺入适量锆和镧后，样品的室温介电常数可提高２０倍。     

类钙钛矿新铌酸盐Ba5NdTi2Nb3O18的合成、结构与介电特性

为满足现代通信技术的小型化、集成化与高可靠性的迫切要求,探索具有高介电常数、低介电损耗与低温度系数的微波介电材料引起了材料科学、化学、物理、电子等领域科学工作者的广泛关注,并已开发出复合钙钛矿结构Ba(Zn_(1/3)Ta_(2/3))O_3、钨青铜结     

铌酸盐Ba3NaBiNb10O30的结构与介电特性

一些铁电铌酸盐具有优良的电光性能和非线性光学性能,因此该类化合物的人工合成,结果与性能的研究受到了人们的重视,其中钨青铜结构的系列晶体（例如SBN,KNSBN,SCNN）在材料制备和器件设计方面都取得了很大进展,它们在实时全息存储,集成光学与光信号处理等领域具有广泛的应用前景[1-4],Ba2NaNb5O145(BNN)是目前认为最好的一种倍频晶体,Geusic[5,6]等人报导了在BNN晶体能实现最优位相匹配,可将1．06um红外光以100％的效率转换为0．53um绿光,我们在BaO-Na2O-Nb2O5体系中通过掺杂Bi3 合成了铌酸盐Ba3NaBiNb10O30,并采用粉晶X射线衍射（XRD）对其结构进行了分析,测试了其烧结体的介电特性。     

室温固态反应制备纳米Ba1－xSrxTiO3固溶体及其结构与介电性能研究

采用室温固态反应合成了一系列Ba_1－xSr_xTiO₃固溶体纳米粉末(0≤x≤1.0). 经XRD物相分析和d-间距-组成图证明, 产品为立方晶系的完全互溶取代固溶体. TEM形貌观察, 粒子基本为球形, 平均粒径40 nm. 该方法具有产率高, 无需溶剂, 对环境无污染等优点. 通过制陶实验, 分别测定了该系列固溶体的室温介电常数、介电损失以及介电常数随温度的变化. 结果发现, 采用室温固态反应在BaTiO₃中掺入适量锶, 由于掺杂离子均匀进入母体晶格, 引起居里点降低, 室温介电常数达11000以上, 介电损耗由BaTiO₃纯相的0.03 (3%)降为0.008 (0.8%). 纳米粉体的烧结温度为1180 ℃, 比传统微米级粉体的烧结温度降低100～150 ℃.     

Ba~1~-~xCa~xSn~yTi~1~-~yO~3纳米材料的、合成结构与性能

采用常压水相法,在100℃以下制备了一系列Ba~1~-~xCa~xSn~yTi~1~-~yO~3固溶体纳米粉末(0≤x≤0.5,0≤y≤0.3),经XRD物相分析和d-间距-组成图证明,产品为立方晶系的完全互溶取代固溶体,结果符合Vegard定律。TEM形貌观察,粒子为均匀球形,平均粒径70nm。通过制陶实验,分别测定了该系列固溶体的室温介电常数以及介电常数随温度的变化,结果发现,用软化学方法在BaTiO~3中掺入适量钙和锡,由于掺杂离子均匀进入母体晶格,引起T~c降低,室温介电常数达9800,经BaTiO~3纯相提高6倍,而介电损失却降低50%。     

Synthesis, structure and dielectric properties of Ba1-xSrx My Ti1-yO3 (M = Zr, Sn)

A series of Ba1-xSrxMyTi1-yO3 (M = Zr, Sn, 0≤x≤0.4, 0≤y≤0.3) solid solutions were synthesized with the soft chemical method below 100 ℃. XRD pattern and cell parameters-composition figures of the prepared powder demonstrate that they are completely miscible solid solutions based on BaTiO3. Furthermore, TEM shows that they have a shape of uniform, substantially spherical particles with an average particle size of 70 nm in diameter. The sintered ceramics of the powder doped with Sr2 and Zr4 or Sn4 have dielectric constant eight times higher and dielectric loss thirty per cent lower than those of pure BaTiO3 phase at room temperature.     

室温固态反应制备纳米Ba1－xSrxTiO3固溶体及其结构与介电性能研究

采用室温固态反应合成了一系列Ba_1－xSr_xTiO₃固溶体纳米粉末(0≤x≤1.0). 经XRD物相分析和d-间距-组成图证明, 产品为立方晶系的完全互溶取代固溶体. TEM形貌观察, 粒子基本为球形, 平均粒径40 nm. 该方法具有产率高, 无需溶剂, 对环境无污染等优点. 通过制陶实验, 分别测定了该系列固溶体的室温介电常数、介电损失以及介电常数随温度的变化. 结果发现, 采用室温固态反应在BaTiO₃中掺入适量锶, 由于掺杂离子均匀进入母体晶格, 引起居里点降低, 室温介电常数达11000以上, 介电损耗由BaTiO₃纯相的0.03 (3%)降为0.008 (0.8%). 纳米粉体的烧结温度为1180 ℃, 比传统微米级粉体的烧结温度降低100～150 ℃.     

Synthesis, Structure and Dielectric Property of Ba_(1- x)Sr_xZr_yTi_(1- y)O_3

ＩｎｔｒｏｄｕｃｔｉｏｎＢａＴｉＯ３ｉｓａｓｔｒｏｎｇｄｉｅｌｅｃｔｒｉｃｍａｔｅｒｉａｌ，ｗｈｉｃｈｉｓｗｉｄｅｌｙｕｓｅｄｉｎｔｈｅｐｒｏｄｕｃｔｉｏｎｏｆｅｌｅｃｔｒｉｃｃｏｍｐｏｎｅｎｔｓｓｕｃｈａｓｃｅｒａｍｉｃｃａｐａｃｉｔｏｒ，ＰＴＣ，ｍｅｄｉｕｍａｍｐｌｉｆｅｒ［１］．Ｉｔｈａｓｔｈｅｈｉｇｈｅｓｔｄｉｅｌｅｃｔｒｉｃｃｏｎｓｔａｎｔａｔ１２０℃（ｃａ．１０４），ｗｈｉｌｅｉｔｓｄｉｅｌｅｃｔｒｉｃｃｏｎｓｔａｎｔａｔｒｏｏｍｔｅｍｐｅｒａｔｕｒｅｉｓｏｎｌｙ１／６ｏｆｔｈｅＣｕ…     

Ba~1~-~1~.~5~yLa~ySn~xTi~1~-~xO~3固溶体的合成、结构与性能

用软化学合成方法,在100^oC以下制备了一系列Ba~1~-~1~.~5~yLa~ySn~xTi~1~-~xO~3固溶体纳米粉末,XRD物相分析和d间距-组成图证明,产品为完全互溶取代固溶体.TEM观察,粒子为均匀球形,平均粒径70nm.通过制陶实验,分别测定了该系列固溶体的室温介电常数,结果发现,用化学方法在BaTiO~3中掺入适量锡和镧,引起T~c降低,当x=0.2,y=0.08时,室温介电数高达28000,比BaTiO~3纯相提高20倍.     

Hydrotherrnal synthesis, structure and property of nano-BaTiO3-based dielectric materials

A series of Ba1-xSrxTi1-yZryO3 (0≤x≤0.5, 0≤y≤0.4) and Ba1-xZnxTi1-ySnyO3 (0≤x≤0.3, 0≤y≤0.3) solid solutions were synthesized by Iow-temperature/Iow-pressure hydrothermal method below 170℃, 0.8 MPa. XRD pattern and cell parameters-composition figures of these prepared powders demonstrated that they are completely miscible solid solutions based on BaTiO3. Furthermore, TEM showed that they have a shape of uniform, substantially spherical particles with an average particle size of 70 nm in diameter. The sintered ceramics of those powders doped by Sr2+ and Zr4+ or Zn2+ and Sn4+ have dielectric constant twelve times higher than and dielectric loss 1/6 those of pure BaTiO3 phase at room temperature.     

Hydrothermal synthesis, structure and property of nano-BaTiO_3based dielectric materials

A series of Ba1-xSrxTi1-yZryO3 (0≤x≤0.5, 0≤y≤0.4) and Ba1-xZnxTi1-ySnyO3 (0≤x≤0.3, 0≤y≤0.3) solid solutions were synthesized by low-temperature/low-pressure hydrothermal method below 170℃, 0.8 MPa. XRD pattern and cell parameters-composition figures of these prepared powders demonstrated that they are completely miscible solid solutions based on BaTiO3. Furthermore, TEM showed that they have a shape of uniform, substantially spherical particles with an average particle size of 70 nm in diameter. The sintered ceramics of those powders doped by Sr2+ and Zr4+ or Zn2+ and Sn4+ have dielectric constant twelve times higher than and dielectric loss 1/6 those of pure BaTiO3 phase at room temperature.     

微波反应合成纳米Ba1-xZnxTi1-ySnyO3介电材料及其结构、性能研究

采用微波反应技术,合成了一系列Ba1-xZnxTi1-ySnyO3固溶体纳米粉末（0≤ x≤0.3,0≤y≤0.5),XRD物相分析和d间距一组成图证明,产品为立方晶系的完全 互溶取代固溶体,结果符合Vegard定律。TEM形貌观察,粒子为均匀球形,平均粒 径40nm。通过制陶实验,分别测定了该系列固溶体的室温介电常数、介电损失以及 介电常数随温度的变化,结果发现,采用化学方法在BaTiO3中掺入适量锌和锡,由 于掺杂离子均匀进入母体晶格,引起tc降低,室温介电常数达12000以上,介电损 耗仅为0.007。纳米粉体的烧结温度为1150℃,比传统微米级粉体的烧结温度降低 200－250℃。