Vinyl Polymerization. 439. Vinyl Polymerization Initiated by Poly(Ethylene Glycol] Diglycolic Acid or its Sodium Salt

Abstract

The polymerization of some kinds of vinyl monomer was found to occur in aqueous solutions of poly(ethylene glycol) diglycolic acid (PEG Acid) or sodium poly(ethylene glycol) diglycolate (PEG Acid Na) through radical mechanisms without any further initiator, as a so-called “uncatalyzed polymerization.” Although the initiating radical species for PEG Acid was determined to be the same as that for PEG Acid Na by means of the spin-trapping technique, the initiating ability of PEG Acid was higher than that of PEG Acid Na. These results are assumed to be attributable to the difference in the initiation mechanisms of the two systems and in the incorporating abilities of monomer into the hydrophobic areas formed by PEG Acid and PEG Acid Na.     

Vinyl Polymerization. 287. Polymerization of Methyl Methacrylate Initiated by the Polyacrylonitrile-Water-Cupric Ion System

Abstract

Methyl methacrylate was found to be polymerized by the system polyacrylonitrile-water-cupric ion without any added initiator. Addition of carbon tetrachloride to this system greatly increased the polymerization rate. Acrylonitrile and styrene did not polymerize in this system. The kinetic behavior of polymerization was the same as the system consisting'of cellulose or nylon instead of polyacrylonitrile. When the flaky polyacrylo-nitrile was swelled or dissolved by the solvent DMF, the conversion and the degree of polymerization of the poly-methyl methacrylate formed decreased markedly. Commercial acrylic fiber also initiated polymerization but the activity was lower than with flaky polyacrylonitrile, even after steam treatment, because of the poor permeability of monomer into the fiber.     

Mechanochemical solid-state polymerization (X): the influence of copolymer structure in copolymeric prodrugs on the nature of drug release

From the standpoint of the mechanism of mechanochemical polymerization, two kinds of copolymeric prodrug, whose monomer sequence distribution (MSD) is different from each other, can be prepared by this polymerization under appropriate operational conditions: one is a random copolymer abundant in the longer block consisting of the same repeating units (multi-block copolymer), and the other is a block copolymer. To confirm the difference of MSD, the 13C-NMR spectra of poly(acrylamide-co-sodium acrylate) prepared by mechanochemical polymerization were measured and compared with the spectrum of that synthesized by a conventional radical-initiated solution polymerization, which produces the random copolymer normally. The results show that MSD in copolymers depends on the polymerization method (operational condition). We prepared three kinds of copolymeric prodrug consisting of acrylamide and vinyl monomer of 5-fluorouracil, whose MSD is different from one another. These copolymeric prodrugs had almost the same number average molecular weight, particle diameter and composition, and differed only in MSD. We compared the rate of drug release of these copolymeric prodrugs. The rate of drug release was the highest with the random copolymer, followed by the mechanochemically produced multi-block copolymer and the block copolymer. This result suggests that the rate of drug release depends on MSD of copolymeric prodrugs. These results are useful as they give a fundamental insight into the synthesis of copolymeric prodrugs having the desired rate of drug release.     

Atom transfer radical polymerization of acrylates in an ionic liquid: Synthesis of block copolymers

Atom transfer radical polymerization (ATRP) of acrylates in ionic liquid, 1‐butyl‐3‐methylimidazolium hexaflurophospate, with the CuBr/CuBr₂/amine catalytic system was investigated. Sequential polymerization was performed by synthesizing AB block copolymers. Polymerization of butyl acrylate (monomer that is only partly soluble in an ionic liquid forming a two‐phase system) proceeded to practically quantitative conversion. If the second monomer (methyl acrylate) is added at this stage, polymerization proceeds, and block copolymer formed is essentially free of homopolymer according to size exclusion chromatographic analysis. The number‐average molecular weight of the copolymer is slightly higher than calculated, but the molecular weight distribution is low (M_w/M_n = 1.12). If, however, methyl acrylate (monomer that is soluble in an ionic liquid) is polymerized at the first stage, then butyl acrylate in the second‐stage situation is different. Block copolymer free of homopolymer of the first block (with M_w/M_n = 1.13) may be obtained only if the conversion of methyl acrylate at the stage when second monomer is added is not higher than 70%. Matrix‐assisted laser desorption/ionization time‐of‐flight analysis confirmed that irreversible deactivation of growing macromolecules is significant for methyl acrylate polymerization at a monomer conversion above 70%, whereas it is still not significant for butyl acrylate even at practically quantitative conversion. These results show that ATRP of butyl acrylate in ionic liquid followed by addition of a second acrylate monomer allows the clean synthesis of block copolymers by one‐pot sequential polymerization even if the first stage is carried out to complete conversion of butyl acrylate. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 2799–2809, 2002     

Quantifying and Controlling the Composition and ‘Randomness’ Distributions of Random Copolymers

The effect of disparity in the reactivity ratios of monomer pairs on the composition distribution and microstructure of the resultant copolymer formed through free‐radical polymerization is quantified computationally. This correlation has been determined for the monomer pairs of styrene/methyl methacrylate and styrene/2‐vinyl pyridine for a variety of monomer feed ratios. These monomer pairs were chosen as they represent systems that have been utilized to experimentally examine the importance of copolymer architecture on its ability to compatibilize an immiscible polymer blend. Moreover, their respective random copolymers show conflicting results for this examination. The results of this work show that the difference in the reactivity ratios of styrene and 2‐vinyl pyridine copolymer (r₁ = 0.5, r₂ = 1.3) significantly broadens the composition and randomness distribution of the resultant copolymer. This breadth is not easily avoided as it evolves even in the early stages of the copolymerization. Conversely, for the styrene/methyl methacrylate pair, the reactivity ratios are similar (r₁ = 0.46, r₂ = 0.52) and this results in a copolymer with a narrow composition distribution and sequence distribution dispersion. Stopping the polymerization at early conversion further narrows both distributions. The presented results, therefore, provide fundamental information that must be considered when planning an experimental procedure to evaluate the relative importance of sequence distribution and composition distribution of a random on its application.     

Metallo esters. VII. Stabilizing effect of sodium tert-butoxide on the growth center in the anionic polymerization of methacrylic esters

The growth center in the anionic polymerization of methacrylic esters is stabilized with alkaline alkoxides, sodium tert-butoxide in particular. The lifetime of the growth center was investigated in the polymerization of methyl methacrylate by evaluating yield and molecular weight distribution of the polymer formed when the monomer was added in two doses. The average lifetime of the original growth center stabilized by sodium tert-butoxide at 20°C under the given conditions was longer than several minutes. The stabilization of the growth center was also used in the stepwise copolymerization of n-butyl methacrylate and methyl methacrylate. The copolymer thus obtained in high yield was characterized as a block copolymer on the basis of its solubility, nuclear magnetic resonance (NMR) spectra, and measurements of the complex shear modulus.     

乙烯基二联苯单体的螺旋选择性自由基聚合

为了深入理解乙烯基二联苯单体自由基聚合过程中的手性传递,进行了手性单体(+)-2-[(S)-异丁氧羰基-5-(4′-己氧基苯基)苯乙烯、非手性单体2-丁氧羰基-5-(4′-己氧基苯基)苯乙烯的均聚反应及它们二者的共聚反应,探讨了聚合温度和溶剂性质对手性单体均聚物旋光活性、手性单体含量对共聚物旋光活性以及聚合反应溶剂的超分子手性对共聚物旋光活性的影响.研究发现,降低聚合温度、采用液晶性反应介质有利于得到旋光度大的聚合物;少量手性单体的引入即可诱导共聚物形成某一方向占优的螺旋构象,比旋光度随手性单体的含量增加呈线性增长;在胆甾相液晶中制备的非手性单体聚合物不具有光学活性.这些结果表明,该类乙烯基二联苯聚合物具有动态螺旋构象,其光学活性主要依赖于主链的立构规整度和侧基不对称原子的手性.     

Atom Transfer Radical Polymerization of Styrene with 5‐Chloromethyl‐2‐hydroxy‐benzaldehyde as Initiator

Abstract

Atom transfer radical polymerization (ATRP) of styrene (St) proceeded using 5‐chloromethyl‐2‐hydroxy‐benzaldehyde as initiator, CuCl as catalyst, and N,N,N′,N′,N′‐pentamethyldiethyltriamine (PMDETA) as ligand. The results show that the polymerization is a first order reaction with respect to monomer concentration. The polymerization displayed living character as evidenced by a liner increase of monomer weight with conversation and a relatively narrow distribution (M _n/M _w ranges from 1.25 to 1.50). The end structure of PSt was analyzed by ¹H‐NMR, and PSt initiated MMA to form block copolymer (PSt‐b‐PMMA), which also proved that the polymerization could be controlled. The effects of reaction temperature and monomer to initiator mole ratio on the polymerization displayed living character were discussed.     

Synthesis of Acid Dyeable Acrylonitrile Copolymer

In this paper, a unique and updated technique was applied to obtain an acid dyeable copolymer of acrylonitrile by solution polymerization of acrylonitrile, and a kind of alkaline monomer F (N,N‐dialkylaminoethylacrylate). Azodiisobutyronitrile (AIBN) was used as initiator to prepare the copolymer in sodium sulfocyanate aqueous solution. The effect of initiator concentration on the polymer's molecular weight and conversion during polymerization was studied. The relation between concentration of the alkaline monomer F and the polymer conversion, as well as the relation between concentration of the alkaline monomer F and the % dye‐uptake of the copolymer are discussed. The influence of pH was also researched. The structure of the copolymer was characterized by IR and NMR. The copolymer has excellent acid dyeable characteristics.     

Living Cationic Polymerization of α-Methylstyrene. 2. Synthesis of Block and Random Copolymers with 2-Chloroethyl Vinyl Ether and End-Functionauzed Polymers†

Abstract

Both AB and BA block copolymers of α-methylstyrene (αMeSt) and 2-chloroethyl vinyl ether (CEVE) were synthesized by the sequential living cationic polymerization initiated with the HCl-CEVE adduct (1a)/SnBr₄ system in CH₂Cl₂ at -78°C. αMeSt-CEVE (AB) block copolymers with narrow molecular weight distributions ([Mbar]_w/[Mbar]_n ～ 1.15) were obtained when αMeSt was polymerized first, followed by addition of CEVE to the resulting αMeSt living polymer solution. The reverse order of monomer addition, from CEVE to αMeSt, also led to a BA-type block copolymer. In the polymerization of a mixture of the two monomers, almost random copolymers were obtained. Living polymerizations of αMeSt were also induced with functional initiating systems, HCl-functionalized vinyl ether adducts (1b-1d)/SnBr₄, to give end-function-alized poly(αMeSt)s with a methacrylate, an acetate, or a phthalimide terminal.     

Vinyl Polymerization. 374. Radical Polymerization of Vinyl Monomer Initiated with Sodium Polystyrenesulfonate

The polymerization of vinyl monomer initiated by an aqueous solution of sodium polystyrenesulfonate (PSS-Na) was carried out at 85°C. Methyl methacrylate (MMA) and styrene were polymerized, while acrylonitrile was not. The rate of polymerization of MMA decreased with the increase of the degree of polymerization of PSS-Na. However, the polymerization was not initiated by sodium ethyl benzenesulfonate which was a unit molecule of PSS-Na. The polymerization proved to be a radical reaction. The polymerization was considered to commence with the formation of hydrophobic areas with PSS-Na in the aqueous phase. MMA is incorporated into these areas, and there the polymerization is initiated and proceeds. The hydrophobic areas were assumed to be similar to the micelles formed by anionic detergents such as sodium alkylbenzene sulfonate. An initiation mechanism is proposed.     

Vinyl Polymerization. 274. Polymerization of Acrylonitrile Initiated by the System Tetramethyl Tetrazene and Co(II) Chloride

Abstract

The binary system of tetramethyl tetrazene (TMT) and Co(II) chloride was used as initiator of acrylonitrile (AN) in dimethylformamide. The initial rate of polymerization (Rp) was found to be expressed by Rp = k[TMT]^0.62[Co(II) chloride]^0.57 [AN]^2.00

The polymerization was confirmed to proceed via a radical mechanism. The over-all activation energy for the polymerization was estimated as 15.1 kcal/mole. On the basis of these results and the product analysis of the reaction between the catalyst components in the absence of monomer, the initiation mechanism of the polymerization is discussed.     

Synthesis of star‐shaped copolymers with methyl methacrylate and n‐butyl methacrylate by metal‐catalyzed living radical polymerization: Block and random copolymer arms and microgel cores

Various star‐shaped copolymers of methyl methacrylate (MMA) and n‐butyl methacrylate (nBMA) were synthesized in one pot with RuCl₂(PPh₃)₃‐catalyzed living radical polymerization and subsequent polymer linking reactions with divinyl compounds. Sequential living radical polymerization of nBMA and MMA in that order and vice versa, followed by linking reactions of the living block copolymers with appropriate divinyl compounds, afforded star block copolymers consisting of AB‐ or BA‐type block copolymer arms with controlled lengths and comonomer compositions in high yields (≥90%). The lengths and compositions of each unit varied with the amount of each monomer feed. Star copolymers with random copolymer arms were prepared by the living radical random copolymerization of MMA and nBMA followed by linking reactions. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 633–641, 2002; DOI 10.1002/pola.10145     

Latices of poly(fluoroalkyl mathacrylate)‐b‐poly(butyl methacrylate) copolymers prepared via reversible addition–fragmentation chain transfer polymerization

Poly(fluoroalkyl mathacrylate)‐block‐poly(butyl methacrylate) diblock copolymer latices were synthesized by a two‐step process. In the first step, a homopolymer end‐capped with a dithiobenzoyl group [poly(fluoroalkyl mathacrylate) (PFAMA) or poly(butyl methacrylate) (PBMA)] was prepared in bulk via reversible addition–fragmentation chain transfer (RAFT) polymerization with 2‐cyanoprop‐2‐yl dithiobenzoate as a RAFT agent. In the second step, the homopolymer chain‐transfer agent (macro‐CTA) was dissolved in the second monomer, mixed with a water phase containing a surfactant, and then ultrasonicated to form a miniemulsion. Subsequently, the RAFT‐mediated miniemulsion polymerization of the second monomer (butyl methacrylate or fluoroalkyl mathacrylate) was carried out in the presence of the first block macro‐CTA. The influence of the polymerization sequence of the two kinds of monomers on the colloidal stability and molecular weight distribution was investigated. Gel permeation chromatography analyses and particle size results indicated that using the PFAMA macro‐CTA as the first block was better than using the PBMA RAFT agent with respect to the colloidal stability and the narrow molecular weight distribution of the F‐copolymer latices. The F‐copolymers were characterized with ¹H NMR, ¹⁹F NMR, and Fourier transform infrared spectroscopy. Comparing the contact angle of a water droplet on a thin film formed by the fluorinated copolymer with that of PBMA, we found that for the diblock copolymers containing a fluorinated block, the surface energy decreased greatly, and the hydrophobicity increased. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 471–484, 2007     

Alternating copolymer of butadiene and ethylene. I. Copolymerization by TiCl4–R3Al catalyst systems

Alternating copolymerization of butadiene and ethylene was investigated by the TiCl₄?R₃Al system as catalyst with the use of toluene solutions of monomers of various compositions or by introducing a 1:1 gaseous mixture of both monomers into the reaction system. It was found that the copolymer composition is much influenced by the monomer composition or by the flow rate of monomer. Copolymers containing sequences of alternating monomer arrangement are formed by the polymerization of a monomer mixture having a butadiene: ethylene ratio of 4:1. A suitable catalyst for the alternating copolymerization was found to consist of R₃Al?TiCl₄ at a ratio of 2. The addition of amine was found to modify the catalyst to favor the alternating copolymerization but was accompanied by a decrease in catalyst activity.     

Controlled radical polymerization of N‐vinylcaprolactam mediated by xanthate or dithiocarbamate

Controlled radical polymerization of N‐vinylcaprolactam (NVCL) via reversible addition‐fragmentation chain transfer (RAFT) polymerization or macromolecular design via the interchange of xanthate (MADIX) was described, employing 2‐diphenylthiocarbamoylsulfanyl‐2‐methyl‐propionic acid (CTA1), ((O‐ethylxanthyl)methyl)benzene (CTA2) and (1‐(O‐ethylxanthyl)ethyl)benzene (CTA3) as chain transfer agents (CTA). It was found that all the CTAs led to controlled radical polymerization of NVCL, with the molecular weight increased along with the conversion of monomer and a relatively narrow molecular weight distribution could be obtained, as determined with matrix‐assisted laser desorption and ionization time‐of‐flight (MALDI‐TOF) and gel permeation chromatography (GPC), the polydispersity indices, as determined by MALDI‐TOF, were typically on the order of 1.24, but the polymerization did not proceed in a strictly living manner. The chain transfer ability of these CTAs was in the following order: CTA1 ≈ CTA2 < CTA3. MALTI‐TOF measurement showed that the major population of polymer retained the chain‐end functional group, but minor population deactivated by radical coupling. In preparation of the block copolymer of NVCL and vinyl acetate (VAc) by sequential polymerization, the sequence of monomer addition was important. Using VAc as the first monomer could lead to a block copolymer presenting a unimodal GPC trace and a narrow PDI index, and if NVCL was used as the first monomer, the polymerization was less well controlled. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 3756–3765, 2008     

Vinyl polymerization. 416. Polymerization of vinyl monomer initiated by polyethyleneglycol

The polymerization of vinyl monomer initiated by polyethyleneglycol (PEG) in aqueous solution was carried out at 85°C with shaking. Acrylonitrile (AN), methyl methacrylate (MMA), and methacrylic acid were polymerized by PEG–300 (M?_n = 300), whereas styrene was not. The effects of the amounts of monomer and PEG, the molecular weight of PEG, and the hydrophobic group at the end of PEG molecule on the polymerization were studied. The selectivity of vinyl monomer and the effect of the hydrophobic group are discussed according to “the concept of hard and soft hydrophobic areas and monomers.” The kinetics of the polymerization was investigated. The overall activation energy in the polymerization of AN was estimated as 37.9 kJ mol^?1. The polymerization was effected by a radical mechanism.     

Sulfur-Containing Vinyl Monomers. XV. Kinetic Study of Radical Polymerization of Vinyl Mercaptobenzothiazole and Its Copolymerization

A kinetic study of radical polymerization of vinyl mercaptobenzothiazole (VMBT) with α,α′-azobisisobutyonitrile (AIBN) at 60°C was carried out. The rate of polymerization (R_p) was found to be expressed by the rate equation: R_p = k[AIBN]^0.5 [VMBT]^1.0, indicating that the polymerization of this monomer proceeds via an ordinary radical mechanism. The apparent activation energy for overall polymerization was calculated to be 20.9 kcal/mole. Moreover, this monomer was copolymerized with methyl methacrylate, acrylonitrile, vinyl acetate, phenyl vinyl sulfide, maleic anhydride, and fumaronitrile at 60°C. From the results obtained, the copolymerization parameters were determined and discussed.     

Brush macro‐RAFT agent mediated dispersion polymerization of styrene in the alcohol/water mixture

Dispersion RAFT polymerization of styrene in the alcohol/water mixture mediated with the brush macro‐RAFT agent of poly[poly(ethylene oxide) methyl ether vinylphenyl‐co‐styrene] trithiocarbonate [P(mPEGV‐co‐St)‐TTC] with similar molecular weight but different chemical composition is investigated. Well‐controlled RAFT polymerization including an initial slow homogeneous polymerization and a subsequent fast heterogeneous polymerization at almost complete monomer conversion is achieved. The molecular weight of the synthesized block copolymer increases linearly with the monomer conversion, and the polydispersity is relatively narrow (PDI < 1.3). The RAFT polymerization kinetics is dependent on the chemical composition in the brush macro‐RAFT agents, and those with high content of hydrophobic segment lead to fast RAFT polymerization. The growth of the block copolymer nano‐objects during the RAFT polymerization is explored, and various block copolymer nano‐objects such as nanospheres, worms, vesicles and large‐compound‐micelle‐like particles are prepared. The parameters such as the chemical composition in the brush macro‐RAFT agent, the chain length of the solvatophobic block, the concentration of the feeding monomer and the solvent character affecting the size and morphology of the block copolymer nano‐objects are investigated. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013, 51, 3177–3190     

Metal-Containing Initiator Systems. 30. Vinyl Polymerization Initiated with Bis(ethyl acetoacetato)copper(II) and Maleimide

Some electron-accepting compounds such as maleimide (MIm), maleic anhydride (MAn), and tetracyanoquinodimethane were found to show pronounced accelerating effects on vinyl polymerization initiated with metal chelates. The polymerization of methyl methacrylate (MMA) initiated with bis(ethyl acetoacetato)-copper(II) (Cu(eacac)₂) and MIm was studied kinetically in benzene. The overall activation energy of the polymerization was calculated to be 11.5 kcal/mol. This value was much lower than that (17.6 kcal/mol) for the polymerization of MMA with Cu(eacac)₂ alone. The polymerization rate (R_p) was expressed as R_p =k[MIm]^1/2 [Cu(eacac)₂]^1/2 [MMA] The first-order dependence of R_p on the monomer concentration indicated that the monomer had no participation in the initiation step, in contrast with polymerization in the absence of MIm (where a monomer concentration dependence of 1.4th order was observed). Electronic spectroscopic study revealed that a complex between MIm and Cu(eacac)₂ had been formed. The ligand radical, an acetylcarboethoxymethyl radical, was trapped by 2-methyl-2-nitrosopropane in the reactions of Cu(eacac)₂ with MIm and with MAn in benzene. From these results the mechanism of the initiation of polymerization is discussed.