Hydrolysis of 4‐acetoxystyrene polymers prepared by atom transfer radical polymerization

Hydrolysis of 4‐acetoxystyrene polymers prepared by atom transfer radical polymerization was carried out under various reaction conditions. It was found that hydrazinolysis of 4‐acetoxystyrene homopolymers, random and block copolymers with styrene in 1,4‐dioxane, afforded the corresponding narrow dispersed materials with phenolic groups which were substantially free from crosslinkages. Gel permeation chromatographic (GPC) analysis of these polymers revealed different extents of molecular weight distribution (MWD) broadening for the hydrolysis products for the different structures. On the other hand, by NaOH catalyzed deprotection, the 4‐acetoxystyrene polymers including triblock copolymer poly(4‐acetoxystyrene‐b‐isobutylene‐b‐4‐acetoxystyrene) suffered from some degrees of coupling or even gelation, except for poly(styrene‐b‐4‐acetoxystyrene‐b‐styrene) which also by this method could be conveniently converted to its phenolic product. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 627–633, 1999     

RAFT polymerization of activated 4‐vinylbenzoates

The reversible addition fragmentation chain transfer (RAFT) polymerization of five active ester monomers based on 4‐vinylbenzoic acid had been investigated. Pentafluorophenyl 4‐vinylbenzoate could be polymerized under RAFT conditions yielding polymers with very good control over molecular weight and narrow molecular weight distributions. Following the synthesis of diblock copolymers consisting of polystyrene, polypentafluorostyrene, poly(4‐octylstyrene), or poly(4‐acetoxystyrene) as an inert block and poly(pentafluorophenyl 4‐vinylbenzoate) as a reactive block was successfully performed. The diblock copolymer poly(pentafluoro styrene)‐block‐poly(pentafluorophenyl 4‐vinylbenzoate) had been analyzed by ¹⁹F NMR spectroscopy in solution, demonstrating the synthetic potential of pentafluorophenyl 4‐vinylbenzoate as an extremely valuable monomer for the synthesis of highly functionalized polymeric architectures. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 1696–1705, 2009     

Kinetic investigation of the RAFT polymerization of p‐acetoxystyrene

The kinetics of the RAFT polymerization of p‐acetoxystyrene using a trithiocarbonate chain transfer agent, S‐1‐dodecyl‐S′‐(α,α′‐dimethyl‐α″‐acetic acid)trithiocarbonate, DDMAT, was investigated. Parameters including temperature, percentage initiator, concentration, monomer‐to‐chain transfer agent ratio, and solvent were varied and their impact on the rate of polymerization and quality of the final polymer examined. Linear kinetic plots, linear increase of M_n with monomer conversion, and low final molecular weight dispersities were used as criteria for the selection of optimized polymerization conditions, which included a temperature of 70 or 80 °C with 10 mol % AIBN initiator in bulk for low conversions or in 1,4‐dioxane at a monomer‐to‐solvent volume ratio of 1:1 for higher conversions This study opens the way for the use of DDMAT as a chain transfer agent for RAFT polymerization to incorporate p‐acetoxystyrene together with other functional monomers into well‐defined copolymers, block copolymers, and nanostructures. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 2517–2524, 2010     

Synthesis of Poly(glycidyl methacrylate)‐block‐Poly(pentafluorostyrene) by RAFT: Precursor to Novel Amphiphilic Poly(glyceryl methacrylate)‐block‐Poly(pentafluorostyrene)

Poly(glycidyl methacrylate) (PGMA) was synthesized by the RAFT method in the presence of 2‐cyanoprop‐2‐yl dithiobenzoate (CPDB) chain transfer agent using different [GMA]/[CPDB] molar ratios. The living radical polymerization resulted in controlled molecular weights and narrow polydispersity indices (PDI) of ≈1.1. The polymerization of pentafluorostyrene (PFS) with PGMA as the macro‐RAFT agent yielded narrow PDIs of ≤1.2 at 60 °C and ≤1.5 at 80 °C. The epoxy groups of the PGMA block were hydrolyzed to obtain novel amphiphilic copolymer, poly(glyceryl methacrylate)‐block‐poly(pentafluorostyrene) [PGMA(OH)‐b‐PPFS]. The PGMA epoxy group hydrolysis was confirmed by ¹H NMR and FTIR spectroscopy. DSC investigation revealed that the PGMA‐b‐PPFS polymer was amorphous while the PGMA(OH)‐b‐PPFS displayed a high degree of crystallinity.

     

One‐step synthesis of poly(N‐vinylpyrrolidone)‐b‐poly(l‐lactide) block copolymers using a dual initiator for RAFT polymerization and ROP

Amphiphilic, biocompatible poly(N‐vinylpyrrolidone)‐b‐poly(l ‐lactide) (PVP‐b‐PLLA) block polymers were synthesized at 60 °C using a hydroxyl‐functionalized N,N‐diphenyldithiocarbamate reversible addition–fragmentation chain transfer (RAFT) agent, 2‐hydroxyethyl 2‐(N,N‐diphenylcarbamothioylthio)propanoate (HDPCP), as a dual initiator for RAFT polymerization and ring‐opening polymerization (ROP) in a one‐step procedure. 4‐Dimethylamino pyridine was used as the ROP catalyst for l ‐lactide. The two polymerization reactions proceeded in a controlled manner, but their polymerization rates were affected by the other polymerization process. This one‐step procedure is believed to be the most convenient method for synthesizing PVP‐b‐PLLA block copolymers. HDPCP can also be used for the one‐step synthesis of poly(N‐vinylcarbazole)‐b‐PLLA block copolymers. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 1607–1613     

Multiblock poly(4‐vinylpyridine) and its copolymer prepared with cyclic trithiocarbonate as a reversible addition–fragmentation transfer agent

The polymerization of 4‐vinylpyridine was conducted in the presence of a cyclic trithiocarbonate (4,7‐diphenyl‐[1,3]dithiepane‐2‐thione) as a reversible addition–fragmentation transfer (RAFT) polymerization agent, and a multiblock polymer with narrow‐polydispersity blocks was prepared. Two kinds of multiblock copolymers of styrene and 4‐vinylpyridine, that is, (ABA)_n multi‐triblock copolymers with polystyrene or poly(4‐vinylpyridine) as the outer blocks, were prepared with multiblock polystyrene or poly(4‐vinylpyridine) as a macro‐RAFT agent, respectively. GPC data for the original polymers and polymers cleaved by amine demonstrated the successful synthesis of amphiphilic multiblock copolymers of styrene and 4‐vinylpyridine via two‐step polymerization. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 2617–2623, 2007     

An efficient avenue to poly(styrene)‐block‐poly(ε‐caprolactone) polymers via switching from RAFT to hydroxyl functionality: Synthesis and characterization

The recently introduced procedure of quantitatively switching thiocarbonyl thio capped (RAFT) polymers into hydroxyl terminated species was employed to generate narrow polydispersity (PDI ≈ 1.2) sulfur‐free poly(styrene)‐block‐poly(ε‐caprolactone) polymers (26,000 ≤ M_n/g·mol^?1 < 45,000). The ring‐opening polymerization (ROP) of ε‐caprolactone (ε‐CL) was conducted under organocatalysis employing 1,5,7‐triazabicyclo[4.4.0]dec‐5‐ene (TBD). The obtained block copolymers were thoroughly analyzed via size exclusion chromatography (SEC), NMR, as well as liquid adsorption chromatography under critical conditions coupled to SEC (LACCC‐SEC) to evidence the block copolymer structure and the efficiency of the synthetic process. The current contribution demonstrates that the RAFT process can serve as a methodology for the generation of sulfur‐free block copolymers via an efficient end group switch. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2010     

Chain‐growth condensation polymerization of 4‐aminobenzoic acid esters bearing tri(ethylene glycol) side chain with lithium amide base

Chain‐growth condensation polymerization of p‐aminobenzoic acid esters 1 bearing a tri(ethylene glycol) monomethyl ether side chain on the nitrogen atom was investigated by using lithium 1,1,1,3,3,3‐hexamethyldisilazide (LiHMDS) as a base. The methyl ester monomer 1a afforded polymer with low molecular weight and a broad molecular weight distribution, whereas the polymerization of the phenyl ester monomer 1b at ?20 °C yielded polymer with controlled molecular weight (M_n = 2800–13,400) and low polydispersity (M_w/M_n = 1.10–1.15). Block copolymerization of 1b and 4‐(octylamino)benzoic acid methyl ester ( 2 ) was further investigated. We found that block copolymer of poly 1b and poly 2 with defined molecular weight and low polydispersity was obtained when the polymerization of 1b was initiated with equimolar LiHMDS at ?20 °C and continued at ?50 °C, followed by addition of 2 and equimolar LiHMDS at ?10 °C. Spherical aggregates were formed when a solution of poly 1b in THF was dropped on a glass plate and dried at room temperature, although the block copolymer of poly 1b and poly 2 did not afford similar aggregates under the same conditions. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 1357–1363, 2010     

Synthesis by ATRP of poly(ethylene‐co‐butylene)‐block‐polystyrene,poly(ethylene‐co‐butylene)‐block‐poly(4‐acetoxystyrene) and its hydrolysis product poly(ethylene‐co‐butylene)‐block‐poly(hydroxystyrene)

Diblock copolymers of poly(ethylene‐co‐butylene) and polystyrene or poly(4‐acetoxystyrene) are synthesized by atom transfer radical polymerization (ATRP) using a 2‐bromopropionic ester macroinitiator prepared from commercial monohydroxyl functional narrow dispersity hydrogenated polybutadiene (Kraton Liquid Polymer, L‐1203). ATRP carried out in bulk and in xylene solution with cuprous bromide and two different complexing agents 2,2′‐bipyridine (bipy) and 1,1,4,7,10,10‐hexamethyltriethylenetetraamine (HMTETA) yielded well‐defined diblock copolymers with polydispersities around 1,3. The diblock copolymer with poly(4‐acetoxystyrene) was hydrolyzed to the corresponding poly(4‐hydroxystyrene) sequence.     

Controlled polymerization of 2‐(diethylamino)ethyl methacrylate and its block copolymer with N‐isopropylacrylamide by RAFT polymerization

Poly(2‐(diethylamino)ethyl methacrylate) (PDEAEMA) homopolymers with low polydispersities were synthesized by reversible addition fragmentation chain transfer (RAFT) radical polymerization. The performances of two chain transfer agents, 2‐cyanoprop‐2‐yl dithiobenzoate and 4‐cyanopentanic acid dithiobenzoate (CPADB), were compared. It was found that the polymerization of 2‐(diethylamino) ethyl methylacrylate was under good control in the presence of CPADB with 4,4′‐azobis(4‐cyanopentanoic acid) (ACPA) as initiator in 1,4‐dioxane at 70 °C. The kinetic behaviors were investigated under different CPADB/ACPA molar ratios. A long polymerization inhibition period was observed at high [CPADB]/[ACPA] ratio. The influences of [CPADB]/[ACPA] ratio, monomer/[CPADB] ratio, and temperature were studied with respect to monomer conversion, molecular weight control, and polydispersity index (PDI). The PDI decreased from 1.21 to 1.12, as the CPADB/ACPA molar ratio changed from 2 to 10. The molecular weight of PDEAEMA could be controlled by monomer/CPADB molar ratio. The control over MW and PDI was improved as the temperature increased from 60 to 70 °C; however, an additional increase to 80 °C led to a loss of control. Using PDEAEMA macroRAFT agent, pH/thermo double‐responsive block copolymers of PDEAEMA and poly(N‐isopropylacrylamide) (PDEAEMA‐b‐PNIPAM) with narrow polydispersity (PDI, 1.24) were synthesized. The lower critical solution temperature of PDEAEMA‐b‐PNIPAM block copolymer depended on the environmental pH. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 3294–3305, 2008     

Novel thermoresponsive fluorinated double‐hydrophilic poly{[N‐(2,2‐difluoroethyl)acrylamide]‐b‐[N‐(2‐fluoroethyl)acrylamide]} block copolymers

Novel thermoresponsive double‐hydrophilic fluorinated block copolymers were successfully synthesized by reversible addition‐fragmentation chain transfer (RAFT) polymerization. Poly[N‐(2,2‐difluoroethyl)acrylamide] (P2F) was synthesized via RAFT polymerization of N‐(2,2‐difluoroethyl)acrylamide (M2F) using 2‐dodecylsulfanylthiocarbonylsulfanyl‐2‐methylpropionic acid (DMP) as the chain transfer agent (CTA) and 2,2′‐azobisisobutyronitrile (AIBN) as the initiator. The resulting P2F macroCTA was further chain extended with N‐(2‐fluoroethyl)acrylamide (M1F) to yield poly{[N‐(2,2‐difluoroethyl)acrylamide]‐b‐[N‐(2‐fluoroethyl)acrylamide]} (P2F‐b‐P1F) block copolymers with different lengths of the P1F block. Molecular weight and molecular weight distribution were determined by gel permeation chromatography. The average molecular weight (M_n) of the resulting polymers ranged from 2.9 × 10⁴ to 5.8 × 10⁴ depending on the length of the P1F block. The molecular weight distribution was low (M_w/M_n = 1.11–1.19). Turbidimetry by UV‐Visble (UV‐Vis) spectroscopy, dynamic light scattering, and in situ temperature‐dependent ¹H NMR measurements demonstrated that the P2F block underwent a thermal transition from hydrophilic to hydrophobic, which in turn induced self‐assembly from unimers to aggregates. Transmission electron microscopy studies demonstrated that polymeric aggregates formed from an aqueous solution of P2F‐b‐P1F at 60 °C were disrupted by cooling down to 20 °C and regenerated by heating to 60 °C. Temperature‐triggered release of a model hydrophobic drug, coumarin 102, was also demonstrated. © 2013 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Reversible addition–fragmentation chain transfer polymerization of 2‐naphthyl acrylate with 2‐cyanoprop‐2‐yl 1‐dithionaphthalate as a chain‐transfer agent

The reversible addition–fragmentation chain transfer (RAFT) polymerizations of 2‐naphthyl acrylate (2NA) initiated by 2,2′‐azobisisobutyronitrile were investigated with 2‐cyanoprop‐2‐yl 1‐dithionaphthalate (CPDN) as a RAFT agent at various temperatures in a benzene solution. The results of the polymerizations showed that 2NA could be polymerized in a controlled way by RAFT polymerization with CPDN as a RAFT agent; the polymerization rate was first‐order with respect to the monomer concentration, and the molecular weight increased linearly with the monomer conversion. The polydispersities of the polymer were relatively low up to high conversions in all cases. The chain‐extension reactions of poly(2‐naphthyl acrylate) (P2NA) with methyl methacrylate and styrene successfully yielded poly(2‐naphthyl acrylate)‐b‐poly(methyl methacrylate) and poly(2‐naphthyl acrylate)‐b‐polystyrene block polymers, respectively, with narrow polydispersities. The P2NA obtained by RAFT polymerization had a strong ultraviolet absorption at 270 nm, and the molecular weights had no apparent effect on the ultraviolet absorption intensities; however, the fluorescence intensity of P2NA increased as the molecular weight increased and was higher than that of 2NA. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 2632–2642, 2005     

Synthesis and characterization of well‐defined block and statistical copolymers based on lauryl methacrylate and 2‐(acetoacetoxy)ethyl methacrylate using RAFT‐controlled radical polymerization

Four well‐defined diblock copolymers and one statistical copolymer based on lauryl methacrylate (LauMA) and 2‐(acetoacetoxy)ethyl methacrylate (AEMA) were prepared using reversible addition‐fragmentation chain transfer (RAFT) polymerization. The polymers were characterized in terms of molecular weights, polydispersity indices (ranging between 1.12 and 1.23) and compositions by size exclusion chromatography and ¹H NMR spectroscopy, respectively. The preparation of the block copolymers was accomplished following a two‐step methodology: First, well‐defined LauMA homopolymers were prepared by RAFT using cumyl dithiobenzoate as the chain transfer agent (CTA). Kinetic studies revealed that the polymerization of LauMA followed first‐order kinetics demonstrating the “livingness” of the RAFT process. The pLauMAs were subsequently used as macro‐CTA for the polymerization of AEMA. The glass transition (T_g) and decomposition temperatures (ranging between 200 and 300 °C) of the copolymers were determined using differential scanning calorimetry and thermal gravimetric analysis, respectively. The T_gs of the LauMA homopolymers were found to be around ?53 °C. Block copolymers exhibited two T_gs suggesting microphase separation in the bulk whereas the statistical copolymer presented a single T_g as expected. Furthermore, the micellization behavior of pLauMA‐b‐pAEMA block copolymers was investigated in n‐hexane, a selective solvent for the LauMA block, using dynamic light scattering. pLauMA‐b‐pAEMA block copolymers formed spherical micelles in dilute hexane solutions with hydrodynamic diameters ranging between 30 and 50 nm. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 5442–5451, 2008     

Hyperbranched polymers as scaffolds for multifunctional reversible addition–fragmentation chain‐transfer agents: A route to polystyrene‐core‐polyesters and polystyrene‐block‐poly(butyl acrylate)‐core‐polyesters

Polydisperse hyperbranched polyesters were modified for use as novel multifunctional reversible addition–fragmentation chain‐transfer (RAFT) agents. The polyester‐core‐based RAFT agents were subsequently employed to synthesize star polymers of n‐butyl acrylate and styrene with low polydispersity (polydispersity index < 1.3) in a living free‐radical process. Although the polyester‐core‐based RAFT agent mediated polymerization of n‐butyl acrylate displayed a linear evolution of the number‐average molecular weight (M_n) up to high monomer conversions (>70%) and molecular weights [M_n > 140,000 g mol^?1, linear poly(methyl methacrylate) equivalents)], the corresponding styrene‐based system reached a maximum molecular weight at low conversions (≈30%, M_n = 45,500 g mol^?1, linear polystyrene equivalents). The resulting star polymers were subsequently used as platforms for the preparation of star block copolymers of styrene and n‐butyl acrylate with a polyester core with low polydispersities (polydispersity index < 1.25). The generated polystyrene‐based star polymers were successfully cast into highly regular honeycomb‐structured microarrays. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 3847–3861, 2003     

R‐RAFT approach for the polymerization of N‐isopropylacrylamide with a star poly(ε‐caprolactone) core

Reversible addition‐fragmentation chain transfer (RAFT) polymerization is a more robust and versatile approach than other living free radical polymerization methods, providing a reactive thiocarbonylthio end group. A series of well‐defined star diblock [poly(ε‐caprolactone)‐b‐poly(N‐isopropylacrylamide)]₄ (SPCLNIP) copolymers were synthesized by R‐RAFT polymerization of N‐isopropylacrylamide (NIPAAm) using [PCL‐DDAT]₄ (SPCL‐DDAT) as a star macro‐RAFT agent (DDAT: S‐1‐dodecyl‐S′‐(α, α′‐dimethyl‐α″‐acetic acid) trithiocarbonate). The R‐RAFT polymerization showed a controlled/“living” character, proceeding with pseudo‐first‐order kinetics. All these star polymers with different molecular weights exhibited narrow molecular weight distributions of less than 1.2. The effect of polymerization temperature and molecular weight of the star macro‐RAFT agent on the polymerization kinetics of NIPAAm monomers was also addressed. Hardly any radical–radical coupling by‐products were detected, while linear side products were kept to a minimum by careful control over polymerization conditions. The trithiocarbonate groups were transferred to polymer chain ends by R‐RAFT polymerization, providing potential possibility of further modification by thiocarbonylthio chemistry. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

RAFT‐mediated batch emulsion polymerization of styrene using poly[N‐(4‐vinylbenzyl)‐N,N‐dibutylamine hydrochloride] trithiocarbonate as both surfactant and macro‐RAFT agent

Poly[N‐(4‐vinylbenzyl)‐N,N‐dibutylamine hydrochloride] trithiocarbonate, which contains the reactive trithiocarbonate group and the appending surface‐active groups, is used as both surfactant and macromolecular reversible addition‐fragmentation chain transfer (macro‐RAFT) agent in batch emulsion polymerization of styrene. Under the conditions at high monomer content of ～20 wt % and with the molecular weight of the macro‐RAFT agent ranging from 4.0 to 15.0 kg/mol, well‐controlled batch emulsion RAFT polymerization initiated by the hydrophilic 2‐2′‐azobis(2‐methylpropionamidine) dihydrochloride is achieved. The polymerization leads to formation of nano‐sized colloids of the poly[N‐(4‐vinylbenzyl)‐N,N‐dibutylamine hydrochloride]‐b‐ polystyrene‐b‐poly[N‐(4‐vinylbenzyl)‐N,N‐dibutylamine hydrochloride] triblock copolymer. The colloids generally have core‐shell structure, in which the hydrophilic block forms the shell and the hydrophobic block forms the core. The molecular weight of the triblock copolymer linearly increases with increase in the monomer conversion, and the values are well‐consistent with the theoretical ones. The molecular weight polydispersity index of the triblock copolymer is below 1.2 at most cases of polymerization. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Polyisobutylene‐b‐Poly(N,N‐diethylacrylamide) well‐defined amphiphilic diblock copolymer: Synthesis and thermo‐responsive phase behavior

Polyisobutylene‐b‐poly(N,N‐diethylacrylamide) (PIB‐b‐PDEAAm) well‐defined amphiphilic diblock copolymers were synthesized by sequential living carbocationic polymerization and reversible addition‐fragmentation chain transfer (RAFT) polymerization. The hydrophobic polyisobutylene segment was first built by living carbocationic polymerization of isobutylene at ?70 ° C followed by multistep transformations to give a well‐defined (M_w/M_n = 1.22) macromolecular chain transfer agent, PIB‐CTA. The hydrophilic poly(N,N‐diethylacrylamide) block was constructed by PIB‐CTA mediated RAFT polymerization of N,N‐diethylacrylamide at 60 ° C to afford the desired well‐defined PIB‐b‐PDEAAm diblock copolymers with narrow molecular weight distributions (M_w/M_n ≤1.26). Fluorescence spectroscopy, transmission electron microscope, and dynamic light scattering (DLS) were employed to investigate the self‐assembly behavior of PIB‐b‐PDEAAm amphiphilic diblock copolymers in aqueous media. These diblock copolymers also exhibited thermo‐responsive phase behavior, which was confirmed by UV‐Vis and DLS measurements. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 1143–1150     

Synthesis and characterization of block copolymers containing poly(di(ethylene glycol) 2‐ethylhexyl ether acrylate) by reversible addition–fragmentation chain transfer polymerization

Reversible addition–fragmentation chain transfer (RAFT) polymerization has emerged as one of the important living radical polymerization techniques. Herein, we report the polymerization of di(ethylene glycol) 2‐ethylhexyl ether acrylate (DEHEA), a commercially‐available monomer consisting of an amphiphilic side chain, via RAFT by using bis(2‐propionic acid) trithiocarbonate as the chain transfer agent (CTA) and AIBN as the radical initiator, at 70 °C. The kinetics of DEHEA polymerization was also evaluated. Synthesis of well‐defined ABA triblock copolymers consisting of poly(tert‐butyl acrylate) (PtBA) or poly(octadecyl acrylate) (PODA) middle blocks were prepared from a PDEHEA macroCTA. By starting from a PtBA macroCTA, a BAB triblock copolymer with PDEHEA as the middle block was also readily prepared. These amphiphilic block copolymers with PDEHEA segments bearing unique amphiphilic side chains could potentially be used as the precursor components for construction of self‐assembled nanostructures. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 5420–5430, 2007     

Reversible addition–fragmentation chain transfer polymerization of glycidyl methacrylate with 2‐cyanoprop‐2‐yl 1‐dithionaphthalate as a chain‐transfer agent

A reversible addition–fragmentation chain transfer (RAFT) agent, 2‐cyanoprop‐2‐yl 1‐dithionaphthalate (CPDN), was synthesized and applied to the RAFT polymerization of glycidyl methacrylate (GMA). The polymerization was conducted both in bulk and in a solvent with 2,2′‐azobisisobutyronitrile (AIBN) as the initiator at various temperatures. The results for both types of polymerizations showed that GMA could be polymerized in a controlled way by RAFT polymerization with CPDN as a RAFT agent; the polymerization rate was first‐order with respect to the monomer concentration, and the molecular weight increased linearly with the monomer conversion up to 96.7% at 60 °C, up to 98.9% at 80 °C in bulk, and up to 64.3% at 60 °C in a benzene solution. The polymerization rate of GMA in bulk was obviously faster than that in a benzene solution. The molecular weights obtained from gel permeation chromatography were close to the theoretical values, and the polydispersities of the polymer were relatively low up to high conversions in all cases. It was confirmed by a chain‐extension reaction that the AIBN‐initiated polymerizations of GMA with CPDN as a RAFT agent were well controlled and were consistent with the RAFT mechanism. The epoxy group remained intact in the polymers after the RAFT polymerization of GMA, as indicated by the ¹H NMR spectrum. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2558–2565, 2004     

Synthesis and characterization of tris(2,2′‐bipyridine)ruthenium‐cored star‐shaped polymers via RAFT polymerization

A new bipyridine‐functionalized dithioester was synthesized and further used as a RAFT agent in RAFT polymerization of styrene and N‐isopropylacrylamide. Kinetics analysis indicates that it is an efficient chain transfer agent for RAFT polymerization of the two monomers which produce polystyrene and poly(N‐isopropylacrylamide) polymers with predetermined molecular weights and low polydispersities in addition to the end functionality of bipyridine. The bipyridine end‐functionalized polymers were further used as macroligands for the preparation of star‐shaped metallopolymers. Hydrophobic polystyrene macroligand combined with hydrophiphilic poly(N‐isopropylacrylamide) was complexed with ruthenium ions to produce amphiphilic ruthenium‐cored star‐shaped metallopolymers. The structures of these synthesized metallopolymers were further elucidated by UV–vis, fluorescence, size exclusion chromatography (SEC), and differential scanning calorimetry (DSC) as well as NMR techniques. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4225–4239, 2007