孔道结构H3PW12040／TiO2的制备及其可见光光催化降解水溶性染料的性能

采用溶胶一凝胶方法制备了孔道结构复合材料H3PW12040／TiO2，采用ICP-AES，UV／DRS，^31PMAS NMR，TEM和N2吸附等技术对其组成和结构进行了表征．结果表明，催化剂中活性组分H3PW12O40的基本骨架结构未发生改变，H3PW12O40的担载量为22．29％，催化剂平均粒径为40nm，具有双孔结构，其平均微孔和介孔孔径分别为0．6l和3．06nm．考察了催化剂可见光光催化降解6种水溶性染料的性能．结果表明，6种染料均可不同程度地被降解和矿化．通过对染料中性红的光催化降解实验，比较了H3PW12040／TiO2，Degussa P-25和锐钛矿结构Ti02的可见光光催化活性，其中，H3PW12040／TiO2活性最高，且催化剂最易分离，可循环使用．     

复合光催化材料H3PW122O40/Ta2O5光催化降解染料的研究

采用溶胶-凝胶法制备了半导体型金属氧化物Ta2O5,并通过浸渍法与杂多酸H,PW12O40复合,获得了纳米复合光催化材料H3PW12O40/Ta2O5.通过1CP-AES、FT-lR、N2吸附、Tc等手段对其组成、结构及其表面物理化学性质进行了表征,并在可见光下考察了该复合材料对可溶性染料罗丹明B和亚甲基蓝的光催化活性.实验结果表明,该复合材料存可见光下有较好的光催化活性,其中,H3PW12O40/Ta2O5在180min内对亚甲基蓝的光催化降解转化率达到78%.     

微波增强H3PW12O40／TiO2光催化降解染料和水杨酸的研究

以孔雀石绿为模型分子, 考察了微波无极灯的形状、微波功率和溶液初始浓度对光催化降解效果的影响. 并且在最佳微波反应条件下, 考察了通过溶胶-凝胶再结合程序升温水热法制备的复合材料H3PW12O40/TiO2对刚果红、酸性黑、酸性品红和水杨酸的光催化降解情况. 结果表明, 微波无极灯具有更好地增强H3PW12O40/TiO2光催化降解有机污染物的作用.     

TiO2/SiO2的制备及其光催化降解敌敌畏

二氧化钛;溶胶-凝胶法;表面复合物;TiO2/SiO2的制备及其光催化降解敌敌畏     

LiF掺杂TiO2的制备及其光催化性能

采用溶胶-凝胶法制备了LiF掺杂的TiO2光催化剂,并采用X射线衍射、X射线光电子能谱和光致发光光谱等技术对样品进行了表征.以亚甲基蓝的光催化降解为反应模型,考察了LiF掺杂量、退火温度和溶液pH值对催化剂光催化性能的影响.结果表明,LiF的掺杂降低了金红石相的形成温度,同时在TiO2表面引入大量羟基氧并提高了TiO2表面氧空穴浓度,因此提高了TiO2的光催化性能.在LiF掺杂量为8%,退火温度为500℃和反应液pH值为6.6的条件下,LiF掺杂的TiO2的光催化活性是未掺杂TiO2的6倍.     

金属离子掺杂的TiO2薄膜的制备及其光催化降解甲苯的性能

 采用溶胶-凝胶法制备了负载于铝板上掺杂金属离子的TiO2薄膜光催化剂,并通过空气中甲苯光催化降解实验评价了其光催化活性. 结果表明,Pt和Fe的掺杂对TiO2薄膜的光催化活性起促进作用,甲苯降解率分别提高了17%和6%; Ag的掺杂引起催化剂失活; Mn的掺杂未对TiO2薄膜的光催化活性起明显促进作用. XRD结果表明,掺杂金属离子前后TiO2均为锐钛矿相; TEM观察到薄膜催化剂微观结构为球形颗粒,粒径分布均匀,平均粒径为19 nm; 紫外漫反射光谱表明,Pt-TiO2薄膜催化剂的反射率几乎为0,表明其对光的吸收能力很强,因而Pt掺杂的TiO2薄膜光催化降解甲苯的活性最高.     

磁性纳米TiO2/Fe3O4光催化复合材料的制备及性能

采用溶胶-凝胶法，在磁性Fe3O4表面包覆TiO2，制备了一种新型纳米TiO2/Fe3O4光催化复合材料．XRD，TEM对材料形态结构及包覆情况的分析，显示TiO2包覆在Fe3O4表面，形成平均尺寸为35～50nm的复合结构；UV-vis吸收曲线表明，复合材料对光的吸收出现红移，吸收强度增大；对染料废水光催化降解的模拟研究表明，该复合材料对活性艳红染料的脱色率达100％，是一种便于回收、可重复使用的高效光催化剂．     

三维有序介孔/大孔TiO2微球的制备、表征及光催化性能

以聚甲基丙烯酸甲酯微球为模板,分别以钛酸四丁酯和四异丙醇钛为钛源,通过溶胶-凝胶法辅助模板法制得TiO2纳米微球前驱体,并用程序升温控制其焙烧温度,最终成功制得了具有三维有序介孔/大孔复合结构的TiO2微球.以罗丹明B(RhB)为模型污染物,探索了以不同钛源制备得到的介孔/大孔复合TiO2微球的光催化性能;并采用XRD、SEM、TEM、UV-vis DRS、比表面积测试、光催化性能测试等对样品的晶粒尺寸、物相、形貌、光吸收、比表面积及性能等进行了分析.结果表明,运用溶胶凝胶法辅助模板法能够合成结晶度高、形貌规整、比表面积大、光催化活性良好的锐钛矿相TiO2微球.     

多酸/二氧化钛复合光催化剂的制备及光催化苯胺的研究

采用溶胶-凝胶法,将Keggin结构的饱和磷钨酸、硅钨酸复合到二氧化钛薄膜中,合成出POM/TiO2复合光催化剂.红外光谱表明在复合膜中,多酸仍保持其基本结构不变.详细考察了催化剂种类、催化剂用量和反应体系等因素对苯胺的光催化降解反应的影响.     

纳米复合材料CdS/TiO2制备与不同模式光催化降解多种染料

采用化学水浴沉淀法再结合溶胶-凝胶和程序升温溶剂热两步法制备了一系列不同比例的CdS/TiO2。通过XRD、XPS、SEM、UV-Vis/DRS等手段对所合成纳米复合材料的组成、结构和形貌等进行了表征。结果表明,该系列CdS/TiO2为锐钛矿TiO2和六方相CdS的混合晶相,其在可见光有较强吸收,并且随着复合材料中TiO2比例的增加,BET值明显增大。另外,所合成CdS/TiO2呈圆球形,颗粒比较均匀。紫外光催化降解甲基橙的实验结果表明,摩尔比为1:4的CdS/TiO2的活性明显高于CdS、P25以及其它不     

镧系离子掺杂TiO2的制备及其对咪唑降解反应的光催化活性

 以TiCl4和镧系元素的氯化盐溶液为前驱体,采用溶胶-凝胶法制备了不同含量镧系离子掺杂的TiO2光催化剂,用X射线衍射(XRD)、 光致发光光谱(PLS)、 表面光电压谱(SPS)和X射线光电子能谱(XPS)对催化剂进行了表征. XRD结果表明,样品为锐钛矿和金红石的混晶相,镧系离子未进入到TiO2晶格中. PLS和SPS测定结果表明,随着掺杂离子的不同和掺杂含量的不同,样品的谱强度呈现有规律的变化. 在紫外光照射下,以咪唑为目标降解物比较了催化剂的光催化活性. 结果表明,适当含量的镧系离子掺杂可有效促进TiO2表面光生载流子的分离,从而显著提高其光催化活性.     

多孔二氧化钛微球的制备、表征及其光催化性能

以Lutensol TO(异构十三醇聚氧乙烯醚)系列非离子表面活性剂为辅助剂,采用溶胶-凝胶法制备了比表面积高、孔径分布窄的锐钛矿型TiO2多孔微球,并用透射电镜、扫描电镜、热重-差热分析、X射线衍射和氮吸附进行了表征.以亚甲基蓝降解为模型反应评价了其光催化性能,并与商品化TiO2Degussa P25进行了比较.实验结果表明,样品在425℃焙烧后,形成具有孔状结构的锐钛矿型TiO2微球,粒径为0.7~1.0μm,比表面积为70.5 m2/g,总孔容为0.12 cm3/g,平均孔径为4.26nm,晶粒尺寸为12 nm.这种多孔TiO2微球具有较高的催化活性,与Degussa P25纳米TiO2的催化活性相当.     

TiO2/SiO2的制备及其对染料X-3B溶液降解的光催化活性

 以粗孔球形硅胶为载体,以聚乙二醇和二乙醇单乙醚的钛酸四丁酯无水乙醇溶液为浸涂液,用涂覆法制备了TiO2／SiO2光催化剂．用XRD,SEM和UV－Vis等对催化剂的物相、形貌及TiO2负载量进行了表征,并通过可溶性染料活性艳红X－3B的降解反应,考察了其光催化活性．实验结果表明,当选用16．79％TiO2／SiO2光催化剂时,活性艳红X－3B溶液的脱色率可达93％以上．     

二氧化钛悬浆体系中八种染料的太阳光催化氧化降解

研究了二氧化钛悬浆体系中具有不同结构和不同取代基的八种染料化合物在太阳光作用下的降解过程。实验中测定了染料溶液的脱色速度、总有机碳去除率以及降解过程中部分无机离子的生成情况。结果显示,在此条件下,八种染料化合物均得到不同程度的降解。着重比较了染料分子在光催化降解过程中,不同取代基以及取代基的不同位置对染料分子降解及无机离子生成情况的影响,从而进一步揭示了染料分子的光催化降解机理。     

Preparation,Microstructure and Photocatalytic Activity of the Porous TiO2 Anatase Coating by Sol-Gel Processing

In this study the porous TiO² anatase coatings are prepared from alkoxide solutions containing polyethylene glycol (PEG) by a dip-coating technique. The effects of PEG addition to the precursor solution on the photocatalytic activity and microstructure of the resultant coatings are studied. The larger amount and the larger molecular weight of PEG, the larger size and more pores produced in the resultant coatings on the decomposition of PEG during heat-treatment. The adsorbed hydroxyl content of such porous coatings is found to increase due to the larger size and more pores in the coatings. However, the transmittance of the coatings decreases due to the scattering by the larger size and more pores. Photocatalytic degradation experiments show that organophosphorous insecticide, dimethyl-2,2-dichlorovinyl phosphate (DDVP), was efficiently degraded in the presence of the porous TiO₂ coatings by exposing the DDVP solution to sunlight. Photocatalytic degradation rate was related to the adsorbed hydroxyl content, transmittance and morphology of the resultant coatings.     

超临界 CO2 辅助制备 TiO2 外负载火山岩复合体及其光催化降解亚甲基蓝性能

 以钛酸丁酯为前驱体, 封堵的火山岩为载体, 通过超临界 CO₂ 辅助制备了 TiO₂ 外负载火山岩复合体, 并将其用于光催化降解亚甲基蓝反应, 考察了溶液 pH 值及催化剂浓度对反应性能的影响. 结果表明, TiO₂ 外负载火山岩复合体的光催化性能优于纯 TiO₂ 和 TiO₂ 体负载火山岩复合体. 这是由于外负载复合体对亚甲基蓝的高吸附性、小晶粒尺寸的 TiO₂ 颗粒以及吸附和光催化降解间的协同效应. 亚甲基蓝浓度为 1.5 mg/L, 溶液 pH 为 8, 催化剂浓度为 6.8 mg/L 时, 外负载 TiO₂ 火山岩复合体上亚甲基蓝降解速率最高, 且使用后的催化剂仍具有高的光催化活性.     

微波加热制备泡沫镍负载La3+掺杂纳米TiO2及其光催化降解甲醛的性能

 采用常规加热和微波加热方法制备了两种泡沫镍负载La3+掺杂的纳米TiO2光催化剂,以甲醛光催化降解为模型反应,考察了制备方法和掺杂La3+对催化剂催化性能的影响,并采用扫描电镜、透射电镜、 X射线衍射和能量分散式光谱分析对催化剂进行了表征. 结果表明,微波加热法制备的纳米TiO2具有典型的锐钛矿型晶体结构,其粒径均匀且明显小于常规加热法制备的催化剂. 泡沫镍负载1.5%La3+掺杂的TiO2的光催化性能得到明显改善,反应90 min后甲醛的降解率仍达到93%. 在实验中发现催化剂有失活现象,但经简单清洗后其活性能够恢复.     

Preparation and Photocatalytic Activity of Ce,H3PW12O40 co-doped TiO2 Hollow Fibers

A series of Ce, H3PW12O40 co-doped TiO2 hollow fibers photocatalysts have been prepared by sol-gel method using ammonium ceric nitrate, H3PW12O40 and tetrabutyltitanate as precursors and cotton fibers as template, followed by calcination at 500 ℃ in N2 atmosphere for 2 h. Scanning electron microscopy, X-ray diffraction, nitrogen adsorption-desorption mea- surements, and UV-Vis spectroscopy are employed to characterize the morphology, crystal structure, surface structure, and optical absorption properties of the samples. The photo- catalytic performance of the samples has been studied by photodegradation phenol in water under UV and visible light irradiation. The results show that the TiO2 fiber materials have hollow structures, and the co-doped TiO2 hollow fibers exhibit higher photocatalytic activities for the degradation of phenol than un-doped, single-doped TiO2 hollow fibers under UV and visible light. In addition, the recyclability of co-doped TiO2 fibers is also confirmed that the TiO2 fiber retains ca. 90% of its activity after being used four times. It is shown that the co-doped TiO2 fibers can be activated by visible light and may be potentially applied to the treatment of water contaminated by organic pollutants. The synergistic effect of Ce and H3PW12O40 co-doping plays an important role in improving the photocatalytic activity.     

H_3PW_(12)O_(40)掺杂TiO_2介孔材料的制备及光催化性能

以P123为模板剂,采用溶胶-凝胶的溶剂热合成方法制备了H3PW12O40掺杂TiO2介孔材料H3PW12O40/TiO2.利用紫外可见漫反射吸收光谱(UV-vis/DRS)、X射线粉末衍射(XRD)、N2吸附和透射电子显微镜(TEM)手段对所制备的材料进行结构表征,罗丹明B(RB)为模型污染物评价其光催化性能.结果表明,所制备的介孔材料具有锐钛矿与板钛矿复合的晶型结构、大的BET比表面积和孔径均匀分布的介孔结构.光催化实验表明,H3PW12O40/TiO2可将罗丹明B完全矿化.