Initial stages of oxidation of Cu(1 1 1)

Several surface analysis techniques were combined to study the initial stages of oxidation of Cu(1 1 1) surfaces exposed to O₂ at low pressure (<5 × 10⁻⁶ mbar) and room temperature. Scanning tunneling microscopy (STM) results show that the reactivity is governed by the restructuring of the Cu(1 1 1) surface. On the terraces, oxygen dissociative adsorption leads to the formation of isolated O adatoms and clusters weakly bound to the surface. The O adatoms are located in the fcc threefold hollow sites of the unrestructured terraces. Friedel oscillations with an amplitude lower than 5 pm have been measured around the adatoms. At step edges, surface restructuring is initiated and leads to the nucleation and growth of a two-dimensional disordered layer of oxide precursor. The electronic structure of this oxide layer is characterised by a band gap measured by scanning tunneling spectroscopy to be ∼1.5 eV wide. The growth of the oxide islands progresses by consumption of the upper metal terraces to form triangular indents. The extraction of the Cu atoms at this interface generates a preferential orientation of the interface along the close-packed directions of the metal. A second growth front corresponds to the step edges of the oxide islands and progresses above the lower metal terraces. This is where the excess Cu atoms extracted at the first growth front are incorporated. STM shows that the growing disordered oxide layer consists of units of hexagonal structure with a first nearest neighbour distance characteristic of a relaxed Cu-Cu distance (∼0.3 nm), consistent with local Cu₂O(1 1 1)-like elements. Exposure at 300 °C is necessary to form an ordered two-dimensional layer of oxide precursor. It forms the so-called “29” superstructure assigned to a periodic distorted Cu₂O(1 1 1)-like structure.     

Effects of steps and defects on O2 dissociation on clean and modified Cu(1 0 0)

Dissociative chemisorption of O₂ on Cu(1 0 0), S/Cu(1 0 0) and Ag/Cu(1 0 0) surface alloy has been investigated by Auger electron spectroscopy (AES). A strong reduction in the initial O₂ chemisorption probability (S₀) from 0.05 to 7.4 × 10⁻³ is observed already at an Ag coverage of 0.02 ML. Further Ag deposition results only in a moderate decrease in S₀. Similar inhibition of O₂ dissociation is observed on S/Cu(1 0 0). It is concluded that at very low Ag coverages, the reduced reactivity of Ag/Cu(1 0 0) towards O₂ dissociation is primarily due to the steric blocking of the surface defects and that any electronic effects are only secondary and present only at higher Ag coverages.     

Oxygen-induced nano-faceting of Ir(2 1 0)

The adsorption of oxygen and the nanometer-scale faceting induced by oxygen have been studied on Ir(2 1 0). Oxygen is found to chemisorb dissociatively on Ir(2 1 0) at room temperature. The molecular desorption process is complex, as revealed by a detailed kinetic analysis of desorption spectra. Pyramid-shaped facets with {3 1 1} and (1 1 0) orientations are formed on the oxygen-covered Ir(2 1 0) surface when annealed to T?600 K. The surface remains faceted for substrate temperatures T<850 K. For T>850 K, the substrate structure reverts to the oxygen-covered (2 1 0) planar state and does so reversibly, provided that oxygen is not lost due to desorption or via chemical reactions upon which the planar (2 1 0) structure remains. A clean faceted surface was prepared through the use of low temperature surface cleaning methods: using CO oxidation, or reaction of H₂ to form H₂O, oxygen can be removed from the surface while preserving (“freezing”) the faceted structure. The resulting clean faceted surface remains stable for T<600 K. For temperatures above this value, the surface irreversibly relaxes to the planar state.     

Characterisation of the interaction of glycine with Cu(1 0 0) and Cu(1 1 1)

Reflection-absorption infrared spectroscopy (RAIRS) has been used to characterise the interaction of standard and fully deuterated glycine with Cu(1 0 0) and Cu(1 1 1). RAIRS shows clearly that the surface interaction leads to formation of the adsorbed deprotonated glycinate (NH₂CH₂COO-) species, with some evidence for changes in orientation with coverage previously seen on Cu(1 1 0). Qualitative low energy electron diffraction observations were also conducted to characterise the long-range ordering, although effects of electron-beam-induced radiation damage limited the information obtained. Nevertheless, the results do suggest some subtle isotopic-mass-related structural variations. The results are discussed in the context of previously published scanning tunnelling microscopy and photoelectron diffraction measurements.     

Growth of Ce on Rh(1 1 1)

We have studied the growth of cerium films on Rh(1 1 1) using STM (scanning tunneling microscopy), LEED (low energy electron diffraction), XPS (X-ray photoelectron spectroscopy) and AES (Auger electron spectroscopy). Measurements of the Ce films after room temperature deposition showed that Ce is initially forming nanoclusters in the low coverage regime. These clusters consist of 12 Ce atoms and have the shape of pinwheels. At a coverage of 0.25 ML (monolayer, ML) an adatom layer with a (2 × 2) superstructure is observed. Above 0.4 ML, Rh is diffusing through pinholes into the film, forming an unstructured mixed layer. Annealing at 250 °C leads to the formation of ordered Ce-Rh compounds based on the bulk compound CeRh₃. At a coverage of 0.1 ML, small ordered (2 × 2) surface alloy domains are observed. The exchanged Rh atoms form additional alloy islands situated on the pure Rh(1 1 1) surface, showing the same (2 × 2) superstructure as the surface alloy. At a coverage of 0.25 ML, the surface is completely covered by the surface alloy and alloy islands. The (2 × 2) structure is equivalent to a (1 1 1)-plane of CeRh₃, contracted by 6%. Annealing a 1 ML thick Ce layer leads to a flat surface consisting of different rotational domains of CeRh₃(1 0 0). The Rh needed for alloy formation comes from 50 Å deep pits in the substrate. Finally we show that LEIS (low energy ion scattering) is not suitable for the characterization of Ce and CeRh films due to strong effects of neutralization.     

A route to continuous ultra-thin cerium oxide films on Cu(1 1 1)

The growth and morphology of ultra-thin CeO₂(1 1 1) films on a Cu(1 1 1) substrate were investigated by means of low energy electron diffraction (LEED) and scanning tunneling microscopy (STM). The films were grown by physical vapor deposition of cerium in an oxygen atmosphere at different sample temperatures. The preparation procedure is based on a modification of a previous method suggested by Matolin and co-workers [1], involving growth at elevated temperature (520 K). Here, LEED shows good long range ordering with a “(1.5 × 1.5)” superstructure, but STM reveals a three-dimensional growth mode (Vollmer-Weber) with formation of a closed film only at larger thickness. Using a kinetically limited growth process by reactive deposition at low sample temperatures (100 K) and subsequent annealing, we show that closed layers of ceria with atomically flat terraces can be prepared even in the regime of ultra-thin films (1.5 ML). Closed and atomically flat ceria films of larger thickness (3 ML) are obtained by applying a multistep preparation procedure, in which successive ceria layers are homoepitaxially grown on this initial film. The resulting overlayers show strong similarities with the morphology of CeO₂(1 1 1) single crystal surfaces, suggesting the possibility to model bulk ceria by thin film systems.     

STM and LEED observations of a c(2 × 2) Ge overlayer on Pt(1 0 0)

We have investigated surface structures formed by deposition of 0.2 and 0.5-ML Ge on Pt(1 0 0) by using scanning tunneling microscopy (STM) and low electron energy diffraction (LEED). In addition, their temperature dependence and reactivity to CO have been studied. We observed the formation of disordered domains for Ge adatom coverages below 0.25-ML and complete c(2 × 2) structures at 0.25 to 0.5-ML Ge after annealing at 600-1200 K. Deposition of 0.2-ML Ge on a clean, hexagonally reconstructed (5 × 20)-Pt(1 0 0) substrate at 400 K lifts the reconstruction and ejects excess Pt atoms from the first layer into the adlayer. After annealing this surface to 600 K, the deposited Ge formed Ge adatoms on flat terraces and on round Pt adislands with incomplete c(2 × 2) structures, in addition to the presence of clean (1 × 1)-Pt(1 0 0) domains that were several nanometers across. Some domains of the unreconstructed (5 × 20)-Pt(1 0 0) surface still remained. After the deposition of 0.5-ML Ge and annealing at 600 K, disordered Ge domains disappeared and a c(2 × 2) Ge overlayer was produced all over the surface. Square terraces with square domains of the clean (1 × 1)-Pt(1 0 0) surface extended for nanometers. Annealing this surface to 900 K produced disordered Ge domains, and this was associated with an increase in Ge vacancies. When surfaces with 0.2-ML Ge were heated to 900 or 1200 K, or when a surface with 0.5-ML Ge was heated to 1200 K, larger domains of (5 × 20)-Pt(1 0 0) were formed with the agglomeration of disordered Ge adatoms. Pt clusters were observed in the Ge domains, and we consider these to be composed of those excess Pt atoms formed by lifting the reconstruction of the (5 × 20)-Pt(1 0 0) surface upon Ge agglomeration during cooling. A paper published elsewhere [T. Matsumoto, C. Ho, M. Batzill, B.E. Koel, Physical Review B, submitted for publication.] describes Na⁺-ion scattering spectroscopy (Na⁺-ISS) and X-ray photoelectron diffraction (XPD) experiments that distinguish between Ge present in an overlayer from incorporation into the top Pt layer to form a surface alloy for the surface structures reported here. Furthermore, these investigations revealed that disordered Ge adatoms observed herein might be associated with incomplete c(2 × 2) structures. Therefore, our observations of the formation of complete and incomplete domains of c(2 × 2) Ge adatoms indicate that interactions between Ge adatoms are repulsive at nearest neighbor distances and attractive at second-nearest neighbor distances. Regarding the reactivity of these surfaces, CO does not chemisorb on a Pt(1 0 0) surface with a c(2 × 2)-Ge overlayer and no measurable CO uptake was observed under UHV conditions at 220 K.     

Distribution of lattice-strain on partly nitrogen-covered Cu(0 0 1) surfaces

In-plane elastic lattice strain on the Cu(0 0 1)-c(2 × 2)N surfaces is investigated by scanning tunneling microscopy on the surface where nitrogen-adsorbed patches with average size of 5 × 5 nm² (c(2 × 2)N patches) are well separated by wide clean Cu surface. The lattice distortion on clean Cu surface is recognized in the vicinity of the boundary to a c(2 × 2)N patch. The positions of the protrusions observed on the c(2 × 2)N patch are compared with the surrounding undistorted (1 × 1) lattice of the clean Cu surface. Most of the protrusions on the c(2 × 2)N patches locate on the fourfold hollow sites of the undistorted Cu lattice. The lattice distortion is significant only near the boundary to the surrounding clean Cu surface.     

Chemisorption of atomic oxygen on Pd(1 1 1) studied by STM

Atomic oxygen resulting from the dissociation of O₂ on Pd(1 1 1) at low coverage was studied in a variable temperature scanning tunneling microscope (STM) in the range from 30 to 210 K. Oxygen atoms, which typically appear as 30-40 pm deep depressions on Pd(1 1 1), occupy fcc hollow sites and form ordered p(2 × 2) islands upon annealing above 180 K. The mobility of the atoms diminishes rapidly below 180 K, with an approximate diffusion barrier of 0.4-0.5 eV. Oxygen atom pairs produced by thermal dissociation of O₂ at 160 K occupy both fcc and hcp hollow sites. The atoms travel approximately 0.25 nm after dissociation, and the distribution of pairs is strongly influenced by the presence of subsurface impurities within the Pd sample. At much lower temperatures, the STM tip can dissociate oxygen molecules. Dissociation occurs at sample bias voltages exceeding approximately 0.1 V. Following tip-induced dissociation, the product atoms occupy only fcc hollow sites. Oxygen atoms can be manipulated via short range repulsive interactions with the STM tip.     

Aromatic interactions in the close packing of phenyl-imides at Cu(1 1 0) surfaces

The oxidation of aniline at Cu(1 1 0) surfaces at 290 K has been studied by XPS and STM. A single chemisorbed product, assigned to a phenyl imide (C₆H₅N(a)), is formed together with water which desorbs. Reaction with preadsorbed oxygen results in a maximum surface concentration of phenyl imide of 2.8 × 10¹⁴ mol cm⁻² and a surface dominated by domains of three structures described by , and unit meshes. However, concentrations of phenyl imide of up to 3.3 × 10¹⁴ mol cm⁻² were obtained from the coadsorption of aniline and dioxygen (300:1 mixture) resulting in a highly ordered biphasic structure with and domains. Comparison of the STM and XPS data shows that only half the phenyl imides at the surface are imaged. Pi-stacking of the phenyl rings is proposed to account for this observation.     

Variety of iron silicides grown on Si(0 0 1) surfaces by solid phase epitaxy: Schematic phase diagram

We systematically studied the formation of various iron-silicide phases, grown on Si(0 0 1) surfaces by solid phase epitaxy, with scanning tunneling microscopy, low-energy electron diffraction and reflection high-energy electron diffraction. We found and studied the phases of c(2 × 2) islands, rectangle-like islands, elongated islands, layered islands, dome-like islands, eddy and cracked structures, and small clusters. A schematic phase diagram of these phases is successfully summarized against iron coverage at room temperature and subsequent annealing temperature.     

Epitaxial C60 thin films on Bi(0 0 0 1)

We have used the Bi(0 0 0 1)/Si(1 1 1) template to grow highly ordered C₆₀ epitaxial thin films and analyzed them using scanning tunneling microscopy and low-energy electron microscopy. The in situ low-energy electron microscope investigations show that the initial nucleation of the C₆₀ islands on the surface takes place at surface defects, such as domain boundaries and multiple steps. The in-plane lattice parameters of this C₆₀ film turns out to be the same as that of the bulk fcc(1 1 1) C₆₀. The line-on-line epitaxial structure is realized in spite of a weak interaction between the C₆₀ molecules and Bi(0 0 0 1) surface, while scanning tunneling spectroscopy indicates that there is a negligible charge transfer between the molecules and the surface.     

Sulfur-induced mobilization of Au surface atoms on Au(1 1 1) studied by real-time STM

The interaction of sulfur with gold surfaces has attracted considerable interest due to numerous technological applications such as the formation of self-assembled monolayers and as a chemical sensor. Here, we report on the interaction of sulfur with Au(1 1 1) at two different temperatures (300 K and 420 K) studied by real-time scanning tunnelling microscopy, low energy electron diffraction and Auger electron spectroscopy. In the low coverage regime (<0.1 ML), S adsorption lifts the herringbone reconstruction of the clean Au(1 1 1) surface indicating a lateral expansion of the surface layer. An ordered (√3 × √3)R30° sulfur adlayer develops as the coverage reaches ∼0.3 ML. At higher S coverages (>0.3 ML) gold surface atoms are removed from regular terrace sites and incorporated into a growing gold sulfide phase. At 300 K this process leads to the formation of a rough pit and mound surface morphology. This gold sulfide exhibits short-range order and an incommensurate, long-range ordered AuS phase develops upon annealing at 450-525 K. In contrast, formation of an ordered AuS phase via rapid step-retraction rather than etch pit formation is observed during S-interaction with Au(1 1 1) surfaces at 420 K. Our results shed new light on the S-Au(1 1 1) interaction.     

Anisotropic kinetics on growing Ge(0 0 1) surfaces

Reflection high-energy electron diffraction (RHEED), reflectance difference spectroscopy (RDS), and scanning tunneling microscopy (STM) have been used to study the anisotropic kinetics on the growing Ge(0 0 1) surface. While switching of dimer direction in alternate (2 × 1)/(1 × 2) layers causes the bilayer-period oscillations in RD response, RHEED oscillations are governed by variations in surface step densities. We show that the RHEED oscillations are strongly affected by the growth front morphology: when the growth front becomes distributed over several layers, the transition from bilayer- to monolayer-period occurs in RHEED oscillations.     

Formation and structure of a (√19 × √19)R23.4°-Ge/Pt(1 1 1) surface alloy

An ordered (√19 × √19)R23.4°-Ge/Pt(1 1 1) surface alloy can be formed by vapor depositing one-monolayer Ge on a Pt(1 1 1) substrate at room temperature and subsequently annealing at 900-1200 K. The long-range order of this structure was observed by low energy electron diffraction (LEED) and confirmed by scanning tunneling microscopy (STM). The local structure and alloying of vapor-deposited Ge on Pt(1 1 1) at 300 K was investigated by using X-ray Photoelectron Diffraction (XPD) and low energy alkali ion scattering spectroscopy (ALISS). XPS indicates that Ge adatoms are incorporated to form an alloy surface layer at ∼900 K. Results from XPD and ALISS establish that Ge atoms are substitutionally incorporated into the Pt surface layer and reside exclusively in the topmost layer, with excess Ge diffusing deep into the bulk of the crystal. The incorporated Ge atoms at the surface are located very close to substitutional Pt atomic positions, without any corrugation or “buckling”. Temperature Programmed Desorption (TPD) shows that both CO and NO adsorb more weakly on the Ge/Pt(1 1 1) surface alloy compared to that on the clean Pt(1 1 1) surface.     

RT growth of acetonitrile and acrylonitrile on Si(0 0 1)-2 × 1 studied by XPS and LEED

In this work we show the adsorption of acetonitrile (CH₃CN) and acrylonitrile (CH₂CHCN) on Si(0 0 1)-2 × 1 at room temperature by increasing the molecular doses. Especially, by means of XPS and LEED data, we stress the action of these molecules on the silicon surface locating the dangling-bonds quasi-saturation within 10 L. The shortage of nitrogen XPS signal and some anomalies in carbon spectra point to an invading action from a traditional X-ray source (Al-K_α line) against chemisorbed molecules. In particular, we think that a long exposure to this radiation could break carbon-silicon bonds changing some adsorption geometries and making desorb molecular fragments.     

Electron and lattice structure of ultra thin Ag films on Si(1 1 1) and Si(0 0 1)

We studied the low temperature (T ? 130 K) growth of Ag on Si(0 0 1) and Si(1 1 1) flat surfaces prepared by Si homo epitaxy with the aim to achieve thin metallic films. The band structure and morphology of the Ag overlayers have been investigated by means of XPS, UPS, LEED, STM and STS. Surprisingly a (√3 × √3)R30° LEED structure for Ag films has been observed after deposition of 2-6 ML Ag onto a Si(1 1 1)(√3 × √3)R30°Ag surface at low temperatures. XPS investigations showed that these films are solid, and UPS measurements indicate that they are metallic. However, after closer STM studies we found that these films consists of sharp Ag islands and (√3 × √3)R30°Ag flat terraces in between. On Si(0 0 1) the low-temperature deposition yields an epitaxial growth of Ag on clean Si(0 0 1)-2 × 1 with a twinned Ag(1 1 1) structure at coverage’s as low as 10 ML. Furthermore the conductivity of few monolayer Ag films on Si(1 0 0) surfaces has been studied as a function of temperature (40-300 K).     

Epitaxial growth of ultra-thin NiO films on Cu(1 1 1)

The very first stages of the growth of NiO on Cu(1 1 1) is examined on a microscopic scale. The paper focuses on the morphological and structural characterization of nanostructures formed in the 0-1 Å thickness range. Ultra-thin NiO films, obtained through evaporation of a Ni rod under an oxygen atmosphere were grown at 550 K. In the early stages of the growth the oxide film morphology shows 10-30 nm large, monolayer high, islands with a partial incorporation of metallic Ni in the first Cu(1 1 1) surface plane. The first layer is formed by an epitaxial atomic layer exhibiting a STM contrast similar to the one observed on adsorbed oxygen on Cu(1 1 0). A NiO cluster nucleation and coalescence mechanism is proposed in order to explain the formation of the second NiO layer. A α-Ni₂O₃ hexagonal phase, or a structural distortion of the NiO(1 1 1)()R30° structure could both explain the complex LEED patterns.     

Phase discrimination of iron-silicides on Si(0 0 1) surfaces by three-dimensional reciprocal-lattice mapping

Various iron-silicides are grown on clean Si(0 0 1) surfaces by solid phase epitaxy, a process which involves the deposition of iron and subsequent annealing [6]. Among them, we studied the structure of three-dimensional (3D) elongated islands, which are the major silicide type produced at lower Fe coverage (∼1 monolayer) and ?500-600 °C annealing. We applied a newly developed method of azimuth-scan reflection high-energy electron diffraction (RHEED) to obtain 3D reciprocal-lattice mapping. We succeeded in discriminating an α-FeSi₂ phase from controversial bulk phases of the islands, and we were also able to determine the orientation relation as and , where the lattice mismatches are −1% in direction and +34% in direction. The attenuation of the incident electron beam along the length direction of the islands leads to extremely weak spots in the RHEED pattern. We emphasize that such an analysis of the reciprocal-lattice mapping is also useful in studying other 3D island structures. Using scanning tunneling microscopy, we showed that the island’s elongated directions are perpendicular to the dimer rows of the substrate located under the islands. The islands are located near the S_B step edges. The elongation lengths of the islands are almost the same as the widths of the Si substrate terraces. We discussed the formation mechanism of the 3D-elongated islands. From an atomic image of the facet and edge of a 3D-elongated island, we proposed an atomic-structure model of the island facet and edge: a Si adatom on the hollow site of four Si atoms of an unit, with ordering in the direction of the elongation, forming an facet locally.     

Orientation and structure of triple step staircase on vicinal Si(1 1 1) surfaces

The vicinal Si(1 1 1) surface, inclined towards the direction, was investigated by scanning tunnelling microscopy and spot profile analysing low energy electron diffraction. It has been established that the surface, consisting of regularly spaced triple steps and (1 1 1) terraces with a width equal to that of a single unit cell of the Si(1 1 1)-7 × 7 surface structure, has the (7 7 10) orientation. An atomic model of the triple step is proposed.