The CuGaSe2(0 0 1) surface: A (4 × 1) reconstruction

We report on the formation of a stable (4 × 1) reconstruction of the chalcopyrite CuGaSe₂(0 0 1) surface. Using Ar⁺ ion-bombardment and annealing of epitaxial CuGaSe₂ films grown on GaAs(0 0 1) substrates it was possible to obtain flat, well-ordered surfaces showing a clear (4 × 1) reconstruction. The cleanliness and structure were analyzed in situ by AES and LEED. AES data suggest a slight Se-enrichment and Cu-depletion upon surface preparation. Our results demonstrate that (0 0 1) surfaces of the Cu-III-VI₂(0 0 1) material can show stable, unfacetted surfaces.     

Observation of a (√3 × √3)-R30° reconstruction on GaN(0 0 0 1) by RHEED and LEED

A new reconstruction of √3 × √3-R30° has been observed on a GaN film grown on a 6H-SiC (0 0 0 1)-√3 × √3 surface using RHEED and LEED experimental techniques. The experimental LEED PF shows that the GaN film is Ga-terminated hexagonal. The surface is a mixture of two structures with a single bilayer height difference between them. One is a √3 × √3-R30° reconstruction with Ga-adatoms occupying the T4 sites. Another is a Ga-terminated 1 × 1 with no extra Ga on top. The area ratio of the √3 × √3 part to the 1 × 1 part is slightly larger than 1. The first principle total energy calculations and Tensor-LEED I-V curves simulations further confirm this structure model.     

Formation of oxygen-induced Si(1 1 3)-3 × 2 facets on the Si(5 5 12) surface

We report the formation of Si(1 1 3)-3 × 2 facets upon exposing oxygens on the Si(5 5 12) surface at an elevated temperature. These facets are found to form only for a limited range of oxygen exposure and exhibit a well-defined 3 × 2 LEED pattern. We also find the surface electronic state unique only to the facets in the valence band. The spectral feature of these electronic states and the behavior of a (1/3 1/2) LEED spot upon oxygen contents in the facets indicate that the formation is a heterogeneous mixture of the clean Si(1 1 3) facets free of oxygens and other facets containing oxygen atoms.     

Surface pre-melting and surface flattening of Bi nanofilms on Si(1 1 1)-7 × 7

We report on the in situ observation of temperature-driven drastic morphology evolution and surface pre-melting of the Bi(0 0 1) nanofilm deposited on the Si(1 1 1)-7 × 7 surface by use of spot-profile-analyzing low-energy electron diffraction (SPA-LEED). Surface step density of the single-crystalline, epitaxial Bi(0 0 1) film decreases above 350 K in a critical manner. On annealed Bi(0 0 1) films, we have detected surface pre-melting with a transition temperature of 350 K, which yields reversible diffraction intensity drop in addition to the harmonic Debye-Waller behavior. The observed surface flattening of the as-deposited film is driven by the increased amount of mobile adatoms created through the surface pre-melting.     

Formation and structure of a (√19 × √19)R23.4°-Ge/Pt(1 1 1) surface alloy

An ordered (√19 × √19)R23.4°-Ge/Pt(1 1 1) surface alloy can be formed by vapor depositing one-monolayer Ge on a Pt(1 1 1) substrate at room temperature and subsequently annealing at 900-1200 K. The long-range order of this structure was observed by low energy electron diffraction (LEED) and confirmed by scanning tunneling microscopy (STM). The local structure and alloying of vapor-deposited Ge on Pt(1 1 1) at 300 K was investigated by using X-ray Photoelectron Diffraction (XPD) and low energy alkali ion scattering spectroscopy (ALISS). XPS indicates that Ge adatoms are incorporated to form an alloy surface layer at ∼900 K. Results from XPD and ALISS establish that Ge atoms are substitutionally incorporated into the Pt surface layer and reside exclusively in the topmost layer, with excess Ge diffusing deep into the bulk of the crystal. The incorporated Ge atoms at the surface are located very close to substitutional Pt atomic positions, without any corrugation or “buckling”. Temperature Programmed Desorption (TPD) shows that both CO and NO adsorb more weakly on the Ge/Pt(1 1 1) surface alloy compared to that on the clean Pt(1 1 1) surface.     

RT growth of acetonitrile and acrylonitrile on Si(0 0 1)-2 × 1 studied by XPS and LEED

In this work we show the adsorption of acetonitrile (CH₃CN) and acrylonitrile (CH₂CHCN) on Si(0 0 1)-2 × 1 at room temperature by increasing the molecular doses. Especially, by means of XPS and LEED data, we stress the action of these molecules on the silicon surface locating the dangling-bonds quasi-saturation within 10 L. The shortage of nitrogen XPS signal and some anomalies in carbon spectra point to an invading action from a traditional X-ray source (Al-K_α line) against chemisorbed molecules. In particular, we think that a long exposure to this radiation could break carbon-silicon bonds changing some adsorption geometries and making desorb molecular fragments.     

The dense α-√3 × √3Pb/Si(1 1 1) phase: A comprehensive STM and SPA-LEED study of ordering, phase transitions and interactions

The T-θ phase diagram for the system Pb/Si(1 1 1) was determined in the coverage range 6/5 ML < θ < 4/3 ML from complementary STM and SPA-LEED experiments. This coverage is within the range where a “Devil’s Staircase” (DS) has been realized. The numerous DS phases answer conflicting information in the Pb/Si(1 1 1) literature and update the previously published phase diagram. The measurements reveal the thermal stability of the different linear DS phases with the transition temperature found to be a function of phase period. Because of additional complexity in the experimental system (i.e. two-dimensionality and 3-fold symmetry) the linear DS phases transform at higher temperature into commensurate phases of 3-fold symmetry HIC (historically named “hexagonal incommensurate phase”). Different types of HIC phases have been discovered differing in the size of the supercell built out of √3 × √3 domains separated by domain walls of the √7 × √3 phase. The detailed structures of these HIC phases (coverage, binding site, twist angle, etc.) have been deduced from the comparison of STM images and diffraction patterns. After heating the system to even higher temperature the HIC phase transforms into the disordered phase. For sufficiently high coverage a SIC (“striped incommensurate phase” which is also built from √3 × √3 domains but meandering √7 × √3 domain walls) is observed which also disorders at high temperatures.     

Holographic diffuse LEED image reconstruction for simultaneous occupation of different oxygen adsorption sites on Ni(1 1 1)

We determined the local adsorption structure of disordered oxygen on the Ni(1 1 1) surface by means of diffuse holographic LEED. The measurements have been performed above the critical temperature (T_c=450 K) for the oxygen order-disorder phase transition at 500 K and at a coverage of Θ=0.25 ML. At this temperature we found, in agreement with a previous LEED-IV-analysis [Surf. Sci. 349 (1996) 185], that besides the fcc threefold sites also hcp sites are occupied. In addition, a small amount seems to be located also at top and bridge sites. Reconstructing the holographic wavefield information, the different oxygen adsorption geometries are superimposed in the real space image. Nevertheless, a spatial resolution of 0.5-1 Å was sufficient to clearly distinguish between them. The influence of algorithmic parameters on the image quality was tested.     

Structure analysis of W(0 0 1)2 × 1-O surface at room and liquid nitrogen temperatures

Surface structure of O-adsorbed W(0 0 1) surface after annealing to 1200 K has been analyzed by low energy electron diffraction at 77 K as well as at room temperature. The optimum structure has tungsten missing rows and oxygen double rows. Furthermore, the R-factor is minimized at the structure that O atoms are adsorbed on one of the two different threefold hollow sites of the (1 1 0) facet appearing on the W(0 0 1)2 × 1 with missing row. However, the results suggest that two domains of O atoms adsorbed on both the two different threefold hollow sites coexist. Then, I-V curves have been analyzed as a function of the mixing ratio of the two domains having different O adsorption sites at room and low temperatures. The energy difference between these two sites has been estimated to be 6.5 meV from the temperature dependence of the mixing ratio.     

Structure and composition of the NiPd(1 1 0) surface

The NiPd(1 1 0) alloy surface was studied using low energy electron diffraction to measure the structure and composition of the first three atomic layers. The surface layer is highly enriched in Pd and has a significantly buckled structure. The second layer is also buckled, with displacements even larger than the surface layer. The second layer also exhibits intralayer segregation (chemical ordering), with alternate close-packed rows of atoms being Ni enriched and Pd enriched. The third layer has a structure and composition close to that of the bulk alloy. These results are compared with results for the other low index faces of NiPd, the extensive literature on NiPt alloy surfaces, and the growing body of theoretical literature for NiPd alloy surfaces.     

CuPc molecules adsorbed on Au(1 1 0)-(1 × 2): growth morphology and evolution of valence band states

We present the growth morphology, the long-range ordering, and the evolution of the valence band electronic states of ultrathin films of copper phthalocyanine (CuPc) deposited on the Au(1 1 0)-(1 × 2) reconstructed surface, as a function of the organic molecule coverage. The low energy electron diffraction patterns present a (5 × 3) reconstruction from the early adsorption stages. High-resolution UV photoelectron spectroscopy data show the disappearance of the Au surface states related to the (1 × 2) reconstruction, and the presence of new electronic features related to the molecule-substrate interaction and to the CuPc molecular states. The CuPc highest occupied molecular orbital gradually emerges in the valence band, while the interface electronic states are quenched, upon increasing the coverage.     

Adsorption of Pb on NiAl(1 1 0): energetics and structure

The adsorption of Pb onto a NiAl(1 1 0) single crystal surface at 300 K has been studied by Auger electron spectroscopy (AES), Low energy electron diffraction (LEED), molecular beam/surface scattering and single crystal adsorption calorimetry (SCAC). AES indicates a Stranski-Krastanov growth mode, i.e., Pb initially grows on NiAl(1 1 0) two-dimensionally until the first layer completes at 0.89 ML, where a superstructure is observed by LEED, followed by 3D islanding. Measurements of the Pb gas that does not stick indicate that Pb sticks on NiAl(1 1 0) with an initial probability of 0.99. The initial heat of adsorption of Pb on NiAl(1 1 0) is 249 ± 10 kJ/mol. Due to the repulsive interactions between Pb adatoms, the heat of adsorption decreases within the first layer to a value identical to the heat of sublimation of bulk Pb (195 kJ/mol), where it remains at higher coverages. This first application of adsorption calorimetry on such a thick sample (75 μm versus 0.2-8 μm previously) demonstrates that adsorption calorimetry can be extended to a wider range of surfaces, since this thickness can be achieved with nearly any single crystal material by simple mechanical thinning.     

Lateral interactions and nonequilibrium in adsorption and desorption. Part 1. Experimental results for (2 × 2)-(3O + NO)/Ru(0 0 1)

Extending earlier vibrational spectroscopy and thermal desorption measurements on this system, its geometrical structure and its adsorption/desorption kinetics have been investigated in detail. The adsorption and desorption of NO proceed, with little influence on the 3O template, on its (2 × 2) lattice of empty hcp sites. The desorption kinetics, with splitting of the TPD spectra into two peaks, are far from the expected behavior for independent sites. Also, the vibrational band structure shows dispersion beyond dipole-dipole interactions. So, despite the quite large NO-NO distance and their screening by the O atoms, there is clear evidence for static and dynamic lateral interactions which should be extractable from the data. A qualitative analysis suggests that these interactions are due to elastic coupling between the positions and vibrations, respectively, of the O and NO adsorbates. However, quantitative conclusions cannot be drawn directly as the kinetic data cannot be interpreted in a quasiequilibrium approach, as would be the normal procedure, due to the presence of strong nonequilibrium effects. The lack of internal equilibration is presumably caused by slow diffusion. The results are sufficiently complete and detailed to justify the effort of theoretical modeling with the aim to quantitatively describe both the lateral interactions and the nonequilibrium effects.     

Determination of a (4 × 4) structure formed on a Cu(0 0 1) surface by adsorption of calcium

The adsorption of calcium (Ca) atoms on a Cu(0 0 1) surface has been studied by low-energy electron diffraction (LEED) at 130, 300 and 400 K. It is found that a (4 × 4) was the only LEED pattern appeared at 400 K while a quasi-hexagonal structure was formed in a wide range of submonolayer coverage at 130 K. At 300 K, the (4 × 4) LEED spots were broad and weak. The (4 × 4) structure formed at 400 K was determined by a tensor LEED I-V analysis. It is a new-type of surface alloys consisting of five substitutional Ca atoms, nine surface Cu atoms, and two atomic vacancies in the unit cell. In spite of a quite large size-difference between Ca (3.94 Å) and Cu (2.55 Å) atoms, all Ca atoms are located at the substitutional sites. Among surface alloys so far reported, the atomic size ratio between Cu and Ca in the (4 × 4), 1.54, is the largest. Optimized structural parameters reveal that large lateral displacements of surface Cu atoms, being enabled by the appearance of the vacancies, allow the formation of the (4 × 4) structure.     

Water monolayer and multilayer adsorption on Ni(1 1 1)

Water adsorbed on Ni(1 1 1) forms an ordered, hydrogen bonded ice structure with a (2√7 × 2√7)R19° unit cell. The 2√7 wetting structure forms as islands and persists up to saturation of the first layer. Adsorption of a fraction of a monolayer more water into a second layer destroys the 2√7 registry and creates a disordered ice film. Gas adsorption measurements indicate that the wetting layer is completely covered by a second layer of water before thicker multilayer ice forms. As the second layer is completed the film orders to form an incommensurate crystalline ice film with a hexagonal LEED pattern, oriented to the Ni close packed rows. This ordered, incommensurate structure persists as the ice multilayer grows thicker.     

Growth and structure of vanadium oxide on anatase (1 0 1) terraces

The interaction of vanadium oxide with epitaxial anatase films exposing (1 0 1) terraces was characterized. The TiO₂ films were grown on vicinal LaAlO₃ (1 1 0) substrates by oxygen plasma-assisted molecular beam epitaxy (OPA-MBE); reflection high energy and low energy electron diffraction (RHEED and LEED) indicated that the films exposed (1 0 1) terraces of the anatase TiO₂ polymorph. When a vanadium oxide monolayer was deposited onto the anatase surface by OPA-MBE at 725 K, only (1 × 1) RHEED and LEED patterns were observed. The V X-ray photoelectron spectroscopy (XPS) peak intensities indicated that the monolayer wetted the anatase surface and so the diffraction patterns were attributed to an epitaxial vanadia layer. Analysis of the vanadium oxide monolayer by X-ray and ultraviolet photoelectron spectroscopies revealed that the V was predominantly 5+. When the vanadia coverage was increased at 725 K, Auger electron spectra showed only very slow attenuation of the anatase Ti peaks while spots began to develop in RHEED patterns recorded along the LaAlO₃ direction; both indicative of 3-D cluster formation. In the orthogonal direction, the RHEED patterns showed unusual diagonal streaks. Meanwhile, the (1 × 1) LEED pattern persisted even after 30 nm of vanadia was deposited. This was attributed to gaps between the 3-D clusters exposing the epitaxial monolayer. Core level XPS spectra of the 3-D clusters revealed a broad V 2p_3/2 peak that was centered at the position expected for V⁴⁺ but could be deconvoluted into three peaks corresponding to V³⁺, V⁴⁺, and V⁵⁺. It is shown that crystallographic shear that accommodates such variations in the oxygen content of V oxides can lead to the diagonal streaks in RHEED patterns recorded along the LaAlO₃ [0 0 1] direction even as the pattern in the orthogonal direction shows sharp transmission spots. The results show that vanadia growth on anatase (1 0 1) proceeds through the Stranski-Krastanov mode with a strong vanadia-titania interaction stabilizing a dispersed vanadia monolayer. The results are compared with previous data for vanadia growth on anatase (0 0 1) where smooth, epitaxial VO₂ films grow ad infinitum.     

Surface alloy formation after deposition of Ce on Rh(1 1 0)

Vapour deposition of Ce onto a Rh(1 1 0) single crystal at room temperature is studied by X-ray photoelectron spectroscopy (XPS), ultraviolet photoelectron spectroscopy (UPS) and low energy electron diffraction (LEED). The thicknesses of the deposited Ce layers are estimated to be between 2 and 9 Å. To study the changes in the Ce-Rh surface layer, the samples are annealed at temperatures between 500 and 1000 °C after Ce deposition.After heating, a c(2 × 2) LEED pattern appears for the sample with the thinnest deposited Ce layer (2.4 Å). For samples with thicker Ce-films, the LEED pattern co-exists of a c(2 × 2) structure and a more diffuse 6% contracted (2 × 1) structure. This appears at the same temperature as the Ce 3d and Rh 3d core levels exhibit sharp intensity changes and binding energy shifts.The intensity of the f⁰, f¹ and f² multiplets in the Ce 3d core level spectra change when the annealing temperature is increased. The relative intensity of the Ce 3d f⁰ and f² features compared to the Ce 3d f¹ features is largest after annealing to 500 °C. This is below the temperature at which the ordered surface alloy is formed. When the sample is heated above the formation temperature of the surface alloy, the relative intensity of the Ce 3d f⁰ and f² features decrease.     

The adsorption geometry of sulphur on Ir{1 0 0}: A quantitative LEED study

A quantitative low energy electron diffraction (LEED) analysis has been performed for the p(2 × 2)-S and c(2 × 2)-S surface structures formed by exposing the (1 × 1) phase of Ir{1 0 0} to H₂S at 750 K. S is found to adsorb on the fourfold hollow sites in both structures leading to Pendry R-factor values of 0.17 for the p(2 × 2)-S and 0.16 for the c(2 × 2)-S structures. The distances between S and the nearest and next-nearest Ir atoms were found to be similar in both structures: 2.36 ± 0.01 Å and 3.33 ± 0.01 Å, respectively. The buckling in the second substrate layer is consistent with other structural studies for S adsorption on fcc{1 0 0} transition metal surfaces: 0.09 Å for p(2 × 2)-S and 0.02 Å for c(2 × 2)-S structures. The (1 × 5) reconstruction, which is the most stable phase for clean Ir{1 0 0}, is completely lifted and a c(2 × 2)-S overlayer is formed after exposure to H₂S at 300 K followed by annealing to 520 K. CO temperature-programmed desorption (TPD) experiments indicate that the major factor in the poisoning of Ir by S is site blocking.     

Structural investigation of the c(√2 × 5√2)R45° surface alloy formed by Ti deposition on Cu(0 0 1)

The alloying process of Ti deposited on Cu(0 0 1) was studied by means of XPS, LEIS, XPD and LEED intensity analysis. With the sample held at 570 K, a linear decrease of the Cu LEIS signal as a function of the amount of Ti deposited is observed in the early stages of deposition until a constant value is reached. At the onset of the plateau a c(√2 × 5√2)R45° LEED pattern starts to be visible. XPD and LEED intensity measurements were performed for the c(√2 × 5√2)R45° phase prepared depositing ca. 1.5 monolayer of Ti. The angle-scanned XPD curves measured for the phase c(√2 × 5√2)R45° reveal that Ti atoms substitute Cu atoms in the fcc lattice of the substrate. The polar XPD curves show that at least the first four layers of the substrate are involved in the alloying process. We found that the (3 1 0) plane of the Cu₄Ti alloy (D1_a type-structure) fits, without significant contraction or expansion of the lattice parameters, the c(√2 × 5√2)R45° structure. The intensity versus energy curves of the diffracted beams were calculated on the basis of this structural model using the tensor LEED method. The results of the LEED intensity analysis provide a further evidence of the formation of a slab of Cu₄Ti(3 1 0) layers.     

An ordered surface ternary alloy of a c(6 × 4) structure formed on Cu(0 0 1) by substitutional coadsorption of Mg and Bi

A c(6 × 4) structure formed on Cu(0 0 1) by the coadsorption of Mg and Bi atoms at room temperature has been determined by a tensor low energy electron diffraction analysis. It is an ordered surface ternary alloy with a thickness of single layer, in which Mg, Bi and Cu atoms are mixed in the top layer. In the primitive unit cell, there are one Mg, four Bi, six Cu atoms and one vacancy in the top layer, and substituted Mg and Bi atoms form MgBi₄ plane clusters being arranged in the c(6 × 4) order. Structural parameters show that Mg-Bi bond distances in the MgBi₄ cluster are 3.01 and 3.07 Å, which are shorter than the summation of metallic radii of Mg and Bi. It is concluded that a direct, attractive interaction between Mg and Bi atoms plays critical role in the formation of the c(6 × 4) structure.