Effect of thermal annealing in the microstructural and the optical properties of uncapped InAs quantum dots grown on GaAs buffer layers

The effect of thermal annealing on self-assembled uncapped InAs/GaAs quantum dots (QDs) has been investigated using transmission electron microscopy (TEM) and photoluminescence (PL) measurements. The TEM images showed that the lateral sizes and densities of the InAs QDs were not changed significantly up to 650 °C. When the InAs/GaAs QDs were annealed at 700 °C, while the lateral size of the InAs QDs increased, their density decreased. The InAs QDs disappeared at 800 °C. PL spectra showed that the peaks corresponding to the interband transitions of the InAs QDs shifted slightly toward the high-energy side, and the PL intensity decreased with increasing annealing temperature. These results indicate that the microstructural and the optical properties of self-assembled uncapped InAs/GaAs can be modified due to postgrowth thermal annealing.     

PHOTOLUMINESCENCE STUDY OF InAs/GaAs SELF-ORGANIZED QUANTUM DOTS WITH BIMODAL SIZE DISTRIBUTION

We have investigated the temperature dependence of the photoluminescence (PL) spectrum of self-organized InAs/GaAs quantum dots. A distinctive double-peak feature of the PL spectra from quantum dots has been observed, and a bimodal distribution of dot sizes has also been confirmed by scanning tunneling microscopy image for uncapped sample. The power-dependent PL study demonstrates that the distinctive PL emission peaks are associated with the ground-state emission of islands in different size branches. The temperature-dependent PL study shows that the PL quenching temperature for different dot families is different. Due to lacking of the couple between quantum dots, an unusual temperature dependence of the linewidth and peak energy of the dot ensemble photoluminescence has not been observed. In addition, we have tuned the emission wavelength of InAs QDs to 1.3 μm at room temperature.     

Abnormal temperature dependence of photoluminescence from self-assembled InAs quantum dots covered by an InAlAs/InGaAs combination layer

In this report we have investigated the temperature dependence of photoluminescence (PL) from self-assembled InAs quantum dots (QDs) covered by an InAlAs/InGaAs combination layer. The ground state experiences an abnormal variation of PL linewidth from 15 K up to room temperature. Meanwhile, the PL integrated intensity ratio of the first excited state to the ground state for InAs QDs unexpectedly decreases with increasing temperature, which we attribute to the phonon bottleneck effect. We believe that these experimental results are closely related to the partially coupled quantum dots system and the large energy separation between the ground and the first excited states.     

Effects of thermal annealing on the interband transitions of single and vertically stacked InAs/GaAs self-assembled quantum dots

Photoluminescence (PL) measurements have been carried out to investigate the annealing effects in one-period and three-periods of InAs/GaAs self-assembled quantum dots (QDs) grown on GaAs substrates by using molecular beam epitaxy. After annealing, the PL spectra for the annealed InAs/GaAs QDs showed dramatic blue shifts and significant linewidth narrowing of the PL peaks compared with the as-grown samples. The variations in the PL peak position and the full width at half-maximum of the PL peak are attributed to changes in the composition of the InAs QDs resulting from the interdiffusion between the InAs QDs and the GaAs barrier and to the size homogeneity of the QDs. These results indicate that the optical properties and the crystal qualities of InAs/GaAs QDs are dramatically changed by thermal treatment.     

Abnormal Energy Dependence of Photoluminescence Decay Time in InGaN Epilayer

We employ photoluminescence (PL) and time-resolved PL to study exciton localization effect in InGaN epilayers.By measuring the exciton decay time as a function of the monitored emission energy at different temperatures,we have found unusual behaviour of the energy dependence in the PL decay process. At low temperature, the measured PL decay time increases with the emission energy. It decreases with the emission energy at 200K, and remains nearly constant at the intermediate temperature of 12OK. We have studied the dot size effect on the radiative recombination time by calculating the temperature dependence of the exciton recombination lifetime in quantum dots, and have found that the observed behaviour can be well correlated to the exciton localization in quantum dots. This suggestion is further supported by steady state PL results.     

Photoreflectance study of energy level structure of self-assembled InAs/GaAs quantum dots emitting at 1.3 μm

Photoreflectance and photoluminescence measurements were performed on the ensemble of self assembled InAs/GaAs quantum dots designed to emit at 1.3 μm. As many as six QDs-related optical transitions were observed in PR spectra, the energies of which were confirmed by high-excitation PL results. Numerical calculations allowed estimating the average size of the dots, which is larger than for standard InAs/GaAs QDs. This result is in agreement with structural data. Additionally, the energy level structure for such QDs was derived and compared with the electronic structure of standard InAs/GaAs dots. It was shown that the energy level structure of such large dots qualifies them for the active region of a laser emitting at 1.3 μm.     

Sb-mediated growth of high-density InAs quantum dots and GaAsSb embedding growth by MBE

Self-assembled InAs quantum dots (QDs) with high-density were grown on GaAs(0 0 1) substrates by antimony (Sb)-mediated molecular beam epitaxy technique using GaAsSb/GaAs buffer layer and InAsSb wetting layer (WL). In this Sb-mediated growth, many two-dimensional (2D) small islands were formed on those WL surfaces. These 2D islands provide high step density and suppress surface migration. As the results, high-density InAs QDs were achieved, and photoluminescence (PL) intensity increased. Furthermore, by introducing GaAsSb capping layer (CL), higher PL intensity at room temperature was obtained as compared with that InGaAs CL.     

Emission wavelength engineering of InAs/InP(001) quantum wires

In this work we have studied the dependence of the optical properties of self-assembled InAs quantum wires (QWr) grown on InP(001) on the growth temperature of the InP cap layer, as a mean for controlling the InAs QWr size. Our main result is that we can tune the emission wavelength of InAs QWr either at 1.3 m or 1.55 m at room temperature. We suggest that the role of growth temperature is to modify the As/P exchange at the InAs QWr/InP cap layer interface and consequently the amount of InAs involved in the nanostructure. In this way, due to the enhancement of the As/P exchange, the higher the growth temperature of the cap layer, the smaller in height the InAs quantum wires. Accordingly, the emission wavelength is blue shifted with InP cap layer growth temperature as the electron and hole ground state moves towards higher energies. Optical studies related to the dynamics of carrier recombination and light emission quenching with temperature are also included.Received: 16 December 2003, Published online: 3 August 2004PACS: 81.16.Dn Self-assembly - 78.67.Lt Quantum wires - 81.07.Vb Quantum wires     

Selective growth of stacked InAs quantum dots by using the templates formed by the Nano-Jet Probe

We have demonstrated the selective area growth of stacked self-assembled InAs quantum dot (QD) arrays in the desired regions on a substrate and confirmed the photoluminescence (PL) emission exhibited by them at room temperature. These InAs QDs are fabricated by the use of a specially designed atomic force microscope cantilever referred to as the Nano-Jet Probe (NJP). By using the NJP, two-dimensional arrays with ordered In nano-dots are fabricated in the desired square regions on a GaAs substrate and directly converted into InAs QD arrays through the subsequent annealing by the irradiation of As flux. By using the converted QD arrays as strain templates, self-organized InAs QDs are stacked. These stacked QDs exhibit the PL emission peak at a wavelength of 1.02 μm.     

Power density and temperature dependent multi-excited states in InAs/GaAs quantum dots

Self-assembled InAs/GaAs (001) quantum dots (QDs) were grown by molecular beam epitaxy using ultra low-growth rate. A typical dot diameter of around 28 ± 2 nm and a typical height of 5 ± 1 nm are observed based on atomic force microscopy image. The photoluminescence (PL) spectra, their power and temperature dependences have been studied for ground (GS) and three excited states (1–3ES) in InAs QDs. By changing the excitation power density, we can significantly influence the distribution of excitons within the QD ensemble. The PL peak energy positions of GS and ES emissions bands depend on an excitation light power. With increasing excitation power, the GS emission energy was red-shifted, while the 1–3ES emission energies were blue-shifted. It is found that the full width at half maximum of the PL spectra has unusual relationship with increasing temperature from 9 to 300 K. The temperature dependence of QD PL spectra shown the existence of two stages of PL thermal quenching and two distinct activation energies corresponding to the temperature ranges I (9–100 K) and II (100–300 K).     

The emission wavelength tuning of InAs/InP quantum dots with thin GaAs, InGaAs, InP capping layers by MOCVD

InAs quantum dots (QDs) were grown on InP substrates by metalorganic chemical vapor deposition. The width and height of the dots were 50 and 5.8 nm, respectively on the average and an areal density of 3.0×10¹⁰ cm⁻² was observed by atomic force microscopy before the capping process. The influences of GaAs, In_0.53Ga_0.47As, and InP capping layers (5–10 ML thickness) on the InAs/InP QDs were studied. Insertion of a thin GaAs capping layer on the QDs led to a blue shift of up to 146 meV of the photoluminescence (PL) peak and an InGaAs capping layer on the QDs led to a red shift of 64 meV relative to the case when a conventional InP capping layer was used. We were able to tune the emission wavelength of the InAs QDs from 1.43 to 1.89 μm by using the GaAs and InGaAs capping layers. In addition, the full-width at half-maximum of the PL peak decreased from 79 to 26 meV by inserting a 7.5 ML GaAs layer. It is believed that this technique is useful in tailoring the optical properties of the InAs QDs at mid-infrared regime.     

Strong photoluminescence and laser operation of InAs quantum dots covered by a GaAsSb strain-reducing layer

GaAsSb strain-reducing layers (SRLs) are applied to cover InAs quantum dots (QDs) grown on GaAs substrates. The compressive strain induced in InAs QDs is reduced due to the tensile strain induced by the GaAsSb SRL, resulting in a redshift of photoluminescence (PL) peaks of the InAs QDs. A strong PL signal around a wavelength of 1.3 μm was observed even at room temperature. A laser diode containing InAs QDs with GaAsSb SRLs in the active region was fabricated, which exhibits laser oscillation in pulsed operation at room temperature. These results indicate that GaAsSb SRLs have a high potential for fabricating high efficient InAs QDs laser diodes operating at long-wavelength regimes.     

Single-Photon Emission at Liquid Nitrogen Temperature from a Single InAs/GaAs Quantum Dot

We report on the single photon emission from single InAs/GaAs self-assembled Stranski-Krastanow quantum dots up to 80 K under pulsed and continuous wave excitations. At temperature 8OK, the second-order correlation function at zero time delay, g^（2）（0）, is measured to be 0.422 for pulsed excitation. At the same temperature under continuous wave excitation, the photon antibunching effect is observed. Thus, our experimental results demonstrate a promising potential application of self-assembled InAs/GaAs quantum dots in single photon emission at liquid nitrogen temperature.     

Photoluminescence and lasing properties of InAs/GaAs quantum dots grown by metal-organic chemical vapour deposition

Photoluminescence （PL） and lasing properties of InAs/GaAs quantum dots （QDs） with different growth procedures prepared by metalorganic chemical vapour deposition are studied. PL measurements show that the low growth rate QD sample has a larger PL intensity and a narrower PL line width than the high growth rate sample. During rapid thermal annealing, however, the low growth rate sample shows a greater blueshift of PL peak wavelength. This is caused by the larger InAs layer thickness which results from the larger 2-3 dimensional transition critical layer thickness for the QDs in the low-growth-rate sample. A growth technique including growth interruption and in-situ annealing, named indium flush method, is used during the growth of GaAs cap layer, which can flatten the GaAs surface effectively. Though the method results in a blueshift of PL peak wavelength and a broadening of PL line width, it is essential for the fabrication of room temperature working QD lasers.     

Photoluminescence scanning on InAs/InGaAs quantum dot structures

The photoluminescence spectra of InAs quantum dots (QDs) embedded into four types of In_xGa_1−xAs/GaAs (x = 0.10, 0.15, 0.20 and 0.25) multi quantum well MBE structures have been investigated at 300 K in dependence on the QD position on the wafer. PL mapping was performed with 325 nm HeCd laser (35 mW) focused down to 200 μm (110 W/cm²) as the excitation source. The structures with x = 0.15 In/Ga composition in the In_xGa_1−xAs capping layer exhibited the maximum photoluminescence intensity. Strong inhomogeneity of the PL intensity is observed by mapping samples with the In/Ga composition of x ≥ 0.20-0.25. The reduction of the PL intensity is accompanied by a gradual “blue” shift of the luminescence maximum at 300 K as follows from the quantum dot PL mapping. The mechanism of this effect has been analyzed. PL peak shifts versus capping layer composition are discussed as well.     

Analysis of room temperature PL spectra of InAs/GaAs/InP and InAs/InP self-assembled QDs: A five-band study

In this paper, room temperature PL spectra of InAs self-assembled dots grown on GaAs/InP and InP substrate are presented. For analyzing different positions of the PL peaks, we examine the strain tensor in these quantum dots (QDs) using a valence force field model, and use a five-band k·p formalism to find the electronic spectra. We find that the GaAs tensile-stained layer affects the position of room temperature PL peak. The redshift of PL peak of InAs/GaAs/InP QDs compared to that of InAs/InP QDs is explained theoretically.     

Time-resolved photoluminescence spectroscopy of InAs quantum dots on InP with various InAlGaAs barrier thicknesses

The Optical characteristics of InAs quantum dots (QDs) embeded in InAlGaAs on InP have been investigated by photoluminescence (PL) spectroscopy and time-resolved PL. Four different QD samples are grown by using molecular beam epitaxy, and all the QD samples have five-stacked InAs quantum dot layers with a different InAlGaAs barrier thickness. The PL yield from InAs QDs was increased with an increase in the thickness of the InAlGaAs barrier, and the emission peak positions of all InAs QD samples were measured around 1.5 μm at room temperature. The decay time of the carrier in InAs QDs is decreased abruptly in the QD sample with the 5 nm InAlGaAs barrier. This feature is explained by the tunneling and coupling effect in the vertical direction and probably defect generation.     

Chemical role of amines in the colloidal synthesis of CdSe quantum dots and their luminescence properties

The role of organic amines in the colloidal synthesis of CdSe quantum dots (QDs) has been studied. CdSe QDs were synthesized from the source solutions containing 5 vol% of amines having various alkyl chain lengths, stereochemical sizes and electron donation abilities. The role of the additional amines was evaluated on the basis of the photoluminescence (PL) properties such as PL wavelength and intensity of the obtained CdSe QDs. The observed PL spectra were explained by the fact that the amines behaved as capping ligands on the surface of the QDs in the product colloidal solution and complex ligands for cadmium in the source solutions. It was shown that the particle size was controlled by the diffusion process depending on the mass and stereochemical shape of the amines, and the luminescence intensity increased with the increasing electron donation ability and capping density of the amines.     

Ultrafast Kerr rotations and zero-field dephasing time of electron spins in InAs/GaAs quantum disks

Time-resolved Kerr rotation (TRKR) measurements based on pump-probe arrangement were carried out at 5 K on the monolayer fluctuation induced InAs/GaAs quantum disks grown on GaAs substrate without external magnetic field. The lineshape of TRKR signals shows an unusual dependence on the excitation wavelength, especially antisymmetric step-shaped structures appearing when the excitation wavelength was resonantly scanned over the heavy- and light-hole subbands. Moreover, these step structures possess an almost identical decay time of ∼40 ps which is believed to be the characteristic spin dephasing time of electrons in the extremely narrow InAs/GaAs quantum disks.     

Growth conditions effects on optical properties of InAs quantum dots grown by molecular beam epitaxy on GaAs (1 1 3)A substrate

We have investigated the optical properties of InAs/GaAs (1 1 3)A quantum dots grown by molecular beam epitaxy (MBE) with different growth rates by photoluminescence spectroscopy (PL) as a function of the excitation density and the sample temperature (10–300 K). Reflection high-energy electron diffraction (RHEED) is used to investigate the formation process of InAs quantum dots (QDs). A redshift of the InAs QDs PL band emission was observed when the growth rate was increased. This result was explained by the increase of the InAs quantum dot size with increasing growth rate. A significant redshift was observed when the arsenic flux was decreased. The evolution of the PL peak energy with increasing temperature has showed an S-shaped form due to the localization effects and is attributed to the efficient relaxation process of carriers in different InAs quantum dots and to the exciton transfer localized at the wetting layer.